WO2007090265A1 - Revetement stratifie thermoretractable - Google Patents

Revetement stratifie thermoretractable Download PDF

Info

Publication number
WO2007090265A1
WO2007090265A1 PCT/CA2007/000133 CA2007000133W WO2007090265A1 WO 2007090265 A1 WO2007090265 A1 WO 2007090265A1 CA 2007000133 W CA2007000133 W CA 2007000133W WO 2007090265 A1 WO2007090265 A1 WO 2007090265A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat shrinkable
layer
covering according
laminated heat
propylene
Prior art date
Application number
PCT/CA2007/000133
Other languages
English (en)
Inventor
Peter Jackson
Dilip Tailor
Original Assignee
Shawcor
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shawcor filed Critical Shawcor
Priority to GB0813136A priority Critical patent/GB2448857B/en
Publication of WO2007090265A1 publication Critical patent/WO2007090265A1/fr

Abstract

La présente invention concerne un revêtement stratifié thermorétractable comprenant : a) au moins une couche thermorétractable comprenant un matériau polymérique réticulé ; b) une couche fonctionnelle ayant au moins une propriété supérieure à ladite couche thermorétractable, ladite ou lesdites propriétés étant choisies dans le groupe comprenant : la résistance à la pénétration à haute température, le point de ramollissement, la résistance aux chocs, la stabilité thermique à long terme, la résistance à la traction, la ténacité, la rigidité, l'isolation thermique, la conductivité électrique ou dissipation statique et l'imperméabilité aux gaz et à l'humidité ; et c) une couche adhésive.
PCT/CA2007/000133 2006-02-07 2007-01-31 Revetement stratifie thermoretractable WO2007090265A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB0813136A GB2448857B (en) 2006-02-07 2007-01-31 Heat shrinkable laminated covering

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CA2,535,503 2006-02-07
CA2535503A CA2535503C (fr) 2006-02-07 2006-02-07 Revetement stratifie thermoretractable

Publications (1)

Publication Number Publication Date
WO2007090265A1 true WO2007090265A1 (fr) 2007-08-16

Family

ID=38337901

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA2007/000133 WO2007090265A1 (fr) 2006-02-07 2007-01-31 Revetement stratifie thermoretractable

Country Status (3)

Country Link
CA (1) CA2535503C (fr)
GB (1) GB2448857B (fr)
WO (1) WO2007090265A1 (fr)

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2232124A1 (fr) * 2007-12-21 2010-09-29 ShawCor Ltd. Isolation en styrène pour tuyau
US7871697B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US7871696B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
CN102029755A (zh) * 2010-09-27 2011-04-27 沈阳防锈包装材料有限责任公司 一种阻燃可收缩防腐蚀包装膜及制造方法
US8389596B2 (en) 2010-02-26 2013-03-05 Kraft Foods Global Brands Llc Low-tack, UV-cured pressure sensitive adhesive suitable for reclosable packages
US8398306B2 (en) 2005-11-07 2013-03-19 Kraft Foods Global Brands Llc Flexible package with internal, resealable closure feature
CN103009746A (zh) * 2010-09-27 2013-04-03 沈阳防锈包装材料有限责任公司 一种阻燃可收缩防腐蚀包装膜及制造方法
CN101666415B (zh) * 2008-09-03 2013-05-15 日立空调·家用电器株式会社 真空绝热材料、冰箱及供热水器
US8763890B2 (en) 2010-02-26 2014-07-01 Intercontinental Great Brands Llc Package having an adhesive-based reclosable fastener and methods therefor
US20160257090A1 (en) * 2013-10-16 2016-09-08 Shawcor Ltd. Heat shrinkable multilayer sleeve
US9532584B2 (en) 2007-06-29 2017-01-03 Kraft Foods Group Brands Llc Processed cheese without emulsifying salts
US9533472B2 (en) 2011-01-03 2017-01-03 Intercontinental Great Brands Llc Peelable sealant containing thermoplastic composite blends for packaging applications
CN108670416A (zh) * 2018-05-08 2018-10-19 东莞市鸿德医用塑料制品有限公司 导液型易分解的手术单
US10669412B2 (en) 2016-09-09 2020-06-02 Leoni Kabel Gmbh Elongated article with good flexibility and high flame retardancy
CN111837200A (zh) * 2017-12-18 2020-10-27 博里利斯股份公司 具有优越电性能的用于电线电缆应用的聚合物组合物
US10920049B2 (en) 2016-09-09 2021-02-16 Leoni Kabel Gmbh Polymer composition with high flexibility and flame retardancy
US11248111B2 (en) 2016-09-09 2022-02-15 Leoni Kabel Gmbh Conjunction device such as a cable and polymer composition for preparing same
US11453764B2 (en) 2016-09-09 2022-09-27 Leoni Kabel Gmbh Strand-shaped elements and polymer composition for preparing same

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160039184A1 (en) * 2013-03-26 2016-02-11 Shawcor Ltd. Apparatus and polypropylene-based composition for wrapping a pipe weld
GB201318915D0 (en) 2013-10-25 2013-12-11 Wellstream Int Ltd Flexible pipe body and method of producing same

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1077667A (fr) * 1975-10-02 1980-05-20 Norman D. Bornstein Pellicule multicouche thermoretrecissable, et methode de fabrication connexe
JPH0298425A (ja) * 1988-10-04 1990-04-10 Fujikura Ltd 熱収縮チューブの製造方法
US5029241A (en) * 1989-03-03 1991-07-02 Rxs Schrumpftechnik-Garnituren Gmbh Heat-shrinkable repair cover for pressurized cables
US5035955A (en) * 1987-12-29 1991-07-30 Kureha Kagaku Kogyo Kabushiki Kaisha Heat-shrinkable laminated film
US5270390A (en) * 1990-08-22 1993-12-14 Kureha Kagaku Kogyo Kabushiki Kaisha Resin composition and heat shrinkable film comprising the same composition layer
US5593747A (en) * 1993-07-12 1997-01-14 Viskase Corporation Puncture resistant heat shrinkable film containing narrow molecular weight ethylene alpha olefin
US5635261A (en) * 1989-10-10 1997-06-03 Viskase Corporation Thermoplastic film incorporating high melt index resins
US20020068137A1 (en) * 2000-09-29 2002-06-06 Mario Paleari Heat-shrinkable multi-layer thermoplastic film and container obtained therefrom
EP0765219B1 (fr) * 1994-05-25 2004-04-07 Cryovac, Inc. Film contenant un copolymere aromatique alpha-olefine/vinyle
US6828011B2 (en) * 2001-07-24 2004-12-07 Cooper Technology Services, Llc Moisture crosslinkable thermoplastics in the manufacture of vehicle weather strips

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1077667A (fr) * 1975-10-02 1980-05-20 Norman D. Bornstein Pellicule multicouche thermoretrecissable, et methode de fabrication connexe
US5035955A (en) * 1987-12-29 1991-07-30 Kureha Kagaku Kogyo Kabushiki Kaisha Heat-shrinkable laminated film
JPH0298425A (ja) * 1988-10-04 1990-04-10 Fujikura Ltd 熱収縮チューブの製造方法
US5029241A (en) * 1989-03-03 1991-07-02 Rxs Schrumpftechnik-Garnituren Gmbh Heat-shrinkable repair cover for pressurized cables
US5635261A (en) * 1989-10-10 1997-06-03 Viskase Corporation Thermoplastic film incorporating high melt index resins
US5270390A (en) * 1990-08-22 1993-12-14 Kureha Kagaku Kogyo Kabushiki Kaisha Resin composition and heat shrinkable film comprising the same composition layer
US5593747A (en) * 1993-07-12 1997-01-14 Viskase Corporation Puncture resistant heat shrinkable film containing narrow molecular weight ethylene alpha olefin
EP0765219B1 (fr) * 1994-05-25 2004-04-07 Cryovac, Inc. Film contenant un copolymere aromatique alpha-olefine/vinyle
US20020068137A1 (en) * 2000-09-29 2002-06-06 Mario Paleari Heat-shrinkable multi-layer thermoplastic film and container obtained therefrom
US6828011B2 (en) * 2001-07-24 2004-12-07 Cooper Technology Services, Llc Moisture crosslinkable thermoplastics in the manufacture of vehicle weather strips

Cited By (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8398306B2 (en) 2005-11-07 2013-03-19 Kraft Foods Global Brands Llc Flexible package with internal, resealable closure feature
US7871697B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US7871696B2 (en) 2006-11-21 2011-01-18 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US8110286B2 (en) 2006-11-21 2012-02-07 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US9309027B2 (en) 2006-11-21 2016-04-12 Intercontinental Great Brands Llc Peelable composite thermoplastic sealants in packaging films
US8470397B2 (en) 2006-11-21 2013-06-25 Kraft Foods Global Brands Llc Peelable composite thermoplastic sealants in packaging films
US9532584B2 (en) 2007-06-29 2017-01-03 Kraft Foods Group Brands Llc Processed cheese without emulsifying salts
US8714206B2 (en) 2007-12-21 2014-05-06 Shawcor Ltd. Styrenic insulation for pipe
EP2232124A4 (fr) * 2007-12-21 2011-06-08 Shawcor Ltd Isolation en styrène pour tuyau
EP2232124A1 (fr) * 2007-12-21 2010-09-29 ShawCor Ltd. Isolation en styrène pour tuyau
AU2008340937B2 (en) * 2007-12-21 2013-10-10 2543500 Alberta Ltd. Styrenic insulation for pipe
CN101666415B (zh) * 2008-09-03 2013-05-15 日立空调·家用电器株式会社 真空绝热材料、冰箱及供热水器
US9096780B2 (en) 2010-02-26 2015-08-04 Intercontinental Great Brands Llc Reclosable fasteners, packages having reclosable fasteners, and methods for creating reclosable fasteners
US10287077B2 (en) 2010-02-26 2019-05-14 Intercontinental Great Brands Llc Low-tack, UV-cured pressure sensitive adhesive suitable for reclosable packages
US8389596B2 (en) 2010-02-26 2013-03-05 Kraft Foods Global Brands Llc Low-tack, UV-cured pressure sensitive adhesive suitable for reclosable packages
US9382461B2 (en) 2010-02-26 2016-07-05 Intercontinental Great Brands Llc Low-tack, UV-cured pressure sensitive adhesive suitable for reclosable packages
US8763890B2 (en) 2010-02-26 2014-07-01 Intercontinental Great Brands Llc Package having an adhesive-based reclosable fastener and methods therefor
CN103009746A (zh) * 2010-09-27 2013-04-03 沈阳防锈包装材料有限责任公司 一种阻燃可收缩防腐蚀包装膜及制造方法
CN102029755A (zh) * 2010-09-27 2011-04-27 沈阳防锈包装材料有限责任公司 一种阻燃可收缩防腐蚀包装膜及制造方法
US9533472B2 (en) 2011-01-03 2017-01-03 Intercontinental Great Brands Llc Peelable sealant containing thermoplastic composite blends for packaging applications
US20160257090A1 (en) * 2013-10-16 2016-09-08 Shawcor Ltd. Heat shrinkable multilayer sleeve
EP3058262A4 (fr) * 2013-10-16 2017-06-21 ShawCor Ltd. Manchon multicouche thermorétractable
US10920049B2 (en) 2016-09-09 2021-02-16 Leoni Kabel Gmbh Polymer composition with high flexibility and flame retardancy
US10669412B2 (en) 2016-09-09 2020-06-02 Leoni Kabel Gmbh Elongated article with good flexibility and high flame retardancy
US11248111B2 (en) 2016-09-09 2022-02-15 Leoni Kabel Gmbh Conjunction device such as a cable and polymer composition for preparing same
US11453764B2 (en) 2016-09-09 2022-09-27 Leoni Kabel Gmbh Strand-shaped elements and polymer composition for preparing same
CN111837200A (zh) * 2017-12-18 2020-10-27 博里利斯股份公司 具有优越电性能的用于电线电缆应用的聚合物组合物
CN111837200B (zh) * 2017-12-18 2024-03-05 博里利斯股份公司 具有优越电性能的用于电线电缆应用的聚合物组合物
CN108670416A (zh) * 2018-05-08 2018-10-19 东莞市鸿德医用塑料制品有限公司 导液型易分解的手术单
CN108670416B (zh) * 2018-05-08 2021-05-07 东莞市鸿德医用塑料制品有限公司 导液型易分解的手术单

Also Published As

Publication number Publication date
GB0813136D0 (en) 2008-08-27
GB2448857B (en) 2011-09-14
CA2535503C (fr) 2014-12-16
GB2448857A (en) 2008-11-05
CA2535503A1 (fr) 2007-08-07

Similar Documents

Publication Publication Date Title
CA2535503C (fr) Revetement stratifie thermoretractable
CA2527057C (fr) Compositions a base de polyolefines reticulees par rayonnement
CA2325217C (fr) Compositions de polypropylene thermoretrecissables reticulees
EP2226355B1 (fr) Compositions de polyoléfine réticulées par l'humidité
JP6309171B2 (ja) ケーブル廃棄物からリサイクルされたポリエチレンに基づく組成物
WO2014054409A1 (fr) Article multicouche thermorestaurable
CN111655782B (zh) 用于输送烃流体的热塑性硫化橡胶导管
KR101696122B1 (ko) 전도성 외피
CN109121462A (zh) 包含热塑性硫化橡胶组合物的光伏模块背板
CN107428993A (zh) 包括乙烯聚合物、单过氧化碳酸酯和氢过氧化叔烷基的可固化组合物
EP1328572B1 (fr) Compositions de polypropylene reticulees et thermoretractables
KR20210128934A (ko) 절연 조성물 및 이로부터 형성된 절연층을 갖는 전력 케이블
KR20160150607A (ko) 내한성이 우수한 비할로겐계 시스 조성물 및 이로부터 형성된 시스층을 포함하는 케이블
CN113166504B (zh) 用于挠性管的热塑性共混物和复合材料
KR101949643B1 (ko) 반도전성 조성물 및 이로부터 형성된 반도전층을 갖는 전력 케이블
CN109104881A (zh) 用于光伏电池应用的热塑性硫化橡胶组合物
KR20230140866A (ko) 연피 대체용 폴리프로필렌 조성물
JPH01123847A (ja) ポリ‐１‐ブテン樹脂組成物
JP2001253955A (ja) 止水シート

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
ENP Entry into the national phase

Ref document number: 0813136

Country of ref document: GB

Kind code of ref document: A

Free format text: PCT FILING DATE = 20070131

WWE Wipo information: entry into national phase

Ref document number: 0813136.9

Country of ref document: GB

Ref document number: 813136

Country of ref document: GB

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07719369

Country of ref document: EP

Kind code of ref document: A1