WO2007078655A2 - High speed tin plating process - Google Patents
High speed tin plating process Download PDFInfo
- Publication number
- WO2007078655A2 WO2007078655A2 PCT/US2006/047166 US2006047166W WO2007078655A2 WO 2007078655 A2 WO2007078655 A2 WO 2007078655A2 US 2006047166 W US2006047166 W US 2006047166W WO 2007078655 A2 WO2007078655 A2 WO 2007078655A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- alkyl
- tin
- plating solution
- solution
- Prior art date
Abstract
Description
Claims