WO2007074989A1 - Thick steel plate for welded structure having excellent strength and toughness in central region of thickness and small variation of properties through thickness and method of producing the same - Google Patents
Thick steel plate for welded structure having excellent strength and toughness in central region of thickness and small variation of properties through thickness and method of producing the same Download PDFInfo
- Publication number
- WO2007074989A1 WO2007074989A1 PCT/KR2006/005548 KR2006005548W WO2007074989A1 WO 2007074989 A1 WO2007074989 A1 WO 2007074989A1 KR 2006005548 W KR2006005548 W KR 2006005548W WO 2007074989 A1 WO2007074989 A1 WO 2007074989A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel plate
- less
- thickness
- steel
- central region
- Prior art date
Abstract
Description
Claims