WO2006117144A1 - Method for coating a substrate surface and coated product - Google Patents
Method for coating a substrate surface and coated product Download PDFInfo
- Publication number
- WO2006117144A1 WO2006117144A1 PCT/EP2006/003967 EP2006003967W WO2006117144A1 WO 2006117144 A1 WO2006117144 A1 WO 2006117144A1 EP 2006003967 W EP2006003967 W EP 2006003967W WO 2006117144 A1 WO2006117144 A1 WO 2006117144A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- powder
- alloys
- ppm
- less
- coating
- Prior art date
Abstract
Description
Claims