WO2006111156A1 - Noyaux de sels solubles dans l'eau - Google Patents
Noyaux de sels solubles dans l'eau Download PDFInfo
- Publication number
- WO2006111156A1 WO2006111156A1 PCT/DE2006/000706 DE2006000706W WO2006111156A1 WO 2006111156 A1 WO2006111156 A1 WO 2006111156A1 DE 2006000706 W DE2006000706 W DE 2006000706W WO 2006111156 A1 WO2006111156 A1 WO 2006111156A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- soluble salt
- salt cores
- mixture
- soluble
- Prior art date
Abstract
L'invention concerne des noyaux de sels solubles dans l'eau obtenus par compression de sels solubles dans l'eau, comme le NaCl ou le KCl, sous pression puis par traitement thermique consécutif. Ces noyaux de sels ont une fraction de 0,1 à 3 % de disulfure de molybdène (MoS<SUB>2</SUB>) en tant qu'agent de séparation.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102005018614.9 | 2005-04-21 | ||
DE102005018614.9A DE102005018614B4 (de) | 2005-04-21 | 2005-04-21 | Verfahren zur Herstellung von wasserlöslichen Salzkernen |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2006111156A1 true WO2006111156A1 (fr) | 2006-10-26 |
Family
ID=36917436
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/DE2006/000706 WO2006111156A1 (fr) | 2005-04-21 | 2006-04-21 | Noyaux de sels solubles dans l'eau |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE102005018614B4 (fr) |
WO (1) | WO2006111156A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2011054920A3 (fr) * | 2009-11-06 | 2011-10-13 | Emil Müller GmbH | Noyaux à base de sel, procédé de fabrication de ces noyaux et leur utilisation |
CN103347625A (zh) * | 2010-12-23 | 2013-10-09 | 圣让工业公司 | 通过等静压成型的部件实现连续铸造和锻造操作的盐芯的制造方法 |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102010038455A1 (de) | 2010-07-27 | 2012-02-02 | Federal-Mogul Nürnberg GmbH | Verfahren zur Herstellung von wasserlöslichen Salzkernen zur Ausbildung von Hohlformen in Gießverfahren |
DE102010044287A1 (de) | 2010-09-03 | 2012-03-08 | Daimler Ag | Verfahren zum Herstellen von Druckgussbauteilen |
EP2836318A2 (fr) * | 2012-04-10 | 2015-02-18 | Emil Müller GmbH | Noyaux à base de sel, procédé de fabrication de ces noyaux et leur utilisation |
DE102013007735B4 (de) | 2012-05-08 | 2015-10-15 | Audi Ag | Verfahren zum Herstellen eines gussgeeigneten Salzkerns |
CN110315023A (zh) * | 2019-06-21 | 2019-10-11 | 杨红 | 一种铸造用高强度水溶性复合盐芯的制备方法 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1483641A1 (de) * | 1965-06-12 | 1969-02-27 | Schmidt Gmbh Karl | Verfahren zum Eingiessen von Hohlraeumen |
DE1924991A1 (de) * | 1969-05-16 | 1970-11-19 | Schmidt Gmbh Karl | Kern fuer Giessereizwecke |
SU519268A1 (ru) * | 1975-03-14 | 1976-06-30 | Институт Механизации Металлополимерных Систем Ан Белорусской Сср | Смесь дл изготовлени водорастворимых литейных стержней |
DE10312782A1 (de) * | 2003-03-21 | 2004-10-07 | Emil Müller GmbH | Wasserlösliche Salzkerne und Verfahren zur Herstellung wasserlöslicher Salzkerne |
DE10359547B3 (de) * | 2003-12-17 | 2005-03-03 | Emil Müller GmbH | Wasserlösliche Salzkerne |
WO2005080022A2 (fr) * | 2004-02-19 | 2005-09-01 | Emil Müller GmbH | Noyaux de sel solubles dans l'eau pour coulee sous pression |
DE102004038288A1 (de) * | 2004-02-19 | 2005-09-08 | Müller, Emil | Wasserlösliche Salzkerne |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3001102C2 (de) * | 1980-01-14 | 1982-09-23 | Stefan 6057 Dietzenbach Graichen | Festschmierstoff |
JPH069730B2 (ja) * | 1989-01-13 | 1994-02-09 | 花野商事株式会社 | ダイカスト用粉末離型剤 |
DD296862B5 (de) * | 1989-02-06 | 1994-09-29 | Dresden Ev Inst Festkoerper | Verfahren zur Herstellung von Halbzeug, insbesondere von Metallbaendern durch Schnellerstarrung |
-
2005
- 2005-04-21 DE DE102005018614.9A patent/DE102005018614B4/de not_active Expired - Fee Related
-
2006
- 2006-04-21 WO PCT/DE2006/000706 patent/WO2006111156A1/fr active Application Filing
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1483641A1 (de) * | 1965-06-12 | 1969-02-27 | Schmidt Gmbh Karl | Verfahren zum Eingiessen von Hohlraeumen |
DE1924991A1 (de) * | 1969-05-16 | 1970-11-19 | Schmidt Gmbh Karl | Kern fuer Giessereizwecke |
SU519268A1 (ru) * | 1975-03-14 | 1976-06-30 | Институт Механизации Металлополимерных Систем Ан Белорусской Сср | Смесь дл изготовлени водорастворимых литейных стержней |
DE10312782A1 (de) * | 2003-03-21 | 2004-10-07 | Emil Müller GmbH | Wasserlösliche Salzkerne und Verfahren zur Herstellung wasserlöslicher Salzkerne |
DE10359547B3 (de) * | 2003-12-17 | 2005-03-03 | Emil Müller GmbH | Wasserlösliche Salzkerne |
WO2005080022A2 (fr) * | 2004-02-19 | 2005-09-01 | Emil Müller GmbH | Noyaux de sel solubles dans l'eau pour coulee sous pression |
DE102004038288A1 (de) * | 2004-02-19 | 2005-09-08 | Müller, Emil | Wasserlösliche Salzkerne |
Non-Patent Citations (1)
Title |
---|
DATABASE WPI Section Ch Week 197722, Derwent World Patents Index; Class M22, AN 1977-39366Y, XP002397274 * |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2011054920A3 (fr) * | 2009-11-06 | 2011-10-13 | Emil Müller GmbH | Noyaux à base de sel, procédé de fabrication de ces noyaux et leur utilisation |
CN102695572A (zh) * | 2009-11-06 | 2012-09-26 | 埃米尔·米勒有限责任公司 | 盐基型芯、其制造方法和用途 |
CN103347625A (zh) * | 2010-12-23 | 2013-10-09 | 圣让工业公司 | 通过等静压成型的部件实现连续铸造和锻造操作的盐芯的制造方法 |
Also Published As
Publication number | Publication date |
---|---|
DE102005018614B4 (de) | 2016-07-28 |
DE102005018614A1 (de) | 2006-10-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2006111156A1 (fr) | Noyaux de sels solubles dans l'eau | |
EP1978120B1 (fr) | Alliage de fonte, d'aluminium et de silice et son procédé de fabrication | |
DE102016002689A1 (de) | Aluminium-Gusslegierung mit geringen Kosten und hoher Zähigkeit | |
EP1691942B1 (fr) | Noyaux de sel solubles dans l'eau | |
EP2734321B1 (fr) | Masselottes et compositions façonnables pour la fabrication desdites masselottes | |
DE202006006518U1 (de) | Aluminiumgusslegierung | |
DE102016219711B4 (de) | Aluminiumlegierung zum Druckgießen und Verfahren zu ihrer Hitzebehandlung | |
EP2155920A1 (fr) | Utilisation d'un alliage al-mn pour obtenir des produits résistants aux hautes températures | |
WO2009086998A1 (fr) | Mélange aqueux accélérateur | |
DE102009016111B4 (de) | Druckgusskörper aus einer übereutektischen Aluminium-Silizium-Gusslegierung und Verfahren zu dessen Herstellung | |
DE102013006135A1 (de) | Kerne auf der Basis von Salz, Verfahren zu ihrer Herstellung und deren Verwendung | |
WO2020207708A1 (fr) | Alliage d'aluminium pour coulée sous pression | |
EP1715970A2 (fr) | Noyaux de sel solubles dans l'eau pour coulee sous pression | |
WO2006058664A2 (fr) | Utilisation de sels peu solubles combines a du verre soluble pour fabriquer des moules et des noyaux pour des applications en fonderie | |
DE102018118291A1 (de) | Schlichtezusammensetzung zur Reduzierung von Formaldehyd-Emissionen | |
DE102014114594A1 (de) | Hochelastische Aluminiumlegierung aufweisend Titanverbindung und Verfahren zum Herstellen davon | |
DE112012004397T5 (de) | Giesskern, Verfahren zu seiner Herstellung, und Giessverfahren unter Verwendung des Kerns | |
DE10104289B4 (de) | Formbare exotherme Zusammensetzungen und Speiser daraus | |
DE102014217823A1 (de) | Hochelastische übereutektische Aluminiumlegierung und Verfahren zu deren Herstellung | |
WO2006008311A1 (fr) | Corps de separation ou de meulage a liaison organique comportant un additif fonctionnel | |
WO2004082866A2 (fr) | Noyaux de sels hydrosolubles et procede de production desdits noyaux | |
DE102004038288A1 (de) | Wasserlösliche Salzkerne | |
DE102014221432B4 (de) | Hochelastische Aluminiumlegierung und Verfahren zu ihrer Herstellung | |
EP3548448A1 (fr) | Procédé pour produire un corps moulé réfractaire à liaison carbone, et corps moulé réfractaire | |
DE102004028902B4 (de) | Bremsscheibe |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
NENP | Non-entry into the national phase |
Ref country code: RU |
|
WWW | Wipo information: withdrawn in national office |
Country of ref document: RU |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 06722824 Country of ref document: EP Kind code of ref document: A1 |