WO2004011271A1 - Ink-jet printed rigid interlayer and a process for preparing same - Google Patents

Ink-jet printed rigid interlayer and a process for preparing same Download PDF

Info

Publication number
WO2004011271A1
WO2004011271A1 PCT/US2003/024116 US0324116W WO2004011271A1 WO 2004011271 A1 WO2004011271 A1 WO 2004011271A1 US 0324116 W US0324116 W US 0324116W WO 2004011271 A1 WO2004011271 A1 WO 2004011271A1
Authority
WO
WIPO (PCT)
Prior art keywords
interlayer
image
sheet
bearing
rigid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2003/024116
Other languages
English (en)
French (fr)
Inventor
Rebecca L. Smith
Hamdy Elwakil
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EI Du Pont de Nemours and Co filed Critical EI Du Pont de Nemours and Co
Priority to AU2003257995A priority Critical patent/AU2003257995B2/en
Priority to MXPA05001118A priority patent/MXPA05001118A/es
Priority to CA002494057A priority patent/CA2494057A1/en
Priority to DE60312338T priority patent/DE60312338T2/de
Priority to JP2004524278A priority patent/JP2005534527A/ja
Priority to US10/519,655 priority patent/US7232213B2/en
Priority to EP03772174A priority patent/EP1525099B1/en
Publication of WO2004011271A1 publication Critical patent/WO2004011271A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10559—Shape of the cross-section
    • B32B17/10577—Surface roughness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10165—Functional features of the laminated safety glass or glazing
    • B32B17/10247—Laminated safety glass or glazing containing decorations or patterns for aesthetic reasons
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10743—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing acrylate (co)polymers or salts thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10761—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing vinyl acetal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
    • B41J—TYPEWRITERS; SELECTIVE PRINTING MECHANISMS, i.e. MECHANISMS PRINTING OTHERWISE THAN FROM A FORME; CORRECTION OF TYPOGRAPHICAL ERRORS
    • B41J11/00—Devices or arrangements  of selective printing mechanisms, e.g. ink-jet printers or thermal printers, for supporting or handling copy material in sheet or web form
    • B41J11/0015—Devices or arrangements  of selective printing mechanisms, e.g. ink-jet printers or thermal printers, for supporting or handling copy material in sheet or web form for treating before, during or after printing or for uniform coating or laminating the copy material before or after printing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
    • B41J—TYPEWRITERS; SELECTIVE PRINTING MECHANISMS, i.e. MECHANISMS PRINTING OTHERWISE THAN FROM A FORME; CORRECTION OF TYPOGRAPHICAL ERRORS
    • B41J3/00—Typewriters or selective printing or marking mechanisms characterised by the purpose for which they are constructed
    • B41J3/407—Typewriters or selective printing or marking mechanisms characterised by the purpose for which they are constructed for marking on special material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
    • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
    • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
    • B41M5/0041—Digital printing on surfaces other than ordinary paper
    • B41M5/0047—Digital printing on surfaces other than ordinary paper by ink-jet printing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
    • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
    • B41M5/00—Duplicating or marking methods; Sheet materials for use therein
    • B41M5/0041—Digital printing on surfaces other than ordinary paper
    • B41M5/0064—Digital printing on surfaces other than ordinary paper on plastics, horn, rubber, or other organic polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B44—DECORATIVE ARTS
    • B44F—SPECIAL DESIGNS OR PICTURES
    • B44F1/00—Designs or pictures characterised by special or unusual light effects
    • B44F1/06—Designs or pictures characterised by special or unusual light effects produced by transmitted light, e.g. transparencies, imitations of glass paintings
    • B44F1/066—Designs or pictures characterised by special or unusual light effects produced by transmitted light, e.g. transparencies, imitations of glass paintings comprising at least two transparent elements, e.g. sheets, layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
    • B41M—PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING
    • B41M7/00—After-treatment of prints, e.g. heating, irradiating, setting of the ink, protection of the printed stock
    • B41M7/0027—After-treatment of prints, e.g. heating, irradiating, setting of the ink, protection of the printed stock using protective coatings or layers by lamination or by fusion of the coatings or layers

Definitions

  • Laminated safety glass consists of two lites of glass joined by an energy absorbing plastic interlayer, typically polyvinylbutyral (PVB).
  • PVB polyvinylbutyral
  • Laminated safety glass is used in automotive windshields and in architectural building glass. Architects are continually using glass in more demanding applications such as balustrades, partitions, floors, doors, and overhead bolted glass.
  • Laminated safety glass using plasticized PVB as the interlayer typically does not meet the strength or post glass breakage requirements for these applications, lonomers of ethylene/methyacryiic acid copolymers (sold under the DuPont tradename Surlyn®) yield interlayer materials that are rigid, much stiffer and tougher than traditional PVB interlayers.
  • Laminated safety glass utilizing stiffer, tougher interlayer has been shown to possess the strength and post glass breakage requirements needed for these demanding architectural applications.
  • interlayers of ionomeric ethylene/methyacryiic acid copolymers demonstrate much improved edge stability over traditional PVB interlayers.
  • This improved edge stability allows for laminated glass (with interlayers of ionomeric ethylene/methyacryiic acid copolymers) to be used in applications such as shower doors and exterior open edge applications where traditional laminated glass (with PVB interlayers) would not be used.
  • traditional laminated glass with PVB interlayers
  • PVB interlayers have a roughened surface pattern (Rz from 30-60 Dm), which is present to allow for air to escape during the lamination process as described in US 5455103.
  • the rough surface pattern can effect image quality with respect to mottle and resolution.
  • polyvinyl butyral is a viscoelastic polymer, which can lead to poor dimensional stability in the image-bearing interlayer.
  • Interlayers obtained from an ionomer of an ethylene/methyacryiic acid copolymer are stiff relative to other conventional interlayers, and can have improved dimensional stability relative to PVB, for example.
  • the present invention is a process for ink-jet printing an image onto a rigid thermoplastic interlayer comprising the step: feeding a rigid interlayer sheet through an ink jet printer and ink-jet printing an image on the sheet, wherein the interlayer has a Storage Young's Modulus of 50-1 ,000 MPa (mega Pascals) at 0.3 Hz and 25°C, as determined according to ASTM D 5026-95a, and wherein the rigid interlayer sheet has a finite thickness of less than or equal to about 0.38 mm.
  • the present invention is thermoplastic interlayer sheet bearing an image on at least one surface of the interlayer sheet, the image being printed on the sheet by a process comprising the step: feeding a rigid interlayer sheet through an ink jet printer and ink-jet printing an image on the sheet, wherein the interlayer has a Storage Young's Modulus of 50-1 ,000 MPa (mega Pascals) at 0.3 Hz and 25°C, as determined according to ASTM D 5026-95a, and wherein the rigid interlayer sheet has a finite thickness of less than or equal to about 0.38 mm.
  • the present invention is a decorative glass laminate comprising at least two sheets of glass having disposed therebetween a rigid image-bearing interlayer sheet wherein the image bearing interlayer was obtained by a process comprising the steps of: (1) "ink jet" printing pigmented ink onto at least one surface of an interlayer sheet which is a rigid ethylene/methyacryiic acid copolymer ionomer having a thickness of less than or equal to about 0.38 mm and wherein the interlayer has a Storage Young's Modulus of 50-1 ,000 MPa (mega Pascals) at 0.3 Hz and 25°C, as determined according to ASTM D 5026-95a, to obtain an image-bearing interlayer sheet; and (2) laminating the image-bearing interlayer sheet between sheets of transparent materials to obtain a decorative laminate.
  • "ink jet" printing pigmented ink onto at least one surface of an interlayer sheet which is a rigid ethylene/methyacryiic acid copolymer ionomer having
  • this invention is a method for printing a decorative image on a rigid interlayer.
  • a rigid interlayer suitable for use in the practice of the present invention preferably has a Storage Young's Modulus of 50-1 ,000 MPa (mega Pascals) at 0.3 Hz and 25°C, as determined according to ASTM D 5026-95a.
  • Conventional interlayer materials such as conventionally plasticized PVB, do not typically have a modulus in this range.
  • Other conventional interlayer materials can be suitable as a substrate for ink-jet printing, but there are advantages in using a rigid interlayer material.
  • Rigid, stiff Interlayers such as those based upon ionomeric ethylene/methyacryiic acid copolymers, facilitate using a much smoother surface pattern to obtain acceptable deairing during lamination since the surface pattern does not break down as rapidly with a rigid interlayer.
  • a desirable range of Rz for laminating conventionally plasticized (flexible) PVB is 30-60 ⁇ m while an acceptable range of Rz for stiff interlayers is from 5 to 15 ⁇ m.
  • the smooth surface pattern for the ionomeric interlayer yields printed images with higher resolution and less mottle than images printed directly on PVB.
  • the higher modulus of a rigid interlayer relative to other conventional flexible interlayer materials, such as flexible PVB, can yield an interlayer that has improved dimensional stability versus more flexible materials.
  • the improved dimensional stability can improve the image stability of the image-bearing product, and make the entire process more reliable and reproducible with respect to elongation or shrinkage of the image.
  • Printing on a rigid interlayer to obtain an image-bearing rigid with either can be accomplished using either an aqueous or solvent based ink and by using ink jet printing technology and laminating the image bearing rigid interlayer between two lites of glass or other transparent materials. Laminates obtained in this manner have acceptable adhesion for safety glass applications.
  • the image is printed onto the interlayer using an inkjet printer equipped with a piezoelectric drop on demand printhead such as Spectra or Xaar and the inkjet printer is chosen so that the rigid interlayer is held on a bed type support.
  • the interlayer can be any clear, transparent rigid thermoplastic material that can be adhesively bonded to glass.
  • the interlayer for example, can be a PVB sheet having less than 30 parts of plasticizer, or an ionomeric interlayer.
  • the interlayer is preferably an ionomer of an ethylene/(meth)acrylic acid copolymer where the surface roughness (Rz) of the sheet is between 5 and 15 ⁇ m and the total thickness of the interlayer is between 0.38 - 2.29 mm.
  • ethylene/(meth)acrylic acid as used herein is a shorthand term that denotes a copolymer that comprises either ethylene and acrylic acid units or ethylene and methacrylic acid units, lonomers are known conventionally as partially neutralized ethylene/(meth)acrylic acid copolymers.
  • a suitable interlayer for printing according to the practice of the present invention can be obtained from an ethylene/acrylic acid copolymer ionomer, such as those commercially available from E.I DuPont de Nemours and Company, for example.
  • the present invention is a composite image-bearing interlayer which can be obtained by a process comprising the step of feeding a thin substrate film having Storage Young's Modulus of 50 -1 ,000 MPa at 0.3 Hz and 25°C, as determined according to ASTM D 5026-95a, and having a finite thickness less than or equal to about 0.38 mm, through a conventional inkjet printer and ink-jet printing an image onto the surface of the substrate film, and then laminating the image- bearing thin film with a second sheet of a thermoplastic interlayer material.
  • the composite printed interlayer preferably has a thickness of from about 0.40 to about 2.29 mm. The thickness of the other sheets can vary, but should be at least 0.025 mm thick.
  • the other sheets can be blank, bear printed images or colors, can be transparent, semi-transparent, opaque or can otherwise be visually distinct from the printing substrate.
  • the thin printing substrate can be laminated with a thicker (>0.76 mm) film or sheet of, for example, an ionomer of an ethylene/methylacrylic acid copolymer to achieve the desired structural properties in the finished laminate.
  • Lamination of the image-bearing interlayer sheet with a thicker polymer sheet yields a product having an image imprinted on the interlayer and also having the properties of a thicker interlayer.
  • the other sheet can be any thermoplastic interlayer material that can be adhesively bonded to the printed ionomer film.
  • the thicker film can be: an ethylene copolymer and/or terpolymer such as ethylene/acrylic acid or ethylene/alkyl acrylate copolymers and ethylene/acrylic acid/alkyl acrylate terpolymers; a polyacetal; a polyvinylbutyral; a polyurethane; a polyvinyl chloride; or, a polyester.
  • the thin printing substrate film has a thickness in the range of from about 0.025 mm to about 0.45 mm. More preferably, the thickness of the printing substrate is from about 0.1 mm to about 0.40 mm.
  • the thickness of the printing substrate is from about 0.25 mm to about 0.38 mm.
  • the thicker film sheet preferably has a thickness which is complimentary to the thickness of the thin film such that the total thickness of the interlayer sheets is in the range of from about 0.38 mm to about 2.29 mm. More preferably, the total thickness is in the range of from about 0.60 mm to about 1.75 mm. Most preferably, the total thickness of the interlayer is from about 1.14 mm to about 1.52 mm.
  • Laminates of the present invention can be used in any application wherein conventional (that is, non-decorative) laminated glass is used.
  • the laminates of the present invention can be used as decorative articles such as picture windows, decorative countertops, graphic art, image-bearing store-front windows, displays bearing company logos, advertising media, and/or any other use wherein a transparent laminate bearing an image can be desirable.
  • Preferable inks for use in the practice of the present invention are those that provide printed images having a satisfactory combination of image quality, light fastness, and weatherability.
  • laminates that incorporate image-bearing interlayers of the present invention should have the adhesion properties that are acceptable in the various applications in which they will be used.
  • Printing heads useful for piezo electric processes are available from, for example, Epson, Seiko-Epson, Spectra, XAAR and XAAR- Hitachi.
  • Printing heads useful for thermal inkjet printing are available from, for example, Hewlett-Packard and Canon.
  • Printing heads suitable for continuous drop printing are available from Iris and Video Jet, for example.
  • a binder resin is optionally included in an ink system suitable for use in the practice of the present invention.
  • a binder resin can be preferable to improve adhesion between the ink and the laminate substrate.
  • Suitable binders for use in the practice of the present invention can include polyvinyl pyrilidone/vinyl acetate (PVP/VA), polyvinyl pyrilidone (PVP), and PUR, for example. Mixtures of binder resins can also be useful in the practice of the present invention. Other binders are conventionally known and can be useful herein.
  • the dimensional stability test involves printing an image of known size onto the substrate of interest. The size of the printed image exit the printer is compared to that of the digital input.
  • Example - An image of 100 mm x 100 mm in size was printed onto a 0.38 mm thick interlayer of an ionomeric copolymer of ethylene/methacrylic acid. Immediately after printing at ambient conditions, the image was determined to be exactly 100 mm x 100 mm. After the image was allowed to dry at 60°C for 30 minutes, the image size was 100 mm x 100 mm. The shrinkage for the ionomeric copolymer of ethylene/methacrylic acid was determined to be 0%.
  • Comparative Example - An image of 300 mm x 300 mm size was printed onto 0.76 mm PVB. Immediately after printing at ambient conditions, the image was determined to be 302 mm x 298 mm. After the image was allowed to dry at 60°C for 30 minutes, the image size was determined to be 304 mm x 294 mm. The shrinkage for 0.76 mm PVB was determined to be 2%.
  • An image was printed onto the surface of each of the subject interlayers in the following examples via an ink-jet printer.
  • the interlayers Prior to lamination of the image-bearing interlayers, the interlayers were dried to less than 0.2% H 2 O using a 75°C oven for a minimum of 16 hours.
  • a layer of 15 mil blank (non-image-bearing) interlayer was placed on the image- bearing surface.
  • the multi-layered structure was deaired (by either a vacuum bag or nip roll process) and autoclaved using standard lamination conditions.
  • Example 1 A solid yellow color block was printed onto the surface of a 0.38 mm thick interlayer of an ionomer of ethylene/methylacrylic acid copolymer using an Epson 3000 printer. The ink used is described in the table below. The printed interlayer was laminated as described above.
  • Example 2 A solid yellow color block was printed and laminated as described in Example 1. The ink used is described in the table below.
  • Example 3 A solid yellow color block was printed and laminated as described in Example 1. The ink used is described in the table below.
  • Example 4 A solid yellow color block was printed and laminated as described in Example 1. The ink used is described in the table below.
  • Example 5 A solid yellow color block was printed and laminated as described in Example 1. The ink used is described in the table below.
  • Example 6 A solid yellow color block was printed and laminated as described in Example 1. The ink used is described in the table below.

Landscapes

  • Laminated Bodies (AREA)
  • Ink Jet Recording Methods And Recording Media Thereof (AREA)
  • Ink Jet (AREA)
PCT/US2003/024116 2002-07-31 2003-07-31 Ink-jet printed rigid interlayer and a process for preparing same Ceased WO2004011271A1 (en)

Priority Applications (7)

Application Number Priority Date Filing Date Title
AU2003257995A AU2003257995B2 (en) 2002-07-31 2003-07-31 Ink-jet printed rigid interlayer and a process for preparing same
MXPA05001118A MXPA05001118A (es) 2002-07-31 2003-07-31 Capa intermedia rigida impresa por inyeccion de tinta y procedimiento para su preparacion.
CA002494057A CA2494057A1 (en) 2002-07-31 2003-07-31 Ink-jet printed rigid interlayer and a process for preparing same
DE60312338T DE60312338T2 (de) 2002-07-31 2003-07-31 Steife tintenstrahlbedruckte zwischenschicht und verfahren zur deren herstellung
JP2004524278A JP2005534527A (ja) 2002-07-31 2003-07-31 インクジェット印刷された硬質中間層およびその製造方法
US10/519,655 US7232213B2 (en) 2002-07-31 2003-07-31 Ink-jet printed rigid interlayer and a process for preparing same
EP03772174A EP1525099B1 (en) 2002-07-31 2003-07-31 Ink-jet printed rigid interlayer and a process for preparing same

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US40023202P 2002-07-31 2002-07-31
US60/400,232 2002-07-31

Publications (1)

Publication Number Publication Date
WO2004011271A1 true WO2004011271A1 (en) 2004-02-05

Family

ID=31188669

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2003/024116 Ceased WO2004011271A1 (en) 2002-07-31 2003-07-31 Ink-jet printed rigid interlayer and a process for preparing same

Country Status (9)

Country Link
US (1) US7232213B2 (enExample)
EP (1) EP1525099B1 (enExample)
JP (1) JP2005534527A (enExample)
CN (1) CN100379578C (enExample)
AU (1) AU2003257995B2 (enExample)
CA (1) CA2494057A1 (enExample)
DE (1) DE60312338T2 (enExample)
MX (1) MXPA05001118A (enExample)
WO (1) WO2004011271A1 (enExample)

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005014280A1 (en) * 2003-08-07 2005-02-17 E.I. Dupont De Nemours And Company Decorative laminated safety glass utilizing a rigid interlayer and a process for preparing same
WO2005085371A1 (en) * 2004-03-02 2005-09-15 E.I. Dupont De Nemours And Company Decorative laminated safety glass
WO2007079091A1 (en) * 2005-12-30 2007-07-12 E. I. Du Pont De Nemours And Company Multilayer polymeric laminates and high strength laminates produced therefrom
WO2008115567A1 (en) * 2007-03-19 2008-09-25 E. I. Du Pont De Nemours And Company High contrast high strength decorative sheets and laminates
US7625627B2 (en) 2005-12-30 2009-12-01 E.I. Du Pont De Nemours And Company Decorative polyvinyl butyral solar control laminates
GB2469094A (en) * 2009-04-01 2010-10-06 Jeremy Town Decorative panel
US8002938B2 (en) 2002-08-20 2011-08-23 E. I. Du Pont De Nemours And Company Decorative laminated safety glass
WO2012028820A1 (fr) 2010-09-02 2012-03-08 Saint-Gobain Glass France Vitrage feuilleté éclairant a diodes electroluminescentes et sa fabrication
WO2013138352A1 (en) 2012-03-15 2013-09-19 Synergy Pharmaceuticals Inc. Formulations of guanylate cyclase c agonists and methods of use
WO2014131024A2 (en) 2013-02-25 2014-08-28 Synergy Pharmaceuticals Inc. Agonists of guanylate cyclase and their uses
WO2014151200A2 (en) 2013-03-15 2014-09-25 Synergy Pharmaceuticals Inc. Compositions useful for the treatment of gastrointestinal disorders
WO2014151206A1 (en) 2013-03-15 2014-09-25 Synergy Pharmaceuticals Inc. Agonists of guanylate cyclase and their uses
EP2810951A2 (en) 2008-06-04 2014-12-10 Synergy Pharmaceuticals Inc. Agonists of guanylate cyclase useful for the treatment of gastrointestinal disorders, inflammation, cancer and other disorders
US11396160B2 (en) 2017-08-25 2022-07-26 Kuraray Europe Gmbh Laminated glass comprising interlayer film layers with a pigmented frame
US20230182449A1 (en) * 2021-12-10 2023-06-15 Chang Chun Petrochemical Co., Ltd. Polymer film
WO2024162476A1 (ja) 2023-02-02 2024-08-08 積水化学工業株式会社 画像担持積層体、その製造方法、合わせガラス用中間膜、及び合わせガラス
WO2024247770A1 (ja) 2023-05-29 2024-12-05 積水化学工業株式会社 画像担持積層体、その製造方法、合わせガラス用中間膜、及び合わせガラス

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070172636A1 (en) * 2005-12-30 2007-07-26 Smith Rebecca L Decorative sheets having enhanced adhesion and laminates prepared therefrom
GB0600022D0 (en) * 2006-01-03 2006-02-08 Pilkington Plc Glazings
US20080206504A1 (en) * 2007-02-28 2008-08-28 Richard Allen Hayes Decorative Safety Glass
US20080233371A1 (en) * 2007-03-19 2008-09-25 Richard Allen Hayes Decorative safety glass
US20080280076A1 (en) * 2007-05-11 2008-11-13 Richard Allen Hayes Decorative safety glass
FR2962363B1 (fr) * 2010-07-07 2013-01-04 Saint Gobain Structure feuilletee pour la visualisation d'informations
FR2969957B1 (fr) * 2010-12-29 2013-01-04 Saint Gobain Procede de fabrication d'un vitrage feuillete imprime par serigraphie a l'aide d'un ecran de serigraphie double tissage
DE102011004500A1 (de) * 2011-02-22 2012-08-23 Bayerische Motoren Werke Aktiengesellschaft Verfahren zur Herstellung einer bedruckten Fahrzeug-Verbundscheibe
EP3466676B1 (en) 2013-12-06 2020-08-05 Corning Incorporated Methods for forming patterns in thin glass laminate structures
US10780674B2 (en) 2015-02-19 2020-09-22 Agp America S.A. Obscuration having superior strength and optical quality for an automotive laminate
US9623634B2 (en) 2015-02-19 2017-04-18 Agp America S.A. Obscuration having superior strength and optical quality for a laminated automotive windshield
US10710340B2 (en) 2015-02-19 2020-07-14 Agp America S.A. Obscuration having superior strength and optical quality for an automotive laminate
CO2017008445A1 (es) 2016-12-29 2018-01-31 Agp America Sa Oscurecimiento con resistencia y calidad óptica superiores para un laminado para automotores
EP3625051A1 (en) 2017-05-15 2020-03-25 Corning Incorporated Laminate having organic ink decoration and high impact resistance
KR20210123347A (ko) 2019-02-04 2021-10-13 쿠라라이 유럽 게엠베하 허리케인 저항성 음향 글레이징
US20230382087A1 (en) 2020-09-28 2023-11-30 Kuraray Europe Gmbh Glass laminates with reduced creep at elevated temperature
WO2025244985A1 (en) 2024-05-23 2025-11-27 Dow Global Technologies Llc Polyolefin elastomer and its use in laminates with improved vibration dampening

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4868581A (en) * 1985-12-20 1989-09-19 Cannon Kabushiki Kaisha Ink-receiving composite polymer material
JP2000355163A (ja) * 1999-04-16 2000-12-26 Konica Corp インクジェット記録シート及びその製造方法
EP1114734A1 (en) * 1999-06-04 2001-07-11 DAICEL CHEMICAL INDUSTRIES, Ltd. Resin composition for ink-jet recording sheet and recording sheet made with the same

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4303718A (en) * 1980-06-09 1981-12-01 Monsanto Company Printing ink formulations
EP0254187A3 (de) 1986-07-21 1989-07-26 Siemens Aktiengesellschaft Pigmentierter Lack für Schreibsysteme
US4968553A (en) * 1988-09-16 1990-11-06 Claudio Cesar Graphic architectural glass
FR2706446B1 (fr) * 1993-06-18 1995-08-25 Saint Gobain Vitrage Int Vitrage feuilleté comportant un motif apparent.
US5455103A (en) * 1994-01-24 1995-10-03 Monsanto Company Rough-surfaced interlayer
US6013330A (en) * 1997-02-27 2000-01-11 Acushnet Company Process of forming a print
US6500495B2 (en) * 1997-02-27 2002-12-31 Acushnet Company Method for curing reactive ink on game balls
US6248804B1 (en) * 1997-02-27 2001-06-19 Acushnet Company Ultraviolet and or/ visible light curable inks with photoinitiators for game balls, golf balls and the like
DE29706880U1 (de) 1997-04-16 1997-05-28 Vegla Vereinigte Glaswerke Gmbh, 52066 Aachen Dekoratives Verbundglas
AU3899699A (en) 1998-05-14 1999-11-29 Performance Materials Na, Inc. Glass laminates for threat resistant window systems
US6432519B1 (en) * 1999-04-16 2002-08-13 Konica Corporation Ink jet recording sheet
DE20100717U1 (de) 2000-02-18 2001-04-05 Glas Engels Gmbh Verbundkörper aus einer mehrschichtigen Anordnung
EP1129844A1 (en) 2000-02-29 2001-09-05 Brevet 2000 Holding S.A. Composite stratified decorated panel from glass and/or transparent plastics
WO2001078981A1 (en) * 2000-04-14 2001-10-25 E.I. Dupont De Nemours And Company Multilayer, co-extruded, ionomeric decorative surfacing
DE10032683A1 (de) * 2000-07-05 2002-01-17 Clariant Gmbh Farbmittelmischung
CN1473114A (zh) * 2000-09-01 2004-02-04 数字玻璃股份有限公司 带图象的层压材料
US20030124296A1 (en) * 2000-10-26 2003-07-03 Smith Charles Anthony Glass laminates for threat resistant window systems
US20030049415A1 (en) * 2001-03-12 2003-03-13 Pedginski James J. Film constructions and methods
WO2004011538A2 (en) * 2002-07-31 2004-02-05 E.I. Du Pont De Nemours And Company Polyvinylbutyral interlayer sheet with improved adhesion to glass and a process for preparing same
US7041163B2 (en) * 2003-03-28 2006-05-09 E.I. Du Pont De Nemours And Company Non-aqueous inkjet ink set
US20070087137A9 (en) * 2003-06-26 2007-04-19 Elwakil Hamdy A Decorative laminated safety glass
US20070071955A9 (en) * 2002-08-20 2007-03-29 Elwakil Hamdy A Decorative laminated safety glass
US7122077B2 (en) * 2003-03-28 2006-10-17 E. I. Du Pont De Nemours And Company Inkjet ink set and method of using same
CN1842414A (zh) 2003-08-07 2006-10-04 纳幕尔杜邦公司 利用硬质夹层的装饰层压安全玻璃及其制备方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4868581A (en) * 1985-12-20 1989-09-19 Cannon Kabushiki Kaisha Ink-receiving composite polymer material
JP2000355163A (ja) * 1999-04-16 2000-12-26 Konica Corp インクジェット記録シート及びその製造方法
EP1114734A1 (en) * 1999-06-04 2001-07-11 DAICEL CHEMICAL INDUSTRIES, Ltd. Resin composition for ink-jet recording sheet and recording sheet made with the same

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 2000, no. 15 6 April 2001 (2001-04-06) *

Cited By (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9011628B2 (en) 2002-08-20 2015-04-21 Kuraray America Inc. Decorative laminated safety glass
US8002938B2 (en) 2002-08-20 2011-08-23 E. I. Du Pont De Nemours And Company Decorative laminated safety glass
WO2005014280A1 (en) * 2003-08-07 2005-02-17 E.I. Dupont De Nemours And Company Decorative laminated safety glass utilizing a rigid interlayer and a process for preparing same
JP2007526389A (ja) * 2004-03-02 2007-09-13 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー 装飾性積層安全ガラス
US7278730B2 (en) 2004-03-02 2007-10-09 E. I. Du Pont De Nemours And Company Decorative laminated safety glass
AU2005219867B2 (en) * 2004-03-02 2009-10-08 Kuraray America, Inc. Decorative laminated safety glass
CN1926205B (zh) * 2004-03-02 2013-08-28 纳幕尔杜邦公司 装饰性层压安全玻璃
JP4852031B2 (ja) * 2004-03-02 2012-01-11 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー 装飾性積層安全ガラス
WO2005085371A1 (en) * 2004-03-02 2005-09-15 E.I. Dupont De Nemours And Company Decorative laminated safety glass
US7625627B2 (en) 2005-12-30 2009-12-01 E.I. Du Pont De Nemours And Company Decorative polyvinyl butyral solar control laminates
WO2007079091A1 (en) * 2005-12-30 2007-07-12 E. I. Du Pont De Nemours And Company Multilayer polymeric laminates and high strength laminates produced therefrom
US8101267B2 (en) 2005-12-30 2012-01-24 E. I. Du Pont De Nemours And Company Multilayer polymeric laminates and high strength laminates produced therefrom
WO2008115567A1 (en) * 2007-03-19 2008-09-25 E. I. Du Pont De Nemours And Company High contrast high strength decorative sheets and laminates
EP2810951A2 (en) 2008-06-04 2014-12-10 Synergy Pharmaceuticals Inc. Agonists of guanylate cyclase useful for the treatment of gastrointestinal disorders, inflammation, cancer and other disorders
GB2469094A (en) * 2009-04-01 2010-10-06 Jeremy Town Decorative panel
WO2012028820A1 (fr) 2010-09-02 2012-03-08 Saint-Gobain Glass France Vitrage feuilleté éclairant a diodes electroluminescentes et sa fabrication
WO2013138352A1 (en) 2012-03-15 2013-09-19 Synergy Pharmaceuticals Inc. Formulations of guanylate cyclase c agonists and methods of use
WO2014131024A2 (en) 2013-02-25 2014-08-28 Synergy Pharmaceuticals Inc. Agonists of guanylate cyclase and their uses
WO2014151200A2 (en) 2013-03-15 2014-09-25 Synergy Pharmaceuticals Inc. Compositions useful for the treatment of gastrointestinal disorders
WO2014151206A1 (en) 2013-03-15 2014-09-25 Synergy Pharmaceuticals Inc. Agonists of guanylate cyclase and their uses
US11396160B2 (en) 2017-08-25 2022-07-26 Kuraray Europe Gmbh Laminated glass comprising interlayer film layers with a pigmented frame
US20230182449A1 (en) * 2021-12-10 2023-06-15 Chang Chun Petrochemical Co., Ltd. Polymer film
WO2024162476A1 (ja) 2023-02-02 2024-08-08 積水化学工業株式会社 画像担持積層体、その製造方法、合わせガラス用中間膜、及び合わせガラス
KR20250142863A (ko) 2023-02-02 2025-09-30 세키스이가가쿠 고교가부시키가이샤 화상 담지 적층체, 그 제조 방법, 접합 유리용 중간막, 및 접합 유리
EP4660168A1 (en) 2023-02-02 2025-12-10 Sekisui Chemical Co., Ltd. Image-carrying laminate, method for manufacturing same, intermediate film for laminated glass, and laminated glass
WO2024247770A1 (ja) 2023-05-29 2024-12-05 積水化学工業株式会社 画像担持積層体、その製造方法、合わせガラス用中間膜、及び合わせガラス

Also Published As

Publication number Publication date
DE60312338T2 (de) 2007-11-29
MXPA05001118A (es) 2005-04-28
AU2003257995A1 (en) 2004-02-16
DE60312338D1 (de) 2007-04-19
EP1525099A1 (en) 2005-04-27
US7232213B2 (en) 2007-06-19
CA2494057A1 (en) 2004-02-05
CN100379578C (zh) 2008-04-09
AU2003257995B2 (en) 2008-05-22
CN1671560A (zh) 2005-09-21
JP2005534527A (ja) 2005-11-17
US20050285920A1 (en) 2005-12-29
EP1525099B1 (en) 2007-03-07

Similar Documents

Publication Publication Date Title
US7232213B2 (en) Ink-jet printed rigid interlayer and a process for preparing same
US20080105371A1 (en) Decorative Laminated Safety Glass Utilizing a Rigid Interlayer and a Process for Preparing Same
EP1539487B1 (en) Decorative laminated safety glass
US9011628B2 (en) Decorative laminated safety glass
CN100398314C (zh) 用于层压玻璃的数字颜色-设计复合体
AU2006332747B2 (en) Decorative sheets having enhanced adhesion and laminates prepared therefrom
CN101668629A (zh) 高对比度装饰片材和层压体
US20070196630A1 (en) Decorative solar control laminates
US20070071955A9 (en) Decorative laminated safety glass
US20070172637A1 (en) Decorative sheets having enhanced adhesion and penetration resistant laminates prepared therefrom
WO2009008856A1 (en) Decorative solar control laminates

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2003257995

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: 10519655

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 2003772174

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: PA/a/2005/001118

Country of ref document: MX

Ref document number: 2004524278

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 2494057

Country of ref document: CA

Ref document number: 20038183854

Country of ref document: CN

WWP Wipo information: published in national office

Ref document number: 2003772174

Country of ref document: EP

WWG Wipo information: grant in national office

Ref document number: 2003772174

Country of ref document: EP