WO2003080752A1 - Wässrige 2k-pur-systeme - Google Patents
Wässrige 2k-pur-systeme Download PDFInfo
- Publication number
- WO2003080752A1 WO2003080752A1 PCT/EP2003/002531 EP0302531W WO03080752A1 WO 2003080752 A1 WO2003080752 A1 WO 2003080752A1 EP 0302531 W EP0302531 W EP 0302531W WO 03080752 A1 WO03080752 A1 WO 03080752A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- weight
- aqueous
- polyurethane systems
- polyol
- Prior art date
Abstract
Description
Claims