WO2003020993A1 - Rare earth magnet alloy ingot, manufacturing method for the same, r-t-b type magnet alloy ingot, r-t-b type magnet, r-t-b type bonded magnet, r-t-b type exchange spring magnet alloy ingot, r-t-b type exchange spring magnet, and r-t-b type exchange spring bonded magnet - Google Patents
Rare earth magnet alloy ingot, manufacturing method for the same, r-t-b type magnet alloy ingot, r-t-b type magnet, r-t-b type bonded magnet, r-t-b type exchange spring magnet alloy ingot, r-t-b type exchange spring magnet, and r-t-b type exchange spring bonded magnet Download PDFInfo
- Publication number
- WO2003020993A1 WO2003020993A1 PCT/JP2002/008931 JP0208931W WO03020993A1 WO 2003020993 A1 WO2003020993 A1 WO 2003020993A1 JP 0208931 W JP0208931 W JP 0208931W WO 03020993 A1 WO03020993 A1 WO 03020993A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alloy ingot
- rare earth
- type
- magnet alloy
- magnet
- Prior art date
Links
- 229910045601 alloy Inorganic materials 0.000 title claims abstract description 403
- 239000000956 alloy Substances 0.000 title claims abstract description 403
- 229910052761 rare earth metal Inorganic materials 0.000 title claims abstract description 109
- 150000002910 rare earth metals Chemical class 0.000 title claims abstract description 93
- 238000004519 manufacturing process Methods 0.000 title claims description 80
- 230000005291 magnetic effect Effects 0.000 claims abstract description 115
- 229910052742 iron Inorganic materials 0.000 claims abstract description 37
- 229910052802 copper Inorganic materials 0.000 claims abstract description 34
- 229910052782 aluminium Inorganic materials 0.000 claims abstract description 27
- 229910052759 nickel Inorganic materials 0.000 claims abstract description 23
- 229910052779 Neodymium Inorganic materials 0.000 claims abstract description 22
- 229910052804 chromium Inorganic materials 0.000 claims abstract description 22
- 229910052748 manganese Inorganic materials 0.000 claims abstract description 22
- 229910052777 Praseodymium Inorganic materials 0.000 claims abstract description 20
- 229910052733 gallium Inorganic materials 0.000 claims abstract description 20
- 229910052692 Dysprosium Inorganic materials 0.000 claims abstract description 19
- 239000000126 substance Substances 0.000 claims abstract description 19
- 229910052751 metal Inorganic materials 0.000 claims description 104
- 239000002184 metal Substances 0.000 claims description 103
- 239000013078 crystal Substances 0.000 claims description 88
- 239000000843 powder Substances 0.000 claims description 65
- 238000000034 method Methods 0.000 claims description 61
- 238000005266 casting Methods 0.000 claims description 48
- 238000010298 pulverizing process Methods 0.000 claims description 40
- 239000002245 particle Substances 0.000 claims description 33
- 229910000859 α-Fe Inorganic materials 0.000 claims description 16
- 230000000694 effects Effects 0.000 claims description 15
- 238000009750 centrifugal casting Methods 0.000 claims description 13
- 239000000463 material Substances 0.000 claims description 13
- 239000011248 coating agent Substances 0.000 claims description 9
- 238000000576 coating method Methods 0.000 claims description 9
- 238000005507 spraying Methods 0.000 claims description 9
- 239000000919 ceramic Substances 0.000 claims description 8
- 239000002131 composite material Substances 0.000 claims description 8
- 238000005520 cutting process Methods 0.000 claims description 6
- 238000000227 grinding Methods 0.000 claims description 6
- 238000005498 polishing Methods 0.000 claims description 6
- 230000015572 biosynthetic process Effects 0.000 claims description 5
- 239000002994 raw material Substances 0.000 claims description 4
- 238000007747 plating Methods 0.000 claims description 3
- 238000003466 welding Methods 0.000 claims description 3
- 239000012071 phase Substances 0.000 description 88
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 74
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 60
- 125000004429 atom Chemical group 0.000 description 54
- 239000012298 atmosphere Substances 0.000 description 53
- 239000000203 mixture Substances 0.000 description 49
- 238000001816 cooling Methods 0.000 description 36
- 239000010949 copper Substances 0.000 description 32
- 239000007789 gas Substances 0.000 description 32
- 229910052786 argon Inorganic materials 0.000 description 30
- 239000000700 radioactive tracer Substances 0.000 description 29
- 239000000047 product Substances 0.000 description 27
- 239000001257 hydrogen Substances 0.000 description 25
- 229910052739 hydrogen Inorganic materials 0.000 description 25
- 238000005245 sintering Methods 0.000 description 21
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 19
- 238000000151 deposition Methods 0.000 description 18
- 230000008021 deposition Effects 0.000 description 18
- 230000005415 magnetization Effects 0.000 description 18
- PXHVJJICTQNCMI-UHFFFAOYSA-N nickel Substances [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 17
- 239000011651 chromium Substances 0.000 description 16
- 239000011261 inert gas Substances 0.000 description 16
- 239000011572 manganese Substances 0.000 description 14
- 238000000465 moulding Methods 0.000 description 14
- 229920005989 resin Polymers 0.000 description 14
- 239000011347 resin Substances 0.000 description 14
- 230000000052 comparative effect Effects 0.000 description 13
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 12
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 12
- 230000001965 increasing effect Effects 0.000 description 12
- 238000010438 heat treatment Methods 0.000 description 11
- 230000006698 induction Effects 0.000 description 11
- 238000002844 melting Methods 0.000 description 11
- 230000008018 melting Effects 0.000 description 11
- 238000007711 solidification Methods 0.000 description 11
- 230000008023 solidification Effects 0.000 description 10
- 238000010521 absorption reaction Methods 0.000 description 9
- 230000007423 decrease Effects 0.000 description 8
- 230000001747 exhibiting effect Effects 0.000 description 8
- 238000005259 measurement Methods 0.000 description 8
- 238000003825 pressing Methods 0.000 description 7
- 230000008569 process Effects 0.000 description 7
- 239000011369 resultant mixture Substances 0.000 description 7
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 6
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 6
- 150000002431 hydrogen Chemical class 0.000 description 6
- 239000000314 lubricant Substances 0.000 description 6
- QEFYFXOXNSNQGX-UHFFFAOYSA-N neodymium atom Chemical compound [Nd] QEFYFXOXNSNQGX-UHFFFAOYSA-N 0.000 description 6
- 239000001301 oxygen Substances 0.000 description 6
- 229910052760 oxygen Inorganic materials 0.000 description 6
- 238000007750 plasma spraying Methods 0.000 description 6
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 5
- 238000003795 desorption Methods 0.000 description 5
- 239000006185 dispersion Substances 0.000 description 5
- 239000003822 epoxy resin Substances 0.000 description 5
- 150000002739 metals Chemical class 0.000 description 5
- 229910001172 neodymium magnet Inorganic materials 0.000 description 5
- 239000012299 nitrogen atmosphere Substances 0.000 description 5
- 230000006911 nucleation Effects 0.000 description 5
- 238000010899 nucleation Methods 0.000 description 5
- 229920000647 polyepoxide Polymers 0.000 description 5
- 239000007858 starting material Substances 0.000 description 5
- 230000001133 acceleration Effects 0.000 description 4
- 239000012300 argon atmosphere Substances 0.000 description 4
- 229910017052 cobalt Inorganic materials 0.000 description 4
- 239000010941 cobalt Substances 0.000 description 4
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 description 4
- 230000006866 deterioration Effects 0.000 description 4
- 230000002542 deteriorative effect Effects 0.000 description 4
- 229910001873 dinitrogen Inorganic materials 0.000 description 4
- 230000002708 enhancing effect Effects 0.000 description 4
- -1 ferroboron Chemical compound 0.000 description 4
- 230000004907 flux Effects 0.000 description 4
- 230000005381 magnetic domain Effects 0.000 description 4
- 230000014759 maintenance of location Effects 0.000 description 4
- 239000007769 metal material Substances 0.000 description 4
- 239000010955 niobium Substances 0.000 description 4
- 238000007254 oxidation reaction Methods 0.000 description 4
- 230000001105 regulatory effect Effects 0.000 description 4
- 239000004677 Nylon Substances 0.000 description 3
- 150000004678 hydrides Chemical class 0.000 description 3
- 229910001004 magnetic alloy Inorganic materials 0.000 description 3
- 238000001465 metallisation Methods 0.000 description 3
- 238000002156 mixing Methods 0.000 description 3
- 229910052750 molybdenum Inorganic materials 0.000 description 3
- 229910052758 niobium Inorganic materials 0.000 description 3
- 229920001778 nylon Polymers 0.000 description 3
- 230000002093 peripheral effect Effects 0.000 description 3
- 238000005096 rolling process Methods 0.000 description 3
- 229910052715 tantalum Inorganic materials 0.000 description 3
- 229910052719 titanium Inorganic materials 0.000 description 3
- 239000010936 titanium Substances 0.000 description 3
- 229910052721 tungsten Inorganic materials 0.000 description 3
- 229910052720 vanadium Inorganic materials 0.000 description 3
- XOOUIPVCVHRTMJ-UHFFFAOYSA-L zinc stearate Chemical compound [Zn+2].CCCCCCCCCCCCCCCCCC([O-])=O.CCCCCCCCCCCCCCCCCC([O-])=O XOOUIPVCVHRTMJ-UHFFFAOYSA-L 0.000 description 3
- 229910052726 zirconium Inorganic materials 0.000 description 3
- 229910000521 B alloy Inorganic materials 0.000 description 2
- PZNSFCLAULLKQX-UHFFFAOYSA-N Boron nitride Chemical compound N#B PZNSFCLAULLKQX-UHFFFAOYSA-N 0.000 description 2
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N Iron oxide Chemical compound [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 description 2
- 229910001566 austenite Inorganic materials 0.000 description 2
- QVQLCTNNEUAWMS-UHFFFAOYSA-N barium oxide Chemical compound [Ba]=O QVQLCTNNEUAWMS-UHFFFAOYSA-N 0.000 description 2
- 229910052796 boron Inorganic materials 0.000 description 2
- 230000015556 catabolic process Effects 0.000 description 2
- 230000007547 defect Effects 0.000 description 2
- 238000006731 degradation reaction Methods 0.000 description 2
- 230000005294 ferromagnetic effect Effects 0.000 description 2
- 238000005242 forging Methods 0.000 description 2
- 229910052735 hafnium Inorganic materials 0.000 description 2
- 238000007731 hot pressing Methods 0.000 description 2
- AMWRITDGCCNYAT-UHFFFAOYSA-L hydroxy(oxo)manganese;manganese Chemical compound [Mn].O[Mn]=O.O[Mn]=O AMWRITDGCCNYAT-UHFFFAOYSA-L 0.000 description 2
- 238000001746 injection moulding Methods 0.000 description 2
- 239000000696 magnetic material Substances 0.000 description 2
- 238000002595 magnetic resonance imaging Methods 0.000 description 2
- 230000003647 oxidation Effects 0.000 description 2
- PUDIUYLPXJFUGB-UHFFFAOYSA-N praseodymium atom Chemical compound [Pr] PUDIUYLPXJFUGB-UHFFFAOYSA-N 0.000 description 2
- 230000009467 reduction Effects 0.000 description 2
- 238000010583 slow cooling Methods 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 2
- 229910052582 BN Inorganic materials 0.000 description 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- 229910000592 Ferroniobium Inorganic materials 0.000 description 1
- 230000005374 Kerr effect Effects 0.000 description 1
- 229910000990 Ni alloy Inorganic materials 0.000 description 1
- 244000137852 Petrea volubilis Species 0.000 description 1
- 235000002492 Rungia klossii Nutrition 0.000 description 1
- 244000117054 Rungia klossii Species 0.000 description 1
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 1
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 1
- WGLPBDUCMAPZCE-UHFFFAOYSA-N Trioxochromium Chemical compound O=[Cr](=O)=O WGLPBDUCMAPZCE-UHFFFAOYSA-N 0.000 description 1
- XHCLAFWTIXFWPH-UHFFFAOYSA-N [O-2].[O-2].[O-2].[O-2].[O-2].[V+5].[V+5] Chemical compound [O-2].[O-2].[O-2].[O-2].[O-2].[V+5].[V+5] XHCLAFWTIXFWPH-UHFFFAOYSA-N 0.000 description 1
- 230000002159 abnormal effect Effects 0.000 description 1
- 230000002411 adverse Effects 0.000 description 1
- 230000003064 anti-oxidating effect Effects 0.000 description 1
- 230000004888 barrier function Effects 0.000 description 1
- 230000005540 biological transmission Effects 0.000 description 1
- BRPQOXSCLDDYGP-UHFFFAOYSA-N calcium oxide Chemical compound [O-2].[Ca+2] BRPQOXSCLDDYGP-UHFFFAOYSA-N 0.000 description 1
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium oxide Inorganic materials [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 description 1
- 239000000292 calcium oxide Substances 0.000 description 1
- 229910052799 carbon Inorganic materials 0.000 description 1
- 229910010293 ceramic material Inorganic materials 0.000 description 1
- UFGZSIPAQKLCGR-UHFFFAOYSA-N chromium carbide Chemical compound [Cr]#C[Cr]C#[Cr] UFGZSIPAQKLCGR-UHFFFAOYSA-N 0.000 description 1
- 229910000423 chromium oxide Inorganic materials 0.000 description 1
- 230000001276 controlling effect Effects 0.000 description 1
- 230000007797 corrosion Effects 0.000 description 1
- 238000005260 corrosion Methods 0.000 description 1
- 238000005536 corrosion prevention Methods 0.000 description 1
- 230000001627 detrimental effect Effects 0.000 description 1
- 238000009826 distribution Methods 0.000 description 1
- KBQHZAAAGSGFKK-UHFFFAOYSA-N dysprosium atom Chemical compound [Dy] KBQHZAAAGSGFKK-UHFFFAOYSA-N 0.000 description 1
- 238000004880 explosion Methods 0.000 description 1
- 239000012467 final product Substances 0.000 description 1
- 238000000265 homogenisation Methods 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- ZFGFKQDDQUAJQP-UHFFFAOYSA-N iron niobium Chemical compound [Fe].[Fe].[Nb] ZFGFKQDDQUAJQP-UHFFFAOYSA-N 0.000 description 1
- 239000007791 liquid phase Substances 0.000 description 1
- CPLXHLVBOLITMK-UHFFFAOYSA-N magnesium oxide Inorganic materials [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 description 1
- 239000000395 magnesium oxide Substances 0.000 description 1
- AXZKOIWUVFPNLO-UHFFFAOYSA-N magnesium;oxygen(2-) Chemical compound [O-2].[Mg+2] AXZKOIWUVFPNLO-UHFFFAOYSA-N 0.000 description 1
- 230000007246 mechanism Effects 0.000 description 1
- UNASZPQZIFZUSI-UHFFFAOYSA-N methylidyneniobium Chemical compound [Nb]#C UNASZPQZIFZUSI-UHFFFAOYSA-N 0.000 description 1
- 239000013081 microcrystal Substances 0.000 description 1
- 229910052757 nitrogen Inorganic materials 0.000 description 1
- QGLKJKCYBOYXKC-UHFFFAOYSA-N nonaoxidotritungsten Chemical compound O=[W]1(=O)O[W](=O)(=O)O[W](=O)(=O)O1 QGLKJKCYBOYXKC-UHFFFAOYSA-N 0.000 description 1
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 1
- RVTZCBVAJQQJTK-UHFFFAOYSA-N oxygen(2-);zirconium(4+) Chemical compound [O-2].[O-2].[Zr+4] RVTZCBVAJQQJTK-UHFFFAOYSA-N 0.000 description 1
- 230000002265 prevention Effects 0.000 description 1
- 229910001404 rare earth metal oxide Inorganic materials 0.000 description 1
- 238000001878 scanning electron micrograph Methods 0.000 description 1
- 238000005204 segregation Methods 0.000 description 1
- 229910052814 silicon oxide Inorganic materials 0.000 description 1
- KKCBUQHMOMHUOY-UHFFFAOYSA-N sodium oxide Chemical compound [O-2].[Na+].[Na+] KKCBUQHMOMHUOY-UHFFFAOYSA-N 0.000 description 1
- 229910001948 sodium oxide Inorganic materials 0.000 description 1
- 241000894007 species Species 0.000 description 1
- 238000003892 spreading Methods 0.000 description 1
- 230000007480 spreading Effects 0.000 description 1
- 239000010935 stainless steel Substances 0.000 description 1
- 229910001220 stainless steel Inorganic materials 0.000 description 1
- 229910002058 ternary alloy Inorganic materials 0.000 description 1
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 description 1
- 229910003470 tongbaite Inorganic materials 0.000 description 1
- MTPVUVINMAGMJL-UHFFFAOYSA-N trimethyl(1,1,2,2,2-pentafluoroethyl)silane Chemical compound C[Si](C)(C)C(F)(F)C(F)(F)F MTPVUVINMAGMJL-UHFFFAOYSA-N 0.000 description 1
- UONOETXJSWQNOL-UHFFFAOYSA-N tungsten carbide Chemical compound [W+]#[C-] UONOETXJSWQNOL-UHFFFAOYSA-N 0.000 description 1
- 229910001930 tungsten oxide Inorganic materials 0.000 description 1
- 229910001935 vanadium oxide Inorganic materials 0.000 description 1
- 230000003245 working effect Effects 0.000 description 1
- 229910001928 zirconium oxide Inorganic materials 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y25/00—Nanomagnetism, e.g. magnetoimpedance, anisotropic magnetoresistance, giant magnetoresistance or tunneling magnetoresistance
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D13/00—Centrifugal casting; Casting by using centrifugal force
- B22D13/04—Centrifugal casting; Casting by using centrifugal force of shallow solid or hollow bodies, e.g. wheels or rings, in moulds rotating around their axis of symmetry
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D13/00—Centrifugal casting; Casting by using centrifugal force
- B22D13/08—Centrifugal casting; Casting by using centrifugal force in which a stationary mould is fed from a rotating mass of liquid metal
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
- B22F1/06—Metallic powder characterised by the shape of the particles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
- B22F3/115—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces by spraying molten metal, i.e. spray sintering, spray casting
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C1/00—Making non-ferrous alloys
- C22C1/04—Making non-ferrous alloys by powder metallurgy
- C22C1/0433—Nickel- or cobalt-based alloys
- C22C1/0441—Alloys based on intermetallic compounds of the type rare earth - Co, Ni
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/10—Ferrous alloys, e.g. steel alloys containing cobalt
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
- H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
- H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
- H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
- H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
- H01F1/047—Alloys characterised by their composition
- H01F1/053—Alloys characterised by their composition containing rare earth metals
- H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
- H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
- H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
- H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
- H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
- H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
- H01F1/047—Alloys characterised by their composition
- H01F1/053—Alloys characterised by their composition containing rare earth metals
- H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
- H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
- H01F1/0571—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
- H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
- H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
- H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
- H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
- H01F1/047—Alloys characterised by their composition
- H01F1/053—Alloys characterised by their composition containing rare earth metals
- H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
- H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
- H01F1/0571—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes
- H01F1/0574—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes obtained by liquid dynamic compaction
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
- H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
- H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
- H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
- H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
- H01F1/047—Alloys characterised by their composition
- H01F1/053—Alloys characterised by their composition containing rare earth metals
- H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
- H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
- H01F1/0571—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes
- H01F1/0575—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes pressed, sintered or bonded together
- H01F1/0577—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes pressed, sintered or bonded together sintered
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
- H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
- H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
- H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
- H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
- H01F1/047—Alloys characterised by their composition
- H01F1/053—Alloys characterised by their composition containing rare earth metals
- H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
- H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
- H01F1/0579—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B with exchange spin coupling between hard and soft nanophases, e.g. nanocomposite spring magnets
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F2999/00—Aspects linked to processes or compositions used in powder metallurgy
Definitions
- the present invention relates to a rare earth alloy ingot, a sintered magnet comprising the rare earth alloy ingot, a production method for a rare earth alloy ingot, a production method for a rare earth alloy flake, an R-T-B type magnet alloy ingot, an R-T-B type magnet, an R-T-B type magnet alloy flake, an R-T-B type magnet alloy powder, an R-T-B type bonded magnet, an R-T-B type exchange spring magnet alloy ingot, an R-T-B type exchange spring magnet, an R-T-B type exchange spring magnet alloy powder, and an R-T-B type exchange spring bonded magnet.
- An R-T-B alloy contains, as the dominant phase, a ferromagnetic phase formed of R 2 T ! B crystals, which contribute to magnetization, and, in grain boundaries of the R 2 T ] B crystals, a nonmagnetic R-rich phase having a low melting point and containing a rare earth element(s) at high concentration.
- the R-T-B alloy is an active metallic material. Therefore, the alloy is generally melted and mold-cast in vacuum or under inert gas.
- an ingot of the alloy is pulverized to powder having a particle size of about 3 ⁇ m (as measured by means of FSSS (Fisher Sub-Sieve Sizer)); the powder is subjected to press-forming in a magnetic field; the resultant compact is sintered in a sintering furnace at a temperature as high as about 1 ,000 to about 1 ,100°C; and in accordance with needs, the sintered product is heated, mechanically processed, and plated for corrosion prevention.
- the R-rich phase plays the following important roles.
- the R-rich phase functions to smoothen grain boundaries, thereby reducing the number of nucleation sites in a reversed magnetic domain, thereby enhancing the coercivity.
- the R-rich phase magnetically insulates the dominant phase, thereby enhancing the coercivity.
- the distribution of the R-rich phase in a magnet the final product depends greatly on the metallographic structure of the raw material alloy ingot. Specifically, when the alloy is mold-cast, a slow cooling rate often results in formation of large crystal grains. In such a case, the particle size of the pulverized product becomes considerably smaller than that of the crystal grain size.
- R-rich phase is included not in crystal grains but virtually in crystal grain boundaries. Therefore, particles formed only of the dominant phase containing no R-rich phase and those formed only of the R-rich phase result, making it difficult to mix the dominant phase and R-rich phase homogeneously.
- a molten metal is slowly poured onto a copper roll whose inside is cooled by water and which rotates at a peripheral velocity of about 1 mm/sec, and is solidified through rapid cooling, to thereby produce flake having a thickness in a range from about 0.1 to 1 mm (Japanese Patent Application Laid-Open (kokai) Nos. 05-222488 and 05-295490).
- the molten metal was solidified through rapid cooling, to thereby yield an alloy having a microcrystalline structure in which R-rich phase is minutely dispersed.
- FIG. 9 is a back-scattered electron image, observed under an SEM (scanning electron microscope), showing a cross section of an Nd-Fe-B ingot (Nd: 30.0% by mass) cast through a conventional SC method.
- Nd-rich (i.e., R of the R-rich phase is Nd) phase corresponds to bright portions. Some portion of the Nd-rich phase assumes the shape of linked rods extending in the solidification direction (left (roll side) to right (free side)). Another portion of the Nd-rich phase assumes a dot shape and is dispersed. In the rod-shaped Nd-rich phase, the growth direction in grain boundaries and that in crystal grains coincide with the longitudinal direction of the rod-shaped Nd-rich phase. Although the rod-shaped phase is slightly reduced or fragmented through heat treatment performed after casting, effects exerted during casting still prevail, and the dot-shaped or rod-shaped Nd-rich phase shows nonuniform dispersion. Such a microcrystalline feature is typical to a cross-sectional metallographic structure of an Nd-Fe-B alloy ingot cast through the SC method.
- the R-T-B type alloy contains, as the dominant phase, a ferromagnetic phase formed of R 2 T ⁇ B crystals, which contribute to magnetization, and, in grain boundaries of the R 2 T
- the R-T-B type alloy is an active metallic material. Therefore, the alloy is generally melted and cast in vacuum or under inert gas, and the cast alloy provides sintered magnets and bonded magnets. Below, the sintered magnet and the bonded magnets are explained.
- the alloy ingot produced through any of the above methods is pulverized in an inert gas atmosphere, such as argon, nitrogen, to have a particle size of about 3 ⁇ m (as measured by means of an FSSS (Fisher Sub-Sieve Sizer)); the resultant powder is subjected to press-forming in a magnetic field at 0.8 to 2 ton/cm ; the resultant compact is sintered in a sintering furnace at a temperature as high as about 1,000 to about 1 ,100°C (hereinafter, the steps of pulverization to sintering are collectively referred to as the powder metallurgical method); and in accordance with needs, the sintered product is heated at 500 to 800°C, mechanically processed, and plated for prevention of corrosion, to thereby produce a magnet.
- an inert gas atmosphere such as argon, nitrogen
- the SC method provides a minute microcrystalline structure and forms an alloy in which a low-melting-temperature R-rich phase formed of concentrated nonmagnetic rare earth elements is minutely dispersed. Since the R-rich phase is minutely dispersed in the alloy, dispersibility of the R-rich phase after pulverizing and sintering the alloy also becomes satisfactory, to thereby successfully attain improved magnetic characteristics as compared with those of alloy ingots produced through the BM method.
- An alloy ingot for bonded magnets in the form of ribbon having a thickness in a range from 10 to 100 ⁇ m, is produced through the ultra-rapid-cooling method; i.e., by injecting a molten metal from a crucible, via an orifice provided in the bottom of the crucible, onto a copper roll which rotates at a high peripheral velocity of about 20 m/sec.
- the ribbon produced through the ultra-rapid-cooling method may be heated at 400 to 1 ,000°C in accordance with needs, followed by pulverization to powder having a particle size of 500 ⁇ m or less.
- a mixture of the powder and a resin is press-molded or injection-molded, to thereby form a magnet. Since the ribbon is isotropic in terms of magnetic characteristics, the bonded magnet produced from the ribbon also exhibits magnetic isotropy.
- the hard magnetic phase of the exchange spring magnet must exhibit a highly anisotropic magnetic field
- the hard magnetic phase is formed of a rare earth material such as R 2 T ⁇ B, Sm ⁇ Co 5 , or Sm 2 C ⁇ 7 .
- the soft magnetic phase is formed of Fe, Fe 2 B, Fe 3 B, etc., which exhibit high saturation magnetization.
- R-T-B type magnet alloy ingots produced through the BM method or the SC method exhibit very weak magnetic characteristics, and so, they cannot be used as a magnet.
- the reason therefor is as follows.
- coercive force is exhibited on a nucleation-based mechanism.
- crystal grain boundaries contain lattice defects and irregularities in an as-cast state, and these lattice defects and irregularities serve as nuclei for generating a reverse magnetic domain (hereinafter the nuclei are referred to as nucleation sites). Even when a weak reverse magnetic field is applied, magnetization inversion occurs from the nucleation sites, resulting in magnetization inversion of the entirety of crystal grains.
- an alloy ingot produced through the BM method contains a large number of crystal grains having a major grain size of about some mm
- an alloy ingot produced through the SC method contains a large number of crystal grains having a major grain size of 100 ⁇ m or more.
- the volume required for magnetization inversion with respect to the total volume of the alloy is large, resulting in very poor magnetic characteristics.
- the alloy ingot is pulverized to have a particle size of about 3 ⁇ m, followed by sintering, to thereby produce a magnet.
- the thus-produced magnet has a crystal grain size of about 5 to about 20 ⁇ m, and the low-melting-temperature R-rich phase which becomes a liquid phase during sintering smoothens irregularities of grain boundaries, leading to reduction of nucleation sites, thereby enhancing coercive force.
- the steps of pulverization to sintering involve a considerably high cost.
- the alloy powder is an active R-T-B type magnet alloy powder
- measures such as performing the steps of pulverization to sintering in an inert gas atmosphere are required, from the viewpoints of product quality with less variation and greater safety in production steps. Such measures also increase the cost.
- ribbon for R-T-B type bonded magnets produced through the ultra-rapid-cooling method is heated at 500 to 800°C in accordance with needs, so as to obtain optimal magnetic characteristics.
- ribbon having a crystal grain size in a range from 10 to 100 nm and exhibiting magnetic isotropy is provided. Since the ribbon-form ingot is not practical for use, the ribbon is pulverized to have a particle size of 500 ⁇ m or less.
- a mixture of the powder and a resin is press-molded or injection-molded, to thereby provide an isotropic bonded magnet.
- There has also been proposed a method for producing bulk isotropic magnets including hot-pressing the ribbon at 700°C and 1 ton/cm 2 (R. W. Lee, Appl. Phys. Lett. 46 (1985), Japanese Patent Application Laid-Open (kokai) No. 60-100402).
- the ultra-rapid-cooling method has low productivity.
- a production method of bulk isotropic magnets including hot-pressing requires a high cost.
- the present inventors attempted to increase the solidification-cooling rate in the CC process by reducing the deposition rate of a molten metal and previously proposed a centrifugal casting method including sprinkling a molten metal from a rotating tundish and causing the sprinkled molten metal to be deposited on an inner surface of a rotating mold (Japanese Patent Application No. 2000-262605).
- a centrifugal casting method including sprinkling a molten metal from a rotating tundish and causing the sprinkled molten metal to be deposited on an inner surface of a rotating mold.
- R-rich phase content decreases, possibly resulting in failure to produce sintered magnets of high density and enhanced coercive force. Therefore, it is thought that a minute and uniform dispersion state of the R-rich phase must be attained through more rapid cooling-solidification so as to attain further enhanced magnetic characteristics.
- the thus-produced R-T-B type alloy ingot contains a large number of crystal grains having a major size of 1,000 ⁇ m or more, and exhibits very poor magnetic characteristics in an as-cast state. Therefore, further enhancement of the solidification-cooling rate, to thereby reduce the crystal grain size, is deemed necessary.
- the present invention has an object of providing a production method for a rare earth alloy ingot and a production method for a rare earth alloy flake which improve the efficiency of heat transfer from the cast surface of the cast ingot to the inner surface wall of the casting mold.
- the present invention has an object of providing a rare earth magnet alloy ingot and a sintered magnet, which have improved magnetic properties.
- the present invention has an object of providing an R-T-B type magnet alloy ingot, an R-T-B type magnet, an R-T-B type magnet alloy flake, an R-T-B type magnet alloy powder, an R-T-B type bonded magnet, an R-T-B type exchange spring magnet alloy ingot, an R-T-B type exchange spring magnet, an R-T-B type exchange magnet alloy powder, and an R-T-B type exchange spring bonded magnet, which have fine crystal grains not available conventionally.
- the present invention provides a rare earth magnet alloy ingot, characterized by comprising an R-T-B type magnet alloy (R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.) containing at least one element selected from among Nd, Pr, and Dy in a total amount of 11.8 to 16.5% by atom and B in an amount of 5.6 to 9.1% by atom, and characterized in that, as determined in an as-cast state of the alloy ingot, R-rich phase that measures 100 ⁇ m or more is substantially absent on a cross section.
- R-T-B type magnet alloy R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.
- Nd, Pr, and Dy in
- the present invention provides another rare earth magnet alloy ingot, characterized by comprising an R-T-B type magnet alloy (R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.) containing at least one element selected from among Nd, Pr, and Dy in a total amount of 11.8 to 16.5% by atom and B in an amount of 5.6 to 9.1% by atom, and characterized in that, as determined in an as-cast state of the alloy ingot, an area in which R-rich phase that measures 50 ⁇ m or less is dispersed accounts for at least 50% the cross section.
- R-T-B type magnet alloy R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.
- the present invention provides another rare earth magnet alloy ingot, characterized by comprising an R-T-B type magnet alloy (R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.) containing at least one element selected from among Nd, Pr, and Dy in a total amount of 11.8 to 16.5% by atom and B in an amount of 5.6 to 9.1% by atom, and characterized in that, as determined in an as-cast state of the alloy ingot, R-rich phase having an aspect ratio of at least 20 is substantially absent on a cross section.
- R-T-B type magnet alloy R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.
- Nd, Pr, and Dy in a
- the crystal grains having a diameter of at least 1,000 ⁇ m as measured along the major axis occupy an area percentage of at least 5%, and average R-rich phase spacing is 10 ⁇ m or less.
- ⁇ -Fe is substantially absent.
- the rare earth magnet alloy ingot is cast through centrifugal casting comprising receiving molten metal by means of a rotary body; sprinkling the molten metal by the effect of rotation of the rotary body; and causing the sprinkled molten metal to be deposited and solidify on an inner surface of a rotating cylindrical mold, the inner surface including a non-smooth surface.
- an axis of rotation of the rotary body and an axis of rotation of the cylindrical mold form an angle of inclination ⁇ .
- the present invention provides a sintered magnet produced from the rare earth magnet alloy ingot as a raw material.
- an axis of rotation of the rotary body and an axis of rotation of the cylindrical mold form an angle of inclination ⁇ .
- the rare earth magnet alloy ingot is an R-T-B type magnet alloy ingot.
- the inner wall surface of the rotating cylindrical mold it is preferable for the inner wall surface of the rotating cylindrical mold to contain a non-smooth surface.
- the thermal conductivity of the film it is preferable for the thermal conductivity of the film to equal 80 W/mK or less.
- the film is preferable for the film to be made of a metal, a ceramic, or a metal-ceramic composite.
- the film is preferable for the film to be provided on the inner wall surface of the mold by at least one selected from coating, plating, spray coating, and welding.
- the film In the production method, it is preferable for the film to have a thickness falling within a range of 1 ⁇ m to 1 mm. In the production method, it is preferable for an axis of rotation of the rotary body and an axis of rotation of the cylindrical mold to form an angle of inclination ⁇ .
- two or more layers comprising rare earth alloy ingot are deposited and casted on the inner wall surface of the mold by centrifugal casting method.
- the production method it is preferable to further comprise the step of hot- working the obtained rare earth alloy ingot at 500 to 1,100°C.
- the production method it is preferable to further comprise the step of hot-treating the obtained rare earth alloy ingot at 400 to 1,000°C.
- the production method it is preferable to further comprise the steps of heat-treating the obtained rare earth alloy ingot at 1,000 to 1,100°C, and subsequently, an heat- treating at 400 to 1,000°C.
- the rare earth alloy ingot is an R-T-B type magnet alloy (R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.).
- R represents at least one element selected from among rare earth elements, including Y
- T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.
- the present invention provides a production method for a rare earth alloy flakes comprising the steps of: receiving a molten alloy of rare earth metal alloy by means of a rotary body; sprinkling the molten alloy by the effect of rotation of the rotary body, and causing the sprinkled molten alloy to be deposited and solidify on an inner wall surface of a rotating cylindrical mold; wherein a film having a thermal conductivity lower than that of material comprising the mold is provided to the inner wall surface of the cylindrical mold; and casting is performed while alloy flakes deposited on the inner wall surface of the cylindrical mold are scraped.
- the production method it is preferable to further comprise the step of hot-treating the obtained rare earth alloy flakes at 400 to 1,000°C.
- the production method it is preferable to further comprise the steps of heat-treating the obtained rare earth alloy flakes at 1,000 to 1,100°C, and subsequently, an heat- treating at 400 to 1,000°C.
- the rare earth alloy flakes it is preferable for the rare earth alloy flakes to be R-T-B type magnet alloy flakes (R represents at least one element selected from among rare earth elements, including Y; and T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.).
- the present invention provides an R-T-B type magnet alloy ingot, wherein it comprises at least one element selected from among Nd, Pr, and Dy in a total amount of 1 1.8 to 16.5% by atom and B in an amount of 5.6 to 9.1% by atom, with a balance being T (T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.); wherein it contains crystal grains having a grain size of 10 ⁇ m or less in a volume of at least 50% on the basis of the entire volume of the alloy; and wherein it is produced by the production method for an R-T-B type magnet alloy ingot.
- T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.
- the R-T-B type magnet alloy ingot it is preferable to have a thickness of at least 1 mm as it is casted.
- the present invention provides an R-T-B type magnet, wherein it is obtainable by mechanical processing at least one method selected from cutting, grinding, polishing, and blanking the R-T-B type magnet alloy ingot.
- the R-T-B type magnet it is preferable to have a cylindrical shape having an outer diameter of at least 100 mm.
- the present invention provides an R-T-B type magnet alloy flakes, wherein they are produced by the production method for the F-T-B type magnet alloy flakes; wherein they comprise at least one element selected from among Nd, Pr, and Dy in a total amount of 11.8 to 16.5% by atom and B in an amount of 5.6 to 9.1% by atom, with a balance being T (T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.); and wherein they contain crystal grains having a grain size of 10 ⁇ m or less in a volume of at least 50% on the basis of the entire volume of the flakes.
- the R-T-B type magnet alloy flakes it is preferable to have maximum length of 5 cm or less, and the thickness of 1 mm or less.
- the present invention provides an R-T-B type magnet alloy powder produced through pulverization of the R-T-B type magnet alloy ingot to a particle size of 500 ⁇ m or less.
- the present invention provides an R-T-B type magnet alloy powder produced through pulverization of the R-T-B type magnet alloy flakes to a particle size of 500 ⁇ m or less.
- the present invention provides an R-T-B type bonded magnet produced by use of the R-T-B type magnet alloy powder.
- the present invention provides an R-T-B type exchange spring magnet alloy ingot, wherein it is produced by the production method for rare earth alloy ingot; it comprises at least one element selected from Nd, Pr, and Dy in a total amount of 1 to 12% by atom and B in an amount of 3 to 30% by atom, with a balance being T (T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.); it is produced through formation of a composite of crystal grains of a hard magnetic phase and crystal grains of a soft magnetic phase; and it contains crystal grains of a hard magnetic phase having a grain size of 1 ⁇ m or less and crystal grains of a soft magnetic phase having a grain size of 1 ⁇ m or less in a volume of at least 50% on the basis of the entire volume of the alloy.
- T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr,
- the R-T-B type exchange spring magnet alloy ingot it is preferable to have a thickness of 1 mm or greater as it is casted.
- the present invention provides an R-T-B type exchange spring magnet, wherein it is obtainable by mechanical processing at least one method selected from cutting, grinding, polishing, and blanking the R-T-B type exchange spring magnet alloy ingot.
- the present invention provides an R-T-B type exchange spring magnet alloy powder produced through pulverization of the R-T-B type exchange spring magnet alloy ingot to a particle size of 500 ⁇ m or less.
- the present invention provides an R-T-B type exchange spring bonded magnet produced by use of the R-T-B type exchange spring magnet alloy powder.
- FIG. 1 is a view showing a metallographic structure (cross section) of a rare earth alloy ingot of the present invention.
- FIG. 2 is a view showing an exemplary apparatus for producing a rare earth magnet alloy ingot according to the present invention.
- FIG. 3 is a cross-sectional view of an exemplary feature of the inner surface of a mold employed in the present invention.
- FIG. 4 is a cross-sectional view of an exemplary feature of the inner surface of another mold employed in the present invention.
- FIG. 5 is a cross-sectional view of an exemplary feature of the inner surface of another mold employed in the present invention.
- FIG. 6 is a cross-sectional view of an exemplary feature of the inner surface of another mold employed in the present invention.
- FIG. 7 is a cross-sectional view of an exemplary feature of the inner surface of another mold employed in the present invention.
- FIG. 8 is a view showing a conventional casting apparatus employed in the SC method.
- FIG. 9 is a view showing a metallographic structure (cross section) of an alloy ingot produced through a conventional SC method.
- FIG. 1 is a photograph showing a cross section of an ingot (Nd: 30.0% by mass) of the present invention.
- the ingot of the present invention is characterized in that Nd-rich phase is uniformly dispersed in an almost dot-like manner.
- the dot-shaped, dispersed Nd-rich phase generally has a maximum width of 50 ⁇ m or less, and virtually no wire-shaped or rod-shaped Nd-rich phase, which is observed in conventional SC materials, is identified.
- Nd-rich phase which measures 100 ⁇ m or more is substantially absent.
- the state "substantially absent” can be confirmed through observation of a cross section of an ingot in the following manner.
- a cross section of the ingot is polished, and arbitrary observation areas on the cross section are observed under an SEM at a magnification of ⁇ 400.
- the rod-shaped Nd-rich phase having a length of 100 ⁇ m or longer along a longitudinal direction is identified.
- the Nd-rich phase is evaluated as "substantially absent.”
- the ingot of the present invention contains a minutely dispersed, dot-shaped Nd-rich phase, and in the SEM image, an area in which only Nd-rich phase that measures 50 ⁇ m or less is dispersed accounts for at least 50% the cross section.
- Nd-rich phase that measures 50 ⁇ m or less is dispersed
- the ingot of the present invention is also characterized in that the ingot contains reduced rod-shaped R-rich phase.
- R-rich phase having an aspect ratio of at least 20 is "substantially absent.”
- the state "substantially absent” generally refers to a level such that, among ten randomly selected SEM (x 1 ,000) observation areas of a similarly polished cross section, the number of observation areas in which R-rich phase having an aspect ratio of at least 20 is present is about one or zero.
- the ingot of the present invention is also characterized in that crystal grains having a diameter of at least 1,000 ⁇ m as measured along the major axis occupy an area percentage of at least 5%, leading to excellent crystal orientation, and average R-rich phase spacing is 10 ⁇ m or less, leading to excellent sinterability of pulverized products.
- the R-rich phase spacing is obtained through observation of a cross section under an SEM.
- the spacing is an average of spacing values in a direction normal to the cast thickness direction obtained through image processing or manual measurement of a photographic image.
- no substantial ⁇ -Fe is formed until the R content reaches approximately its stoichiometric value.
- the expression "no substantial ⁇ -Fe is formed” generally refers to a state in which, when presence of ⁇ -Fe is confirmed in ten arbitrary observation areas of an arbitrary cross section of an ingot, ⁇ -Fe is not identified in 90% or more of the observation areas. In the back-scattered electron image obtained through SEM, ⁇ -Fe is observed as dendrite-like dark portions.
- FIG. 2 is an illustration showing one example apparatus for producing a rare earth magnet alloy ingot of the present invention. With reference to the illustration, the above method will be described specifically.
- An outline of the centrifugal casting apparatus according to the present invention is shown in FIG. 2.
- FIG. 2 is one example of the present invention.
- the rare earth alloy containing alloys for R-T-B type magnets, and the like, are melted in a melting chamber 1 , for example, an alumina crucible 3, which is evacuated or contains an inert gas atmosphere for the purpose of the active properties thereof.
- the casting of the rare earth alloy is carried out by gradually tilting the crucible so that the molten metal 31 of the rare earth alloy flows in the runner 6, and is received by a cylindrical revolving body 5 having a base, for example.
- the molten metal is distributed from a plurality of holes 11 provided in the side surfaces of the rotating body 5 to the inner wall of the cylindrical mold 4 which is on the outside of the rotating body.
- the cylindrical rotating body 5 is manufactured so as to rotate around a rotation axis R which passes through the center of the circular base and is perpendicular to the base.
- the mold is arranged horizontally.
- the cylindrical mold being arranged horizontally, or vertically, or being inclined.
- the rotating body and the mold it is preferable for the rotating body and the mold to be rotated in the same directions at different speeds of rotation.
- a splash phenomenon occurs readily in which when the molten metal strikes the mold, it is scattered and does not stay on the mold, leading to a reduction in the yield.
- the speed of rotation of the two should not be too close, and usually, the difference in the speed of rotation of the two should be about 10% or greater and preferably 20% or greater.
- the specific number of rotations is determined in consideration of size of the rotating body and the mold, the direction in which the molten metal is sprayed out from the rotating body, the amount of molten metal which splashes without settling in the mold, and the like.
- the present invention is also characterized in that the inner surface of the rotatable mold 4 is rendered to be a non-smooth surface, thereby increasing the cooling area of the mold, leading to an increase in cooling performance and rate of cooling.
- the non-smooth inner surface may have a curved surface as shown in FIG. 3.
- grooves having a cross-section formed of linear segments having angles therebetween as shown in FIGS. 4, 5, and 6 are preferable, since slippage of the molten metal from the mold surface, caused by shrinkage at solidification occurring at the moment of collision of the molten metal with the mold surface, can be prevented, thereby increasing adhesion of the molten metal with the mold and preventing deterioration of heat transfer.
- the depth of the grooves must be preset in consideration of volume and surface area of the mold, specific heat, etc., and the depth is appropriately 0.5 mm to some mm. When the depth is considerably small, cooling effect becomes poor, resulting in failure to form desired metallographic structure, whereas when the depth is excessively large, removal of cast products from the inner surface becomes difficult.
- the relationship between the size of molten metal droplets coming from the rotary body and the size and shape of the grooves is critical.
- molten metal droplets are large and the grooves have a small width and a large depth, a problem arises; i.e., molten metal droplets fail to completely penetrate the grooves, whereby a gap is formed between the mold and deposited molten metal, possibly deteriorating the cooling effect.
- the mold is preferably formed of Cu, from the viewpoint of thermal conductivity.
- Fe is also employed without any problem.
- R-rich phase is crystallized along the formed columnar crystals and assumes the shape of a rod.
- R-rich phase is dispersed in a nonuniform manner.
- the metallographic structure tends to be formed of equiaxed crystals, since cooling performance of the inner surface of the mold is enhanced through increase in rate of solidification.
- R-rich phase is minutely crystallized and assumes virtually no rod shape. Thus, the R-rich phase is considered to be dispersed more uniformly.
- a molten metal is deposited in a mold and a subsequent molten metal is added to the deposited molten metal that is being solidified. Since heat transfer for cooling is effected by mediation of a cast ingot, the thickness of the produced ingot is limited. Generally, the maximum thickness is some tens of mm, and the preferred thickness is about 1 to about 10 mm. When the thickness is as thin as less than 1 mm, handling in the subsequent magnet production step becomes cumbersome, whereas when the thickness is in excess of 10 mm, cooling performance of the surface of the ingot opposite the mold inner surface decreases.
- an R-T-B type magnet alloy ingot which is produced through the casting method is pulverized, shaped, and sintered, to thereby produce an anisotropic magnet of excellent characteristics.
- pulverization is sequentially performed in the order of hydrogen decrepitation, intermediate pulverization, and micro-pulverization, to thereby produce a powder generally having a size of approximately 3 ⁇ m (FSSS).
- hydrogen decrepitation includes a hydrogen absorption step as a first step and a hydrogen desorption step as a second step.
- hydrogen absorption step hydrogen is caused to be absorbed predominantly in the R-rich phase of alloy ingots in a hydrogen gas atmosphere at 267 hPa to 50,000 hPa.
- the R-rich phase is expanded in volume due to R hydride generated in this step, to thereby minutely reduce the alloy ingots themselves or generate numerous micro-cracks.
- Hydrogen absorption is carried out within a temperature range of ambient temperature to approximately 600°C. However, in order to increase expansion in volume of R-rich phase so as to effectively reduce the flakes in size, hydrogen absorption is preferably performed within a temperature range of ambient temperature to approximately 100°C.
- the time for hydrogen absorption is preferably one hour or longer.
- the R hydride formed through the hydrogen absorption step is unstable in the atmosphere and readily oxidized.
- the hydrogen-absorbed product is preferably subjected to hydrogen desorption treatment by maintaining the product at about 200 to about 600°C in vacuum of 1.33 hPa or less. Through this treatment, R hydride can be transformed into a product stable in the atmosphere.
- the time for hydrogen desorption treatment is preferably 30 minutes or longer. If the atmosphere is controlled for preventing oxidation during steps to be carried out after hydrogen absorption to sintering, hydrogen desorption treatment can also be omitted.
- pulverization may be performed through intermediate pulverization and micro-pulverization without performing hydrogen decrepitation.
- Intermediate pulverization is a pulverization step in which alloy flakes are pulverized in an inert gas atmosphere such as argon gas or nitrogen gas, to a particle size of, for example, 500 ⁇ m or less.
- inert gas atmosphere such as argon gas or nitrogen gas
- examples of pulverizers for performing this pulverization include a Brawn mill.
- the alloy flakes have been subjected to hydrogen decrepitation, the alloy flakes have already been reduced minutely or have included numerous minute cracks generated therein. Thus, intermediate pulverization may be omitted.
- Micro-pulverization is a pulverization step for attaining a particle size of approximately 3 ⁇ m (FSSS).
- pulverizers for performing the pulverization include a jet mill.
- the atmosphere is controlled to an inert gas atmosphere such as an argon gas atmosphere or nitrogen gas atmosphere.
- the inert gas may contain oxygen in an amount of 2% by mass or less, preferably 1 % by mass or less. The presence of oxygen enhances pulverization efficiency and attains oxygen concentration of the powder produced through pulverization to 1 ,000 to 10,000 ppm, to thereby enhance oxidation resistance.
- abnormal grain growth during sintering can be prevented.
- a lubricant such as zinc stearate is preferably added to the powder during molding in magnetic field.
- the amount of the lubricant to be added is 0.01 to 1% by mass.
- the lubricant may be added before or after micro-pulverization, the lubricant is preferably mixed sufficiently, before molding in magnetic field, in an inert gas atmosphere such as argon gas or nitrogen gas by use of a mixing apparatus such as a V-blender.
- the powder pulverized to approximately 3 ⁇ m is press-molded in magnetic field by use of a molding apparatus.
- the mold to be employed is fabricated from a magnetic material and a non-magnetic material in combination in consideration of the orientation of magnetic field in the mold cavity.
- the pressure at molding is preferably 0.5 to 2 t/cm , and the magnetic field in the mold cavity during molding is preferably 5 to 20 kOe.
- the atmosphere during molding is preferably an inert gas atmosphere such as argon gas or nitrogen gas. However, if the powder has been subjected to the aforementioned anti-oxidation treatment, molding can be performed in air.
- Sintering is performed at 1,000-1,100°C. Prior to reaching the sintering temperature, a lubricant and hydrogen contained in the micro-powder must be completely removed from a compact to be sintered.
- the lubricant is removed by maintaining the compact preferably under the conditions: in vacuum of 1.33 x 10 " hPa or under an Ar flow atmosphere at reduced pressure; at 300 to 500°C; and for 30 minutes or longer.
- Hydrogen is removed by maintaining the compact preferably under the conditions: in vacuum of 1.33 x 10 "2 hPa or less; at 700 to 900°C; and for 30 minutes or longer.
- the atmosphere during sintering is preferably an argon gas atmosphere or a vacuum atmosphere of 1.33 x 10 "2 hPa or less. A retention time of one hour or longer is preferred.
- the sintered product may be treated at 500 to 650°C in accordance with needs.
- An argon gas atmosphere or a vacuum atmosphere is preferred, and a retention time of 30 minutes or longer is preferred.
- the casting method is applicable to rare earth alloys such as misch metal-Ni alloys used for anodes of nickel-hydrogen batteries. According to quick-cooling solidification involved in the method, segregation of Mn and other metals can be prevented.
- Another feature of the present invention lies in the provision of a film having a thermal conductivity which is lower than the material of the mold on the inner wall of the cylindrical mold which rotates.
- the thermal conductivity of iron at normal temperatures is approximately 80W/mK.
- the thermal conductivity of the film provided on the inner surface of the mold is preferably 80 W/mK or less. Since this film acts as a barrier to the transmission to the mold of the heat of the molten metal deposited on the mold, the temperature of the alloy ingot 7 deposited on the inner surface of the mold at the initial stage of the casting is maintained at a high temperature and does not fall very much.
- This high temperature alloy ingot is pressed against the inner surface of the mold by the centrifugal force of the mold, and the surface which is in contact with the mold becomes as smooth as the inner surface of the mold with almost no gaps between it and the mold.
- the heat transfer coefficient from the alloy ingot to the mold is conversely increased, and molten metal which is deposited thereafter has an extremely fast rate of cooling.
- the particle size of the crystals of the alloy ingot for the R-T-B type magnet is extremely fine. It is possible to make the content of the alloy occupied by crystals having a particle size of 10 ⁇ m or less be 50% or greater of the total alloy, preferably 70%) or greater of the total alloy, and more preferably 80% or greater of the total alloy. As a result, it is possible for the cast ingot to display isotropically high magnetic properties even in its cast form.
- the rate of deposition of the molten metal on the mold is also important. In order to increase the rate of cooling, it is necessary to slow the rate of deposition, and preferably this rate is an average of 0.1 mm/second or less, and more preferably an average of 0.05 mm/second or less.
- the molten metal deposited, at an initial casting stage, on the inner wall of the mold is rapidly cooled and solidified in such a form as provided at deposition.
- the surface (mold side) of the alloy ingot is imparted with a large number of irregularities, which considerably deteriorate the rate of heat transfer from molten metal to be subsequently deposited onto the mold.
- crystal grain growth occurs in the ingot, thereby generating a large number of crystal grains having a major grain size of at least 1,000 ⁇ m.
- the crystal grain size of the alloy ingot may be determined through observation of a cross section of the alloy ingot in the following manner. Specifically, the cross section of the alloy ingot is polished, and an arbitrary observation area is observed under a polarizing microscope (x200) on the basis of the magnetic Kerr effect. The size of each crystal grain observed in the photographed observation area is measured through, for example, image processing. The ratio of the volume of crystal grains having a specific grain size or less to the entire volume of the alloy may be obtained in the following manner. Specifically, ten arbitrary observation areas of a cross section of an alloy ingot are observed under the magnetic Kerr microscope ( ⁇ 200). From the photographed ten observation areas, the total area corresponding to crystal grains having the specific grain size or less is measured through, for example, image processing, and the total area of such crystal grains is divided by the sum often photographed observation areas.
- the method of attaching the film to the inner wall of the mold may be by any one of coating, plating, spraying, or welding.
- coating there are brush application, spraying, and the like
- spraying there are high-pressure-gas spraying, explosion spraying, plasma spraying, self-fluxing alloy spraying, and the like.
- the thickness of the film is preferably in a range from 1 ⁇ m to 1 mm, and more preferably 1 ⁇ m to 500 ⁇ m.
- the material of the film is preferably selected from among a metal, a ceramic, and a metal-ceramic composite. In addition it is preferable for the film to comprises two or more layers which are made of different materials.
- the material for the film is selected such that the formed film has thermal conductivity lower than that of the mold. Examples of metallic materials for forming the film include stainless steel, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Nb, Mo, Ta, W, and alloys thereof. Even when the mold and the film are both formed of Cu, the thermal conductivity of the film can be lowered as compared with the mold by, for example, providing a large number of micropores in the film. In a similar manner, Fe film can be used even when the mold is formed of Fe.
- Ceramic materials for forming the film include boron nitride, sodium oxide, iron oxide, titanium oxide, aluminum oxide, calcium oxide, chromium oxide, zirconium oxide, tungsten oxide, vanadium oxide, barium oxide, manganese oxide, magnesium oxide, silicon oxide, rare earth oxides, tungsten carbide, chromium carbide, niobium carbide, titanium carbide, and composite ceramics thereof.
- composite films formed of the aforementioned metallic materials and ceramics may also be employed.
- the inner wall surface of the rotatable mold may be rendered to be a non-smooth surface, thereby increasing the cooling area of the mold, whereby a film is provided thereon, leading to an increase in cooling performance and rate of cooling.
- the non-smooth inner wall surface may have a curved surface.
- grooves having a cross-section formed of linear segments having angles therebetween are preferable, since slippage of the molten metal from the mold surface, which would otherwise be caused by shrinkage at solidification occurring at the moment of collision of the molten metal with the mold surface, can be prevented, thereby increasing adhesion of the molten metal with the mold and preventing deterioration of heat transfer.
- the depth of the grooves must be preset in consideration of volume and surface area of the mold, specific heat, etc., and the depth is appropriately 0.5 mm to some mm. When the depth is considerably small, cooling effect becomes poor, resulting in failure to form desired metallographic structure, whereas when the depth is excessively large, removal of cast products from the inner surface becomes difficult.
- the alloy ingot preferably has a thickness of at least 1 mm, more preferably at least 5 mm, most preferably at least 10 mm.
- anisotropy When the alloy ingot of the present invention is hot worked at high temperature in an inert gas atmosphere or in vacuum, anisotropy can be provided.
- methods of preferable hot workings include die-upsetting, rolling, forging, and pressing.
- the temperature of deformation is preferably 500 to 1,100°C, more preferably 600 to 800°C.
- the preferable pressure is at least 0.5 ton/cm 2 , more preferably at least 1 ton/cm .
- the R-T-B type magnetic alloy of the present invention comprises at least one element selected from among Nd, Pr, and Dy in a total amount of 11.8 to 16.5% by atom, and B in an amount of 5.6 to 9.1%) by atom, with a balance being T (T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.).
- the alloy is formed of at least one element selected from among Nd, Pr, and Dy in a total amount of 11.8 to 16.5%) by atom and B in an amount of 5.6 to 9.1 % by atom, with a balance being T.
- high-melting-point metals such as Ti, V, Cr, Mn, Zr, Nb, Mo, Hf, Ta, and W may be added.
- the total amount of the metals is preferably regulated to 1% by mass or less so as to prevent deterioration in magnetization.
- the R-T-B type magnetic alloy of the present invention exhibits excellent magnetic characteristics isotropically even when in an ingot state after casting. Therefore, isotropic magnets exhibiting excellent magnetic characteristics can be produced through mere mechanical processing; e.g., cutting, grinding, polishing, or blanking, of an alloy ingot to form a predetermined shape. Briefly, steps of pulverization, pressing in a magnetic field, and sintering, which are necessary for producing the conventional sintered magnets, or steps of pulverization and press-molding or injection molding performed in production of bonded magnets can be omitted, thereby reducing production costs. Since the magnets produced through mechanical processing have a density higher than that of bonded magnets, strong magnets exhibiting high magnetization can be produced.
- the outer diameter of the cylindrical R-T-B type magnets is preferably controlled to 100 mm or more.
- the R-T-B type magnet of the present invention contains a rare earth component and Fe, which are highly prone to oxidization.
- the magnet is preferably coated with a resin or a metal such as Ni or Al. More preferably, the magnet is sequentially coated with a resin and a metal.
- the aforementioned R-T-B type alloy ingot of the present invention contains crystal grains, most of which are minute. Thus, even when the alloy ingot is pulverized, magnetic characteristics are not greatly deteriorated.
- the ingot is pulverized to a particle size of 500 ⁇ m or less, and the powder is mixed with an epoxy resin or a similar resin and the resultant mixture press-molded; or the powder is mixed with Nylon or a similar resin and the resultant mixture injection- molded, to thereby produce a bonded magnet.
- the production method for R-T-B type magnet alloy ingot of the present invention attains productivity higher than that attained by the aforementioned ultra-rapid-cooling production method, thereby providing low-price R-T-B type bonded magnet alloy powder.
- casting is continued while rare earth alloy deposited on the inner wall surface of the mold are scraped by use of a scraper or a similar device, thereby producing flat rare earth alloy flakes having a maximum length of 5 cm and a thickness of 1 mm or less.
- the flakes are heat-treated at 400 to 1 ,000°C in vacuum or in an inert gas atmosphere, to thereby enhance coercive force and squareness properties.
- the flakes are heat-treated at 1 ,000 to 1,100°C in vacuum or in an inert gas atmosphere and, subsequently, at 400 to 1 ,000°C in vacuum or in an inert gas atmosphere, to thereby further enhance magnetization and coercive force.
- the R-T-B type alloy flakes contain crystal grains, most of which are minute. Thus, even when the alloy flakes are pulverized, magnetic characteristics are not greatly deteriorated.
- the flakes are pulverized to a particle size of 500 ⁇ m or less, and the powder is mixed with an epoxy resin or a similar resin and the resultant mixture press-molded; or the powder is mixed with Nylon or a similar resin and the resultant mixture injection-molded, to thereby produce a bonded magnet. If the bonded magnets are produced by pulverizing alloy flakes is preferable because low-price alloy powder can be provided by virtue of high pulverization efficiency, as compared with pulverization of alloy ingots and obtaining the bonded magnets.
- the production method for rare earth alloy of the present invention can provide an R-T-B TYPE exchange spring magnet alloy ingot comprising at least one element selected from among Nd, Pr, and Dy in a total amount of 1 to 12% by atom and B in an amount of 3 to 30% by atom, with a balance being T (T represents a substance predominantly comprising Fe, with a portion of Fe atoms being optionally substituted by Co, Ni, Cu, Al, Ga, Cr, and Mn.); containing crystal grains of the hard magnetic phase and the soft magnetic phase having a crystal grain size of 1 ⁇ m or less in a total volume of at least 50%), preferably at least 70%, more preferably at least 80%, on the basis of the entire volume of the alloy.
- the thickness of the alloy ingot is 1 mm or greater, preferably 5 mm or greater, and even more preferably 10 mm or greater.
- the R-T-B type exchange spring magnet of the present invention contains a hard magnetic phase formed of R 2 T ) B, exhibiting large anisotropic magnetic field, and a soft magnetic phase formed of at least one species selected from among Fe, Fe 2 B, and Fe 3 B, exhibiting high saturation magnetization.
- high-melting-point metals such as Ti, V, Cr, Mn, Zr, Nb, Mo, Hf, Ta, and W may be added.
- the total amount of the metals is preferably regulated to 1% by weight or less so as to prevent deterioration in magnetization.
- the rate of rotation of the mold is preferably regulated to generate centrifugal force of at least 2G, more preferably at least 5Q most preferably at least 10G, such that the cooling effect is increased by bringing the molten metal into contact with the inner wall of the mold.
- the rate of rotation of the rotary body is preferably regulated to impart, to the molten metal, centrifugal force of at least 5G, more preferably at least 20G, most preferably at least 30G, such that collision of the molten metal with the inner wall surface of the mold is intensified, to thereby increase the solidification rate of the molten metal.
- Rate of deposition of a molten metal on the inner wall surface of the mold is also critical.
- the average deposition rate for increasing the cooling rate of the deposited molten metal is 0.1 mm/sec or less, preferably 0.05 mm/sec or less, more preferably 0.03 mm/sec or less.
- the R-T-B type exchange spring magnet alloy ingot is heat-treated at 400 to 1 ,000°C in vacuum or in an inert gas atmosphere, to thereby enhance coercive force and squareness properties.
- the exchange spring magnet alloy ingot of the present invention exhibits large percent spring-back; i.e., even when magnetization decreases in a reverse magnetic field, magnetization is almost completely restored to the initial value through controlling the magnetic field to 0.
- the alloy also exhibits excellent magnetic characteristics isotropically at an ingot state. Therefore, exchange spring magnets exhibiting excellent magnetic characteristics isotropically can be produced only through mechanical processing; e.g., cutting, grinding, polishing, or blanking, of an alloy ingot to form a predetermined shape. Briefly, steps of pulverization and press molding or injection molding, which are required for producing the conventional bonded magnets can be omitted, thereby reducing production costs.
- the magnets produced through mechanical processing have a density higher than that of bonded magnets, strong magnets exhibiting high magnetization can be produced.
- the R-T-B type exchange spring magnets of a cylindrical shape can be produced directly from a molten metal.
- the outer diameter of the cylindrical magnets is preferably controlled to 100 mm or more.
- anisotropy can be provided.
- methods of deformation include die-upsetting, rolling, forging, and pressing.
- the temperature of deformation is preferably 400 to
- the pressure required for deformation is at least
- the exchange spring magnet of the present invention contains a rare earth component and Fe, which are highly prone to oxidization.
- the magnet is preferably coated with a resin or a metal such as Ni or Al. More preferably, the magnet is sequentially coated with a resin and a metal.
- the aforementioned exchange spring magnet alloy ingot of the present invention contains crystal grains, most of which are minute. Thus, even when the alloy ingot is pulverized, magnetic characteristics are not greatly deteriorated.
- the ingot is pulverized to a particle size of 500 ⁇ m or less, and the powder is mixed with an epoxy resin or a similar resin and the resultant mixture press-molded; or the powder is mixed with Nylon or a similar resin and the resultant mixture injection-molded, to thereby produce a bonded magnet.
- the exchange spring magnet alloy ingot is produced by the production method of the present invention, the alloy attains productivity higher than that attained by the aforementioned ultra-rapid-cooling production method, thereby providing low-price alloy powder.
- Elemental neodymium, ferroboron, cobalt, aluminum, copper, and iron were mixed so as to obtain the following composition: Nd: 30.0%) by mass; B: 1.00% by mass; Co: 1.0% by mass; Al: 0.30% by mass; and Cu: 0.10%) by mass, a balance being iron.
- the resulting mixture was melted in an alumina crucible in an argon gas atmosphere at 1 atm by use of a high-frequency induction melting furnace.
- the resulting molten mixture was subjected to casting by use of the apparatus shown in FIG. 2.
- the mold has an inside diameter of 500 mm and a length of 500 mm, and grooves shown in FIG. 7 having a depth of 1 mm and a bottom width of 5 mm are provided with intervals of 3 mm in the inner surface of the mold.
- the rotary receptacle has an inside diameter of 250 mm and eight holes of 2 mm in diameter formed in the surrounding wall of the receptacle.
- the angle ⁇ formed by the axis of rotation of the rotary receptacle and the axis of rotation of the mold was fixed to 25°, and the average molten metal deposition rate for deposition on the inner wall of the mold was 0.01 cm/sec.
- the rotational speed of the mold was set to 189 rpm so as to generate a centrifugal force of lOG.
- the rotational speed of the rotary receptacle was 535 rpm so as to impose a centrifugal force of about 40G on molten metal.
- the thus-obtained alloy ingot had a thickness of 6 to 8 mm as measured at a central portion of the cylindrical mold and a thickness of 11 to 13 mm as measured at thickest portions located in the vicinity of opposite end portions.
- the micro-structure of the cross section was observed as a back-scattered electron image under an electron microscope. The results are shown in Table 1.
- Elemental neodymium, ferroboron, cobalt, aluminum, copper, and iron were mixed so as to obtain the following composition: Nd: 28.0% by mass; B: 1.00% by mass; Co: 1.0% by mass; Al: 0.30% by mass; and Cu: 0.10% by mass, a balance being iron.
- the resulting mixture was melted in an alumina crucible in an argon gas atmosphere at 1 atm by use of a high-frequency induction melting furnace.
- the resulting molten mixture was subjected to casting by use of the apparatus shown in FIG. 2.
- a mold and a rotary receptacle having the same dimensions as those of Example 1 were employed. However, the inner surface of the mold was smooth, and the rotational speed of the mold was set to 231 rpm so as to generate a centrifugal force of 15G.
- a mixture having a composition similar that of the alloy of Example 1 was prepared, and the mixture was melted in a manner similar to that of Example 1 and cast by use of a casting apparatus similar to that employed in Example 1.
- the inner surface of the mold had no grooves, and the surface was polished to be smooth in advance by use of sand paper (No. 240).
- the rotational speed of the mold was adjusted so as to generate a centrifugal force of 2.5G
- the alloy ingot obtained through the above casting had a thickness of 7 to 8 mm as measured at a central portion of the cylindrical mold and a thickness of 12 to 13 mm as measured at thickest portions located in the vicinity of opposite end portions.
- the micro-structure of the cross section was observed as a back-scattered electron image. The results are shown in Table 1.
- a mixture having a composition similar that of the alloy of Example 1 was prepared, and the mixture was melted under argon at 1 atm and cast by use of a casting apparatus shown in FIG. 8 for the SC method.
- the water-cooling copper roller 23 had an outer diameter of 400 mm, and the roller was rotated at a peripheral velocity of 1 m/s, thereby yielding a flaky alloy ingot having a mean thickness of 0.32 mm.
- the micro-structure of the cross section of the thus-obtained alloy ingot was observed as a back-scattered electron image. The results are shown in Table 1.
- Example 3 describes a production example of sintered magnets.
- the alloy flakes produced in Example 1 were pulverized in the order of hydrogen decrepitation, intermediate pulverization, and micro-pulverization.
- Hydrogen absorption step the first step of hydrogen decrepitation was performed under the conditions: 100% hydrogen atmosphere, atmospheric pressure, and retention time of 1 hour.
- the temperature of the metal flakes at the start of hydrogen absorption reaction was 25°C.
- Hydrogen desorption step subsequent step was performed under the conditions: vacuum of 0.13 hPa, 500°C, and retention time of 1 hour.
- Intermediate pulverization was performed by use of a Brawn mill, and the hydrogen-decrepitated powder was pulverized in a 100%) nitrogen atmosphere to a particle size of 425 ⁇ m or less.
- zinc stearate powder was added in an amount of 0.07% by mass.
- the mixture was sufficiently mixed in a 100% nitrogen atmosphere by use of a V-blender, and then micro-pulverized by use of a jet mill in a nitrogen atmosphere incorporated with oxygen (4,000 ppm), to a particle size of 3.2 ⁇ m (FSSS).
- the resultant powder was sufficiently mixed again in a 100% nitrogen atmosphere by use of a V-blender.
- the obtained powder was found to have an oxygen concentration of 2,500 ppm.
- the zinc stearate content of the powder was calculated to be 0.05% by mass.
- the thus-obtained powder was press-molded in a 100% nitrogen atmosphere and a lateral magnetic field by use of a molding apparatus.
- the molding pressure was 1.2 t/cm , and the magnetic field in the mold cavity was controlled to 15 kOe.
- the thus-obtained compact was maintained sequentially in vacuum of 1.33 x 10 "5 hPa at 500°C for one hour and in vacuum of 1.33 x 10 "5 hPa at 800°C for two hours, and was further maintained in vacuum of 1.33 x 10 "5 hPa at 1,060°C for two hours for sintering.
- the density of the sintered product was as sufficiently high as 7.5 g/cm or more.
- the sintered product was further heat-treated at 540°C for one hour in an argon atmosphere. Magnetic characteristics of the sintered product were measured by means of a direct-current BH curve tracer, and the results are shown in Table 2.
- a cross-section of the sintered product was mirror-polished, and the polished surface was observed under a polarizing microscope.
- the obtained mean crystal grain size was 15 to 20 ⁇ m, with substantial homogeneity in size.
- each of the alloy flakes produced in Comparative Examples 1 and 2 was pulverized in a manner similar to that of Example 3, to thereby produce a powder having a particle size of 3.3 ⁇ m (FSSS).
- the powder was found to have an oxygen concentration of 2,600 ppm.
- each powder was molded in a magnetic field and sintered, to thereby produce an anisotropic magnet. Magnetic characteristics of the thus-produced sintered magnets are shown in Table 2.
- Table 2 indicates that the magnet produced in Comparative Example 3 exhibits a coercive force (iHc) lower, by 2 kOe or more, than that of the magnet produced in Example 3, conceivably due to a poor dispersion state of R-rich phase.
- the magnet produced in Comparative Example 4 exhibits a Br as low as 0.15 kG conceivably due to crystal orientation inferior to that of the alloy of the present invention.
- Elemental neodymium, elemental praseodymium, ferroboron, aluminum, electrolytic copper, electrolytic cobalt, and electrolytic iron were mixed so as to obtain the following composition: Nd: 10.4% by atom (23.0% by mass); Pr: 3.2% by atom (7.0% by mass); B: 6.0% by atom (1.0% by mass); Al: 0.7% by atom (0.30% by mass); Cu: 0.1% by atom (0.10% by mass); Co: 1.1% by atom (1.0% by mass); and a balance of iron.
- the resulting mixture was melted in an alumina crucible in an argon gas atmosphere through high-frequency induction melting.
- the resulting molten mixture was subjected to casting under the following conditions using the device shown in FIG. 2.
- the cylindrical mold which is made of iron (thermal conductivity at 27°C: 80.3 W/mK) has an inside diameter of 500 mm and a length of 500 mm.
- Coating film thermal conductivity at 27°C: 12.6 W/mK
- the rotary body was a cylindrical receptacle having an inside diameter of 250 mm and eight holes of 3 mm in diameter formed in the surrounding wall of the receptacle.
- the axis L of rotation of the cylindrical mold is set to the horizontal direction.
- the angle ⁇ of inclination formed by the axis R of rotation of the receptacle and the axis L of rotation of the cylindrical mold was fixed to 25° during molding, and the average molten metal deposition rate for deposition on the inner wall of the mold was adjusted to 0.05 mm/sec.
- the rotational speed of the mold was controlled so as to generate a centrifugal acceleration of lOG
- the rotational speed of the rotary receptacle was controlled so as to impose a centrifugal force of about 20G on molten metal.
- the thus-obtained alloy ingot had a thickness of 8 mm as measured at a central portion of the cylindrical mold and about 10 mm as measured at thickest portions located in the vicinity of opposite end portions.
- a cross section of the alloy ingot was observed under a polarizing microscope for determining the crystal grain size. Through observation, the percent area in which the crystal grain size of 10 ⁇ m or less occupied was found to be 95%.
- Example 5 The same materials were mixed so as to obtain the composition similar to that of the alloy produced in Example 4.
- the resulting mixture was melted in an alumina crucible in an argon gas atmosphere through high-frequency induction melting.
- the resulting molten mixture was subjected to casting by use of the apparatus and under the conditions similar to those employed in Example 4.
- boron nitride (BN) film instead of the above coating film, was provided in a thickness of 10 ⁇ m through spray coating on the inner wall surface of the mold.
- a cross section of the thus-obtained alloy ingot was observed under a polarizing microscope for determining the crystal grain size. Through observation, the percent area in which the crystal grain size of 10 ⁇ m or less occupied was found to be 88%.
- Elemental neodymium, ferroboron, and electrolytic iron were mixed so as to obtain the following composition: Nd: 4.6% by atom (12.5% by mass); B: 15.2% by atom (3.1 % by mass); and a balance of iron.
- Nd 4.6% by atom (12.5% by mass
- B 15.2% by atom (3.1 % by mass)
- a balance of iron The resulting mixture was melted in an alumina crucible in an argon gas atmosphere through high-frequency induction melting.
- the resulting molten mixture was subjected to casting by use of the apparatus shown in FIG. 2 and under the conditions described below.
- the cylindrical mold which is made of iron (thermal conductivity at 27°C: 80.3 W/mK) has an inside diameter of 500 mm and a length of 500 mm.
- Coating film thermal conductivity at 27°C: 12.6 W/mK
- the rotary body was a cylindrical receptacle having an inside diameter of 250 mm and eight holes of 2 mm in diameter formed in the surrounding wall of the receptacle.
- the axis L of rotation of the cylindrical mold is set to the horizontal direction.
- the angle ⁇ of inclination formed by the axis R of rotation of the rotary receptacle and the axis L of rotation of the cylindrical mold was fixed to 25° during molding.
- the average molten metal deposition rate for deposition on the inner wall of the mold was adjusted to 0.02 mm/sec.
- the rotational speed of the mold was controlled so as to generate a centrifugal acceleration of 20G.
- the rotational speed of the rotary receptacle was controlled so as to impose a centrifugal force of about 40G on molten metal.
- a cross section of the thus-obtained alloy ingot was observed under a polarizing microscope for determining the crystal grain size. Through observation, the percent area in which the crystal grain size of 1 ⁇ m or less occupied was found to be 65%.
- Example 4 The same materials were mixed so as to obtain the composition similar to that of the alloy produced in Example 4.
- the resulting mixture was melted in an alumina crucible in an argon gas atmosphere through high-frequency induction melting.
- the resulting molten mixture was subjected to casting by use of the apparatus and under the conditions similar to those employed in Example 4. However, no coating film was provided on the inner wall surface of the mold, and the molten alloy was deposited and solidified directly on the inner wall surface of the iron mold.
- a cross section of the thus-obtained alloy ingot was observed under a polarizing microscope for determining the crystal grain size. Through observation, a large number of columnar crystals having a major size of 1 mm or more were observed, and the percent area in which the crystal grain size of 10 ⁇ m or less occupied was found to be as low as 3%.
- Example 6 The same materials were mixed so as to obtain the composition similar to that of the alloy produced in Example 6.
- the resulting mixture was melted in an alumina crucible in an argon gas atmosphere through high-frequency induction melting.
- the resulting molten mixture was subjected to casting by use of the apparatus and under the conditions similar to those employed in Example 4. However, no coating film was provided on the inner wall surface of the mold, and the molten alloy was deposited and solidified directly on the inner wall surface of the iron mold.
- a cross section of the thus-obtained alloy ingot was observed under a polarizing microscope for determining the crystal grain size. Through observation, a large number of columnar crystals having a major size of 1 mm or more were observed.
- the alloy ingot of Example 4 was pulverized to 500 ⁇ m or less in an argon gas atmosphere by use of a stamp mill, and iHc of the resultant powder was found to be 9.5 kOe as measured by means of a vibrating sample magnetometer (VSM), indicating a small decrease in iHc.
- VSM vibrating sample magnetometer
- the alloy powder was mixed with epoxy resin (3%> by weight), and the resultant mixture was press-formed at 6 ton/cm 2 in an argon gas atmosphere.
- the resultant compact was fired at 180°C in an argon gas atmosphere, to thereby cure the epoxy resin. After completion of curing, the density of the product was found to be 5.8 g/cm 3 .
- Example 8 The alloy ingot of Example 8 was pulverized to 500 ⁇ m or less in an argon gas atmosphere by use of a stamp mill, and iHc of the resultant powder was found to be 10.5 kOe as measured by means of a VSM, indicating a small decrease in iHc.
- the alloy ingot of Example 10 was pulverized to 500 ⁇ m or less in an argon gas atmosphere by use of a stamp mill, and iHc of the resultant powder was found to be 10.7 kOe as measured by means of a VSM, indicating a small decrease in iHc.
- the alloy ingot of Comparative Example 4 was pulverized to 500 ⁇ m or less in an argon gas atmosphere by use of a stamp mill, and iHc of the resultant powder was found to be as low as 0.4 kOe as measured by means of a vibrating sample magnetometer (VSM).
- VSM vibrating sample magnetometer
- each of the starting materials of metal neodymium, ferro-boron, aluminum, electrolytic copper, ferro-niobium, electrolytic iron were mixed, and melted by high frequency induction heating using an alumina crucible in an argon gas atmosphere, and then casting was carried out using the same apparatus and conditions as were used in Example 5.
- a portion having a thickness of 16 to 18 mm was cut out from the alloy ingot of Example 12, and was enclosed in an evacuated iron vessel having a thickness of 3.2 mm.
- the iron vessel in which this alloy ingot was enclosed was placed in an atmospheric oven set at 800°C, sufficiently heated, and then rolled by passing between rollers set to have a draft of 30%. Thereafter, the vessel was returned to the atmospheric oven maintained at 800°C, sufficiently heated, and then rolled again with the interval between the rollers reduced with a draft of 30%. This rolling operation was repeated for a total of 4 times, and the alloy ingot was rolled to a thickness of 4.0 mm. Two pieces of this alloy ingot were laminated together and processed to give a cube having sides of 7 mm.
- Example 13 The alloy ingot which was hot rolled in Example 13 was heat treated for 1 hour at 550°C in a vacuum. Thereafter, two pieces of this alloy ingot were laminated together and processed to give a cube having sides of 7 mm.
- Example 15 The alloy ingot which was hot rolled in Example 13 was heat treated for 2 hours at 1,020°C in a vacuum, and then further heat treated for 1 hour at 550°C in a vacuum. Thereafter, two pieces of this alloy ingot were laminated together and processed to give a cube having sides of 7 mm.
- the alloy ingot of Example 6 was crushed to 500 ⁇ m or less in an argon gas atmosphere using a stamp mill.
- the iHc measured using VSM was 2.9 kOe, and degradation in the iHc was low.
- Example 6 The alloy ingot of Example 6 was heat treated for 5 minutes at 750°C in a vacuum.
- the alloy ingot of Example 17 was crushed to 500 ⁇ m or less in an argon gas atmosphere using a stamp mill.
- the iHc measured using VSM was 4.0 kOe, and degradation in the iHc was low.
- composition comprise Nd: 10.8% by atom (23.5% by mass), Pr: 3.3% by atom (7.0% by mass), Dy: 0.6% by atom (1.5% by mass), B: 6.1% by atom (1.0% by mass), Al: 0.7% by atom (0.30% by mass), Co: 1.1% by atom (1.0% by mass), Cu: 0.1% by atom (0.1% by mass), Zr: 0.4% by atom (0.5%) by mass), and the remainder iron, each of the starting materials of metal neodymium, metal praseodymium, metal dysprosium, ferro-boron, aluminum, electrolytic cobalt, electrolytic copper, ferro-zirconium, and electrolytic iron were mixed, and melted by high frequency induction heating using an alumina crucible in an argon gas atmosphere, and then a cylindrically shaped alloy ingot was obtained by casting under the following conditions.
- the cylindrical mold was made of copper (thermal conductivity at 27°C is 398 W/mK) and had an internal diameter of 150 mm and a length of 150 mm.
- the rotating body was a cylindrical vessel with an internal diameter of 50 mm, and 8 holes having diameters of 3 mm were formed in the side walls.
- the rotation axis L of the cylindrical mold and the rotation axis R of the vessel were both arranged in the vertical direction.
- the average rate of deposition of the molten metal on the inner wall of the mold was 0.05 mm/second.
- the number of rotations of the mold in this case was set to produce a centrifugal acceleration of 20G, and the rate of rotation of the vessel form rotating body exert a centrifugal force of approximately 10G on the molten metal.
- the rotating vessel was moved back and forth over a distance of 50 mm in the vertical direction in a 4 second cycle.
- the exterior of the cylindrically shaped alloy ingot was 150 mm, the thickness at the center section along the longitudinal axis was 8 mm, and the thickness was approximately 10 mm at the thickest sections in the vicinity of both edges.
- the area occupied by crystals having a particle size of 10 ⁇ m or less was 96%.
- a cube have sides of 7 mm was cut out from the alloy ingot and the magnetic properties were measured using a BH curve tracer.
- each of the raw materials were mixed such that the composition was the same as the composition of Example 19, and melted by high frequency induction heating using an alumina crucible in an argon gas atmosphere, and casting was carried out using the same apparatus and under the same conditions as used in Example 19.
- the exterior of the obtained cylindrically shaped alloy ingot was 150 mm, the thickness at the center section along the longitudinal axis was 8 mm, and the thickness was approximately 10 mm at the thickest sections in the vicinity of both edges.
- the area occupied by crystals having a particle size of 10 ⁇ m or less was 5%.
- Example 21
- cylindrical shaped alloy ingot manufactured using the same composition under the same conditions as in Example 19 was heat treated for 2 hours at 1 ,020°C in an argon atmosphere, and then further heat treated for 1 hour at 550°C in a vacuum.
- Example 4 Casting was carried out using the same composition under the same conditions as in Example 4, and using the same apparatus as used in Example 4. However, a cylindrical copper mold (thermal conductivity at 27°C is 80.3 W/mK) was used in which grooves of a depth of 1 mm with a base of a width of 5 mm had been cut at 3 mm intervals in the inner surface wall, and on which a film having a thickness of 100 ⁇ m and a composition of SUS304 (thermal conductivity at 27°C is 16.0 W/mK) had been formed by means of plasma spraying, thereafter.
- a cylindrical copper mold thermal conductivity at 27°C is 80.3 W/mK
- SUS304 thermal conductivity at 27°C is 16.0 W/mK
- the thickness of the obtained alloy ingot was 8 mm at the center section of the cylindrical mold, and approximately 10 mm at the thickest sections in the vicinity of both edges.
- the area occupied by crystals having a particle size of 10 ⁇ m or less was 98%.
- Example 19 Using the apparatus used in Example 19, a cylindrically shaped alloy ingot was obtained by mixing alloy starting materials to obtain the same composition as in Example 6, and using the same conditions as in Example 19. However, the average rate of deposition of the molten metal on the inner wall of the mold was 0.02 mm/second.
- the exterior of the obtained cylindrically shaped alloy ingot was 150 mm, the thickness at the center section along the longitudinal axis was 8 mm, and the thickness was approximately 10 mm at the thickest sections in the vicinity of both edges.
- the area occupied by crystals having a particle size of 1 ⁇ m or less was 65%.
- the area occupied by crystals having a particle size of 1 ⁇ m or less was 65%.
- Alloy starting materials were mixed to obtain the same composition as in Example 4, and melted by high frequency induction heating using an alumina crucible in an argon gas atmosphere, and then casting was conducted under the following conditions.
- the cylindrical mold was made of iron (thermal conductivity at 27°C is 80.3 W/mK) and had an internal diameter of 600 mm and a length of 600 mm.
- the rotating body was a cylindrical vessel with an internal diameter of 250 mm, and 8 holes having diameters of 3 mm were formed in the side walls.
- the rotation axis L of the cylindrical mold was in the horizontal direction and the inclined angle ⁇ formed by the rotation axis R of the vessel and the rotation axis L of the cylindrical mold was fixed at 25°.
- a scraper was installed on the inner wall of the mold so as to make contact with the leading edge.
- a metal plate guard wall having a thickness of 5 mm was arranged on the scraper side of the rotating body to prevent the direct deposition of the molten metal onto the scraper itself during casting.
- the average rate of deposition of the molten metal onto the inner wall of the mold was 0.05 mm/second.
- the number of rotations of the mold was set so that the centrifugal acceleration was lOG, and the rate of rotation of the vessel form rotating body exerted a centrifugal force of approximately 20G on the molten metal.
- the size of the obtained alloy flakes was of the order of 5 mm and the thickness was about 50 to 100 ⁇ m.
- the area occupied by crystals having a particle size of 10 ⁇ m or less was 95%>.
- the alloy flakes of Example 25 was heat treated for 1 hour at 550°C in a vacuum.
- the iHc of this heat treated alloy flakes was measured by VSM and found to be 10.2 kOe.
- This alloy flakes was crushed to 500 ⁇ m or less in an argon gas atmosphere using a stamp mill, and thereafter, a bonded magnet having a density of 5.8 g/cm 3 was prepared using the same method as used in Example 7.
- the alloy flakes of Example 25 was heat treated for 2 hours at 1,020°C in an argon atmosphere, and thereafter it was heat treated for 1 hour at 550°C in a vacuum.
- the iHc of this heat treated alloy flakes was measured by VSM and found to be 11.3 kOe.
- This alloy flakes was crushed to 500 ⁇ m or less in an argon gas atmosphere using a stamp mill, and there after, a bonded magnet having a density of 5.8 g/cm 3 was prepared using the same method as used in Example 7.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Crystallography & Structural Chemistry (AREA)
- Organic Chemistry (AREA)
- Metallurgy (AREA)
- Materials Engineering (AREA)
- Nanotechnology (AREA)
- Inorganic Chemistry (AREA)
- Power Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Composite Materials (AREA)
- Manufacturing Cores, Coils, And Magnets (AREA)
- Hard Magnetic Materials (AREA)
- Powder Metallurgy (AREA)
Applications Claiming Priority (12)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2001266278A JP4754739B2 (ja) | 2001-09-03 | 2001-09-03 | 希土類磁石用合金塊、その製造方法および焼結磁石 |
JP2001-266278 | 2001-09-03 | ||
US32274801P | 2001-09-18 | 2001-09-18 | |
US60322,748 | 2001-09-18 | ||
JP2002-065263 | 2002-03-11 | ||
JP2002065263 | 2002-03-11 | ||
US36772002P | 2002-03-28 | 2002-03-28 | |
US60/367,720 | 2002-03-28 | ||
JP2002-195404 | 2002-06-04 | ||
JP2002195404A JP4213417B2 (ja) | 2002-03-11 | 2002-07-04 | 希土類合金の製造方法、r−t−b系磁石用合金塊、r−t−b系磁石、r−t−b系ボンド磁石、r−t−b系交換スプリング磁石用合金塊、r−t−b系交換スプリング磁石、およびr−t−b系交換スプリングボンド磁石 |
US39675402P | 2002-07-19 | 2002-07-19 | |
US60/396,754 | 2002-07-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2003020993A1 true WO2003020993A1 (en) | 2003-03-13 |
Family
ID=27554993
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2002/008931 WO2003020993A1 (en) | 2001-09-03 | 2002-09-03 | Rare earth magnet alloy ingot, manufacturing method for the same, r-t-b type magnet alloy ingot, r-t-b type magnet, r-t-b type bonded magnet, r-t-b type exchange spring magnet alloy ingot, r-t-b type exchange spring magnet, and r-t-b type exchange spring bonded magnet |
Country Status (2)
Country | Link |
---|---|
CN (1) | CN100591788C (zh) |
WO (1) | WO2003020993A1 (zh) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2005098878A2 (en) * | 2004-04-07 | 2005-10-20 | Showa Denko K.K. | Alloy lump for r-t-b type sintered magnet, producing method thereof, and magnet |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8907755B2 (en) * | 2012-03-30 | 2014-12-09 | Toda Kogyo Corporation | R-T-B-based rare earth magnet particles, process for producing the R-T-B- based rare earth magnet particles, and bonded magnet |
CN103769595A (zh) * | 2013-11-26 | 2014-05-07 | 王利民 | 一种制备微晶和非晶态粉末材料的方法 |
CN103769596A (zh) * | 2013-11-26 | 2014-05-07 | 王利民 | 一种制备高堆积密度扁圆形状粉末材料的方法 |
CN103632834B (zh) * | 2013-12-03 | 2015-12-02 | 江苏大学 | 一种高性能各向异性钕铁硼磁体的制备方法 |
CN103801669B (zh) * | 2014-01-16 | 2016-01-20 | 厦门钨业股份有限公司 | 离心铸造方法及其设备和工艺 |
CN105817632A (zh) * | 2015-01-09 | 2016-08-03 | 中国科学院宁波材料技术与工程研究所 | 片状粉末的制备装置及方法 |
JP7087558B2 (ja) * | 2018-03-29 | 2022-06-21 | セイコーエプソン株式会社 | 軟磁性粉末および焼結体の製造方法 |
CN111029128A (zh) * | 2019-12-31 | 2020-04-17 | 浙江大学 | 一种稀土永磁的快速热处理方法 |
CN113579191A (zh) * | 2021-08-31 | 2021-11-02 | 深圳市金鼎丰贵金属设备科技有限公司 | 一种金属薄片制造装置 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH07109504A (ja) * | 1993-10-06 | 1995-04-25 | Sumitomo Special Metals Co Ltd | 異方性ボンド磁石用原料粉末の製造方法 |
EP0924717A2 (en) * | 1997-12-22 | 1999-06-23 | Shin-Etsu Chemical Co., Ltd. | Rare earth-iron-boron permanent magnet and method for the preparation thereof |
EP1118601A1 (en) * | 1998-06-22 | 2001-07-25 | Showa Denko Kabushiki Kaisha | Refractory for casting rare earth alloy and method for producing the same and method for casting rare earth alloy |
JP2002301554A (ja) * | 2000-08-31 | 2002-10-15 | Showa Denko Kk | 遠心鋳造方法、遠心鋳造装置、それにより製造した合金 |
-
2002
- 2002-09-03 WO PCT/JP2002/008931 patent/WO2003020993A1/en active Application Filing
- 2002-09-03 CN CN02817079A patent/CN100591788C/zh not_active Expired - Fee Related
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH07109504A (ja) * | 1993-10-06 | 1995-04-25 | Sumitomo Special Metals Co Ltd | 異方性ボンド磁石用原料粉末の製造方法 |
EP0924717A2 (en) * | 1997-12-22 | 1999-06-23 | Shin-Etsu Chemical Co., Ltd. | Rare earth-iron-boron permanent magnet and method for the preparation thereof |
EP1118601A1 (en) * | 1998-06-22 | 2001-07-25 | Showa Denko Kabushiki Kaisha | Refractory for casting rare earth alloy and method for producing the same and method for casting rare earth alloy |
JP2002301554A (ja) * | 2000-08-31 | 2002-10-15 | Showa Denko Kk | 遠心鋳造方法、遠心鋳造装置、それにより製造した合金 |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2005098878A2 (en) * | 2004-04-07 | 2005-10-20 | Showa Denko K.K. | Alloy lump for r-t-b type sintered magnet, producing method thereof, and magnet |
WO2005098878A3 (en) * | 2004-04-07 | 2006-02-02 | Showa Denko Kk | Alloy lump for r-t-b type sintered magnet, producing method thereof, and magnet |
US7594972B2 (en) | 2004-04-07 | 2009-09-29 | Showda Denko K.K. | Alloy lump for R-T-B type sintered magnet, producing method thereof, and magnet |
Also Published As
Publication number | Publication date |
---|---|
CN100591788C (zh) | 2010-02-24 |
CN1549867A (zh) | 2004-11-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7431070B2 (en) | Rare earth magnet alloy ingot, manufacturing method for the same, R-T-B type magnet alloy ingot, R-T-B type magnet, R-T-B type bonded magnet, R-T-B type exchange spring magnet alloy ingot, R-T-B type exchange spring magnet, and R-T-B type exchange spring bonded magnet | |
US7442262B2 (en) | Alloy flake for rare earth magnet, production method thereof, alloy powder for rare earth sintered magnet, rare earth sintered magnet, alloy powder for bonded magnet and bonded magnet | |
JP5510457B2 (ja) | R−t−b系焼結磁石の製造方法 | |
EP1780736B1 (en) | R-T-B type alloy, production method of R-T-B type alloy flake, fine powder for R-T-B type rare earth permanent magnet, and R-T-B type rare earth permanent magnet | |
EP0886284B1 (en) | Cast alloy used for production of rare earth magnet and method for producing cast alloy and magnet | |
US7264683B2 (en) | Centrifugal casting method, centrifugal casting apparatus, and cast alloy produced by same | |
US7594972B2 (en) | Alloy lump for R-T-B type sintered magnet, producing method thereof, and magnet | |
EP1479787B1 (en) | Sinter magnet made from rare earth-iron-boron alloy powder for magnet | |
JP2017139259A (ja) | R−t−b系焼結磁石用合金、及びr−t−b系焼結磁石 | |
JP4879503B2 (ja) | R−t−b系焼結磁石用合金塊、その製造法および磁石 | |
JPH1036949A (ja) | 希土類磁石用合金及びその製造方法 | |
WO2003020993A1 (en) | Rare earth magnet alloy ingot, manufacturing method for the same, r-t-b type magnet alloy ingot, r-t-b type magnet, r-t-b type bonded magnet, r-t-b type exchange spring magnet alloy ingot, r-t-b type exchange spring magnet, and r-t-b type exchange spring bonded magnet | |
JP4479944B2 (ja) | 希土類磁石用合金薄片およびその製造方法 | |
WO2002072900A2 (en) | Method for controlling structure of rare earth element-containing alloy, powder material of the alloy and magnet using the same | |
EP1632299A1 (en) | Method for producing rare earth based alloy powder and method for producing rare earth based sintered magnet | |
JP4213417B2 (ja) | 希土類合金の製造方法、r−t−b系磁石用合金塊、r−t−b系磁石、r−t−b系ボンド磁石、r−t−b系交換スプリング磁石用合金塊、r−t−b系交換スプリング磁石、およびr−t−b系交換スプリングボンド磁石 | |
JP2003183787A (ja) | 希土類磁石用主相系合金、その製造方法、希土類焼結磁石用混合粉末および希土類磁石 | |
JP2002301554A (ja) | 遠心鋳造方法、遠心鋳造装置、それにより製造した合金 | |
JP4754739B2 (ja) | 希土類磁石用合金塊、その製造方法および焼結磁石 | |
JP2004330279A (ja) | 希土類含有合金薄片の製造方法、希土類磁石用合金薄片、希土類焼結磁石用合金粉末、希土類焼結磁石、ボンド磁石用合金粉末、及びボンド磁石 | |
EP1652606B1 (en) | Centrifugal casting method, centrifugal casting apparatus, and cast alloy produced by same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BY BZ CA CH CN CO CR CU CZ DE DM DZ EC EE ES FI GB GD GE GH HR HU ID IL IN IS KE KG KR KZ LC LR LS LT LU LV MA MD MG MK MN MX MZ NO NZ OM PH PL PT RO RU SE SG SI SK SL TJ TM TN TR TT TZ UG UZ VC VN YU ZA ZM Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS KE KG KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR IE IT LU MC NL PT SE SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ UG ZM ZW AM AZ BY KG KZ RU TJ TM AT BE BG CH CY CZ DK EE ES FI FR GB GR IE IT LU MC PT SE SK TR BF BJ CF CG CI GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 20028170792 Country of ref document: CN |
|
122 | Ep: pct application non-entry in european phase |