WO2000031206A1 - Pompe a chaleur chimique utilisant une substance solide - Google Patents

Pompe a chaleur chimique utilisant une substance solide Download PDF

Info

Publication number
WO2000031206A1
WO2000031206A1 PCT/SE1999/002187 SE9902187W WO0031206A1 WO 2000031206 A1 WO2000031206 A1 WO 2000031206A1 SE 9902187 W SE9902187 W SE 9902187W WO 0031206 A1 WO0031206 A1 WO 0031206A1
Authority
WO
WIPO (PCT)
Prior art keywords
substance
layer
heat pump
heat
slurry
Prior art date
Application number
PCT/SE1999/002187
Other languages
English (en)
Inventor
Staffan Jonsson
Ray Olsson
Mona KÅREBRING-OLSSON
Original Assignee
Suncool Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suncool Ab filed Critical Suncool Ab
Priority to AU20130/00A priority Critical patent/AU2013000A/en
Priority to JP2000584023A priority patent/JP2002530619A/ja
Publication of WO2000031206A1 publication Critical patent/WO2000031206A1/fr
Priority to US09/863,406 priority patent/US20020017380A1/en

Abstract

Cette invention concerne une pompe à chaleur chimique dans laquelle on utilise une substance qui entre en interaction de manière efficace avec un liquide volatil tel que de l'eau. Cette substance est choisie en tenant compte, entre autres, de la magnitude de son ΔT et de son contenu énergétique de sorte que la pompe à chaleur puisse être utilisée dans la transformation de l'énergie thermique à basse température, telle que l'énergie solaire, à des fins de réfrigération pour la climatisation, ainsi que dans la production simultanée de chaleur utilisée par exemple pour l'eau chaude dans les habitations. Cette pompe à chaleur peut également être utilisée dans des caissons de réfrigération. Les substances convenables consistent en de l'hydroxyde de baryum, de l'hydroxyde de lithium, du bromure de strontium et du chlorure de cobalt. La substance est appliquée sous forme d'une couche (23) à la surface d'une paroi thermoconductrice (21) en appliquant un mélange de type bouillie de la substance et du liquide, et en le faisant vibrer contre la paroi entre des bords thermoconducteurs (25). Le mélange est séché sous vide, puis chauffé et comprimé simultanément en appliquant une force de pression depuis l'extérieur. On obtient ainsi une couche solide et qui adhère bien d'une substance qui possède une porosité élevée et qui peut résister à un grand nombre de cycles sans aucune dégradation de la structure interne de la couche ni de son adhérence à la paroi et aux bords thermoconducteurs.
PCT/SE1999/002187 1998-11-24 1999-11-24 Pompe a chaleur chimique utilisant une substance solide WO2000031206A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
AU20130/00A AU2013000A (en) 1998-11-24 1999-11-24 A chemical heat pump using a solid substance
JP2000584023A JP2002530619A (ja) 1998-11-24 1999-11-24 固体物質を使用するケミカルヒートポンプ
US09/863,406 US20020017380A1 (en) 1998-11-24 2001-05-24 Chemical heat pump using a solid substance

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
SE9804034A SE513178C2 (sv) 1998-11-24 1998-11-24 Kemisk Värmepump med fast substans
SE9804034-8 1998-11-24

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US09/863,406 Continuation US20020017380A1 (en) 1998-11-24 2001-05-24 Chemical heat pump using a solid substance

Publications (1)

Publication Number Publication Date
WO2000031206A1 true WO2000031206A1 (fr) 2000-06-02

Family

ID=20413404

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE1999/002187 WO2000031206A1 (fr) 1998-11-24 1999-11-24 Pompe a chaleur chimique utilisant une substance solide

Country Status (5)

Country Link
US (1) US20020017380A1 (fr)
JP (1) JP2002530619A (fr)
AU (1) AU2013000A (fr)
SE (1) SE513178C2 (fr)
WO (1) WO2000031206A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002002998A1 (fr) * 2000-07-06 2002-01-10 Thermagen Sa Appareil refrigerant d'adsorption
FR2811412A1 (fr) * 2000-07-06 2002-01-11 Thermagen Dispositif de refrigeration par adsorption
US6895779B2 (en) 2000-11-13 2005-05-24 Thermagen Adsorption refrigerating device
WO2007139476A1 (fr) 2006-05-29 2007-12-06 Climatewell Ab (Publ) Pompe à chaleur chimique fonctionnant avec une substance hybride
JP2013513779A (ja) * 2009-12-09 2013-04-22 クライメイトウエル エービー（パブル） 一体化された化学ヒート・ポンプを備えた太陽熱パネル
EP2225500A4 (fr) * 2007-11-29 2015-08-05 Climatewell Ab Publ Collecteur d'énergie solaire thermique pour produire de la chaleur et/ou un refroidissement

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040231828A1 (en) * 2003-05-22 2004-11-25 Dunne Stephen R. Adsorber generator for use in sorption heat pump processes
JP4938323B2 (ja) * 2006-03-14 2012-05-23 大阪瓦斯株式会社 熱交換型反応器の製造方法
US7439630B2 (en) * 2006-09-08 2008-10-21 Helius Inc. System and methodology for generating electricity using a chemical heat engine and piezoelectric material
US20080078198A1 (en) * 2006-09-28 2008-04-03 Peter James Breiding Microchannel heat exchanger
SE532024C2 (sv) * 2008-02-12 2009-10-06 Climatewell Ab Publ Absorptionsmaskin med inbyggt energilager enligt matrismetoden
EP2321140A1 (fr) * 2008-07-30 2011-05-18 Solaris Synergy Ltd. Système de génération d'énergie solaire photovoltaïque
JP2015127616A (ja) * 2013-12-27 2015-07-09 サンデンホールディングス株式会社 吸着熱交換器及びその吸着熱交換器に用いる吸着フィンの製造方法
US10386100B2 (en) * 2014-11-12 2019-08-20 Carrier Corporation Adsorption system heat exchanger
JP7296207B2 (ja) * 2018-12-20 2023-06-22 三菱重工業株式会社 板状化学蓄熱体
CN111978922B (zh) * 2020-07-31 2021-04-23 西安交通大学 水合盐基中低温化学蓄热材料以及制备方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5054544A (en) * 1989-01-20 1991-10-08 Zeo-Tech (Zeolith-Technologie Gmbh) Sorption container for solid sorption medium
US5291942A (en) * 1993-05-24 1994-03-08 Gas Research Institute Multiple stage sorption and desorption process and apparatus
US5360057A (en) * 1991-09-09 1994-11-01 Rocky Research Dual-temperature heat pump apparatus and system

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4146013A (en) * 1975-10-24 1979-03-27 Foulke Willing B Solar-exothermic solution heat pump
US4441484A (en) * 1977-10-17 1984-04-10 Leonard Greiner Chemical heat pump
DE3408192A1 (de) * 1984-03-06 1985-09-19 Markus 8085 Erding Rothmeyer Verfahren zum hochtransformieren der temperatur von waerme sowie waermetransformator
JPS60263060A (ja) * 1984-06-12 1985-12-26 日立造船株式会社 反応熱回収方法
US4993239A (en) * 1987-07-07 1991-02-19 International Thermal Packaging, Inc. Cooling device with improved waste-heat handling capability
FR2620048B1 (fr) * 1987-09-07 1989-12-22 Elf Aquitaine Procede de conduite d'une reaction thermochimique et installation permettant la mise en oeuvre de ce procede
ATE133991T1 (de) * 1989-06-06 1996-02-15 Gerd Hoermansdoerfer Latentwärmespeichermittel und deren verwendung
US5161389A (en) * 1990-11-13 1992-11-10 Rocky Research Appliance for rapid sorption cooling and freezing
DE4237991A1 (de) * 1992-11-11 1994-05-19 Schloemann Siemag Ag Verfahren und Vorrichtung zur Abkühlung von warmgewalzten Profilen insbesondere von Schienen
JP3348336B2 (ja) * 1995-10-26 2002-11-20 株式会社豊田中央研究所 吸着ヒートポンプ

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5054544A (en) * 1989-01-20 1991-10-08 Zeo-Tech (Zeolith-Technologie Gmbh) Sorption container for solid sorption medium
US5360057A (en) * 1991-09-09 1994-11-01 Rocky Research Dual-temperature heat pump apparatus and system
US5291942A (en) * 1993-05-24 1994-03-08 Gas Research Institute Multiple stage sorption and desorption process and apparatus

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002002998A1 (fr) * 2000-07-06 2002-01-10 Thermagen Sa Appareil refrigerant d'adsorption
FR2811412A1 (fr) * 2000-07-06 2002-01-11 Thermagen Dispositif de refrigeration par adsorption
US7000426B2 (en) 2000-07-06 2006-02-21 Thermagen (S.A.) Adsorption refrigerating device
US6895779B2 (en) 2000-11-13 2005-05-24 Thermagen Adsorption refrigerating device
WO2007139476A1 (fr) 2006-05-29 2007-12-06 Climatewell Ab (Publ) Pompe à chaleur chimique fonctionnant avec une substance hybride
EP2225500A4 (fr) * 2007-11-29 2015-08-05 Climatewell Ab Publ Collecteur d'énergie solaire thermique pour produire de la chaleur et/ou un refroidissement
JP2013513779A (ja) * 2009-12-09 2013-04-22 クライメイトウエル エービー（パブル） 一体化された化学ヒート・ポンプを備えた太陽熱パネル

Also Published As

Publication number Publication date
SE9804034D0 (sv) 1998-11-24
US20020017380A1 (en) 2002-02-14
AU2013000A (en) 2000-06-13
SE513178C2 (sv) 2000-07-24
JP2002530619A (ja) 2002-09-17
SE9804034L (sv) 2000-05-25

Similar Documents

Publication Publication Date Title
US20020017380A1 (en) Chemical heat pump using a solid substance
US5328671A (en) Heat and mass transfer
EP2021704B1 (fr) Pompe à chaleur chimique fonctionnant avec une substance hybride
AU681092B2 (en) Improved method and apparatus for achieving high reaction rates
Shkatulov et al. Core–shell encapsulation of salt hydrates into mesoporous silica shells for thermochemical energy storage
US11859877B2 (en) Hybrid adsorber heat exchanging device and method of manufacture
CA1123293A (fr) Methode de stockage de chaleur de reaction pour les reservoirs d'hydrure
US8839642B2 (en) Thermal solar energy collector for producing heat and/or cooling
AU653791B2 (en) Portable cooler
WO1991017392A1 (fr) Procedes et appareils pour realiser un stockage avec refrigeration et/ou pour purifier l'eau
WO2022071405A1 (fr) Pompe à chaleur absorbante
KR100306706B1 (ko) 높은반응속도를얻기위한개선된방법및그장치
Elsayed The potential of MIL-100 (Fe) composites with CPO-27 (Ni) and MIL-101 (Cr) in adsorption applications
Ferrigno Thermal characterization of MOFs for thermal energy storage
KR100760380B1 (ko) 냉각 및 난방을 위한 화학열펌프용 열전도성 단위반응블록및 이의 제조방법

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
ENP Entry into the national phase

Ref country code: JP

Ref document number: 2000 584023

Kind code of ref document: A

Format of ref document f/p: F

WWE Wipo information: entry into national phase

Ref document number: 09863406

Country of ref document: US

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase