Classifications

• • E—FIXED CONSTRUCTIONS
  • E01—CONSTRUCTION OF ROADS, RAILWAYS, OR BRIDGES
  • E01F—ADDITIONAL WORK, SUCH AS EQUIPPING ROADS OR THE CONSTRUCTION OF PLATFORMS, HELICOPTER LANDING STAGES, SIGNS, SNOW FENCES, OR THE LIKE
  • E01F9/00—Arrangement of road signs or traffic signals; Arrangements for enforcing caution
  • E01F9/50—Road surface markings; Kerbs or road edgings, specially adapted for alerting road users
  • E01F9/506—Road surface markings; Kerbs or road edgings, specially adapted for alerting road users characterised by the road surface marking material, e.g. comprising additives for improving friction or reflectivity; Methods of forming, installing or applying markings in, on or to road surfaces
  • E01F9/524—Reflecting elements specially adapted for incorporation in or application to road surface markings
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
  • Y10T428/24355—Continuous and nonuniform or irregular surface on layer or component [e.g., roofing, etc.]
  • Y10T428/24372—Particulate matter
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
  • Y10T428/24355—Continuous and nonuniform or irregular surface on layer or component [e.g., roofing, etc.]
  • Y10T428/24372—Particulate matter
  • Y10T428/24421—Silicon containing
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/25—Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
  • Y10T428/252—Glass or ceramic [i.e., fired or glazed clay, cement, etc.] [porcelain, quartz, etc.]

Definitions

• the present invention relates to pavement markings containing optical elements or skid-resistant particles.
• the present invention also relates to pavement markings having enhanced retroreflectivity under dry or wet conditions.
• pavement markings e.g., paints, retroreflective elements, tapes, and raised pavement markings
• These pavement markings often are retroreflective so motorists can see the markings at night.
• the pavement marking in turn becomes wet and often the retroreflective performance diminishes.
• Retroreflection describes the mechanism where light incident on a surface is reflected so that much of the incident beam is directed back toward its source.
• the optical elements which typically are transparent, substantially spherical, glass or ceramic lenses
• the ratio of the refractive index at the exposed-lens surface changes which affects light gathering.
• Raised pavement markers include, but are not limited to, U.S. Patent No. 4,875,798 (May et al.), U.S. Patent No. 5,667,335 (Khieu et al.), and U.S. Patent No. 5,667,334 (Boyce).
• Raised pavement markers may be used to elevate retroreflective sheeting (e.g., enclosed-lens, sealed-lens, or prismatic-lens sheeting) on one or more surface(s) above any water or other liquids on the roadway.
• retroreflective sheeting e.g., enclosed-lens, sealed-lens, or prismatic-lens sheeting
• Raised pavement markings are often susceptible to scratching of the outer plastic surface.
• raised pavement markings are about 1 to 3 centimeters in height. These scratches significantly reduce retroreflectivity under dry conditions.
• raised pavement markers are subject to damage from snowplows and often are used in combination with other forms of pavement markings to provide
• Preformed pavement marking tapes are generally classified as "flat” tapes or “patterned” tapes which have generally vertical surfaces, usually in the form of retroreflective protuberances or protrusions (see, e.g., U.S. Patent Nos. 4,388,359 (Ethen et al.), 4,988,555 (Hedblom), 4,988,541 (Hedblom), 5,670,227 (Hedblom et al.) and
• retroreflective elements include, but are not limited to, U.S. Patent No. 5,750,191 (Hachey et al.), U.S. Patent No. 5,774,265 (Mathers et al.), and
• U.S. Patent Nos. 4,072,403 (Eigenmann) and 5,268,789 (Bradshaw) describe pavement markings having good wet and dry retroreflectivity. However, the outer surface of these pavement markings may be readily scratched which decreases the dry retroreflectivity. These pavement markings tend to be rather rigid, which can make adhesion to the road difficult. Further, these pavement markings may be difficult to manufacture. The pavement markings are discreet and thus, do not provide continuous wet or dry delineation.
• U.S. Patent No. 4,145,112 (Crone) describes a wet retroreflective optical system based on refracting and retroreflective optics.
• One disadvantage of this system is durability.
• the plastic surface may scratch which reduces dry and wet retroreflective performance, particularly because this system relies on a refracting surface and on a total internal reflecting surface.
• Pavement markings having a mixture of microspheres having different refractive indices have been used to obtain dry and wet retroreflectivity. See for example, U.S. Patent No. 5,777,791 (Hedblom).
• the higher refractive index microspheres tend to be glass which is not as durable and is more readily scratched than the lower refractive index ceramic microspheres.
• EP Patent No. 385746 Bl discloses a pavement marking having a layer of large glass microspheres embedded in the top of retroreflective enclosed-lens type base sheeting.
• the retroreflective pavement marking is said to be particularly useful in rainy conditions because the larger glass microspheres are partially exposed in air.
• Pavement markings containing large glass microspheres tend to recover retroreflectivity quicker after rain has stopped falling.
• actual retroreflective performance during rain tends to be poor because water covers the microsphere surface.
• These larger glass microspheres often have a relatively low refractive index (e.g., 1.5), which yields lower dry and wet retroreflection.
• the present invention provides pavement marking articles which are retroreflective under dry or wet conditions. Surprisingly, some embodiments of the present invention have enhanced retroreflection when exposed to water, for example, when wet by rainwater.
• These pavement marking articles can be preformed pavement marking tapes, retroreflective flakes, or retroreflective elements embedded in a preformed pavement marking tape or in a road binder.
• the articles of the present invention comprise a monolayer of exposed-lens optical elements and a reflective layer, characterized in that there is a spacing layer between the optical elements and the reflective layer.
• the articles typically further comprise one or more top layers, a base layer, and an adhesive layer.
• the articles When the articles are retroreflective elements, the articles further comprise a core layer.
• the present invention also provides a means for making these retroreflective pavement marking articles.
• One method comprises the steps of:
• one or more binder materials can be applied to the exposed-lens film prior to embossing the exposed-lens film onto the preformed pavement marking tape.
• the film may be selectively applied to a preformed tape.
• the film may be applied to only the vertical surfaces, only the protrusions, in a continuous stripe down or crossweb, etc. when applied to a preformed pavement marking tape.
• the exposed-lens film composite can be laminated to a base layer comprising a plurality of protuberances.
• FIG. 1 is a cross-section of a retroreflective pavement marking article 10 having a layer of optical elements 12 with an exposed-lens surface 11 and an embedded-lens surface 13, a spacing layer 14, and a reflective layer 16.
• FIG. 2 is a cross-section of a retroreflective preformed pavement marking tape 20 having a layer of optical elements 12 with an exposed-lens surface 11 and an embedded- lens surface 13, a spacingM, a reflective layer 16, a top layer 22, a base layer 24, and an adhesive layer 26 for bonding the preformed tape to a roadway surface 28.
• FIG. 3 is a cross-section of a retroreflective pavement marking article 30 having a layer of optical elements 12 where the optical elements have different average diameters, a spacing layer 14, and a reflective layer 16.
• FIG 4 is a cross-section of a retroreflective pavement marking article 40 having a layer of optical elements 12 with substantially the same average diameter, a spacing layer 14 having a variable thickness and a reflective layer 16.
• FIG. 5 is a cross-section of a retroreflective pavement marking article 50 having a layer of optical elements 12 with two different refractive indices, a spacing layer 14, and a reflective layer 16.
• FIG 6 is a cross-section of a preformed pavement marking tape 60 having protrusions where the protrusions have a layer of optical elements 12 with a spacing layer 14 on the embedded-lens surface side of the optical elements and a reflective layer 16 layered on the spacing layer embedded therein.
• the tape has a binder layer 64 and a base layer 62.
• FIG. 7 is a cross-section of a preformed pavement marking tape 70 having protrusions, with a layer of optical elements 12 having a spacing layer 14 on the embedded-lens surface side of the optical elements and a reflective layer 16 layered on the spacing layer embedded in the binder layer 64 on the top surface of the preformed tape.
• FIG. 8 is a cross-section of a preformed pavement marking 80 having protrusions, with a layer of optical elements 12 having a spacing layer 14 on the embedded-lens surface side of the optical elements and a reflective layer 16 layered on the spacing layer and retroreflective flake 82 adhered to the preformed tape 80 with a binder layer 64.
• the figures which are idealized and not to scale, are intended to be merely illustrative and non-limiting.
• the present invention provides a retroreflective pavement marking article comprising a monolayer of exposed-lens optical elements, a spacing layer, and a reflective layer.
• the pavement markings are retroreflective under wet or dry conditions.
• the pavement marking articles are attached to the surface of a road or other traffic- bearing surface. These articles can be preformed pavement marking tapes, retroreflective flakes, or retroreflective elements.
• the tapes are typically attached to the roadway with an adhesive.
• the retroreflective flakes may be adhered to a preformed pavement marking tape or attached to a traffic-bearing surface using a road binder material.
• the retroreflective elements may be adhered to a preformed pavement marking tape or attached to the traffic-bearing surface using a road binder material.
• Pavement marking articles and other substantially horizontal markings typically exhibit high retroreflective brightness when the light is incident at high entrance angles (typically greater than about 85°).
• Retroreflective sheeting and other retroreflective articles attached to vertical surfaces tend to exhibit high retroreflective brightness at lower entrance angles (e.g., within 30° to 40° of normal).
• the optical requirements of pavement marking articles differ from the optical requirements of retroreflective sheeting.
• optical elements are suitable for use in the present invention.
• the optical elements are exposed-lens. Exposed-lens is defined herein as having at least a portion of the optical element open to the air upon initial application to a traffic-bearing surface.. After use on the traffic-bearing surface, the exposed-lens portion may become coated with oil, dust, road debris, etc.
• the portion of the optical element that is in contact with the spacing layer, or not the exposed-lens portion, is the embedded-lens portion.
• various surface treatments may be present on the exposed-lens surface of the optical elements.
• these treatments may be residual coatings used to enhance the adhesion of the optical element to the spacing layer.
• low adhesion topsize materials may be present on the exposed-lens surface to allow a preformed pavement marking tape article having an adhesive to be rolled-up and unwound.
• various surface treatments may be present in small quantities on the surface of exposed-lens or embedded-lens elements to enhance the adhesion of the retroreflective flake or element to the binder or road binder or to modify wicking of the binder or road binder around the retroreflective flake or element.
• the thin films or surface treatments on the exposed-lens optical elements may temporarily affect the wetting of rain on the surface of the marking.
• the optical elements typically have a refractive index ranging from about 1.5 to about 2.0 for optimal dry retroreflectivity, preferably ranging from about 1.5 to about 1.8.
• the optical elements For optimal wet retroreflectivity, have a refractive index ranging from about 1.7 to about 2.4, preferably ranging from about 1.9 to 2.4, and more preferably ranging from about 1.9 to about 2.1.
• the layer of optical elements can contain optical elements having the same, or approximately the same refractive index.
• the layer of optical elements can contain optical elements having two or more refractive indices.
• optical elements having a higher refractive index perform better when wet and optical elements having a lower refractive index perform better when dry.
• the ratio of the higher refractive index optical elements to the lower refractive index optical elements is preferably about 1.05 to about 1.4, and more preferably from about 1.08 to about 1.3.
• optical elements having about 50 to about 1000 micrometers average diameter are preferred for use in the present invention.
• the optical element layer may contain optical elements having the same, or approximately the same average diameter.
• the optical element layer may contain optical * elements having two or more average diameters.
• optical elements having a larger average diameter perform better when dry, while optical elements having a smaller average diameter perform better when wet.
• Blends of optical elements having both different average diameter and refractive index may be used. Typically, a larger average diameter lower refractive index optical element is used to achieve better dry retroreflectivity, while a smaller average diameter higher refractive index optical element is used to achieve better wet retroreflectivity.
• the optical elements can contain an amorphous phase, a crystalline phase, or a combination, as desired.
• the optical elements preferably contain inorganic materials that are not readily susceptible to abrasion. Suitable optical elements include, for example, microspheres formed of glass such as soda-lime-silicate glasses.
• Microcrystalline ceramic optical elements as disclosed in U.S. Patent Nos. 3,709,706; 4,166,147; 4,564,556; 4,758,469; and 4,772,511 have enhanced durability.
• Preferred ceramic optical elements are disclosed in U.S. Patent Nos. 4,564,556, 4,772,511 and 4,758,469. These optical elements are resistant to scratching and chipping, are relatively hard (above 700 Knoop hardness).
• These ceramic optical elements may contain zirconia, alumina, silica, titania, and mixtures thereof.
• the optical elements can be colored to retroreflect a variety of colors. Techniques to prepare colored ceramic optical elements that can be used herein are described in U.S. Patent No. 4,564,556.
• Colorants such as ferric nitrate (for red or orange) may be added in an amount of about 1 to about 5 weight percent of the total metal oxide present. Color may also be imparted by the interaction of two colorless compounds under certain processing conditions (e.g., TiO 2 and ZrO 2 may interact to produce a yellow color).
• the optical elements may be colored so that, for example, colorless, yellow, orange, or some other color of light is retroreflected at night.
• optical elements are typically partially embedded in the spacing layer in a hexagonal close-packed arrangement. In certain product applications, it may be advantageous to have the optical elements applied at less than the close-packed rate.
• the pavement marking articles of the present invention contain a spacing layer that preferably "cups" the optical elements.
• the spacing layer has two major surfaces. The first major surface is in contact with the embedded-lens surface of the optical elements.
• the second major surface of the spacing layer is next to the reflective layer and follows a radius of curvature (preferably the radius of curvature is such that the spacing layer forms a concentric hemisphere with respect to the optical element) larger than the optical element with an origin approximately at the center of the optical element. This forms the
• the spacing layer can be applied to the optical elements using various techniques, including, but not limited to, solution coating, curtain coating, extrusion, lamination, and powder coating. Processing the spacing layer into a cup may include, but is not limited to, solvent evaporation, sagging of the spacing layer under the forces of gravity, displacement of the spacing layer due to fluid forces, or electrostatic deposition. Solidification of the spacing layer can include, but is not limited to, drying, chemical reaction, temporary ionic bonds, or quenching.
• the spacing layer contains a resin such as polyvinyl butyral, polyurethanes, polyesters, acrylics, acid olefin copolymers such as ethylene acrylic acid, ethylene methacrylic acid, acid olefin copolymers neutralized with a base "ionomer", polyvinyl chloride and its copolymers, epoxies, polycarbonates, and mixtures thereof.
• a resin such as polyvinyl butyral, polyurethanes, polyesters, acrylics, acid olefin copolymers such as ethylene acrylic acid, ethylene methacrylic acid, acid olefin copolymers neutralized with a base "ionomer", polyvinyl chloride and its copolymers, epoxies, polycarbonates, and mixtures thereof.
• optical transparency typically is a requirement.
• the spacing layer preferably has a 70% or greater transparency to visible light, more preferably, 80% or greater, and most preferably 90% or greater.
• the refractive index of the spacing layer generally ranges from about 1.4 to about 1.7, preferably from about 1.4 to about 1.6, and more preferably from about 1.45 to about 1.55.
• the thickness of the spacing layer varies with the refractive index and the size of the optical elements. In general, assuming the optical elements have the same refractive index and the same size or average diameter, then the thicker the spacing layer, the better the optics when the pavement marking article is wet.
• the relative thickness of the spacing layer to the optical element radius ranges from about 0.05 to about 1.4, preferably from about 0.1 to about 0.9, and more preferably from about 0.2 to about 0.9.
• the preferred range of the relative spacing layer thickness is about ⁇ 0.15 for low refractive index optical elements and about +0.1 for high refractive index optical elements.
• the preferred range of the relative spacing layer thickness is about ⁇ 0.20 for low refractive index optical elements and about ⁇ 0.1 for high refractive index optical elements.
• the spacing layer may have the same, or approximately the same, thickness throughout the pavement marking article. Alternatively, the spacing layer thickness may vary across the pavement marking article crossweb or downweb. The spacing layer thickness may also vary sinusoidally downweb or crossweb. Suitable methods to vary the spacing layer thickness include, but are not limited to, extrusion with variable drawings speeds; extrusion with a profiled die; powdercoating with different web conductivities downweb or crossweb; and solution coating with a multiple orifice die.
• the reflective layer can contain a diffuse reflector or a specular reflector.
• the diffuse reflector typically contains a diffuse pigment.
• useful diffuse pigments include, but are not limited to, titanium dioxide, zinc oxide, zinc sulfide, lithophone, zirconium silicate, zirconium oxide, natural and synthetic barium sulfates, and combinations thereof.
• the diffuse pigment is typically delivered to the back of the spacing layer via a polymeric coating.
• the polymeric coating may be applied using a variety of techniques such as knife coating, roll coating, extrusion, or powder coating.
• suitable polymeric materials include thermoset materials and thermoplastic materials.
• Suitable polymeric materials include, but are not limited to, urethanes, epoxies, alkyds, acrylics, acid olefin copolymers such as ethylene/ methacrylic acid, polyvinyl chloride/polyvinyl acetate copolymers, etc.
• the specular reflector may be a specular pigment, a metallized layer, or multi- layered di-electric materials.
• a useful specular pigment is a pearlescent pigment.
• Useful pearlescent pigments include, but are not limited to, AFFLAIRTM 9103 and 9119 (obtained from EM Industries, Inc., New York), Mearlin Fine Pearl # 139V and Bright Silver #139Z (obtained from The Mearl Corporation, Briarcliff Manor, New York).
• the reflective layer may also contain a thin metallic film or films.
• These thin metallic films may be applied by precipitation (e.g., precipitation of silver nitrate), thermal evaporation in a vacuum (e.g., resistive heating of Ag, Al; exploding wire; laser evaporation; and the like), sputtering (e.g., glow discharge) and chemical methods (e.g., electrodeposition, chemical vapor deposition). Resistive heating of aluminum is the presently preferred method of coating thin metallic films.
• Another suitable reflective layer includes multi-quarter wavelength layers of various dielectric materials. An odd number of stacks of high and low refractive index films can yield reflectances close to 100 percent. These multilayer thin films can be applied by thermal evaporation and chemical methods.
• spacing layer thickness spacing layer refractive index
• optical element diameter optical element refractive index
• optical element refractive index optical element refractive index
• optical element refractive index optical element refractive index
• preformed pavement marking tapes may contain additional layers to improve the performance of the resultant pavement marking tape.
• the tapes may contain a top layer that typically is a top coat or a top film.
• the top layer is beneath the reflective layer.
• the top layer preferably adheres well to the reflective layer.
• the top layer may function as the binder layer to adhere the retroreflective article to the preformed pavement marking tape.
• the top layer may be located beneath the binder layer when the binder layer is present.
• Useful top layers are known in the art. Examples of suitable top layers include both thermoplastic and thermoset polymeric materials.
• Suitable polymeric materials include, but are not limited to, urethanes, epoxies, alkyds, acrylics, acid olefin copolymers such as ethylene/ methacrylic acid, polyvinyl chloride/ polyvinyl acetate copolymers, etc.
• the top layer material may contain pigments for color.
• Illustrative samples of common colorants include, but are not limited to Titanium Dioxide CI 77891 Pigment
• the preformed pavement marking tapes may also contain a base layer (e.g., a conformance layer) or an adhesive layer. These layers are located beneath the top layer.
• a base layer e.g., a conformance layer
• an adhesive layer e.g., an adhesive layer
• Suitable base layers include, but are not limited to, those disclosed in U.S. Patent Nos. 4,117,192; 4,490,432; 5,114,193; 5,316,406; and 5,643,655.
• suitable adhesives include, but are not limited to, pressure-sensitive adhesives, rubber resin adhesives, neoprene contact adhesives, etc.
• Preformed pavement marking tapes of the present invention may be substantially flat or have protrusions.
• substantially flat pavement marking tapes which may be modified to include the invention described herein, include, but are not limited to, U.S.
• tapes having protrusions which may be modified to include the invention described herein, include, but are not limited to U.S. Patent No. 4,388,359, 4,988,555, 5,557,461, 4,969,713, 5,139,590, 5,087,148, 5,108,218, and 4,681,401.
• a preferred pavement marking tape having protrusions is disclosed in U.S. Patent No.
• the tapes may also be removable for short-term usage.
• the retroreflective flakes can contain the optical layer, the spacing layer, and the reflective layer.
• the retroreflective flakes may also include one or more bottom layers adhered to the reflective layer.
• the retroreflective flakes are discreet segments of the retroreflective article which are attached to a preformed pavement marking tape or on a traffic-bearing substrate.
• the retroreflective flakes typically are adhered to a preformed pavement marking tape having protrusions.
• the flakes are selectively adhered to just the vertical surfaces of the protrusions. Preferred binder materials and road binder materials are described below.
• the presently preferred area of the retroreflective flakes is approximately 0.04 to about 1 (millimeters) 2 and more preferably the flakes are about 0.04 to about 0.25 (millimeters) 2 .
• Another embodiment of the present invention is a retroreflective element attached to a preformed pavement marking tape or partially embedded in a road binder.
• the retroreflective elements contain the optical layer, the spacing layer, the reflective layer, and the core layer.
• Suitable core layer material includes polymeric materials, both thermoplastic and thermoset materials and mixtures thereof. Particular examples of suitable material can be readily selected by those skilled in the art. Potential core layer materials can be selected from a wide range of thermoplastic materials.
• non-crosslinked elastomer precursors e.g., nitrile rubber formulations
• the core layer material can contain one or more resin materials.
• thermoset materials useful for the core layer include amino resins, thermosetting acrylic resins, thermosetting methacrylic resins, polyester resins, drying oils, alkyd resins, epoxy and phenolic resins, polyurethanes based on isocyanates, polyureas based on isocyanates, and the like.
• Such compositions are described in detail in Organic Coatings: Science and Technology, Volume I: Film Formation, Components, and Appearance, Zeno W. Wicks, Jr., Frank N. Jones and S. Peter Pappas, ed., John Wiley & Sons, Inc., New York, 1992.
• the presently preferred dimensions of the retroreflective elements are approximately about 1 to about 2.5 millimeters thickness, about 0.5 to about 1 centimeter width, and about 0.5 to about 10 centimeters length.
• the retroreflective elements may be any shape. However, the shape typically is rectangular or square.
• the retroreflective article is attached to at least one surface of the core layer, and is typically attached to two or more surfaces of the core layer.
• the retroreflective elements may be attached to either a flat or a protrusioned preformed tape. When the preformed tape has protrusions, the retroreflective elements preferably are adhered only to the generally up-right or "vertical" surfaces of the protrusions, where they provide the most efficient retroreflection. However, the retroreflective elements may be attached to the top surface of the top layer of the preformed tape.
• the retroreflective elements or flakes can be attached to the tape using a binder material.
• Suitable binder materials include, but are not limited to polyurethanes, polyureas, epoxy resins, polyamides, polyesters, and mixtures thereof and to those disclosed in U.S. Patent Nos. 4,248,932, and 5,077,117 incorporated by reference herein.
• a magnetic layer may be applied to the reflective layer of the retroreflective flake or element.
• the retroreflective flake or element may then be applied to a preformed pavement marking tape in the present of a magnetic field to help orient the retroreflective flake or element.
• Road binders for pavement marking articles are well-known in the art.
• Suitable road binder materials include, but are not limited to, wet paint, thermoset materials, or hot thermoplastic materials (e.g., U.S. Patent Nos. 3,849,351, 3,891,451, 3,935,158, 2,043,414, 2,440,584, 4,203,878, 5,478,596).
• retroreflective elements or flakes and skid-resistant particles are sprinkled or otherwise applied to a road binder material while it is in a liquid state.
• the retroreflective elements or flakes or particles become partially embedded in the road binder material while it is liquid.
• the road binder material subsequently becomes solid resulting in retroreflective elements or flakes or particles partially embedded therein.
• the paint or thermoset or thermoplastic material forms a matrix that serves to hold the pavement marking articles in a partially embedded and partially protruding orientation.
• the matrix can be formed from durable two component systems such as epoxies or polyurethanes, or from thermoplastic polyurethanes, alkyds, acrylics, polyesters, and the like. Alternate coating compositions that serve as a matrix and include the pavement marking articles described herein are also contemplated to be within the scope of the present invention.
• Skid-Resistant Particles typically a retroreflective preformed pavement marking tape also contains skid- resistant particles.
• Illustrative examples of particularly useful skid-resistant particles include those disclosed in U.S. Patent Nos. 5,124,178; 5,094,902; 4,937,127; and 5,053,253.
• Skid-resistant particles may also be embedded in a retroreflective element, or embedded in a road-binder.
• skid-resistant particles are randomly sprinkled and become embedded in the binder material while it is in a softened state. The skid-resistant particles may also be embedded in the spacing layer.
• the retroreflective pavement marking articles of the present invention may be made by first making exposed-lens film and then placing this film in a vertical orientation using an embossing process.
• the exposed-lens retroreflective film can be made by first coating a cupping resin onto a liner such as polyethylene terephthalate (PET), paper, or the like.
• a liner such as polyethylene terephthalate (PET), paper, or the like.
• PET polyethylene terephthalate
• Suitable cupping resins include resins which have significantly lower viscosity than the spacing layer at the process temperature and which also exhibit low adhesion to the spacing layer (e.g., VITELTM 3300 resin available from Bostik, Middleton, MA).
• the cupping resin generally about 0.05 to about 0.25 millimeters thick
• the liner generally about 0.01 to about 0.10 millimeters thick
• the cupping film After drying, the cupping film can be wound up.
• the spacing layer (which typically is a substantially transparent film) is coated (e.g., extruded or powder coated) on top of the cupping film forming a composite spacing layer.
• the spacing layer may contain, for example PRIMACORTM 3440 resin, (an extrusion grade thermoplastic, high molecular weight copolymer believed to contain a major portion of ethylene monomer and a minor portion of acrylic acid monomer, available from Dow Chemical Co. Midland, MI, and having a melt flow index of about 10), a weather stabilizing system, and an antioxidant.
• This composite spacing layer can then be wound up.
• powder coating produces a spacing layer having uniform thickness on the optical elements.
• a polymer is made or ground to about 30 micron mean particle size.
• the powder is fluidized and conveyed with compressed air to an electrostatic spray gun where the powder is charged by corona or triboelectric methods.
• the powder is then sprayed towards the optical element film which is over a conductive substrate or base plate that is maintained at electrical ground.
• the powder particles adhere due to electrostatic attraction.
• the dynamics of the electrostatic attraction are such that the powder tends to collect at a uniform thickness over the three dimensional optical element film.
• the powder coated optical element film is then passed through an oven to fuse the powder onto the substrate.
• Various fluidized bed powdercoating techniques can alternatively be employed to deliver a uniform thickness of powder over the optical element containing film prior to the powder fusing operation. Further processing may then take place.
• a second film (which usually serves as the optical element carrier) is made by extruding a polyolefin (e.g., polyethylene) onto a liner such as PET, paper, or the like.
• the thickness of the polyolefin is commensurate with the optical element average radius.
• the second film is heated to a temperature about the melting temperature of the film (e.g. for polyethylene film, above 135°C).
• the optical elements are then dropped from a dispenser and partially embedded, preferably to about 30% or more of their average diameter, into the softened second film to form a monolayer of optical elements.
• This optical element film composite can then be wound up.
• the optical elements can be coated with a surface treatment such as silane to help the optical elements adhere to the spacing layer.
• a surface treatment such as silane
• this surface treatment can be applied by reverse roll coating a solution of Al 100 silane (available from Union Carbide, Danbury, CT) in deionized water and then drying.
• the optical element film composite is then laminated to the composite spacing layer to partially embed the optical elements into the spacing layer. This may be accomplished by heating the composite spacing layer (e. g., run over a hot can or through an oven) and then laminating the two composites together using a nip to form "the laminate".
• the cupping film has a lower viscosity than the spacing layer. This helps the spacing layer form a more uniform cup around the optical element. The degree to which the spacing layer cups the optical element has an affect on the angularity of the retroreflective article.
• the cupping film is stripped away from the composite spacing layer which is now adhered to the optical elements.
• the spacing layer becomes exposed and is cured if desired (e.g., ultraviolet radiation, e-beam).
• a reflective layer e.g., vapor coating an aluminum metallic layer
• the optical element carrier is stripped away from the laminate, exposing the optical elements.
• the resulting article can then be wound up.
• the resulting article includes the optical elements, and behind the optical elements is the spacing layer backed by a reflective layer (e.g., an aluminum vapor coat).
• a top layer may be laminated to the reflective layer before or after removal of the optical element carrier.
• a pigmented thermoplastic resin e.g., EMAA film
• EMAA film may be laminated to the bottom side of the reflective layer opposite the optical elements.
• the top layer may act as the binder layer or alternatively, a binder layer may be used to attach the retroreflective article (here a film) to a preformed pavement marking tape.
• This retroreflective film can then be placed on the top surface of a preformed pavement marking tape by feeding the film into an embossing nip.
• the film can first be coated with a binder material and then be laminated to a preformed pavement marking tape having protrusions.
• the film can be selectively placed on a preformed pavement marking tape by indexing.
• the film can be appropriately spaced such that when applied to the preformed tape, the film is located only on the vertical surfaces, only on the pattern of the tape, only on the protrusions, or only in stripes downweb or crossweb. Preferably at least 5 percent of the top surface area of the preformed pavement marking tape is covered with the retroreflective film.
• Methods of Application The preformed pavement marking tape articles of the present invention may be installed on a roadway or other location using any one of a variety of apparatus such as human pushable dispensers, "behind a truck” type dispensers, and "built into a truck” type dispensers.
• U.S. Pat. No. 4,030,958 discloses a behind a truck type dispenser that can be used to apply articles of the invention in the form of adhesive-backed tapes to a surface.
• pavement marking tape articles of the invention may be used to install the pavement marking tape articles of the invention, such as simple manual application, or use of the previously mentioned mechanical fasteners.
• Pavement marking articles 5 through 66 and 76 through 102 were prepared as follows.
• the top surface of the exposed-lens optical elements was scrubbed with toothpaste and a toothbrush. This scrubbing removes any low surface energy contamination on top of the optical elements and facilitates the rain wetting out the optics.
• the reflective layer-side of the exposed-lens optical element films was laminated using a pressure-sensitive adhesive to LEXANTM pieces measuring 10 centimeters long, 0.64 centimeters wide and 3.0 millimeters in height.
• the exposed-lens films were attached to the 3.0 millimeter by 10 centimeter side.
• the exposed-lens optical element films were then trimmed to 3.0 millimeters by 10 centimeters producing a retroreflective element.
• the retroreflective elements were then mounted with a spacing of about 5.8 centimeters onto an aluminum panel measuring 1.5 millimeters thick by 10 centimeters wide by 1.5 meters long to produce a pavement marking article.
• Example 4 Various methods of manufacturing 1.75 ceramic optical elements are available, such as described in Example 4 of U.S. Patent No. 4,564,556.
• a stable, ion-exchanged zirconia sol was prepared by mixing a nitrate stabilized zirconia sol containing about 20% Z >2 by weight and about 0.83 M NO3 per mole Zrt_>2 (obtained from Nyacol Products Company), with an ion exchange resin (Amberlyst A-21 resin made by Rohm and Haas Company) in a ratio of about 100 g of sol to 15 g resin.
• an ion exchange resin Amberlyst A-21 resin made by Rohm and Haas Company
• the acidified colloidal silica was added to 320.0 grams of rapidly stirring zirconyl acetate solution.
• 52.05 grams of Niacet aluminum formoacetate (33.4% fired solids) were mixed in 300 milliliters deionized water and dissolved by heating to 80° C.
• the solution when cooled, was mixed with the zirconyl acetate-silica mixture described previously.
• the resulting mixture was concentrated by rotoevaporation to 35% fired solids.
• the concentrated optical element precursor solution was added dropwise to stirred, hot (88° - 90° C) peanut oil.
• the precursor droplets were reduced in size by the agitation of the oil and gelled. Agitation was continued in order to suspend most of the resulting gelled droplets in the oil. After about one hour, agitation was stopped and the gelled microspheres were separated by filtration.
• the recovered gelled microspheres were dried in an oven for about 5 hours at about 78° C prior to firing. The dried microspheres were placed in a quartz dish and fired in air by raising the furnace temperature slowly to about 900°C over 10 hours, maintaining about 900° for 1 hour, and cooling the microspheres with the furnace. The initial firing of all the samples was done in a box furnace with the door slightly open.
• the optical element constituents were in the molar ratio of Zr ⁇ 2:Al2 ⁇ 3:Si ⁇ 2 of
• RA coefficient of retroreflection
• the coefficient of Retroreflective Luminance, R L was measured for each pavement marking article at a geometry which approximates an automobile at 30 meters distance from the sample.
• the pavement marking articles were placed onto a table in a dark room. Above the pavement marking articles was a plumbing system capable of delivering a uniform artificial rainfall at a rate of about 3.3 centimeters per hour.
• the pavement marking articles were illuminated with projector lamps. The nominal entrance angle to the samples was 88.8 degrees.
• a photometer (IL 1700 Research Radiometer/Photometer by International Light, Inc.; Newburyport, Mass.) was used to measure the Illuminance on the sample. Typical illumination of the prototypes was about 70 Lux.
• a telephotometer Digital Luminance Meter Series L 1000 by LMT; Berlin,
• the Luminance of each of the samples was measured with the telephotometer, units of cd/m 2 .
• R L is calculated by dividing the Luminance of the sample by the Illuminance.
• the rainfall measurements were made two ways. The first was a fast draining experiment. The pavement marking articles were rained on. The rainfall was allowed to drain immediately off the aluminum panels onto which the pavement marking articles were attached. When a steady state rain Luminance was achieved, the rainfall was turned off. The Luminance was allowed to recover and the steady state recovered Luminance again was measured. Typically, the steady state recovered Luminance after the rain was turned on or off took about 3 minutes.
• the pavement marking articles were contained within a trough.
• the trough was nominally 15 centimeters wide by about 1.5 meters long by about 1.5 millimeters deep.
• the pavement marking articles were thus elevated to a height of 1.5 millimeters and contained within a trough of about 1.5 millimeters deep.
• This trough resulted in a significantly slower drainage of water from the pavement marking articles representing a higher rainfall rate.
• the steady state recovered Luminance was measured during the rainfall and after recovery.
• Comparative Example 1 A piece of 3M STAMARKTM High Performance Pavement Marking Tape Series 380
• This sample is a piece of new 3M STAMARKTM High Performance Pavement Marking Tape Series 380.
• This sample is a piece of 3M SCOTCHLANETM Removable Tape Series 750 (available from 3M), which is a wet retroreflective product primarily for use in construction zones.
• This sample is a flat preformed pavement marking tape having 1350 micron average diameter glass optical elements with a refractive index of 1.5.
• the optical elements were coated onto polyurethane (730 grams per square meter).
• the polyurethane contained 27 weight percent titanium dioxide pigment.
• a polyurethane solution was mixed using the following components:
• Rutile titanium dioxide pigment available as TIPURETM R-960, E.I. duPont de Nemours, New John sonvi lie, TN.
• TONETM 0301 polyester polyol available from Union Carbide
• the thickness and the viscosity of the polyurethane were adjusted to provide nominally 50 percent optical element embedment.
• the polyurethane was cured in an oven at about 120°C for about 15 minutes.
• Comparative Examples 1 through 4 were mounted on aluminum panels (1.5 millimeters thick, 10 centimeters wide and 1.5 meters long). The R L values were then measured for each example.
• R L values less than about 150 mCd/m 2 /Lx provide poor contrast and are not desirable for pavement marking articles.
• R L values at about 300 mCd/m 2 /Lx adequate contrast was provided and acceptable pavement marking article delineation was provided.
• Excellent contrast and pavement marking delineation was obtained at R L values at about 600 mCd/m 2 /Lx.
• RL values greater than 1000 mCd/m 2 /Lx are highly desirable for pavement marking articles.
• the polyurethane solution of Comparative Example 4 was coated onto a paper release liner using a notch bar.
• Optical elements having different refractive indices (as set forth in the following table) were then flood coated onto the surface of the polyurethane and oven cured at about 120°C for about 15 minutes.
• the coefficient of retroreflection (R A ) was measured.
• Retroreflective elements were then made as previously described.
• a pavement marking article was then made from the retroreflective elements as previously described.
• the coefficient of retroreflected luminance R L was then measured for the pavement marking articles.
• a polyurethane solution was mixed using the following components: 35.0% pearlescent pigment (AFFLAIRTM 9119, available from EM
• the polyurethane solution was coated onto a paper release liner using a notch bar.
• Optical elements having different refractive indices (as set forth in the following table) were then flood coated onto the surface of the polyurethane and oven cured at about 120°C for about 15 minutes.
• the coefficient of retroreflection (R A ) was measured.
• Retroreflective elements were then made as previously described.
• a pavement marking article was then made from the retroreflective elements as previously described.
• the coefficient of retroreflected luminance R L was then measured for the pavement marking articles.
• Glass optical elements having a 1.9 refractive index and an average diameter of 65 microns were embedded to approximately 40 percent of their average diameter in a polyethylene coated paper.
• the polyethylene coated paper was heated to about 135 °C and flood coated with glass optical elements preheated to about 135°C.
• the optical element coated web was maintained at about 135°C for about an additional 3 minutes resulting in the glass optical elements becoming embedded to about 40 percent of their average diameter.
• a spacing layer solution was coated on top of the optical elements using a notch bar.
• the notch bar gap ranged from 0 to about 250 microns.
• the spacing layer solution consisted of:
• DOWANOLTM EB ethylene glycol monobutyl ether solvent Dow Chemical USA; Midland, MI
• CYCLO-SOLTM 53 #100 solvent Shell Chemical Company; Baytown, TX
• AROPLAZTM1351 Reichhold Chemicals Inc.; Newark, NJ
• BUTVARTM B76 Solutia Inc.; Trenton, MI
• Beckamine PI 38 Reichhold Chemicals Inc.; Newark, NJ
• Tri-ethylamine Air Products & Chemicals, Inc.; Shakopee, MN).
• the spacing layer solution was dried and cured in a succession of ovens at about 65°C, about 77°C, about 150°C, about 155°C, and about 170°C for about one minute each. No spacing layer was applied to the optical elements in Example 12.
• the exposed portion of the spacing layer was vapor coated with aluminum as follows:
• the vacuum evaporator used was a NRC 3115 purchased from the Norton
• Examples 18-23 Samples were prepared as described in Examples 12-17 substituting 165 micron average diameter ceramic optical elements. In addition, the spacing layer bar gaps were varied from 0 to about 250 microns. The coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance R was then measured (the slow water drainage data was gathered at a later date) on the pavement marking article.
• the extruded films were placed polyester side-down on a hot plate at a temperature of about 205°C.
• Optical elements having various sizes were previously heated to the same temperature and were then flooded over the surface of the extruded film.
• the optical elements were allowed partially to embed themselves in the extruded film for about 30 seconds.
• the optical element- coated films were then removed and cooled.
• the polyester liner was removed.
• the optical element-coated film was then placed optical element side-down on the hot plate at about 205°C surface for about 5 minutes. These conditions allowed the extrusion to sag down the optical element and form a concentric spacing layer by cupping.
• the spacing layer-coated optical elements (or spacing layer composite) was then removed and quenched in room temperature water.
• Ceramic optical elements having a 165 micron average diameter were embedded in an extruded spacing layer having a thickness ranging from 0 to about 150 microns. After cupping the spacing layer, the films were vaporcoated with about 900 angstroms of aluminum as described in Examples 12-17. The coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance R was then measured for the pavement marking articles.
• extruded spacing layers on larger optical elements provide improved R L values in the rain (slow water drainage) than the solvent coated spacing layers of Examples 18-23.
• the examples also illustrate that the spacing layer articles can have better dry and raining R L values than specular reflective pigment systems (Comparative Examples 10 and 11).
• Samples were prepared as described in Examples 24-33 substituting a diffuse reflective layer onto the back of the spacing layer in place of the aluminum vaporcoat.
• the diffuse reflective layer consisted of a 27% by weight titanium dioxide-filled polyurethane as described in Comparative Example 4.
• the coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance RL was then measured for the pavement marking articles.
• Samples were prepared as described in Examples 34-39.
• a pearlescent pigmented polyurethane layer (35% by weight pearlescent pigment-filled polyurethane as described in Comparative Examples 9-11) was coated onto the back of the spacing layer in place of the aluminum vaporcoat.
• the coefficient of retroreflection (R A ) was measured.
• Retroreflective elements were then made as previously described.
• a pavement marking article was then made from the retroreflective elements as previously described.
• the coefficient of retroreflected luminance R L was then measured for the pavement marking articles.
• Examples 46-55 Samples were prepared as described in Examples 24-33. 275 micron average diameter glass optical elements were substituted for the ceramic optical elements of Examples 24-33. The spacing layer thickness ranged from about 62.5 to about 225 microns. The coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance R L was then measured on the pavement marking article.
• Samples were prepared as described in Examples 24-33. 460 micron average diameter glass optical elements were substituted for the ceramic optical elements of Examples 24-33. The spacing layer thickness ranged from about 100 to about 300 microns. The coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance R L was then measured for the pavement marking articles.
• Examples 67-74 Ceramic optical elements having an average diameter of about 165 microns were partially embedded into a polyethylene coated polyester film by flood coating in an oven at 135°C to about 30% of their average diameter.
• the optical elements were wetted with a 0.15% dilute aqueous solution of gamma- aminopropyltriethoxysilane (obtained from Union Carbide Corporation; Danbury, CT), then dried in an oven at about 120°C.
• a pressure-sensitive adhesive was used to laminate the optical element film composite to an aluminum panel using a handroller.
• the aluminum panel was used to provide electrical grounding to the substrate during the powder coating operation.
• the aluminum panel measured about 15.2 centimeters by about
• the optical element film was then electrostatically powder coated with a powder of approximate 30 micron particle size made from ElvaciteTM 2013 (an acrylic copolymer available from ICI Acrylics Inc., Cordova, TN).
• ElvaciteTM 2013 an acrylic copolymer available from ICI Acrylics Inc., Cordova, TN
• a Nordson electrostatic powder spray gun operating at +80 kilovolts was mounted about 40 cm above electrically grounded rollers.
• the aluminum panel to which the optical element film was laminated was placed on the grounded rollers.
• the grounded rollers were driven at different speeds to affect the powder coating weight. Powder coating weights ranged from about 3.4 grams to about 6.6 grams for the 15 centimeters by 30 centimeters panel.
• the powder coatings were fused onto the optical elements, conveyed through a series of ovens having heater temperatures at about 245°C, about 255°C, and about 320°C for a total time of about 3 minutes.
• the web temperature ranged from about 120°C and 150°C.
• the spacing layer was then vaporcoated with about 900 angstroms of aluminum as described in Examples 12-17.
• the vaporcoat side was then coated with an epoxy onto a rigid piece of aluminum. After the epoxy was cured, the polyethylene coated polyester optical element carrier was stripped off of the optical elements.
• the coefficient of retroreflection, R A was measured at -4.0/0.2 for both dry and under water conditions. The results are given in the following table:
• spacing layer can be applied to moderate sized optical elements (165 microns) by using powder coating.
• Example 75 To form a white base layer material, the ingredients in the following table were mixed in a Banbury internal mixer where they reached an internal temperature of approximately 150°C. The material was then cooled on a rubber mill and calendered into a sheet having a thickness of about 1.4 millimeters.
• thermoplastic topcoat was prepared by extruding a pigment concentrate blended with a thermoplastic.
• the pigment concentrate consists of 50% rutile titanium dioxide compounded with 50% ethylene methacrylic acid copolymer (NUCRELTM 699, E. I. duPont de Nemours, Wilmington, Del.).
• NUCRELTM 699 50% ethylene methacrylic acid copolymer
• the pigment concentrate was supplied by M. A. Hanna Color, Elk Grove Village, IL. 40% of the pigment concentrate was blended with 60% of additional NUCRELTM 699 and extruded to a thickness of about 1.1 millimeters. The extrusion was trimmed to a width of about 15 centimeters.
• the spacing layer-coated and vapor-coated optical elements of Example 15 were cut into stripes about 1 centimeters wide and 15 centimeters long.
• the vaporcoat side of the film was laminated transversely on the extruded thermoplastic topcoat.
• the spacing layer coated stripes were spaced about 6 centimeters apart.
• the thermoplastic topcoat was heated to about 100°C. At this temperature the vaporcoat adhered tightly to the topcoat.
• a 15 centimeters wide white base layer material was passed over a hot roll and heated to a temperature of about 140°C.
• the base layer was then passed through an embossing nip.
• the pattern on the embossing roll was the same as is used in the production of 3M STAMARKTM High Performance Pavement Marking Tape Series 380, available from 3M.
• the embossing roll was maintained at a temperature of about 40°C.
• the anvil roll was maintained at a temperature of about 25°C.
• the base layer was embossed at a pressure of about 8000 Newtons/ cm.
• the thermoplastic topcoat with the laminated spacing layer was fed over the pattern roll into the embossing nip.
• the spacing layer side of the topcoat was against the pattern roll.
• the pavement marking product was cooled to room temperature.
• the spacing layer-coated optical elements had very good dry retroreflectivity.
• the pavement marking was then submersed in water. When viewed with a flashlight the spacing layer-coated optical elements had improved retroreflectivity.
• Examples 76-84 Glass optical elements having a refractive index of about 1.5 were embedded in the extruded spacing layer of Examples 24-66.
• the spacing layer thickness was varied from about 50 to about 150 microns.
• the glass optical elements were embedded and cupped by the extruded spacing layer in a similar manner as Examples 24-66 except the temperature was about 175°C.
• the films were vaporcoated with about 900 angstroms of aluminum.
• the coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance R L was then measured for the pavement marking articles.
• Ceramic optical elements having a refractive index of about 1.75 were embedded in the extruded spacing layer of Examples 24-66.
• the spacing layer thickness was varied from about 50 to about 88 microns.
• the glass optical elements were embedded and cupped by the extruded spacing layer in a similar manner as Examples 24-66 except the temperature was about 175°C.
• the films were vaporcoated with about 900 angstroms of aluminum as described in Examples 12-17.
• the coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described.
• a pavement marking article was then made from the retroreflective elements as previously described.
• the coefficient of retroreflected luminance R L was then measured for the pavement marking articles.
• Ceramic optical elements having a refractive index of about 1.91 were screened to an average size of about 165 microns.
• Glass optical elements having a refractive index of about 1.5 were screened to an average size of about 165 microns.
• Mixtures of the optical elements were embedded in the extruded spacing layer of Examples 24-66.
• the spacing layer thickness was about 113 microns.
• the optical element mixture was embedded and cupped by the extruded spacing layer in a similar manner as Examples 24-66. After cupping the spacing layer, the films were vaporcoated with about 900 angstroms of aluminum as described in Examples 12-17.
• the coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described.
• the coefficient of retroreflected luminance RL was then measured for the pavement marking articles.
• Examples 98-102 Ceramic optical elements having a refractive index of about 1.91 were screened to an average size of about 165 microns. Ceramic optical elements having a refractive index of about 1.75 were screened to an average size of about 350 microns. Mixtures of the optical elements were embedded in the extruded spacing layer of Examples 24-66. The spacing layer thickness was about 100 microns. The optical element mixture was embedded and cupped by the extruded spacing layer in a manner similar to Examples 24-
• the films were vaporcoated with about 900 angstroms of aluminum as described in Examples 12-17.
• the coefficient of retroreflection (R A ) was measured. Retroreflective elements were then made as previously described. A pavement marking article was then made from the retroreflective elements as previously described. The coefficient of retroreflected luminance R L was then measured for the pavement marking articles.

Landscapes

• Engineering & Computer Science (AREA)
• Architecture (AREA)
• Civil Engineering (AREA)
• Structural Engineering (AREA)
• Road Signs Or Road Markings (AREA)
• Optical Elements Other Than Lenses (AREA)
• Processing Of Solid Wastes (AREA)
• Illuminated Signs And Luminous Advertising (AREA)

Priority Applications (7)

Applications Claiming Priority (2)

Publications (1)

Family

ID=22640558

Family Applications (1)

Country Status (11)

Cited By (5)

Families Citing this family (65)

Citations (26)

Family Cites Families (72)

• 1998
  • 1998-10-20 US US09/175,523 patent/US6365262B1/en not_active Expired - Lifetime
• 1999
  • 1999-08-03 KR KR1020017004835A patent/KR100702923B1/ko not_active Expired - Fee Related
  • 1999-08-03 DE DE69917800T patent/DE69917800T2/de not_active Expired - Lifetime
  • 1999-08-03 WO PCT/US1999/017562 patent/WO2000023655A1/en not_active Ceased
  • 1999-08-03 CA CA002346374A patent/CA2346374C/en not_active Expired - Fee Related
  • 1999-08-03 CN CNB998123331A patent/CN1161515C/zh not_active Expired - Fee Related
  • 1999-08-03 JP JP2000577361A patent/JP2002527797A/ja not_active Withdrawn
  • 1999-08-03 AU AU53332/99A patent/AU765493B2/en not_active Ceased
  • 1999-08-03 AT AT99938958T patent/ATE268412T1/de not_active IP Right Cessation
  • 1999-08-03 MX MXPA01003871A patent/MXPA01003871A/es not_active IP Right Cessation
  • 1999-08-03 EP EP99938958A patent/EP1127190B1/en not_active Expired - Lifetime
• 2001
  • 2001-12-27 US US10/034,912 patent/US6479132B2/en not_active Expired - Lifetime
• 2010
  • 2010-03-10 JP JP2010052872A patent/JP2010170146A/ja active Pending