WO1998056566A1 - Couches de poudre deposees par jet et formation de lits de poudre fine a l'aide de celles-ci - Google Patents

Couches de poudre deposees par jet et formation de lits de poudre fine a l'aide de celles-ci Download PDF

Info

Publication number
WO1998056566A1
WO1998056566A1 PCT/US1998/012280 US9812280W WO9856566A1 WO 1998056566 A1 WO1998056566 A1 WO 1998056566A1 US 9812280 W US9812280 W US 9812280W WO 9856566 A1 WO9856566 A1 WO 9856566A1
Authority
WO
WIPO (PCT)
Prior art keywords
slurry
depositing
layer
powder
binder
Prior art date
Application number
PCT/US1998/012280
Other languages
English (en)
Inventor
Emanuel M. Sachs
Michael J. Cima
Michael A. Caradonna
Jason Grau
James G. Serdy
Patrick C. Saxton
Scott A. Uhland
Jooho Moon
Original Assignee
Massachusetts Institute Of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Massachusetts Institute Of Technology filed Critical Massachusetts Institute Of Technology
Priority to JP50326999A priority Critical patent/JP4314414B2/ja
Priority to CA2293638A priority patent/CA2293638C/fr
Priority to EP98929036A priority patent/EP1009614A4/fr
Priority to US09/445,670 priority patent/US6596224B1/en
Publication of WO1998056566A1 publication Critical patent/WO1998056566A1/fr

Abstract

L'invention concerne un lit (32) de poudre formé par dépôt répété d'une boue contenant de la poudre. Des couches sont constituées par dépôt d'une dispersion liquide contenant la matière poudreuse voulue, qui est ensuite coulée en barbotine dans le lit de poudre de formage pour produire une nouvelle couche (34). La boue peut être déposée par tout moyen approprié, tel un balayage de trame ou vectoriel, par plusieurs jets simultanés qui coalescent avant que le liquide ne soit coulé en barbotine dans le lit, ou par des gouttes isolées dont le dépôt est commandé individuellement, ce qui permet de produire une surface régulière pour chaque couche.
PCT/US1998/012280 1996-05-24 1998-06-12 Couches de poudre deposees par jet et formation de lits de poudre fine a l'aide de celles-ci WO1998056566A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
JP50326999A JP4314414B2 (ja) 1997-06-13 1998-06-12 パウダーのジェッティング層とこれによるファインパウダーベッドの形成
CA2293638A CA2293638C (fr) 1997-06-13 1998-06-12 Couches de poudre deposees par jet et formation de lits de poudre fine a l'aide de celles-ci
EP98929036A EP1009614A4 (fr) 1997-06-13 1998-06-12 Couches de poudre deposees par jet et formation de lits de poudre fine a l'aide de celles-ci
US09/445,670 US6596224B1 (en) 1996-05-24 1998-06-12 Jetting layers of powder and the formation of fine powder beds thereby

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US5001597P 1997-06-13 1997-06-13
US60/050,015 1997-06-13

Publications (1)

Publication Number Publication Date
WO1998056566A1 true WO1998056566A1 (fr) 1998-12-17

Family

ID=21962941

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1998/012280 WO1998056566A1 (fr) 1996-05-24 1998-06-12 Couches de poudre deposees par jet et formation de lits de poudre fine a l'aide de celles-ci

Country Status (4)

Country Link
EP (1) EP1009614A4 (fr)
JP (1) JP4314414B2 (fr)
CA (1) CA2293638C (fr)
WO (1) WO1998056566A1 (fr)

Cited By (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001036171A2 (fr) * 1999-11-16 2001-05-25 University Of Warwick Procede et appareil de fabrication d'article
WO2001064385A1 (fr) * 2000-02-28 2001-09-07 Vaw Aluminium Ag Procede de production d'un composant cylindrique, partiellement cylindrique ou cylindrique creux dont la surface est alliee, et dispositif pour la mise en oeuvre de ce procede
US6397922B1 (en) 2000-05-24 2002-06-04 Massachusetts Institute Of Technology Molds for casting with customized internal structure to collapse upon cooling and to facilitate control of heat transfer
GB2378151A (en) * 2001-07-31 2003-02-05 Dtm Corp Fabricating a three-dimensional article from powder
US7108733B2 (en) 2003-06-20 2006-09-19 Massachusetts Institute Of Technology Metal slurry for electrode formation and production method of the same
US7455804B2 (en) 2001-02-15 2008-11-25 Huntsman Advanced Materials Americas Inc. Three-dimensional structured printing
US7578958B2 (en) 2001-05-24 2009-08-25 Huntsman Advanced Materials Americas Inc. Three-dimensional structured printing
WO2011067358A1 (fr) * 2009-12-02 2011-06-09 Prometal Rct Gmbh Dispositif d'impression pour une installation de prototypage rapide
WO2013030064A1 (fr) * 2011-08-26 2013-03-07 Swerea Ivf Ab Fabrication en couches de microcomposants multi-matériaux de forme libre
CN105936129A (zh) * 2015-03-04 2016-09-14 精工爱普生株式会社 三维造型物制造装置以及三维造型物
EP2200736B1 (fr) 2007-10-08 2016-11-30 Basf Se Procédé de préparation de corps façonnés dotés de propriétés catalytiques comme éléments de réacteur
US9649811B2 (en) 2011-04-17 2017-05-16 Stratasys Ltd. System and method for additive manufacturing of an object
US9839392B2 (en) 2011-07-20 2017-12-12 Elminda Ltd. Method and system for estimating brain concussion
US9895077B2 (en) 2010-01-18 2018-02-20 Elminda Ltd. Method for diagnosing a brain related disorder using brain network activity patterns
WO2018086645A1 (fr) * 2016-11-09 2018-05-17 Voxeljet Ag Procédé et dispositif de fabrication de pièces moulées en 3d par un procédé d'enduction par trempage
US10030961B2 (en) 2015-11-27 2018-07-24 General Electric Company Gap measuring device
EP3360659A1 (fr) * 2017-02-02 2018-08-15 Bundesrepublik Deutschland, vertreten durch den Bundesminister für Wirtschaft und Energie Procédé de fabrication additive par application continue de couches
FR3070134A1 (fr) * 2017-08-18 2019-02-22 3Dceram Procede et machine de fabrication d'au moins une piece en au moins un materiau ceramique et/ou metallique par la technique des procedes additifs
US10335856B2 (en) 2015-06-29 2019-07-02 Applied Materials, Inc. System for temperature controlled additive manufacturing
CN110167743A (zh) * 2016-11-07 2019-08-23 诺丁汉大学 增材制造
DE102010063982B4 (de) 2010-12-22 2020-07-16 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Verfahren und Vorrichtung zum Erzeugen einer dreidimensionalen Struktur auf einem Substrat
WO2020145980A1 (fr) 2019-01-10 2020-07-16 Hewlett-Packard Development Company, L.P. Impression en trois dimensions
US10828824B2 (en) 2012-11-05 2020-11-10 Stratasys Ltd. Method for direct inkjet printing of 3D objects
US12064850B2 (en) 2021-12-30 2024-08-20 Saint-Gobain Abrasives, Inc. Abrasive articles and methods for forming same

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9757801B2 (en) 2011-06-01 2017-09-12 Bam Bundesanstalt Für Material Forschung Und Prüfung Method for producing a moulded body and device
DE102013019716A1 (de) * 2013-11-27 2015-05-28 Voxeljet Ag 3D-Druckverfahren mit Schlicker
JP2015150708A (ja) * 2014-02-10 2015-08-24 株式会社リコー インクジェット３次元物体造形方法、プログラム、及びインクジェット３次元物体造形システム
JP2015171782A (ja) * 2014-03-12 2015-10-01 セイコーエプソン株式会社 三次元造形物製造装置および三次元造形物
JP6458346B2 (ja) 2014-03-18 2019-01-30 セイコーエプソン株式会社 三次元造形物製造装置および三次元造形物の製造方法
JP2015182424A (ja) * 2014-03-26 2015-10-22 セイコーエプソン株式会社 三次元造形物の製造方法、三次元造形物製造装置および三次元造形物
JP5904231B2 (ja) * 2014-04-16 2016-04-13 セイコーエプソン株式会社 造形方法
TW201609934A (zh) 2014-07-01 2016-03-16 精工愛普生股份有限公司 三維造形用組合物、三維造形物之製造方法及三維造形物
US9751259B2 (en) * 2014-10-07 2017-09-05 Xerox Corporation System and method for operating a three-dimensional printer to compensate for radial velocity variations
JP5920498B2 (ja) * 2015-02-04 2016-05-18 セイコーエプソン株式会社 造形方法
JP6313254B2 (ja) * 2015-03-18 2018-04-18 株式会社東芝 三次元造形方法
EP3231588A1 (fr) * 2016-04-12 2017-10-18 Evonik Röhm GmbH Polymere d'emulsion en phase molle seche par pulverisation pour le remplissage du soufflet dans des couches de polymere perle selon le procede de projection de liant
US10307823B1 (en) * 2017-11-13 2019-06-04 General Electric Company Methods and systems for repairing powder containment structures
KR102410683B1 (ko) * 2020-03-26 2022-07-18 주식회사 정상기술 주물사 소재를 이용한 냉각코어의 3d 프린팅 방법
KR102383639B1 (ko) * 2020-03-26 2022-04-06 최성환 주물사 소재를 이용한 냉각코어의 3d 프린팅 방법

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4505987A (en) * 1981-11-10 1985-03-19 Oiles Industry Co., Ltd. Sliding member
US5038014A (en) * 1989-02-08 1991-08-06 General Electric Company Fabrication of components by layered deposition
US5121329A (en) * 1989-10-30 1992-06-09 Stratasys, Inc. Apparatus and method for creating three-dimensional objects
US5122632A (en) * 1989-10-20 1992-06-16 Konrad Kinkelin Device for laser plasma coating
US5204055A (en) * 1989-12-08 1993-04-20 Massachusetts Institute Of Technology Three-dimensional printing techniques
US5429790A (en) * 1993-03-29 1995-07-04 Takahashi; Yasunori Method for preparing multilayer dielectric powder condensers
US5433280A (en) * 1994-03-16 1995-07-18 Baker Hughes Incorporated Fabrication method for rotary bits and bit components and bits and components produced thereby
US5510066A (en) * 1992-08-14 1996-04-23 Guild Associates, Inc. Method for free-formation of a free-standing, three-dimensional body
US5529471A (en) * 1995-02-03 1996-06-25 University Of Southern California Additive fabrication apparatus and method
US5531955A (en) * 1993-09-14 1996-07-02 Katayama Special Industries, Ltd. Method of manufacturing a metallic porous sheet having pores surrounded by a three-dimensional net-shaped framework of metallic layers
US5540884A (en) * 1991-09-12 1996-07-30 The Dow Chemical Company Method of making co-fired, multilayer substrates
US5616423A (en) * 1994-05-19 1997-04-01 Sumitomo Metal Industries, Ltd. Ceramic substrate having a multilayered metallic thin film
US5622769A (en) * 1993-02-12 1997-04-22 Kabushiki Kaisha Toshiba Ceramic circuit board having a thermal conductivity substrate

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4944817A (en) * 1986-10-17 1990-07-31 Board Of Regents, The University Of Texas System Multiple material systems for selective beam sintering
US5637175A (en) * 1988-10-05 1997-06-10 Helisys Corporation Apparatus for forming an integral object from laminations
US5286573A (en) * 1990-12-03 1994-02-15 Fritz Prinz Method and support structures for creation of objects by layer deposition
WO1994019112A2 (fr) * 1993-02-18 1994-09-01 Massachusetts Institute Of Technology Impression tridimensionnelle de haute qualite a grande vitesse
JPH07227895A (ja) * 1994-02-04 1995-08-29 Internatl Business Mach Corp <Ibm> 部品製造方法
JPH08217525A (ja) * 1995-02-15 1996-08-27 Fuji Elelctrochem Co Ltd セラミックスグリーンシートの成形乾燥方法及び装置

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4505987A (en) * 1981-11-10 1985-03-19 Oiles Industry Co., Ltd. Sliding member
US5038014A (en) * 1989-02-08 1991-08-06 General Electric Company Fabrication of components by layered deposition
US5122632A (en) * 1989-10-20 1992-06-16 Konrad Kinkelin Device for laser plasma coating
US5121329A (en) * 1989-10-30 1992-06-09 Stratasys, Inc. Apparatus and method for creating three-dimensional objects
US5204055A (en) * 1989-12-08 1993-04-20 Massachusetts Institute Of Technology Three-dimensional printing techniques
US5540884A (en) * 1991-09-12 1996-07-30 The Dow Chemical Company Method of making co-fired, multilayer substrates
US5510066A (en) * 1992-08-14 1996-04-23 Guild Associates, Inc. Method for free-formation of a free-standing, three-dimensional body
US5622769A (en) * 1993-02-12 1997-04-22 Kabushiki Kaisha Toshiba Ceramic circuit board having a thermal conductivity substrate
US5429790A (en) * 1993-03-29 1995-07-04 Takahashi; Yasunori Method for preparing multilayer dielectric powder condensers
US5531955A (en) * 1993-09-14 1996-07-02 Katayama Special Industries, Ltd. Method of manufacturing a metallic porous sheet having pores surrounded by a three-dimensional net-shaped framework of metallic layers
US5433280A (en) * 1994-03-16 1995-07-18 Baker Hughes Incorporated Fabrication method for rotary bits and bit components and bits and components produced thereby
US5616423A (en) * 1994-05-19 1997-04-01 Sumitomo Metal Industries, Ltd. Ceramic substrate having a multilayered metallic thin film
US5529471A (en) * 1995-02-03 1996-06-25 University Of Southern California Additive fabrication apparatus and method

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP1009614A4 *

Cited By (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2001036171A3 (fr) * 1999-11-16 2002-05-10 Univ Warwick Procede et appareil de fabrication d'article
WO2001036171A2 (fr) * 1999-11-16 2001-05-25 University Of Warwick Procede et appareil de fabrication d'article
US6830643B1 (en) 1999-11-16 2004-12-14 3D Systems Inc Method of manufacturing an item and apparatus for manufacturing an item
WO2001064385A1 (fr) * 2000-02-28 2001-09-07 Vaw Aluminium Ag Procede de production d'un composant cylindrique, partiellement cylindrique ou cylindrique creux dont la surface est alliee, et dispositif pour la mise en oeuvre de ce procede
US6858262B2 (en) 2000-02-28 2005-02-22 Vaw Aluminium Ag Method for producing a surface-alloyed cylindrical, partially cylindrical or hollow cylindrical component and a device for carrying out said method
AU781334B2 (en) * 2000-02-28 2005-05-19 Vaw Aluminium Ag Method for producing a surface-alloyed cylindrical, partially cylindrical or hollow cylindrical component and a device for carrying out said method
US6397922B1 (en) 2000-05-24 2002-06-04 Massachusetts Institute Of Technology Molds for casting with customized internal structure to collapse upon cooling and to facilitate control of heat transfer
US6629559B2 (en) 2000-05-24 2003-10-07 Massachusetts Institute Of Technology Molds for casting with customized internal structure to collapse upon cooling and to facilitate control of heat transfer
US7455804B2 (en) 2001-02-15 2008-11-25 Huntsman Advanced Materials Americas Inc. Three-dimensional structured printing
US7767132B2 (en) 2001-02-15 2010-08-03 Huntsman Advanced Materials Americas, Inc. Three-dimensional structured printing
US7578958B2 (en) 2001-05-24 2009-08-25 Huntsman Advanced Materials Americas Inc. Three-dimensional structured printing
US6694207B2 (en) 2001-07-31 2004-02-17 3D Systems, Inc. Selective laser sintering with interleaved fill scan
GB2378151A (en) * 2001-07-31 2003-02-05 Dtm Corp Fabricating a three-dimensional article from powder
US7108733B2 (en) 2003-06-20 2006-09-19 Massachusetts Institute Of Technology Metal slurry for electrode formation and production method of the same
EP2200736B1 (fr) 2007-10-08 2016-11-30 Basf Se Procédé de préparation de corps façonnés dotés de propriétés catalytiques comme éléments de réacteur
WO2011067358A1 (fr) * 2009-12-02 2011-06-09 Prometal Rct Gmbh Dispositif d'impression pour une installation de prototypage rapide
US9895077B2 (en) 2010-01-18 2018-02-20 Elminda Ltd. Method for diagnosing a brain related disorder using brain network activity patterns
DE102010063982B4 (de) 2010-12-22 2020-07-16 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Verfahren und Vorrichtung zum Erzeugen einer dreidimensionalen Struktur auf einem Substrat
US11872766B2 (en) 2011-04-17 2024-01-16 Stratasys Ltd. System and method for additive manufacturing of an object
US11254057B2 (en) 2011-04-17 2022-02-22 Stratasys Ltd. System and method for additive manufacturing of an object
US10406752B2 (en) 2011-04-17 2019-09-10 Stratasys Ltd. System and method for additive manufacturing of an object
US10016937B2 (en) 2011-04-17 2018-07-10 Stratasys Ltd. System and method for additive manufacturing of an object
US9649811B2 (en) 2011-04-17 2017-05-16 Stratasys Ltd. System and method for additive manufacturing of an object
US9839392B2 (en) 2011-07-20 2017-12-12 Elminda Ltd. Method and system for estimating brain concussion
EA025234B1 (ru) * 2011-08-26 2016-12-30 Диджитл Метал Аб Способ послойного производства трехмерного объекта
US9545669B2 (en) 2011-08-26 2017-01-17 Digital Metal Ab Layered manufacturing of free-form multi-material micro-components
WO2013030064A1 (fr) * 2011-08-26 2013-03-07 Swerea Ivf Ab Fabrication en couches de microcomposants multi-matériaux de forme libre
CN103826830A (zh) * 2011-08-26 2014-05-28 数字金属Ab公司 自由形式的多材料微型元件的分层制造
JP2014529523A (ja) * 2011-08-26 2014-11-13 ディジタル メタル アーベー 多材料から構成される自由造形可能な微細部品の積層造形法
US10828824B2 (en) 2012-11-05 2020-11-10 Stratasys Ltd. Method for direct inkjet printing of 3D objects
CN105936129A (zh) * 2015-03-04 2016-09-14 精工爱普生株式会社 三维造型物制造装置以及三维造型物
US10335856B2 (en) 2015-06-29 2019-07-02 Applied Materials, Inc. System for temperature controlled additive manufacturing
US10030961B2 (en) 2015-11-27 2018-07-24 General Electric Company Gap measuring device
CN110167743B (zh) * 2016-11-07 2021-10-12 诺丁汉大学 增材制造
CN110167743A (zh) * 2016-11-07 2019-08-23 诺丁汉大学 增材制造
WO2018086645A1 (fr) * 2016-11-09 2018-05-17 Voxeljet Ag Procédé et dispositif de fabrication de pièces moulées en 3d par un procédé d'enduction par trempage
EP3360659A1 (fr) * 2017-02-02 2018-08-15 Bundesrepublik Deutschland, vertreten durch den Bundesminister für Wirtschaft und Energie Procédé de fabrication additive par application continue de couches
EP3444050A3 (fr) * 2017-08-18 2019-02-27 S.A.S 3DCeram-Sinto Procede et machine de fabrication d'au moins une piece en au moins un materiau ceramique et/ou metallique par la technique des procedes additifs
FR3070134A1 (fr) * 2017-08-18 2019-02-22 3Dceram Procede et machine de fabrication d'au moins une piece en au moins un materiau ceramique et/ou metallique par la technique des procedes additifs
WO2020145980A1 (fr) 2019-01-10 2020-07-16 Hewlett-Packard Development Company, L.P. Impression en trois dimensions
EP3887127A4 (fr) * 2019-01-10 2022-07-06 Hewlett-Packard Development Company, L.P. Impression en trois dimensions
US11787108B2 (en) 2019-01-10 2023-10-17 Hewlett-Packard Development Company, L.P. Three-dimensional printing
US12064850B2 (en) 2021-12-30 2024-08-20 Saint-Gobain Abrasives, Inc. Abrasive articles and methods for forming same

Also Published As

Publication number Publication date
EP1009614A4 (fr) 2004-04-21
JP2002507940A (ja) 2002-03-12
CA2293638C (fr) 2010-08-24
CA2293638A1 (fr) 1998-12-17
JP4314414B2 (ja) 2009-08-19
EP1009614A1 (fr) 2000-06-21

Similar Documents

Publication Publication Date Title
US6596224B1 (en) Jetting layers of powder and the formation of fine powder beds thereby
CA2293638C (fr) Couches de poudre deposees par jet et formation de lits de poudre fine a l&#39;aide de celles-ci
EP1268165B1 (fr) Procede et dispositif de fabrication d&#39;un composant de construction suivant une technique de deposition multicouche, et moule ou noyau tel que fabrique par le procede
KR102317567B1 (ko) 분말 분배를 이용한 적층 제조
US7700016B2 (en) Method and apparatus for fabricating three dimensional models
US6036777A (en) Powder dispensing apparatus using vibration
KR20180122643A (ko) 인 시추 인퓨전을 활용하여 물체들의 솔리드 프리폼 제조를 위한 방법 및 장치
US20200269320A1 (en) Molding method and apparatus, particularly applicable to metal and/or ceramics
JP2017524579A (ja) 複数素材三次元プリンタ
US20200009795A1 (en) Interface layers and removable object supports for 3d printing
US11806927B2 (en) Method of continuous high-speed 3D printing
Cima et al. Slurry-based 3DP and fine ceramic components
WO2001068336A2 (fr) Procede de fabrication d&#39;une piece structurelle au moyen d&#39;une technique de depot
JPH08192468A (ja) 立体モデルの製造方法及び装置
US20230321723A1 (en) Method for producing a 3d shaped article, and device using a sieve plate
JP7234716B2 (ja) 立体造形用粉末、粉末入り容器、立体造形物の製造方法、及び立体造形物の製造装置
DeBear Slurry deposition of high quality layers for 3D printing

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CA JP US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
ENP Entry into the national phase

Ref document number: 2293638

Country of ref document: CA

Ref country code: CA

Ref document number: 2293638

Kind code of ref document: A

Format of ref document f/p: F

WWE Wipo information: entry into national phase

Ref document number: 1998929036

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 09445670

Country of ref document: US

WWP Wipo information: published in national office

Ref document number: 1998929036

Country of ref document: EP