Classifications

• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04D—ROOF COVERINGS; SKY-LIGHTS; GUTTERS; ROOF-WORKING TOOLS
  • E04D1/00—Roof covering by making use of tiles, slates, shingles, or other small roofing elements
  • E04D1/26—Strip-shaped roofing elements simulating a repetitive pattern, e.g. appearing as a row of shingles
  • E04D1/265—Strip-shaped roofing elements simulating a repetitive pattern, e.g. appearing as a row of shingles the roofing elements being rigid, e.g. made of metal, wood or concrete
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B26/00—Compositions of mortars, concrete or artificial stone, containing only organic binders, e.g. polymer or resin concrete
  • C04B26/02—Macromolecular compounds
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04D—ROOF COVERINGS; SKY-LIGHTS; GUTTERS; ROOF-WORKING TOOLS
  • E04D1/00—Roof covering by making use of tiles, slates, shingles, or other small roofing elements
  • E04D1/12—Roofing elements shaped as plain tiles or shingles, i.e. with flat outer surface
  • E04D1/20—Roofing elements shaped as plain tiles or shingles, i.e. with flat outer surface of plastics; of asphalt; of fibrous materials
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
  • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
  • C04B2111/00586—Roofing materials

Definitions

• This invention relates to shingles of the type suitable for providing an aesthetically pleasing appearance and a high degree of weatherability when applied to a building. More particularly, this invention relates to shingles comprised of organic, resinous material and an inorganic filler material.
• clay and slate tiles require significant labor to apply.
• the asphalt or wood shingles are nailable and are simply nailed to a roof deck in courses, usually from the bottom or eave to the top or ridge of the roof.
• Clay, concrete, and slate tiles are heavier than asphalt shingles, and require more support to hold up the roof .
• the installed cost of clay and slate tiles exceeds that of asphalt shingles.
• Clay and slate tiles are inherently fragile, and surfer much breakage during shipping and installation. These materials are fragile even after installation on the roof, and can be damaged by foot traffic on the roof.
• Wooden shake shingles are generally flat boards, usually of cedar or other coniferous trees.
• the wooden shakes are nailed in courses on the roof deck, with the exposed or tab portions of the shingles of a subsequent course being laid over the headlap portions of the previous course of shingles.
• the shingles are cut so that the wood grain runs up the slope of the roof for an aesthetically pleasing appearance.
• the cutting of the wood, and the subsequent weathering of the shingles after installation on the roof create grooves and ridges running in the direction of the wood grain.
• a disadvantage of wooden shake shingles is that they absorb moisture and swell. Therefore, they must be applied in a spaced-apart arrangement to allow room for expansion.
• any roofing material is to be able to resist fires. This is particularly true in regions having a hot and dry climate, although fire resistance is desirable everywhere.
• a particularly important aspect of fire resistance is the ability of the roofing material to prevent a fire, or a source of heat such as a burning ember, from burning through the roofing material to thereby expose the roof deck or interior of the building to the fire.
• Metal roofs and clay and tile roofs have inherent advantages in fire resistance over wood-shake shingle roofs.
• Asphalt shingles contain greater than 60 percent filler of finely ground inorganic paniculate matter, such as limestone, and therefore are sufficiently fire-resistant to obtain a Class A fire rating when measured by appropriate tests.
• Wooden shake shingles even when treated with a fire-retardant material, are not generally fire-resistant and cannot achieve a Class A fire rating.
• Shake shingles are particularly prone to failing the fire tests (absent fireproofing underlayments) because the shingles cannot be placed with side edges abutting, and the gaps between adjacent shingles contribute to the failure of the shake shingles to pass the fire tests.
• the ideal shingle would have an aesthetically pleasing appearance, such as the appearance of a wooden shake shingle, and yet would be superior to the wooden shake shingle in both weatherability and fire resistance.
• the shingle would be lightweight, low in manufacturing cost, and would have a generally permanent color.
• the shingle comprises an organic, resinous material and a filler material.
• the shingle is preferably molded, and most preferably compression molded, and is nailable onto a roof deck to form an aesthetically pleasing roof-covering having high weatherability.
• the shingle has the appearance of a shake shingle.
• the organic, resinous material in the shingle is in an amount within the range of from about 12 to about 35 percent by weight, and a filler material is in an amount within the range of from about 65 to about 88 percent by weight.
• the high amount of inorganic filler material contributes to a Class A fire-resistance rating.
• the resin comprises polyester resin derived from input stock containing PET.
• the filler material preferably comprises one or more of the group consisting of clay particles, slate particles, shale particles, and glass fibers.
• the resin contains no pigment other than the color of the filler material.
• a roofing shingle comprising organic, resinous material and an inorganic filler material, the shingle having a top surface, two side surfaces, an upper end, and a lower or butt end, defining a cavity on the underside of the shingle, with ribs positioned within the cavity.
• the shingle top surface has a tab portion which is normally exposed on the roof and a headlap portion which is normally covered up on the roof, the lower part of the tab portion being thicker than the remainder of the tab portion, and the upper part of the headlap portion being thinner than the remainder of the headlap portion to facilitate efficient packing of two adjacent shingles during packaging, with the top portions of the two shingles in contact with each other, and the lower part of the tab portion being aligned with the upper part of the headlap portion.
• the two side surfaces, the upper end, and the butt end extend downwardly, with the bottom or downwardly extending edges of the two side surfaces, the upper end, and the butt end generally lying in a common plane, and ribs also extend generally downwardly from the top surface to the same plane, so that the ribs support the top surface of the shingle, thereby preventing sag of the shingle when the shingle is heated.
• the shingle has a nailing strip in the lower end of the headlap portion, with the ribs in the lower end of the tab portion being recessed so that they do not extend fully to the common plane in the area which normally overlies the nailing strip of the previous course of shingles on a roof, so that the ribs do not come in contact with nails in the nailing strips of the previously laid course of shingles.
• the tab portion of the shingle is narrower than the headlap portion so that the distance between the shingle side surfaces in the tab portion is shorter than the distance between the side surfaces in the headlap portion.
• the roofing shingle has a nailing strip comprising a plurality of ridges molded into the top surface of the shingle, and the shingle has ribs on the underside of the top surface which are aligned with the ridges in the nailing strip, with a ridge positioned above each rib, so that nails striking the muling strip will be directed to the spaces between the ridges, and thereby the nails will be directed away from the ribs.
• the invention also includes a roof comprising a roof deck and a plurality of roofing shingles of the invention.
• Figure 1 is a schematic plan view of the top of a shingle of the invention.
• Figure 2 is a view in elevation taken along line 2-2 of Figure 1.
• Figure 3 is a schematic plan view of the underside of the shingle shown in
• Figure 4 is a cross-sectional view in elevation taken along line 4-4 of Figure
• Figure 5 is a schematic view in perspective of a bundle of shingles of the invention.
• Figure 6 is a schematic view in elevation of a pair of mated shingles of the invention.
• Figure 7 is a schematic view in perspective of a roof containing shingles of the invention.
• Figure 8 is a schematic view in elevation illustrating detail of the joint where two shingles are molded together.
• roofing shingles which are similar in appearance to wood-shake shingles. It is to be understood, however, that the terms "shingles” and “roofing shingles” also include shingles, tiles, and panels; and the shingles, tiles, and panels can have appearances other than wood-shake shingles, such as, for example, slate panels or tiles and mission tiles.
• the shingle 10 has a top surface 12, two side surfaces 14, upper end 16, and lower or butt end 18.
• the top surface of the shingle can be divided into a tab portion 20 and a headlap portion 22.
• the headlap portion 22 of a shingle is covered by the exposed or tab portion 20 of the next course of shingles.
• the tab portion of the shingle has a multiplicity of grooves running in a direction which is intended to be up the slope of the roof when the shingle is installed on the roof to give the appearance of a wooden shake shingle.
• the butt end of the shingle preferably has a plurality of oblique surfaces 23 at differing angles to the butt end to provide the viewer with something other than a simple, straight butt end of the shingle. This will greatly enhance the aesthetic appearance of the shingle.
• the top surface of the shingle contains optional nailing strips to indicate to the roofer the best location for the nails or staples to be applied to the shingle.
• the nailing strip 24 at the upper end of the headlap portion 22 of the shingle preferably contains ridges 26 which serve as a nailing indicator for the roofer, and which make a stronger structure for nailing purposes.
• the ridges can be molded into the surface of the shingle.
• nailing strip 28 at the lower end of the headlap portion preferably contains ridges 30 for the same purpose.
• the ridges are preferably oriented parallel to the side surfaces of the shingle.
• the ridges can be made to look similar to the wood-shake markings or grooves in the tab portion of the shingle, so that any surface showing through a gap or cutout will be similar in appearance to the wood-shake look of the tab portion of the shingle.
• the side surfaces 14 have curved portions 32 so that the width of tab portion 20 (in the direction from left to right as shown in Figure 1) is less than the width of the headlap portion 22.
• This design enables the shingles of the invention to be applied so that the side surfaces of the headlap portions of adjacent shingles on a roof can be physically abutting, and yet the tab portions of the shingles need not be abutting. By avoiding a requirement that the tab portions of the shingles need to be abutting, a more pleasing appearance can be made on the roof.
• the roof system By designing the shingle to allow the headlap areas to be abutting, the roof system will have a greater chance of meeting the fire standards of a Class A shingle because there will be no gap providing a thermal short- circuit to expose the roof deck to the heat of the burning brand. This is a distinct improvement over wooden shake shingles.
• the shingle can be molded as a double molded shingle, with a groove, such as break line 34, which enables the shingle to be broken or split into two smaller shingles.
• the break line is sufficiently thin so as to enable the shingle to be separated into two shingles by hand.
• the lower part 36 of the tab portion 20 is raised or thicker than the remainder of the tab portion. This improves the aesthetic appearance on the roof by making the butt end 18 of the shingles thicker, thereby making the entire shingle appear thicker to a person viewing the roof from the ground.
• the shingle has a corresponding thinner or tapered portion at the other end of the shingle, which is at the upper part 38 of the headlap portion 22.
• two shingles can be packed or nested for packaging and storage in an efficient manner, with the thickened lower parts 36 of the tab portions in contact with or nesting into the thinner upper parts 38 of the headlap portion.
• the top surface 12, two side surfaces 14, upper end 16, and butt end 18 define an open space or cavity 40 on the underside of the shingle.
• the side surfaces, the upper end, and the butt end all extend downwardly from the top surface to the extent that the bottom edges of the side surfaces and upper and butt ends all lie in a common plane 42.
• a plurality of ribs 44 are molded into the cavity to strengthen the shingle.
• the ribs can be of any design, but are conveniently arranged generally parallel to the side surfaces 14 of the shingle.
• One of the purposes of the ribs is to provide integrity to the shingle so that, when fastened to the roof with nails, the shingle will not split or tear away from the nails.
• Another purpose of the ribs is to provide sufficient flexural strength and rigidity required for the product with efficient use of material. Since the shingles of the invention are nailable, the nails can be driven anywhere through the shingle, but are preferably driven through the nailing strips. Nail holes are not required.
• the ribs are preferably molded integrally with the top surface 12.
• the ribs can support the top surface of the shingle. This will enable the shingle to be supported to prevent sagging when the shingle is in a heated condition, such as during the cool-down phase following the molding process, or during storage of the shingles, or after application to a roof.
• the ribs Although it is generally desirable for the ribs to extend all the way down from the underside of the top surface to the common plane, there is one area where the ribs should be shallower.
• nails are driven through the lower nailing strip 28.
• the overlying shingle will have the lower end 48 of the tab portion 20 directly over nailing strip 28. If any nails are not completely driven home, the rib of the overlying shingle could potentially rest on a nail protruding above the top surface of the shingle. For this reason, the ribs beneath the lower end 48 of the tab portion are provided with recess 50, as shown in Figure 4. The recess keeps the ribs from coming into contact with nails in the nailing strips of the previously laid course of shingles.
• the shingle is adapted with several side ribs 46 which are generally perpendicular to the side surfaces 14. These side ribs prevent a shingle from nesting within an adjacent shingle while the shingles are packaged in a bundle. "Nesting" is where one of the side surfaces slides or slips into the cavity of an adjacent shingle in a bundle. The nesting of the shingles after they are packaged in a bundle is undesirable because nesting makes the bundle smaller, thereby having the effect of loosening the bundle.
• the shingle can be packaged in a bundle 52 and secured by any means, such as strap 54.
• the bundle contains two different shingle types.
• First is a wide shingle, such as shingle 56.
• the second is a double molded shingle, having a break line such as break line 34, so that the shingle can be broken by hand into an intermediate shingle 58 and a narrow shingle 60.
• the cutout between the intermediate and narrow shingles is indicated at 62.
• the break line 34 is shown in more detail in Figure 8.
• the two shingles 58 and 60 are joined by a thin attachment strip 61 formed during the molding process, which is defined by the break line 34.
• the attachment strip 61 is of sufficient strength to enable the double molded shingle to be applied on the roof as two connected shingles, and yet thin enough that a roofer can separate the parts of the double molded shingle into two distinct shingles.
• the attachment strip 61 is narrower on one side, such as the right hand side 63 shown in Figure 8, so that the splitting of the double molded shingle into two distinct shingles by hand will always result in a predictable, even break line which is aesthetically pleasing on the roof.
• the intermediate and narrow shingles For packaging purposes it is advantageous for the intermediate and narrow shingles to have a combined width approximately equal to the width of the wide shingle.
• a b + c
• a is the width of the wide shingle 56
• the terminology “a equals b + c” is intended to include arrangements in which the width of "a” is within 5 percent of the width of b + c.
• Preferred widths for the three shingles are about 13 inches (330 mm) for "a”, about SVi inches (140 mm) for "b”, and about TA inches (190 mm) for "c”.
• the shingles are shown as being applied as a roof covering on a roof.
• the roof comprises an appropriate support structure such as joists or rafters 64 and a roof deck 66 which can be continuous or intermittently spaced boards.
• the shingles are laid in courses from the bottom up, and provide an aesthetically pleasing appearance.
• a water-resistant roofing felt 68 is preferably applied above each course of shingles to overlay the upper nailing strip 24.
• the composition of the shingle includes organic, resinous material in an amount within the range of from about 12 to about 35 percent by weight, and a filler material in an amount within the range of from about 65 to about 88 percent by weight.
• the resinous material is present in an amount within the range of from about 15 to about 24 percent by weight, and a filler material is present in an amount within the range of from about 76 to about 85 percent by weight.
• the shingle comprises about 20 percent resinous material by weight and about 80 percent filler material by weight.
• the terms "resin” and "resinous material” mean any organic substance which can act as a matrix for the inorganic filler material.
• the resin or resinous material can be either a thermoplastic or thermoset, but is preferably a thermoset material.
• materials which are resinous and suitable for use with the invention are polyester, polyethyleneterephthalate (PET), polycarbonate, and polypropylene resins.
• PET polyethyleneterephthalate
• the resins preferred are plastic resins, containing no asphalts, or only small amounts of asphalt, such as less than about 5 percent.
• Thermoset polyester resins are the most preferred, although a small amount of PET can be added to the input stock in the resin process so that the polyester resin is derived from input stock containing PET. This provides more flexibility to the shingle.
• resins suitable for use with the invention include resins E-606, E-650, E-120, and 55M-70 from
• the resinous material can include small amounts of other materials such as mold release agents.
• filler materials can be used with the invention. Examples include clay, aluminum trihydrate, glass fibers of various lengths, other fibrous reinforcements (organic or inorganic), and finely divided slate, shale, limestone, fly ash, bottom ash, and talc.
• the filler material is finely ground. The particles must be small enough to blend into the resin matrix, especially when molded into narrow parts, such as the ridges and the ribs. The filler particles cannot be too small or else the surface area will be so great as to excessively bind up all the resin, thereby requiring increased amounts of the resin, which is a much more expensive component of the composition than is the filler material.
• Preferred fillers include slate dust which imparts a black color, green shale, red clay, and white clay. These fillers can be combined to provide commonly used wood- shake shingle colors such as light brown, gray, and dark brown. By selecting the appropriate color for the filler material, the desired color of the molded shingle can be produced without the use of pigments. This is an important feature of the molded shingle because experience has shown that molded roof tiles and shingles using pigments tend to bleach out or wear off and change color after the shingle has been subjected to weathering on a roof. It is preferred that any slate present have a fineness such that substantially all the material is capable of passing through an 18-mesh screen, and that any shale present also have a fineness such that substantially all the material is capable of passing through an 18- mesh screen.
• the composition includes no more than about five percent, and more preferably about two to three percent by weight, chopped glass fibers, such as one-quarter inch (6.35 mm) 405 glass fibers from Owens Corning, Toledo, Ohio. A smaller percentage of other reinforcement fibers, such as nylon fibers, may also be used.
• the flexural strength is at a level sufficient for the product requirements with only a small percentage of reinforcement fibers in the composition. One would expect a higher percentage of reinforcement fiber would be needed for such flexural strength.
• a test for flexural strength is an International Congress of Building Officials (ICBO) test which measures the load- carrying capacity of a material and simulates the loading of roofing materials installed over spaced sheathing.
• ICBO International Congress of Building Officials
• the molding process includes mixing the resin and the filler by any suitable means, such as a bulk molding compound mixer.
• a charge of the composition can be applied to a compression mold operating at a temperature within the range of from about 300°F (149°C) to about 350°F (177°C) and within a pressure range of from about 600 psi (4.1 MPa) to about 800 psi (5.5 MPa). If glass fibers are used, they should be added after nearly all the mixing is completed.
• Other molding processes such as injection molding or transfer molding, can be used with the invention.
• a very important attribute of the shingles of the invention is that when applied to a roof they will form a Class A fire barrier.
• the Class A fire barrier is determined by testing the roof according to ASTM test E 108-93 for flame spread, burning brand, and intermittent flame.
• the shingles of this invention can successfully pass the fire test without additional fireproofing measures such as additional layers of underlayment of type 30 roofing felt or mineral surface cap sheets.
• the Class A fire rating can be achieved with the shingles of the invention, applied over either a solid wood deck or spaced sheathing, with an interleaved layer, such as 18-inch (457-mm) type 30 felts, applied on 10-inch (254- mm) centers or less, as is traditional in the application of wood-shake shingles.
• the invention can be useful for aesthetically pleasing roofing shingles having high weatherability and a Class A fire rating.

Landscapes

• Engineering & Computer Science (AREA)
• Structural Engineering (AREA)
• Architecture (AREA)
• Civil Engineering (AREA)
• Chemical & Material Sciences (AREA)
• Ceramic Engineering (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• Roof Covering Using Slabs Or Stiff Sheets (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (1)

Applications Claiming Priority (2)

Publications (1)

Family

ID=23694452

Family Applications (1)

Country Status (3)

Cited By (1)

Citations (9)

• 1996
  • 1996-04-10 AU AU54463/96A patent/AU5446396A/en not_active Abandoned
  • 1996-04-10 WO PCT/US1996/004825 patent/WO1996034160A1/en active Application Filing
  • 1996-04-17 TW TW085104596A patent/TW323312B/zh active

Patent Citations (9)

Non-Patent Citations (2)

Also Published As

Similar Documents

Legal Events