WO1996001711A1 - Enveloppe de guidage et protections anti-projections utilisees avec une machine de coulee a deux cylindres et un panier de coulee - Google Patents

Enveloppe de guidage et protections anti-projections utilisees avec une machine de coulee a deux cylindres et un panier de coulee Download PDF

Info

Publication number
WO1996001711A1
WO1996001711A1 PCT/CA1995/000406 CA9500406W WO9601711A1 WO 1996001711 A1 WO1996001711 A1 WO 1996001711A1 CA 9500406 W CA9500406 W CA 9500406W WO 9601711 A1 WO9601711 A1 WO 9601711A1
Authority
WO
WIPO (PCT)
Prior art keywords
tundish
twin
steel
pool
casting rolls
Prior art date
Application number
PCT/CA1995/000406
Other languages
English (en)
Inventor
Liu-Kuen Chiang
Original Assignee
Ipsco Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ipsco Inc. filed Critical Ipsco Inc.
Priority to AU28775/95A priority Critical patent/AU2877595A/en
Publication of WO1996001711A1 publication Critical patent/WO1996001711A1/fr

Abstract

Une machine de coulée à deux cylindres produit une plaque d'acier dont l'épaisseur est, de préférence, de 5-35 mm. De préférence, un panier primaire (par exemple de 30 tonnes) et un panier secondaire (par exemple de 5 tonnes) sont placés au-dessus de la machine de coulée. Une atmosphère de gaz inerte ou réducteur est créée au-dessus de la surface de la masse d'acier en fusion accumulé au-dessus du point de contact des deux cylindres. Une enveloppe de guidage (4) rectangulaire, de forme allongée, s'étend, vers le bas, depuis l'orifice de sortie du panier secondaire, et une protection anti-projections (5) transversale s'étend généralement horizontalement, vers l'extérieur, depuis l'enveloppe de guidage (4), sur le dessous du panier secondaire. L'enveloppe de guidage (4) et la protection anti-projections (5) peuvent également être utilisées avec un seul panier et avec d'autres types de machines de coulée.
PCT/CA1995/000406 1994-07-08 1995-07-07 Enveloppe de guidage et protections anti-projections utilisees avec une machine de coulee a deux cylindres et un panier de coulee WO1996001711A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU28775/95A AU2877595A (en) 1994-07-08 1995-07-07 Guiding shroud and splash guard for use with twin-roll caster and tundish

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US27267894A 1994-07-08 1994-07-08
US08/272,678 1994-07-08
US46606595A 1995-06-06 1995-06-06
US08/466,065 1995-06-06

Publications (1)

Publication Number Publication Date
WO1996001711A1 true WO1996001711A1 (fr) 1996-01-25

Family

ID=26955673

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA1995/000406 WO1996001711A1 (fr) 1994-07-08 1995-07-07 Enveloppe de guidage et protections anti-projections utilisees avec une machine de coulee a deux cylindres et un panier de coulee

Country Status (2)

Country Link
AU (1) AU2877595A (fr)
WO (1) WO1996001711A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3924001A1 (de) * 1988-07-26 1990-02-01 Ishikawajima Harima Heavy Ind Doppelrollen-stranggiessmaschine
WO1994002269A1 (fr) * 1992-07-21 1994-02-03 Ishikawajima-Harima Heavy Industries Company Limited Dispositif de coulee de bandes de metal

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3924001A1 (de) * 1988-07-26 1990-02-01 Ishikawajima Harima Heavy Ind Doppelrollen-stranggiessmaschine
WO1994002269A1 (fr) * 1992-07-21 1994-02-03 Ishikawajima-Harima Heavy Industries Company Limited Dispositif de coulee de bandes de metal

Also Published As

Publication number Publication date
AU2877595A (en) 1996-02-09

Similar Documents

Publication Publication Date Title
US7594533B2 (en) Casting steel strip
EP0830223B1 (fr) Absorbeurs de chaleur sans contact pour la coulee en bandes
US5381857A (en) Apparatus and method for continuous casting
US6220335B1 (en) Casting metal strip
US5857514A (en) Strip casting
KR20110020905A (ko) 가장자리 부분의 품질을 제어하기 위한 스트립 캐스팅 방법 및 그를 위한 장치
WO1996001710A1 (fr) Procede de coulee et de laminage d'acier au moyen d'une machine de coulee a deux cylindres
JPH0470105B2 (fr)
GB2266256A (en) Delivery nozzle in metal strip casting
WO2007087686A1 (fr) Machine de coulee a deux rouleaux
KR101320353B1 (ko) 침지형 초음파 발생장치
WO1996001708A1 (fr) Machine de coulee a deux cylindres et laminoir utilisable avec ladite machine
WO1996001709A1 (fr) Panier double utilise avec une machine de coulee a deux cylindres
US10882100B2 (en) Method and apparatus for near net shape casting (NNSC) of metals and alloys
JPH0131976B2 (fr)
FI78250C (fi) Foerfarande och anordning foer direktgjutning av smaelt metall.
WO1996001711A1 (fr) Enveloppe de guidage et protections anti-projections utilisees avec une machine de coulee a deux cylindres et un panier de coulee
CN1011867B (zh) 金属尤其是钢的带材连铸工艺方法及其设备
WO1996001707A1 (fr) Moule fixe utilise avec une machine de coulee a deux cylindres
JPS59137159A (ja) 金属の連続鋳造方法及び装置
US6354363B1 (en) Ingot mould with multiple angles for loaded continuous casting of metallurgical product
JPS60121051A (ja) 薄鋳片連続鋳造装置
JPH0641019B2 (ja) 非酸化雰囲気中で結晶質ストリップを直接鋳造する方法および装置
AU712322B2 (en) Non-contact heat absorbers for strip casting
KR100701192B1 (ko) 연속주조공정에서 침지노즐 막힘 방지장치

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AM AU BB BG BR BY CA CH CN CZ EE ES FI GE HU IS JP KE KG KP KR KZ LK LR LT LV MD MG MN MW MX NO NZ PL RO RU SD SE SG SI SK TJ TM TT UA UG UZ VN

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE MW SD SZ UG AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase