WO1996000321A1 - Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production - Google Patents

Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production Download PDF

Info

Publication number
WO1996000321A1
WO1996000321A1 PCT/JP1994/001027 JP9401027W WO9600321A1 WO 1996000321 A1 WO1996000321 A1 WO 1996000321A1 JP 9401027 W JP9401027 W JP 9401027W WO 9600321 A1 WO9600321 A1 WO 9600321A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
ion
antibacterial
fiber
ion exchange
Prior art date
Application number
PCT/JP1994/001027
Other languages
English (en)
Inventor
Nobuya Matsumoto
Shinichi Kunisaki
Goro Fujiwara
Mitsunobu Masuda
Hiroshi Horie
Asaichi Kawanaka
Original Assignee
Suntory Limited
Takuma Co., Ltd.
Nitivy Company Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suntory Limited, Takuma Co., Ltd., Nitivy Company Limited filed Critical Suntory Limited
Priority to PCT/JP1994/001027 priority Critical patent/WO1996000321A1/fr
Priority to AU69836/94A priority patent/AU6983694A/en
Priority to EP94918574A priority patent/EP0715663A1/fr
Publication of WO1996000321A1 publication Critical patent/WO1996000321A1/fr
Priority to KR1019960700929A priority patent/KR960704107A/ko

Abstract

La présente invention concerne une fibre antibactérienne incorporant une fibre d'échange ionique, un ion métal antibactérien étant piégé à l'intérieur de la fibre d'échange ionique grâce à une réaction d'échange ionique. L'invention concerne également des textiles et des éléments de traitement des eaux à base de ces fibres.
PCT/JP1994/001027 1994-06-24 1994-06-24 Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production WO1996000321A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
PCT/JP1994/001027 WO1996000321A1 (fr) 1994-06-24 1994-06-24 Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production
AU69836/94A AU6983694A (en) 1994-06-24 1994-06-24 Antibacterial fiber, textile and water-treating element using the fiber and method of producing the same
EP94918574A EP0715663A1 (fr) 1994-06-24 1994-06-24 Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production
KR1019960700929A KR960704107A (ko) 1994-06-24 1996-02-24 항균 섬유, 그 섬유를 사용한 직물 및 수처리소자와 그것들의 제조방법(an tibacterial fiber, textile and water-treating elem ent using the fiber and method of producing the same)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP1994/001027 WO1996000321A1 (fr) 1994-06-24 1994-06-24 Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production

Publications (1)

Publication Number Publication Date
WO1996000321A1 true WO1996000321A1 (fr) 1996-01-04

Family

ID=14098467

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1994/001027 WO1996000321A1 (fr) 1994-06-24 1994-06-24 Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production

Country Status (4)

Country Link
EP (1) EP0715663A1 (fr)
KR (1) KR960704107A (fr)
AU (1) AU6983694A (fr)
WO (1) WO1996000321A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100443183B1 (ko) * 1995-12-29 2004-10-06 니혼 엑스란 고교 (주) 금속미립자-함유섬유및이의제조방법
DE102007027632A1 (de) * 2007-06-12 2008-12-18 Detlef Militz Verfahren zur Behandlung von zumindest teilweise metallisiertem Textil, behandeltes Textil und dessen Verwendung
CN103556455A (zh) * 2013-10-29 2014-02-05 郑州大学 高交换容量聚苯硫醚基强酸离子交换纤维的制备方法
WO2014117286A1 (fr) 2013-02-01 2014-08-07 Compañia Minera San Geronimo Matrice imprégnable d'origine végétale, animale ou synthétique ou constituée de mélanges de ces dernières qui contient un composé antimicrobien distribué de manière homogène; procédé pour imprégner un composé dans ladite matrice; et son utilisation dans la préparation d'éléments antimicrobiens
US9205109B2 (en) 2009-11-06 2015-12-08 Carefusion 2200, Inc. Copper salts of ion exchange materials for use in the treatment and prevention of infections
CN113338029A (zh) * 2021-05-28 2021-09-03 桂林正翰科技开发有限责任公司 一种抗病毒的载银纤维及其制备方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20000037298A (ko) * 2000-04-17 2000-07-05 김영환 항균섬유의 제조방법과 제조장치 및 그 항균섬유

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1063669A (en) * 1963-12-23 1967-03-30 Pall Corp Filter assembly for sterilizing water
JPS5292000A (en) * 1976-01-29 1977-08-02 Toray Industries Antiibacterial fiber
US4089816A (en) * 1973-09-19 1978-05-16 Sumitomo Chemical Company, Limited Cation exchanger
GB2051770A (en) * 1979-06-01 1981-01-21 Everpure Bacteriostatic filter media
EP0159490A1 (fr) * 1984-03-06 1985-10-30 Chemiefaser Lenzing Aktiengesellschaft Matériau fibreux désodorisant et microbistatique
EP0195819A1 (fr) * 1984-09-10 1986-10-01 Toray Industries, Inc. Procede d'echange ou d'adsorption d'ions
EP0329355A2 (fr) * 1988-02-12 1989-08-23 Takuma Co., Ltd. Elément constructif pour machines de traitement de liquides
EP0364111A1 (fr) * 1988-09-20 1990-04-18 Kabushiki Kaisha Aiaishi Purificateur d'eau
EP0413833A1 (fr) * 1989-03-14 1991-02-27 Sunstar Kabushiki Kaisha Brosse a dents
EP0426862A1 (fr) * 1989-03-08 1991-05-15 Nippon Kayaku Kabushiki Kaisha Fibre et resine antibacterienne et sa production
JPH0422410A (ja) * 1990-05-17 1992-01-27 Takuma Co Ltd 濾材
JPH05214671A (ja) * 1992-02-04 1993-08-24 Toray Ind Inc 消臭抗菌繊維

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1063669A (en) * 1963-12-23 1967-03-30 Pall Corp Filter assembly for sterilizing water
US4089816A (en) * 1973-09-19 1978-05-16 Sumitomo Chemical Company, Limited Cation exchanger
JPS5292000A (en) * 1976-01-29 1977-08-02 Toray Industries Antiibacterial fiber
GB2051770A (en) * 1979-06-01 1981-01-21 Everpure Bacteriostatic filter media
EP0159490A1 (fr) * 1984-03-06 1985-10-30 Chemiefaser Lenzing Aktiengesellschaft Matériau fibreux désodorisant et microbistatique
EP0195819A1 (fr) * 1984-09-10 1986-10-01 Toray Industries, Inc. Procede d'echange ou d'adsorption d'ions
EP0329355A2 (fr) * 1988-02-12 1989-08-23 Takuma Co., Ltd. Elément constructif pour machines de traitement de liquides
EP0364111A1 (fr) * 1988-09-20 1990-04-18 Kabushiki Kaisha Aiaishi Purificateur d'eau
EP0426862A1 (fr) * 1989-03-08 1991-05-15 Nippon Kayaku Kabushiki Kaisha Fibre et resine antibacterienne et sa production
EP0413833A1 (fr) * 1989-03-14 1991-02-27 Sunstar Kabushiki Kaisha Brosse a dents
JPH0422410A (ja) * 1990-05-17 1992-01-27 Takuma Co Ltd 濾材
JPH05214671A (ja) * 1992-02-04 1993-08-24 Toray Ind Inc 消臭抗菌繊維

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
CHEMICAL ABSTRACTS, vol. 88, no. 16, 17 April 1978, Columbus, Ohio, US; abstract no. 110132U, "Bactericidal fibers fo wastewater." page 306; column L; *
DATABASE WPI Section Ch Week 9210, Derwent World Patents Index; Class D22, AN 92-076970 *
DATABASE WPI Section Ch Week 9338, Derwent World Patents Index; Class A94, AN 93-300113 *

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100443183B1 (ko) * 1995-12-29 2004-10-06 니혼 엑스란 고교 (주) 금속미립자-함유섬유및이의제조방법
DE102007027632A1 (de) * 2007-06-12 2008-12-18 Detlef Militz Verfahren zur Behandlung von zumindest teilweise metallisiertem Textil, behandeltes Textil und dessen Verwendung
US9205109B2 (en) 2009-11-06 2015-12-08 Carefusion 2200, Inc. Copper salts of ion exchange materials for use in the treatment and prevention of infections
RU2582283C2 (ru) * 2009-11-06 2016-04-20 КЕЭФЬЮЖН 2200, Инк. Медные соли ионообменных материалов для использования при лечении и предотвращении инфекций
WO2014117286A1 (fr) 2013-02-01 2014-08-07 Compañia Minera San Geronimo Matrice imprégnable d'origine végétale, animale ou synthétique ou constituée de mélanges de ces dernières qui contient un composé antimicrobien distribué de manière homogène; procédé pour imprégner un composé dans ladite matrice; et son utilisation dans la préparation d'éléments antimicrobiens
CN103556455A (zh) * 2013-10-29 2014-02-05 郑州大学 高交换容量聚苯硫醚基强酸离子交换纤维的制备方法
CN113338029A (zh) * 2021-05-28 2021-09-03 桂林正翰科技开发有限责任公司 一种抗病毒的载银纤维及其制备方法

Also Published As

Publication number Publication date
KR960704107A (ko) 1996-08-31
EP0715663A1 (fr) 1996-06-12
AU6983694A (en) 1996-01-19

Similar Documents

Publication Publication Date Title
US5496860A (en) Antibacterial fiber, textile and water-treating element using the fiber and method of producing the same
US5011602A (en) Antibacterial material for water
US4664812A (en) Liquid filtration apparatus and process
US5951869A (en) Method for treating fluids
US6833075B2 (en) Process for preparing reactive compositions for fluid treatment
CA1169234A (fr) Milieu filtrant; methode d'oxydation et d'extraction du fer soluble; methode d'extraction et d'inactivation de micro-organismes; adjuvant de filtration de particules
JP4726415B2 (ja) 微孔性濾材、それを含有する濾過システム、その製造法および使用
US5275737A (en) Method for treating fluids
US4525410A (en) Particle-packed fiber article having antibacterial property
US5904854A (en) Method for purifying water
KR100977610B1 (ko) 나권형 필터 카트리지
US7335299B2 (en) Dual filter
CN100366316C (zh) 具有提高的微生物拦截能力的过滤介质
RU2426579C2 (ru) Фильтрующее устройство для питьевой воды
CN102892474A (zh) 水过滤器组件和过滤元件
WO1996000321A1 (fr) Fibre antibacterienne, textile et element de traitement des eaux a base de cette fibre et procede de production
CA1140522A (fr) Garniture filtrante bacteriostatique
JPH10314754A (ja) 浄水用カートリッジならびに浄水器
JP2003164714A (ja) 濾過装置
JPH06200472A (ja) 抗菌性繊維及びそれの製造方法並びに繊維製素材
RU83941U1 (ru) Картридж для очистки жидкости (варианты)
JPH01278408A (ja) 防菌性活性炭
WO1999033539A1 (fr) Filtre purificateur d'eau
EP0238639A4 (fr) Procede de traitement de fluides.
JP2018166466A (ja) 藻の成長を抑制するためのフィルタおよびそれを含む装置

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU CA KR

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): CH DE FR GB IT SE

WWE Wipo information: entry into national phase

Ref document number: 1994918574

Country of ref document: EP

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWP Wipo information: published in national office

Ref document number: 1994918574

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: CA

WWW Wipo information: withdrawn in national office

Ref document number: 1994918574

Country of ref document: EP