Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
  • B32B17/10036—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising two outer glass sheets
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
  • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
  • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/10165—Functional features of the laminated safety glass or glazing
  • B32B17/10293—Edge features, e.g. inserts or holes
  • B32B17/10302—Edge sealing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
  • B32B17/10678—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer comprising UV absorbers or stabilizers, e.g. antioxidants
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
  • B32B17/10743—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing acrylate (co)polymers or salts thereof
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
  • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
  • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
  • H10F19/804—Materials of encapsulations
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
  • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
  • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
  • H10F19/807—Double-glass encapsulation, e.g. photovoltaic cells arranged between front and rear glass sheets
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F24—HEATING; RANGES; VENTILATING
  • F24S—SOLAR HEAT COLLECTORS; SOLAR HEAT SYSTEMS
  • F24S25/00—Arrangement of stationary mountings or supports for solar heat collector modules
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E10/00—Energy generation through renewable energy sources
  • Y02E10/50—Photovoltaic [PV] energy

Definitions

• This invention relates to the manufacture and construction of photovoltaic solar cell modules, and more particularly to the encapsulation of an interconnected multi-cell array of photovoltaic solar cells.
• Photovoltaic solar cells for directly converting radiant energy from the sun into electrical energy are well known.
• the manufacture of photovoltaic solar cells involves provision of semiconductor substrates in the form of sheets or wafers having a shallow p-n junction adjacent one surface thereof (commonly called the "front surface") .
• Such substrates may include an insulating anti-reflection (“AR") coating on their front surfaces, and are sometimes referred to as "solar cell wafers".
• AR insulating anti-reflection
• the anti-reflection coating is transparent to solar radiation.
• the AR coating is often made of silicon nitride or an oxide of silicon or titanium.
• a typical solar cell wafer may take the form of a rectangular EFG-grown polycrystalline silicon substrate of p-type conductivity having a thickness in the range of 0.010 to 0.018 inches and a p-n junction located about 0.3-0.5 microns from its front surface, and also having a silicon nitride coating about 800 Angstroms thick covering its front surface.
• Equivalent solar cell wafers also are well known, e.g. circular or square single crystal silicon substrates and rectangular cast polycrystalline silicon substrates.
• Amorphous silicon solar cells and other thin film solar cells are also known equivalents contemplated by this invention.
• the solar cell wafers are converted to finished solar cells by providing them with electrical contacts (sometimes referred to as "electrodes") on both the front and rear sides of the semiconductor substrate, so as to permit recovery of an electrical current from the cells when they are exposed to solar radiation.
• electrical contacts sometimes referred to as "electrodes"
• These contacts are typically made of aluminum, silver, nickel or other metal or metal alloy.
• a common preferred arrangement is to provide silicon solar cells with rear contacts made of aluminum and front contacts made of silver.
• the contact on the front surface of the cell is generally in the form of a grid, comprising an array of narrow fingers and at least one elongate bus (also hereinafter called a "bus bar") that intersects the fingers.
• the width and number of the fingers and busses are selected so that the area of the front surface exposed to solar radiation is maximized.
• an AR coating as described overlies and is bonded to those areas of the front surface of the cell that are not covered by the front contact.
• the rear contact may cover the entire rear surface of the solar cell wafer, but more commonly it is formed so as to terminate close to but short of the edges of the blank.
• Aluminum is preferred for the rear contact for cost and other reasons.
• the exposed surface of an aluminum contact tends to oxidize in air, making it difficult to solder a wire lead to the contact. Therefore, to facilitate soldering, it has been found useful additionally to provide apertures in the aluminum coating, with silver soldering pads being formed in those apertures so as to slightly overlap the adjacent aluminum layer.
• the silver soldering pads form ohmic bonds with the underlying substrate and also low resistance electrical connections with the aluminum contact, and are used as sites for making soldered connections to the rear contact.
• the silver soldering pads are considered to be an integral part of the rear contact.
• Such a contact arrangement is disclosed in PCT International Publication No. WO 92/02952, based on U.S. Patent Application Serial No. 07/561,101, filed September 1, 1990 by Frank Bottari et. al. for "Method Of Applying Metallized Contacts To A Solar Cell" .
• An alternative but similar back contact arrangement wherein the aluminum coating has apertures filled with silver soldering pads involves having the aluminum overlap the edges of the silver soldering pads.
• the grid-shaped contact and the AR coating on the front surface may be formed in various ways, as exemplified by U.S. Patents Nos. 4451969, 4609565, 4751191, 5010040, 5074920, British Patent No. 2215129, and PCT International Application WO 89/12321, published 14 December 1989. Regardless of how the front grid contact and the AR coating are formed, at least a portion of each bus of the front contact is not covered with the AR coating, so as to permit making a soldered connection to that contact.
• Photovoltaic solar cells e.g., silicon solar cells
• Photovoltaic solar cells are typically small in size, e.g., 2-6 inches on a side in the case of cells made from rectangular EFG-grown substrates, with the result that their power output also is small.
• industry practice is to combine a plurality of cells so as to form a physically integrated module with a correspondingly greater power output.
• Several solar modules may be connected together to form a larger array with a correspondingly greater power output.
• the cells in a module are electrically connected in parallel and/or in series, and two or more modules in an array may be connected in series or in parallel, depending on the voltage and current output that is desired from the combined modules.
• a usual practice is to form a module from two or more "strings" of silicon solar cells, with each string consisting of a straight row of cells connected in series, and the several strings being arranged physically in parallel with one another.
• the several strings are electrically connected to one another in parallel or in series, according to voltage and current requirements.
• a common practice is to use solder coated copper wire, preferably in the form of a flat ribbon, to interconnect a plurality of cells in a string, with each ribbon being . oldered to the front or back contact of a particular cell, e.g., by means of a suitable solder paste as described in U.S Patent No. 5074920.
• modules in the form of laminated structures consist of front and back protective sheets, with at least the front sheet being made of clear glass or a suitable plastic material that is transparent to solar radiation, and the back sheet being made of the same or a different material as the front sheet. Disposed between the front and back sheets so as to form a sandwich arrangement are the solar cells and a polymer material that encapsulates the solar cells and is also bonded to the front and back sheets.
• the laminated sandwich-style module is designed to mechanically support the brittle silicon cells and also to protect the cells against environmental degradation.
• Photovoltaic solar cell modules having an effective working life of 30 years or more have been a well known industry objective.
• the materials used in constructing modules are selected with concern for providing adequate resistance to damage from impact and physical and thermal shock, maximizing the amount of solar radiation received by the cells, avoiding short-circuiting and electrical leakage, and otherwise minimizing degradation from such environmental factors as moisture, temperature and ultra-violet sunlight-induced chemical reactions.
• the thirty year useful life objective must be attainable at a commercially acceptable cost.
• EVA ethylene vinyl acetate copolymer
• ionomer ionomer
• EVA has received wide commercial acceptance as an encapsulant for solar cell modules.
• EVA has been found to be a less than ideal solar cell encapsulating material.
• a well known problem associated with the use of EVA as an encapsulant is the occurrence of progressive darkening of the EVA under intense sunlight. This discoloration can result in a greater than 30% loss in power output of the solar module after only four or more years of exposure to the environment. This phenomena is well documented. See, for example, the article written by F. J. Pern and A. W.
• the discoloration which often is a yellow-brown color, results from the EVA chemically degrading under the influence of ultraviolet light. As the EVA decomposes, it releases acetic acid, which in turn acts like a catalyst in the EVA to cause further degradation. It has also been found that the degradation of the EVA may be further accelerated by heat and/or the presence of oxygen.
• EVA as an encapsulant
• a cross-linking agent e.g., an organic peroxide
• Cross-linking deprives the EVA of the ability to be remelted.
• any unreacted organic peroxide in the cross-linked EVA encapsulant will further assist the degradation process.
• the primary object of the present invention is to provide an improved photovoltaic solar cell module which employs ionomer as the cell encapsulant, with the ionomer being modified by the addition of additives which have the effect of improving the light transmission and stabilization properties of the ionomer so as to extend the effective useful life of the module.
• Another object of the present invention is to provide an improved photovoltaic solar cell module capable of an increased working life without any substantial loss of power output.
• Yet another object of the present invention is to provide an improved photovoltaic solar cell module that is characterized by an encapsulant that has a greater resistance to discoloration under intense sunlight than EVA.
• Still another object is to provide a module of the type described wherein the solar cells are encapsulated in a thermoplastic light-transmitting material that is less expensive and has a greater resistance to discoloration than EVA.
• a novel photovoltaic module comprising an array of electrically interconnected photovoltaic cells disposed in planar relationship between first and second sheets of a supporting material and encapsulated by a thermoplastic light-transmitting material in the form of an additive modified ionomer that is less expensive and has a greater resistance to discoloration than EVA.
• the module is fabricated by laminating together a sandwich comprising in stacked relation a first sheet of a relatively stiff supporting material, a first ionomer layer, a plurality of interconnected photovoltaic solar cells, a second ionomer layer, and a second sheet of supporting material, with at least one of the sheets of supporting material being transparent to solar radiation.
• the two sheets of supporting material are made of glass and the light-transmitting encapsulating material comprises a sodium ionomer containing selected additives as hereinafter described.
• Fig. 1 is a front perspective view in elevation of a prior art photovoltaic solar energy collection and conversion array
• Fig. 2 is a front view of a well-known type of photovoltaic cell
• Fig. 3 is a rear view of the photovoltaic cell shown in Fig. 2;
• Fig. 4 is a fragmentary perspective view in elevation illustrating assembly of a solar module embodying the present invention
• Fig. 5 is a cross-sectional view taken along line 5-5 in Fig. 4 showing the solar module of the present invention prior to lamination;
• Fig. 6 is a cross-sectional view, similar to that shown in Fig. 5, showing the solar module of the present invention after lamination and framing.
• the solar panel assembly comprises a plurality of photovoltaic (“PV") modules 2A-2H which have metal frames 4 made of aluminum channel members and are attached to a metal support structure 8 which is secured to a suitable base 10, e.g., a base in the form of a flat roof or a concrete slab on the ground.
• PV photovoltaic
• Each module comprises a plurality of photovoltaic cells (not shown) which are interconnected in series or in parallel by suitable conductors (also not shown) , so that each module has a predetermined voltage and current output.
• the electrically interconnected solar cells are terminated by electrical conductors (not shown) that extend outside of the module so as to permit connection to another module and/or an exterior circuit.
• each of the modules 2A-2H is a laminated structure which comprises (1) a top (front) protective support sheet in the form of a pane of glass, (2) a bottom (back) protective support sheet which may be made of a suitable insulating material, e.g., a synthetic material such as TEDLAR (Tedlar is the trade name for a polyvinyl fluoride polymer made by E.I. duPont de Nemeurs Co.) , (3) a plurality of silicon solar cells interconnected in series or in parallel by suitable conductors so that the module will have a predetermined voltage and current output, and (4) a light transparent encapsulant in the form of EVA surrounding the cells and bonded to the top and bottom protective sheets.
• a suitable insulating material e.g., a synthetic material such as TEDLAR (Tedlar is the trade name for a polyvinyl fluoride polymer made by E.I. duPont de Nemeurs Co.)
• TEDLAR Tedlar is
• the EVA is provided in the form of two sheets, one disposed between the back protective sheet and the cells and the other disposed between the cells and the front protective sheet.
• the lamination process (which involves heating under pressure in a vacuum laminator followed by cooling) the two sheets of EVA are liquified enough to fill the voids between adjacent solar cells, and on cooling the two sheets are merged into a single cross-linked polymer layer in which the cells are encapsulated. Additionally the cooled EVA is bonded to the front and back protective sheets so as to form an integrated, unified structure.
• FIGS 2 and 3 illustrate a conventional solar cell 20 of a kind utilized in making modules of the type illustrated at 2A-2H in Fig. 1.
• Each cell comprises a silicon EFG-grown substrate in the form of a sheet or wafer -hat has been processed so as to have a shallow P-N junction (not shown) adjacent its front surface 24. Typically the junction is located between 0.3 and 0.5 microns below front surface 24.
• the cell also has on its front surface 24 a silver front contact in the form of a grid consisting of an array of narrow, elongate, parallel fingers 30 interconnected by two bus bars 32.
• a thin silicon nitride anti-reflective coating covers those portions of front surface 24 of the substrate that are not occupied by the grid electrode.
• the rear surface 34 of cell 20 comprises a rear contact 36 (Fig. 3) that is made of aluminum metal and terminates short of the outer edges of the rectangular cell so as to have an uncoated margin portion that extends along each side of the cell substrate coextensive with the periphery of the substrate, and also two rows of silver metal soldering pads 38 that fill apertures formed in the rear aluminum contact and are fused to the underlying solar cell substrate. Pads 38 overlap rear contact 36 around the periphery of the apertures in that contact.
• Fig. 3 shows eight soldering pads, it is to be understood that the number and spacing of the soldering pads may be varied and is not critical to this invention.
• Solar cells 20 of the type shown in Figs. 2 and 3 are well known and, for example, are disclosed by PCT International Publication No. WO 92/02952.
• Figs. 4-6 illustrate construction of a module 40 which constitutes a preferred embodiment of the present invention.
• Module 40 is formed by laminating together a top (front) protective support sheet 42 of clear transparent glass, a first encapsulating layer 44 of an ionomer, an array of silicon solar cells 46 interconnected by ribbon-like conductors 47 in series or in parallel according to the output voltage and current requirements, a second encapsulating layer 48 of ionomer, a bottom (back) protective support sheet 50 made of glass.
• Each of the layers 44 and 48 may comprise one or more sheets of an ionomer, depending on the thickness in which ionomer sheets are available commercially.
• the ionomer comprises certain additives as are hereinafter described for extending the effective useful life of the module.
• the module also includes hermetic edge sealing means hereinafter described.
• Cells 46 are arranged in straight rows, i.e., strings, and an end cell in one string is connected to an adjacent string by conductors (not shown) similar to conductors 47, with the whole interconnected array having terminal leads (not shown) that extend out through an aperture in the back protective support sheet 50 or else through the edge sealing means.
• the term "ionomer” means and denotes a thermoplastic resin containing both covalent and ionic bonds derived from ethylene copolymers.
• ionomers formed by partial neutralization of ethylene-methacrylic acid copolymers or ethylene-acrylic acid copolymers with inorganic bases having cations of elements from Groups I, II or III of the Periodic table, notably, sodium, zinc, aluminum, lithium, magnesium and barium.
• the term "ionomer” and the resins identified thereby are well known in the art, as evidenced by Richard W. Rees, "Ionic Bonding In Thermoplastic Resins", DuPont Innovation, 1971, 2(2), pp. 1-4, and Richard W. Rees, "Physical Properties And Structural Features Of Surlyn Ionomer Resins” , Polyelectrolytes, 1976, C, 177-197.
• Zinc-based ionomers do not have light transmissibility as good as sodium-based ionomers, and hence it is preferred to limit the zinc-based ionomers to the back layer 48, especially where it is desired that layer 48 be white or translucent.
• the best results are obtained by using the sodium based ionomer manufactured and sold by E.I. duPont de Nemeurs & Co., under the trade mark designation SURLYN 1601. That particular ionomer offers the advantages of excellent optical properties and high hot tack strength.
• Another ionomer product having excellent optical properties and useful in practicing the invention is duPont's Surlyn 1707.
• Modules made with an ionomer as described above, e.g., with Surlyn 1601 have a superior effective working life than modules that employ EVA as an encapsulant.
• the present invention is based on and comprises the discovery that the addition of certain additivies will improve resistance of ionomer to degradation caused by UV radiation and thereby cause. the module to have an effective working life approaching 30 years.
• the invention involves combining the ionomer resin of choice with one or more selected additives designed to facilitate absorption of UV radiation and/or stabilize the ionomer against degradation induced by incident solar radiation. More specifically, the ionomer resin is modified by the addition of both a UV absorber and also a UV stabilizer in small amounts in the range of 0.3 to 2.0 wt. percent.
• the preferred additives are manufactured and sold by the Cyanamid Polymer Products Division of the American Cyanamid Corporation under the trade names Cyasorb 5411, a UVA absorbing agent, and Cyasorb 3346, a hindered amine light-stabilizer (HALS) .
• Cyasorb 5411 is the tradename for 2-(2'-hydroxy-5'-tert-octylphenyl) benzotriazole; Cyasorb 3346 is the tradename for poly[ (6-morpholino-s-triazine-2, 4-diyl) ] [ (2,2, 6, 6-tetramethy1-4-piperidyl) imino] hexamethylene [ (2,2,6, 6-tetramethy1-4-piperidyl) imino] .
• These additives are added to the ionomer resin before the latter is converted into sheets for use as herein described. They have been found to be very effective in reducing the rate of light induced degradation of the ionomer encapsulant.
• module 40 is constructed by first placing the top glass sheet 42 on a suitable support. Next, a first rectangular layer of an additive modified ionomer 44 of suitable thickness is placed in overlying relationship with glass sheet 42. Layer 44 is sized so that its outer edges are spaced from the corresponding edges of glass sheet 42.
• Ionomer layer 44 is positioned on glass plate 42 without the use of any adhesive since it will bond directly to the glass during processing, as will be hereinafter disclosed in further detail in connection with Figs. 5 and 6.
• the inner facing surface of glass sheet 42 is coated with a film of a suitable liquid coupling agent to improve bonding of ionomer layer 44 to the glass during lamination.
• aminofunctional coupling agents such as the one available from the Union Carbide Corporation under the tradename
• Organofunctional Silane A-1100 which is believed to be gamma-aminopropyltriethoxysilane, may be used to improve bonding of the ionomer to the surface of the glass pane.
• the method of the present invention may be practiced without using a coupling agent and still yield acceptable modules.
• an array consisting of several strings of photovoltaic solar cells 46 is placed in overlying relationship with first ionomer layer 44 in a desired pattern.
• the array of cells is provided with terminal leads (not shown) for connecting that array to another like module or to an exterior circuit.
• the cells are disposed with their grid contacts facing glass plate 42.
• sealing strip 54 is placed on glass sheet 42 so that it extends along the entire periphery of that sheet in surrounding relation to the ionomer layer 44.
• Strip 54 preferably has a rectangular cross-section and two of its opposite surface, i.e., the top and bottom surfaces shown in Figs. 5 and 6, are coated with a pressure sensitive adhesive.
• Sealing strip 54 may be one continuous strip, but preferably it is made up of four pieces, each extending along a different edge of glass plate 42.
• sealing strip 54 is an acrylic foamed tape, such as Scotch Brand VHB Double Coated Acrylic Foam Tape, manufactured by the 3M company of Minnesota.
• the terminal leads of the array of cells are to be brought out through an edge of the module, the terminal leads (not shown) are positioned so that they extend through sealing strip 54.
• a second additive modified ionomer layer 48 similar in length and width to layer 44 is placed in overlying relationship with the interconnected solar cell array 46 and also the sealing strip 54. As shown in Fig. 5, layers 44 and 48 extend beyond the periphery of array 46.
• the sandwich used to make the module is completed by placing the back glass sheet 50 over the second ionomer layer 48 in alignment with the first (front) glass sheet 42.
• the inner facing surface of glass sheet 50 be coated with a suitable liquid coupling agent to improve bonding of that sheet to ionomer layer 48.
• the terminal leads of the solar cell have been positioned so as to project out from between sealing strip 54 and ionomer layer 48, the terminal leads are passed out through an opening or openings (not shown) in back sheet 50.
• the foregoing sandwich is heated to a temperature of about 170 degrees C and held there long enough to cause the two ionomer layers 44 and 48 to soften enough to flow into encapsulating relation with each of the cells and the conductors 47 that connect the cells to one another.
• the sandwich is heated up to about 170 to 180°C within about 10 to 15 minutes and held there for between about 10 to 60 minutes, preferably for between about 10 to 20 minutes.
• the layers of the sandwich are compressed together under a pressure not exceeding about 14 to 14.6 PSI. Thereafter, the pressure is relieved and the heating is terminated.
• the assembly is allowed to cool to ambient temperature, whereupon the ionomer solidifies and in so doing it bonds to the cells and the connecting conductors and also to the two glass plates.
• the two additive modified ionomer sheets are fused together, forming a single encapsulating additive modified ionomer mass 60.
• the terminal leads (not shown) of the solar cell array are encased by ionomer where they pass out of the cooled module.
• sealing strip 62 is applied to the now laminated module 40 so as to cover the first sealing strip and overlap the margins of the exposed surfaces of the two glass plates.
• sealing strip 62 is made of the same material as sealing strip 54, but it is thinner and is oriented so that the adhesive on one side thereof engages the exposed surfaces of the glass sheets and the first sealing strip 54.
• the second sealing strip 62 may consist of several individual sections.
• a metal frame 70 preferably one made of a plurality of aluminum channel members, is applied in the manner shown in Fig. 6 to the four edges of the module.
• a solar cell module may be formed according to this invention by providing (a) two panes of 1/8" thick glass each measuring 50" wide and 74" long, (b) two layers of additive modified Surlyn 1601 ionomer having a thickness of .020", and (c) an array of silicon solar cells of the type illustrated in Figs. 2 and 3.
• the Surlyn 1601 ionomer was modified by addition of 0.5 wt. percent Cyasorb 5411 and 0.5 wt. percent Cyasorb 3346.
• Each layer of additive modified ionomer may consist of two identical sized sheets each having a thickness of 0.010". Each ionomer layer is approximately 1" less in width and length than the glass panes.
• the array is made up of twelve strings of cells, with each string consisting of 18 cells connected in series.
• the strings are arranged in side-by-side relation and connected in parallel.
• a sandwich is formed in the manner described above in connection with Figs. 4-6, with 3M "Scotch” brand VHB double-coated acrylic foam tape being used to form a sealing member corresponding to sealing strip 54 described above.
• the tape has a rectangular cross section and measures about 3/8" on each side.
• the surfaces of the glass which contact the ionomer sheets are washed and then coated with Union Carbide Organofunctional Silane A-1100 coupling agent and then dried.
• This loose sandwich is then placed in a Spire Corporation SPI laminator Model 460, which is essentially a heated vacuum-type press.
• the laminator is closed and then simultaneously heat and vacuum are applied to the sandwich.
• the sandwich is brought up to a temperature of approximately 175°C, reaching that temperature in approximately ten minutes.
• the sandwich is then kept at that temperature for approximately another 15 minutes while under a pressure of about 14 pounds per square inch.
• the vacuum to the press is then released so as to remove the pressure on the sandwich and at about the same time the heaters of the press are deenergized to terminate active heating.
• the laminator is then opened and the laminated sandwich is allowed to cool to room temperature.
• the front and rear glass plates 42 and 50 may be replaced by a sheet of a suitable transparent plastic material, e.g., a polycarbonate or an acrylic polymer or a polyester such as polyethylene terephthalate (“PET”) .
• PET polyethylene terephthalate
• the rear supporting sheet 50 may be made of a non-transparent material, e.g., a sheet comprising or consisting of Tedlar or some other material.
• a suitable transparent plastic material e.g., a polycarbonate or an acrylic polymer or a polyester such as polyethylene terephthalate (“PET”)
• PET polyethylene terephthalate
• the rear supporting sheet 50 may be made of a non-transparent material, e.g., a sheet comprising or consisting of Tedlar or some other material.
• the second ionomer layer 48 applied over the rear contacts of the cells need not be transparent. Instead, it may be translucent or white. It has been found that the use of translucent or white ionomer as a backing for silicon cells 20 tends to enhance the current output of the cells, since the non-transparent ionomer can reflect additional light passing between the cells back toward the front plate 42 for further reflection onto the active front surfaces of the silicon cells, thus increasing their efficiency.
• sealing strips 54 and 62 may be made of a material other than an acrylic foam, e.g., an adhesive-coated polyethylene tape, without departing from the scope of the present invention. However, the various alternative materials must be compatible with the ionomer. Also some other form of edge sealing means known to persons skilled in the art may be used in place of strips 54 and 62. It also is contemplated that strip 62 may be omitted depending on the nature of sealing member 54 or its replacement.
• Another possible modification is to incorporate the silane coupling agent into the ionomer material.
• the most important advantage of the present invention is that accelerated aging tests performed on modules encapsulated with an ionomer modified according to this invention have established a sound basis for estimating an effective working life approaching thirty years. That represents an unobvious improvement over modules made with EVA. The reasons for that improvement are evident from the other advantages hereinafter described.
• Another advantage of the present invention over EVA encapsulated solar modules is the fact that ionomers do not require the addition of an organic peroxide cross-linking agent.
• Organic peroxide additives are required to be added to EVA resin in order to cause the EVA to undergo cross-linking when it is heated to form a laminated module as described above.
• the presence of the cross-linking agent reduces the shelf life of the EVA sheets and renders the shelf life light-and temperature-dependent, since evaporation of the cross-linking agent can be accelerated by an increase in temperature.
• Ionomer sheets modified according to this invention have a substantially longer shelf life than EVA since they do not employ any added cross-linking agent.
• modules made with an ionomer encapsulant do not require a back support sheet having a finite porosity, e.g., Tedlar, so as to permit escape of any by-products released by the encapsulant.
• Tedlar is believed to be a polyvinyl fluoride polymer manufactured by the E.I. duPont de Nemours Corporation. Often, Tedlar is applied to the back of solar modules in the form of a laminated sheet of Tedlar and another polymer, such as a polyester.
• Acetic acid not only encourages degradation of the EVA but also acts to corrode the various metal contacts and electrical conductors associated with the photovoltaic solar cell array. Tedlar, due to its finite porosity, allows oxygen to enter the cell, thus promoting oxidation of the cells and the encapsulant.
• ionomer In contrast to EVA, ionomer has a relatively slow rate of degradation under the influence of heat and solar radiation; furthermore, as the ionomer degrades it produces H 2 0 and C0 2 by-products, both of which are relatively benign agents in relation to the components of the solar cell module.
• Yet another advantage of the present invention over EVA encapsulated solar modules is the fact that even allowing for the cost of introducing additives as provided by the invention, ionomer sheets are cheaper than sheets of EVA containing a cross-linking agent. Furthermore, because of the properties of the EVA and the organic peroxide added to it to foster cross-linking, EVA sheets are generally limited in width to approximately 18 inches, while ionomer sheet size is substantially unlimited. This advantage helps reduce labor costs in assembling the sandwich of components that are laminated to form solar modules.
• Another important advantage of the present invention over EVA encapsulated solar cell modules is the fact that ionomer, with or without additives as provided by this invention, forms a cohesive bond with glass, metal and other materials while EVA bonds only adhesively to glass and hence does not form as strong a bond as an ionomer material. The stronger bond helps extend the effective working life of the modules and creates a better seal.

Landscapes

• Life Sciences & Earth Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Biochemistry (AREA)
• Photovoltaic Devices (AREA)

Priority Applications (1)

Applications Claiming Priority (2)

Publications (1)

Family

ID=22733578

Family Applications (1)

Country Status (4)

Cited By (17)

Families Citing this family (107)

Citations (4)

Family Cites Families (14)

• 1994
  • 1994-02-18 US US08/198,485 patent/US5476553A/en not_active Expired - Fee Related
• 1995
  • 1995-02-10 AU AU19150/95A patent/AU1915095A/en not_active Abandoned
  • 1995-02-10 WO PCT/US1995/001686 patent/WO1995022844A1/en not_active Ceased
  • 1995-02-17 TW TW084101476A patent/TW320774B/zh active

Patent Citations (4)

Also Published As

Similar Documents

Legal Events