WO1991014035A1 - Capitonnage et procede de production - Google Patents
Capitonnage et procede de production Download PDFInfo
- Publication number
- WO1991014035A1 WO1991014035A1 PCT/FI1991/000068 FI9100068W WO9114035A1 WO 1991014035 A1 WO1991014035 A1 WO 1991014035A1 FI 9100068 W FI9100068 W FI 9100068W WO 9114035 A1 WO9114035 A1 WO 9114035A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fibres
- mat
- clusters
- wad
- fibre
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP91905049A EP0607121A1 (fr) | 1990-03-08 | 1991-03-08 | Capitonnage et procede de production |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FI901184 | 1990-03-08 | ||
FI901184A FI85033C (fi) | 1990-03-08 | 1990-03-08 | Vaddmatta samt foerfarande foer tillverkning av densamma. |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1991014035A1 true WO1991014035A1 (fr) | 1991-09-19 |
Family
ID=8530032
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/FI1991/000068 WO1991014035A1 (fr) | 1990-03-08 | 1991-03-08 | Capitonnage et procede de production |
Country Status (4)
Country | Link |
---|---|
EP (1) | EP0607121A1 (fr) |
AU (1) | AU7345291A (fr) |
FI (1) | FI85033C (fr) |
WO (1) | WO1991014035A1 (fr) |
Cited By (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1993007318A1 (fr) * | 1991-09-30 | 1993-04-15 | Oy Scanwoven Ab | Element de capitonnage et procede de production |
EP0604933A1 (fr) * | 1992-12-27 | 1994-07-06 | Günter TESCH | Revêtement de sol textil avec des sphères de fibres textiles enroulies se composant de fibres agglomérées sous forme de billes et son procédé de fabrication |
KR20030065784A (ko) * | 2002-02-01 | 2003-08-09 | 하종언 | 반발성이 우수한 부직포 |
CN102356188A (zh) * | 2010-04-23 | 2012-02-15 | 朴泰根 | 利用球纤维制备纤维板的方法及利用该方法制备的纤维板 |
DE102014002060A1 (de) * | 2014-02-18 | 2015-08-20 | Carl Freudenberg Kg | Volumenvliesstoff |
WO2016035255A1 (fr) * | 2014-09-01 | 2016-03-10 | 株式会社アライ | Feuille fibreuse et son procédé de production |
CN105463697A (zh) * | 2015-12-30 | 2016-04-06 | 3M创新有限公司 | 保温絮片材料及其制备方法、保温制品 |
CN105862252A (zh) * | 2016-06-08 | 2016-08-17 | 昆山吉美川纤维科技有限公司 | 一种纤维垫的制备工艺及纤维垫 |
EP3133196A1 (fr) | 2015-08-18 | 2017-02-22 | Carl Freudenberg KG | Non-tisse destine a donner du volume |
WO2017058986A1 (fr) * | 2015-09-29 | 2017-04-06 | Primaloft, Inc. | Isolation à flocons soufflable et son procédé de préparation |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CH373728A (de) * | 1961-05-23 | 1963-08-30 | Freudenberg Carl Fa | Verfahren zur Herstellung von Vliesstoffen durch thermoplastische Verfestigung |
US4298418A (en) * | 1978-12-29 | 1981-11-03 | Sadaaki Takagi | Method and apparatus for the manufacture of a locked material of filament |
CH627802A5 (de) * | 1977-04-30 | 1982-01-29 | Sadaaki Takagi | Polstermaterial. |
DK148715B (da) * | 1979-01-09 | 1985-09-09 | Breveteam Sa | Fladt tekstilmateriale og anvendelse af et saadant materiale |
US4619723A (en) * | 1980-08-18 | 1986-10-28 | Sadaaki Takagi | Method for preformation of cushion and apparatus therefor |
NO163222B (no) * | 1986-10-21 | 1990-01-15 | Du Pont | Fiberkuler i det vesentlige bestaaende av spiralkrusede fibre, fremgangsmaate for fremstilling av disse. |
-
1990
- 1990-03-08 FI FI901184A patent/FI85033C/fi not_active IP Right Cessation
-
1991
- 1991-03-08 AU AU73452/91A patent/AU7345291A/en not_active Abandoned
- 1991-03-08 EP EP91905049A patent/EP0607121A1/fr not_active Withdrawn
- 1991-03-08 WO PCT/FI1991/000068 patent/WO1991014035A1/fr not_active Application Discontinuation
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CH373728A (de) * | 1961-05-23 | 1963-08-30 | Freudenberg Carl Fa | Verfahren zur Herstellung von Vliesstoffen durch thermoplastische Verfestigung |
CH627802A5 (de) * | 1977-04-30 | 1982-01-29 | Sadaaki Takagi | Polstermaterial. |
US4298418A (en) * | 1978-12-29 | 1981-11-03 | Sadaaki Takagi | Method and apparatus for the manufacture of a locked material of filament |
DK148715B (da) * | 1979-01-09 | 1985-09-09 | Breveteam Sa | Fladt tekstilmateriale og anvendelse af et saadant materiale |
US4619723A (en) * | 1980-08-18 | 1986-10-28 | Sadaaki Takagi | Method for preformation of cushion and apparatus therefor |
NO163222B (no) * | 1986-10-21 | 1990-01-15 | Du Pont | Fiberkuler i det vesentlige bestaaende av spiralkrusede fibre, fremgangsmaate for fremstilling av disse. |
Cited By (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1993007318A1 (fr) * | 1991-09-30 | 1993-04-15 | Oy Scanwoven Ab | Element de capitonnage et procede de production |
EP0604933A1 (fr) * | 1992-12-27 | 1994-07-06 | Günter TESCH | Revêtement de sol textil avec des sphères de fibres textiles enroulies se composant de fibres agglomérées sous forme de billes et son procédé de fabrication |
KR20030065784A (ko) * | 2002-02-01 | 2003-08-09 | 하종언 | 반발성이 우수한 부직포 |
CN102356188A (zh) * | 2010-04-23 | 2012-02-15 | 朴泰根 | 利用球纤维制备纤维板的方法及利用该方法制备的纤维板 |
US10900156B2 (en) | 2014-02-18 | 2021-01-26 | Carl Freudenberg Kg | Volume nonwoven fabric |
DE102014002060A1 (de) * | 2014-02-18 | 2015-08-20 | Carl Freudenberg Kg | Volumenvliesstoff |
CN105992843A (zh) * | 2014-02-18 | 2016-10-05 | 科德宝两合公司 | 提供体积的无纺织物 |
DE102014002060B4 (de) * | 2014-02-18 | 2018-01-18 | Carl Freudenberg Kg | Volumenvliesstoffe, Verwendungen davon und Verfahren zu ihrer Herstellung |
WO2016035255A1 (fr) * | 2014-09-01 | 2016-03-10 | 株式会社アライ | Feuille fibreuse et son procédé de production |
JP2016094692A (ja) * | 2014-09-01 | 2016-05-26 | 株式会社アライ | 繊維シート |
JP5957162B1 (ja) * | 2014-09-01 | 2016-07-27 | 株式会社アライ | 繊維シートの製造方法 |
KR101883419B1 (ko) | 2014-09-01 | 2018-07-30 | 아라이 씨오., 엘티디. | 섬유 시트 및 그 제조 방법 |
KR20170004016A (ko) * | 2014-09-01 | 2017-01-10 | 아라이 씨오., 엘티디. | 섬유 시트 및 그 제조 방법 |
CN106460269A (zh) * | 2014-09-01 | 2017-02-22 | 株式会社荒井 | 纤维片材及其制造方法 |
WO2017029191A1 (fr) | 2015-08-18 | 2017-02-23 | Carl Freudenberg Kg | Matière non-tissée à gonflant volumineux |
DE202016008648U1 (de) | 2015-08-18 | 2018-10-25 | Carl Freudenberg Kg | Volumenvliesstoff |
EP3133196A1 (fr) | 2015-08-18 | 2017-02-22 | Carl Freudenberg KG | Non-tisse destine a donner du volume |
CN107923091A (zh) * | 2015-08-18 | 2018-04-17 | 科德宝两合公司 | 大体积无纺织物 |
CN107923091B (zh) * | 2015-08-18 | 2021-02-26 | 科德宝两合公司 | 大体积无纺织物 |
US10876234B2 (en) | 2015-08-18 | 2020-12-29 | Carl Freudenberg Kg | Volume nonwoven fabric |
KR20180051644A (ko) * | 2015-09-29 | 2018-05-16 | 프리마로프트, 인크. | 팽창 가능한 면상 응집물 절연 재료 및 이의 제조방법 |
KR101964024B1 (ko) | 2015-09-29 | 2019-03-29 | 프리마로프트, 인크. | 팽창 가능한 면상 응집물 절연 재료 및 이의 제조방법 |
US10633244B2 (en) | 2015-09-29 | 2020-04-28 | Primaloft, Inc. | Blowable floccule insulation and method of making same |
US10870573B2 (en) | 2015-09-29 | 2020-12-22 | Primaloft, Inc. | Method of making blowable floccule insulation |
WO2017058986A1 (fr) * | 2015-09-29 | 2017-04-06 | Primaloft, Inc. | Isolation à flocons soufflable et son procédé de préparation |
CN108474155A (zh) * | 2015-12-30 | 2018-08-31 | 3M创新有限公司 | 隔热絮片材料及其制备方法以及隔热产品 |
CN105463697A (zh) * | 2015-12-30 | 2016-04-06 | 3M创新有限公司 | 保温絮片材料及其制备方法、保温制品 |
CN105862252A (zh) * | 2016-06-08 | 2016-08-17 | 昆山吉美川纤维科技有限公司 | 一种纤维垫的制备工艺及纤维垫 |
Also Published As
Publication number | Publication date |
---|---|
FI85033C (fi) | 1992-02-25 |
FI901184A (fi) | 1991-09-09 |
AU7345291A (en) | 1991-10-10 |
FI901184A0 (fi) | 1990-03-08 |
EP0607121A1 (fr) | 1994-07-27 |
FI85033B (fi) | 1991-11-15 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP0295038B1 (fr) | Nattes thermo-isolantes non tissées | |
CA1336873C (fr) | Nappe de fibres synthetiques densifiees obtenue par thermoliage | |
US4794038A (en) | Polyester fiberfill | |
US5685757A (en) | Fibrous spun-bonded non-woven composite | |
AU691278B2 (en) | Multilayer nonwoven thermal insulating batts | |
US20090101294A1 (en) | Process for making bamboo fiberfill and articles thereof | |
US5597427A (en) | Method of making multilayer nonwoven thermal insulating batts | |
EP3234244B1 (fr) | Nappe ouatée en boulettes de fibres et articles la comprenant | |
US4259400A (en) | Fibrous padding material and process for its manufacture | |
WO1991014035A1 (fr) | Capitonnage et procede de production | |
US4392903A (en) | Process for making a thermal-insulating nonwoven bulky product | |
US4320166A (en) | Thermal-insulating nonwoven bulky product | |
JP2022548370A (ja) | 人工羽毛充填材料 | |
TWI827160B (zh) | 具有核區域和殼區域的纖維球、其後續產品以及它們的製備方法和用途 | |
US12029268B2 (en) | Article of apparel including insulation | |
JPH0375189B2 (fr) | ||
EP3788195A1 (fr) | Article d'habillement comprenant une isolation | |
CA2296876A1 (fr) | Methode de production de bourre ondulee a densite variable, liee a la resine ou par procede thermique, et structure obtenue par ladite methode |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AT AU BB BG BR CA CH DE DK ES FI GB HU JP KP KR LK LU MC MG MW NL NO PL RO SD SE SU US |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE BF BJ CF CG CH CM DE DK ES FR GA GB GR IT LU ML MR NL SE SN TD TG |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1991905049 Country of ref document: EP |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
NENP | Non-entry into the national phase |
Ref country code: CA |
|
WWP | Wipo information: published in national office |
Ref document number: 1991905049 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1991905049 Country of ref document: EP |