WO1986000744A1 - Structure de stockage optique - Google Patents

Structure de stockage optique Download PDF

Info

Publication number
WO1986000744A1
WO1986000744A1 PCT/US1985/001284 US8501284W WO8600744A1 WO 1986000744 A1 WO1986000744 A1 WO 1986000744A1 US 8501284 W US8501284 W US 8501284W WO 8600744 A1 WO8600744 A1 WO 8600744A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
active layer
recording structure
optical recording
nickel
Prior art date
Application number
PCT/US1985/001284
Other languages
English (en)
Inventor
Fred W. Spong
Boris J. Muchnik
Robert E. Revay
Original Assignee
Storage Technology Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Storage Technology Corporation filed Critical Storage Technology Corporation
Publication of WO1986000744A1 publication Critical patent/WO1986000744A1/fr

Abstract

Dans un dispositif de stockage optique comportant une couche active contenant un alliage de chalcogénure, un métal, de préférence du nickel, est codéposé avec le chalcogénure afin d'inhiber l'obscurcissement de la structure de stockage.
PCT/US1985/001284 1984-07-06 1985-07-03 Structure de stockage optique WO1986000744A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US62869784A 1984-07-06 1984-07-06
US628,697 1984-07-06

Publications (1)

Publication Number Publication Date
WO1986000744A1 true WO1986000744A1 (fr) 1986-01-30

Family

ID=24519947

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1985/001284 WO1986000744A1 (fr) 1984-07-06 1985-07-03 Structure de stockage optique

Country Status (2)

Country Link
EP (1) EP0189462A1 (fr)
WO (1) WO1986000744A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4857373A (en) * 1987-03-31 1989-08-15 E. I. Du Pont De Nemours And Company Optical recording element

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0050047A2 (fr) * 1980-10-15 1982-04-21 Hitachi, Ltd. Support d'enregistrement d'information et son procédé de fabrication
FR2507805A1 (fr) * 1981-06-12 1982-12-17 Rca Corp Milieu d'enregistrement reversible et disque contenant de l'information realise a partir de ce milieu
WO1984004824A1 (fr) * 1983-05-31 1984-12-06 Storage Technology Corp Structure d'enregistrement optique impliquant une reaction chimique in situ dans la structure active

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0050047A2 (fr) * 1980-10-15 1982-04-21 Hitachi, Ltd. Support d'enregistrement d'information et son procédé de fabrication
FR2507805A1 (fr) * 1981-06-12 1982-12-17 Rca Corp Milieu d'enregistrement reversible et disque contenant de l'information realise a partir de ce milieu
WO1984004824A1 (fr) * 1983-05-31 1984-12-06 Storage Technology Corp Structure d'enregistrement optique impliquant une reaction chimique in situ dans la structure active

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4857373A (en) * 1987-03-31 1989-08-15 E. I. Du Pont De Nemours And Company Optical recording element

Also Published As

Publication number Publication date
EP0189462A1 (fr) 1986-08-06

Similar Documents

Publication Publication Date Title
US4430659A (en) Protuberant optical recording medium
US4947372A (en) Optical information memory medium for recording and erasing information
EP0092113B1 (fr) Elément d'enregistrement optique pour un système de mémoire optique et un procédé de fabrication de l'élément
US4470053A (en) Protuberant optical recording medium
JP2001023244A (ja) 光記録媒体およびその製造方法と、光記録装置
US4600682A (en) Optical storage structure
US4539572A (en) Optical recording medium
EP0360466A1 (fr) Support d'enregistrement d'information optique et méthode d'enregistrement et de reproduction
WO1986000744A1 (fr) Structure de stockage optique
JP3873605B2 (ja) 情報記録媒体用原盤、スタンパー及び情報記録媒体の製造方法
EP0096504B1 (fr) Feuilles d'enregistrement aureuses, destinées à des fins archivistiques, pour mettre en mémoire des données digitales
US4625217A (en) Broad band multilayer optical storage structure having a thin metallic optically transmissive layer
JPS6025035A (ja) 光学記録媒質
EP0098046B1 (fr) Feuilles d'enregistrement destinées à des fins archivistiques pour mettre en mémoire des données digitales en utilisant un laser à écrire à puissance basse
JPH0273537A (ja) 光学的情報記録媒体
EP0096501B1 (fr) Procédé de détection d'incendie
EP0097430B1 (fr) Procédé de détection d'incendie
EP0098045B1 (fr) Feuilles d'enregistrement contenant de l'or, destinées à des fins archivistiques, pour mettre en mémoire des données digitales en utilisant un laser à écrire à puissance basse
JP4244090B2 (ja) 光学的情報記録用媒体
JPH10289478A (ja) 光学式情報記録媒体及びその製造方法
JP2810092B2 (ja) 光学情報記録媒体
JPH08267925A (ja) 光記録媒体およびその製造方法
WO1983004333A1 (fr) Films d'enregistrement isoles a ilots pour le stockage de donnees numeriques utilisant un laser d'ecriture a faible energie
JPH02122985A (ja) 光学記録媒体
JPH0573954A (ja) 光学情報記録媒体及びその製造方法

Legal Events

Date Code Title Description
AK Designated states

Designated state(s): JP

AL Designated countries for regional patents

Designated state(s): DE FR GB NL