WO1979000904A1 - Etancheite des bords d'un materiau en plaque - Google Patents
Etancheite des bords d'un materiau en plaque Download PDFInfo
- Publication number
- WO1979000904A1 WO1979000904A1 PCT/DK1979/000013 DK7900013W WO7900904A1 WO 1979000904 A1 WO1979000904 A1 WO 1979000904A1 DK 7900013 W DK7900013 W DK 7900013W WO 7900904 A1 WO7900904 A1 WO 7900904A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin composition
- edge
- moisture
- resistant
- resin
- Prior art date
Abstract
Methode pour assurer une protection etanche des bords d'un materiau en plaque, en particulier d, un materiau en plaque comprenant un noyau ou materiau de base non resistant a l'humidite, dont les surfaces ont ete rendues resistantes a l'humidite, par exemple en les recouvrant avec un lamine resistant a l'humidite. La methode consiste a deposer sur les surfaces des bords dudit materiau une couche circonferentielle d'une composition de resine durcissable, ladite composition de resine subissant un retrait lors de son durcissement, et a laisser durcir ladite couche d'une composition de resine pour former un moulage fixe et coherent sur le pour tour des bords.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE792945434A DE2945434A1 (en) | 1978-04-08 | 1979-04-06 | Edge-sealing of plate materials |
DK523079A DK523079A (da) | 1978-04-08 | 1979-12-07 | Kantforsegling af pladeformede materialer |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB1385378 | 1978-04-08 | ||
GB13853/78 | 1978-04-08 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1979000904A1 true WO1979000904A1 (fr) | 1979-11-15 |
Family
ID=10030564
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/DK1979/000013 WO1979000904A1 (fr) | 1978-04-08 | 1979-04-06 | Etancheite des bords d'un materiau en plaque |
Country Status (7)
Country | Link |
---|---|
EP (1) | EP0014208A1 (fr) |
JP (1) | JPS55500259A (fr) |
DE (1) | DE2945434A1 (fr) |
DK (1) | DK523079A (fr) |
GB (1) | GB2035898A (fr) |
SE (1) | SE7910043L (fr) |
WO (1) | WO1979000904A1 (fr) |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1154090A1 (fr) * | 2000-05-11 | 2001-11-14 | POZZI AROSIO INDUSTRIA VERNICI SPECIALI DI ALESSANDRO POZZI & C. S.A.S. | Procédé pour fabriquer des articles composites et article composite ainsi obtenu |
EP1300225A1 (fr) * | 2001-10-05 | 2003-04-09 | SACEA S.p.A. | Procédé de biseautage de panneaux de copeaux de bois ou similaires, et panneaux biseautés ainsi obtenus |
GB2418174A (en) * | 2003-09-19 | 2006-03-22 | Kingspan Res & Dev Ltd | Composite insulating panel |
US11000875B2 (en) | 2015-10-02 | 2021-05-11 | Homag Gmbh | Method and device for narrow surface coating |
CN113083646A (zh) * | 2021-04-06 | 2021-07-09 | 嵊州市艺匠木艺股份有限公司 | 铝木复合板侧面油漆涂装方法 |
WO2021254329A1 (fr) * | 2020-06-17 | 2021-12-23 | 程建平 | Procédé de coulage de bord de panneau et application de ce dernier |
RU2794049C1 (ru) * | 2022-08-31 | 2023-04-11 | Юрий Александрович Акифьев | Способ изготовления влагостойкой мебельной или строительной детали |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2175820B (en) * | 1985-12-20 | 1989-10-11 | Strand Furniture Limited | Plastics laminated worktop |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1104353A (en) * | 1966-01-28 | 1968-02-28 | Sidney Axelrod | Covering material for model airplanes and other frames and methods for applying same |
SE381071B (sv) * | 1974-01-11 | 1975-11-24 | Casco Ab | Beleggning och tetning av spanskivekanter |
SE396199B (sv) * | 1975-03-11 | 1977-09-12 | Casco Ab | Sett for beleggning av kanterna hos span- och trefiberskivor och liknande cellulosabaserade formkroppar |
-
1979
- 1979-04-06 WO PCT/DK1979/000013 patent/WO1979000904A1/fr unknown
- 1979-04-06 GB GB7944215A patent/GB2035898A/en not_active Withdrawn
- 1979-04-06 JP JP50066279A patent/JPS55500259A/ja active Pending
- 1979-04-06 DE DE792945434A patent/DE2945434A1/de active Pending
- 1979-11-08 EP EP79900411A patent/EP0014208A1/fr not_active Withdrawn
- 1979-12-06 SE SE7910043A patent/SE7910043L/xx unknown
- 1979-12-07 DK DK523079A patent/DK523079A/da not_active Application Discontinuation
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1104353A (en) * | 1966-01-28 | 1968-02-28 | Sidney Axelrod | Covering material for model airplanes and other frames and methods for applying same |
SE381071B (sv) * | 1974-01-11 | 1975-11-24 | Casco Ab | Beleggning och tetning av spanskivekanter |
SE396199B (sv) * | 1975-03-11 | 1977-09-12 | Casco Ab | Sett for beleggning av kanterna hos span- och trefiberskivor och liknande cellulosabaserade formkroppar |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1154090A1 (fr) * | 2000-05-11 | 2001-11-14 | POZZI AROSIO INDUSTRIA VERNICI SPECIALI DI ALESSANDRO POZZI & C. S.A.S. | Procédé pour fabriquer des articles composites et article composite ainsi obtenu |
EP1300225A1 (fr) * | 2001-10-05 | 2003-04-09 | SACEA S.p.A. | Procédé de biseautage de panneaux de copeaux de bois ou similaires, et panneaux biseautés ainsi obtenus |
GB2418174A (en) * | 2003-09-19 | 2006-03-22 | Kingspan Res & Dev Ltd | Composite insulating panel |
GB2418174B (en) * | 2003-09-19 | 2008-12-24 | Kingspan Res & Dev Ltd | A composite insulating panel and its method of manufacture |
US11000875B2 (en) | 2015-10-02 | 2021-05-11 | Homag Gmbh | Method and device for narrow surface coating |
WO2021254329A1 (fr) * | 2020-06-17 | 2021-12-23 | 程建平 | Procédé de coulage de bord de panneau et application de ce dernier |
CN113083646A (zh) * | 2021-04-06 | 2021-07-09 | 嵊州市艺匠木艺股份有限公司 | 铝木复合板侧面油漆涂装方法 |
RU2794049C1 (ru) * | 2022-08-31 | 2023-04-11 | Юрий Александрович Акифьев | Способ изготовления влагостойкой мебельной или строительной детали |
RU2814229C1 (ru) * | 2023-05-03 | 2024-02-28 | Юрий Александрович Акифьев | Способ изготовления влагостойкой мебельной или строительной детали |
Also Published As
Publication number | Publication date |
---|---|
DE2945434A1 (en) | 1980-12-11 |
SE7910043L (sv) | 1979-12-06 |
EP0014208A1 (fr) | 1980-08-20 |
DK523079A (da) | 1979-12-07 |
GB2035898A (en) | 1980-06-25 |
JPS55500259A (fr) | 1980-05-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1097278B1 (fr) | Ensemble porte moule par compression | |
US6226958B1 (en) | Insulated door assembly with low thermal deflection | |
RU2494869C2 (ru) | Композитные изделия и способ их изготовления (варианты) | |
EP0157681B1 (fr) | Article conformé en résine de polycarbonate résistant au rayage et aux intempéries et procédé pour sa fabrication | |
JPS60253542A (ja) | 化粧板及びその製法 | |
US6113199A (en) | Laboratory countertop | |
US5102710A (en) | Composite decorate panel | |
WO1979000904A1 (fr) | Etancheite des bords d'un materiau en plaque | |
CA2760402A1 (fr) | Utilisation d'un materiau composite a base de colle polyurethane monocomposant | |
US5688602A (en) | Method for producing laminated articles | |
CA2246181A1 (fr) | Ensemble de porte isolee amelioree presentant une faible deformation thermique | |
DE2355652A1 (de) | Flammhemmende massen und gegenstaende | |
US6200686B1 (en) | Unsaturated polyester resin composition, molding using the same, and production process thereof | |
US3885075A (en) | Composite slate structure | |
US4729919A (en) | Protective barrier coating for styrofoam using an unsaturated thermosettable resin composition | |
KR100563994B1 (ko) | 실험대용 내화학성 상판 | |
KR200402925Y1 (ko) | 멜라민 수지를 이용한 콘크리트 거푸집 패널 | |
US4562103A (en) | Weather resistant boards | |
JP2001519496A (ja) | 圧縮成形され、挿入された熱硬化性ドア採光窓枠、埋め込み成形品および装飾パネル | |
EP0727304B1 (fr) | Procédé de fabrication d'un élément de structure et élément ainsi obtenu | |
CA2295816A1 (fr) | Materiau sous forme de panneau | |
AU732825B2 (en) | Method for producing laminated articles | |
CN2387189Y (zh) | 一种防腐强化竹地板 | |
TW202112959A (zh) | 環保型聚酯模塑組合物及塑膠板材的製作方法 | |
AU2003203706B2 (en) | Entry Way Door Members |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Designated state(s): BR CH DE DK GB JP LU SE SU US |
|
AL | Designated countries for regional patents |
Designated state(s): FR |
|
RET | De translation (de og part 6b) |
Ref country code: DE Ref document number: 2945434 Date of ref document: 19801211 Format of ref document f/p: P |