US20230256491A1 - 6xxx aluminum alloys - Google Patents

6xxx aluminum alloys Download PDF

Info

Publication number
US20230256491A1
US20230256491A1 US18/135,553 US202318135553A US2023256491A1 US 20230256491 A1 US20230256491 A1 US 20230256491A1 US 202318135553 A US202318135553 A US 202318135553A US 2023256491 A1 US2023256491 A1 US 2023256491A1
Authority
US
United States
Prior art keywords
extruded product
6xxx
product
extruded
billet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US18/135,553
Other languages
English (en)
Inventor
Yimin Ruan
John S. Maskell
Bryan K. Murphy
Patrick Berube
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Arconic Technologies LLC
Original Assignee
Arconic Technologies LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arconic Technologies LLC filed Critical Arconic Technologies LLC
Priority to US18/135,553 priority Critical patent/US20230256491A1/en
Assigned to ARCONIC TECHNOLOGIES LLC reassignment ARCONIC TECHNOLOGIES LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BERUBE, PATRICK, MASKELL, John S., MURPHY, Bryan K., RUAN, Yimin
Publication of US20230256491A1 publication Critical patent/US20230256491A1/en
Assigned to JPMORGAN CHASE BANK, N.A. reassignment JPMORGAN CHASE BANK, N.A. NOTICE OF GRANT OF SECURITY INTEREST (ABL) IN INTELLECTUAL PROPERTY Assignors: ARCONIC TECHNOLOGIES LLC
Assigned to U.S. BANK TRUST COMPANY, NATIONAL ASSOCIATION reassignment U.S. BANK TRUST COMPANY, NATIONAL ASSOCIATION NOTICE OF GRANT OF SECURITY INTEREST IN INTELLECTUAL PROPERTY (FIRST LIEN) Assignors: ARCONIC TECHNOLOGIES LLC
Pending legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/05—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys of the Al-Si-Mg type, i.e. containing silicon and magnesium in approximately equal proportions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21C—MANUFACTURE OF METAL SHEETS, WIRE, RODS, TUBES OR PROFILES, OTHERWISE THAN BY ROLLING; AUXILIARY OPERATIONS USED IN CONNECTION WITH METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL
    • B21C23/00—Extruding metal; Impact extrusion
    • B21C23/002—Extruding materials of special alloys so far as the composition of the alloy requires or permits special extruding methods of sequences
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21C—MANUFACTURE OF METAL SHEETS, WIRE, RODS, TUBES OR PROFILES, OTHERWISE THAN BY ROLLING; AUXILIARY OPERATIONS USED IN CONNECTION WITH METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL
    • B21C29/00—Cooling or heating work or parts of the extrusion press; Gas treatment of work
    • B21C29/003—Cooling or heating of work
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/003—Alloys based on aluminium containing at least 2.6% of one or more of the elements: tin, lead, antimony, bismuth, cadmium, and titanium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent
    • C22C21/08—Alloys based on aluminium with magnesium as the next major constituent with silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/043—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
    • C22F1/053—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with zinc as the next major constituent

Definitions

  • Press-quenching of extruded 6xxx aluminum alloy products facilitates rapid production of such extruded products without the need for a separate solution heat treatment step following the extrusion process.
  • a press quenched product is one that has been rapidly cooled from an elevated deformation extrusion temperature by immersion in a liquid bath, such as oil or water, so as to withdraw heat rapidly from the product.
  • the purpose of quenching is to suppress a phase transformation so as to obtain increased hardness, or other desirable properties.
  • an aluminum alloy product such as a billet or ingot
  • it is first reheated to and held at a temperature in the alloy above the solubility temperature in the precipitated phases in the aluminum matrix, for instance the solubility temperature for the magnesium (Mg)-silicon (Si) phases in a billet made of an Al—Mg—Si-alloy, until the phases are dissolved.
  • the product is then quickly cooled or quenched to the desired extrusion temperature to prevent new precipitation of these phases in the alloy structure, and then extruded.
  • the present patent application relates to new press-quenched 6xxx aluminum alloy products and methods and systems for producing the same.
  • the new methods and systems may facilitate, for instance, production of 6xxx aluminum alloy products having an improved combination of properties, such an improved combination of strength and ductility (elongation).
  • the method includes homogenizing ( 110 ) a billet of a 6xxx aluminum alloy, preheating ( 120 ) the billet, extruding ( 130 ) the billet in an extrusion apparatus, discharging ( 140 ) the extruded product from extrusion apparatus while maintaining ( 145 ) the extruded product at an appropriate pre-quench temperature, quenching ( 150 ) the extruded product, and then artificially aging ( 160 ) the extruded product.
  • FIG. 2 One embodiment of a system ( 200 ) for completing method ( 100 ) is illustrated in FIG. 2 .
  • FIGS. 1 - 2 are used below, in a non-limiting fashion, to illustrate embodiments of the new inventive methods and systems.
  • the homogenizing step ( 110 ) is optional and generally includes heating a billet of the 6xxx aluminum alloy to one or more temperatures for one or more times to homogenize the as-cast structure. After the homogenizing step, the billet is generally cooled to room temperature and stored until it is to be extruded.
  • the term “billet” encompassed both round billet and rectangular ingot.
  • the preheating step ( 120 ), the extruding step ( 130 ), the discharging step ( 140 ) and the quenching step ( 150 ) are completed in order and without any intervening steps. This is to ensure an appropriate microstructure is achieved in the final product.
  • the billet is preheated ( 120 ) to a preheat temperature and then held at this temperature for a time sufficient to dissolve at least some precipitate phases of the billet.
  • the preheating step ( 120 ) may be completed in a furnace ( 220 ).
  • the preheat temperature is at least 50% of the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. For instance, if the solvus temperature is 962° F., “at least 50% of the solvus temperature” is ⁇ 481° F., so the preheat temperature would be ⁇ 481° F. but below the incipient melting point of the 6xxx aluminum alloy.
  • solvus temperature means the lowest temperature at which all of the following precipitate phases would completely be dissolved at equilibrium in the 6xxx aluminum alloy billet and without incipient melting of the 6xxx aluminum alloy billet:
  • the preheat temperature is at least 60% of the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In another embodiment, the preheat temperature is at least 70% of the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In yet another embodiment, the preheat temperature is at least 80% of the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In another embodiment, the preheat temperature is at least 90% of the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy.
  • the preheat temperature is at least 95% of the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In another embodiment, the preheat temperature is at or above the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In yet another embodiment, the preheat temperature is at least 5° F. above the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In another embodiment, the preheat temperature is at least 10° F. above the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy.
  • the preheat temperature is at least 15° F. above the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. In another embodiment, the preheat temperature is at least 20° F. above the solvus temperature of the 6xxx aluminum alloy but below the incipient melting point of the 6xxx aluminum alloy. Generally, when high mechanical properties are desired, the preheat temperature should be at least 90-100% of the solvus temperature, or higher.
  • the preheating step ( 120 ) also includes holding the billet at the preheat temperature for a period of time sufficient to dissolve at least some precipitate phases of the 6xxx aluminum alloy.
  • the holding time may depend on, for instance, the size of the billet and the desired end properties.
  • the preheating step ( 120 ) includes holding the billet at the preheat temperature for a period of time sufficient to dissolve the majority of, or even all of, the precipitate phases of the 6xxx aluminum alloy.
  • the holding time is at least 1 minute.
  • the holding time is at least 5 minutes.
  • the holding time is at least 10 minutes.
  • the holding time is at least 20 minutes.
  • the holding time is at least 30 minutes.
  • the holding time is at least 40 minutes. In yet another embodiment, the holding time is at least 50 minutes, or more. Generally, when high mechanical properties are desired, the holding time at the preheat temperature should be sufficient to dissolve the majority of, or even all of, the precipitate phases of the 6xxx aluminum alloy. As may be appreciated, a plurality of preheat temperatures and a corresponding plurality of preheat holding times may be employed.
  • the preheat temperature is at least 950° F. In another embodiment, the preheat temperature is at least 960° F. In yet another embodiment, the preheat temperature is at least 970° F. In another embodiment, the preheat temperature is at least 975° F. In any of the above embodiments, the preheat holding time may be 40-60 minutes (e.g., with a fifteen-inch diameter billet).
  • Non-limiting embodiments of a preheating step are shown in FIGS. 3 a - 3 b .
  • the billet is heated (a) from room temperature (T room ) to a preheat temperature, which, in this case is the metallurgical required temperature (T MR ) or the temperature required to achieve high mechanical properties.
  • T MR metallurgical required temperature
  • T solvus T solvus
  • the preheat holding time referred to as t mr and shown as (b) in FIGS. 3 a - 3 b , is generally long so as to dissolve the majority of, or even all of, the precipitate phases of the 6xxx aluminum alloy.
  • the preheat temperature (T MR ) is below the incipient melting temperature or T solidus , i.e., no eutectic melting should occur.
  • the extrusion process (described in further detail below) may result in further heating of the product. This further heating generally should avoid the product exceeding the incipient melting temperature or T solidus of the 6xxx aluminum alloy.
  • the preheat temperature is generally at least 10° F. below the incipient melting temperature of the 6xxx aluminum alloy billet. In one embodiment, the preheat temperature is at least 20° F. below the incipient melting temperature of the 6xxx aluminum alloy billet.
  • the preheat temperature is at least 30° F. below the incipient melting temperature of the 6xxx aluminum alloy billet. In yet another embodiment, the preheat temperature is at least 40° F. below the incipient melting temperature of the 6xxx aluminum alloy billet. In another embodiment, the preheat temperature is at least 50° F. below the incipient melting temperature of the 6xxx aluminum alloy billet.
  • the preheated billet is immediately transferred to an extrusion apparatus where the billet is extruded ( 130 ).
  • the term “immediately transferred to an extrusion press” means that the surface of the billet realizes a temperature drop of not greater than 100° F. from the time it exits the preheating apparatus (e.g., furnace 220 ) to the time it enters the extrusion apparatus (e.g., extrusion press 230 ). This is also shown in FIGS. 3 a - 3 b , where the transferring step (c) shows a very low temperature drop.
  • the low temperature drop is generally completed by utilizing a small distance between the preheating apparatus and the extrusion apparatus in combination with appropriate scheduling of billet flow through the various apparatus of the system ( 200 ). Maintaining a low temperature drop from the preheat apparatus to the extrusion apparatus may facilitate realization of the desired microstructure and properties. Due to the high preheat temperatures employed with the preheating step ( 120 ), an extrusion press ( 230 ) can rapidly and efficiently extrude the billet into the end product during the extrusion step ( 130 ), which increases productivity.
  • the billet realizes a temperature drop of not greater than 75° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus. In another embodiment, the billet realizes a temperature drop of not greater than 50° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus. In yet another embodiment, the billet realizes a temperature drop of not greater than 40° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus. In another embodiment, the billet realizes a temperature drop of not greater than 30° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus.
  • the billet realizes a temperature drop of not greater than 20° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus. In another embodiment, the billet realizes a temperature drop of not greater than 10° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus. In yet another embodiment, the billet realizes a temperature drop of not greater than 5° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus. In another embodiment, the billet realizes a temperature drop of not greater than 2° F. from the time it exits the preheating apparatus to the time it enters the extrusion apparatus.
  • the extruding step ( 130 ) generally comprises extruding the billet into an appropriate suitable end product, such as a bar, rod, tube or a complex shape via an extrusion apparatus, such as an extrusion press ( 230 ).
  • the extruding step may be accomplished by direct or indirect extrusion.
  • the extruding step ( 130 ) comprises maintaining the billet and the extruded product at or above the preheat temperature.
  • the extruding step comprises heating the extruded product during the extruding step ( 130 ). Extrusion heating may result, for instance, due to friction imparted on the billet by the extrusion apparatus (e.g., extrusion press ( 230 )) during the extruding step).
  • the extrusion exit temperature (EET) is the temperature of the extruded product immediately after it exits the extrusion apparatus.
  • the extrusion exit temperature (EET) is at least 10° F. higher than the preheat temperature.
  • the extrusion exit temperature (EET) is at least 20° F. higher than the preheat temperature.
  • the extrusion exit temperature (EET) is at least 30° F. higher than the preheat temperature.
  • the extrusion exit temperature (EET) is at least 40° F. higher than the preheat temperature.
  • the extrusion exit temperature (EET) is at least 50° F. higher than the preheat temperature.
  • the extruded product is discharged from the extrusion apparatus ( 140 ).
  • the temperature of the extruded product is maintained ( 145 ) close to that of the extrusion exit temperature (EET) until the product can be quenched ( 150 ) by water or another suitable quenching medium.
  • EET extrusion exit temperature
  • FIGS. 3 a - 3 b the temperature drop (e) from the extruding step (d) to the quenching step (f) is low.
  • the temperature of the extruded product is maintained within 100° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences.
  • the temperature of the extruded product is maintained within 75° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences. In another embodiment, the temperature of the extruded product is maintained within 50° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences. In yet another embodiment, the temperature of the extruded product is maintained within 40° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences. In another embodiment, the temperature of the extruded product is maintained within 30° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences.
  • the temperature of the extruded product is maintained within 20° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences. In another embodiment, the temperature of the extruded product is maintained within 10° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences. In yet another embodiment, the temperature of the extruded product is maintained within 5° F. of the extrusion exit temperature (EET) until the quenching step ( 150 ) commences.
  • the maintaining step ( 145 ) comprises maintaining the extruded product at or above the solvus temperature until the quenching step ( 150 ) commences. In one embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 5° F. above the solvus temperature until the quench commences. In another embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 10° F. above the solvus temperature until the quench commences. In yet another embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 15° F. above the solvus temperature until the quench commences. In another embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 20° F.
  • the maintaining step ( 145 ) comprises maintaining the extruded product at least 25° F. above the solvus temperature until the quench commences. In another embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 30° F. above the solvus temperature until the quench commences. In yet another embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 35° F. above the solvus temperature until the quench commences. In another embodiment, the maintaining step ( 145 ) comprises maintaining the extruded product at least 40° F. above the solvus temperature until the quench commences.
  • an exit shroud ( 240 ) may be used to facilitate the maintaining step ( 145 ).
  • the exit shroud ( 240 ) may be directly adjacent to the outlet of the extrusion apparatus ( 230 ) so as to facilitate the maintaining step ( 145 ).
  • an extrusion press tunnel Within the extrusion press tunnel may be located one or more passive and/or active heating apparatus. Examples of a passive heating apparatus include a surrounding shield designed to reflect heat radiated from the extruded product back towards the product.
  • the surrounding shield may fully encompass (e.g., encircle) the extruded product or may partially surround the extruded product.
  • a heat shield comprises a material adapted to reflect heat radiated from the extruded product, such as a metal (e.g., stainless steel). Insulating materials such as supported fiberglass, ceramic fiber, and mineral wool blankets, for instance, may also or alternatively be used to maintain the extruded product temperature within the needed tolerance.
  • Other apparatus useful for retaining heat include hot air curtains or physical curtains, such as chain mail.
  • active heating apparatus include radiative heat lamps, hot air fans, and resistance heaters, among others. Both active and passive heating apparatus/materials may be used.
  • the extruded product is immediately moved to a quenching apparatus ( 250 ), such as an apparatus including a stationary or moving water spray and/or a water bath, so as to rapidly quench the product to a suitable low temperature, such as room temperature.
  • a quenching apparatus such as an apparatus including a stationary or moving water spray and/or a water bath
  • the quenching step (f) rapidly quenches the extruded product received from the exit shroud to T room .
  • the quenching step ( 150 ) occurs immediately after the discharging step ( 140 ).
  • the quenching step may be begin by contacting exposed portions of the extruded product as they exit the exit shroud ( 240 ), i.e., when the exposed portions are those no longer contained within the exit shroud ( 240 ).
  • the exposed portions of the extruded product are within 50° F. of the solvus temperature when the quenching medium initially contacts the discharged extruded product.
  • the exposed portions of the extruded product are within 40° F. of the solvus temperature when the quenching medium initially contacts the discharged extruded product.
  • the exposed portions of the extruded product are within 30° F.
  • the exposed portions of the extruded product are within 20° F. of the solvus temperature when the quenching medium initially contacts the discharged extruded product. In yet another embodiment, the exposed portions of the extruded product are within 10° F. of the solvus temperature when the quenching medium initially contacts the discharged extruded product. In another embodiment, the exposed portions of the extruded product are at or above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In yet another embodiment, the exposed portions of the extruded product are at least 5° F.
  • the exposed portions of the extruded product are at least 10° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In yet another embodiment, the exposed portions of the extruded product are at least 15° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In another embodiment, the exposed portions of the extruded product are at least 20° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In yet another embodiment, the exposed portions of the extruded product are at least 25° F.
  • the exposed portions of the extruded product are at least 30° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In yet another embodiment, the exposed portions of the extruded product are at least 35° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In another embodiment, the exposed portions of the extruded product are at least 40° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product. In yet another embodiment, the exposed portions of the extruded product are at least 45° F. above the solvus temperature when the quenching medium initially contacts the discharged extruded product.
  • the quenching step ( 150 ) may begin by contacting the exposed portions of the extruded product as they exit the exit shroud ( 240 ). As shown in FIG. 4 , this may be accomplished, for instance, by using a water spray located immediately adjacent the outlet of the exit shroud, which may be in the form of an extrusion press tunnel. In one embodiment, the water contacts the exposed portions of the extrusion within 60 seconds of their exit from the exit shroud. In another embodiment, the water contacts the exposed portions of the extrusion within 45 seconds of their exit from the exit shroud. In yet another embodiment, the water contacts the exposed portions of the extrusion within 30 seconds of their exit from the exit shroud.
  • the water contacts the exposed portions of the extrusion within 20 seconds of their exit from the exit shroud. In yet another embodiment, the water contacts the exposed portions of the extrusion within 10 seconds of their exit from the exit shroud. In another embodiment, the water contacts the exposed portions of the extrusion within 8 seconds of their exit from the exit shroud. In yet another embodiment, the water contacts the exposed portions of the extrusion within 5 seconds of their exit from the exit shroud.
  • the quenching apparatus may include a quench bath, such as an immersion bath (stationary water cooling).
  • the quench bath may be located downstream of any quenching water spray.
  • the use of the water bath may facilitate further rapid cooling of the extruded product (extrudate) to an appropriate temperature (e.g., quenching to room temperature, as shown in FIGS. 3 a - 3 b (T room )).
  • the relative motion between the extrudates and the water creates a shear flow on the surfaces of the extrudate, which increases cooling effectiveness.
  • the water bath facilitates a quench rate of at least 1° F./second.
  • the water bath quench rate is measured by determining the temperature of the extruded prior to entering the water bath and then measuring the time it takes for the extruded product to reach a temperature of 125° F.
  • the water bath facilitates a quench rate of at least 5° F./second.
  • the water bath facilitates a quench rate of at least 10° F./second.
  • the water bath facilitates a quench rate of at least 20° F./second.
  • the water bath facilitates a quench rate of at least 30° F./second.
  • quenching medium may be used, which quenching medium is preferably in liquid form.
  • steps ( 120 )-( 150 ) and their associated system components ( 220 )-( 250 ), described above, facilitate the production of press-quenched 6xxx aluminum alloy product having improved microstructures and, hence, an improved combination of properties.
  • press-quenched products may be immediately aged (g) and/or further cold worked (h) (e.g., drawn) and without any additional solution heat treatment steps.
  • the extruded products may be processed to any of a T6, T8 or T9 temper, as illustrated in FIGS. 3 a - 3 b .
  • T6, T8 or T9 tempered products generally realize an improved combination of properties due to the press-quenching methods and apparatus described herein.
  • an extruded product may be discharged ( 140 ) from the extrusion apparatus but without the use of an exit shroud ( 240 ).
  • the extruded product should be quenched ( 150 ) as soon as possible after the discharging step ( 140 ) when high tensile properties are required.
  • the new systems and methods may be applied to any 6xxx aluminum alloy that is suited for extrusion.
  • the 6xxx aluminum alloy includes from 0.2 to 2.0 wt. % Si, from 0.2 to 1.5 wt. % Mg, from 0.07 to 1.0 wt. % Mn, up to 1.5 wt. % Bi, up to 1.5 wt. % Sn, up to 1.0 wt. % Cu, up to 1.0 wt. % Zn, up to 0.7 wt. % Pb, up to 0.7 wt. % Fe, up to 0.35 wt. % Cr, up to 0.35 wt. % V, up to 0.25 wt. % Zr, and up to 0.20 wt. % Ti, the balance being aluminum, optional incidental elements and impurities.
  • incidental elements means those elements or materials, other than the above listed elements, that may optionally be added to the alloy to assist in the production of the alloy.
  • incidental elements include casting aids, such as deoxidizers.
  • Optional incidental elements may be included in the alloy in a cumulative amount of up to 1.0 wt. %.
  • one or more incidental elements may be added to the alloy during casting to reduce or restrict (and in some instances eliminate) ingot cracking due to, for example, oxide fold, pit and oxide patches.
  • deoxidizers examples include Ca, Sr, and Be.
  • Ca calcium
  • it is generally present in an amount of up to about 0.05 wt. %, or up to about 0.03 wt. %.
  • Ca is included in the alloy in an amount of about 0.001-0.03 wt % or about 0.05 wt. %, such as 0.001-0.008 wt. % (or 10 to 80 ppm).
  • Strontium (Sr) may be included in the alloy as a substitute for Ca (in whole or in part), and thus may be included in the alloy in the same or similar amounts as Ca.
  • beryllium (Be) additions have helped to reduce the tendency of ingot cracking, though for environmental, health and safety reasons, some embodiments of the alloy are substantially Be-free.
  • Be When Be is included in the alloy, it is generally present in an amount of up to about 20 ppm. Incidental elements may be present in minor amounts, or may be present in significant amounts, and may add desirable or other characteristics on their own without departing from the alloy described herein, so long as the alloy retains the desirable characteristics described herein. It is to be understood, however, that the scope of this disclosure should not/cannot be avoided through the mere addition of an element or elements in quantities that would not otherwise impact on the combinations of properties desired and attained herein.
  • the new 6xxx aluminum alloys may contain low amounts of impurities.
  • a new 6xxx aluminum alloy includes not greater than 0.15 wt. %, in total, of the impurities, and wherein the aluminum alloy includes not greater than 0.05 wt. % of each of the impurities.
  • a new 6xxx aluminum alloy includes not greater than 0.10 wt. %, in total, of the impurities, and wherein the aluminum alloy includes not greater than 0.03 wt. % of each of the impurities.
  • the 6xxx aluminum alloy is one of a 6026LF, 6020, 6262A and a 6061 aluminum alloy.
  • the compositions of the conventional 6020, 6262A, and 6061 alloys described herein are per the Aluminum Association document entitled “International Alloy Designations and Chemical Composition Limits for Wrought Aluminum and Wrought Aluminum Alloys” (2015).
  • the “6026LF” alloy is a lead-free version of the 6026 alloy, and includes 0.60-1.40 wt. % Si, ⁇ 0.70 wt. % Fe, 0.20-0.50 wt. % Cu, 0.20-1.00 wt. % Mn, 0.60-1.20 wt. % Mg, ⁇ 0.30 wt.
  • the 6xxx aluminum alloy products may realize inventive microstructure.
  • a 6xxx aluminum alloy realizes an unrecrystallized microstructure as measured from T/10 to 9T/10 of the 6xxx extruded product wherein the unrecrystallized microstructure comprises at least 50 vol. % unrecrystallized grains.
  • at least 60% of the unrecrystallized grains are fibrous grains. Fibrous grains are those having an aspect ratio (grain length/diameter) of at least 5:1.
  • the average grain size of the unrecrystallized microstructure is not greater than 200 microns.
  • the 6xxx extruded product realizes a recrystallized microstructure as measured from T/10 to 9T/10 of the 6xxx extruded product wherein the recrystallized microstructure comprises at least 50 vol. % recrystallized grains.
  • at least 60% of the recrystallized grains are equiaxed grains having as aspect ratio of less than 5:1 (L:LT) (e.g., from 1:1 to 4.9:1; or from 1.5:1 to 4.9:1).
  • the average grain size of the recrystallized microstructure is not greater than 200 microns.
  • the new 6xxx aluminum alloys may realize an improved combination of properties, such as an improved combination of strength and elongation.
  • the new 6xxx aluminum alloy is a new 6026LF extruded product i.e., made by the inventive methods and/or systems described herein.
  • the new 6026LF extruded product may realize at least 5% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6026LF product.
  • a new 6026LF extruded product may realize at least 10% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6026LF product of the same product form, size and temper.
  • a new 6026LF extruded product may realize at least 15% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6026LF product of the same product form, size and temper. In yet another embodiment, a new 6026LF extruded product may realize at least 20% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6026LF product of the same product form, size and temper.
  • a new 6026LF extruded product realizes a tensile yield strength (typical)(L) of at least at least 54 ksi, or at least 55 ksi, or at least 56 ksi, or at least 57 ksi, or more.
  • a tensile yield strength typically (typical)(L) of at least at least 54 ksi, or at least 55 ksi, or at least 56 ksi, or at least 57 ksi, or more.
  • the new 6026LF extruded product may realize the above strength values in combination with an elongation (longitudinal or L) of at least 3%. In another embodiment, the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 4% (L). In yet another embodiment, the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 5% (L). In another embodiment, the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 6% (L). In yet another embodiment, the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 7% (L).
  • the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 8% (L). In another embodiment, the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 9% (L). In yet another embodiment, the new 6026LF extruded product may realize the above strength values in combination with an elongation of at least 10% (L).
  • a new extruded 6026LF aluminum alloy product realizes at least one of (a) 17 vol. % cube (ED) texture and (b) a maximum ODF [001] intensity of at least 9.7, as measured per the EBSD Sample Procedure, below.
  • the extruded 6026LF aluminum alloy realizes at least 18 vol. % cube (ED) texture, or at least 19 vol. % cube (ED) texture.
  • the extruded 6026LF aluminum alloy product realizes a maximum ODF [001] intensity of at least 9.8, or at least 10.0, or at least 10.2, or at least 10.4, or at least 10.6, or at least 10.8, or at least 11.0, or at least 11.2.
  • the new 6xxx aluminum alloy is a new 6020 extruded product i.e., made by the inventive methods and/or systems described herein.
  • the new 6020 extruded product may realize at least 5% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6020 product, e.g., a 6020 extruded product made in accordance with U.S. Pat. No. 7,422,645, of the same product form, size and temper.
  • a new 6020 extruded product may realize at least 10% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6020 product of the same product form, size and temper. In another embodiment, a new 6020 extruded product may realize at least 15% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6020 product of the same product form, size and temper.
  • a new 6020 extruded product may realize at least 20% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6020 product of the same product form, size and temper.
  • a new extruded 6020 product realizes a tensile yield strength (typical) (L) of at least 34 ksi, or at least 35 ksi, or at least 36 ksi, or at least 37 ksi, or at least 38 ksi, or at least 39 ksi, or at least 40 ksi, or at least 41 ksi, or at least 42 ksi, or at least 43 ksi, or at least 44 ksi, or at least 45 ksi.
  • the new 6020 extruded product may realize the above strength values in combination with an elongation (longitudinal or L) of at least 8%.
  • the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 9% (L). In yet another embodiment, the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 10% (L). In another embodiment, the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 11% (L). In yet another embodiment, the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 12% (L). In another embodiment, the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 13% (L).
  • the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 14% (L). In another embodiment, the new 6020 extruded product may realize the above strength values in combination with an elongation of at least 15% (L).
  • a new extruded 6020 aluminum alloy product realizes at least one of (a) 17 vol. % cube (ED) texture and (b) a maximum ODF [001] intensity of at least 3.6, as measured per the EBSD Sample Procedure, below.
  • a new extruded 6020 aluminum alloy product realizes at least 18 vol. % cube (ED) texture, or at least 19 vol. % cube (ED) texture, or at least 20 vol. % cube (ED) texture, or at least 21 vol. % cube (ED) texture, at least 22 vol. % cube (ED) texture, or at least 23 vol. % cube (ED) texture, at least 24 vol.
  • a new 6020 extruded aluminum alloy product realizes a maximum ODF [001] intensity of at least 3.8, or at least 4.0, or at least 4.2, or at least 4.4, or at least 4.6, or at least 4.8, or at least 5.0, or at least 5.2, or at least 5.4, or at least 5.6, or at least 5.8, or at least 6.0, or at least 6.2, or at least 6.4, or at least 6.6, or at least 6.8, or at least 7.0.
  • the new 6xxx aluminum alloy is a new 6262A extruded product i.e., made by the inventive methods and/or systems described herein.
  • the new 6262A extruded product may realize at least 5% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6262A product.
  • a new 6262A extruded product may realize at least 10% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6262A product of the same product form, size and temper.
  • a new 6262A extruded product may realize at least 15% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6262A product of the same product form, size and temper. In yet another embodiment, a new 6262A extruded product may realize at least 20% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6262A product of the same product form, size and temper.
  • a new 6262A extruded product realizes a tensile yield strength (typical) (L) of at least 37 ksi, or at least 38 ksi, or at least 39 ksi, or at least 40 ksi, or at least 41 ksi, or at least 42 ksi, or at least 43 ksi, or at least 44 ksi, or at least 45 ksi, or at least 46 ksi, or at least 47 ksi, or at least 48 ksi, or at least 49 ksi, or at least 50 ksi, or at least 51 ksi, or at least 52 ksi, or at least 53 ksi, or at least 54 ksi.
  • L tensile yield strength
  • the new 6262A extruded product may realize the above strength values in combination with an elongation (longitudinal or L) of at least 5%. In another embodiment, the new 6262A extruded product may realize the above strength values in combination with an elongation of at least 6% (L). In yet another embodiment, the new 6262A extruded product may realize the above strength values in combination with an elongation of at least 7% (L). In another embodiment, the new 6262A extruded product may realize the above strength values in combination with an elongation of at least 8% (L).
  • a new extruded 6262A aluminum alloy product realizes at least one of (a) 18 vol. % cube (ED) texture and (b) a maximum ODF [001] intensity of at least 3.9, as measured per the EBSD Sample Procedure, below.
  • a new extruded 6262A aluminum alloy product realizes at least 19 vol. % cube (ED) texture, or at least 20 vol. % cube (ED) texture, or at least 21 vol. % cube (ED) texture, at least 22 vol. % cube (ED) texture, or at least 23 vol. % cube (ED) texture, at least 24 vol. % cube (ED) texture, or at least 25 vol.
  • a new extruded 6262A aluminum alloy product realizes a maximum ODF [001] intensity of at least 3.8, or at least 4.0, or at least 4.2, or at least 4.4, or at least 4.6, or at least 4.8, or at least 5.0, or at least 5.2, or at least 5.4, or at least 5.6, or at least 5.8, or at least 6.0, or at least 6.2, or at least 6.4, or at least 6.6, or at least 6.8, or at least 7.0.
  • the new 6xxx aluminum alloy is a new 6061 extruded product i.e., made by the inventive methods and/or systems described herein.
  • the new 6061 extruded product may realize at least 5% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6061 product.
  • a new 6061 extruded product may realize at least 10% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6061 product of the same product form, size and temper.
  • a new 6061 extruded product may realize at least 15% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6061 product of the same product form, size and temper. In yet another embodiment, a new 6061 extruded product may realize at least 20% higher tensile yield strength (typical) and/or ultimate tensile strength (typical) than a conventionally press-quenched 6061 product of the same product form, size and temper.
  • a new extruded 6061 product realizes a tensile yield strength (typical) (L) of at least 22 ksi, or at least 24 ksi, or at least 26 ksi, or at least 28 ksi, or at least 30 ksi, or at least 32 ksi, or at least 34 ksi, or at least 36 ksi, or at least 38 ksi, or at least 40 ksi, or at least 42 ksi, or at least 44 ksi, or at least 46 ksi, or at least 47 ksi, or at least 48 ksi, or at least 49 ksi, or at least 50 ksi, or at least 51 ksi, or at least 52 ksi.
  • L tensile yield strength
  • the new 6061 extruded product may realize the above strength values in combination with an elongation (longitudinal or L) of at least 8%. In another embodiment, the new 6061 extruded product may realize the above strength values in combination with an elongation of at least 10% (L). In yet another embodiment, the new 6061 extruded product may realize the above strength values in combination with an elongation of at least 12% (L). In another embodiment, the new 6061 extruded product may realize the above strength values in combination with an elongation of at least 14% (L).
  • a new extruded 6061 aluminum alloy product realizes at least one of (a) 5 vol. % cube (ED) texture and (b) a maximum ODF [001] intensity of at least 2.0, as measured per the EBSD Sample Procedure, below.
  • a new extruded 6061 aluminum alloy product realizes at least 6 vol. % cube (ED) texture, or at least 7 vol. % cube (ED) texture, or at least 8 vol. % cube (ED) texture, at least 9 vol. % cube (ED) texture, or at least 10 vol. % cube (ED) texture, at least 11 vol. % cube (ED) texture, or at least 12 vol. % cube (ED) texture, at least 13 vol.
  • % cube (ED) texture or at least 14 vol. % cube (ED) texture, or at least 15 vol. % cube (ED) texture, at least 16 vol. % cube (ED) texture, or at least 17 vol. % cube (ED) texture.
  • a new extruded 6061 aluminum alloy product realizes a maximum ODF [001] intensity of at least 2.5, or at least 3.0, or at least 3.5, or at least 4.0, or at least 4.5, or at least 5.0, or at least 5.5, or at least 6.0, or at least 6.5, or at least 7.0, or at least 7.5, or at least 8.0, or at least 8.5, or at least 9.0, or at least 9.5, or at least 10.0, or at least 10.2, or at least 10.4, or at least 10.6, or at least 10.8.
  • the new 6xxx extruded aluminum alloy products described herein may be used in a variety of product applications, such as rods, bars and profiles. Such products may be used make transmission valves (e.g., for free-machining 6xxx aluminum alloys having Sn, Bi, and/or Pb). Automotive structural components may also be produced. The extrusions may also be used as electrical connectors and in general industrial applications.
  • Hot working such as by hot extruding means working the aluminum alloy product at elevated temperature, and generally at least 250° F. Strain-hardening is restricted/avoided during hot working, which generally differentiates hot working from cold working.
  • Cold working such as by cold drawing means working the aluminum alloy product at temperatures that are not considered hot working temperatures, generally below about 250° F. (e.g., at ambient).
  • Temper definitions are per ANSI H35.1 (2009), entitled “American National Standard Alloy and Temper Designation Systems for Aluminum,” published by The Aluminum Association.
  • the term “or” is an inclusive “or” operator and is equivalent to the term “and/or,” unless the context clearly dictates otherwise.
  • the term “based on” is not exclusive and allows for being based on additional factors not described, unless the context clearly dictates otherwise.
  • the meaning of “a,” “an,” and “the” include plural references, unless the context clearly dictates otherwise.
  • the meaning of “in” includes “in” and “on”, unless the context clearly dictates otherwise.
  • FIG. 1 is a block diagram illustrating one embodiment of a method ( 100 ) for producing extruded 6xxx aluminum alloy products.
  • FIG. 2 is a block diagram illustrating one embodiment of system ( 200 ) for producing extruded 6xxx aluminum alloy products relative to the methods of FIG. 1 .
  • FIG. 3 a is a flowchart illustrating one method for producing extruded 6xxx aluminum alloy products in the T6 or T9 temper.
  • FIG. 3 b is a flowchart illustrating one method for producing extruded 6xxx aluminum alloy products in the T8 temper.
  • FIG. 4 is a top-down schematic view of one embodiment of portions of a system for producing extruded 6xxx aluminum alloy products relative to the methods of FIG. 1 .
  • FIG. 5 a illustrates micrographs of a conventionally press-quenched 6026LF product.
  • FIG. 5 b illustrates micrographs of a new 6026LF product made by the inventive systems and methods described herein.
  • FIG. 6 a is a micrograph of a 6026LF product made with a conventional process employing a separate post-extrusion solution heat treatment.
  • FIG. 6 b is a micrograph of a new 6026LF product made by the inventive systems and methods described herein.
  • FIGS. 7 a - 7 b are graphs showing properties of a 6026LF product made by the inventive systems and methods described herein.
  • FIG. 8 a illustrates micrographs of a new 6020 product made by the inventive systems and methods described herein.
  • FIG. 9 a is a micrograph of a new 6020 product (50 micrometer scale) made by the inventive systems and methods described herein.
  • FIG. 9 b is a micrograph of a 6020 product (50 micrometer scale) made with a conventional press-quench process.
  • FIGS. 9 c - 9 d illustrate additional micrographs (200 micrometer scale) of a new 6020 product made by the inventive systems and methods described herein.
  • FIGS. 10 a - 10 b are graphs showing properties of a 6020 product made by the inventive systems and methods described herein.
  • FIGS. 11 a - 11 b illustrate micrographs of a new 6262A product made by the inventive systems and methods described herein.
  • FIGS. 12 a - 12 b are graphs showing properties of a 6262A product made by the inventive systems and methods described herein.
  • FIG. 13 a is a photograph showing machining chips of a 6262A product made with a conventional process employing a separate post-extrusion solution heat treatment.
  • FIG. 13 b is a photograph showing machining chips of a 6262A product made by the inventive systems and methods described herein.
  • FIGS. 14 a - 14 b are graphs showing properties of a 6061 product made by the inventive systems and methods described herein.
  • a conventional 6026LF (lead free) aluminum alloy was produced by two different methods. The basic steps of the two methods are shown in Table 1, below.
  • Method 1 Method 2 (Conventional) (Inventive) Cast Billet Cast Billet Homogenize Billet Homogenize Billet Cool to Ambient Cool to Ambient Preheat to 775-800° F. Preheat above the solvus temperature Hold at preheat temperature Hold at preheat temperature for 3 to 5 minutes for ⁇ 50 minutes Reduce the temperature and Move to extrusion press within move to extrusion press 90 seconds (e.g., to achieve (high heat losses) a heat loss of ⁇ 10° F.) Extrude billet into rod Extrude billet into rod Discharge rod to ambient air Discharge rod to exit shroud (e.g., to maintain the rod above its solvus temperature) Move rod from ambient Move rod from heating shroud to air to water bath water sprays and then water bath Temper to T6, T8 or T9 Temper to T6, T8 or T9 The systems used to conduct the second, inventive method are consistent with those illustrated in FIGS. 2 and 4 .
  • FIG. 5 a illustrates the microstructure of the 6026LF-T9 alloys processed via Method 1, i.e., a conventional press-quench.
  • FIG. 5 b illustrates the microstructure of the 6026LF-T9 alloys processed via Method 2, i.e., the inventive method.
  • Method 1 results in the 6026LF product having large recrystallized grains near the surface.
  • Method 2 produces fine fibrous unrecrystallized grains, uniform in the cross-section direction.
  • the microstructure of Method 2 results in a uniform distribution of fine and small constituent particles, consistent with that of a conventionally processed rod that has a completely separate furnace solution heat treatment after extrusion ( FIG. 6 a ).
  • FIG. 7 a illustrates the strength properties achieved by 0.5625 inch extruded 6026LF-T9 rod extruded produced according to Method 2.
  • FIG. 7 b illustrates the elongation properties achieved by these same rods. As shown, the strength and elongation of the extruded rod significantly exceed the ASTM requirements for the 6026LF alloy. The measured property values are also shown in Table 2. (All values are relative to the longitudinal direction.)
  • FIG. 8 a shows the microstructure of a 6020 alloy that has been prepared using the methods consistent with those illustrated in FIGS. 1 and 3 b (T8 temper) and using systems consistent with those illustrated in FIGS. 2 and 4 .
  • the grains of the extruded 6020 alloy are fibrous and uniform in the cross section direction.
  • FIG. 9 a illustrates a micrograph of a 6020 alloy product made by the inventive methods and systems described herein.
  • FIG. 9 b is a micrograph of a 6020 alloy product made by a conventional press-quench process.
  • the new 6020 product has fewer large tin-bearing constituent particles and the tin-bearing constituent particles are spheroidized. Finer and better distributed tin-bearing phases contribute to improved machinability for the 6xxx free machining alloys.
  • the new 6020 product realizes small constituent particles are that are uniformly distributed. Such particle sizes and particle size distribution is consistent with that of a conventionally processed rod that has a completely separate furnace solution heat treatment after extrusion.
  • FIGS. 10 a - 10 b The mechanical properties of the 6020 alloy in rod form (1.16 inch under 20%, 25% and 30% draw) produced by the inventive methods and systems in the T8 temper are shown in FIGS. 10 a - 10 b . As shown, the strength and elongation values significantly exceed the 6020-T8 ASTM minimums. The measured property values are also shown in Table 3, below. (All values are relative to the longitudinal direction.)
  • Alloy 6262A was also made by the inventive methods and systems (e.g., consistent with FIGS. 1 and 3 a (T9 temper) and FIGS. 2 and 4 ). Again, as shown in FIGS. 11 a - 11 b , the new 6262A products contain small constituent particles and the particle size distribution is uniform, which is consistent with that of a conventionally processed rod that has a completely separate furnace solution heat treatment after extrusion.
  • the mechanical properties of the 6262A alloy in rod form (0.5626 inch rod) produced by the inventive methods and systems in the T9 temper are shown in FIGS. 12 a - 12 b . As shown, the strength and elongation values significantly exceed the 6262A-T9 ASTM minimums. The measured property values are also shown in Table 4, below. (All values are relative to the longitudinal direction.)
  • the machinability of the 6262A rods produced by the inventive methods and systems is also significantly improved.
  • 6262A-T9 products made using a conventional post-extrusion solution heat treatment typically exhibit a large amount of extra-long chips.
  • the new 6262A-T9 products manufactured using the inventive methods and systems described herein exhibit finer chips, which shows superior machinability.
  • Alloy 6061 was also made by the inventive methods and systems (e.g., consistent with FIGS. 1 - 2 a (T6 temper) and FIGS. 3 - 4 ).
  • the mechanical properties of the 6061 alloy in rod form (1.50 inch rod) produced by the inventive methods and systems in the T6 temper are shown in FIGS. 14 a - 14 b .
  • the strength and elongation values again significantly exceed the 6061-T6 ASTM minimums.
  • the measured property values are also shown in Table 5, below. (All values are relative to the longitudinal direction.)
  • Microstructure data for the alloys was obtained per the EBSD sample procedure shown below. Table 6 provides some illustrative properties of the alloys. The reported maximum ODF texture intensities are in the [001] plane, through the cross section. The cube texture and grain size values are in the transverse direction.
  • the alloys produced by the invention process realize a much higher maximum texture intensity over the conventional press quenched alloys and even the solution heat treated alloys.
  • the alloys produced by the invention process realize more cube ED (extrusion direction) texture as compared to the conventional press quenched alloys and even the solution heat treated alloys.
  • the new 6020 extruded alloy includes 9 vol. % more cube ED texture than the conventionally extruded and press-quenched 6020 alloy (26 vol. % versus 17 vol. %).
  • Textured aluminum alloys have grains whose axes are not randomly distributed. Since the images can vary based on various factors, measured texture intensities are generally normalized by calculating the amount of background intensity, or random intensity, and comparing that background intensity to the intensity of the textures of the image. Thus, the relative intensities of the obtained texture measurements are dimensionless quantities that can be compared to one another to determine the relative amount of the different textures within a polycrystalline material. For example, an OIM analysis may determine a background (random) intensity and use orientation distribution functions (ODFs) to produce ODF intensity values. These ODF intensity values may be representative of the amount of texture within a given aluminum alloy (or other polycrystalline material).
  • ODFs orientation distribution functions
  • ODF intensities are measured according to the EBSD sample procedure (described below), or a substantially similar OIM procedure (x-ray diffraction is not used), where a series of ODF plots containing intensity (times random) representations may be created.
  • the new 6xxx aluminum alloy products generally have a high maximum ODF intensity, indicating a high amount of texture. It is believed that the high amount of texture in the new 6xxx aluminum alloy products may contribute to their improved properties.
  • the new extruded 6xxx aluminum alloy product realizes a maximum ODF intensity that is at least about 10% higher than a conventionally extruded and press-quenched 6xxx aluminum alloy product of comparable product form, composition and temper. For instance, if a conventionally extruded and press-quenched 6026 alloy realized a maximum ODF intensity of 4.0, then a new 6026 aluminum alloy product made by the new processing disclosed herein may realize a maximum ODF intensity of at least 4.4 (10% higher than the 4.0).
  • the new extruded 6xxx aluminum alloy product may realize a maximum ODF intensity that is at least about 20% higher, or at least about 40% higher, or at least about 40% higher, or at least about 60% higher, or at least about 80% higher, or at least about 100% higher, or at least about 120% higher, or at least about 140% higher, or at least about 160% higher, or at least about 180% higher, or at least about 200% higher, or at least about 220% higher, or at least about 240% higher, or at least about 260% higher, or at least about 300% higher, or at least about 340% higher, or at least about 360% higher, or at least about 380% higher, or at least about 400%, or at least about 420% higher, or at least about 440% higher, or at least about 460% higher, or at least about 480% higher, or at least about 500% higher, or more, than a conventionally extruded and press-quenched 6xxx aluminum alloy product of comparable product form, composition and temper.
  • the new extruded 6xxx aluminum alloy product realizes at least 1 vol. % more cube ED texture that than a conventionally extruded and press-quenched 6xxx aluminum alloy product of comparable product form, composition and temper. For instance, if a conventionally extruded and press-quenched 6026 alloy realized 15 vol. % cube ED texture, then a new 6026 aluminum alloy product made by the new processing disclosed herein may realize 16 vol. % cube ED texture (1 vol. % more than 15 vol. %). In other embodiments, the new extruded 6xxx aluminum alloy product may realize at least 2 vol. % more, or at least 3 vol. % more, or at least 4 vol. % more, or at least 5 vol.
  • vol. % more or at least 6 vol. % more, or at least 7 vol. % more, or at least 8 vol. % more, or at least 9 vol. % more, or at least 10 vol. % more, or at least 11 vol. % more, or at least 12 vol. % more, or at least 13 vol. % more than a conventionally extruded and press-quenched 6xxx aluminum alloy product of comparable product form, composition and temper.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Extrusion Of Metal (AREA)
US18/135,553 2020-10-30 2023-04-17 6xxx aluminum alloys Pending US20230256491A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US18/135,553 US20230256491A1 (en) 2020-10-30 2023-04-17 6xxx aluminum alloys

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US202063108077P 2020-10-30 2020-10-30
PCT/US2021/057580 WO2022094406A1 (en) 2020-10-30 2021-11-01 Improved 6xxx aluminum alloys
US18/135,553 US20230256491A1 (en) 2020-10-30 2023-04-17 6xxx aluminum alloys

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2021/057580 Continuation WO2022094406A1 (en) 2020-10-30 2021-11-01 Improved 6xxx aluminum alloys

Publications (1)

Publication Number Publication Date
US20230256491A1 true US20230256491A1 (en) 2023-08-17

Family

ID=81383308

Family Applications (1)

Application Number Title Priority Date Filing Date
US18/135,553 Pending US20230256491A1 (en) 2020-10-30 2023-04-17 6xxx aluminum alloys

Country Status (8)

Country Link
US (1) US20230256491A1 (zh)
EP (1) EP4237591A1 (zh)
JP (1) JP2023548476A (zh)
KR (1) KR20230098208A (zh)
CN (1) CN116391054A (zh)
CA (1) CA3194579A1 (zh)
MX (1) MX2023004983A (zh)
WO (1) WO2022094406A1 (zh)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2024086068A1 (en) * 2022-10-20 2024-04-25 Arconic Technologies, Llc New 6xxx aluminum alloys

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5776269A (en) * 1995-08-24 1998-07-07 Kaiser Aluminum & Chemical Corporation Lead-free 6000 series aluminum alloy
SI20122A (sl) * 1998-12-22 2000-06-30 Impol, Industrija Metalnih Polizdelkov, D.D. Aluminijeva avtomatna zlitina, postopki za njeno izdelavo in uporabo
US7422645B2 (en) 2005-09-02 2008-09-09 Alcoa, Inc. Method of press quenching aluminum alloy 6020
US9194028B2 (en) * 2010-09-08 2015-11-24 Alcoa Inc. 2xxx aluminum alloys, and methods for producing the same
ES2738948T3 (es) * 2013-12-11 2020-01-27 Constellium Valais Sa Ag Ltd Proceso de fabricación para obtener productos extruidos de alta resistencia obtenidos a partir de aleaciones de aluminio 6xxx
US10513766B2 (en) * 2015-12-18 2019-12-24 Novelis Inc. High strength 6XXX aluminum alloys and methods of making the same

Also Published As

Publication number Publication date
KR20230098208A (ko) 2023-07-03
CA3194579A1 (en) 2022-05-05
CN116391054A (zh) 2023-07-04
EP4237591A1 (en) 2023-09-06
MX2023004983A (es) 2023-05-12
WO2022094406A1 (en) 2022-05-05
JP2023548476A (ja) 2023-11-17

Similar Documents

Publication Publication Date Title
CN108774696B (zh) 一种6系铝合金超薄圆管挤压型材生产工艺
JP6785772B2 (ja) 表面ローピングが低減されたまたは全くない高度に成形可能な自動車用アルミニウムシート及びその製造方法
US11697866B2 (en) Manufacturing process for obtaining high strength extruded products made from 6xxx aluminium alloys
CN102549185B (zh) 弯曲破碎性和耐腐蚀性优异的铝合金挤压材
JP3705320B2 (ja) 耐食性に優れる高強度熱処理型７０００系アルミニウム合金
EP3842561B1 (en) Method of manufacturing an aluminium alloy rolled product
CN111989415B (zh) 用于具有优异的碰撞性能和高屈服强度的挤压件的6xxx铝合金及其制备方法
US20230256491A1 (en) 6xxx aluminum alloys
WO2016204043A1 (ja) 高強度アルミニウム合金熱間鍛造材
CN113302327A (zh) 7xxx系列铝合金产品
US20180363113A1 (en) High-strength aluminum alloy plate
CN111004950A (zh) 2000铝合金型材及其制造方法
US5194102A (en) Method for increasing the strength of aluminum alloy products through warm working
JP2017133097A (ja) 機械部品およびその製造方法、押出材
JP3843363B2 (ja) 高強度で耐食性に優れる熱処理型７０００系アルミニウム合金及びその製造方法
WO2018088351A1 (ja) アルミニウム合金押出材
JP7352583B2 (ja) 高い強度および高い電気伝導率を有するアルミニウムストリップの製造方法
JP2001181771A (ja) 高強度耐熱アルミニウム合金材
WO2017126413A1 (ja) 機械部品およびその製造方法、押出材
JP7538775B2 (ja) 銅合金
CN112593114B (zh) 一种高性能Cu-Cr-Zr-Mg-Si合金板带制备方法
Hirsch Annealing of Aluminum and Its Alloys
JPH1060567A (ja) 成形性、焼き付け硬化性及び耐食性に優れるアルミニウム合金板及びその製造方法
WO2022196381A1 (ja) 高強度アルミニウム合金押出材およびその製造方法
KR100560252B1 (ko) 고온 피로 강도가 우수한 알루미늄 합금 단조재

Legal Events

Date Code Title Description
AS Assignment

Owner name: ARCONIC TECHNOLOGIES LLC, PENNSYLVANIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:RUAN, YIMIN;MASKELL, JOHN S.;MURPHY, BRYAN K.;AND OTHERS;REEL/FRAME:063347/0311

Effective date: 20201103

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

AS Assignment

Owner name: JPMORGAN CHASE BANK, N.A., NEW YORK

Free format text: NOTICE OF GRANT OF SECURITY INTEREST (ABL) IN INTELLECTUAL PROPERTY;ASSIGNOR:ARCONIC TECHNOLOGIES LLC;REEL/FRAME:064641/0798

Effective date: 20230818

Owner name: U.S. BANK TRUST COMPANY, NATIONAL ASSOCIATION, NEW YORK

Free format text: NOTICE OF GRANT OF SECURITY INTEREST IN INTELLECTUAL PROPERTY (FIRST LIEN);ASSIGNOR:ARCONIC TECHNOLOGIES LLC;REEL/FRAME:064641/0781

Effective date: 20230818