US20220310994A1 - Selectively permeable nanostructured materials - Google Patents

Selectively permeable nanostructured materials Download PDF

Info

Publication number
US20220310994A1
US20220310994A1 US17/619,480 US202017619480A US2022310994A1 US 20220310994 A1 US20220310994 A1 US 20220310994A1 US 202017619480 A US202017619480 A US 202017619480A US 2022310994 A1 US2022310994 A1 US 2022310994A1
Authority
US
United States
Prior art keywords
contained
certain embodiments
liquid phase
volume
poly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US17/619,480
Other languages
English (en)
Inventor
Stephen Burkhardt
Christopher A. Simoneau
Larry Beck
Jay J. Farmer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Conamix Inc
Original Assignee
Conamix Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Conamix Inc filed Critical Conamix Inc
Priority to US17/619,480 priority Critical patent/US20220310994A1/en
Assigned to CONAMIX INC. reassignment CONAMIX INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SIMONEAU, CHRISTOPHER A., BURKHARDT, STEPHEN, FARMER, JAY J., BECK, LARRY
Publication of US20220310994A1 publication Critical patent/US20220310994A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/139—Processes of manufacture
    • H01M4/1397—Processes of manufacture of electrodes based on inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B17/00—Sulfur; Compounds thereof
    • C01B17/02—Preparation of sulfur; Purification
    • C01B17/0243—Other after-treatment of sulfur
    • C01B17/0248—Other after-treatment of sulfur of particulate sulfur
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B17/00—Sulfur; Compounds thereof
    • C01B17/02—Preparation of sulfur; Purification
    • C01B17/0253—Preparation of sulfur; Purification from non-gaseous sulfur compounds other than sulfides or materials containing such sulfides
    • C01B17/0259—Preparation of sulfur; Purification from non-gaseous sulfur compounds other than sulfides or materials containing such sulfides by reduction of sulfates
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/362—Composites
    • H01M4/366—Composites as layered products
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/38—Selection of substances as active materials, active masses, active liquids of elements or alloys
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/38—Selection of substances as active materials, active masses, active liquids of elements or alloys
    • H01M4/381—Alkaline or alkaline earth metals elements
    • H01M4/382—Lithium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/38—Selection of substances as active materials, active masses, active liquids of elements or alloys
    • H01M4/386—Silicon or alloys based on silicon
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
    • H01M4/581—Chalcogenides or intercalation compounds thereof
    • H01M4/5815—Sulfides
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
    • H01M4/621—Binders
    • H01M4/622—Binders being polymers
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
    • H01M4/624—Electric conductive fillers
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/40—Electric properties
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/026—Electrodes composed of, or comprising, active material characterised by the polarity
    • H01M2004/027—Negative electrodes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/026—Electrodes composed of, or comprising, active material characterised by the polarity
    • H01M2004/028—Positive electrodes
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries

Definitions

  • This application relates to nanostructured materials having selective permeability; such nanostructured materials have utility in the manufacture of electrode compositions for secondary batteries and other energy storage devices.
  • a major objective in the commercial development of next generation rechargeable batteries is to provide batteries with higher energy densities than state of the art lithium ion batteries.
  • One of the most promising approaches to this goal is use of a sulfur cathode coupled with a lithium metal anode. Sulfur is inexpensive, abundant, and offers a theoretical charge capacity that is an order of magnitude higher than conventional metal oxide-based intercalation cathodes used in current lithium ion cells. Similarly, anodes based on metallic lithium have much higher energy density than the lithium graphite anodes used in current lithium ion cells.
  • ethereal electrolytes such as dimethoxyethane (DME) and 1,3-dioxolane (DOL) are widely used in place of carbonates in sulfur batteries.
  • DME dimethoxyethane
  • DOL 1,3-dioxolane
  • SEIs solid electrolyte interfaces
  • the present invention encompasses the recognition that engineered materials having selective permeability can be applied to solve problems in sulfur batteries including preventing polysulfide shuttling and addressing the challenges of combining electrolytes and additives optimized for sulfur in cells with lithium metal anodes.
  • the invention provides nanostructured materials for sulfur cathode construction characterized in that the materials comprise structures that are selectively permeable to one or more components of a liquid phase with which the nanostructured material is in contact.
  • the structure having selective permeability has differential permeability based on the size, charge, or polarity of a molecule (or any combination of these features).
  • such structures comprise nanofiltration membranes, or compositions with nanofiltration properties.
  • provided nanostructured materials are characterized in that they contain or encapsulate an interior volume that is physically isolated from a volume outside of the nanostructure (e.g. an enclosed volume).
  • the present invention provides a nanostructured material comprising a contained volume that is physically separated from a volume outside of the nanostructure, wherein the contained volume encloses a contained electroactive substance and a contained liquid phase in contact with the contained electroactive substance.
  • provided nanostructured materials comprise a contained volume that is physically separated from a volume outside of the nanostructure by a permeable membrane, wherein the contained volume encloses an electroactive substance and a contained liquid phase in contact with the electroactive substance.
  • provided nanostructured materials comprise a contained volume that is physically separated from a volume outside of the nanostructure by a selectively permeable membrane, wherein the contained volume encloses an electroactive substance and a contained liquid phase in contact with the electroactive substance.
  • the nanostructured material comprises a core shell nanoparticle having a shell with selective permeability.
  • core shell particles are characterized in that the shell encloses a volume in which an electroactive sulfur substance is in contact with a contained liquid electrolyte composition.
  • a contained electrolyte composition comprises a mixture of substances to which the shell has different degrees of permeability.
  • the shell is impermeable to one or more components of the contained liquid electrolyte, thereby preventing their flow out of the contained volume within the core shell particle.
  • the shell is highly permeable to one or more components of the contained liquid electrolyte and such components may flow in and out of the core shell particle.
  • the invention encompasses a composition comprising such electrolyte-containing core shell nanoparticles characterized in that an electrolyte composition outside of the shell has a different composition than the electrolyte contained within the shell.
  • the shell is impermeable to one or more components of the electrolyte outside of the shell, thereby preventing their flow into the interior volume of the core shell particle.
  • the present invention provides methods of forming nanostructured materials with selective permeability to one or more components of a liquid phase with which the nanostructured material is in contact.
  • provided methods comprise the steps of providing a sulfur-based electroactive material, and coating or encapsulating the sulfur-based electroactive material with a selectively-permeable polymer.
  • such methods comprise the step of contacting the sulfur-based electroactive material with a monomer (or a mixture of monomers) under conditions that cause the deposition of a selectively-permeable polymer on a surface of the sulfur-based electroactive material.
  • such methods comprise the step of contacting the sulfur-based electroactive material with a monomer (or mixture of monomers) under conditions that cause the deposition of a polymer layer on the surface of the sulfur-based electroactive material and further treating the polymer to modify its permeability properties.
  • the step of further treating the polymer to enhance its selective permeability comprises cross-linking the polymer.
  • the present invention provides nanostructured materials having an interior liquid phase contained within an interior volume by a selectively-permeable structure (“a contained liquid phase”) wherein the contained liquid phase comprises one or more components to which the selectively permeable structure is substantially impermeable.
  • a contained liquid phase a selectively-permeable structure
  • the present invention provides methods of forming nanostructured materials wherein an interior liquid phase is separated from an exterior liquid phase by a selectively-permeable structure, wherein the contained liquid phase and the exterior liquid phase have different compositions.
  • such methods comprise the steps of: placing a nanostructured material having an interior volume in contact with a first liquid phase under conditions that cause the first liquid phase to enter the interior volume of the nanostructured material and then treating the nanostructured material under conditions that modify the permeability of one or more materials composing the nanostructured material such that its permeability to at least one component of the contained liquid phase is decreased.
  • the component of the first liquid phase to which the permeability of the nanostructured material is decreased is then substantially unable to diffuse out of the interior volume of the structured nanomaterial (e.g. it is trapped in the interior volume of the nanostructured material).
  • the nanostructured material thus formed is contacted with a second liquid phase having a composition different from the first liquid phase contained within the interior volume of the nanostructured material.
  • one or more components of the second liquid phase enter the interior volume of the nanostructured material thereby changing its composition.
  • the present invention provides a system comprising a nanostructured material in contact with a first liquid phase, the nanostructured material comprising a contained volume that encloses a contained electroactive substance and a contained liquid phase in contact with the electroactive substance, wherein the contained liquid phase is physically separated from the first liquid phase by a selectively permeable membrane and wherein at least one of the first liquid phase and the contained liquid phase comprises substances to which the selectively permeable structure is substantially impermeable.
  • provided methods comprise the steps of providing a sulfur-based electroactive material, and coating or encapsulating the sulfur-based electroactive material with a selectively-permeable polymer. In certain embodiments such methods comprise the step of contacting the sulfur-based electroactive material with a monomer (or a mixture of monomers) under conditions that cause the formation of a polymer layer on the sulfur-based electroactive material.
  • the present invention provides methods of forming electrolyte-containing core shell nanoparticles having a contained liquid-phase within an interior volume defined by the shell and characterized in that the shell is permeable to some components of the contained liquid phase and impermeable to other components of the contained liquid phase.
  • Such particles have the property of enabling those components to which the shell is permeable to flow in and out of the core shell particle while retaining those components to which the shell is impermeable within the volume contained by the shell.
  • the components of the contained liquid phase to which the shell is impermeable are additives that are beneficial to sulfur electrochemistry.
  • the present invention provides a method of making a nanostructure comprising the steps of: forming a nanoscale particle of an electroactive substance, coating the nanoscale particle with a permeable encapsulant to contain the electroactive substance, reducing the volume of the contained electroactive substance to create a void space contained within the encapsulant, introducing a liquid phase into the void space, and coating the nanoscale particle with a second encapsulant that is impermeable to one or more of the substances in the liquid phase.
  • the present invention provides a method of making a nanostructure comprising the steps of: forming a nanoscale particle of an electroactive substance, coating the nanoscale particle with a permeable encapsulant to contain the electroactive substance, reducing the volume of the contained electroactive substance to create a void space contained within the encapsulant, introducing a liquid phase into the void space, and modifying the encapsulant to make it less permeable to one or more substances in the liquid phase.
  • the present invention provides a method of making a nanostructure comprising the steps of: forming a hollow structure with a permeable encapsulant, introducing a nanoscale particle of an electroactive substance into the hollow structure, introducing a liquid phase into the void space, and modifying the encapsulant to make it less permeable to one or more substances in the liquid phase.
  • the present invention provides a method of making a nanostructure comprising the steps of: forming a hollow structure with a permeable encapsulant; introducing a liquid phase into the void space comprising a dissolved electroactive substance or precursor to the electroactive substance; treating the nanostructure to solidify the dissolved electroactive substance or precursor to the electroactive substance contained in the hollow structure; and modifying the encapsulant to make it less permeable to one or more substances in the liquid phase.
  • the present invention provides, among other things, compositions that have utility in the construction of cathodes for electrochemical devices.
  • the invention provides a cathode composition comprising the provided nanostructured materials. Because of the unique characteristics of the nanostructured materials, such cathode compositions have properties not previously attainable in prior art cathode compositions.
  • the selectively permeable nanostructured materials are utilized as an electroactive material in a cathode composition of a secondary alkali metal/sulfur battery.
  • cathode compositions are characterized in that they comprise electroactive sulfur in contact with a contained liquid phase that is physically separated from a volume outside of the nanostructured material wherein the contained liquid phase contains one or more components that are substantially absent from a liquid phase with which the bulk cathode is in contact.
  • cathode compositions are characterized in that they comprise electroactive sulfur in contact with a contained liquid phase that is physically separated from a volume outside of the nanostructured material wherein the contained liquid phase is substantially free of one or more components that are present in a liquid phase with which the bulk cathode is in contact.
  • cathode compositions are characterized in that they comprise electroactive sulfur in contact with a contained liquid phase that is physically separated from a volume outside of the nanostructured material wherein the volume outside of the nanostructured material (e.g. the electrolyte with which the bulk cathode is in contact) is occupied by a solid, or a gel.
  • the present invention further provides electrochemical devices.
  • the invention provides a secondary battery comprising a provided cathode composition. Because of the unique characteristics of the nanostructured materials, such batteries have properties not previously attainable.
  • the selectively permeable nanostructured materials are utilized as an electroactive material in the cathode of a secondary sulfur battery.
  • such batteries are characterized in that they comprise electroactive sulfur in contact with a contained liquid phase that contains one or more components that are absent from the electrolyte with which the bulk cathode and the anode are in contact.
  • such batteries are characterized in that they comprise electroactive sulfur in contact with a contained liquid phase that is substantially free of one or more components that are present in the electrolyte with which the bulk cathode and the anode are in contact.
  • cathode compositions are characterized in that they comprise electroactive sulfur in contact with a liquid phase contained within a volume of the nanostructured material while the electrolyte with which the bulk cathode and anode are in contact comprises a solid or gel electrolyte.
  • the term “a” may be understood to mean “at least one.”
  • the term “or” may be understood to mean “and/or.”
  • the terms “comprising” and “including” may be understood to encompass itemized components or steps whether presented by themselves or together with one or more additional components or steps.
  • the term “comprise” and variations of the term, such as “comprising” and “comprises,” are not intended to exclude other additives, components, integers or steps.
  • the term “approximately” or “about” refers to a range of values that fall within 25%, 20%, 19%, 18%, 17%, 16%, 15%, 14%, 13%, 12%, 11%, 10%, 9%, 8%, 7%, 6%, 5%, 4%, 3%, 2%, 1%, or less in either direction (greater than or less than) of the stated reference value unless otherwise stated or otherwise evident from the context (except where such number would exceed 100% of a possible value).
  • Aliphatic As used herein, the term “aliphatic” may be understood to encompass a straight-chain (i.e., unbranched) or branched, substituted or unsubstituted hydrocarbon chain that is completely saturated or that contains one or more units of unsaturation, or a monocyclic hydrocarbon or bicyclic hydrocarbon that is completely saturated or that contains one or more units of unsaturation. Unless otherwise specified, aliphatic groups contain 1-12 aliphatic carbon atoms. In some embodiments, aliphatic groups contain 1-6 aliphatic carbon atoms. In some embodiments, the aliphatic groups contain 1-5 aliphatic carbon atoms. In some embodiments, aliphatic groups contain 1-4 aliphatic carbon atoms.
  • aliphatic groups contain 1-3 aliphatic carbon atoms.
  • Suitable aliphatic groups include, but are not limited to, linear or branched, substituted or unsubstituted alkyl, alkenyl, alkynyl groups, and hybrids thereof.
  • Electroactive Substance refers to a substance that changes its oxidation state, or partakes in a formation or breaking of chemical bonds, in a charge-transfer step of an electrochemical reaction.
  • Nanoparticle, Nanostructure, Nanomaterial As used herein, these terms may be used interchangeably to denote a particle of nanoscale dimensions or a material having nanoscale structures.
  • the nanoparticles can have essentially any shape or configuration, such as a tube, a wire, a laminate, sheets, lattices, a box, a core and shell, or combinations thereof.
  • Polymer generally refers to a substance that has a molecular structure consisting chiefly or entirely of repeated sub-units bonded together, such as synthetic organic materials used as plastics and resins.
  • substantially refers to the qualitative condition of exhibiting total or near-total extent or degree of a characteristic or property of interest.
  • FIG. 1 is a pictorial representation of a nanostructured material in accordance with one or more embodiments of the invention.
  • FIG. 2 is another pictorial representation of a nanostructured material in accordance with one or more embodiments of the invention.
  • FIG. 3 is a cross-sectional representation of a nanoparticle in accordance with one or more embodiments of the invention at two different states of electrochemical charge.
  • FIG. 4 is a cross-sectional representation of a nanoparticle in accordance with one or more embodiments of the invention at three different states of electrochemical charge.
  • FIG. 5 is a pictorial representation and flow chart showing a method of fabricating a nanostructured material according to one or more embodiments of the invention.
  • FIG. 6 a is a pictorial representation and flow chart showing an alternate method of fabricating a nanostructured material according to one or more embodiments of the invention.
  • FIG. 6 b is a pictorial representation and flow chart showing an alternate method of fabricating a nanostructured material according to one or more embodiments of the invention.
  • FIG. 7 is a pictorial representation and flow chart showing another alternate method of fabricating a nanostructured material according to one or more embodiments of the invention.
  • FIG. 8 is a pictorial representation of a cross section of an electrochemical cell according to one or more embodiments of the invention.
  • FIG. 9 is a pictorial representation of a cylindrical battery embodying concepts of the invention.
  • the present disclosure is directed to novel nanostructured materials for use in energy storage devices and related methods for fabricating and using such materials.
  • provided nanostructured materials comprise yolk-shell structures. In some such embodiments, a liquid is contained in the void space of the yolk-shell structure. In certain embodiments, provided nanostructured materials comprise structures that are permeable. In some such embodiments, flow of solvent, salts, and additives across the permeable structure is afforded through changes in hydrostatic pressure, temperature, potential, and concentration gradient.
  • provided nanostructured materials comprise structures that are selectively permeable.
  • the selectively permeable structure allows exchange of certain solvents, salts, and additives.
  • the selective permeability characteristics of the provided nanostructured materials provide a means to improve the performance of electrochemical devices and, in particular, alkali metal sulfur batteries (e.g. lithium/sulfur or sodium/sulfur batteries) by enabling different liquid phase compositions to be present at different points in a battery (e.g. at the anode and cathode of the battery).
  • alkali metal sulfur batteries e.g. lithium/sulfur or sodium/sulfur batteries
  • Such materials can enable independent optimization of solvents, salts and additives at the cathode and anode of an electrochemical cell while maintaining ionic and electronic conduction between them.
  • the invention provides compositions comprising nanostructured materials that encompass a contained volume that is isolated from the volume outside of the nanostructured material by a permeable structure (e.g., a membrane).
  • a permeable structure e.g., a membrane
  • a permeable structure comprises: an inner surface in contact with the contained volume, an outer surface in contact with a volume outside of the nanostructured material, wherein the exchange of liquids and/or solutes across the permeable structure is modulated through changes in conditions including hydrostatic pressure, temperature, potential, and concentration gradient.
  • the invention provides compositions comprising nanostructured materials that encompass a contained volume that is isolated from the volume outside of the nanostructured material by a selectively permeable structure.
  • the selectively permeable structure comprises: an inner surface in contact with the contained volume, an outer surface in contact with a volume outside of the nanostructured material, and a thickness comprising a composition that has differential permeability to different liquids and/or solutes based on their molecular characteristics.
  • the nanostructured material comprises a contained a liquid phase situated within the contained volume and in contact with the inner surface of the selectively permeable structure.
  • Molecules to which the selectively permeable structure is highly permeable thereby have the ability to exchange between the contained liquid phase and a liquid phase that is external to the nanostructured material, while molecules to which the selectively permeable structure has little or no permeability will be substantially unable to exchange between the contained and external liquid phases.
  • Nanostructured materials of the present invention are not limited to any specific morphology.
  • the inventive nanostructures have a morphology that defines a contained interior volume that is physically isolated from the space outside of the nanostructured material.
  • the interior volume of the nanostructure is separated from an exterior space by a permeable structure.
  • the interior volume of the nanostructure is separated from an exterior space by a selectively permeable structure.
  • Nanostructured materials having such characteristics may take various morphological forms and the invention places no particular limitations on the morphology of the nanostructured materials.
  • Non-limiting examples of nanostructured materials that may be fashioned with an interior volume separated from the exterior volume include: core shell particles, nanowires, nanostructured porous materials, closed-cell nanoporous foams, encapsulated nanocomposites, and related structures.
  • provided nanostructures comprise core-shell nanoparticles.
  • Such nanoparticles comprise a substantially continuous shell that contains an internal volume and separates that volume from the space outside of the shell.
  • core shell particles are substantially spherical, though other geometries are also possible including: oblong or ovoid shapes, cylinders, prismatic shapes, irregular shapes, and polyhedral shapes.
  • the optimal shape of nanoparticles may vary for different applications—while the descriptions and examples below concentrate on spherical core shell nanoparticles as a way of demonstrating the broader principles of the invention, it is to be understood that these principles apply to nanostructured materials with other morphologies and that such alternatives are contemplated within the scope of certain embodiments of the invention.
  • Control of nanoparticle morphology is well understood in the art (e.g. using techniques such as templating, surfactant control, mechanical processing, and the like) and it is therefore within the ability of the skilled person to adapt the concepts described herein with respect to spherical core shell particles to other nanostructured materials.
  • the optimal dimensions of the nanostructures may vary to suit a particular application.
  • the nanostructure is a nanoparticle (e.g. a material comprising discrete nanoscale particles).
  • such nanoparticles have at least one dimension in the range of about 10 to about 1000 nm.
  • the nanostructured material does not comprise nanoscale particles per se but has nanoscale features, as for example in nanoporous or mesoporous solids which may be present as larger particles, monoliths, or composites which may be formed with nanoscale features or constituents.
  • the provided nanostructures comprise substantially spherical nanoparticles with a diameter in the range of about 10 to about 5000 nm.
  • the diameter of such spherical particles is, on average, less than about 100 nm—for example, provided nanoparticles may have diameters of 10 to 40 nm; 25 to 50 nm; or 50 to 100 nm.
  • provided nanoparticles comprise spherical particles with a diameter less than about 500 nm—for example, provided nanoparticles may have diameters of 75 to 150 nm; 100 to 200 nm; 150 to 300 nm; 200 to 500 nm; or 300 to 500 nm.
  • provided nanoparticles comprise spherical particles with a diameter less than about 1000 nm—for example, provided nanoparticles may have diameters of 200 to 600 nm; 500 to 800 nm; 600 to 800 nm; or 750 to 1000 nm. In certain embodiments, provided nanoparticles comprise spherical particles with a diameter between about 300 and 800 nm. In certain embodiments, provided nanoparticles comprise spherical particles with a diameter less than about 2000 nm—for example, provided nanoparticles may have diameters of 1000 to 1200 nm; 1000 to 1500 nm; 1300 to 1800; or 1500 to 2000 nm.
  • provided nanoparticles comprise spherical particles with a diameter less than about 5000 nm—for example, provided nanoparticles may have diameters of 1000 to 2000 nm; 2000 to 3000 nm; 2500 to 3500 nm; 2000 to 4000 nm; or 3000 to 5000 nm.
  • the provided nanoparticles comprise cylindrical particles with a cross-sectional diameter in the range of about 10 to about 1000 nm.
  • the cross-sectional diameter of such nanoparticles is less than about 100 nm—for example, provided cylindrical particles may have diameters of 10 to 40 nm; 25 to 50 nm; or 50 to 100 nm.
  • the provided cylindrical particles have a cross-sectional diameter less than about 500 nm—for example, provided cylindrical particles may have diameters of 75 to 150 nm; 100 to 200 nm; 150 to 300 nm; 200 to 500 nm; or 300 to 500 nm.
  • the provided nanoparticles comprise cylinders with a cross-sectional diameter less than about 1000 nm—for example, provided nanoparticles may have diameters of 200 to 600 nm; 500 to 800 nm; 600 to 800 nm; or 750 to 1000 nm.
  • the provided nanoparticles comprise cylindrical particles with a diameter between about 100 and 400 nm.
  • provided cylindrical particles have lengths greater than 1 ⁇ m.
  • provided cylindrical nanoparticles have lengths greater than 5 ⁇ m, greater than 10 ⁇ m, greater than 20 ⁇ m, or greater than 50 ⁇ m.
  • provided cylindrical nanoparticles have lengths of about 1 ⁇ m to about 1 cm.
  • provided cylindrical nanoparticles have lengths of about 5 ⁇ m to about 1 cm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 10 ⁇ m to about 1 cm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 20 ⁇ m to about 1 cm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 50 ⁇ m to about 1 cm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 1 ⁇ m to about 1 mm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 5 ⁇ m to about 1 mm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 10 ⁇ m to about 1 mm.
  • provided cylindrical nanoparticles have lengths of about 20 ⁇ m to about 1 mm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 50 ⁇ m to about 1 mm. In certain embodiments, provided cylindrical nanoparticles have lengths of about 1 ⁇ m to about 100 ⁇ m. In certain embodiments, provided cylindrical nanoparticles have lengths of about 5 ⁇ m to about 100 ⁇ m. In certain embodiments, provided cylindrical nanoparticles have lengths of about 10 ⁇ m to about 100 ⁇ m. In certain embodiments, provided cylindrical nanoparticles have lengths of about 20 ⁇ m to about 100 ⁇ m. In certain embodiments, provided cylindrical nanoparticles have lengths of about 50 ⁇ m to about 100 ⁇ m. In certain embodiments, provided nanoparticles have an aspect ratio greater than 3, greater than 5, greater than 10, greater than 20. In certain embodiments, provided nanoparticles have an aspect ratio greater than 50, greater than 100, greater than 200, greater than 500, or greater than 1000.
  • the provided nanoparticles comprise a structure which separates an internal volume contained within the nanoparticle from a volume outside the nanoparticle (e.g. a shell or wall)
  • a structure which separates an internal volume contained within the nanoparticle from a volume outside the nanoparticle (e.g. a shell or wall)
  • such a structure may have a thickness of between about 0.5 and about 100 nm.
  • the optimal thickness of such a structure will vary depending on the material from which it is made, the dimensions of the nanostructure of which it is a part, and/or the specific application for which the nanoparticle is being engineered.
  • provided nanoparticles have a shell or wall thickness less than about 15 nm—for example, having a thickness in the range of about 1 to about 2 nm; about 2 to about 5 nm; about 5 to about 7 nm; about 5 to about 10 nm; or about 10 to about 15 nm. In certain embodiments, provided nanoparticles have a shell or wall thickness less than about 25 nm. In certain embodiments, provided nanoparticles have a shell or wall thickness less than about 50 nm—for example, having a thickness in the range of about 5 to about 15 nm; about 10 to about 20 nm; about 15 to about 30 nm; about 25 to about 40 nm; or about 30 to about 50 nm.
  • provided nanoparticles have a shell or wall thickness less than about 75 nm. In certain embodiments, provided nanoparticles have a shell or wall thickness less than about 100 nm—for example, having a thickness in the range of about 50 to about 60 nm; about 50 to about 75 nm; about 60 to about 80 nm; or about 75 to about 100 nm.
  • the shape of the enclosed volume may therefore be dictated by the morphology of the nanostructured material.
  • the enclosed volume may comprise a single chamber, or it may comprise a plurality of smaller spaces that are isolated from each other or that have varying degrees of interconnectedness.
  • certain nanostructured materials of the present invention are characterized in that they enclose a contained volume that is separated from a volume outside the nanostructured material by a permeable structure.
  • the structure with permeability comprises a membrane separating the contained volume from the external volume and for convenience, the permeable structure may be referred to simply as a “permeable membrane” herein.
  • Permeability refers to the property of allowing the movement of molecules across a structure (or membrane).
  • the exchange of liquids and/or solutes across the permeable membrane is controlled through changes in conditions including hydrostatic pressure, temperature, potential, and concentration gradient.
  • liquids and/or solutes will exchange across a permeable membrane from areas of high concentration to low concentration.
  • liquids and/or solutes will exchange across a permeable membrane from areas of high hydrostatic pressure to areas of low hydrostatic pressure.
  • provided nanostructured materials comprise permeable membranes that are nanoporous.
  • permeable structures have pore sizes less than 5 nm; for example, less than 4 nm, less than 3 nm, less than 2 nm, or less than 1.5 nm.
  • permeable structures have pore sizes less than 1 nm; for example, less than 0.9 nm, less than 0.8 nm, less than 0.7 nm, or less than 0.6 nm.
  • permeable structures have pore sizes less than 0.5 nm; for example, less than 0.4 nm, less than 0.3 nm, less than 0.25 nm, less than 0.2 nm, less than 0.15 or less than 0.10 nm. In certain embodiments, permeable structures have pore sizes between about 1 and about 5 nm. In certain embodiments, permeable structures have pore sizes between about 1 and about 2 nm. In certain embodiments, permeable structures have pore sizes between about 0.5 and about 1.5 nm. In certain embodiments, permeable structures have pore sizes between about 0.1 and about 1 nm. In certain embodiments, permeable structures have pore sizes between about 0.5 and about 1 nm. In certain embodiments, permeable structures have pore sizes between about 0.1 and about 0.5 nm. In certain embodiments, permeable structures have pore sizes between about 0.1 and about 0.5 nm. In certain embodiments, the pore size is measured by microscopy (e.g. TEM
  • a permeable structure comprises a polymer.
  • a permeable structure comprises an inorganic solid.
  • a permeable structure comprises a composite of a polymer and an inorganic solid.
  • a permeable structure comprises a polymer composition wherein the polymer is selected from the group consisting of polyolefins, polyesters, polyamides, polyimides, polyheterocycles, and polyketones.
  • a permeable structure comprises a polymer composition wherein the polymer is selected from the group consisting of: polyethylene, polypropylene, polytetrafluoroethylene (PTFE), polyvinylidene difluoride (PVDF), polysulfone, polyethersulfone, polyacrylonitrile, polyamide, polyimide, polyamideimide, polyetherimide, cellulose acetate, polyaniline, polypyrrole, polyetheretherketone (PEEK), polybenzimidazole, and composites or mixtures thereof.
  • a permeable structure comprising such polymers can be made by any technique known in the art, including in situ polymerization, solution coating, sintering, stretching, track etching, template leaching, interfacial poly
  • a permeable structure comprises an inorganic material such as, for example, a ceramic, a metal oxide, a metal sulfide, or a clay.
  • a permeable structure comprises an inorganic material selected from the group consisting of: silicon carbide, silicon oxide, iron oxide, manganese oxide, titanium disulfide, molybdenum disulfide, zirconium oxide, titanium oxide, and zeolites.
  • a permeable structure comprises a polymer with dispersed organic or inorganic matrices in the form of nano-sized powdered solids present at amounts up to 20 wt % of a polymer membrane.
  • Carbon matrices can be prepared by pyrolysis of any suitable material as described in U.S. Pat. No. 6,585,802. Zeolites as described in U.S. Pat. No. 6,755,900 may also be used as an inorganic matrix.
  • matrices are particles less than about 50 nanometers diameter, for example less than about 40 nm, less than about 25 nm, less than about 20 nm, less than about 10 nm, less than about 5 nm, less than about 2 nm, or less than 1 nm in diameter.
  • a permeable structure comprises a plurality of polymer layers. In certain embodiments, a permeable structure comprises two polymer layers. In certain embodiments, a permeable structure comprises three polymer layers.
  • permeable structures of the present invention comprise electronically conductive polymers.
  • permeable structures of the present invention comprise polymers selected from the group consisting of: polyaniline, polydopamine, polypyrrole, polyselenophene, polythiophene, polynaphthalene, polyphenylene sulfide, and derivatives, mixtures or copolymers of any of these.
  • permeable structures of the present invention comprise polymers selected from the group consisting of: polypyrrole (PPy), polythiophene (PTh), polydopamine, poly(3,4-ethylenedioxythiophene) (PEDOT), poly(3,4-propylenedioxythiophene) (ProDOT), poly(3,4-ethylenedioxypyrrole) (PEDOP), poly(3,4-propylenedioxypyrrole) (ProDOP), poly(3,4-ethylenedithiopyrrole) (PEDTP), poly(3,4-ethyleneoxyhiathiophene) (PEOTT), poly(3,4-ethylenedioxyselenophene) (PEDOSe), and derivatives, mixtures or copolymers of any of these.
  • permeable structures of the present invention comprise polymers selected from the group consisting of: polyaniline (PAni), poly(o-methylaniline) (POTO), poly(o-methoxyaniline) (POAS), poly(2,5-dimethylaniline) (PDMA), poly(2,5-dimethoxyaniline) (PDOA), sulfonated polyaniline (SPAN), poly(l-aminonaphthalene) (PNA), poly(5-aminonaphthalene-2-sulfonic acid) polyphenylene sulfide, and derivatives, mixtures or copolymers of any of these.
  • PAni polyaniline
  • POTO poly(o-methylaniline)
  • POAS poly(o-methoxyaniline)
  • PDMA poly(2,5-dimethylaniline)
  • PDOA poly(2,5-dimethoxyaniline)
  • SPAN sulfonated polyaniline
  • PNA poly(l-aminonaphthalene
  • certain nanostructured materials of the present invention are characterized in that they enclose a contained volume that is separated from a volume outside the nanostructured material by a selectively permeable structure.
  • the structure with selective permeability comprises a membrane separating the contained volume from the external volume and for convenience, the selectively permeable structure may be referred to simply as a “selectively permeable membrane” herein.
  • Selective permeability refers to the property of preferentially allowing or preventing permeation of molecules based on differences in their properties.
  • the selectively permeable structures have selectivity based on molecular size, polarity, charge, or combinations of these features.
  • selectively permeable structures are size selective—e.g. the structure selectively retains or permeates molecules based on differences in their molecular weights or molecular volumes.
  • selectively permeable structures have selectivity based on the charges of molecules—e.g. the structure selectively retains or permeates molecules based on differences in their overall charges or their charge-to-mass or charge-to-size ratios.
  • a selectively permeable structure is characterized in that it selectively retains or permeates molecules based on their sizes.
  • the permeability of a selectively permeable structure is defined by its molecular weight cutoff (MWCO) value.
  • the MWCO is expressed in Daltons (Da) and is defined as the lowest molecular weight at which at least 90% of a component in a mixture in contact with the structure will be prevented from permeating through the structure.
  • the MWCO of the selectively permeable structure in the provided nanostructured materials can be measured directly in the nanostructured material or indirectly inferred by reference to the MWCO values published for the material from which the selectively permeable structure is composed (i.e. published values).
  • the permeability is measured, this may be done experimentally, for example by performing experiments immersing the nanostructured material in a liquid containing test components with various specific molecular weights and measuring the ability of the components to diffuse into the contained liquid phase enclosed by the nanostructured material. Such measurements can also be performed on samples of the selectively permeable composition that are not incorporated into the nanostructured material—for example, by testing the MWCO of a film of the material from which the selectively permeable structure in the provided nanostructured material is composed.
  • provided nanostructured materials comprise selectively permeable structures characterized in that they have a MWCO less than 1000 Da.
  • selectively permeable structures are characterized in that they have a MWCO less than 800 Da, less than 600 Da, less than 500 Da, less than 400 Da, less than 300 Da, or less than 200 Da.
  • selectively permeable structures are characterized in that they have a MWCO around 150 Da.
  • selectively permeable structures are characterized in that they have a MWCO around 200 Da.
  • selectively permeable structures are characterized in that they have a MWCO around 250 Da.
  • selectively permeable structures are characterized in that they have a MWCO around 300 Da. In certain embodiments, selectively permeable structures are characterized in that they have a MWCO between about 150 and about 250 Da. In certain embodiments, selectively permeable structures are characterized in that they have a MWCO between about 200 and about 300 Da. In certain embodiments, selectively permeable structures are characterized in that they have a MWCO between about 300 and about 400 Da. In certain embodiments, selectively permeable structures are characterized in that they have a MWCO between about 250 and about 500 Da. In certain embodiments, the MWCO refers to a value determined in a liquid composition corresponding to an electrolyte to which the nanostructured material will be exposed in its intended application in an electrochemical device.
  • a selectively permeable structure is a porous membrane.
  • the selective permeability properties of the structure are determined by the physical dimensions of pores in the membrane.
  • the porosity and related characteristics such as the pore size and pore size distribution of the selectively permeable membrane can be determined by performing measurements on the nanostructured material (e.g. by scanning electron microscopy (SEM), by tunneling electron microscopy (TEM), or atomic force microscopy (AFM)).
  • measurements can be utilized to measure the porosity and pore characteristics of the selectively permeable structures. Measurements can be performed directly on the nanostructured material or, if this is not feasible, can be performed on samples of the selectively permeable composition that are not incorporated into the nanostructured material—for example by measuring the porosity of films of the material composing the selectively permeable structure in the provided nanostructured material. The porosity of the structure can also be inferred from published values for the porosity of the same material in other contexts.
  • provided nanostructured materials comprising selectively permeable membranes are nanoporous.
  • the selectively permeable structures have pore sizes less than 5 nm; for example, less than 4 nm, less than 3 nm, less than 2 nm, or less than 1.5 nm.
  • the selectively permeable structures have pore sizes less than 1 nm; for example, less than 0.9 nm, less than 0.8 nm, less than 0.7 nm, or less than 0.6 nm.
  • the selectively permeable structures have pore sizes less than 0.5 nm; for example, less than 0.4 nm, less than 0.3 nm, less than 0.25 nm, less than 0.2 nm, less than 0.15 or less than 0.10 nm. In certain embodiments, the selectively permeable structures have pore sizes between about 1 and about 5 nm. In certain embodiments, the selectively permeable structures have pore sizes between about 1 and about 2 nm. In certain embodiments, the selectively permeable structures have pore sizes between about 0.5 and about 1.5 nm. In certain embodiments, the selectively permeable structures have pore sizes between about 0.1 and about 1 nm.
  • the selectively permeable structures have pore sizes between about 0.5 and about 1 nm. In certain embodiments, the selectively permeable structures have pore sizes between about 0.1 and about 0.5 nm. In certain embodiments, the pore size is measured by microscopy (e.g. TEM, SEM, or AFM).
  • the material is characterized in that it has a narrow distribution of pore sizes.
  • provided nanostructured materials comprise selectively permeable membranes wherein at least 80% of the pores have a diameter within +/ ⁇ 20% of the mean pore diameter.
  • provided nanostructured materials comprise selectively permeable membranes wherein at least 90% of the pores have a diameter within +/ ⁇ 20% of the mean pore diameter.
  • provided nanostructured materials comprise selectively permeable membranes wherein at least 90% of the pores have a diameter within +/ ⁇ 15% of the mean pore diameter.
  • provided nanostructured materials comprise selectively permeable membranes wherein at least 90% of the pores have a diameter within +/ ⁇ 10% of the mean pore diameter.
  • the pore size distribution is measured by microscopy (e.g. TEM, SEM, or AFM).
  • the selectively permeable structures have selectivity based on the charges of molecules—e.g. the structure selectively retains or permeates molecules based on differences in their overall charges, their charge-to-mass ratios, or their charge-to-size ratios.
  • the provided structures permeate lithium cations.
  • the selectively permeable structure has high permeability to cations, but low permeability to anions.
  • the selectively permeable structure has high permeability to lithium ions and mono-anions, but low permeability to di-anions.
  • the selectively permeable structure has high permeability to lithium ions, but low permeability to di-anions.
  • the present invention places no particular restriction on the composition of the selectively permeable structures described above.
  • Particularly useful aspects of the compositions include suitable permeability characteristics as described above as well as physical and chemical compatibility with the electrolytes, active species, additives and solutes that will be encountered in the electrochemical devices to which the nanostructured materials are to be applied.
  • the selectively permeable structure comprises a polymer.
  • the selectively permeable structure comprises an inorganic solid.
  • the selectively permeable structure comprises a composite of a polymer and an inorganic solid.
  • the selectively permeable structure comprises a polymer composition with nanofiltration properties wherein the polymer is selected from the group consisting of: polyethylene, polypropylene, polytetrafluoroethylene (PTFE), polyvinylidene difluoride (PVDF), polysulfone, polyethersulfone, polyacrylonitrile, polyamide, polyimide, polyamideimide, polyetherimide, cellulose acetate, polyaniline, polypyrrole, polyetheretherketone (PEEK), polybenzimidazole, and composites or mixtures thereof.
  • the selectively permeable structure comprising such polymers can be made by any technique known in the art, including in situ polymerization, solution coating, sintering, stretching, track etching, template leaching, interfacial polymerization, or phase inversion.
  • the selectively permeable structure may comprise polymers that are crosslinked or treated so as to improve their stability.
  • a selectively permeable structure may comprise membranes described in GB2437519, the contents of which are incorporated herein by reference.
  • the selectively permeable structure comprises a composite material having a macroporous support layer and a non-porous or nanoporous selectively permeable layer.
  • the thin, non-porous, selectively permeable layer may, for example, be formed from or comprise a material chosen from modified polysiloxane based elastomers including polydimethylsiloxane (PDMS) based elastomers, ethylene-propylene diene (EPDM) based elastomers, polynorbornene based elastomers, polyoctenamer based elastomers, polyurethane based elastomers, butadiene and nitrile butadiene rubber based elastomers, natural rubber, butyl rubber based elastomers, polychloroprene (Neoprene) based elastomers, epichlorohydrin elastomers, polyacrylate elastomers, poly(
  • the selectively permeable structure comprises an inorganic material such as, for example, a metal oxide, metal sulfide, ceramic or clay.
  • the selectively permeable structure comprises an inorganic material selected from: silicon carbide, silicon oxide, iron oxide, manganese oxide, titanium disulfide, molybdenum disulfide, zirconium oxide, titanium oxide, and zeolites.
  • the selectively permeable structure comprises a polymer with dispersed organic or inorganic matrices in the form of nano-sized powdered solids.
  • dispersed materials are present at amounts up to 20 wt % of the polymer membrane.
  • Carbon matrices can be prepared by pyrolysis of any suitable material as described in U.S. Pat. No. 6,585,802. Zeolites as described in U.S. Pat. No. 6,755,900 may also be used as an inorganic matrix.
  • the matrices will be particles less than about 50 nanometers diameter, for example, less than about 40 nm, less than about 25 nm, less than about 20 nm, less than about 10 nm, less than about 5 nm, less than about 2 nm, or less than 1 nm in diameter.
  • the selectively permeable structure comprises a plurality of polymer layers. In certain embodiments, the selectively permeable structure comprises two polymer layers. In certain embodiments, the selectively permeable structure comprises three polymer layers. In certain embodiments, the selectively permeable structure comprises more than three polymer layers.
  • the selectively permeable structure comprises a polymer-based membrane of the phase inversion type (e.g. produced from polyimide dope solutions) or a coated type (e.g. coated with rubber compounds such as silicone and derivatives) or thin-film composite type (e.g. with a separating layer generated via interfacial polymerization).
  • a polymer-based membrane of the phase inversion type e.g. produced from polyimide dope solutions
  • a coated type e.g. coated with rubber compounds such as silicone and derivatives
  • thin-film composite type e.g. with a separating layer generated via interfacial polymerization
  • selectively permeable structures of the present invention comprise polyimide membranes.
  • selectively permeable structures of the present invention comprise P84 (CAS No. 9046-51-9) and P84HT (CAS No. 134119-41-8) and/or blends thereof and/or blends comprising one or both of said polyimides.
  • the polyimide membranes are crosslinked according to GB2437519.
  • selectively permeable structures of the present invention comprise crosslinked or non-crosslinked, coated polyimide membranes, especially made of P84 and/P84HT and/or mixtures thereof, wherein the coating comprises silicone acrylates. Particular preferred silicone acrylates to coat the membranes are described in U.S. Pat. Nos. 6,368,382, 5,733,663, JP 62-136212, JP 59-225705, DE 102009047351 and EP 1741481 A1.
  • selectively permeable structures of the present invention comprise electronically conductive polymers.
  • selectively permeable structures of the present invention comprise polymers selected from the group consisting of: polyaniline, polypyrrole, polythiophene, polyphenylene sulfide, and derivatives, mixtures or copolymers of any of these.
  • selectively permeable structures of the present invention comprise polymers selected from the group consisting of: polypyrrole (PPy), polythiophene (PTh), polydopamine, poly(3,4-ethylenedioxythiophene) (PEDOT), poly(3,4-propylenedioxythiophene) (ProDOT), poly(3,4-ethylenedioxypyrrole) (PEDOP), poly(3,4-propylenedioxypyrrole) (ProDOP), poly(3,4-ethylenedithiopyrrole) (PEDTP), poly(3,4-ethyleneoxyhiathiophene) (PEOTT), poly(3,4-ethylenedioxyselenophene) (PEDOSe) and derivatives, mixtures or copolymers of any of these.
  • selectively permeable structures of the present invention comprise polymers selected from the group consisting of: polyaniline (PAni), poly(o-methylaniline) (POTO), poly(o-methoxyaniline) (POAS), poly(2,5-dimethylaniline) (PDMA), poly(2,5-dimethoxyaniline) (PDOA), sulfonated polyaniline (SPANi), poly(l-aminonaphthalene) (PNA), poly(5-aminonaphthalene-2-sulfonic acid) polyphenylene sulfide, and derivatives, mixtures or copolymers of any of these.
  • selectively permeable structures of the present invention comprise cross-linked conductive polymer compositions.
  • such cross-linked conductive polymer compositions comprise any of the above conductive polymers that have been thermally or chemically crosslinked. In certain embodiments, such crosslinked conductive polymer compositions comprise any of the above conductive polymers crosslinked by vulcanization.
  • selectively permeable structures of the present invention comprise cross-linked polymer membranes that are stable to ethereal solvents.
  • the cross-linked polymer membranes are stable to solvents selected from the group consisting of: dimethoxyethane, glyme, diglyme, triglyme, tetraglyme, higher glymes, polyethers, trimethoxymethane, dimethoxyethane, diethoxyethane, 1,2-dimethoxypropane, ethylene glycol divinylether, diethylene glycol divinylether, triethylene glycol divinylether, dipropylene glycol dimethyl ether, butylene glycol ethers, 1,3-dimethoxypropane, 1,3 dioxolane, 1,4 dioxane, 1,3 dioxane, trioxane, tetrahydrofuran, furan, dihydrofuran, 2-methyltetrahydrofuran, tetrahydropyr
  • the cross-linked polymer membranes are stable to solvents selected from the group consisting of: dimethoxyethane, 1,2-dimethoxypropane, 1,3 dioxolane, 1,4 dioxane, 1,3 dioxane, trioxane, tetrahydrofuran, furan, and mixtures of any two or more of these.
  • the cross-linked membranes are stable to solvents selected from the group consisting of: dimethoxyethane, 1,2-dimethoxypropane, 1,3 dioxolane, and mixtures of these.
  • selectively permeable structures of the present invention comprise cross-linked polymer membranes that are stable to sulfone solvents.
  • the cross-linked membranes are stable to solvents selected from the group consisting of: sulfolane, 3-methyl sulfolane, 3-sulfolene, diethyl sulfone, dimethyl sulfone, methylethyl sulfone, and mixtures of two or more of these.
  • the cross-linked membranes are stable to solvents selected from the group consisting of: sulfolane, 3-methyl sulfolane, and 3-sulfolene, and mixtures of two or more of these.
  • the selectively permeable structures of the present invention comprise cross-linked polymer membranes that are stable to solvents
  • the membrane does not swell by more than 50% when immersed in the solvent.
  • the membrane does not swell by more than 40%, more than 30%, more than 25%, more than 20%, more than 15%, or more than 10% when immersed in the solvent.
  • the permeability or inverse barrier is an important physical property for many industrial applications of polymers.
  • polymers with low, high or tailored (i.e., selective) permeability such as protective coatings or barriers to control the flow of certain substances there through.
  • polymer barriers e.g., polymeric shells
  • the permeability of a substance through the shell can be very different for different polymers and permeants.
  • permeability and solubility of polymers at a given temperature depend on the degree of crystallinity (morphology), the molecular weight, the type of permeant and its concentration or pressure, and in the case of copolymers, also on the composition.
  • the selective permeability of the selectively permeable structure it is possible to control which substances are allowed to enter the interior volume of the nanostructured material, or not, and which substances are allowed to exit the interior volume, or not.
  • the selective permeability of the structure is determined by the presence, size, morphology (e.g., void shapes), and distribution of pores within the polymer, which can be controlled by, for example, acid doping, dedoping and redoping, cross-linking, the introduction of certain additives, or combinations thereof during the polymerization process, or in some cases as part of a post-polymerization process.
  • the selectively permeable structures are characterized in that they have high permeability to the organic solvents comprising an electrolyte in an electrochemical cell in which the nanostructured material is to be utilized. In certain embodiments, the selectively permeable structures are characterized in that they have high permeability to dimethoxyethane (DME) and 1,3-dioxolane (DOL). In certain embodiments, the selectively permeable structures are characterized in that they have high permeability to sulfolane, sulfolene, dimethyl sulfone, or methyl ethyl sulfone. In certain embodiments, the selectively permeable structures are characterized in that they have high permeability to ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, and methylethyl carbonate.
  • the flux of the solvent through the selectively permeable structure is at least 1 ⁇ 10 ⁇ 6 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 . In certain embodiments, the flux of the solvent through the selectively permeable structure is at least 1 ⁇ 10 ⁇ 6 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 . In certain embodiments, the flux of the solvent through the selectively permeable structure is at least 5 ⁇ 10 ⁇ 6 , 1 ⁇ 10 ⁇ 5 , 5 ⁇ 10 ⁇ 5 , 1 ⁇ 10 ⁇ 4 , 5 ⁇ 10 ⁇ 4 , 1 ⁇ 10 ⁇ 3 , or 1 ⁇ 10 ⁇ 2 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 .
  • the flux of the solvent through the selectively permeable structure is between 1 ⁇ 10 ⁇ 6 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 and 100 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 .
  • the selectively permeable structures are characterized in that they have high permeability to the organic solvents, this means that the flux of the solvent through the structure is at least 0.005, at least 0.01, at least 0.05, at least 0.1, at least 0.5, or at least 1 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 (e.g., between 0.005 and 100 l ⁇ m ⁇ 2 ⁇ h ⁇ 1 bar ⁇ 1 ).
  • the solvent flux of a selectively permeable structure may be measured directly on the nanostructured material (for example by subjecting the nanostructured material to the test solvent under a pressure differential and measuring how much of the test solvent enters the contained volume).
  • the flux can be measured for a sample material from which the selectively permeable structure is constructed using methods known in the art.
  • the selectively permeable structures are characterized in that they have high permeability to lithium ions. In certain embodiments, the selectively permeable structures are characterized in that they have a lithium ion conductivity of at least 1 ⁇ 10 ⁇ 6 S cm ⁇ 1 . In certain embodiments, the selectively permeable structures are characterized in that they have a lithium ion conductivity of at least 5 ⁇ 10 ⁇ 6 , at least 1 ⁇ 10, at least 5 ⁇ 10 ⁇ 5 , at least 1 ⁇ 10 ⁇ 4 , or at least 5 ⁇ 10 ⁇ 4 S cm ⁇ 1 (e.g., between 5 ⁇ 10 ⁇ 6 and 5 ⁇ 10 ⁇ 1 S cm ⁇ 1 .
  • the selectively permeable structures are characterized in that they have a lithium ion conductivity of at least 1 mS cm ⁇ 1 . In certain embodiments, the selectively permeable structures are characterized in that they have a lithium ion conductivity of at least 2, at least 5, or at least 10 mS cm ⁇ 1 .
  • the invention encompasses nanostructured materials wherein a volume enclosed within the nanostructure contains a liquid phase (a ‘contained liquid phase’), which is physically separated from the volume outside of the nanostructured material by the selectively permeable structure.
  • a liquid phase a ‘contained liquid phase’
  • the selectively permeable structure comprises a substantially continuous shell of a core shell nanoparticle (e.g. a selectively permeable shell).
  • the selectively permeable shell has an interior surface in contact with a contained liquid phase in the core of the nanoparticle and an exterior surface that is in contact with the volume outside of the nanoparticle.
  • the selectively permeable structure is present in a three dimensional form characterized in that one dimension (i.e. its thickness) is substantially smaller than the other two dimensions, examples of these include sheets, shells, coatings, and the like. In certain embodiments, such compositions are characterized in that they have a smallest dimension (e.g. thickness) less than 50 nm. In certain embodiments, the selectively permeable structure is present in a sheet-like form or a shell having a thickness between about 5 and about 10 nm, between about 5 and about 25 nm, between about 10 and about 40 nm, or between about 25 and about 50 nm.
  • the selectively permeable structure is a shell that has a thickness in the range of about 0.5 nm to about 100 nm.
  • provided nanoparticles have a selectively permeable shell less than about 15 nm thick—for example, having a thickness in the range of about 1 to about 2 nm; about 2 to about 5 nm; about 5 to about 7 nm; about 5 to about 10 nm; or about 10 to about 15 nm.
  • provided nanoparticles have a selectively permeable shell less than about 25 nm thick.
  • provided nanoparticles have a selectively permeable shell less than about 50 nm thick—for example, having a thickness in the range of about 5 to about 15 nm; about 10 to about 20 nm; about 15 to about 30 nm; about 25 to about 40 nm; or about 30 to about 50 nm. In certain embodiments, provided nanoparticles have a selectively permeable shell less than about 75 nm thick. In certain embodiments, provided nanoparticles have a selectively permeable shell less than about 100 nm thick—for example, having a thickness in the range of about 50 to about 60 nm; about 50 to about 75 nm; about 60 to about 80 nm; or about 75 to about 100 nm.
  • the selectively permeable shell is characterized in that it is permeable to at least one constituent of an electrolyte composition of an electrochemical cell in which the nanoparticle will be utilized.
  • the selectively permeable shell is engineered with a surface area and permeability such that it can accommodate the volume expansion of an electroactive species present in the contained volume of the nanostructured material.
  • a shell that is engineered with sufficient surface area and permeability is able to permit electrolyte to permeate out of the contained volume at a rate sufficient to accommodate the increasing volume of the electroactive sulfur as it is converted to lithium sulfide during discharge and thereby avoid damage to the nanostructured material—in the example of sulfur as the electroactive species in a lithium battery, the volume of the contained electroactive species increases to approximately 1.73 ⁇ its original volume meaning a volume of electrolyte corresponding to 73% of the sulfur volume must permeate through the shell during complete discharge of the contained sulfur.
  • the selectively permeable shell has sufficient permeability to allow a volume of solvent equal to at least 50% of the contained volume to permeate through the shell in one hour during discharge of a contained electroactive sulfur composition. In certain embodiments, the selectively permeable shell has sufficient permeability to allow a volume of solvent equal to at least 50% of the contained volume to permeate through the shell in 30 minutes during discharge of a contained electroactive sulfur composition. In certain embodiments, the selectively permeable shell has sufficient permeability to allow a volume of solvent equal to at least 50% of the contained volume to permeate through the shell in 15 minutes, or in 10 minutes during discharge of a contained electroactive sulfur composition.
  • the portions of the structure comprising the selectively permeable structure may consist entirely of a permeable material, or may comprise the permeable material along with additional materials.
  • additional materials may be present in various forms, for example: additional materials can be present as discrete layers contained within or disposed upon the selectively permeable structure (e.g. in a multilayer shell); the additional materials may be present as mixtures intimately mixed or compounded with a semipermeable material; or the additional materials may be present in composites with the semipermeable material.
  • Suitable additional materials that may be present include polymers, elemental carbon, metallic elements or alloys, metal oxides, metal chalcogenides, metal salts, ceramics, glasses, clays, semiconductors, and the like.
  • nanostructured materials of the present invention comprise electroactive substances that are contained within an enclosed volume that is separated from space outside of the nanostructured material by a selectively permeable structure. Such substances undergo electrochemical reactions and provide electrical capacity to devices fabricated from the provided nanostructured materials. These substances are referred to generically herein as ‘contained electroactive materials’.
  • the provided nanostructured materials comprise solid electroactive materials which are contained within the enclosed volume and which are in contact with a contained liquid phase.
  • the contained electroactive material may be a liquid or may be dissolved in a liquid phase.
  • the contained electroactive materials are solids, they may be referred to generically as ‘contained electroactive solids’. Such solids have a composition different from the solid substance(s) composing the structure of the nanostructured materials. No specific limitations are placed on the shape of such contained electroactive solids or their distribution within the enclosed volume.
  • the contained electroactive solid is provided as a particle which is partially or wholly separated from the nanostructured material in which it is contained (i.e. as the yolk in a yolk shell nanoparticle).
  • the contained electroactive substance is in physical contact or is wholly or partially adhered to the nanostructured material.
  • the contained electroactive substance is present as a coating on an interior surface defining the contained volume in the nanostructured material. It is noteworthy that contained electroactive solids may be produced or manufactured with a particular shape or arrangement within the nanostructured material, but that these may change during the operation (e.g. charge or discharge) of an electrochemical device comprising the electroactive material.
  • the size and shape of a contained electroactive solid will also vary to suit a particular application and may have a diameter in the range of about 10 to about 2000 nm.
  • the solid will occupy from about 20% to about 80% of the enclosed volume, with the contained liquid phase and/or other solid materials (e.g. conductive additives, etc.) occupying the remaining volume (e.g., about 80% to about 20%) depending on the charge/discharge status of an electrode or energy storage device containing the nanoparticles.
  • the solid will occupy from about 20% to about 70% of the enclosed volume.
  • the solid will occupy from about 20% to about 60% of the enclosed volume.
  • the solid will occupy from about 20% to about 50% of the enclosed volume.
  • the solid will occupy from about 20% to about 40% of the enclosed volume. In some embodiments, the solid will occupy from about 20% to about 30% of the enclosed volume. In some embodiments, the solid will occupy from about 30% to about 70% of the enclosed volume. In some embodiments, the solid will occupy from about 40% to about 60% of the enclosed volume. In some embodiments, the solid will occupy from about 45% to about 55% of the enclosed volume. In some embodiments, the solid will occupy from about 50% to about 60% of the enclosed volume. In some embodiments, the solid will occupy from about 50% to about 70% of the enclosed volume. In some embodiments, the solid will occupy from about 50% to about 80% of the enclosed volume. In some embodiments, the solid will occupy from about 60% to about 80% of the enclosed volume. In some embodiments, the solid will occupy from about 75% to about 80% of the enclosed volume.
  • the contained electroactive solid is present in a form having at least one dimension with a length in the range of about 5 to about 3,000 nm. In certain embodiments, the contained electroactive solid is present in a form having at least one dimension with a length in the range of about 10 to about 50 nm, about 30 to about 100 nm, about 100 to about 500 nm, or about 500 to about 1000 nm. In certain embodiments, the contained electroactive solid is present in a form having at least one dimension with a length in the range of about 1000 to about 1500 nm, about 1000 to about 2000 nm, about 1500 to about 3000 nm, or about 2000 to about 3000 nm.
  • the contained electroactive material comprises sulfur and the nanostructured materials have utility as cathode materials for sulfur batteries.
  • Such compositions comprise an electroactive sulfur-based material.
  • suitable electroactive sulfur materials include elemental sulfur; sulfur-containing organic molecules, sulfur-containing polymers or composites; or metal sulfides as well as combinations or composites of two or more of these.
  • the electroactive sulfur is present in the form of elemental sulfur.
  • the electroactive sulfur material comprises Ss.
  • the electroactive sulfur is present as a metal sulfide.
  • the metal sulfide comprises an alkali metal sulfide; in certain embodiments, the metal sulfide comprises lithium sulfide.
  • the electroactive sulfur material is present as a composite with another material.
  • Such composites may include materials such as graphite, graphene, other carbon allotropes, metal sulfides or oxides, or conductive polymers.
  • the sulfur may be alloyed with other chalcogenides such as selenium or arsenic.
  • the dimensions and shape of the electroactive sulfur-based material in the cathode composition may be varied to suit a particular application and/or be controlled as a result of the morphology of the nanostructure comprising the electroactive sulfur.
  • the electroactive sulfur-based material is present as a nanoparticle.
  • such electroactive sulfur-based nanoparticles have a spherical or spheroid shape.
  • nanostructured materials of the present invention comprise substantially spherical sulfur-containing particles with a diameter in the range of about 50 to about 1200 nm. In certain embodiments, such particles have a diameter in the range of about 50 to about 250 nm, about 100 to about 500 nm, about 200 to about 600 nm, about 400 to about 800 nm, or about 500 to about 1000 nm.
  • Such nanoparticles may have various morphologies as described above.
  • the electroactive sulfur-based material is present as the core of a core-shell particle, where it is surrounded by a selectively permeable shell.
  • such core-shell particles may comprise yolk-shell particles as described above.
  • nanostructured materials of the present invention comprise electroactive substances that are contained within an enclosed volume that is separated from space outside of the nanostructured material by a selectively permeable structure.
  • the provided nanostructured materials comprise a contained liquid phase that is enclosed within the nanostructured material and separated from the volume outside of the nanostructured material by the selectively permeable structure.
  • the fraction of the enclosed volume that is occupied by the contained liquid phase is controlled to optimize characteristics of the nanostructured material.
  • the contained liquid phase occupies between 5 and 80 percent of the enclosed volume. In certain embodiments, the contained liquid phase occupies less than about 30% of the enclosed volume—for example, between about 5 and about 10%; between about 10 and about 20%; between about 15 and about 25%; between about 20 and about 30%; or between about 25 and about 30%. In certain embodiments, the contained liquid phase occupies less than about 40% of the enclosed volume—for example, between about 25 and about 40%; between about 30 and about 40%; or between about 35 and about 40%.
  • the contained liquid phase occupies less than about 50% of the enclosed volume—for example, between about 25 and about 50%; between about 30 and about 50%; or between about 40 and about 50%. In certain embodiments, the contained liquid phase occupies more than about 10% of the enclosed volume; more than about 15%, more than about 20%, more than about 30%, more than about 40%, or more than about 50% of the enclosed volume. In certain embodiments, the contained liquid phase, the contained electroactive substance(s) and any other contained additives occupy essentially 100% of the contained volume. In certain embodiments, the contained liquid phase, the contained electroactive substance(s) and any other contained additives occupy less than 100% of the contained volume. In certain such embodiments, the balance of the contained space is occupied by a gas or by a vacuum.
  • the liquid phase in the enclosed volume of the provided nanostructured materials contains one or more species to which the selectively permeable structure is substantially impermeable—such species are thereby substantially trapped in the enclosed volume such species are referred to herein as ‘trapped species’.
  • trapped species comprise additives that facilitate the electrochemical conversion of sulfur to lithium sulfide.
  • the provided nanostructured materials are characterized in that they comprise:
  • a contained volume enclosing: a contained liquid phase, a contained electroactive material, and one or more contained additives;
  • the selectively permeable structure is permeable to at least one component of the contained liquid phase, and substantially impermeable to at least one contained additive.
  • the contained electroactive substance in such nanostructured materials changes volume upon undergoing electrochemical conversion and the nanostructured material is characterized in that the enclosed volume is at least 25% larger than the maximum volume occupied by the contained electroactive substance in its most voluminous state.
  • FIG. 1 shows a representative core shell nanoparticle 1 having certain features of the inventive nanostructured materials.
  • the particle 1 comprises a selectively permeable shell 2 surrounding an enclosed volume, which is occupied by a contained liquid phase 4 and a contained electroactive solid 3 .
  • the inset shows that the selectively permeable shell has an outer surface 2 a and an inner surface 2 b . Outer surface 2 a is in contact with a volume 5 outside of the nanoparticle while inner surface 2 b is in contact with the contained liquid phase 4 .
  • FIG. 1 shows a representative core shell nanoparticle 1 having certain features of the inventive nanostructured materials.
  • the particle 1 comprises a selectively permeable shell 2 surrounding an enclosed volume, which is occupied by a contained liquid phase 4 and a contained electroactive solid 3 .
  • the inset shows that the selectively permeable shell has an outer surface 2 a and an inner surface 2 b . Outer surface 2 a is in contact with a volume 5 outside of the nanoparticle while inner surface 2
  • the contained liquid phase 4 contains three species labeled A, B, and C, while the outside volume 5 contains three species A, B, and D.
  • the selectively permeable shell 2 is permeable to species A and B, but not to C or D. This means that species D is excluded from entering the contained liquid phase 4 while species C is prevented from exiting the contained volume 4 and entering the outside volume 5 .
  • FIG. 3 depicts cross sections of a core shell nanoparticle according to the present invention at two different states of charge.
  • the particle 1 a on the left-hand side of FIG. 3 is depicted in a state of charge where the contained electroactive solid 3 a has a first volume. In this state, the enclosed volume contains a large volume of liquid phase 4 a . After electrochemical conversion, the particle is converted to state 1 b where the contained electroactive solid 3 b has increased in volume and the contained liquid phase 4 b has a correspondingly reduced volume.
  • the selectively permeable shell 2 remains substantially unchanged in shape and size, meaning the total volume contained is substantially unchanged.
  • FIG. 4 further illustrates the operation of certain embodiments of the provided inventive nanoparticles.
  • FIG. 4 shows a cross sectional view of a core shell nanoparticle where the contained electroactive substance is elemental sulfur and where the particle is part of an operating lithium sulfur battery.
  • the particle 1 a depicted at left-hand side of the figure is in a charged state and the contained electroactive solid 3 a comprises solid sulfur.
  • lithium ions and electrons enter the particle and convert the sulfur to soluble lithium polysulfides (e.g. Li 2 S x where 2 ⁇ x ⁇ 9) which dissolve in the contained liquid phase 4 a leading to a particle in state 1 i depicted at the center of FIG. 4 .
  • the selectively permeable structure e.g. shell 2
  • the selectively permeable structure allows a sufficient volume of solvent to permeate through the shell to equilibrate the created pressure differential.
  • an important feature of certain nanostructured materials provided by the present invention is that they have a permeability to at least one component of the contained liquid phase sufficient to allow the permeation of a volume of liquid out of the contained liquid phase at a rate sufficient to permit pressure equilibration at a desired discharge rate of a battery incorporating such nanostructures in an electrode.
  • nanostructured materials of the present invention comprise a contained volume that is separated from a volume outside of the nanostructure by a selectively permeable structure wherein the contained volume encloses a contained electroactive substance and a contained liquid electrolyte that is in contact with the contained electroactive substance, and wherein the selectively permeable structure has a sufficient permeability to constituents of the contained liquid electrolyte to permit permeation of a volume fraction of the contained liquid electrolyte that is at least equivalent to a volume increase in the contained electroactive substance as the substance changes its state of charge.
  • such nanostructured materials comprise:
  • V tot a contained volume that is separated from a volume outside of the nanostructured material by the selectively permeable structure
  • V tot a contained electrolyte (contained within V tot ) having a total volume (V e ) and comprising a volume fraction (V p ) of components to which the selectively permeable structure is permeable, and a volume fraction (V imp ) to which the selectively permeable structure is substantially impermeable;
  • V i a contained electroactive substance having a first volume (V i ) at an initial charged state and a second volume (V f ) at a final charged state where V i and V f differ by a volume ⁇ V if .
  • such nanostructured materials are characterized in that V p is greater than or equal to ⁇ V if . In certain such embodiments, V p is at least 25% greater than ⁇ V if . In certain such embodiments, V p is at least 50%, at least 60%, at least 70%, at least 80%, or at least 100% greater than ⁇ V if . In certain such embodiments, V p is at least twice, at least three times, at least four times, or at least five times greater than ⁇ V if .
  • such nanostructured materials are characterized in that the contained volume V tot does not change by more than 10% between the initial and final charged states. In certain embodiments, such nanostructured materials are characterized in that the contained volume V tot does not change by more than 15%, more than 20%, more than 25%, more than 30%, or more than 40% between the initial and final charged states. In certain embodiments, the change in V tot can be determined experimentally by measuring the size of the nanoparticles by microscopy at different states of charge (e.g. in the initial and final charged states).
  • such nanostructured materials are characterized in that a volume fraction of one or more substances comprising V imp relative to V tot does not change by more than 10% between the initial and final charged states. In certain embodiments, such nanostructured materials are characterized in that the volume fraction of one or more substances comprising V imp relative to V tot does not change by more than 15%, more than 20%, more than 25%, more than 30%, or more than 40% between the initial and final charged states.
  • such nanostructured materials are characterized in that the volume fraction V p of one or more permeable substances (i.e., a substance that shows sufficient ability to permeate through a selectively permeable structure as described herein, e.g., via the indirect measurement of permeability described in Example 5) changes by more than 10% between the initial and final charge states.
  • one or more permeable substances i.e., a substance that shows sufficient ability to permeate through a selectively permeable structure as described herein, e.g., via the indirect measurement of permeability described in Example 5
  • such nanostructured materials are characterized in that the volume fraction V p of permeable substances within the contained volume changes by an amount ⁇ V p between the initial and final charge states.
  • ⁇ V p is approximately equal to but opposite from the change in the volume of the electroactive substance ⁇ V if between the initial and final charge states.
  • such nanostructured materials comprise a selectively permeable structure with a permeability sufficient to allow a portion of the substances comprising V p to permeate through the selectively permeable structure to maintain the contained volume within 10% of its initial value throughout the conversion of substantially all of the contained electroactive substance at a rate of at least 0.1 C.
  • such nanostructured materials comprise a selectively permeable structure with a permeability sufficient to allow a portion of the substances comprising V p to permeate through the selectively permeable structure to maintain the contained volume within 15%, within 20%, within 25%, within 30%, or within 40% of its initial value throughout the conversion of substantially all of the contained electroactive substance at a rate of at least 0.1 C.
  • the permeability is sufficient to maintain the contained volume within 10% of its initial value throughout the conversion of substantially all of the contained electroactive substance at a rate of at least 0.2 C, at least 0.5 C, at least 1 C, at least 2 C, or at least 5 C. In certain embodiments, the permeability is sufficient to maintain the contained volume within 15%, within 20%, within 25%, within 30%, or within 40% of its initial value throughout the conversion of substantially all of the contained electroactive substance at a rate of at least 0.2 C, at least 0.5 C, at least 1 C, at least 2 C, or at least 5 C.
  • the selectively permeable structure has a permeability to permeable substances comprising the permeable volume fraction V p of the contained electrolyte of P 1 (L ⁇ m ⁇ 2 ⁇ hr ⁇ 1 ), and an interior surface area A int (m ⁇ 2 ) in contact with the contained liquid phase.
  • the nanostructured material is characterized in that the rate defined by the product P 1 A int is greater than the rate of volume change of the contained electroactive substance during the charge or discharge of the contained electroactive substance when the rate of charge is at least 0.1 C.
  • the rate defined by the product P 1 A int is greater than the rate of volume change of the contained electroactive substance during the charge or discharge of the contained electroactive substance when the rate of charge is at least 0.2 C, at least 0.5 C, at least 1 C, at least 2 C, or at least 5 C.
  • a characteristic of certain nanostructured materials of the present invention is that the composition of the contained liquid phase changes as the state of charge of the contained electroactive solid changes. Referring again to FIGS. 3 and 4 , this means that the concentration of a component of the liquid phase 4 a is higher than the concentration of the same component in state 4 b (or vice versa).
  • the operational characteristics of the nanostructured materials are such that the concentration of components to which the selectively permeable structure has little or no permeability will be increased in state 4 b relative to state 4 a , while components to which the selectively permeable structure is highly permeable may be lower in state 4 b than in state 4 a.
  • the contained liquid phase 4 contains a mixture comprising components to which the selectively permeable structure has little or no permeability and other components to which the selectively permeable structure has high permeability—such particles are characterized in that in a first state of charge the concentration of the impermeable components is lower in a first state and increases to a higher concentration at a second state of charge by virtue of the fact that some portion of the permeable components present in the contained liquid phase in the first charge state will be forced to permeate out of the contained liquid phase (through the selectively permeable structure) as the volume of the contained electroactive substance increases.
  • the concentration of a contained impermeable component increases due to a decrease in the quantity of other components present in the contained liquid phase rather than due to any increase in the amount of the impermeable component within the particle.
  • such particles are characterized in that the concentration of an impermeable component of the contained liquid phase at a first state of charge is less than the concentration of the impermeable component in a second state of charge.
  • the particles are characterized in that in a first state of charge the concentration of the impermeable components is less than 9/10, less than 4 ⁇ 5, less than 3 ⁇ 4, less than 2 ⁇ 3, less than 1 ⁇ 2, less than 1 ⁇ 3, less than 1 ⁇ 4, less than 1 ⁇ 5 or less than 1/10 of the concentration of the impermeable components in a second state of charge.
  • the impermeable component is further characterized in that it is not a component of, or derivative from, the contained electroactive substance.
  • the impermeable component is further characterized in that the amount of the impermeable component in the contained volume does not change appreciably during electrochemical cycling between the first and second states of charge.
  • the impermeable component is other than lithium polysulfide. In certain such embodiments, the impermeable component is other than sulfur.
  • the first state of charge is defined as the state in which the contained electroactive substance is in a substantially charged state.
  • the second state of charge is defined as a state in which the contained electroactive substance is at least 50% discharged.
  • the effectiveness of the provided nanostructured materials can be optimized by carefully selecting the identity and abundances of the materials comprising the contained liquid phases.
  • the following strategies can be employed to optimize the electrochemical capacity and cycle life of the contained electroactive substance(s):
  • the contained liquid phase comprises one or more components to which the selectively permeable structure has high permeability—such components will therefore move between the contained volume and the volume outside of the nanostructured material (e.g. between the contained liquid phase and a bulk electrolyte in an electrochemical cell in which the nanostructured material is utilized). It is therefore desirable that such components be non-detrimental to other components of an electrochemical device in which the nanostructured material is utilized.
  • the contained electroactive substance comprises a sulfur cathode material and the provided nanostructured material is to be utilized in a lithium sulfur battery with a lithium metal anode in contact with the electrolyte
  • the permeable substances to be compatible with lithium metal.
  • suitable permeable substances comprise low molecular weight solvents.
  • the permeable substances are organic solvents typically used as electrolytes in sulfur batteries (e.g. low molecular weight ethers, sulfones, or nitriles).
  • the permeable substances are low molecular weight solvents that have low polarity or little dipole moment.
  • solvents are not typically used as battery electrolytes, because they are not good solvents for lithium salts—nonetheless, such solvents can be utilized in the present system as diluents where the property of being able to readily permeate through the selectively permeable structures within the nanostructured materials provides value by maintaining the internal volume of the nanostructure.
  • Such materials are referred to herein as “permeable diluents”.
  • permeable diluents comprise hydrocarbon or fluorocarbon solvents.
  • the contained liquid phase comprises one or more components to which the selectively permeable structure has little or no permeability—such components will therefore be trapped in the contained volume and unable to enter the volume outside of the nanostructured material (e.g. the bulk electrolyte).
  • such trapped components comprise additives that facilitate the electrochemical conversion between sulfur and lithium sulfide.
  • additives comprise lithium salts, such as LiCF 3 SO 3 , LiClO 4 , LiNO 3 , LiPF 6 , and LiTFSI; ionic liquids, such as 1-ethyl-3-methylimidzaolium-TFSI, N-butyl-N-methyl-piperidinium-TFSI, N-methyl-n-butyl pyrrolidinium-TFSI, and N-methyl-N-propylpiperidinium-TFSI; and superionic conductors, such as sulfides, oxides, and phosphates, for example, phosphorous pentasulfide.
  • lithium salts such as LiCF 3 SO 3 , LiClO 4 , LiNO 3 , LiPF 6 , and LiTFSI
  • ionic liquids such as 1-ethyl-3-methylimidzaolium-TFSI, N-butyl-N-methyl-piperidinium-TFSI, N-methyl-n-butyl
  • such additives comprise organic amines, or other basic organic compounds such as guanidines, amidines, phosphazenes, and related N-containing molecules.
  • such trapped additives have sufficiently high molecular weights to prevent them from readily permeating through the selectively permeable structure.
  • such additives are characterized in that they have molecular weights above about 150 g/mol.
  • such additives are characterized in that they have molecular weights above about 200 g/mol, above about 250 g/mol, above about 400 g/mol, above about 500 g/mol, above about 750 g/mol, or above about 1000 g/mol (e.g., between about 1000 g/mol and 500,000 g/mol).
  • trapped substances comprise solvents to which the selectively permeable structure is substantially impermeable.
  • solvents for example, protic solvents
  • such solvents may facilitate the electrochemical interconversion of sulfur and lithium sulfide, but may be incompatible with lithium metal anodes—such solvents are particularly suitable to deploy as trapped solvents in the provided nanostructured materials.
  • such trapped solvents have sufficiently high molecular weights to prevent them from readily permeating through the selectively permeable structure.
  • such solvents are characterized in that they have molecular weights above about 150 g/mol.
  • such solvents are characterized in that they have molecular weights above about 200 g/mol, above about 250 g/mol, above about 400 g/mol, above about 500 g/mol, above about 750 g/mol, or above about 1000 g/mol.
  • such trapped solvents comprise ethers, diethers, or polyethers.
  • such trapped solvents comprise sulfones, di-sulfones, or polysulfones.
  • such trapped solvents comprise nitriles, dinitriles, or polynitriles.
  • such trapped solvents comprise thioesters, dithioesters, thiocarbonates, dithiocarbonates, or trithiocarbonates. In certain embodiments, such trapped solvents comprise sulfonamides. In certain embodiments, such trapped solvents comprise protic solvents. In certain embodiments, such trapped solvents comprise high molecular weight alcohols, diols, or polyols. In certain embodiments, such trapped solvents comprise high molecular weight amines, diamines, or polyamines. In certain embodiments, such trapped solvents comprise high molecular weight thiols, dithiols, or polythiols.
  • such trapped solvent compositions are characterized in that polysulfides have high solubility therein.
  • such solvent compositions are characterized in that the polysulfide Li 2 S 8 has a solubility of at least 1 M, at least 2 M, at least 3 M, at least 3 M, or at least 4 M at 25° C.
  • such solvent compositions are characterized in that the polysulfide Li 2 S 8 has a solubility between 1 M and 10 M at 25° C.
  • such trapped solvent compositions are characterized in that polysulfides have low solubility therein.
  • such solvent compositions are characterized in that the polysulfide Li 2 S 8 has a solubility less than 1 M, less than 0.5 M, less than 0.2 M, less than 0.1 M, less than 50 mM, or less than 25 mM at 25° C.
  • a liquid phase outside of the nanostructured material comprises one or more components to which the selectively permeable structure has little or no permeability—such components will therefore be excluded from the nanostructured material and unable to enter the contained liquid phase or to contact the contained electroactive substance.
  • such excluded components comprise additives that facilitate the electrochemical conversion of lithium metal or prevent dendrite formation during lithium plating.
  • such excluded components comprise salts that enhance the ionic conductivity of the electrolyte.
  • such excluded components comprise additives that react with polysulfides.
  • such excluded additives have sufficiently high molecular weights to prevent them from readily permeating through the selectively permeable structure.
  • excluded additives are characterized in that they have molecular weights above about 150 g/mol.
  • such excluded additives are characterized in that they have molecular weights above about 200 g/mol, above about 250 g/mol, above about 400 g/mol, above about 500 g/mol, above about 750 g/mol, or above about 1000 g/mol (e.g., between about 1000 g/mol and 500,000 g/mol).
  • excluded substances according to strategy (c) above comprise solvents to which the selectively permeable structure is substantially impermeable.
  • solvents may facilitate the electrochemical consumption and re-plating of lithium metal anodes, but may be incompatible with electroactive sulfur cathode materials— such solvents are particularly suitable to deploy as excluded components in combination with the provided nanostructured materials.
  • such excluded solvents comprise aliphatic carbonates.
  • such excluded solvents comprise dialkyl carbonates.
  • such excluded solvents comprise esters or amides.
  • such excluded solvents comprise ethers.
  • such excluded solvents have sufficiently high molecular weights to prevent them from readily permeating through the selectively permeable structure.
  • excluded solvents are characterized in that they have molecular weights above about 150 g/mol.
  • such excluded solvents are characterized in that they have molecular weights above about 200 g/mol, above about 250 g/mol, above about 400 g/mol, above about 500 g/mol, above about 750 g/mol, or above about 1000 g/mol (e.g., between about 1000 g/mol and 500,000 g/mol).
  • the strategies for selecting solvents and additives to which the selectively permeable structures of the provided nanostructured materials are either permeable or impermeable and of placing such materials either inside of the contained volume or in a liquid outside of the nanostructured material presents valuable options to independently optimize the performance of a battery cathode and anode using materials that were previously not practical due to their incompatibility with the relevant counter-electrode.
  • the invention therefore provides a system for an electrochemical cell comprising the following components:
  • the present invention provides methods of manufacturing the provided nanostructured materials.
  • the art of nanomaterial synthesis and engineering is well advanced and the skilled artisan will be familiar with bountiful literature teaching methods to make nano-sized structures suitable for application in the current invention, including methods for making materials where an electroactive substance is contained within a volume defined by a nanostructure.
  • Nanostructured materials of the present invention may be produced by combining these methods with the specific steps and strategies described herein to control the selective permeability properties of such nanostructures and/or to incorporate into such nanostructured materials a contained liquid phase that is in contact with the electroactive substance and to incorporate within the contained liquid phase trapped substances to which the selectively permeable structure is impermeable.
  • the present invention provides methods to achieve these ends.
  • One approach to producing nanostructured materials comprises the following steps:
  • FIG. 5 illustrates a scheme for such a process where the electroactive substance 12 is provided as a spherical nanoparticle (a).
  • the electroactive substance 12 is then coated with a permeable encapsulant 14 a to provide core-shell nanoparticle (b).
  • the core shell nanoparticle is then treated to remove a portion of the electroactive core 12 (e.g. by dissolution or sublimation through permeable shell 14 a ) to provide nanostructure (c) which contains a smaller electroactive core 12 a and a void space 15 .
  • the void space 15 is then infused with a liquid to provide nanostructure (d) which encompasses contained liquid phase 16 in contact with electroactive core 12 a .
  • the shell 14 a is then modified to convert it into selectively permeable shell 14 b which is substantially impermeable to one or more components of the contained liquid phase 16 .
  • the step of reducing the volume of the contained electroactive core 12 and introducing the contained liquid phase can be combined—for example, in cases where the electroactive substance has some solubility in the introduced liquid 16 , the steps can be accomplished concomitantly by treating particle (b) with an excess of the introduced liquid 16 .
  • FIG. 5 and other figures that follow illustrate spherical core-shell particles
  • electroactive substances having other morphologies (e.g. an electroactive nanowire, nano-scale platelet or the like could be substituted for the nanosphere 12 ) to provide other structured nanomaterials with similar operational characteristics.
  • the step of reducing the volume of the contained electroactive core 12 and introducing the contained liquid phase can be combined—for example, in cases where the electroactive substance has some solubility in the introduced liquid 16 , the steps can be accomplished concomitantly by treating particle (b) with an excess of the introduced liquid 16 .
  • FIG. 6 a shows a method similar to that described in FIG. 5 , except in this case after forming the nanostructured particle (d) rather than modifying the permeability of the encapsulating shell 12 a to change its permeability characteristics, an additional selectively permeable coating 20 is added on top the shell 12 to provide nanostructure (e) having a double layer shell.
  • FIG. 6 b illustrates an alternative method that begins with a pre-formed nanostructure (a) comprising a permeable structure 14 a containing a void space 15 .
  • Electroactive substance 12 a is then introduced into the nanostructure—preferably leaving part of the void space 15 unoccupied as shown in (b).
  • This particle is then treated to introduce liquid phase 16 into the void space as shown at (c).
  • the permeable structure 14 a is then treated to transform it into selectively permeable structure 14 b which is substantially impermeable to at least one component of the contained liquid phase 16 .
  • an additional step analogous to the conversion of (b) to (c) in FIG. 5 or 6 a may be included in this process to reduce the volume of the electroactive substance 12 a prior to introducing liquid phase 16 .
  • the schemes shown in FIGS. 5 and 6 a can incorporate known methods of producing sulfur nanoparticles (e.g. producing sulfur particles from the reaction of thiosulfate or polysulfide and an acid, or by precipitating elemental sulfur colloids from suitable solvent/surfactant systems, or by spray drying or milling sulfur or sulfur precursors).
  • nanoparticles of other electroactive sulfur compounds such as lithium sulfide or sulfur-containing polymers can be utilized as particle 12 .
  • known methods for introducing sulfur into structured nanomaterials can be used (e.g. melt or vapor diffusion of elemental sulfur into void spaces).
  • FIG. 7 demonstrates an alternative method of producing nanostructured materials of the present invention where the electroactive material is introduced as part of a liquid phase.
  • a nanostructured material (a) which includes a void space 18 contained within a permeable shell 17 can be treated to introduce into the void space a liquid phase 19 containing a dissolved electroactive substance (or one or more precursors to an electroactive substance) to provide particle (b).
  • This particle can then be treated to convert permeable shell 17 into selectively permeable shell 17 b which has reduced permeability to more components of the contained liquid phase 19 .
  • the resulting particle (c2) can then be treated to produce a contained electroactive solid 20 which separates from a modified contained liquid phase 19 b (e.g. by precipitation or an induced chemical reaction).
  • the order of the last two steps can be reversed as shown for particle (c1).
  • the solid electroactive substance is formed prior to modifying the permeability of the shell.
  • the liquid phase 19 contains a high concentration of lithium polysulfide (for example, a saturated or near-saturated solution of Li 2 S 8 or other lithium polysulfides or polysulfide mixtures of formula Li 2 S x where 1 ⁇ x ⁇ 9.
  • the solid electroactive substance 20 comprises sulfur and the step of forming the solid electroactive substance 20 comprises electrochemical oxidation of soluble sulfides to sulfur.
  • the solid electroactive substance 20 comprises lithium sulfide (Li 2 S) and the step of forming the solid electroactive substance comprises reduction of soluble lithium polysulfide.
  • the step of reducing the permeability of the selectively permeable structure can be accomplished by any number of means. Examples of such steps include: adding additional materials to the structure to reduce or modify its permeability (e.g. by adding additional layers, or by absorbing or adsorbing additional materials into the structure); chemically modifying one or more materials comprising the structure (e.g. by reducing, or oxidizing the material or by functionalizing the material through reaction with reactive substances); by cross-linking one or more materials comprising the structure (e.g.
  • the step of modifying the permeability of the structure comprises cross-linking the polymer.
  • Polymer cross-linking is a well-developed technology and can be accomplished by many means known to the skilled polymer chemist. The selection of appropriate cross-linking processes depends on the structure of the polymer, the desired degree of cross-linking and the compatibility of the other constituents of the nanostructured material with the processes employed.
  • steps comprise intramolecularly cross-linking a polymer by inducing reaction of functional groups present on the polymer chains. Depending on the polymer, such intramolecular cross-linking can be induced by heat (e.g.
  • steps may comprise cross-linking by reaction with a cross-linking agent—in certain embodiments, such chemical cross-linking may comprise treatment with polyfunctional reactants that can react at multiple sites or multiple times through a single site.
  • any molecule capable of forming two or more covalent bonds to polymer chains present in the precursor to the selectively permeable structure can be employed to modify its permeability.
  • a wide range of di- and polyfunctional cross-linking reagents are known in the art, and the skilled artisan can readily select suitable cross-linking agents for a given polymer based on knowledge of chemical reactivity and literature precedents.
  • Common examples of such poly-functional cross-linking agents include aldehydes, dicarbonyl compounds, sulfur or polysulfur compounds, diacid chlorides, alkyl dihalides, diamines, di-epoxides, polyisocyanates, melamine, and the like.
  • nanostructured compositions of the present invention comprise the polymer polyaniline.
  • such polyaniline compositions are cross-linked to modify their permeability characteristics.
  • Such cross-linking can be accomplished by heating to induce intramolecular cross-linking, or by reaction with a poly-functional cross-linking agent.
  • Suitable cross-linking agents include molecules having reactive functional groups such as aldehydes, ketones, carboxylic acids, and derivatives of these, such as acetals, ketals, esters, acid chlorides, and the like.
  • each carbonyl functional group can condense with two nitrogen atoms in the polyaniline chains thereby creating potential inter-chain cross-links.
  • a carboxylic acid or derivative e.g., ester or acid chloride
  • cross-linking requires use of a di- or polyacid (or related derivative).
  • a similar post-polymerization cross-linking approach comprises reacting polyaniline with di- or poly-electrophiles such as dihalides, or bis-sulfonate esters. Such electrophiles react with polymer nitrogen atoms to form covalent cross-links.
  • di- or poly-electrophiles such as dihalides, or bis-sulfonate esters.
  • electrophiles react with polymer nitrogen atoms to form covalent cross-links.
  • a wide range of suitable polyfunctional electrophiles are known in the art and may be utilized for this purpose. Shown below is an example of the cross-linking of PAni by reaction with ⁇ , ⁇ ′-dichloro p-xylene (where squiggly lines indicate the attachment point to a crosslinked unit of PAni).
  • the density of cross-linking can be controlled by modulating the molar ratio of the cross-linking reagent to the polymer repeat units.
  • conductive polymers While the invention has been primarily described with respect to PAni-based shells, alternative categories of conductive polymers are contemplated and considered within the scope of the invention. Such alternatives include polyheterocycles, such as polythiophenes, polypyrrole, poly(3,4-ethylenedioxythiophene) (PEDOT), poly(3,4-ethylenedioxypyrrole) (PEDOP), as well conductive polyenes and polyarenes (e.g., polystyrene sulfonate).
  • Selectively permeable structures e.g., polymer shells
  • Li/S batteries e.g. 1.5-2.4 V
  • the permeability or inverse barrier is an important physical property for many industrial applications of polymers.
  • polymers with low, high or tailored (i.e., selective) permeability such as protective coatings or barriers to control the flow of certain substances.
  • polymer barriers e.g., polymeric shells
  • the permeability of a substance through the shell can be very different for different polymers and permeants.
  • permeability and solubility at a given temperature depend on the degree of crystallinity (morphology), the molecular weight, the type of permeant and its concentration or pressure, and in the case of copolymers, also on the composition.
  • the selective permeability of the shell is determined by the presence, size, morphology (e.g., void shapes), and distribution of pores within the polymer shell, which can be controlled by, for example acid doping, dedoping and redoping, cross-linking, the introduction of certain additives, or combinations thereof during the polymerization process, or in some cases as part of a post-polymerization process.
  • the selectivity of the permeable polymer shell can be tuned by using a particular acid in the doping, dedoping, and redoping processes, either with or without cross-linking or the use of other additives.
  • Acids such as dodecyl benzene sulfonic acid, camphor sulfonic acid, and p-phenol sulfonic acid have been shown to be effective in tuning the selective permeability of the shell.
  • the selective permeability of the shell can be further tuned by the inclusion of additives, such as phenanthrene, pyrene, triphenyl phosphate, and polystyrene.
  • a particular application e.g., the particular substances that need to be retained within or excluded from the contained volume.
  • the use of unbound additives and/or changing the solvent composition of the dope solution can decrease the permeability and selectivity of the selectively permeable structure.
  • Certain porosities can be induced in various polymers by a sequence of doping, dedoping, and redoping with particular acids.
  • doping with hydrochloric acid results in a highly selective permeability.
  • the induced porosity can be dependent on the size of the acid counter ion.
  • Other possible acids can include halogenic acids, sulfonic acids such as toluene sulfonic acid, methane sulfonic acid, substituted aryl sulfonic acids, and long-chain aliphatic sulfonic acids, and carboxylic acids, such as formic acid, acetic acid, and propionic acid.
  • the permeability properties of the selectively permeable structure can be tuned by entrapping acid dopants as pore templating agents in a polymer matrix composing the structure and by subsequently creating permeation pathways by removing these dopants via alkaline extraction.
  • an unprotonated polyaniline is exposed to various strong acids.
  • the strong electrostatic interactions involved in the protonation of the polyaniline nitrogen atoms, through a strong acid forces the polymer network to conformationally re-organize, so as to accommodate the proton of the acid and the counter ion.
  • Subsequent removal of the acid results in inducing porosity due to the removal of acid from the newly formed cavities in the polymer matrix as shown in the illustration below.
  • Partial redoping of the dedoped structure can have an additional effect on permeability of the polymer as the inclusion of different sized acid counter ions leads to a change in the dimensions of the pores.
  • the nanostructured materials of the present invention have utility in the manufacture of electrochemical devices.
  • the nanostructured materials disclosed herein would be physically combined with other materials to create formulated mixtures which have utility for the manufacture of electrodes for electrochemical devices and, in particular, mixtures useful for forming cathodes in secondary lithium batteries.
  • the present invention provides such cathode compositions (e.g., mixtures).
  • provided mixtures will include one or more of the nanostructured materials described hereinabove (e.g., core-shell particles, etc.), in addition to additives such as electrically conductive particles, binders, and other functional additives typically found in battery cathode mixtures.
  • provided cathode mixtures include plentiful conductive particles to increase the electrical conductivity of the cathode and provide a low resistance pathway for electrons to access the manufactured cathode.
  • other additives may be included to alter or otherwise enhance a cathode produced from the mixture.
  • such mixtures will comprise at least 50 wt. % of a nanostructured material.
  • such mixtures comprise at least about 60 wt. %, at least about 75 wt. %, at least about 80 wt. %, at least about 85 wt. %, or at least about 90 wt. % of the nanostructured material.
  • such mixtures will comprise about 50 to about 90% of the nanostructured material.
  • such mixtures will comprise about 60 to about 90% of the nanostructured material. In certain embodiments, such mixtures will comprise about 60 to about 80% of the nanostructured material. In certain embodiments, such mixtures will comprise about 70 to about 90% of the nanostructured material. In certain embodiments, such mixtures will comprise about 75 to about 85% of the nanostructured material.
  • the inventive nanostructured materials are mixed with the electrically conductive additives (e.g., conductive carbon powders, such as carbon black, Super P®, C-NERGYTM Super C65, Ensaco® black, Ketjenblack®, acetylene black, synthetic graphite such as Timrex® SFG-6, Timrex® SFG-15, Timrex® SFG-44, Timrex® KS-6, Timrex® KS-15, Timrex® KS-44, natural flake graphite, carbon nanotubes, graphene, fullerenes, hard carbon, or mesocarbon microbeads, etc.) and a binder.
  • the electrically conductive additives e.g., conductive carbon powders, such as carbon black, Super P®, C-NERGYTM Super C65, Ensaco® black, Ketjenblack®, acetylene black, synthetic graphite such as Timrex® SFG-6, Timrex® SFG-15, Timre
  • Typical binders include polyvinylidene fluoride, poly(vinylidene fluoride-co-hexafluoropropene) (PVDF/HFP), Polytetrafluoroethylene (PTFE), Kynar Flex® 2801, Kynar® Powerflex LBG, Kynar® HSV 900, Teflon®, carboxymethylcellulose, styrene-butadiene rubber (SBR), polyethylene oxide, polypropylene oxide, polyethylene, polypropylene, polyacrylates, polyvinyl pyrrolidone, poly(methyl methacrylate), polyethyl acrylate, polytetrafluoroethylene, polyvinyl chloride, polyacrylonitrile, polycaprolactam, polyethylene terephthalate, polybutadiene, polyisoprene or polyacrylic acid, or derivatives, mixtures, or copolymers of any of these.
  • the binder is water soluble binder, such as sodium alginate or
  • the provided mixtures can be formulated without a binder, which can be added during the manufacture of the electrodes (e.g. dissolved in a solvent used to form a slurry from the provided mixture).
  • the binder can be activated when made into a slurry to manufacture the electrodes.
  • Suitable materials for use in cathode mixtures are disclosed in Cathode Materials for Lithium Sulfur Batteries: Design, Synthesis, and Electrochemical Performance , Lianfeng, et al., Interchopen.com, Published June 1st 2016, and The strategies of advanced cathode composites for lithium - sulfur batteries , Zhou et al., SCIENCE CHINA Technological Sciences, Volume 60, Issue 2: 175-185(2017), the entire disclosures of each of which are hereby incorporated by reference herein.
  • the present invention provides novel electrode compositions comprising nanostructured materials according to the embodiments described herein.
  • the invention provides cathode compositions.
  • Such cathodes typically comprise a layer of electroactive material coated on a highly conductive current collector.
  • One process such as a “wet process,” involves adding a positive active material (i.e., the provided nanostructured materials), a binder and a conducting material (i.e., the cathode mixture) to a liquid to prepare a slurry composition.
  • a positive active material i.e., the provided nanostructured materials
  • a binder i.e., the binder
  • a conducting material i.e., the cathode mixture
  • Appropriate mixing devices include ball mills, magnetic stirrers, sonication, planetary mixers, high speed mixers, homogenizers, universal type mixers, and static mixers.
  • the liquid used to make the slurry may be any one that can homogeneously disperse the positive active material, the binder, the conducting material, and any additives, and that can be easily evaporated.
  • Possible slurry liquids include, for example, N-methylpyrrolidone, acetonitrile, methanol, ethanol, propanol, butanol, tetrahydrofuran, water, isopropyl alcohol, dimethylpyrrolidone, and the like.
  • the prepared composition is coated on the current collector and dried to form the electrode.
  • the slurry is used to coat an electrical conductor to form the electrode by evenly spreading the slurry on to the conductor, which may then be roll-pressed (e.g. calendared) and heated as is known in the art.
  • a matrix of the nanoparticles and conductive material are held together and on the conductor by the binder.
  • the matrix comprises a lithium conducting polymer binder, such as polyvinylidene fluoride (PVDF), poly(vinylidene fluoride-co-hexafluoropropene) (PVDF/HFP), Polytetrafluoroethylene (PTFE), Kynar Flex® 2801, Kynar® Powerflex LBG, Kynar® HSV 900, Teflon®, styrene butadiene rubber (SBR), polyethylene oxide (PEO), and polytetrafluoroethylene (PTFE).
  • PVDF polyvinylidene fluoride
  • PVDF/HFP poly(vinylidene fluoride-co-hexafluoropropene)
  • PTFE Polytetrafluoroethylene
  • Kynar Flex® 2801 Kynar® Powerflex LBG
  • Kynar® HSV 900 Teflon®
  • SBR styrene butadiene rubber
  • PEO polyethylene oxide
  • PTFE poly
  • the current collector may be selected from the group consisting of: aluminum foil, copper foil, nickel foil, stainless steel foil, titanium foil, zirconium foil, molybdenum foil, nickel foam, copper foam, carbon paper or fiber sheets, polymer substrates coated with conductive metal, and/or combinations thereof.
  • the thickness of the matrix may range from a few microns to tens of microns (e.g., 2-500 microns). In one embodiment, the matrix has a thickness of 10-50 microns. Generally, increasing the thickness of the matrix increases the percentage of active nanoparticles to other constituents by weight, and may increase the cell capacity. However, diminishing returns may be exhibited beyond certain thicknesses. In one embodiment, the film has a thickness of between about 5 and about 200 microns. In a further embodiment, the film has a thickness of between about 10 and about 100, between about 50 and about 100, between about 60 and about 120, between about 75 and about 150, or between about 100 and about 200 microns.
  • the negative electrode (i.e., anode) contains a negative active material.
  • the negative active material is one that can reversibly provide lithium ions. This may simply be lithium metal, or a substance that can intercalate or de-intercalate lithium atoms or ions.
  • Intercalating materials may include carbon materials, preferably any carbon-based negative active material that is typically used for a lithium battery, such as crystalline carbon, amorphous carbon or a combination thereof.
  • the material, which can reversibly form a lithium-containing compound by reacting with the lithium ions may include tin oxide (SnO 2 ), titanium nitrate, silicon (Si), and the like, but not limited thereto.
  • Lithium may be provided in the form of pure lithium or may be provided as an alloy of lithium and metal selected from the group consisting of: Na, K, Rb, Cs, Fr, Be, Mg, Ca, Sr, Ba, Ra, Al, In and Sn.
  • the negative electrode may also be disposed on a current collector, such as those described above.
  • FIG. 8 illustrates a cross section of an electrochemical cell 800 in accordance with exemplary embodiments of the disclosure.
  • Electrochemical cell 800 includes a negative electrode 802 , a positive electrode 804 , a separator 806 interposed between negative electrode 802 and positive electrode 804 , a container 810 , and a fluid electrolyte 812 in contact with negative and positive electrodes 802 , 804 .
  • Such cells optionally include additional layers of electrode and separators 802 a , 802 b , 804 a , 804 b , 806 a , and 806 b.
  • Negative electrode 802 (also sometimes referred to herein as the anode) comprises a negative electrode active material that can accept cations.
  • Non-limiting examples of negative electrode active materials for lithium-based electrochemical cells include Li metal, Li alloys such as those of Si, Sn, Bi, In, and/or Al alloys, Li 4 Ti 5 O 12 , hard carbon, graphitic carbon, metal chalcogenides, and/or amorphous carbon.
  • most (e.g., greater than 90 wt % to all) of the anode active material can be initially included in a discharged positive electrode 804 (also sometimes referred to herein as the cathode) when electrochemical cell 800 is initially made, so that the electrode active material forms part of first electrode 802 during a first charge of electrochemical cell 800 .
  • Negative electrode 802 and positive electrode 804 can further include one or more electronically conductive additives as described above.
  • negative electrode 802 and/or positive electrode 804 further include one or more polymer binders as described above.
  • FIG. 9 illustrates an example of a battery in which the above nanostructured materials, methods, and other techniques, or combinations thereof, may be applied according to various embodiments.
  • a cylindrical battery is shown here for illustration purposes, but other types of arrangements, including prismatic or pouch (laminate-type) batteries, may also be used as desired.
  • the example Li battery 901 includes a negative anode 902 , a positive cathode 904 , a separator 906 interposed between the anode 902 and the cathode 904 , an electrolyte (not shown) impregnating the separator 906 , 906 a , a battery case 905 , and a sealing member 908 sealing the battery case 905 . It will be appreciated that the example battery 901 may simultaneously embody multiple aspects of the present invention in various designs.
  • Example 1 Core Shell Nanoparticles Featuring Electroactive Sulfur in a Selectively Permeable Shell
  • Step 1 Formation of Sulfur Nanoparticles.
  • Sulfur nanoparticles are prepared via the reaction of aqueous sodium thiosulfate with excess hydrochloric acid in the presence of 1 wt % of polyvinylpyrrolidone (PVP, Mw about 40,000).
  • PVP polyvinylpyrrolidone
  • the freshly prepared sulfur particles are isolated by centrifugation and analyzed by SEM to confirm the composition consists of spherical sulfur having particles with an average diameter less than 1000 nm and a narrow size distribution.
  • Step 2 Formation of Core Shell Particles.
  • the sulfur nanoparticles from step 1 are dispersed in water by sonication.
  • aniline and dilute sulfuric acid are added to the resulting suspension.
  • the suspension is maintained at 0° C. under strong stirring for 12 hours.
  • the particles are isolated by centrifugation and rinsed with water.
  • Cryogenic TEM analysis of the particles shows they comprise nanoscale spherical particles with a core-shell morphology featuring a sulfur core conformally coated with PAni shells (S@PAni) and reveals that the PAni shells have thicknesses between 10 and 50 nm (the thickness is varied by controlling the amount of aniline used and the length of time the polymerization is allowed to proceed).
  • Step 3 Formation of Yolk-Shell Particles.
  • the S@PAni nanoparticles are re-suspended in a calibrated volume of 1:1 water/isopropanol, the suspension is stirred and aliquots are taken periodically, filtered to remove the nanoparticles, weighed, and analyzed by combustion analysis to determine the amount of dissolved sulfur present. Once combustion analysis of the filtrate shows that 50% of the sulfur present in the S@PAni particles has dissolved, the suspension is centrifuged, and the isolated nanoparticles are rinsed twice with water and dried.
  • Step 4 Introduction of a Contained Liquid Phase.
  • the core shell S@PAni nanoparticles are placed in a thick walled glass tube outfitted with a valved cap plumbed to vacuum and a nitrogen manifold.
  • the tube is briefly subjected to a vacuum of 50 mTorr before a mixture of diglyme containing 10% (v/v) octanedinitrile is introduced to the evacuated tube.
  • the headspace pressure is then normalized by introduction of nitrogen gas, and then alternately cycled between 100 psig and ambient pressure.
  • Step 5 Modification of the Permeability of the PAni Shell.
  • a sequence consisting of doping and then cross-linking the polyaniline is used.
  • DBSA dodecyl benzene sulfonic acid
  • the color of the particles changes from light grey to dark blackish-green.
  • the mixture is stirred for 1 h, then glutaraldehyde is added as a cross-linking agent and the mixture heated to 60° C. After stirring for 4 h at this temperature, the mixture is cooled to ambient temperature, centrifuged, and the isolated particles are rinsed twice with NMP and dried.
  • Example 2 is performed according to the protocols of Example 1, except that at step 5, instead of chemically cross-linking with glutaraldehyde, the PAni shell is intramolecularly cross-linked by heat-treating the Doped particle suspension at 180° C. for 6 h.
  • the doped PAni particles are isolated by centrifugation prior to heat-treating in a 180° C. oven for 4 h.
  • Example 3 is performed according to the protocols of Example 1, except that at step 5 modification of the permeability is performed by doping and dedoping the PAni shell with acid.
  • a suspension of the nanoparticles is treated with dodecyl benzene sulfonic acid (DBSA). Protonation of the polyaniline nitrogen atoms induces a conformational change in the polymer network.
  • the nanoparticles are treated with a base to deprotonate the polyaniline nitrogen atoms and remove the acid.
  • the doped/dedoped PAni particles are isolated by centrifugation. The particles are subjected to cryogenic TEM analysis to measure the porosity of the PAni shells.
  • Example 4 is performed according to the protocols of Example 1, except that a mixture of diglyme, octanedinitrile and toluene (10:1:2 by volume) is used as the solvent for the sulfur removal described in step 3. The resulting suspension is then used directly for step 5.
  • Example 5 Change of Doping Agent Size to a Smaller Acid to Modulate Permeability of the Cross-Linked Nanostructured Material
  • Example 5 is performed according to the protocols of Example 1, except different acids are used to dope the PAni at step 5.
  • a series of separate samples are processed using naphthalene 1-sulfonic acid, p-toluene sulfonic acid, methane sulfonic acid, trifluoroacetic acid, and hydrobromic acid as the doping agent in place of DBSA.
  • the resulting nanostructured materials are then isolated and then evaluated for the ability of the constituents of the contained liquid phase (e.g. diglyme and octanedinitrile) to permeate through the cross-linked PAni shell.
  • This evaluation is done by stirring the nanoparticles in electrolyte (e.g. 1:1 DME/DOL containing 1 M LiTFSI and 0.2 M LiNO 3 ) for 72 hours and periodically sampling the mixture, filtering it and analyzing the supernatant by GC to assay the amount of diglyme and octanedinitrile in the DME/DOL.
  • electrolyte e.g. 1:1 DME/DOL containing 1 M LiTFSI and 0.2 M LiNO 3
  • a cathode is formed by combining samples of the nanostructured materials with conducting carbon and a PVDF binder in an NMP slurry and coating an aluminum current collector with the mixture. A strip of this cathode is then placed in an electrochemical cell containing a lithium metal anode and an electrolyte (1:1 DME/DOL containing 1 M LiTFSI and 0.2 M LiNO 3 ) and sampling the electrolyte for gas chromatographic analysis as the cell is alternately charged and discharged.
  • the concentration of diglyme and octanedinitrile in the electrolyte is used as an indirect measurement of the permeability of the PAni shells to these substances.
  • the electrolyte in each cell is analyzed by spectrophotometry to assay the concentration of lithium polysulfides present in the electrolyte. These values are correlated to the permeability of the PAni shells to polysulfide and/or to the ability of the core shell particles to accommodate the solvent flux caused by volume changes of the electroactive sulfur core.
  • the cycled cathodes are evaluated by SEM to assess whether the core shell particles are intact and differentiate whether higher polysulfide concentrations result from breakage of nanoparticles or permeation of polysulfides through the particle shells.
  • Example 6 Change of Doping Agent Size to a Smaller Acid to Modulate Permeability of the Doped/Dedoped Nanostructured Material
  • Example 6 is performed according to the protocols of Example 3, except different acids are used to dope the PAni.
  • a series of separate samples are processed using formic acid, acetic acid, propionic acid, and hydrochloric acid as the doping agent in place of DBSA. The permeability of these samples was assessed according to the protocols of Example 5.
  • Example 7 is performed according to the protocols of Example 1, except elemental sulfur that has been ball-milled to sub-micron particles is suspended in an aqueous solution and used for step 2, instead of the synthesized sulfur nanoparticles of step 1 of Example 1.
  • compositions, systems, devices, methods, and processes of the present application encompass variations and adaptations developed using information from the embodiments described in the present disclosure. Adaptation or modification of the methods and processes described in this specification may be performed by those of ordinary skill in the relevant art.
  • headers in the present disclosure are provided for the convenience of the reader.
  • the presence and/or placement of a header is not intended to limit the scope of the subject matter described herein.
  • embodiments located in one section of the application apply throughout the application to other embodiments, both singly and in combination.
  • compositions, compounds, or products are described as having, including, or comprising specific components, or where processes and methods are described as having, including, or comprising specific steps, it is contemplated that, additionally, there are articles, devices, and systems of the present application that consist essentially of, or consist of, the recited components, and that there are processes and methods according to the present application that consist essentially of, or consist of, the recited processing steps.
  • Embodiment 1 A nanostructured material comprising a contained volume that is physically separated from a volume outside of the nanostructure, wherein the contained volume encloses a contained electroactive substance and a contained liquid phase in contact with the contained electroactive substance.
  • Embodiment 2 A nanostructured material comprising a contained volume that is physically separated from a volume outside of the nanostructure by a permeable membrane, wherein the contained volume encloses an electroactive substance and a contained liquid phase in contact with the electroactive substance.
  • Embodiment 3 A nanostructured material comprising a contained volume that is physically separated from a volume outside of the nanostructure by a selectively permeable membrane, wherein the contained volume encloses an electroactive substance and a contained liquid phase in contact with the electroactive substance.
  • Embodiment 4 The nanostructured material of any one of embodiments 1 to 3, wherein the electroactive substance comprises sulfur.
  • Embodiment 5 The nanostructured material of embodiment 4, wherein the electroactive sulfur material is in the form of elemental sulfur, sulfur-containing organic molecules, polymers or composites, metal sulfides, or mixtures thereof.
  • Embodiment 6 The nanostructured material of embodiment 4 or 5, wherein the electroactive sulfur material comprises S 8 .
  • Embodiment 7 The nanostructured material of any one of embodiments 4 to 6, wherein the electroactive sulfur material forms a composite with one or more additional materials selected from the group consisting of: graphite, graphene, chalcogenides, metal sulfides, metal oxides, conductive polymers, or mixtures thereof.
  • Embodiment 8 The nanostructured material of any one of the preceding embodiments, wherein the electroactive substance comprises about 20% to about 80% of the contained volume.
  • Embodiment 9 The nanostructured material of any one of the preceding embodiments, wherein the contained liquid phase comprises about 20% to about 80% of the contained volume.
  • Embodiment 10 The nanostructured material of any one of the preceding embodiments, wherein the nanoparticle has a substantially spherical shape.
  • Embodiment 11 The nanostructured material of any one of embodiments 2 to 10, wherein the membrane has a dimension of about 10 to 1000 nm.
  • Embodiment 12 The nanostructured material of any one of embodiments 2 to 11, wherein the membrane has a wall thickness of about 0.5 to 100 nm.
  • Embodiment 13 The nanostructured material of any one of embodiments 2 to 12, wherein the membrane comprises a polymer selected from the group consisting of: polyethylene, polypropylene, polytetrafluoroethylene (PTFE), polyvinylidene difluoride (PVDF), polysulfone, polyethersulfone, polyacrylonitrile, polyamide, polyimide, polyamideimide, polyetherimide, cellulose acetate, polyaniline, polypyrrole, polyetheretherketone (PEEK), polybenzimidazole, and derivatives, mixtures or co-polymers thereof.
  • PTFE polytetrafluoroethylene
  • PVDF polyvinylidene difluoride
  • PES polysulfone
  • polyethersulfone polyacrylonitrile
  • polyamide polyimide
  • polyamideimide polyamideimide
  • polyetherimide cellulose acetate
  • PEEK polyetheretherketone
  • PEEK polybenzimidazole
  • Embodiment 14 The nanostructured material of any one of embodiments 2 to 12, wherein the membrane comprises one or more electronically conductive polymers.
  • Embodiment 15 The nanostructured material of embodiment 14, wherein at least one electronically conductive polymer is selected from the group consisting of: polyaniline, polydopamine, polypyrrole, polyselenophene, polythiophene, polynaphthalene, polyphenylene sulfide, and derivatives, mixtures or copolymers thereof.
  • Embodiment 16 The nanostructured material of embodiment 14, wherein at least one electronically conductive polymer is selected from the group consisting of: polypyrrole (PPy), polythiophene (PTh), polydopamine, poly(3,4-ethylenedioxythiophene) (PEDOT), poly(3,4-propylenedioxythiophene) (ProDOT), poly(3,4-ethylenedioxypyrrole) (PEDOP), poly(3,4-propylenedioxypyrrole) (ProDOP), poly(3,4-ethylenedithiopyrrole) (PEDTP), poly(3,4-ethyleneoxyhiathiophene) (PEOTT), poly(3,4-ethylenedioxyselenophene) (PEDOSe), and derivatives, mixtures or copolymers thereof.
  • Py polypyrrole
  • PTh polythiophene
  • PDOT poly(3,4-ethylenedioxythiophene)
  • ProDOT poly(3,4-propylenedi
  • Embodiment 17 The nanostructured material of embodiment 14, wherein at least one electronically conductive polymer is selected from the group consisting of: polyaniline (PAni), poly(o-methylaniline) (POTO), poly(o-methoxyaniline) (POAS), poly(2,5-dimethylaniline) (PDMA), poly(2,5-dimethoxyaniline) (PDOA), sulfonated polyaniline (SPAN), poly(l-aminonaphthalene) (PNA), poly(5-aminonaphthalene-2-sulfonic acid), polyphenylene sulfide, and derivatives, mixtures or copolymers thereof.
  • PAni polyaniline
  • POTO poly(o-methylaniline)
  • POAS poly(o-methoxyaniline)
  • PDMA poly(2,5-dimethylaniline)
  • PDOA poly(2,5-dimethoxyaniline)
  • SPAN sulfonated polyaniline
  • PNA poly
  • Embodiment 18 The nanostructured material of embodiment 16 further comprising at least one electronically conductive polymer is selected from the group consisting of: polyaniline (PAni), poly(o-methylaniline) (POTO), poly(o-methoxyaniline) (POAS), poly(2,5-dimethylaniline) (PDMA), poly(2,5-dimethoxyaniline) (PDOA), sulfonated polyaniline (SPAN), poly(l-aminonaphthalene) (PNA), poly(5-aminonaphthalene-2-sulfonic acid), polyphenylene sulfide, and derivatives, mixtures or copolymers thereof.
  • PAni polyaniline
  • POTO poly(o-methylaniline)
  • POAS poly(o-methoxyaniline)
  • PDMA poly(2,5-dimethylaniline)
  • PDOA poly(2,5-dimethoxyaniline)
  • SPAN sulfonated polyaniline
  • PNA
  • Embodiment 19 The nanostructured material of embodiments 13 to 18, wherein the polymer is cross-linked.
  • Embodiment 20 The nanostructured material of any one of embodiments 2 to 12, wherein the membrane comprises an inorganic solid selected from the group consisting of, silicon carbide, silicon oxide, iron oxide, manganese oxide, titanium disulfide, molybdenum disulfide, zirconium oxide, titanium oxide, zeolites, and mixtures thereof.
  • an inorganic solid selected from the group consisting of, silicon carbide, silicon oxide, iron oxide, manganese oxide, titanium disulfide, molybdenum disulfide, zirconium oxide, titanium oxide, zeolites, and mixtures thereof.
  • Embodiment 21 The nanostructured material of any one of embodiments 2 to 12, wherein the membrane comprises a polymer with dispersed organic or inorganic matrices.
  • Embodiment 22 The nanostructured material of embodiment 21, wherein the organic or inorganic matrices are selected from the group consisting of: carbon matrices and zeolites.
  • Embodiment 23 The nanostructured material of embodiment 2, wherein the contained liquid phase comprises one or more substances that exchange across the permeable membrane.
  • Embodiment 24 The nanostructured material of embodiment 23, wherein movement of the substances in the contained liquid phase across the permeable membrane is induced by changes in hydrostatic pressure.
  • Embodiment 25 The nanostructured material of embodiment 3, wherein the contained liquid phase comprises at least one substance to which the selectively permeable membrane is substantially impermeable.
  • Embodiment 26 The nanostructured material of embodiment 25, wherein an impermeable substance is lithium polysulfide.
  • Embodiment 27 The nanostructured material of embodiment 25, wherein the at least one impermeable substance is a trapped solvent.
  • Embodiment 28 The nanostructured material of embodiment 27, wherein the trapped solvent is selected from the group consisting of: ethers, diethers, polyethers, sulfones, disulfones, polysulfones, nitriles, dinitriles, polynitriles, thioesters, dithioesters, thiocarbonates, dithiocarbonates, trithiocarbonates, or mixtures thereof.
  • the trapped solvent is selected from the group consisting of: ethers, diethers, polyethers, sulfones, disulfones, polysulfones, nitriles, dinitriles, polynitriles, thioesters, dithioesters, thiocarbonates, dithiocarbonates, trithiocarbonates, or mixtures thereof.
  • Embodiment 29 An electrode composition comprising the nanostructured material of any one of the preceding embodiments.
  • Embodiment 30 The electrode composition of embodiment 29, further comprising one or more electrically conductive additive and one or more binders.
  • Embodiment 31 The electrode composition of embodiment 29, wherein the nanostructured material comprises at least 50% of the composition.
  • Embodiment 32 The electrode composition of embodiment 31, wherein the nanostructured material comprises about 60 to 90% of the composition.
  • Embodiment 33 A cathode formulated with the electrode composition of any one of embodiments 29 to 32.
  • Embodiment 34 An electrochemical energy storage device comprising the cathode of embodiment 33, an anode, a separator, and a primary electrolyte.
  • Embodiment 35 The electrochemical energy storage device of embodiment 34, wherein the primary electrolyte and the contained liquid in the nanostructured materials comprise different compositions.
  • Embodiment 36 A system comprising a nanostructured material in contact with a first liquid phase, the nanostructured material comprising a contained volume that encloses a contained electroactive substance and a contained liquid phase in contact with the electroactive substance wherein the contained liquid phase is physically separated from the first liquid phase by a selectively permeable membrane and wherein at least one of the first liquid phase and the contained liquid phase comprises substances to which the selectively permeable structure is substantially impermeable.
  • Embodiment 37 The system of embodiment 36, wherein the nanostructured material is from any one of embodiments 3 to 22 or 25 to 28.
  • Embodiment 38 The system of embodiment 36 or 37, wherein the contained liquid phase comprises one or more ethers to which the selectively permeable structure is substantially impermeable.
  • Embodiment 39 The system of any one of embodiments 36 to 38, wherein the first liquid phase comprises one or more aliphatic carbonates to which the selectively permeable structure is substantially impermeable.
  • Embodiment 40 A method of making a nanostructure comprising the steps of: forming a nanoscale particle of an electroactive substance; coating the nanoscale particle with a permeable encapsulant to contain the electroactive substance; reducing the volume of the contained electroactive substance to create a void space contained within the encapsulant; introducing a liquid phase into the void space; and coating the nanoscale particle with a second encapsulant that is impermeable to one or more of the substances in the liquid phase.
  • Embodiment 41 A method of making a nanostructure comprising the steps of: forming a nanoscale particle of an electroactive substance; coating the nanoscale particle with a permeable encapsulant to contain the electroactive substance; reducing the volume of the contained electroactive substance to create a void space contained within the encapsulant; introducing a liquid phase into the void space; and modifying the encapsulant to make it less permeable to one or more substances in the liquid phase.
  • Embodiment 42 A method of making a nanostructure comprising the steps of: forming a hollow structure with a permeable encapsulant, introducing a nanoscale particle of an electroactive substance into the hollow structure, introducing a liquid phase into the void space, and modifying the encapsulant to make it less permeable to one or more substances in the liquid phase.
  • Embodiment 43 A method of making a nanostructure comprising the steps of: forming a hollow structure with a permeable encapsulant; introducing a liquid phase into the void space comprising a dissolved electroactive substance or precursor to the electroactive substance; treating the nanostructure to solidify the dissolved electroactive substance or precursor to the electroactive substance contained in the hollow structure; and modifying the encapsulant to make it less permeable to one or more substances in the liquid phase.
  • Embodiment 44 The method of any one of embodiments 41 to 43, wherein the encapsulant comprises at least one polymer.
  • Embodiment 45 The method of embodiment 44, wherein the at least one polymer is selected from the group consisting of: polyethylene, polypropylene, polytetrafluoroethylene (PTFE), polyvinylidene difluoride (PVDF), polysulfone, polyethersulfone, polyacrylonitrile, polyamide, polyimide, polyamideimide, polyetherimide, cellulose acetate, polyaniline, polypyrrole, polyetheretherketone (PEEK), polybenzimidazole, and derivatives, mixtures, or copolymers thereof.
  • PTFE polytetrafluoroethylene
  • PVDF polyvinylidene difluoride
  • polysulfone polyethersulfone
  • polyacrylonitrile polyamide
  • polyimide polyimide
  • polyetherimide polyetherimide
  • cellulose acetate polyaniline
  • PEEK polyetheretherketone
  • PEEK polyetheretherketone
  • Embodiment 46 The method of embodiment 44, wherein at least one polymer is an electronically conducting polymer.
  • Embodiment 47 The method of embodiment 46, wherein at least one electronically conductive polymer is selected from the group consisting of: polyaniline, polydopamine, polypyrrole, polyselenophene, polythiophene, polynaphthalene, polyphenylene sulfide, and derivatives, mixtures, or copolymers thereof.
  • Embodiment 48 The method of embodiment 46, wherein at least one electronically conductive polymer is selected from the group consisting of: polypyrrole (PPy), polythiophene (PTh), polydopamine, poly(3,4-ethylenedioxythiophene) (PEDOT), poly(3,4-propylenedioxythiophene) (ProDOT), poly(3,4-ethylenedioxypyrrole) (PEDOP), poly(3,4-propylenedioxypyrrole) (ProDOP), poly(3,4-ethylenedithiopyrrole) (PEDTP), poly(3,4-ethyleneoxyhiathiophene) (PEOTT), poly(3,4-ethylenedioxyselenophene) (PEDOSe), and derivatives, mixtures or copolymers thereof.
  • Py polypyrrole
  • PTh polythiophene
  • PDOT poly(3,4-propylenedioxythiophene)
  • ProDOT poly(3,4-propylenedi
  • Embodiment 49 The method of embodiment 46, wherein at least one electronically conductive polymer is selected from the group consisting of: polyaniline (PAni), poly(o-methylaniline) (POTO), poly(o-methoxyaniline) (POAS), poly(2,5-dimethylaniline) (PDMA), poly(2,5-dimethoxyaniline) (PDOA), sulfonated polyaniline (SPAN), poly(l-aminonaphthalene) (PNA), poly(5-aminonaphthalene-2-sulfonic acid), polyphenylene sulfide, and derivatives, mixtures or copolymers thereof.
  • PAni polyaniline
  • POTO poly(o-methylaniline)
  • POAS poly(o-methoxyaniline)
  • PDMA poly(2,5-dimethylaniline)
  • PDOA poly(2,5-dimethoxyaniline)
  • SPAN sulfonated polyaniline
  • PNA poly(l
  • Embodiment 50 The method of embodiment 48 further comprising at least one polymer is selected from the group consisting of: polyaniline (PAni), poly(o-methylaniline) (POTO), poly(o-methoxyaniline) (POAS), poly(2,5-dimethylaniline) (PDMA), poly(2,5-dimethoxyaniline) (PDOA), sulfonated polyaniline (SPAN), poly(l-aminonaphthalene) (PNA), poly(5-aminonaphthalene-2-sulfonic acid), polyphenylene sulfide, and derivatives, mixtures or copolymers thereof.
  • PAni polyaniline
  • POTO poly(o-methylaniline)
  • POAS poly(o-methoxyaniline)
  • PDMA poly(2,5-dimethylaniline)
  • PDOA poly(2,5-dimethoxyaniline)
  • SPAN sulfonated polyaniline
  • PNA poly(l-amin
  • Embodiment 51 The method of any one of embodiments 44 to 45, wherein the step of modifying the permeability of the encapsulant comprises cross-linking the polymer.
  • Embodiment 52 The method of embodiment 51, wherein the polymer is cross-linked with one or more cross-linking reagent selected from the group consisting of: aldehydes, dicarbonyl compounds, sulfur or polysulfur compounds, diacid chlorides, alkyl dihalides, diamines, di-epoxides, polyisocyanates, and mixtures thereof.
  • one or more cross-linking reagent selected from the group consisting of: aldehydes, dicarbonyl compounds, sulfur or polysulfur compounds, diacid chlorides, alkyl dihalides, diamines, di-epoxides, polyisocyanates, and mixtures thereof.
  • Embodiment 53 The method of any one of embodiments 41 to 43, wherein the step of modifying the permeability of the encapsulant comprises acid doping and dedoping.
  • Embodiment 54 The method of embodiment 53, wherein the acid is selected from the group consisting of: acetic acid, decyl benzene sulfonic acid, camphor sulfonic acid, carboxylic acids, halogenic acids, p-phenol sulfonic acid, or combinations thereof.
  • the acid is selected from the group consisting of: acetic acid, decyl benzene sulfonic acid, camphor sulfonic acid, carboxylic acids, halogenic acids, p-phenol sulfonic acid, or combinations thereof.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Composite Materials (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Battery Electrode And Active Subsutance (AREA)
  • Secondary Cells (AREA)
  • Electric Double-Layer Capacitors Or The Like (AREA)
US17/619,480 2019-06-18 2020-06-18 Selectively permeable nanostructured materials Pending US20220310994A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US17/619,480 US20220310994A1 (en) 2019-06-18 2020-06-18 Selectively permeable nanostructured materials

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201962863138P 2019-06-18 2019-06-18
US201962863816P 2019-06-19 2019-06-19
US17/619,480 US20220310994A1 (en) 2019-06-18 2020-06-18 Selectively permeable nanostructured materials
PCT/US2020/038508 WO2020257509A1 (en) 2019-06-18 2020-06-18 Selectively permeable nanostructured materials

Publications (1)

Publication Number Publication Date
US20220310994A1 true US20220310994A1 (en) 2022-09-29

Family

ID=74040694

Family Applications (2)

Application Number Title Priority Date Filing Date
US17/619,480 Pending US20220310994A1 (en) 2019-06-18 2020-06-18 Selectively permeable nanostructured materials
US17/619,489 Pending US20220310992A1 (en) 2019-06-18 2020-06-18 Selectively permeable nanostructured materials for lithium anode compositions

Family Applications After (1)

Application Number Title Priority Date Filing Date
US17/619,489 Pending US20220310992A1 (en) 2019-06-18 2020-06-18 Selectively permeable nanostructured materials for lithium anode compositions

Country Status (5)

Country Link
US (2) US20220310994A1 (ko)
EP (2) EP3987595A4 (ko)
JP (2) JP2022536978A (ko)
KR (2) KR20220024708A (ko)
WO (2) WO2020257509A1 (ko)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113484469B (zh) * 2021-06-30 2022-11-18 中国科学院青海盐湖研究所 水合盐体系相变储能材料纳米尺度相分离的原位表征方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120196186A1 (en) * 2008-06-20 2012-08-02 Toyota Motor Engineering & Manufacturing North America, Inc. Electrode material with core-shell structure
US20130026409A1 (en) * 2011-04-08 2013-01-31 Recapping, Inc. Composite ionic conducting electrolytes
US20140057179A1 (en) * 2012-08-24 2014-02-27 Sila Nanotechnologies Inc. Scaffolding matrix with internal nanoparticles
US20180219215A1 (en) * 2017-02-01 2018-08-02 Toyota Motor Engineering & Manufacturing North America, Inc. Sulfur particles coated with inorganic-organic hybrid membranes as cathode active material and batteries containing the particles

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59225705A (ja) 1983-06-07 1984-12-18 Nitto Electric Ind Co Ltd 複合膜及びその製造方法
JPS62136212A (ja) 1985-12-07 1987-06-19 Mitsubishi Paper Mills Ltd 選択透過性複合膜の製造方法
DE4416330A1 (de) 1994-05-09 1995-11-16 Hoechst Ag Verbundmembran und Verfahren zu ihrer Herstellung
US5458745A (en) * 1995-01-23 1995-10-17 Covofinish Co., Inc. Method for removal of technetium from radio-contaminated metal
US6368382B1 (en) 2000-07-27 2002-04-09 Uop Llc Epoxysilicone coated membranes
US6503295B1 (en) 2000-09-20 2003-01-07 Chevron U.S.A. Inc. Gas separations using mixed matrix membranes
US20030131731A1 (en) 2001-12-20 2003-07-17 Koros William J. Crosslinked and crosslinkable hollow fiber mixed matrix membrane and method of making same
DE102005031703B3 (de) 2005-07-05 2007-01-11 Gkss-Forschungszentrum Geesthacht Gmbh Kompositmembran
GB2437519B (en) 2006-04-28 2010-04-21 Imp Innovations Ltd Method for separation
US8361659B2 (en) * 2008-06-20 2013-01-29 Toyota Motor Engineering & Manufacturing North America, Inc. Lithium-alloying-material/carbon composite
DE102009047351A1 (de) 2009-12-01 2011-06-09 Evonik Goldschmidt Gmbh Komposit-Siliconmembranen mit hoher Trennwirkung
CN103875097A (zh) 2011-09-12 2014-06-18 小利兰斯坦福大学理事会 可再充电锂电池的囊封硫阴极
US8932764B2 (en) * 2012-02-28 2015-01-13 Sila Nanotechnologies, Inc. Core-shell composites for sulfur-based cathodes in metal-ion batteries
US10505180B2 (en) 2012-11-07 2019-12-10 The Regents Of The University Of California Core-shell structured nanoparticles for lithium-sulfur cells
US20160372742A1 (en) 2013-07-05 2016-12-22 Cornell Uniiversity Yoke-shell nanoparticle, method and applications
CN104852083B (zh) * 2015-05-14 2017-06-13 珠海泰坦储能科技有限公司 一种液流形式的锂硫电池储能系统
EP3323164A4 (en) * 2015-07-13 2019-01-09 Sila Nanotechnologies Inc. STABLE CATHODES ON LITHIUM FLUORIDE BASE FOR METAL AND METAL ION BATTERIES
WO2017091645A1 (en) 2015-11-24 2017-06-01 Oasys Water, Inc. Support layers for forward osmosis membranes
CN109689186A (zh) 2016-09-07 2019-04-26 欧赛斯水务有限公司 有可替代的选择性层的膜
US11394082B2 (en) * 2016-09-28 2022-07-19 Sepion Technologies, Inc. Electrochemical cells with ionic sequestration provided by porous separators

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120196186A1 (en) * 2008-06-20 2012-08-02 Toyota Motor Engineering & Manufacturing North America, Inc. Electrode material with core-shell structure
US20130026409A1 (en) * 2011-04-08 2013-01-31 Recapping, Inc. Composite ionic conducting electrolytes
US20140057179A1 (en) * 2012-08-24 2014-02-27 Sila Nanotechnologies Inc. Scaffolding matrix with internal nanoparticles
US20180219215A1 (en) * 2017-02-01 2018-08-02 Toyota Motor Engineering & Manufacturing North America, Inc. Sulfur particles coated with inorganic-organic hybrid membranes as cathode active material and batteries containing the particles

Also Published As

Publication number Publication date
EP3987595A1 (en) 2022-04-27
EP3987595A4 (en) 2023-12-20
JP2022537573A (ja) 2022-08-26
EP3987594A1 (en) 2022-04-27
EP3987594A4 (en) 2023-12-06
US20220310992A1 (en) 2022-09-29
JP2022536978A (ja) 2022-08-22
KR20220024708A (ko) 2022-03-03
KR20220035389A (ko) 2022-03-22
WO2020257509A1 (en) 2020-12-24
WO2020257503A1 (en) 2020-12-24

Similar Documents

Publication Publication Date Title
US11837712B2 (en) Anode electrode composition of Li-ion battery cell
US10686217B2 (en) Lithium-sulfur secondary battery containing gradient electrolyte
JP6732810B2 (ja) 電池に応用するためのナノ構造材料
Liu et al. Graphene-based interlayer for high-performance lithium–sulfur batteries: A review
CN107623103B (zh) 锂硫电池单元电极
US9917303B2 (en) Rechargeable lithium-sulfur battery having a high capacity and long cycle life
US20180331352A1 (en) Carbon composites
KR20180061034A (ko) 금속 황화물 나노입자를 포함하는 리튬-황 전지용 양극 활물질 및 이의 제조방법
TW201834965A (zh) 混合型同素異形體微粒碳膜及碳纖維墊
KR20130119432A (ko) 재충전형 리튬-황 전지 전극용 그래핀-황 나노복합체
KR101645075B1 (ko) 그래핀 층과 알루미늄이 코팅된 섬유조직 형태의 중간전극 층이 삽입된 리튬­황 전지 및 그 제조방법
US20220259408A1 (en) Functionalized polymer for battery applications
US20210119216A1 (en) Sulfur-carbon composite, method for preparing same, and lithium secondary battery comprising same
US11658293B2 (en) Sulfur-carbon composite, preparation method therefor, and lithium secondary battery comprising same
US20220310994A1 (en) Selectively permeable nanostructured materials
KR20190083397A (ko) 질소 및 황이 도핑된 다공성 탄소재 제조방법
US20230207822A1 (en) Coated sulfur particles with no gap
Banitaba Application of electrospun fibers for the fabrication of high performance all-solid-state fibrous batteries
Choi et al. Applications of halloysite in separators for secondary batteries
Kumar et al. A state-of-the-art review on MXene-based hybrid nanomaterial for energy storage applications

Legal Events

Date Code Title Description
AS Assignment

Owner name: CONAMIX INC., NEW YORK

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BURKHARDT, STEPHEN;SIMONEAU, CHRISTOPHER A.;BECK, LARRY;AND OTHERS;SIGNING DATES FROM 20200708 TO 20200917;REEL/FRAME:058400/0669

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED