US20220134715A1 - Wood laminate material and method for manufacturing same - Google Patents
Wood laminate material and method for manufacturing same Download PDFInfo
- Publication number
- US20220134715A1 US20220134715A1 US17/580,790 US202217580790A US2022134715A1 US 20220134715 A1 US20220134715 A1 US 20220134715A1 US 202217580790 A US202217580790 A US 202217580790A US 2022134715 A1 US2022134715 A1 US 2022134715A1
- Authority
- US
- United States
- Prior art keywords
- strand
- density
- layers
- strands
- woodbased
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Provided is a strand board with improved strength and water resistance. Reduction in productivity is prevented and characteristics of the strand board can be varied as desired while achieving certain strength and water resistance of the strand board. A strand board B is formed by stacking and laminating five strand layers 1 each formed by a large number of strands 5. The strand board B has substantially constant density distribution in the lamination direction of the strand layers 1. Three of the five strand layers 1 of the strand board B are high-density strand layers 1a having a higher density than the other strand layers 1, and the other strand layers 1 are low-density strand layers 1b.
Description
- This is a divisional under 35 USC § 120 of U.S. application Ser. No. 16/088,904, filed Sep. 27, 2018, which is a national stage under 35 USC § 371 of International Application No. PCT/JP2017/033872, filed Sep. 20, 2017, which claims priority under 35 USC § 119 to Japanese Patent Application Nos. 2016-194762, filed Sep. 30, 2016 and 2017-063447, filed Mar. 20, 2017. The disclosure of each of these applications is incorporated herein in its entirety.
- The present invention relates to wood laminate materials that are formed by stacking and laminating multiple woodbased material layers each formed by a woodbased material or woodbased materials, and methods for manufacturing the same.
- Today there are less and less tropical hardwood species including broadleaf tress such as apitong and keruing, and it is difficult to obtain high-quality veneer at low cost. Degradation in quality of plywood using tropical hardwood species has therefore become a big problem. Wood fiberboards such as oriented strand boards (OSBs) are increasingly used as a substitute material for plywood. However, OSBs with common densities do not provide sufficient strength.
- Conventionally,
Patent Document 1, for example, discloses a large OSB plate having a density of at most 700 kg/m3, a length of at least 7 m, and a flexural modulus of at least 7000 N/mm2 in the primary load direction. -
Patent Document 2 discloses a technique of using a strand material, which is formed by orienting and stacking woodbased material pieces and compressing and heating the stack, for joists, foundations, etc. -
- PATENT DOCUMENT 1: Japanese Patent No. 4307992
- PATENT DOCUMENT 2: Japanese Patent No. 4227864
- In the OSB plate of
Patent Document 1, a press pressure higher than common pressures is required to form a board. This OSB plate therefore cannot be formed without using a special press machine. - The inventors found that a board formed at a press pressure higher than common pressures with a special press machine as described above has uneven density distribution in the thickness direction of the boards. A board having uneven density distribution tends to be weak in its low-density portion. Moreover, the low-density portion of the board is more water absorbent and thus has lower water resistance as compared to a high-density portion of the board. With such uneven density distribution, strength and water resistance are governed by the low-density portion, and sufficient strength and water resistance cannot be obtained.
- High strength and high water resistance can be achieved by using layers with a high density as all of woodbased material layers of a wood laminate material that is a laminate of woodbased materials such as strands.
- In this case, however, it takes a lot of time and effort to increase the density of all of the multiple woodbased material layers of the wood laminate material, and reduction in productivity is therefore unavoidable. Moreover, since all of the woodbased material layers have a high density, characteristics as the wood laminate material are always the same, and it is difficult to vary characteristics of the wood laminate material for various applications.
- It is an object of the present invention to allow a wood laminate material, which is a laminate of multiple woodbased materials, to have high strength and high water resistance by adjusting density distribution in the lamination direction, namely the direction in which the woodbased materials are laminated. It is another object of the present invention to prevent reduction in productivity for manufacturing wood laminate materials and make it possible to vary characteristics of the wood laminate materials while achieving a certain level of strength and water resistance of the wood laminate materials.
- In order to achieve the above objects, in the present invention, a wood laminate material is formed so as to have substantially constant density distribution in the lamination direction, thereby improving strength and water resistance of the wood laminate material.
- Specifically, in the present invention, a wood laminate material formed by stacking and laminating multiple woodbased material layers each formed by laminated woodbased materials that are laminated multiple cut pieces or a woodbased material that is a veneer is characterized by having substantially constant density distribution in a lamination direction of the woodbased material layers.
- According to this configuration, the wood laminate material has substantially constant density distribution in the lamination direction. As described above, if the wood laminate material has uneven density distribution in the lamination direction, strength and water resistance of the wood laminate material are governed by a low-density portion. However, the wood laminate material according to the present invention does not have such a problem. A wood laminate material with high strength and high water resistance is thus implemented.
- In the above configuration, the woodbased material may have a density of 300 kg/m3 or more and 1100 kg/m3 or less, and preferably 300 kg/m3 or more and 800 kg/m3.
- Since the woodbased material has a density of 300 kg/m3 or more, the thickness of a stack of woodbased material layers (the thickness of the stack before being laminated) required to form a wood laminate material with the same density and strength can be reduced. Since the thickness of the stack can be reduced, workability of processes associated with lamination (e.g., a stacking process and a forming process) is improved. Moreover, a pressure for lamination which is required to form a wood laminate material with the same density and strength can be reduced.
- The multiple woodbased material layers may be composed so that a thickness of the woodbased material layer gradually increases from the middle woodbased material layer in the lamination direction of the wood laminate material to the top and bottom woodbased material layers.
- The outer layers that are more likely to be subjected to load and impact and are more susceptible to humidity etc. thus have a larger thickness than the inner layer(s). This allows the wood laminate layer to have improved performance regarding influences from the external environment.
- In the present invention, not all of the woodbased material layers of the wood laminate material have a high density, but only a part of the woodbased material layers has a high density. High strength, high water resistance, etc. of the wood laminate material are thus implemented by the woodbased material layer with a high density.
- Specifically, a wood laminate material formed by stacking and laminating multiple woodbased material layers each formed by laminated woodbased materials that are laminated multiple cut pieces or a woodbased material that is a veneer is characterized in that the multiple woodbased material layers include at least one high-density woodbased material layer, the remainder of the multiple woodbased material layers is a low-density woodbased material layer, and the high-density woodbased material layer has a higher density than the low-density woodbased material layer. As used herein, the “density of the woodbased material layer” refers to the density of a mat of cut pieces in the case where the woodbased materials are cut pieces, and refers to the density of a veneer if the woodbased material is a veneer.
- In this configuration, at least one of the multiple woodbased material layers is a high-density woodbased material layer, and the remainder of the woodbased material layers is a low-density woodbased material layer. High strength and high water resistance of the wood laminate material are thus implemented by the high-density woodbased material layer.
- In the case where the density of the woodbased material layer is increased, the density of the woodbased material need be increased only in the woodbased material layer required to have a high density, and it is not necessary to increase the density of the woodbased material in all the woodbased material layers. Press time with a press machine is therefore reduced accordingly and the pressure to be used is also reduced. This improves productivity and reduces or eliminates the risk of delamination when forming the wood laminate material.
- Moreover, since at least one of the woodbased material layers is a high-density woodbased material layer, the layer(s) to be used as a high-density woodbased material layer can be selected as necessary from the multiple woodbased material layers. Characteristics of the wood laminate material can thus be varied as desired by changing the position(s) of the high-density woodbased material layer(s).
- In the above configuration, the woodbased material layers located at both ends in the lamination direction of the woodbased material layers may be the high-density woodbased material layers.
- In this case, the woodbased material layers located at both ends in the lamination direction are the high-density woodbased material layers and have a higher density than the woodbased material layer(s) located in the remaining part. This improves flexural strength of the wood laminate material and also improves water resistance of the top and bottom parts of the wood laminate material.
- The woodbased material layer located in an intermediate part in the lamination direction of the woodbased material layers may be the high-density woodbased material layer.
- In this case, as opposed to the case described above, the woodbased material layer located in the intermediate part in the lamination direction of the woodbased material layers is the high-density woodbased material layer and has a higher density than the woodbased material layers located in the remaining part (at both ends in the lamination direction of the woodbased material layers). The density in the intermediate part is therefore increased. This allows the wood laminate material to have uniform density distribution in the lamination direction. Moreover, since the wood laminate material has the high-density woodbased material layer in its intermediate part in the thickness direction and the top and bottom parts of the wood laminate material have a low density, the risk of delamination when forming the wood laminate material is effectively reduced or eliminated and productivity is improved.
- The woodbased material layer located in a part other than the ends and a middle part in the lamination direction of the woodbased material layers may be the high-density woodbased material layer.
- In this configuration, the woodbased material layer located in the part other than the ends and the middle part in the lamination direction of the woodbased material layers is the high-density woodbased material layer, and the woodbased material layers located at the ends and in the middle part in the lamination direction have a low density. The pressure to be used to form the wood laminate material is thus reduced by the low-density woodbased material layers in the top and bottom parts of the wood laminate material, and nail pull resistance (force) of the wood laminate material is increased by the high-density woodbased material layer.
- Fibers of the woodbased materials may extend in the same direction in each woodbased material layer, and the fibers of the woodbased materials in adjoining ones of the woodbased material layers may extend in directions crossing or parallel to each other.
- As used herein, the expressions “fibers extend in the same direction” and “fibers extend in directions parallel to each other” are not limited to the case where the fibers of all the woodbased materials are oriented in the same direction, but define a concept including the case where the fibers of a part of the woodbased materials are tilted to some extent. The fibers of a part of the woodbased materials may be tilted by, e.g., about 20° with respect to a predetermined reference direction. Similarly, the expression “fibers extend in directions crossing each other” is not limited to the case where the fibers are oriented in directions perpendicular to each other. The fibers of a part of the woodbased materials may be tilted by, e.g., about 20° with respect to a direction perpendicular to the reference direction.
- According to this configuration, in the case where the fibers of the woodbased materials in adjoining ones of the woodbased material layers extend in directions crossing each other, the wood laminate material has high strength against forces acting in various directions, as compared to the case where the fibers extend in the same direction in all of the woodbased material layers. Especially, the larger the number of woodbased material layers is, the more significant the difference in strength due to the difference in fiber direction between the woodbased material layers is. In the case where the fibers are oriented in the same direction along the entire thickness in the lamination direction of the wood laminate material, the strength may vary depending on the direction in which a force is applied. However, this problem does not occur in the case where the fibers of the woodbased materials in adjoining ones of the woodbased material layers extend in directions crossing each other.
- On the other hand, in the case where the fibers of the woodbased materials in adjoining ones of the woodbased material layers extend in directions parallel to each other, namely in the case where the fiber directions of the woodbased materials are the same along the entire thickness in the lamination direction of the wood laminate material, the wood laminate material has high strength against a force acting in a specific direction.
- Of the multiple woodbased material layers, the fibers of the woodbased materials in the top and bottom woodbased material layers may extend in the same direction.
- Performance such as load resistance and impact resistance in the top part of the wood laminate material is therefore about the same as that in the bottom part of the wood laminate material. That is, this configuration allows the wood laminate material to have similar performance in its top and bottom parts. This is advantageous in that the user can use the wood laminate material without having to worry about which side is the top and which side is the bottom.
- The number of woodbased material layers may be odd. In this case, the wood laminate material is a laminate of the odd number of woodbased material layers. This configuration allows the wood laminate material to have similar performance in its top and bottom parts, as in the case described above.
- The multiple woodbased material layers may be laminated so that overall density distribution provided by the multiple woodbased material layers is plane symmetric with respect to a center in the lamination direction. Since the overall density distribution provided by the multiple woodbased material layers is plane symmetric with respect to the center in the lamination direction, the wood laminate material has similar performance in its top and bottom parts. The user can therefore use the wood laminate material without having to know which side is the top and which side is the bottom.
- The woodbased materials may be strands that are cut pieces. This implements a strand material having high strength and high water resistance or a strand material having high productivity and varied characteristics.
- A method for manufacturing a wood laminate material is characterized by including: a stacking step of stacking multiple woodbased materials, which are cut pieces or veneers, to form multiple woodbased material layers so that at least one of the multiple woodbased material layers is formed by a high-density woodbased material or high-density woodbased materials having a relatively higher density than the remainder of the woodbased material layers; and a forming step of compressing or compacting the multiple woodbased material layers formed in the stacking step.
- Since the woodbased material layers include a layer formed by the high-density woodbased material or high-density woodbased materials having a relatively higher density than the remainder of the woodbased material layers, density distribution in the lamination direction after the forming step can be adjusted, whereby a wood laminate material with desired characteristics can be produced. For example, density distribution in the lamination direction of the wood laminate material can be made substantially constant by inserting the woodbased material layer formed by the high-density woodbased material or high-density woodbased materials at an optimal position.
- As described above, according to the present invention, density distribution in the lamination direction of the wood laminate material, which is formed by stacking and laminating multiple woodbased material layers each formed by cut pieces or veneer, is adjusted so that the wood laminate material has substantially constant density distribution in the lamination direction. High strength and high water resistance can therefore be achieved. Moreover, the density distribution in the lamination direction is varied so that at least one of the multiple woodbased material layers is a high-density woodbased material layer having a higher density than the remainder of the woodbased material layers. Accordingly, only the woodbased material layer required to have high strength and high water resistance has a high density, and productivity is improved. Moreover, characteristics of the wood laminate material can be varied as desired by changing the layer that is to be a high-density woodbased material layer.
-
FIG. 1 is a schematic perspective view of a multi-layered structure of a strand board according to a first embodiment of the present invention. -
FIG. 2 is a schematic perspective view of a first example of a strand board according to a second embodiment of the present invention. -
FIG. 3 is a schematic sectional view showing a laminate of strand layers in the first example of the strand board according to the second embodiment. -
FIG. 4 is a sectional view corresponding toFIG. 3 , showing a second example of the strand board according to the second embodiment. -
FIG. 5 is a sectional view corresponding toFIG. 3 , showing a third example of the strand board according to the second embodiment. -
FIG. 6 is a sectional view corresponding toFIG. 3 , showing a fourth example of the strand board according to the second embodiment. -
FIG. 7 is a sectional view corresponding toFIG. 3 , showing a fifth example of the strand board according to the second embodiment. -
FIG. 8 is a sectional view corresponding toFIG. 3 , showing a sixth example of the strand board according to the second embodiment. -
FIG. 9 is a table illustrating specific configurations of the first to sixth examples of the strand board according to the second embodiment. -
FIG. 10 is a sectional image of a strand board of Example 1 of the first embodiment. -
FIG. 11 is a table showing the test results of Examples 1, 2 and Comparative Examples 1, 2. -
FIG. 12 is a graph showing density distribution in the strand board of Example 1 according to the first embodiment, in which the uniform short-dashed line represents an average density of the woodbased material layers in the thickness direction (lamination direction) and the long-dash short-dash line represents a constant density value for reference. -
FIG. 13 is a graph showing density distribution in a strand board of Comparative Example 1 as compared to the first embodiment, in which the uniform short-dashed line represents an average density of the woodbased material layers in the thickness direction (lamination direction) and the long-dash short-dash line represents a constant density value for reference. -
FIG. 14 is a table showing the results of a bending test for Examples 1, 2 and Comparative Example 1 of the second embodiment, along with their other physical properties. -
FIG. 15 is a graph showing density distribution in the thickness direction (lamination direction) of Examples 1, 2 and Comparative Example 1 according to the second embodiment. -
FIG. 16 is a table showing the results of a bending test and a boiling test for Example 3 and Comparative Example 2, along with their other physical properties. -
FIG. 17 is a graph showing density distribution in the thickness direction (lamination direction) of Example 3 and Comparative Example 2 according to the second embodiment. -
FIG. 18 is a table showing the results of a bending test and a boiling test for Example 4 and Comparative Example 3, along with their other physical properties. -
FIG. 19 is a table showing the result of a nail pull test for Example 4 and Comparative Example 4, along with their other physical properties. -
FIG. 20 is a graph showing density distribution in the thickness direction (lamination direction) of Example 4 and Comparative Example 3 according to the second embodiment. - Embodiments of the present invention will be described in detail below with reference to the accompanying drawings. The following description of the preferred embodiments is merely exemplary in nature and is not intended in any way to limit the invention, its applications or uses. Specific numerical values in the embodiments are shown merely by way of example in order to facilitate understanding of the invention and are not intended to limit the scope of the invention and materials of the invention.
-
FIG. 1 schematically shows a strand board B as a wood laminate material according to a first embodiment of the present invention. - As shown in
FIG. 1 , the strand board B has an odd number of (inFIG. 1 , five) strand layers 1, 1, . . . as woodbased material layers, and all of the strand layers 1, 1, . . . have the same thickness. That is,FIG. 1 shows an example in which, with the upper side inFIG. 1 being the top and the lower side being the bottom, the thickness w1 of the top and bottom strand layers 1, 1 is the same as the thicknesses w2, w3, w2 of the threeintermediate strand layers strand layers 1 is not limited to five. The number ofstrand layers 1 may be four or less or six or more. - Each
strand layer 1 is a mat made of laminatedmultiple strands strands multiple strand layers - For example, the
strands 5 are strands or flakes that are about 150 to 200 millimeters long in the fiber direction, about 15 to 25 millimeters wide, and about 0.3 to 2 millimeters thick. - Wood species that are used for the
strands 5 are not particularly limited. For example, tropical wood species or broadleaf trees may be used, or other wood species may be used. Specific examples include Cedar (Cryptomeria japonica), Cypress (Chamaecyparis), sort of firs such as Douglas fir (Pseudotsuga menziesii), Acacia (Acacia spp.), Aspen (Populus spp.), Poplar (Populus spp.), Pine (Pinus spp.) (Hard pine (Pinus spp.), Soft pine (Pinus spp.), Radiata pine (Pinus radiata), etc.), Birch (Betula spp.), and Rubber tree (Rubber wood (Hevea brasiliensis)). However, the wood species that are used for thestrands 5 are not limited to these, and various other wood species may be used. Examples of the various other wood species include: Japanese wood species such as Sawara cypress (Chamaecyparis pisifera), Japanese elkhorn cypress (Thujopsis dolabrata), Japanese nutmeg-yew (Torreya nucifera), Southern Japanese hemlock (Tsuga sieboldii), Podocarp (Podocarpus macrophyllus), Pinus spp., Princess tree (Paulownia tomentosa), Maple (Acer spp.), Birch (Betula spp.) (Japanese white birch (Betula platyphylla)), Chinquapin (Castanopsis spp.), Japanese beech (Fagus spp.), Live oak (Quercus spp.), Abies firma, Sawtooth oak (Quercus acutissima), Oak (Quercus spp.), Camphor tree (Cinnamomum camphora), and Japanese zelkova (Zelkova serrata); North American wood species such as Port Orford cedar (Chamaecyparis lawsoniana), Yellow cedar (Callitropsis nootkatensis), Western redcedar (Thuja plicata), Grand fir (A. grandis), Noble fir (A. procera), White fir (A. concolor), Spruce (Picea spp.), Western hemlock (Tsuga heterophylla), and Scots pine (Pinus sylvestris); tropical hardwood species such as Agathis (Agathis spp.), Terminalia (Terminalia spp.), Lauan (Shorea spp.), Meranti (Shorea sect.), Sengon laut (A. falcataria), Jongkong (Dactylocladus stenostachys), Kamerere (Eucalyptus deglupta), Kalampayan (Anthocephalus chinensis), Amberoi (Pterocymbium beccarii), Yemane (Gmelina arborea), Teak (Tectona grandis), and Apitong (Dipterocarpus spp.); and other foreign wood species such as Balsa (Ochroma pyramidale), Cedro (Cedrela odorata), Mahogany (Swietenia spp.), Lignum-vitae (Guaiacum spp.), Acacia mangium, Aleppo pine (Pinus halepensis), Bamboo, Sorghum (Sorghum nervosum Bess.), and Kamerere (Eucalyptus deglupta). Any material can be used. - Regarding physical properties of the
strands 5, thestrands 5 preferably have a density of about 300 to 800 kg/m3, more preferably 430 to 700 kg/m3. If the density is less than 300 kg/m3, a multi-layered mat with a larger thickness is required to form a strand board B of the same density and strength, and a higher pressure need be used for hot pressing in a press process described later. - The
strands 5 may have a density higher than 800 kg/m3, but it is difficult to obtainsuch strands 5. Namely, ifstrands 5 having a density higher than 800 kg/m3 can be easily obtained, the upper limit of the density is not limited to 800 kg/m3 and may be higher than 800 kg/m3. - The moisture content of each
strand 5 is preferably about 2 to 20%, more preferably 2 to 8%. If the moisture content is less than 2%, it takes more time to soften thestrands 5 in the hot pressing of the press process. Namely, the press time is increased, which may cause reduction in strength. - If the moisture content of the
strands 5 is higher than 20%, it takes more time to heat and compress thestrands 5 in the hot pressing, and thestrands 5 tend to be blown. Moreover, curing of an adhesive is inhibited, which may cause reduction in strength. - In each
strand layer 1, thestrands strands FIG. 1 , the fibers of thestrands strand layer 1 need not necessarily extend in exactly the same direction. In other words, the fiber directions of the orientedstrands strands - The
multiple strand layers strands FIG. 1 , the fiber direction of thestrands FIG. 1 ) is the same as that of thestrands FIG. 1 ). - The first embodiment is characterized in that the strand board B has substantially constant density distribution in the lamination direction of the strand layers 1 (the thickness direction of the strand board B), namely the direction in which the strand layers 1 are laminated. Specifically, the
multiple strand layers multiple strand layers - Next, a method for manufacturing a strand board B according to the first embodiment will be described. This manufacturing method includes a strand producing process, a strand pretreatment process, an adhesive coating process, a stacking process (mat forming process), and a press process.
- (Strand Producing Process)
- In the method for manufacturing a strand board B, the strand producing process is first performed in which a large number of
strands strands strands - (Strand Pretreatment Process)
- After the strand producing process, it is preferable that a large number of
strands - The physical treatment method is a method in which the
strands 5 are physically compressed. Examples of the physical treatment method include roll pressing, beating, and flat press pressing. The roll pressing is a linear compression method in which, although not shown in the figures, a large number ofstrands strands strands strands 5 are thus compressed without being smashed, whereby high-density strands 5 are produced. - The beating is a point compression method in which, as in metal forging,
strands 5 are compressed and deformed by hitting with multiple continuously installed spring hammers etc. As in the roll pressing, thestrands 5 are thus compressed without being smashed, whereby high-density strands 5 are produced. - The flat press pressing is a surface compression method in which
strands strands 5 are compressed without being smashed, whereby high-density strands 5 are produced. - The high-frequency treatment method is a method in which
strands 5 as dielectrics (nonconductors) are irradiated with high-frequency electromagnetic waves (high-frequency waves) between electrodes etc. and thus dielectrically heated from the inside and softened. This method allows low-pressure pressing using a low pressure to be performed in the later press process without increasing the density of thestrands 5 as in the above physical treatment method. - The high-temperature high-pressure treatment method is a method in which
strands 5 are placed in a pressure vessel where thestrands 5 are subjected to high temperature and high pressure so that cell walls of the strands 5 (woodbased materials) are damaged and thestrands 5 are softened. For example, this method is performed at a temperature of 180° C. and a pressure of about 10 Bar for about two minutes. This method also allows low-pressure pressing using a low pressure to be performed in the later press process without increasing the density of thestrands 5 as in the above physical treatment method. - The high-water pressure treatment method is a method in which
strands 5 are uniformly formed within a mesh material such as metal wire mesh and the surfaces of thestrands 5 are finely scratched by high-pressure water of, e.g., about 200 MPa through the mesh material. This produces fine fractures in thestrands 5. Thesoftened strands 5 are thus obtained. - The repeated deaeration and dehydration treatment method is a method in which
strands 5 are first saturated with water and then placed in a batch type of vessel, and with the vessel being evacuated to vacuum, moisture is removed from thestrands 5 to facilitate damage to cell walls of the strands 5 (woodbased materials) and thus soften thestrands 5. This method also allows low-pressure pressing using a low pressure to be performed in the later press process without increasing the density of thestrands 5 as in the above physical treatment method. - The chemical treatment method is a method in which, for example, sodium hydroxide etc. is added to
strands 5 for alkaline treatment to facilitate plasticization of thestrands 5 themselves and thus soften thestrands 5. This method also allows low-pressure pressing using a low pressure to be performed in the later press process without increasing the density of thestrands 5 as in the above physical treatment method. - In the high-frequency treatment method, the high-temperature high-pressure treatment method, the high water pressure treatment method, the repeated deaeration and dehydration treatment method, and the chemical treatment method, the state of the
strands 5 after the treatment is maintained by drying thestrands 5 as necessary after the treatment. - (Adhesive Coating Process)
- After a large number of
strands strands - (Stacking Process)
- Thereafter, the stacking process (mat forming process) is performed in which a large number of
strands - Specifically, with a mat forming machine etc., a large number of
strands - After the strand mat with a certain thickness is thus formed,
strands strands strands - Subsequently, an additional strand mat is repeatedly stacked in a similar manner until the stack has a desired number of layers (e.g., five layers). At this time, the strand mats are stacked so that the fiber directions of the
strands FIG. 1 , in the case of the strand board B having the fivestrand layers - The number of strand mats in the multi-layered mat is determined based on the number of layers in the strand board B. Accordingly, the number of strand mats in the multi-layered mat may be four or less or six or more.
- The density of the
strands strand layer 1 may be either about the same or different between or among themultiple strand layers - (Press Process)
- After the multi-layered mat is thus formed by stacking multiple strand mats, hot pressing is performed at a predetermined pressure and temperature with a hot press machine to compress or compact the multi-layered mat. This hot pressing is performed at a pressure of, e.g., 2 to 4 N/mm2 for, e.g., about 10 to 20 minutes. The press time varies depending on the thickness of the strand board B (finished product). Accordingly, in some cases, it may take less than 10 minutes to complete the hot pressing, and in other cases, it may take 20 minutes or more to complete the hot pressing. Pre-heat treatment with a heater may be performed before the hot pressing with the hot press machine.
- A strand board B having a density of 750 to 950 kg/m3 and flexural strength of 80 to 150 N/mm2 is thus formed as a laminate by these processes.
- In the first embodiment, the pressure for the hot pressing in the press process is as low as 2 to 4 N/mm2. A high density, high strength strand board B can thus be produced without using a special high pressure press machine.
- In the strand board B, the fiber direction of the
strands top strand layer 1 of the strand board B is the same as that of thestrands bottom strand layer 1 of the strand board B. Performance such as load resistance and impact resistance in the top part of the strand board B is therefore about the same as that in the bottom part of the strand board B. That is, this configuration allows the strand board B to have similar performance in its top and bottom parts. This is advantageous in that the user can use the strand board B without having to worry about which side is the top and which side is the bottom. - The
multiple strand layers - Density distribution in the thickness direction of the strand board B formed by the strand layers 1, 1, . . . is plane symmetric. This allows the strand board B to have similar performance in its top and bottom parts. The user can therefore use the strand board B without having to know (worry about) which side is the top and which side is the bottom.
- In the case where the number of
strand layers - As described above, it is preferable that the
strands strands - Specifically, the
strands strands - The substantial moisture content and density of the
strands strands strands -
FIGS. 2 to 8 shows a second embodiment of the present invention (the same portions as those inFIG. 1 are denoted with the same reference characters and detailed description thereof will omitted).FIGS. 2 to 8 show examples of a strand board B that is a wood laminate material according to the second embodiment.FIGS. 2 and 3 show a first example of the strand board B.FIG. 4 shows a second example,FIG. 5 shows a third example,FIG. 6 shows a fourth example,FIG. 7 shows a fifth example, andFIG. 8 shows a sixth example. - In each of the first to sixth examples, the strand board B includes strand layers 1, 1, . . . as multiple (an odd number of) woodbased material layers. Each
strand layer 1 is made of a mat of a large number ofstrands strands multiple strand layers - In the second embodiment, the upper side in
FIGS. 3 to 8 is the top of the strand board B and the lower side is the bottom thereof, and the strand layers 1, 1, . . . are sequentially numbered from top to bottom as thefirst strand layer 1, thesecond strand layer 1, thethird strand layer 1, . . . . The strand layers 1, 1, . . . are thus marked with circled numbers in theFIGS. 3 to 8 . - In the second embodiment, the
strands 5 preferably have a density of about 300 to 1100 kg/m3. If the density is less than 300 kg/m3, a multi-layered mat with a larger thickness is required to form high-density strand layers 1 a, and a higher pressure need be used for hot pressing in a press process. - The
strands 5 may have a density higher than 1100 kg/m3, but it is difficult to obtainsuch strands 5. Namely, ifstrands 5 having a density higher than 1100 kg/m3 can be easily obtained, the upper limit of the density is not limited to 1100 kg/m3 and may be higher than 1100 kg/m3. - In the second embodiment as well, the
strands strand layer 1 are oriented such that the fibers of thestrands FIG. 2 , the fibers of thestrands strand layer 1 need not necessarily extend in the same direction. Namely, the fiber directions of the orientedstrands strand layer 1 do not have to be parallel to each other. In other words, the fibers of a part of thestrands strand layer 1 may be tilted to some extent with respect to a predetermined reference direction. For example, a part of thestrands strand layer 1 may be oriented so as to be tilted by about 20° with respect to the reference direction. - The second embodiment is characterized in that, unlike in the first embodiment, at least one of the odd number of
strand layers density strand layer 1 a having a density higher than the remainingstrand layers 1 b, and the remainingstrand layers 1 b are low-density strand layers. The “density of the strand layer” as used in the second embodiment does not refer to the density of thestrands 5 but refers to the density of thestrand layer 1 itself made of a mat of thestrands 5. - Each example of the strand board B will be specifically described in detail. In
FIGS. 3 to 8 , the layers shaded with dense dots represent the high-density strand layers 1 a and the layers shaded with sparse dots represent the low-density strand layers 1 b. -
FIGS. 2 and 3 show the first example of the strand board B according to the second embodiment. This strand board B has five strand layers, namely first to fifth strand layers 1, 1, . . . . These strand layers 1, 1, . . . are stacked and laminated such that the fibers of thestrands strands first strand layer 1 located at the top of the strand board B, namely in theuppermost strand layer 1 inFIG. 3 , is the same as that of thestrands fifth strand layer 1 located at the bottom of the strand board B, namely in thelowermost strand layer 1 inFIG. 3 . - Two of the five
strand layers density strand layers 1 a having a density higher than the other three strand layers, which are low-density strand layers 1 b. The two high-density strand layers density strand layers density strand layers 1 b is about the same as that of common strand boards. - Specifically, the
first strand layer 1 located at the top of the strand board B, thefifth strand layer 1 located at the bottom of the strand board B, and thethird strand layer 1 located in the middle part in the thickness direction of the strand board B are low-density strand layers 1 b. Both the second and fourth strand layers 1, 1 located in the parts of the strand board B other than the top and bottom and the middle part in the thickness direction of the strand board B are high-density strand layers 1 a. - The five
strand layers density strand layers 1 b) is, e.g., 25% of the total thickness of the strand board B, the thickness of each of the second and fourth strand layers 1, 1 (high-density strand layers 1 a) is, e.g., 20% of the total thickness of the strand board B, and the thickness of the third strand layer 1 (low-density strand layer 1 b) is, e.g., 10% of the total thickness of the strand board B. The total thickness of the high-density strand layers 1 a is therefore, e.g., 40% of the total thickness of the strand board B. The fivestrand layers - A method for manufacturing a strand board B according to the second embodiment will be described. This manufacturing method is applied not only to the strand board B of the first example but also to the strand boards B of the second to sixth examples.
- The manufacturing method of the second embodiment is basically the same as the first embodiment. Description of the same parts as those in the first embodiment is omitted, and only the differences will be described in detail.
- This manufacturing method has a strand producing process, a strand pretreatment process, an adhesive coating process, a stacking process (mat forming process), and a press process. Of these processes, the strand pretreatment process, the adhesive coating process, and the press process are the same as those of the first embodiment.
- In the second embodiment, when forming a multi-layered mat in the mat forming process by stacking another strand mat on top of a strand mat, the strand mat that is to be a high-
density strand layer 1 a is formed by thestrands 5 having a density higher than thestrands 5 of the strand mat that is to be a low-density strand layer 1 b is. This allows both high-density and low-density strand layers - For example, the following two kinds of strands are prepared in advance in the first process of the manufacturing method, namely in the strand producing process: strands with densities in a common range; and strands with densities higher than the common range. The strands with densities in the common range are used as the
strands 5 of the strand mat that is to be a low-density strand layer 1 b. The strands with densities higher than the common range as a result of compression etc. may be used as thestrands 5 of the strand mat that is to be a high-density strand layer 1 a. - The wood species etc. of the
strands 5 may be different between the strand mat that is to be a high-density strand layer 1 a and the strand mat that is to be a low-density strand layer 1 b. A wood species having a higher density may be used to produce thestrands 5 of the strand mat that is to be a high-density strand layer 1 a than a wood species that is used to produce thestrands 5 of the strand mat that is to be a low-densitylayer strand layer 1 b. - After the multi-layered mat is formed, the press process is performed in which hot pressing is performed at a predetermined pressure and temperature with a hot press machine to compress or compact the multi-layered mat. In the press process, the hot pressing is performed at a pressure of, e.g., 2 to 4 N/mm2 as in the first embodiment, but the press time is, e.g., about 10 to 30 minutes. In the second embodiment as well, the press time varies depending on the thickness of the strand board B (finished product). Accordingly, in some cases, it may take less than 10 minutes to complete the hot pressing, and in other cases, it may take 30 minutes or more to complete the hot pressing. Pre-heat treatment with a heater may be performed before the hot pressing with the hot press machine.
- As described above, it is preferable that the
strands 5 produced in the strand producing process have a density of 300 to 1100 kg/m3 and a moisture content of 2 to 8%. However, thestrands 5 produced in the strand producing process can be used even if their properties are out of these preferred ranges. -
FIG. 4 shows the second example of the strand board B. As in the first example, this strand board B has five strand layers, namely first to fifth strand layers 1, 1, . . . . These strand layers 1, 1, . . . are stacked and laminated such that the fibers of thestrands 5 in adjoining ones of the strand layers 1 extend in directions perpendicular to each other. The fiber direction of thestrands first strand layer 1 located at the top of the strand board B, namely in theuppermost strand layer 1 inFIG. 4 , is the same as that of thestrands fifth strand layer 1 located at the bottom of the strand board B, namely in thelowermost strand layer 1 inFIG. 4 . - Two of the five
strand layers density strand layers 1 a, and the other three strand layers are low-density strand layers 1 b having a density lower than the high-density strand layers 1 a. The two high-density strand layers density strand layers 1 a of the first example. The three low-density strand layers density strand layers 1 b of the first example (because the product density of the strand board B is lower than in the first example). - Unlike in the first example, the
first strand layer 1 located at the top of the strand board B and thefifth strand layer 1 located at the bottom of the strand board B are high-density strand layers 1 a. The remaining strand layers, namely the second to fourth strand layers 1, 1, . . . located in the intermediate part in the thickness direction of the strand board B, are low-density strand layers 1 b. - The five
strand layers strand layer 1 is, e.g., 20% of the total thickness of the strand board B. The total thickness of the high-density strand layers 1 a is therefore, e.g., 40% of the total thickness of the strand board B. The fivestrand layers -
FIG. 5 shows the third example of the strand board B. Unlike in the second example, the strand board B has seven strand layers, namely first to sevenstrand layers strands 5 in adjoining ones of the strand layers 1 extend in directions perpendicular to each other. The fiber direction of thestrands first strand layer 1 located at the top of the strand board B, namely in theuppermost strand layer 1 inFIG. 5 , is the same as that of thestrands seventh strand layer 1 located at the bottom of the strand board B, namely in thelowermost strand layer 1 inFIG. 5 . - Two of the seven
strand layers density strand layers 1 a. The other five strand layers are low-density strand layers 1 b having a density lower than the high-density strand layers 1 a. The two high-density strand layers density strand layers 1 a of the first example. The five low-density strand layers density strand layers 1 b of the first example (because the product density of the strand board B is lower than in the first example). - Specifically, the
first strand layer 1 located at the top of the strand board B and theseventh strand layer 1 located at the bottom of the strand board B are high-density strand layers 1 a. The remaining strand layers, namely the second to sixth strand layers 1, 1, . . . located in the intermediate part in the thickness direction of the strand board B, are low-density strand layers 1 b. - The seven
strand layers density strand layers 1 a) is, e.g., 15% of the total thickness of the strand board B, the thickness of each of the second, third, fifth, and sixth strand layers 1, 1, . . . (low-density strand layers 1 b) is, e.g., 15% of the total thickness of the strand board B, and the thickness of the fourth strand layer 1 (low-density strand layer 1 b) is, e.g., 10% of the total thickness of the strand board B. The total thickness of the high-density strand layers 1 a is therefore, e.g., 30% of the total thickness of the strand board B. The sevenstrand layers -
FIG. 6 shows the fourth example of the strand board B. Unlike in the second and third examples, this strand board B has three strand layers, namely first to third strand layers 1, 1, . . . . These strand layers 1, 1, . . . are stacked and laminated such that the fibers of thestrands 5 in adjoining ones of the strand layers 1 extend in directions perpendicular to each other. The fiber direction of thestrands first strand layer 1 located at the top of the strand board B, namely in theuppermost strand layer 1 inFIG. 6 , is the same as that of thestrands third strand layer 1 located at the bottom of the strand board B, namely in thelowermost strand layer 1 inFIG. 6 . - One of the three
strand layers density strand layer 1 a. The other two strand layers are low-density strand layers 1 b having a density lower than the high-density strand layer 1 a. The density of the high-density strand layer 1 a is, e.g., about 800 kg/m3 (average value), which is lower than that of the high-density strand layers 1 a of the second example. The two low-density strand layers density strand layers 1 b of the first example. - Specifically, only the
second strand layer 1 located in the middle part (intermediate part) in the thickness direction of the strand board B is a high-density strand layer 1 a, and the first and third strand layers 1, 1 located at the top and bottom of the strand board B are low-density strand layers 1 b. - The three
strand layers density strand layers 1 b) is, e.g., 20% of the total thickness of the strand board B, and the thickness of the second strand layer 1 (high-density strand layer 1 a) is, e.g., 60% of the total thickness of the strand board B. The thickness of the high-density strand layer 1 a is therefore, e.g., 60% of the total thickness of the strand board B. The threestrand layers -
FIG. 7 shows the fifth example of the strand board B. As in the fourth example, this strand board B has three strand layers, namely first to third strand layers 1, 1, . . . . Unlike in the first to fourth examples, thesestrand layers strands 5 in adjoining ones of the strand layers 1 extend in directions parallel to each other. That is, the fiber direction of thestrands first strand layer 1 located at the top of the strand board B, namely in theuppermost strand layer 1 inFIG. 7 , is the same as that of thestrands third strand layer 1 located at the bottom of the strand board B, namely in thelowermost strand layer 1 inFIG. 7 . The fiber direction of thestrands second strand layer 1 located in the middle part in the thickness direction of the strand board B is also the same as that of thestrands - Unlike in the fourth example, two of the three
strand layers density strand layers 1 a. The remaining one strand layer is a low-density strand layer 1 b. The two high-density strand layers density strand layer 1 a of the fourth example. The density of the low-density strand layer 1 b is lower than that of the low-density strand layers 1 b of the first example (because the product density of the strand board B is lower than in the first example). - Specifically, the first and third strand layers 1, 1 located at the top and bottom of the strand board B are high-
density strand layers 1 a, and only thesecond strand layer 1 located in the middle part in the thickness direction of the strand board B is a low-density strand layer 1 b. - The three
strand layers density strand layers 1 a) is, e.g., 40% of the total thickness of the strand board B, and the thickness of the second strand layer 1 (low-density strand layer 1 b) is, e.g., 20% of the total thickness of the strand board B. The total thickness of the high-density strand layers 1 a is therefore, e.g., 80% of the total thickness of the strand board B. The threestrand layers -
FIG. 8 shows the sixth example of the strand board B. As in the first example, this strand board B has five strand layers, namely first to fifth strand layers 1, 1, . . . . These strand layers 1, 1, . . . are stacked and laminated such that the fibers of thestrands 5 in adjoining ones of the strand layers 1 extend in directions perpendicular to each other. The fiber direction of thestrands first strand layer 1 located at the top of the strand board B, namely in theuppermost strand layer 1 inFIG. 8 , is the same as that of thestrands fifth strand layer 1 located at the bottom of the strand board B, namely in thelowermost strand layer 1 inFIG. 8 . - Three of the five
strand layers density strand layers 1 a. The other two strand layers are low-density strand layers 1 b having a density lower than the high-density strand layers 1 a. The three high-density strand layers density strand layers 1 a of the first example. The two low-density strand layers density strand layers 1 b of the first example. - Specifically, as opposed to the second example, the second to fourth strand layers 1, 1, . . . located in the intermediate part in the thickness direction of the strand board B are high-
density strand layers 1 a. The remaining strand layers, namely thefirst strand layer 1 located at the top of the strand board B and thefifth strand layer 1 located at the bottom of the strand board B, are low-density strand layers 1 b. - The five
strand layers density strand layers 1 b) is, e.g., 30% of the total thickness of the strand board B, the thickness of each of the second and fourth strand layers 1, 1 (high-density strand layers 1 a) is, e.g., 15% of the total thickness of the strand board B, and the thickness of the third strand layer 1 (high-density strand layer 1 a) is, e.g., 10% of the total thickness of the strand board B. The total thickness of the high-density strand layers 1 a is therefore, e.g., 60% of the total thickness of the strand board B. The fivestrand layers -
FIG. 9 shows specific configurations of the first to sixth examples. - In the second embodiment, the strand board B has
multiple strand layers multiple strand layers density strand layer 1 a having a density higher than theother strand layers density strand layer 1 a provides high strength and high water resistance of the strand board B, whereby the strand board B having high strength and high water resistance is obtained. - In the case where the density of the
strand layer 1 is increased to use thisstrand layer 1 as a high-densitystrange layer 1 a in the strand board B, the density of only thestrands 5 of this high-density strand layer 1 a need be increased, and it is not necessary to increase the density of thestrands 5 of all the strand layers 1, 1, . . . . The press time with a press machine is therefore reduced accordingly and the pressure to be used is also reduced. This improves productivity and reduces or eliminates the risk of delamination in the press process. - Moreover, one to three of the odd number of
strand layers density strand layers 1 a. Accordingly, as shown in the first to sixth examples, a layer(s) to be used as a high-density strand layer(s) 1 a can be selected from themultiple strand layers - That is, in, e.g., the first example shown in
FIGS. 2 and 3 (the sixth example shown inFIG. 8 is substantially similar to this configuration), the second and fourth strand layers 1, 1 located in the parts of the strand board B other than the top and bottom and the middle part in the thickness direction of the strand board B are high-density strand layers 1 a, and the remaining layers, namely the first, third, and fifth strand layers 1, 1, . . . located at the top and bottom and in the middle part in the thickness direction of the strand board B, are low-density strand layers 1 b. This structure is advantageous in that the use of the low-density strand layers 1 b in the top and bottom parts reduces the pressure to be used in the press process and the high-density strand layers 1 a provide increased nail pull resistance (force) for a nail that is a fastener to be driven into the strand board B. Especially, the sixth example shown inFIG. 8 further improves productivity. - In the second example shown in
FIG. 4 and the third example shown inFIG. 5 , the strand layers 1, 1 located at the top and bottom of the strand board B are high-density strand layers 1 a, and the strand layers 1, 1, . . . located in the intermediate part of the strand board B are low-density strand layers 1 b. In this structure, the high-density strand layers 1 a in the top and bottom parts increase flexural strength of the strand board B and improve water resistance in the top and bottom parts of the strand board B. - In the fourth example shown in
FIG. 6 , thestrand layer 1 located in the intermediate part in the thickness direction of the strand board B is a high-density strand layer 1 a, and the strand layers 1, 1 located in the remaining part of the strand board B are low-density strand layers 1 b. In this structure, the strand board B has a higher density in its intermediate part due to the high-density strand layer 1 a, and the strand board B has uniform overall density distribution in the thickness direction. Since the high-density strand layer 1 a is formed in the intermediate part in the thickness direction of the strand board B and the low-density strand layers 1 b are formed in the top and bottom parts of the strand board B, this structure effectively reduces or eliminates the risk of delamination in the press process and improves productivity. - In the fifth example shown in
FIG. 7 , thestrand layer 1 located in the middle part in the thickness direction of the strand board B is a high-density strand layer 1 a, and the first and third strand layers 1, 1 located at the top and bottom of the strand board B are low-density strand layers 1 b. Moreover, the fiber direction of thestrands - In the first to fourth examples of the strand board B of the second embodiment, the fibers of the
strands strand layer 1, and the fibers of thestrands 5 in adjoining ones of the strand layers 1 extend in directions perpendicular to each other. This structure has high strength against forces acting in various directions as compared to the case where the fibers of thestrands 5 extend in the same direction in all of the strand layers 1, 1, . . . as in the fifth example. The larger the number ofstrand layers 1 is, the more significant the difference in strength of the strand board B due to the difference in fiber direction between the strand layers 1 is. - On the other hand, in the case where the
strands - In the second embodiment as well, density distribution in the thickness direction of the strand board B formed by the strand layers 1, 1, . . . is plane symmetric. This allows the strand board B to have similar performance in its top and bottom parts. The user can therefore use the strand board B without having to know which side is the top and which side is the bottom.
- Moreover, the strand board B has an odd number of
strand layers - The present invention is not limited to the first and second embodiments. In the first embodiment, the thicknesses w1 to w3 of the
multiple strand layer layer 1 can be set as desired. - For example, the
multiple strand layers strand layer 1 gradually increases from themiddle strand layer 1 in the thickness direction (lamination direction) of the strand board B to the top and bottom strand layers 1. That is, the thicknesses of themultiple strand layers FIG. 1 may have a relation of w1>w2>w3. The strand layers 1 on the outer sides (top and bottom) of the strand board B, which are more likely to be subjected to load and impact and are more susceptible to humidity etc., have a larger thickness than the remaining strand layer(s) 1. This allows the strand board B to have improved performance regarding influences from the external environment. - One or more of the strand layers 1, 1, . . . may have a different thickness from the remaining strand layer(s) 1. For example, the thickness w1 of the top and bottom strand layers 1, 1 may be different from the thicknesses w2, w3 of the three
intermediate strand layers strand layers - In the first embodiment, the fiber direction of the
strands strand layer 1 is perpendicular to that of thestrands strand layer 1. However, the present invention is not limited to this. For example, the fiber direction of thestrands multiple strand layers strands layer 1. For example, in the case where the strand layers 1, 1 that are different in form of thestrands strands strands strand layers - In the first embodiment, the density or thickness of the strands 5 (woodbased materials) may be different between or among the strand layers 1, 1, . . . of the strand board B.
- For example, in the stacking process (mat forming process), the multiple mats of
strands strands 5 of the mat gradually increases from the top and bottom strand layers 1 to themiddle strand layer 1 in the thickness direction of the strand board B. When the multi-layered mat is pressed in the press process, the relative density of theouter strand layers 1 that are directly subjected to the pressure of a press machine typically tends to become higher than that of the inner strand layer(s) 1. Since the relative density of thestrands 5 of the inner strand layer(s) 1 is thus made higher than that of thestrands 5 of theouter strand layers 1 prior to the pressing, the strand board B formed by the pressing has uniform density distribution in the lamination direction. In this case, the wood species of thestrands 5 may be different or the same between or among the strand layers 1. - That is, in a part of the strand layers 1 or all of the strand layers 1, the wood species, thickness, density, etc. of the
strands 5 of thestrand layer 1 can be selected as appropriate according to required characteristics, cost, etc. - In the stacking process (mat forming process) of the first embodiment, the strand mats may be stacked so that at least one of the
multiple strand layers strands strand layer 1 is a layer formed by thestrands 5 having a relatively higher density than the other strand layers 1. Specifically, in the case where the strand board B has, e.g., an odd number ofstrand layers 1, the strand mats may be stacked so that an odd-numberedstrand layer 1 from the top or bottom of the strand board B is formed by the high-density strands 5. The strand mats may be stacked so that a specific one (at least one) of themultiple strand layers density strands multiple strand layers 1 that are formed by the high-density strands strand layers - In the second embodiment, the strand board B has an odd number of
strand layers strand layers - In the second embodiment, the fibers of the
strands 5 extend in the same direction in each strand layers 1, and the fiber directions of thestrands strands 5 of eachstrand layer 1 may be determined as desired. - The first and second embodiments are described with respect to the strand board B formed by stacking and laminating the mats of the
strands 5 into the shape of a board. However, the present invention is not limited to this strand board B. For example, multiple strand layers having a rectangular section (in the shape of squared timber) and having no significant difference between their thickness and width may be stacked and laminated. In this case, a strand material (wood laminate material) can be used as a joist, pillar, etc. formed by stacking and laminating multiple strand layers. - The first and second embodiments are examples of the strand board B formed by stacking and laminating the
multiple strand layers multiple strands strands 5. That is, in the case of plywood and LVL, each woodbased material layer is formed by at least one veneer. - In the case where the wood laminate material is plywood or LVL, a common manufacturing method is used to manufacture plywood or LVL. Specifically, green wood such as logs or thinnings is cut with a cutting machine to produce veneers. Multiple veneers are then stacked together with an adhesive therebetween such that the fiber directions of adjoining ones of the veneers are the same in the case of LVL and the fiber directions of adjoining ones of the veneers are perpendicular to each other in the case of plywood. Subsequently, the staked veneers are formed by cold pressing or hot pressing to cure the adhesive.
- In the case where density distribution in the lamination direction of the woodbased material layers is to be made substantially uniform as in the first embodiment, the density, thickness, etc. of each veneer are adjusted before, e.g., the stacked veneers are formed in the press process.
- In the case where the woodbased material layers consist of a combination of high-density and low-density woodbased material layers as in the second embodiment, the density of the woodbased material or woodbased materials forming each woodbased material layer is made higher in a part of the woodbased material layers than in the remainder of the woodbased material layers by wood species etc. before, e.g., the stacked veneers are formed in the press process.
- Next, specific examples of the strand boards according to the first and second embodiments will be described. It should be noted that “examples” and “comparative examples” of the first embodiment are different from “examples” and “comparative examples” of second embodiments even though their numbers are the same. The examples and the comparative examples are specified for each embodiment.
- Mats of a large number of cypress strands were stacked into a multi-layered mat having five strand layers and a thickness of 37 mm. The strands were 150 to 200 mm long in the fiber direction, 15 to 25 mm wide, and 0.8 to 2 mm thick and had a density of 500 to 600 kg/m3. The multi-layered mat was then subjected to hot pressing at 140° C. and 4 N/mm2 for 10 minutes, whereby a strand board with a density of 818 kg/m3 and a thickness of 12.4 mm was obtained. This strand board was used as Example 1.
-
FIG. 10 shows an image of Example 1. InFIG. 10 , reference character “B” indicates the strand board and “1” indicates the strand layers.FIG. 11 shows the results of a bending test, a dimensional change test, and a water absorption test for Example 1.FIG. 12 shows the density distribution in the thickness direction (lamination direction) of the strand board measured with a density profile analyzer (“DENSE-LAB X” made by ELECTRONIC WOOD SYSTEMS GMBH). - Mats of a large number of Douglas fir strands were stacked into a multi-layered mat having five strand layers and a thickness of 36 mm. The strands were 150 to 200 mm long in the fiber direction, 15 to 25 mm wide, and 0.8 to 2 mm thick and had a density of 450 to 550 kg/m3. The multi-layered mat was then subjected to hot pressing at 140° C. and 4 N/mm2 for 10 minutes, whereby a strand board with a density of 832 kg/m3 and a thickness of 12.2 mm was obtained. This strand board was used as Example 2.
FIG. 11 shows the results of the bending test, the dimensional change test, and the water absorption test for Example 2. - Mats of a large number of cypress strands were stacked into a multi-layered mat having five strand layers and a thickness of 42 mm. The strands were 150 to 200 mm long in the fiber direction, 15 to 25 mm wide, and 0.8 to 2 mm thick and had a density of 400 to 500 kg/m3. The multi-layered mat was then subjected to hot pressing at 140° C. and 8 N/mm2 for 10 minutes, whereby a strand board with a density of 779 kg/m3 and a thickness of 12.7 mm was obtained. This strand board was used as Comparative Example 1.
FIG. 11 shows the results of the bending test, the dimensional change test, and the water absorption test for Comparative Example 1.FIG. 13 shows the density distribution in the thickness direction (lamination direction) of the strand board measured with the density profile analyzer (“DENSE-LAB X” made by ELECTRONIC WOOD SYSTEMS GMBH). - Mats of a large number of Douglas fir strands were stacked into a multi-layered mat having five strand layers and a thickness of 35 mm. The strands were 150 to 200 mm long in the fiber direction, 15 to 25 mm wide, and 0.8 to 2 mm thick and had a density of 350 to 450 kg/m3. The multi-layered mat was then subjected to hot pressing at 140° C. and 8 N/mm2 for 10 minutes, whereby a strand board with a density of 812 kg/m3 and a thickness of 12.4 mm was obtained. This strand board was used as Comparative Example 2.
FIG. 11 shows the results of the bending test, the dimensional change test, and the water absorption test for Comparative Example 2. - The results in
FIG. 11 show that Example 1 is higher in density, flexural strength, modulus of rupture (MOR), and modulus of elasticity (MOE) than Comparative Example 1. Percentage dimensional change and water absorption of Example 1 are about the same as those of Comparative Example 1. Example 2 has a higher density than Comparative Example 2, approximately the same flexural strength and MOR as Comparative Example 2, and a higher MOE than Comparative Example 2. Percentage dimensional change and water absorption of Example 2 are about the same as those of Comparative Example 2. - The results in
FIGS. 12 and 13 show that Example 1 has substantially constant density distribution in the lamination direction of the multiple strand layers as compared to Comparative Example 1. The substantially constant density distribution includes such density distribution that, in the case where the measurement result of the density distribution varies as shown in, e.g.,FIGS. 12 and 13 , the median shown by dashed line as shown in each figure does not vary significantly but is substantially constant. For example, as can be seen from comparison between the dashed line shown inFIG. 12 (Example 1) and the dashed line shown inFIG. 13 (Comparative Example 1), the median of the density distribution shown inFIG. 12 varies less than the median of the density distribution shown inFIG. 13 , and the median of the density distribution shown inFIG. 12 is substantially constant. - Since the density distribution is substantially constant, the strand board has uniform density distribution and overall water resistance and strength (shear strength etc.) of the strand board are improved. Specifically, a portion with a low density has lower water resistance and strength than a portion with a high density. Accordingly, if the density distribution is uneven, the overall performance of the strand board is governed by the water resistance and strength of the portion with a low density. However, in the case where the density distribution is substantially constant, such a portion that becomes a bottleneck for performance can be eliminated.
- The above bending test was conducted in accordance with IICL_Floor_Performance TB001 Ver. 2. The dimensional change test and the water absorption test were conducted in accordance with the cyclic boiling test of Japanese Agricultural Standard for plywood.
- Mats of a large number of aspen strands were stacked into a multi-layered mat having five strand layers and a thickness of 53 mm. The strands had a thickness of 0.8 mm and a density of 300 to 600 kg/m3. As in the second example (see
FIG. 4 ) of the strand board of the second embodiment, strands with common densities (average value: 393 kg/m3) were used for the second to fourth strand layers located in the intermediate part in the lamination direction out of the five strand layers. Strands with higher densities (average value: 557 kg/m3) than the common densities were used for the first and fifth strand layers located at both ends in the lamination direction. - The multi-layered mat was then subjected to hot pressing at 160° C. and 4 N/mm2 for 8 minutes. The strand board thus obtained was used as Example 1. The time required to achieve a target thickness, namely the time required to press the multi-layered mat to a target thickness, was 24 seconds.
- A multi-layered mat having five strand layers and a thickness of 52 mm was formed in a manner similar to that in Example 1. Strands having a density (average value: 805 kg/m3) higher than Example 1 were used for the first and fifth strand layers located at both ends in the lamination direction out of the five strand layers. The multi-layered mat was then subjected to hot pressing under conditions similar to those in Example 1. The strand board thus obtained was used as Example 2. The time required to achieve a target thickness was 12 seconds. Example 2 is otherwise the same as Example 1.
- A multi-layered mat having five strand layers and a thickness of 62 mm was formed in a manner similar to that in Example 1. Strands with common densities (average value: 393 kg/m3) were used for all of the five strand layers. The multi-layered mat was then subjected to hot pressing under conditions similar to those in Example 1. The strand board thus obtained was used as Comparative Example 1. The time required to achieve a target thickness was 33 seconds. Comparative Example 1 is otherwise the same as Example 1.
- (Test A)
- A normal-state bending test (bending test span: 225 mm) was conducted on each of Examples 1, 2 and Comparative Example 1.
FIG. 14 shows the test results along with other physical properties. - Density distribution in thickness direction (lamination direction) of each strand board was measured with the density profile analyzer (“DENSE-LAB X” made by ELECTRONIC WOOD SYSTEMS GMBH).
FIG. 15 shows the measurement results. - The results in
FIG. 14 show that, as can be seen from comparison between Examples 1, 2 and Comparative Example 1, the use of high-density strand layers as the first and fifth strand layers located at the top and bottom out of the five strand layers allows the multi-layered mat before hot pressing to have a smaller thickness (bulk height) and thus facilitates compression of the multi-layered mat by hot pressing, thereby reducing the press time required to press the multi-layered mat to a target thickness (time to achieve the target thickness). Regarding flexural properties in the normal-state bending test, MORs and MOEs of Examples 1, 2 are about the same as those of Comparative Example 1. - Mats of a large number of aspen strands were stacked into a multi-layered mat having five strand layers and a thickness of 70 mm. The strands had a thickness of 0.8 mm and a density of 300 to 600 kg/m3. As in the first example (see
FIG. 3 ) of the strand board of the second embodiment, strands with common densities (average value: 393 kg/m3) were used for the first, third, and fifth strand layers of the five strand layers, namely the strand layers other than the second and fourth strand layers located in the intermediate part in the lamination direction. Strands with higher densities (average value: 933 kg/m3) than the common densities were used for the second and fourth strand layers. - The multi-layered mat was then subjected to hot pressing at 140° C. and 4 N/mm2 for 10 minutes, whereby a strand board having a density of 846 kg/m3 and a thickness of 12.5 mm was obtained. This strand board was used as Example 3. The MDI content or dozing was 12%.
- A multi-layered mat having five strand layers and a thickness of 78 mm was formed in a manner similar to that in Example 3. Strands with common densities (average value: 393 kg/m3) were used for all of the five strand layers. The multi-layered mat was then subjected to hot pressing at 140° C. and 8 N/mm2 for 10 minutes, whereby a strand board having a density of 846 kg/m3 and a thickness of 12.6 mm was obtained. This strand board was used as Comparative Example 2. Comparative Example 2 is otherwise the same as Example 3.
- (Test B)
- A normal-state bending test and a boiling test were conducted on Example 3 and Comparative Example 2. The boiling test was conducted in accordance with the cyclic boiling test defined in Japanese Agricultural Standard for Plywood. After the boiling test was conducted twice, thickness swelling TS, water absorption WA, and internal bond strength IB were measured.
FIG. 14 shows the measurement results along with other physical properties. -
FIG. 17 shows density distribution in the thickness direction (lamination direction) of each strand board measured with the density profile analyzer as in Test A. - The results in
FIG. 16 show that, regarding Example 3 in which the second and fourth strand layers located in the intermediate part in the thickness direction out of the five strand layers are high-density strand layers and Comparative Example 2 in which all of the five strand layers are low-density strand layers, flexural strength and internal bond strength IB after the boiling tests of Example 3 are either the same or higher than Comparative Example 2. Namely, the flexural strength and internal bond strength IB after the boiling tests of Example 3 are not lower than Comparative Example 2. - The results thus show that the use of high-density strand layers as the second and fourth strand layers of the five strand layers allows a strand board with performance similar to that of Comparative Example 2 to be formed by using a lower pressure of 4 N/mm2 instead of such a high pressure (8 N/mm2) as used in Comparative Example 2.
- Mats of a large number of aspen strands were stacked into a multi-layered mat having five strand layers and a thickness of 130 mm. The strands had a thickness of 0.8 mm and a density of 300 to 600 kg/m3. As in the sixth example (see
FIG. 8 ) of the strand board of the second embodiment, strands with common densities (average value: 413 kg/m3) were used for the first and fifth strand layers of the five strand layers, namely for the strand layers other than the second to fourth strand layers located in the intermediate part in the lamination direction. Strands with higher densities (average value: 1100 kg/m3) than the common densities were used for the second to fourth strand layers. - The multi-layered mat was then subjected to hot pressing at 160° C. and 8 N/mm2 for 60 minutes, whereby a strand board having a predetermined density and thickness (see
FIG. 18 ) was obtained. This strand board was used as Example 4. - A multi-layered mat having five strand layers was formed in a manner similar to that in Example 4. Strands with common densities (average value: 413 kg/m3) were used for all of the five strand layers. The multi-layered mat was then subjected to hot pressing at 140° C. and 8 N/mm2 for 60 minutes, whereby a strand board having a predetermined density and thickness (see
FIG. 18 ) was obtained. This strand board was used as Comparative Example 3. The processes were otherwise the same as those of Example 4. - A multi-layered mat having five strand layers was formed in a manner similar to that in Example 4. Strands with common densities (average value: 413 kg/m3) were used for all of the five strand layers. The multi-layered mat was then subjected to hot pressing at 160° C. and 8 N/mm2 for 30 minutes, whereby a strand board having a predetermined density and thickness was obtained. This strand board was used as Comparative Example 4. In Comparative Example 4, hot pressing was performed at a higher temperature than in Comparative Example 3 in order to avoid insufficient curing of an adhesive during winter time. Comparative Example 4 is small in size, and the press time was shorter than in Example 4 and Comparative Example 3. The processes were otherwise the same as those of Example 4.
- (Test C)
- A normal-state bending test, a boiling test, and a bond durability test were conducted on Example 4 and Comparative Example 3.
FIG. 18 shows the test results along with other physical properties. InFIG. 18 , “Elastic Limit Pmax” refers to elastic limit load, “Ratio of ELP” refers to the ratio of Elastic Limit Pmax to maximum load (Pmax), and “Inside Share Strength” refers to internal shear fracture strength. Regarding the bending direction, “longitudinal” refers to the longitudinal direction of the board, “lateral” refers to the lateral direction of the board, and “N=2 (N=3)” means that the number of test pieces was 2 or 3. Moreover, “TS” indicates thickness swelling, “WA” indicates water absorption, and “IB” indicates internal bond strength. - A nail pull test was conducted on Example 4 and Comparative Example 4. In the nail pull test, a lead hole with an inside diameter of 2 mm and a depth of 25 mm was formed in advance in each sample of Example 4 and Comparative Example 4. Three samples of Example 4 and four samples of Comparative Example 4 were tested, and the average value of the samples was calculated for each of Example 4 and Comparative Example 4.
FIG. 19 shows the results. -
FIG. 20 shows density distribution in the thickness direction (lamination direction) of each strand board measured with the density profile analyzer as in Test A. - The results in
FIG. 18 show that, regarding Example 4 in which the second to fourth strand layers located in the intermediate part in the lamination direction out of the five strand layers are high-density strand layers and Comparative Example 3 in which all of the five strand layers are low-density strand layers, flexural strength of Example 4 is about the same as that of Comparative Example 3, and internal bond strength after the boiling test of Example 4 is higher than that of Comparative Example 3. - These results show that the use of high-density strand layers as the second to fourth strand layers of the five strand layers allows a strand board with performance similar to that of Comparative Example 3 to be formed.
- The results of
FIG. 19 show that the use of high-density strand layers as the second to fourth strand layers located in the intermediate part in the thickness direction out of the five strand layers increases nail pull resistance (force) and achieves improvement in performance. - The present invention is suitable for use as flooring materials for containers, watercraft, vehicles, etc. The present invention is extremely useful as new building materials that are suitable for use as flooring materials and structural bracing boards for buildings such as houses. The present invention thus has high industrial applicability.
-
-
- B Strand Board (Wood Laminate Material)
- 1 Strand Layer (Woodbased Material Layer)
- 1 a High-Density Strand Layer (High-Density Woodbased Material Layer)
- 1 b Low-Density Strand Layer (Low-Density Woodbased Material Layer)
- 5 Strand (Cut Piece)
Claims (6)
1-4. (canceled)
5. A wood laminate material formed by stacking and laminating multiple woodbased material layers each formed by laminated woodbased materials that are laminated multiple cut pieces or a woodbased material that is a veneer, wherein
the multiple woodbased material layers include at least one high-density woodbased material layer, the remainder of the multiple woodbased material layers is a low-density woodbased material layer, and the high-density woodbased material layer has a higher density than the low-density woodbased material layer, and
the woodbased material layers located at both ends in the lamination direction of the woodbased material layers are the high-density woodbased material layers.
6. (canceled)
7. A wood laminate material formed by stacking and laminating multiple woodbased material layers each formed by laminated woodbased materials that are laminated multiple cut pieces or a woodbased material that is a veneer, wherein
the multiple woodbased material layers include at least one high-density woodbased material layer, the remainder of the multiple woodbased material layers is a low-density woodbased material layer, and the high-density woodbased material layer has a higher density than the low-density woodbased material layer, and
the woodbased material layer located in a part other than the ends and a middle part in the lamination direction of the woodbased material layers is the high-density woodbased material layer.
8-12. (canceled)
13. A method for manufacturing a wood laminate material, comprising:
a stacking step of stacking multiple woodbased materials, which are cut pieces or veneers, to form multiple woodbased material layers so that at least one of the multiple woodbased material layers is formed by a high-density woodbased material or high-density woodbased materials having a relatively higher density than the remainder of the woodbased material layers; and
a forming step of compressing or compacting the multiple woodbased material layers formed in the stacking step.