US20220001577A1 - Concrete curing blankets and anti-bacterial textile fibers - Google Patents

Concrete curing blankets and anti-bacterial textile fibers Download PDF

Info

Publication number
US20220001577A1
US20220001577A1 US17/289,741 US201917289741A US2022001577A1 US 20220001577 A1 US20220001577 A1 US 20220001577A1 US 201917289741 A US201917289741 A US 201917289741A US 2022001577 A1 US2022001577 A1 US 2022001577A1
Authority
US
United States
Prior art keywords
concrete
textile
blanket
fibers
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US17/289,741
Other languages
English (en)
Inventor
Dror Selivansky
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US17/289,741 priority Critical patent/US20220001577A1/en
Publication of US20220001577A1 publication Critical patent/US20220001577A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/88—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polycondensation products as major constituent with other polymers or low-molecular-weight compounds
    • D01F6/90—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polycondensation products as major constituent with other polymers or low-molecular-weight compounds of polyamides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B28—WORKING CEMENT, CLAY, OR STONE
    • B28B—SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS; SHAPING SLAG; SHAPING MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
    • B28B11/00—Apparatus or processes for treating or working the shaped or preshaped articles
    • B28B11/24—Apparatus or processes for treating or working the shaped or preshaped articles for curing, setting or hardening
    • B28B11/245—Curing concrete articles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B28—WORKING CEMENT, CLAY, OR STONE
    • B28B—SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS; SHAPING SLAG; SHAPING MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
    • B28B11/00—Apparatus or processes for treating or working the shaped or preshaped articles
    • B28B11/24—Apparatus or processes for treating or working the shaped or preshaped articles for curing, setting or hardening
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B11/00—Layered products comprising a layer of bituminous or tarry substances
    • B32B11/02—Layered products comprising a layer of bituminous or tarry substances with fibres or particles being present as additives in the layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/12—Layered products comprising a layer of synthetic resin next to a fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/32—Layered products comprising a layer of synthetic resin comprising polyolefins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/022—Non-woven fabric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
    • B32B5/24—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer
    • B32B5/26—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary
    • B32B5/265—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary characterised by one fibrous or filamentary layer being a non-woven fabric layer
    • B32B5/266—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary characterised by one fibrous or filamentary layer being a non-woven fabric layer next to one or more non-woven fabric layers
    • B32B5/267—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary characterised by one fibrous or filamentary layer being a non-woven fabric layer next to one or more non-woven fabric layers characterised by at least one non-woven fabric layer that is a spunbonded fabric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/02—Physical, chemical or physicochemical properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/04—Interconnection of layers
    • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/04—Interconnection of layers
    • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
    • B32B7/14—Interconnection of layers using interposed adhesives or interposed materials with bonding properties applied in spaced arrangements, e.g. in stripes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B40/00—Processes, in general, for influencing or modifying the properties of mortars, concrete or artificial stone compositions, e.g. their setting or hardening ability
    • C04B40/02—Selection of the hardening environment
    • C04B40/0277—Hardening promoted by using additional water, e.g. by spraying water on the green concrete element
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B40/00—Processes, in general, for influencing or modifying the properties of mortars, concrete or artificial stone compositions, e.g. their setting or hardening ability
    • C04B40/04—Preventing evaporation of the mixing water
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F1/00—General methods for the manufacture of artificial filaments or the like
    • D01F1/02—Addition of substances to the spinning solution or to the melt
    • D01F1/10—Other agents for modifying properties
    • D01F1/103—Agents inhibiting growth of microorganisms
    • E—FIXED CONSTRUCTIONS
    • E04—BUILDING
    • E04G—SCAFFOLDING; FORMS; SHUTTERING; BUILDING IMPLEMENTS OR AIDS, OR THEIR USE; HANDLING BUILDING MATERIALS ON THE SITE; REPAIRING, BREAKING-UP OR OTHER WORK ON EXISTING BUILDINGS
    • E04G21/00—Preparing, conveying, or working-up building materials or building elements in situ; Other devices or measures for constructional work
    • E04G21/24—Safety or protective measures preventing damage to building parts or finishing work during construction
    • E04G21/246—Safety or protective measures preventing damage to building parts or finishing work during construction specially adapted for curing concrete in situ, e.g. by covering it with protective sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/02—Coating on the layer surface on fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/26—Polymeric coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0223—Vinyl resin fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0253—Polyolefin fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0261—Polyamide fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0276—Polyester fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/04—Cellulosic plastic fibres, e.g. rayon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
    • B32B2264/02—Synthetic macromolecular particles
    • B32B2264/0214—Particles made of materials belonging to B32B27/00
    • B32B2264/0228—Vinyl resin particles, e.g. polyvinyl acetate, polyvinyl alcohol polymers or ethylene-vinyl acetate copolymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
    • B32B2264/02—Synthetic macromolecular particles
    • B32B2264/0214—Particles made of materials belonging to B32B27/00
    • B32B2264/0264—Polyamide particles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/718—Weight, e.g. weight per square meter
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/726—Permeability to liquids, absorption
    • B32B2307/7265—Non-permeable
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/02—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyamides
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/13—Physical properties anti-allergenic or anti-bacterial

Definitions

  • the invention relates to concrete curing blankets and antibacterial textile fibers.
  • Concrete strength, durability, permeability and other characteristics are established as the cement in the concrete hydrates its calcium oxide and silicone dioxide to CSH (Calcium Silica Hydrate), which forms a solid gel that hardens the concrete. It is important to supply the required amount of water for the hydration process in order to keep the optimal water to cement ratio throughout the hardening time for the concrete. As a result, all measures are taken to prevent water depletion from the concrete through evaporation or other causes.
  • CSH Calcium Silica Hydrate
  • the most productive period for the hydration of the cement is within the 10 to 20 days after casting, as 70% of the strength of the concrete is gained after 14 days. Accordingly, the water content of the concrete needs to be maintained for at least 14 days, to make sure the concrete achieves at least 70% of its final strength.
  • concrete is conventionally cured by curing blankets, to prevent evaporation and maintain the water level in the concrete.
  • the present invention improves on contemporary concrete curing blankets, by using combinations of materials which provide high performance beyond 14 days, without having to rewet the blankets.
  • the present invention provides effective, reliable, easy to use, inexpensive and sustainable concrete blankets, which extend the scope of applications of the concrete curing blankets to innovative supply of admixture chemicals for treatment of the covered concrete surfaces.
  • the present invention uses Super Absorbent Polymers (SAP) with high water capacity, which provides for the controlled release of water to maintain high degrees of water saturation at the concrete surface for extended times, and to supply adequate amounts of water molecules for the hydration reaction of the cement to yield superior cured concretes.
  • SAP Super Absorbent Polymers
  • the present invention creates blankets that maintain high water activity to dissolve chemical admixtures as Silicate salts and pozolanes within the curing blanket, which are designed to migrate into the concrete. This migration allows for the hardening, sealing, and the application of various surface treatments to the concrete.
  • SAP at the blanket surface creates interactions with the concrete capillaries. These interactions generate strong cohesion between the curing blanket and the concrete, which stabilizes the curing blanket's position on vertical and horizontal concrete elements.
  • the concrete blankets of the invention allow for a more effective and reliable concrete curing operation with much longer curing performance (sealed blankets), simpler to produce and handle (only three or two layers), easier to apply (lighter weight, and easy spread and faster water absorption and firmer sticking of the blanket to the concrete). less expensive and green (bio degradable SAP, all polyolefin materials that can be regenerated with no cellulose being used) products, such that the blankets of the present invention outperform the current state of the art curing blankets.
  • the present invention improves over conventional concrete blankets as it provides for curing times longer than 14 days, while minimizing water evaporation. As a result, there is no need for additional water at longer curing times. Additionally, the present invention is such that it works with a certain supply of water, which is required to complete the curing requirements (for specified concrete strength after cure time) with the required water content stored in the blanket of the invention. Also, the supply of the exact quantity of the required water molecules for the curing reaction is maintained at the correct W/C ratio versus over or under wetting, as is a problem in current curing practices.
  • the present invention provides concrete blankets made with low cost materials, including thinner fabrics, lower absorbent weights, and which are inexpensive to manufacture.
  • the present invention provides concrete blankets with larger widths than conventional concrete blankets, which cover larger areas, and due to their wettability, which allows the blanket of the invention to firmly adhere to the concrete.
  • This rapid attachment of the concrete blankets of the present invention provides a firm attachment of the concrete blanket to the concrete for stabilizing the blankets under high wind conditions.
  • the blankets of the invention are able to bond to vertically oriented concrete elements.
  • the present invention provides concrete blankets which when covering concrete, cause a raise in concrete temperatures for faster curing under low temperature conditions.
  • the concrete blankets of the present invention incorporate concrete admixtures to the concrete for surface treatment, providing the cured concrete with improved concrete properties.
  • the present invention provides concrete blankets with easy and sustainable regeneration of the all Polypropylene components, without the complications from using cellulose, as is used in the blankets of the contemporary art.
  • the present invention provides concrete blankets made of biodegradable SAP, which is environmentally friendly and non-toxic, allowing for safe disposal.
  • Embodiments of the invention are directed to a concrete curing blanket.
  • the blanket comprises: a contact layer including at least one nonwoven fabric, for contact with a concrete surface; a cover layer including a polymer film which functions as a water barrier; and, a storage layer including a super absorbent polymer material for storing liquid therein, the storage layer intermediate the contact layer and the cover layer.
  • the blanket is such that the super absorbent polymer material coats fibers in a nonwoven fabric forming the storage layer.
  • the blanket is such that the super absorbent polymer material is in a powder form dispersed within the fabric.
  • the blanket is such that the contact layer, storage layer and cover layer are joined together by lamination with a heat activated bonding agent.
  • the blanket is such that wherein the nonwoven fabric of the contact layer includes one or more of: polypropylene, polyethylene, polypropylene co-polyethylene, or polyacrylonitrile (PAN), Nylon, or, Polyester, fibers.
  • PAN polyacrylonitrile
  • the blanket is such that the nonwoven fabric of the storage layer includes one or more of: polypropylene, polyethylene, polypropylene co-polyethylene, or polyacrylonitrile (PAN), Nylon, Polyester fibers, Rayon, or cellulose three acetate.
  • PAN polyacrylonitrile
  • the blanket is such that the nonwoven fabrics are produced by processes including: Spun bonding, Spunbonding-Meltblowing-Spunbonding (SMS), Carding, Calender Bonding, Hydro-entanglement, Air through bonding, Chemical Bonding, Airlaid processes, Needle punching, Stitch Bonding, or, Wet laid process.
  • Spun bonding Spunbonding-Meltblowing-Spunbonding (SMS), Carding, Calender Bonding, Hydro-entanglement
  • Air through bonding Chemical Bonding, Airlaid processes, Needle punching, Stitch Bonding, or, Wet laid process.
  • the blanket is such that the nonwoven fabric of the storage layer is at least one of: stitch bonded or needle punched felts of weight per area units within the range of approximately 30-3,000 grams/square meter (m 2 ).
  • the blanket is such that the super absorbent polymer (SAP) material is selected from the group of: Sodium Polyacrylate and Sodium Polyacrylamide.
  • SAP super absorbent polymer
  • the blanket is such that Sodium Polyacrylate and Sodium Polyacrylamide are applied in the form of either: liquid or powder or SAP fibers incorporated into the fabric, and the Sodium Polyacrylate and Sodium Polyacrylamide are either Bio degradable or Bio non degradable.
  • Embodiments of the invention are directed to a concrete curing blanket comprising: a cover layer including a polymer film which functions as a water barrier; and, a storage layer including a super absorbent polymer material for storing liquid therein and overlying a concrete surface.
  • the invention provides anti-bacterial Nylon fibers, that advance the state of the art.
  • the antibacterial fibers are made of Polyamides, or any other amino end group containing polymers comprising transition metals and/or cations of high antibacterial protection, efficiency, durability and fastness.
  • the invention is based on the affinity of the electrophilic transition metal cations to the Nucleophilic Amino end groups (primary and secondary amines), and their tendency to form complex bonds (transition metal cations with amino group ligands complexes), which bond the reactive transition metal cations to the surface of the fibers, thereby stabilizing the cations on the fibers.
  • the invention maintains high concentrations of reactive biocides on the surface of the fibers, providing highly effective antibacterial protection, that is stable for extended time periods.
  • the fibers of the invention are capable of protecting various textiles against bacteria when mixed with the textile fibers at low fiber content, and extremely low concentrations of transition metals and/or cations in the (protected) textiles.
  • the reactive metals or cations affinity to the amino groups in the polyamide fibers preserves them in the fibers with characteristic long lasting activity and high fastness after excessive washing treatments.
  • Using metal particles of the nano scale dimensions increases the rates of migration of metals to the surface of the fibers, that form a very high surface area of reactive metals at the surface of the fibers.
  • the present invention uses micro fibers of low diameters within the range of approximately 8 to 20 microns. This increases the surface area of the reactive metals that are exposed to the environment on the fibers' surfaces.
  • the present invention uses partially oriented yarns (POY), Nylon fibers of low degrees of crystallinity and orientation and higher water accessibility and diffusion coefficients, such that the antibacterial efficiency of the metal particles in the fibers is increased.
  • POY partially oriented yarns
  • the invention applies Polyamide amino groups for coordination with transition metals or cations/nano-metals/POY microfibers, and their combinations, to create highly reactive fibers for protection of textiles via blending of the reactive fibers with the standard fibers of the textiles.
  • the textiles are fully protected against bacteria at very low reactive fibers content, within the range of 1% over weight of the fabric, and with extremely low metal contents, such as silver, within the range of approximately 15 to 30 PPM (parts per million). This lasts the lifetime of the textile at high fastness (maintaining reactivity after 50 washing cycles at 60 degrees Celsius (C)).
  • the invention is such that its lower costs and ease of application in basic textile operations, render it as superior over contemporary products, such as SilvadurTM from DuPont Dow, or any other contemporary antibacterial technology.
  • the present invention provides for an application of anti-bacterial Nylon POY (non drawn-texturized) fibers in textile fabrics.
  • Embodiments of the invention are directed to polyamide polymer fibers, each fiber comprising: at least 40 miliequvalents per Kg amino end groups and a transition metal and/or cation dispersed inside the polymer at weight contents within the range of approximately 0.10%-15.00%; and, the fibers are configured for blending inside a textile fabric at a weight content within the range of 0.015%-50.0% of the fibers of the textile fabric to render the textile as an antibacterial textile in accordance with American Association of Textile Chemists and Colorists (AATCC) 100-2012 standard.
  • AATCC American Association of Textile Chemists and Colorists
  • the fibers are such that they are entangled within the textile fabric structure.
  • the fibers are such that each fiber includes a transition metal cations complex formation with primary amino groups having K complexing values greater than 2,000.
  • the fibers are such that the content of the transition metal and/or cation in the textile fabric is within the range of approximately 5-100 ppm.
  • the fibers are such that the antibacterial protection of the textile fabric lasts for between 3 to 12 months.
  • the fibers are such that the antibacterial protection of the textile fabric lasts after 50 wash machine cycles at 60 degrees C., in accordance with the machine freshness standard of AATCC 100-2012.
  • the fibers are such that the complex metals or Ions are of the Nano scale sizes that is lower than 0.5 microns median dimeter.
  • the fibers are such that each fiber is of Partially Oriented Yarn (POY) type of tenacity within the range of approximately 3.0-4.5 grams per dtex and elongation within the range of approximately 60%-80%.
  • POY Partially Oriented Yarn
  • each fiber is made of one or more of: Nylon 6.6 polymer, Nylon 6 polymer, and copolymers comprising any combination of the monomers of: Nylon 6, Nylon 10 or Nylon 12.
  • the fibers are such that each fiber of Nylon 6.6 polymer or Nylon 6 polymer includes amino content greater than 70 miliequivalents per Kg
  • the fibers are such that each fiber includes metal selected from the group consisting of: Copper, Silver, and silver cations.
  • the fibers are such that each fiber is of a thickness is within the range of approximately 0.05-8.00 dtex.
  • the fibers are such that each fiber is of a length within the range of approximately 0.1 to 100 mm.
  • the fibers are such that each fiber is in the form of a continuous yarn.
  • the fibers are such that each fiber includes secondary and tertiary amino end groups.
  • FIG. 1 is perspective view of a concrete curing blanket in accordance with the present invention
  • FIG. 2A is a cross-sectional view of the an embodiment of the concrete curing blanket taken along line 2 - 2 of FIG. 1 ;
  • FIG. 2B is a cross-sectional view of the another embodiment of the concrete curing blanket taken along line 2 - 2 of FIG. 1 ;
  • FIGS. 3-6 are photographs of concrete at various stages of curing in accordance with the present invention.
  • Appendices A (7 Pages), B (2 Pages), C (3 Pages), and, D (3 Pages) are attached to this document.
  • FIGS. 1, 2A and 2B show a concrete curing blanket 100 , for example, of three layers ( FIG. 2A ), and 100 ′ of two layers ( FIG. 2B ), resting on a surface 102 a of a concrete slab 102 .
  • the first layer 111 is a base or contact layer 111 for contacting the concrete surface 102 a .
  • This layer 111 is for example, made of a synthetic nonwoven fabric, such as Spun Bonded fabric.
  • a second layer 112 which is a storage layer.
  • This storage layer 112 is, for example, a synthetic fiber made nonwoven fabric comprising SAP (Super Absorbent Polymer) material coating the fibers in the fabric.
  • SAP Super Absorbent Polymer
  • the nonwoven includes SAP powder dispersed within the fabric, the powder for storing water.
  • the third 113 or uppermost layer, over the second layer 112 is a cover layer.
  • This cover layer 113 is, for example, a synthetic film of high water barrier characteristics, which prevents water evaporation, through the blanket 100 .
  • the three layers 111 , 112 , 113 are laminated together via heat activated bonding agents, adhesives, or the like.
  • the contact layer 111 functions to wick water into the blanket 100 via pores of suitable sizes (within the range of approximately 10 to 500 microns) in the contact layer 111 . These pores allow for water permeation (e.g., fast water permeation based on nonwoven liquid strike through times of less than 2 minutes), into the blanket's 100 storage layer 112 , when the blanket 100 is in contact with the water saturated concrete (when the blanket 100 is spread over the concrete slab, to store and to effectively transfer water back to drying concrete spots from the water saturated blanket during the curing process).
  • water permeation e.g., fast water permeation based on nonwoven liquid strike through times of less than 2 minutes
  • the storage layer 112 by its SAP material, absorbs excessive quantities of the supplied water (up to 1,000 times its weight), due to the high osmotic pressure of the water molecules in the SAP's poly-ionomer (e.g., sodium neutralized polyacrylic, or polyacrylamide polymer), that is balanced by the compressive pressure of the crosslinks in the swollen SAP polymer network.
  • SAP's poly-ionomer e.g., sodium neutralized polyacrylic, or polyacrylamide polymer
  • This structure for the SAP restricts the swelling of the storage layer 112 caused by the water uptake.
  • the water molecules stored in the SAP saturate the blanket 100 and the concrete surface 102 a , to prevent drying of the concrete.
  • the SAP may be, for example, the material disclosed in U.S. Pat. No. 6,984,419, attached hereto as Appendix A (7 Pages).
  • the cover layer 113 is an hydrophobic (e.g., polyolefin) film of high water barrier characteristics (very low water absorption and diffusion coefficient) that prevents water evaporation from the blanket 100 , to maintain high water activity within the blanket available for supply to the concrete 102 through diffusion to the desiccated (due to the cement hydration), or other water depleted (due to drying) zones in the concrete 102 .
  • hydrophobic e.g., polyolefin
  • the curing blanket 100 ′ is composed of only two layers, the storage layer 112 and the cover layer 113 .
  • storage layer 112 is in direct contact with the concrete slab 102 , wherein fabric configurations of higher tightness (e.g., high thermal bonding nonwoven fabrics) and low linting (continuous filaments) are applied.
  • the contact layer 111 performs wicking of water and liquid as it is made of a nonwoven fabric of controlled pore sizes.
  • pore sizes are within the range of approximately 50 to 300 microns, with these pore sizes achieved through adjusting the parameters of the SMS (Spunbond-Meltblown-Spunbond) manufacturing method for the non-woven fabric, or any other Nonwoven fabric manufacturing method that control the pore size in the fabric.
  • the pore sizes of the contact layer 111 are capable of high water wicking, rates within the range of 10-60 seconds. This wicking rate is much greater than with conventionally known cellulose wicking layers.
  • the fabrics, e.g., SMS, of the contact layer 111 may be coated with suitable detergents designed for enhancing the wicking performance of nonwoven fabrics (e.g., SilastolTM 163 made by Schill & Zeilacher of Germany).
  • suitable detergents designed for enhancing the wicking performance of nonwoven fabrics (e.g., SilastolTM 163 made by Schill & Zeilacher of Germany).
  • the storage layer 112 serves in deswelling of the water saturated SAP from the storage blanket 100 to the concrete.
  • the storage layer 112 supplies the required water for the energetically favorable hydration reaction of Calcium and Silicon oxides in the cement to form the solid calcium silica hydrate (CSH) in the concrete during the curing stage.
  • CSH solid calcium silica hydrate
  • the supply of water molecules from the SAP to the concrete, against the osmotic pressure in the SAP, is driven thermodynamically by the free energy release of the water hydration reaction with the cement in the concrete.
  • the supply of water from the blanket 100 is stoichiometrically used for curing the cement, leaving no extra water supply, that could affect adversely the concrete strength.
  • the supply of vapor water molecules from the swollen SAP is enhanced by the osmotic pressure in the SAP, which increases the chemical potential of the water in the SAP through higher pressures.
  • the excessive water vapor that is supplied into the sealed blanket 100 accumulates between the impermeable cover layer 113 at the top of the blanket 100 and the concrete slab 102 at the bottom of the blanket 100 , forming high relative humidity levels, which saturate and condense into liquid water droplets, typically on the hydrophobic cover layer 113 .
  • the hydrophobic cover 113 is, for example, a film, which reacts as a nucleate to form the liquid phase as droplets on it, that accumulate as downward flowing water (toward the concrete surface 102 ), as shown in FIG. 3 .
  • the water condensation on the film of the cover layer 113 is affected by using cooler transparent or white films, and by coating the film with water nucleating agents, for example, silver iodine.
  • water nucleating agents for example, silver iodine.
  • transparent or translucent cover layers 113 liquid, e.g., water, droplet (drops) accumulation on the film is observable, as shown in FIG. 3 .
  • the liquid drops merge into a liquid water phase that saturates the blanket 100 .
  • the extra liquid water fraction that is not being absorbed into the concrete capillaries, for wetting the concrete and for the hydration reaction, is absorbed into the storage layer 112 , and reswells the water absorbent SAP in the storage layer 112 .
  • the vapor pressure in the SAP increases, causing faster liquidation of water on the film barrier in the cover layer 113 , saturating the blanket 100 , 100 ′ with higher contents of liquid water and keeping the concrete at a higher degree of humidity, such as approximately 90-100 percent humidity. Additionally, the temperatures inside the blankets 100 , 100 ′ increase via a “green house” effect, as generated by the cover layer 113 , within the blanket 100 , 100 ′.
  • the “reflux” process in the blanket 100 which supplies water from the SAP to continually saturate the blanket 100 and diffuse to the concrete capillaries, can be utilized for hydration of dry chemicals in the blanket 100 to hydrate, dissolve and mobilize the chemicals, through diffusion with the water, into the pores of the concrete surface 102 , for reaction with the concrete.
  • This water “reflux” process allows for the surface treatment of slabs and concrete elements with typical surface finishing admixtures, such as sealers and hardeners, that, for example, are incorporated as powders into the storage layer 112 of the blanket 100 , 100 ′.
  • the sealers and hardeners are effectively administrated to the concrete base 102 for the required surface treatment as described above.
  • Sealers include, for example, Lithium Silicate, while hardeners include, for example, micro silica.
  • Concrete admixtures and chemicals may also be administered to the concretes, and may include, for example, anti-efflorescence ion exchangers, concrete crystalline sealers, colloidal silica, various pigments, accelerators, and other related concrete additives.
  • the cover layer 113 is such that it has transport properties of water transmission WVTR lower than 4.6 gm/m 2 /pascal.
  • the impermeability of the cover layer 113 is increased, for example, by increasing the film thickness, bidirectionaly orientating the film, that reduces diffusion coefficient, as well as tighter adhesion of the cover layer 113 to the storage layer 112 , and higher overlap between the blankets 100 , 100 , for better sealing of the blanket 100 , 100 ′ over the concrete slab 102 .
  • the sun light radiation transport properties through the cover layer 113 may be manipulated via compounding with silica, in order to affect the temperature within the blanket.
  • Control of the cover layer 113 film interactions with solar radiation is used to heat the internal layers of the blanket and to generate a “Greenhouse” effect within the blanket. This is achieved as the transparent films allow the solar radiation to penetrate and heat the fibers of the storage layer 112 and SAP, generating the heat internally, and maintaining it inside the blanket 100 , 100 ′.
  • the effect can be further enhanced via incorporation of “green house” effect silica additives to the film (e.g., 10% over weight of film) of the cover layer 113 , which transfer the NIR (near infra-red) radiation from the sun into the blanket 100 , 100 ′, and absorbs the FIR (far infra-red) radiation that is reflected back from the storage layer 112 .
  • “green house” effect silica additives to the film (e.g., 10% over weight of film) of the cover layer 113 , which transfer the NIR (near infra-red) radiation from the sun into the blanket 100 , 100 ′, and absorbs the FIR (far infra-red) radiation that is reflected back from the storage layer 112 .
  • Higher SAP temperatures substantially increase its vapor pressure with an average vapor pressure increase of approximately 35%, for a temperature increase of approximately 5 degrees C. over ambient external temperatures of around 25 degrees C.
  • Black coloration of the internal layers of the blanket 100 , 100 ′ enhances absorbance and reflectance of the solar radiation inside the blanket 100 , 100 ′.
  • Cover film adjustments for lowering the blanket's 100 , 100 ′ temperature are possible via white pigments (e.g., Titanium Dioxide at weight concentrations of 0.5%-10.0%) that are dispersed in the film of the cover layer 113 , to scatter the sun light and prevent its penetration and heating of the curing blanket 100 , 100 ′.
  • white pigments e.g., Titanium Dioxide at weight concentrations of 0.5%-10.0%
  • the combination of the three layers 111 , 112 , 113 results in a blanket 100 , which maintains high moisture content in the concrete for long periods of time, and supplies adequate water for the required curing.
  • the high vapor pressures in the swollen high osmotic pressure and high temperature SAP in the storage layer 112 effectively fill the sealed blanket 100 volume with high activity water, of relative humidity levels near 100%, which saturate and nucleate into liquid droplets on the hydrophobic films or other surfaces in the blanket or on the concrete surface that is in contact with the curing blanket.
  • the contact layer's 111 water wicking performance is utilized effectively to transfer water to the SAP (in the storage layer 112 ) from the saturated concrete during the concrete covering stage, and to transfer water back to the concrete during deswelling for the hydration reaction of the cement during the curing stage.
  • the contact layer 111 has increased wicking rates (when compared to wicking rates in conventional concrete blankets).
  • Maintaining water saturation at the storage layer for extended times, and the ability to supply large liquid water quantities to saturate the concrete, are being utilized for transport of concrete admixtures from the storage layer 112 to the concrete (e.g., calcium hydroxide, colloidal silica, Lithium Silicate, Potassium Silicate, Sodium Silicate, silanes, siloxanes pigments, and the like):
  • the admixture chemicals that are mixed within the SAP matrix (of the storage layer 112 ), that coats the nonwoven's filaments, or dispersed in powder form within the nonwoven fabrics, are extracted by the condensed water, and diffuse with the water through the concrete 102 .
  • Capillaries in the contact layer 111 interact with the concrete surfaces 102 a , bringing about the required admixtures surface treatment that is superior to the conventional non-reactive concrete blankets.
  • SAP impregnated Nonwoven fabrics at contents of approximately 10 to 100 grams/square meter form strong bonds when in contact with the covered concrete. It is believed that this is related to suction of the SAP swollen gels by the concrete capillaries that are wetted via the lower surface tension hydrophilic SAP.
  • the strong bond that is generated attaches the blankets 100 , 100 ′ firmly to the concrete 102 , stabilizing the blankets against environmental elements, such as wind, and facilitates covering of vertical concrete elements.
  • Controlled SAP ionomer content and cross linking density are implemented in order to achieve suitable wetting and viscosity balance, as well as modulus and yield strength of the SAP, for optimal wetting of the concrete versus debonding of the SAP from the concrete, leaving it on the blanket 100 , 100 ′ after detachment of the blanket 100 , 100 ′ from the concrete surface 102 a .
  • the direct contact between the SAP and concrete 102 enables transfer of chemicals from the SAP directly to the covered concrete 102 in admixtures to the concrete.
  • the contact layer 111 is such that wicking capability is maximized by controlled pore size distribution and by coating the fabric with surfactants, such as SilastolTM 163.
  • the storage layer 112 includes high SAP contents, such as cross-linked sodium neutralized polyacrylic acid. Additionally, admixtures and concrete additives may be incorporated into either to the SAP (of the fabric) before cross linking, by wet impregnation, or in dry powder form mixed with the SAP powder during dry impregnation of the fabric. Additionally, coloring the nonwoven fabric of the storage layer 112 with black colors increases sunlight (solar radiation) absorption.
  • the cover layer 113 is such that it has increased water impermeability and increased light transparency. Silica additive in the cover layer 113 causes the “green house” effect.
  • the cover layer 113 is, for example, black in color for irradiation heating, and pigmented with white Titanium Dioxide for light reflection and cooling.
  • Manufacture of the cover layer 113 includes, for example, single or multi-layer film casting, with optional compounding of the polymers with black or white pigments, or with irradiation transfer controlling agents, such as Silica powder (5%-10% over weight of resin).
  • the cover layer 113 is bound to the storage layer 112 by an extrusion coating process, continually following the stage of SAP impregnation of the storage layer 112 .
  • the storage layer 112 is made by introducing SAP Material into the fabric by methods including continuous coating of the fabric by solution polymerized SAP, compressing the SAP into the fabric, and drying the coated fabric.
  • Continuous coating of the fabric may be performed by using the aqueous SAP system of H.B. Fuller, as disclosed in H.B. Fuller PD8081H Technical Data, attached hereto as Appendix B (Two Pages). This involves in situ cross linking of the SAP polymer solution during impregnation, compressing and drying the coated fabric.
  • a third method includes spreading of the dry powdered SAP particles (approximately 20-1,000 Microns MD (median diameter)) between two nonwoven fabrics at densities sufficient to maintain the powder particles in between. This is followed by adhesive bonding of the two fabrics to form an integral sandwich type of SAP particles hound between the two fabrics.
  • the SAP fibers blend into the nonwoven fabrics, when the nonwoven fabrics of the storage layer 112 are composed of blends of approximately 30%-100% Super Absorbent Fibers.
  • Manufacture of the storage layer 112 includes dispersion of dry Powders of SAP (approximately 20-2,000 microns MD in felt), stitching or needle punching the powder-impregnated felts to maintain the powder encapsulated inside the integrated fabric. Dry powders of SAP (50-1,000 microns MD) may be dispersed into the fabrics via the FibrolineTM process, as disclosed in www.Fibroline.com and Appendix C, attached hereto (3 Pages), are used in the storage layer 112 . Admixture chemicals are incorporated into the Nonwoven fabrics within the storage layer 112 , by one of the following methods:
  • the concrete curing blankets 100 , 100 ′ are, for example, used for curing horizontal concrete elements, such as slabs, floors, decks, piers, molds, and the like, and for curing vertical concrete elements, such as walls, pillars, slops, tilt ups, and the like.
  • the cast concrete age should be beyond the final setting time and after the required contraction joints cutting of the slabs and surface finish applications (abrasives, hardeners, sealers, pigments, and the like).
  • the concrete surface should be water soaked and covered with a 2-5 cm thick water layer. During blanket spreading over the concrete surface, extra water can be applied directly into the blanket via sprinkling.
  • the blankets should be spread strip wise, by unrolling them from cylindrical roll wraps. Blanket width dimensions are, for example, within the range of approximately 0.5-20.0 meters, preferably approximately 1.0-10.0 meters. There should be at least approximately 0.30 meters of overlap between adjacent blanket strips. Following placement, the blankets should be compressed to the concrete, via brooms or rolls, to disperse air bubbles out of the blanket/concrete interface.
  • Fresh concrete in vertical elements is covered with curing blankets that are fastened at their upper points via mechanical anchors, compressed to the concrete surfaces with rollers down to the bottom and bolted to the base of the elements.
  • the cohesion between the blanket's wet SAP and the concrete capillaries causes the blanket to firmly bond to the vertical concrete wall, and stabilizes its position.
  • the three layers 111 , 112 , 113 of the blanket 100 are laminated together via a heat activated bonding agent or any other adhesive type, to generate the combined effects of rapid water charging, high water content storing, extended time water release, and concrete moisturizing.
  • This allows for the blanket 100 to supply the required water molecules to complete curing of the dry concrete, typically, approximately 2-4 liters of water per square meter.
  • the contact layer 111 rapidly wicks the excess water into the SAP material within the storage layer 112 , for example, at typical rates of 1 liter per a square meter in a minute, that absorbs the water amount needed to complete curing of the concrete in the slab 102 .
  • the water barrier film of the cover layer 113 prevents evaporation of water vapor and maintains high water activity within the blanket 100 , which supplies water molecules from the SAP hydrogels to the chemically favorable calcium/silica hydration reaction to form solid CSH for solidification and hardening of the concrete during curing.
  • a concrete curing blanket 100 , 100 ′ may be of dimensions of at least approximately 0.5 meters in width 10 meters in length.
  • the concrete blanket 100 may be modified in the contact layer 111 by: 1) coating the Nonwoven fabric with a wicking agent, for example, a non-washable durable surfactant yielding strike-through time values (method NWSP 70.3) of less than 1 minute; 2) controlling the fabric's pore size range within the range of 1 to 1,000 microns; 3) using continuous filaments spun bonded or SMS produced Nonwovens of a high thermal bonding level and low linting levels; and, 4) using perforated films of wicking capacity with the Strike Through range of up to 1 minute, to replace the nonwoven fabric.
  • a wicking agent for example, a non-washable durable surfactant yielding strike-through time values (method NWSP 70.3) of less than 1 minute
  • NWSP 70.3 non-washable durable surfactant yielding strike-through time values
  • the concrete blankets 100 , 100 ′ may be modified in the storage layer 112 by: 1) increasing the SAP content in the fabric to above the level of 2 gm/square meter to supply the minimum estimated quantity of water required for curing of 30 MPa concrete 20 cm thick slab with 60 ⁇ weight water absorbing SAP in the blanket; 2) incorporating reactive chemicals as admixtures for migration into the concrete and for surface treatment of the concrete slab 102 upon wetting of the blanket 100 , 100 ′ (e.g., Calcium Oxide, Colloidal Silica, Microsilica, Lithium, Silicate, Potassium Silicate, Sodium Silicate, and, Crystalline Concrete Sealer; and, 3) coloring the layer 112 with a black light absorbing color.
  • reactive chemicals e.g., Calcium Oxide, Colloidal Silica, Microsilica, Lithium, Silicate, Potassium Silicate, Sodium Silicate, and, Crystalline Concrete Sealer
  • the concrete blankets 100 , 100 ′ may be modified in the cover layer 113 by: 1) increasing the water barrier efficiency of the film of the layer 113 by increasing film thickness or using double layer film or bi-oriented film of lower water absorption capacity and low diffusion coefficient yielding film water transmission levels within the range of 2.3-6.3 gm/square meter/Sec./Pascal, at 23 Degrees C.
  • WVTR water vapor transfer rate
  • the concrete blankets 100 , 100 ′ are such that they provide for one or more of: 1) rapidly wicking water from the concrete slab 102 into the storage layer 112 , when the blanket 100 , 100 ′ is placed over the wet concrete 102 , where, for example, Strike Through Rate time values are lower than 1 minute; 2) generating smooth, unstained lint free concrete surfaces after curing; 3) keeping the concrete slabs fully moist after more than 14 days; 4) yielding 14 days cured concrete with compressive strength values greater by 30% relative to the uncovered control concretes; 5) increasing concrete slab's 102 tightness, hardness, and/or impermeability, and/or mitigates dusting, mitigates efflorescence, and/or shrinkage and plastic cracking; 6) increasing the temperature within the blanket by more than 5 degrees C.
  • the concrete curing blankets 100 , 100 ′ are designed to be used for curing horizontal concrete elements, such as slabs, floors, decks, piers, molds etc. and for curing vertical concrete elements, such as walls, pillars, slops, and the like.
  • the cast concrete age should be beyond the final setting time, following the required slot cutting in the slabs and surface finish application (abrasives, hardeners, sealers, pigments, and the like).
  • the concrete surface 102 a should be water soaked and covered with a 2-5 cm deep water layer.
  • extra water can be applied directly into the blanket via sprinkling.
  • the blankets 100 , 100 ′ should be spread strip wise, via unrolling them from cylindrical roll wraps.
  • Blanket 100 , 100 ′ width dimensions are typically in the range of 0.5-20.0 meters, preferably 1.0-10.0 meters. There should be, for example, at least 0.30 meters overlap (OL in FIG. 1 ) between adjacent blanket strips.
  • the blankets 100 , 100 ′ should be compressed to the concrete 102 , via brooms or rolls, to disperse air bubbles out of the blanket 100 , 100 ′/concrete interface.
  • the cohesion forces between the blanket's wet SAP and the concrete capillaries firmly bond the blanket 100 , 100 ′ to the covered concrete surface 102 a , preventing detachment and stabilizing the position of the curing blanket 100 , 100 ′ on the concrete 102 .
  • Manufacture of the concrete curing blankets 100 , 100 ′ layers 111 , 112 , 113 for blanket 100 and 112 , 113 for blanket 100 ′ includes: 1) calendaring of the three or two layers using high temperature and pressure rolls, to adhere the respective layers; 2) applying heat/pressure sensitive adhesives or any other suitable adhesives system to bond the cover layer 113 to the storage layer 112 ; 3) single or multi-layer film casting, with optional compounding of the polymers with black pigments or with radiation transfer controlling Silica powder (5%-10% over weight of resin); 4) bonding the cover film of the cover layer 113 to the storage layer 112 via an extrusion coating process continually following SAP impregnation of the storage layer 112 ; 5) introducing of SAP material into the fabric via one of the methods: a) continuous coating of the fabric by solution polymerized SAP, compressing the SAP into the fabric and drying the coated fabric; b) continuous coating of the fabric by the Aqueous SAP system of H.B.
  • Appendix B which involves in situ cross linking of the SAP polymer solution during impregnation, compression (squeezing) and drying the coated fabric; and c) spreading of dry powdered SAP particles (20-1,000 Microns MD) between two Nonwoven fabrics dense enough to maintain the powder particles in between, followed by adhesive bonding of the two fabrics to form an integral sandwich type of SAP particles bound between the two fabrics.
  • the nonwoven fabrics of the storage layer 112 of the blankets 100 , 100 ′ are composed of blends of 30% to 100% Super Absorbent Fibers with fiber types including, for example, polypropylene, polyethylene, polypropylene co-polyethylene, or polyacrylonitrile (PAN), Nylon, or, Polyester.
  • fiber types including, for example, polypropylene, polyethylene, polypropylene co-polyethylene, or polyacrylonitrile (PAN), Nylon, or, Polyester.
  • the storage layer 112 may include nonwoven bonded felts, made by processes such as: 1) dispersion of dry powders of SAP (20-2,000 microns MD) within the stitch bonded or needle punched felts during the fabric production in the unbonded raw felts, stitching or needle punching the powder impregnated felts to maintain the powder encapsulated inside the fabric; or 2) dry powders SAP (50-1,000 microns MD) dispersion into the fabrics via the FibrolineTM process (Appendix C), or any other powder impregnation processes, and detailed above.
  • nonwoven bonded felts made by processes such as: 1) dispersion of dry powders of SAP (20-2,000 microns MD) within the stitch bonded or needle punched felts during the fabric production in the unbonded raw felts, stitching or needle punching the powder impregnated felts to maintain the powder encapsulated inside the fabric; or 2) dry powders SAP (50-1,000 microns MD) dispersion into the fabrics via the FibrolineTM process (Appendix C), or any other
  • the storage layer 112 may include additional admixture chemicals, to react with the concrete 102 , involving one of the following methods: a) mixing of dispersions of the chemical admixtures within the SAP Polymer Solution, or within the Aqueous SAP system of H.B.
  • a three layer concrete blanket 100 is provided, and includes the following layers:
  • Type Spunbond Nonwoven fabric made of Polypropylene
  • Pore size dimensions 200-500 microns
  • SAP Coating content 20 grams/square meter
  • aqueous Super Absorbent Polymer (SAP) system PD8081H supplied by H.B. Fuller, is cross linked with Ammonium Zirconium Carbonate solution in water, Bacote 20 supplied by MEI, and is applied to the Nonwoven fabric via wet impregnation, padding and drying.
  • a solution of sodium neutralized acrylic acid polymer of the PD8081H in the bath is cross linked by the Zirconium of the Bacote 20 in situ during impregnation of the fabric.
  • white SAP film is forming on the fabric that further dries to form SAP coated fabric.
  • Cover Layer 113 includes a low density polyethylene film of thickness 50 microns. Water transmission is: WVTR 2.5 gram/square meter/24 hours at 23 degrees C. and 85% relative humidity. Blanket Production:
  • the nonwoven fabric of the storage layer 112 under goes impregnation in a bath containing ingredients as described before, is compressed, and merged with the nonwoven fabric of the contact layer 111 that is fed from a parallel roller above it. Both merged fabrics go through a 120 degrees C. air circulated drier for 30 seconds residence time and roll together on a storage Bobbin.
  • the two merged fabrics are then covered by the third cover layer film 113 that is continually fed on them.
  • the cover layer film 113 is glued to the two merged layers 111 , 112 with discontinuous dots of pressure sensitive adhesive, which is dispersed between the fabrics before their contact point, and then compressed between the film 113 and Nonwoven fabrics layers 112 by hot compressive rolls.
  • the final blankets were rolled on 1.2 meter cylinders.
  • the concrete curing blanket 100 was used in curing a 500 square meter floor for a compost processing factory at the “Or Compost” regeneration industrial park in the Jordan Valley of Israel.
  • the floor is designed for fork lifts and heavy duty vehicles.
  • the floor is 30 cm thick and reinforced with welded wire fabrics as well as rebars, suitable to overcome the prescribed loads.
  • the concrete was a standard B 30 concrete of 350 Kg/cubic meter cement and water to cement ratio of 0.45. Standard practices of ground tightening, casting and laser screeding were observed.
  • the floor was cut to contraction spacing of 10 meters by 7 meters.
  • the curing blankets were laid following the floor cutting.
  • the floor was saturated with water at a depth of 2.0-3.0 cm.
  • a 1.20 meter wide blanket was unrolled from wrapped cylinders into the top of the floor.
  • the blankets immediately stuck (adhered) to the concrete floor and rapidly adsorbed the water.
  • Extra water was added through a hose in front of the unrolling line to maintain water saturation. Strips of the blanket were laid in parallel with a 30 cm overlap between the adjacent blankets.
  • the blanket was squeezed (compressed) a soft squeeze, to disperse trapped air bubbles out of the interface between the blanket and the floor. About 200 square meters of the floor were not covered, in order to serve as a control.
  • the covered concrete kept high humidity levels under the water saturated blanket.
  • the concrete dried rapidly and quickly lost water, once the blanket was removed for testing the humidity ( FIG. 4 ).
  • the uncovered control dried out within less than a week and developed plastic shrinkage cracks.
  • the covered concrete did not generate any cracks after removal of the blanket and maintained a smooth, tight structure without efflorescence contamination.
  • the blanket 100 ′ is similar to the previous three layer curing blanket, without the contact layer 111 .
  • the blanket 100 ′ included a storage layer 112 and a cover layer 113 , manufactured in the same manner as the blanket 100 detailed above.
  • the layers 112 , 113 were bonded together through hot calendering of the two layers with dotted points of pressure sensitive adhesive in between the layers.
  • the concrete curing blanket 100 ′ was used in curing a 100 square meter indoor floor on a basement of a warehouse at the Bar Lev Industrial Park in Israel.
  • the floor is designed for fork lift traffic.
  • the floor is 20 cm thick and reinforced with steel fibers at the dosage of 35 Kg/Cubic meter without the need for contraction joints.
  • the concrete was a standard B 40 concrete of 400 Kg/cubic meter cement and water to cement ratio of 0.50. Standard practices of ground tightening, casting, and laser screeding were observed.
  • the curing blanket was laid following a helicopter smoothing: The floor was saturated with water at water depth of 2.0-3.0 cm. A 1.20 meter wide blanket was unrolled from wrapped cylinders into the top of the floor. The blanket was tightened with a broom to the concrete floor in order to adhere the blanket to the floor. Strips of the blanket were laid in parallel with a 30 cm overlap (OL in FIG. 1 ) between the adjacent blankets. About 100 square meters of the floor was not covered to serve as a control.
  • the storage layer 112 touching the concrete formed strong bonding spots on the concrete via SAP adhering to the concrete capillaries at multiple points.
  • some of the SAP remained in the concrete and was removed by water sprinkling ( FIG. 6 ). This suggests the potential of using a two-layer blanket with SAP contacting the concrete, in order to develop a strong bond between the blanket and the covered concrete, in horizontal and vertical covering configurations.
  • the present invention provides for protection of textiles that contain polyamides comprising amino end groups by using transition metal cations capable of chemical interactions through complex coordination and electrophilic bonds formations with the amino end groups of the polymer. This provides for higher stability of the metal cation on the fiber surface, for longer and more stable protection.
  • POY partially oriented yarn
  • the low contents of reactive fibers inside the textile structure allow for lower costs and easier textile manufacturing, and the small amounts of transition metals or cations in the textile fabric result in a lower environmental impact.
  • the invention provides a quorum sensing mechanism of protection, resulting in lower consumption of transition metals or cations by the environment.
  • a combination of physical and chemical principles is being used in the invention to produce polyamide fibers of effective antibacterial protection for textiles, with low contents of biocides.
  • the transition metals which are known as effective antibacterial agents, are dispersed within polyamide fibers through injection of master batches of the metal in polymer concentrates, into the polymer in the extruder during melt spinning. This process disperses the metal particles within the fibers. When exposed to ambient conditions, the metal particles undergo solid state migration to the surfaces of the fibers, forming higher concentrations at the surfaces of the fibers. This equilibrates the polymer's vapor pressure and chemical potential within the fibers. This process continually supplies the needed metal particles from the hulk of the fibers to the surface, as the metals are depleted to the protected environment. This process constitutes an internal controlled release mechanism of the metal ions from inside the fibers to the protected environment. The metals at the surface are oxidized to form transition metal cations, which function as biocides.
  • the metal cations at the surface of the fibers form complexes and electrophilic bonds with the amino end groups of the polyamide polymers. This stabilizes the metal cations on the fiber's surface against migration into the aqueous environment around the fibers, restricting their dissolution in the surrounding water to low concentrations, and increasing their stability towards laundry washing cycles.
  • the stability of the anti-bacterial protection by the transition metals in the polyamide fibers is uniquely high. This suggests that the protection mechanism does not involve only “contact killing” with equivalent metal transfer to the bacteria, but rather, also involves either consumption of very small dosages of the dissolved metal in the water, that are highly effective bacteria killers, or, no transfer of metals at all, in a mechanism that is based on a “quorum sensing” effect within the bacteria community. This “quorum sensing” effect prevents the bacterial settling on or near the fibers' surfaces, and halts their multiplication in the protected textile. The bacteria sense the metal biocides on the fibers' surfaces, and detect each other signals, not to settle or multiply there, through their “quorum sensing” communications system.
  • the inventors discovered that the higher the antibacterial efficiency of the metal, the higher is the sensitivity of the bacteria to the metal that can be used at lower contents in the protected fabric. Additionally, the inventors discovered that silver cations are highly effective antibacterial agents, yielding protection at extremely low concentrations in textiles for long times and at high fastness.
  • the fiber formation involves standard Nylon 6.6 POY melt spinning procedure that includes master batch injection through a pressurized additives port in the extruder, allowing for the introduction of the silver metal into the fibers.
  • Textile Nylon 6.6 polymer of relative viscosity is within the range of 35-45, and typically 40, containing 0.3% delustrant is melt spun at speed within the range of 4,500-5,500, and typically 5,000, meters/minute to generate POY fibers of 3.2-4.2, and typically 3.8 grams/dtex tenacity and 70%-80%, and typically 76%, elongation.
  • the fibers dtex/filaments count is 50/40, with dtex per filament 1.25, which is within the microfibers range.
  • the polymer is injected with a silver metal containing master batch designed for uniform and high dispersion in the Nylon 6.6 polymer via long residence times 2-6, and typically 4, minutes in the extruder.
  • the carrier of the silver particles is Nylon 6.
  • the silver particles are of nanosizes, such as less than 0.5 microns.
  • the dosage of the master batch in the polymer is within the range of 1.3%-2.0%.
  • the Master batch type is SUKANO PA am 5652, made by Sukano AG.
  • the spun POY fibers are spin finished with 0.2%-0.6% (typically 0.3%) oil on yarn.
  • the silver concentration in the extruded fibers is within the range of approximately 1,500-4,500 ppm.
  • a typical fiber with parameters within the above range is produced by Nilit Ltd. of Migdal Haemek, Israel. These fibers are designed to be drawn textured to 40/40 dtex/filaments count and used as a typical draw textured yarn in knit wear for antimicrobial protection of the textiles against body perspiration and smell, under the trade name “Body Fresh”.
  • the protected knitted fabrics contain either 100% Body Fresh fibers, or are blended with regular Nylon textured yarns in contents greater than 40%.
  • the above silver containing POY (non texturized) fibers are used as blends in contents lower than 10%, to protect textiles against bacteria.
  • the above produced POY fibers were cut to 12 mm cut length staples.
  • the cut fibers were blended with a mix of regenerated polyester and viscose cut fibers, carded and further stitch bonded to a nonwoven fabric of 280 grams/square meter fabric specific weight via a polyester 150/1 yarn with a 7 gauge needle stitch bonding machine.
  • the Nylon POY reactive fibers contents in the fabrics were 5.0% and 1.0%.
  • the two fabrics along with an untreated control fabric were subjected to bacterial resistance test following the American Association of Textile Chemists and Colorists (AATCC) 100-2012 standard test for assessment of antibacterial finishes on textile materials for the AATCC25922 Escherichia coli.
  • AATCC American Association of Textile Chemists and Colorists
  • nano-particle silver is with 30 to 100 ppm
  • zeolite particle silver is with 80 to 300 PPM
  • fiber imbedded silver is with 2,500 to 5,000 PPM
  • Triclosan is with 1,000 to 5,000 PPM
  • quaternary amines are with 1,000 to 10,000 PPM.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Textile Engineering (AREA)
  • Ceramic Engineering (AREA)
  • Structural Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Architecture (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Toxicology (AREA)
  • Civil Engineering (AREA)
  • Laminated Bodies (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
  • Devices For Post-Treatments, Processing, Supply, Discharge, And Other Processes (AREA)
  • Curing Cements, Concrete, And Artificial Stone (AREA)
US17/289,741 2018-10-29 2019-10-29 Concrete curing blankets and anti-bacterial textile fibers Pending US20220001577A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US17/289,741 US20220001577A1 (en) 2018-10-29 2019-10-29 Concrete curing blankets and anti-bacterial textile fibers

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201862752175P 2018-10-29 2018-10-29
PCT/IB2019/059268 WO2020089789A1 (en) 2018-10-29 2019-10-29 Concrete curing blankets and anti-bacterial textile fibers
US17/289,741 US20220001577A1 (en) 2018-10-29 2019-10-29 Concrete curing blankets and anti-bacterial textile fibers

Publications (1)

Publication Number Publication Date
US20220001577A1 true US20220001577A1 (en) 2022-01-06

Family

ID=70463564

Family Applications (2)

Application Number Title Priority Date Filing Date
US17/289,741 Pending US20220001577A1 (en) 2018-10-29 2019-10-29 Concrete curing blankets and anti-bacterial textile fibers
US17/141,383 Pending US20210130985A1 (en) 2018-10-29 2021-01-05 Concrete curing blankets and anti-bacterial textile fibers

Family Applications After (1)

Application Number Title Priority Date Filing Date
US17/141,383 Pending US20210130985A1 (en) 2018-10-29 2021-01-05 Concrete curing blankets and anti-bacterial textile fibers

Country Status (8)

Country Link
US (2) US20220001577A1 (es)
EP (1) EP3873712A4 (es)
JP (1) JP2022536235A (es)
CN (1) CN113165208A (es)
CA (1) CA3118074A1 (es)
IL (1) IL282768A (es)
MX (1) MX2021004939A (es)
WO (1) WO2020089789A1 (es)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11322051B2 (en) * 2015-07-19 2022-05-03 Picpatch, Llc Universal tamper-evident security label for an electronic device having an integral camera

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1999152A (en) * 1935-04-23 Covering foe
US10751910B1 (en) * 2017-11-29 2020-08-25 Ramshorn Corporation Concrete curing blanket

Family Cites Families (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02128071A (ja) 1988-11-08 1990-05-16 Oji Kenzai Kogyo Kk コンクリートの湿潤養生シート
US5843554A (en) * 1994-02-18 1998-12-01 Katman, Inc. Multi-layer covering articles
AR018063A1 (es) * 1998-02-13 2001-10-31 Basf Se Poliamida inherentemente estabilizada frente a la luz y al calor y metodo para su obtencion.
DE10063286A1 (de) * 2000-12-19 2002-06-20 Zimmer Ag Verfahren zum Spinnen und Aufspulen von PET-Filamenten
KR20040079939A (ko) * 2002-01-23 2004-09-16 이 아이 듀폰 디 네모아 앤드 캄파니 폴리아미드사로부터의 색변화 직물
US20040137076A1 (en) * 2002-04-08 2004-07-15 Naruki Yamauchi Antibacterial processing of fiber products
US20040243080A1 (en) * 2003-05-27 2004-12-02 Bba Nonwovens Simpsonville, Inc. Absorbent pads
US7572525B2 (en) * 2004-07-23 2009-08-11 Mcdonald Stephen F Concrete curing blanket
US8038364B2 (en) * 2007-08-07 2011-10-18 Saint-Gobain Technical Fabrics America, Inc. Reinforcement for asphaltic paving, method of paving, and process for making a grid with the coating for asphaltic paving
US7998564B2 (en) * 2008-01-02 2011-08-16 Precision Fabrics Group, Inc. Concrete curing blankets that promote even concrete curing
CN101775746B (zh) * 2010-01-21 2012-01-25 同济大学 一种混凝土养护材料及其制备方法
US20120289107A1 (en) * 2011-04-22 2012-11-15 OSUS, Inc. Metal/polymer composite fibers
EP3024891B1 (en) * 2013-07-22 2018-03-21 Rhodia Operations Stabilised polyamide composition
US10052791B2 (en) 2015-01-31 2018-08-21 Ramshom Corporation Method of curing concrete using a curing blanket
US20160229162A1 (en) * 2015-02-11 2016-08-11 King Fahd University Of Petroleum And Minerals Concrete curing blanket
US20170291385A1 (en) * 2015-04-13 2017-10-12 Michael E. Carroll Concrete Curing Blanket
CN207175800U (zh) * 2017-06-19 2018-04-03 中国建筑股份有限公司 一种自动补水混凝土养护装置

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1999152A (en) * 1935-04-23 Covering foe
US10751910B1 (en) * 2017-11-29 2020-08-25 Ramshorn Corporation Concrete curing blanket

Also Published As

Publication number Publication date
JP2022536235A (ja) 2022-08-15
IL282768A (en) 2021-06-30
WO2020089789A1 (en) 2020-05-07
CN113165208A (zh) 2021-07-23
US20210130985A1 (en) 2021-05-06
MX2021004939A (es) 2021-11-12
EP3873712A4 (en) 2022-11-09
CA3118074A1 (en) 2020-05-07
EP3873712A1 (en) 2021-09-08

Similar Documents

Publication Publication Date Title
US4851291A (en) Temperature adaptable textile fibers and method of preparing same
US8221910B2 (en) Thermal regulating building materials and other construction components containing polymeric phase change materials
US20080258341A1 (en) Lightweight single-use concrete curing system
CA2974098C (en) Concrete curing blanket and method
US20120312489A1 (en) Reinforcement Sheet to Reinforce a Cementitious Board
BR102012016394A2 (pt) Material de tecido não tecido dispersível em água
US20210130985A1 (en) Concrete curing blankets and anti-bacterial textile fibers
CN100422427C (zh) 填料固着纤维、纤维结构物和纤维成形体以及它们的制造方法
US20080054519A1 (en) Method of Curing Concrete
JP2003193371A (ja) 寝具又はインテリア用繊維製品
US20090169849A1 (en) Concrete curing blankets that promote even concrete curing
ES2230437T3 (es) Material laminado con caracteristicas mejoradas.
EP3532666B1 (en) Air-cured batting insulation
JP2010515835A (ja) 移動ブロックを取り囲む温度調節組成を取り込んだ繊維基材
US20230405871A1 (en) Concrete curing blankets
CA2369904A1 (en) Insulating and footwear system
KR20060081632A (ko) 기능성 부직포 제조방법 및 그 장치
US20160009050A1 (en) Concrete Curing Blanket
US20210123185A1 (en) Breathable hydrostatically-resistant structures
JP2004075903A (ja) 硬質表面処理剤
JPH087666A (ja) 止水テープ
JPS62253803A (ja) 透水性人工芝生敷物
KR20040094006A (ko) 온도조절기능을 갖는 5 층 구조의 합포형 표면초발수이면초속건섬유 시이트
JP3154286B2 (ja) 吸湿性不織布
CN201719388U (zh) 一种医用铺单

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED