US20190381568A1 - Copper porous body, copper porous composite member, method for producing copper porous body, and method for producing copper porous composite member - Google Patents

Copper porous body, copper porous composite member, method for producing copper porous body, and method for producing copper porous composite member Download PDF

Info

Publication number
US20190381568A1
US20190381568A1 US16/468,020 US201816468020A US2019381568A1 US 20190381568 A1 US20190381568 A1 US 20190381568A1 US 201816468020 A US201816468020 A US 201816468020A US 2019381568 A1 US2019381568 A1 US 2019381568A1
Authority
US
United States
Prior art keywords
copper
porous
porous copper
fibers
composite member
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/468,020
Other languages
English (en)
Inventor
Jun Kato
Koichi Kita
Toshihiko Saiwai
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Materials Corp
Original Assignee
Mitsubishi Materials Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Materials Corp filed Critical Mitsubishi Materials Corp
Assigned to MITSUBISHI MATERIALS CORPORATION reassignment MITSUBISHI MATERIALS CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KITA, KOICHI, KATO, JUN, SAIWAI, Toshihiko
Publication of US20190381568A1 publication Critical patent/US20190381568A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/002—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of porous nature
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/10—Sintering only
    • B22F3/11—Making porous workpieces or articles
    • B22F3/1103—Making porous workpieces or articles with particular physical characteristics
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/002—Manufacture of articles essentially made from metallic fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/10—Sintering only
    • B22F3/11—Making porous workpieces or articles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/06—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools
    • B22F7/08—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools with one or more parts not made from powder
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making non-ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making non-ferrous alloys
    • C22C1/08—Alloys with open or closed pores
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/06—Metallic powder characterised by the shape of the particles
    • B22F1/062—Fibrous particles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/10—Copper
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12014—All metal or with adjacent metals having metal particles
    • Y10T428/12028—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.]
    • Y10T428/12042—Porous component

Definitions

  • the present invention relates to a porous copper body (copper porous body) consisting of copper or a copper alloy, a porous copper composite member (copper porous composite member) in which the porous copper body is bonded to a member main body, a method for producing the porous copper body, and a method for producing the porous copper composite member.
  • the porous copper sintered body and the porous copper composite member are used, for example, as electrodes and current collectors in various batteries, heat exchanger components such as heat pipes, silencing components, filters, impact-absorbing components, and the like.
  • Patent Document 1 proposes a heat transfer member in which a porous copper body having a three-dimensional network structure is integrally adhered to a conductive metal member main body.
  • Patent Document 1 discloses a method in which a pressure sensitive adhesive is applied to a skeleton of a three-dimensional network structure (for example, synthetic resin foam having open cells such as urethane foam and polyethylene foam, and a natural fiber cloth, a man-made fiber cloth, and the like) made of a material burned off by heating, and a metal powder material is adhered to obtain a formed body, and the formed body is used, and a method in which a metal powder material is plowed in a material (for example, pulp or wool fiber) made of a raw material burned off by heating and capable of forming a three-dimensional network structure to obtain a sheet-like formed body, and the sheet-like formed body is used.
  • a pressure sensitive adhesive is applied to a skeleton of a three-dimensional network structure (for example, synthetic resin foam having open cells such as urethane foam and polyethylene foam, and a natural fiber cloth, a man-made fiber cloth, and the like) made of a material burned off by heating, and a metal powder
  • Patent Document 2 discloses a method for obtaining a porous copper body by electrically heating copper fibers under pressure.
  • Patent Document 3 discloses a method for obtaining a porous copper body by heating copper fibers at 800° C. in air and then heating the copper fibers at 450° C. in a hydrogen atmosphere.
  • Patent Document 2 there is a problem in that the porosity decreases because it is necessary to perform electrical sintering under pressure in order to sufficiently bond the copper fibers to each other. In addition, there is a problem in that a shape of a forming die to be used at the time of sintering is limited because it is necessary for uniform pressure to be applied.
  • Patent Document 3 since the heating is carried out in air, there are concerns that the oxygen concentration in the copper fibers will increase, or thereafter, voids will be generated when heating in the hydrogen atmosphere and the strength of the porous copper body will decrease.
  • the invention has been made in consideration of the above-described circumstances, and an object thereof is to provide a porous copper body which has high porosity and sufficient strength, a porous copper composite member in which the porous copper body is bonded to a member main body, a method for producing a porous copper body, and a method for producing a porous copper composite member.
  • the porous copper body according to the invention includes a skeleton which is formed of a sintered body of a plurality of copper fibers and has a three-dimensional network structure, wherein the copper fibers forming the skeleton consist of copper or a copper alloy, and the copper fibers have a diameter R in a range of 0.01 mm to 1.0 mm, a ratio L/R of a length L to the diameter R in a range of 4 to 200, and a circularity of a cross section orthogonal to a length direction in a range of 0.2 to 0.9, and the porous copper body has a porosity of 50% to 95%.
  • the diameter R is in a range of 0.01 mm to 1.0 mm and the ratio L/R of the length L to the diameter R is in a range of 4 to 200. Therefore, it is possible to secure sufficient voids between the copper fibers; and thereby, the porosity can be in a range of 50% to 95%.
  • the diameter R is a value that is calculated on the basis of a cross-sectional area A of each fiber, and is defined by the following expression on the assumption that the cross-sectional shape is a perfect circle regardless of an actual cross-sectional shape.
  • the circularity of the cross section orthogonal to the length direction of the copper fibers forming the skeleton is defined.
  • the circularity C is expressed by the following expression when a cross-sectional area of the copper fiber is represented as A and a circumferential length of the cross section of the copper fiber is represented as Q.
  • Circularity C (4 ⁇ A ) 0.5 /Q
  • the circularity C becomes 1.
  • the cross-sectional shape is a concave polygon such as a star shape, a rectangle having a large aspect ratio, or the like, the circularity C approaches 0.
  • the circularity of the cross section of each of the copper fibers forming the skeleton is in a range of 0.2 to 0.9. Therefore, when laminating the copper fibers, there are many portions where the copper fibers are in surface contact with each other. Therefore, it is possible to secure a contact area between the laminated copper fibers; and thereby, bonding strength between the copper fibers can be improved, and in addition, voids can be secured between the copper fibers and the porosity can be increased.
  • the porous copper composite member according to the invention includes: a bonded body of a member main body and a porous copper body including a skeleton of a three-dimensional network structure, wherein the porous copper body is the above-described porous copper body.
  • porous copper composite member having this configuration since it is configured to include the bonded body of a porous copper body having high porosity and excellent strength and the member main body, it is possible to provide a porous copper composite member having excellent characteristics.
  • a bonded surface of the member main body bonded to the porous copper body consists of copper or a copper alloy, and a bonded portion between the porous copper body and the member main body is a sintered layer.
  • the porous copper body and the member main body are strongly bonded to each other, and thus the porous copper composite member can have excellent strength.
  • the method for producing a porous copper body according to the invention is the method for producing a porous copper body including a skeleton which is formed of a sintered body of a plurality of copper fibers and has a three-dimensional network structure, and the method includes: a copper fiber lamination step of laminating the copper fibers, wherein with regard to the copper fibers, a diameter R is in a range of 0.01 mm to 1.0 mm, a ratio L/R of a length L to the diameter R is in a range of 4 to 200, and a circularity of a cross section orthogonal to a length direction is in a range of 0.2 to 0.9; and a sintering step of sintering the plurality of laminated copper fibers together.
  • the diameter R is in a range of 0.01 mm to 1.0 mm
  • the ratio L/R of the length L to the diameter R is in a range of 4 to 200
  • the circularity of the cross section orthogonal to the length direction is in a range of 0.2 to 0.9. Therefore, a contact area between the copper fibers is secured, and thus it is possible to obtain a porous copper body having high strength.
  • the method for producing a porous copper composite member according to the invention is the method for producing a porous copper composite member including a bonded body of a member main body and a porous copper body including a skeleton of a three-dimensional network structure, and the method includes: a bonding step of bonding the above-described porous copper body and the member main body to each other.
  • the porous copper body produced by the above-described method for producing a porous copper body thus it is possible to obtain a porous copper composite member excellent in characteristics such as strength and the like.
  • the member main body include a plate, a rod, a tube, and the like.
  • a bonded surface of the member main body, to which the porous copper body is bonded consists of copper or a copper alloy, and the porous copper body and the member main body are bonded to each other by sintering.
  • the member main body and the porous copper body can be integrated with each other through the sintering, and thus it is possible to produce a porous copper composite member excellent in stability of characteristics.
  • a porous copper body which has high porosity and sufficient strength
  • a porous copper composite member in which this porous copper body is bonded to a member main body
  • a method for producing a porous copper body and a method for producing a porous copper composite member.
  • FIG. 1 is an enlarged schematic view of a porous copper body according to a first embodiment of the invention.
  • FIG. 2 is a graph showing circularity of a regular polygon.
  • FIG. 3 is a graph showing circularity of a rectangle.
  • FIG. 4 is a schematic explanatory view of a cross-sectional shape of one of the copper fibers forming a skeleton of the porous copper body shown in FIG. 1 .
  • FIG. 5 is a flowchart showing an example of a method for producing the porous copper body shown in FIG. 1 .
  • FIG. 6 is a view showing production steps of producing the porous copper body shown in FIG. 1 .
  • FIG. 7 is a view showing an external appearance of a porous copper composite member according to a second embodiment of the invention.
  • FIG. 8 is a flowchart showing an example of a method for producing the porous copper composite member shown in FIG. 7 .
  • FIG. 9 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 10 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 11 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 12 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 13 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 14 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 15 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • FIG. 16 is an external view of a porous copper composite member according to one of other embodiments of the invention.
  • the porous copper body 10 includes a skeleton 12 in which a plurality of copper fibers 11 are sintered.
  • a porosity P is in a range of 50% to 95%.
  • the porosity P is calculated by the following expression.
  • a relative tensile strength S/D A (N/mm 2 ) obtained by normalizing a tensile strength S (N/mm 2 ) with an apparent density ratio D A is 10.0 or greater.
  • the apparent density ratio D A is calculated by the following expression.
  • the copper fibers 11 forming the skeleton 12 consist of copper or a copper alloy, and a diameter R is in a range of 0.01 mm to 1.0 mm, and a ratio L/R of a length L to the diameter R is in a range of 4 to 200.
  • the copper fibers 11 consist of, for example, C1020 (oxygen-free copper).
  • the copper fiber 11 is subjected to shape imparting such as twisting and bending.
  • shape imparting such as twisting and bending.
  • an apparent density ratio D A is 0.50 or less of a true density D T of the copper fibers 11 .
  • a shape of the copper fiber 11 is an arbitrary shape such as a linear shape and a curved shape as long as the apparent density ratio D A is 0.50% or less of the true density D T of the copper fibers 11 .
  • a predetermined shape imparting processing such as twisting processing and bending processing
  • the copper fibers 11 are produced through adjustment into a predetermined diameter R by a drawing method, a coil cutting method, a wire cutting method, a melting spraying method, and the like, and length adjustment for satisfying predetermined L/R by cutting.
  • the diameter R is a value that is calculated on the basis of a cross-sectional area A of each fiber, and is defined by the following expression on the assumption that the cross-sectional shape is a perfect circle regardless of an actual cross-sectional shape.
  • the circularity C of a cross section orthogonal to the length direction is in a range of 0.2 to 0.9.
  • the circularity C is defined by the following expression when a cross-sectional area of the copper fiber 11 is represented as A and a circumferential length of the cross section of the copper fiber 11 is represented as Q.
  • Circularity C (4 ⁇ A ) 0.5 /Q
  • the circularity C is 1.
  • the circumferential length Q is longer than the cross-sectional area A, the circularity C becomes smaller. Accordingly, in the case where the cross section has a shape of a concave polygon such as a star shape or in the case where the cross section has a shape having a large aspect ratio, the circularity C decreases.
  • FIG. 2 shows a graph showing the circularity C of the regular polygon
  • FIG. 3 shows a graph showing a relationship between the aspect ratio and the circularity C in a rectangular cross section.
  • the copper fibers 11 forming the skeleton 12 are assumed to have a substantially triangular cross-sectional shape.
  • the diameter R of the copper fiber 11 is less than 0.01 mm, a bonding area between the copper fibers 11 is small, and thus there is a concern that sintering strength may be deficient.
  • the diameter R of the copper fiber 11 is greater than 1.0 mm, the number of contact points at which the copper fibers 11 come into contact with each other is deficient, and thus there is a concern that the sintering strength may also be deficient.
  • the diameter R of the copper fiber 11 is set to be in a range of 0.01 mm to 1.0 mm. Furthermore, it is preferable that the lower limit of the diameter R of the copper fiber 11 is set to be 0.03 mm or greater, and the upper limit of the diameter R of the copper fiber 11 is set to be 0.5 mm or less so as to further improve the strength.
  • the ratio L/R of the length L to the diameter R of the copper fiber 11 is less than 4, when the copper fibers 11 are laminated, it is difficult to set the bulk density D P to be 50% or less of the true density DT of the copper fibers 11 , and thus there is a concern that it is difficult to obtain the porous copper body 10 having high porosity P.
  • the ratio L/R of the length L to the diameter R of the copper fiber 11 is greater than 200, when the copper fibers 11 are laminated, it is difficult to uniformly disperse the copper fibers 11 , and thus there is a concern that it is difficult to obtain the porous copper body 10 having a uniform porosity P.
  • the ratio L/R of the length L to the diameter R of the copper fiber 11 is set to be in a range of 4 to 200. Furthermore, it is preferable that the lower limit of the ratio L/R of the length L to the diameter R of the copper fiber 11 is set to be 10 or greater so as to further improve the porosity P. In addition, it is preferable that the upper limit of the ratio L/R of the length L to the diameter R of the copper fiber 11 is set to be 100 or less so as to obtain the porous copper body 10 having a more uniform porosity P.
  • the cross-sectional shape of the copper fiber 11 forming the skeleton 12 is a concave polygonal shape such as a star shape and the circularity C is less than 0.2, unevenness of a surface of the copper fiber 11 is large and contacting portions between the copper fibers 11 are not secured, and thus there is a concern that the strength of the porous copper body 10 after sintering may be deficient.
  • the copper fiber 11 in the case where, in the cross-sectional shape of the copper fiber 11 forming the skeleton 12 , the aspect ratio between the long side and the short side becomes large and the circularity C becomes less than 0.2, the copper fiber 11 becomes a foil shape, and thus it becomes difficult to form voids between the copper fibers 11 at the time of filling; and as a result, there is a concern that the porosity P of the porous copper body 10 after sintering may decrease.
  • the cross-sectional shape approaches a perfect circle, and thus the contacting portions between the copper fibers 11 at the time of filling are in point contact. Therefore, bonding strength of the copper fibers 11 at each contact point decreases, and as a result, there is a concern that the strength of the porous copper body 10 after sintering may be deficient.
  • the circularity C of the cross section of the copper fiber 11 forming the skeleton 12 is set to be in a range of 0.2 to 0.9. Furthermore, it is preferable that the lower limit of the circularity C of the cross section of the copper fiber 11 forming the skeleton 12 is set to be 0.3 or greater, and the upper limit thereof is set to be 0.85 or less so as to further improve the porosity P and strength.
  • the above-described copper fibers 11 are distributed from a distributor 31 toward an inside of a graphite container 32 to bulk-fill the graphite container 32 . Thereby, the copper fibers 11 are laminated (copper fiber lamination step S 01 ).
  • a plurality of the copper fibers 11 are laminated so that a bulk density D P after the filling becomes 40% or less of the true density D T of the copper fibers 11 . Furthermore, in this embodiment, shape imparting processing such as twisting processing and bending processing is carried out with respect to copper fibers 11 , and thus it is possible to secure a three-dimensional and isotropic voids between the copper fibers 11 during lamination.
  • the copper fibers 11 with which the graphite container 32 is bulk-filled, are charged into an atmosphere furnace 33 and sintered by heating in a reducing atmosphere, an inert gas atmosphere, or a vacuum atmosphere (sintering step S 02 ).
  • Heating conditions of the sintering step S 02 in this embodiment are as follows. Specifically, a holding temperature is set to be in a range of 500° C. to 1050° C., and holding time is set to be in a range of 5 minutes to 600 minutes.
  • the holding temperature in the sintering step S 02 is lower than 500° C.
  • a sintering rate is slow and thus sintering may not proceed sufficiently.
  • the holding temperature in the sintering step S 02 is higher than 1050° C.
  • heating may be performed at a temperature near the melting point of copper, and thus a decrease in strength and porosity P may occur.
  • the holding temperature in the sintering step S 02 is set to be in a range of 500° C. to 1050° C. Furthermore, in the sintering step S 02 , it is preferable that the lower limit of the holding temperature is set to be 600° C. or higher, and the upper limit of the holding temperature is set to be 1000° C. or lower so as to reliably perform the sintering of the copper fibers 11 .
  • the holding time in the sintering step S 02 is set to be in a range of 5 minutes to 600 minutes.
  • the lower limit of the holding time is set to be 10 minutes or longer and the upper limit of the holding time is set to be 180 minutes or shorter so as to reliably perform the sintering of the copper fibers 11 .
  • a reducing gas such as a hydrogen gas, an RX gas, an ammonia decomposition gas, a nitrogen-hydrogen mixed gas, and an argon-hydrogen mixed gas may be used, and an inert gas such as a nitrogen gas and an argon gas may also be used. Further, a vacuum atmosphere of 100 Pa or less may also be used.
  • the sintering progresses at the contacting portion between the copper fibers 11 through the sintering step S 02 , and the copper fibers 11 are bonded to each other to form a skeleton 12 .
  • the sintering step S 02 is carried out in a reducing atmosphere, an inert atmosphere, and a vacuum atmosphere without pressurizing as described above, a bulk shape and a surface shape of the copper fiber 11 do not change significantly, and the circularity C of the cross section hardly changes before and after sintering.
  • the copper fibers 11 in which the diameter R is in a range of 0.01 mm to 1.0 mm and the ratio L/R of the length L to the diameter R is in a range of 4 to 200, are sintered to form the skeleton 12 , and thus sufficient voids are secured between the copper fibers 11 , and a shrinkage rate during the sintering can be suppressed to a low level. Accordingly, it is possible to attain high porosity P and excellent dimensional accuracy.
  • the circularity C of the cross section of the copper fiber 11 forming the skeleton 12 is in a range of 0.2 to 0.9, the contact area between the copper fibers 11 is secured and the strength after sintering can be enhanced. Also, it is possible to secure voids between the copper fibers 11 and to increase the porosity P.
  • the porous copper body 10 having a porosity P of 50% to 95% which is high and having excellent strength.
  • FIG. 7 shows the porous copper composite member 100 according to this embodiment.
  • the porous copper composite member 100 includes: a copper plate 120 (member main body) consisting of copper or a copper alloy; and a porous copper body 110 that is bonded to a surface of the copper plate 120 .
  • porous copper body 110 a plurality of copper fibers are sintered and a skeleton is formed in the same manner as in the first embodiment.
  • the porosity P is in a range of 50% to 95%.
  • the copper fibers forming the skeleton consist of copper or a copper alloy, and a diameter R is in a range of 0.01 mm to 1.0 mm, and a ratio L/R of a length L to the diameter R is in a range of 4 to 200.
  • the copper fibers consist of, for example, C1020 (oxygen-free copper).
  • the circularity C of the cross section orthogonal to the length direction is in a range of 0.2 to 0.9.
  • the copper fibers are subjected to shape imparting such as twisting and bending.
  • an apparent density ratio D A is 50% or less of a true density D T of the copper fibers.
  • the copper plate 120 that is a member main body is prepared (copper plate disposing step S 100 ).
  • copper fibers are dispersed and laminated on a surface of the copper plate 120 (copper fiber lamination step S 101 ).
  • the copper fiber lamination step S 101 a plurality of the copper fibers are laminated so that a bulk density D P becomes 40% or less of the true density D T of the copper fibers.
  • the copper fibers laminated on the surface of the copper plate 120 are sintered to form the porous copper body 110 , and the porous copper body 110 and the copper plate 120 are bonded to each other (sintering and bonding step S 102 ).
  • Heating conditions of the sintering and bonding step S 102 in this embodiment are as follows. Specifically, a holding temperature is set to be in a range of 500° C. to 1050° C., and holding time is set to be in a range of 5 minutes to 600 minutes.
  • a reducing atmosphere such as a hydrogen gas, an RX gas, an ammonia decomposition gas, a nitrogen-hydrogen mixed gas, and an argon-hydrogen mixed gas may be used, and an inert gas such as a nitrogen gas and an argon gas may also be used.
  • a vacuum atmosphere 100 Pa or less may also be used.
  • the copper fibers are sintered together to form the porous copper body 110 , and the copper fibers and the copper plate 120 are sintered to bond the porous copper body 110 and the copper plate 120 . Accordingly, the porous copper composite member 100 according to this embodiment is produced.
  • the porous copper composite member 100 of this embodiment having this configuration, since the circularity C of the cross section of the copper fiber forming the porous copper body 110 is in a range of 0.2 to 0.9, the contact area between the copper fibers is secured and the strength can be enhanced. Also, it is possible to secure voids between the copper fibers and to increase the porosity P of the porous copper body 110 .
  • porous copper composite member 100 is used as a heat exchanging member such as an evaporator or the like.
  • the copper fibers are laminated on the surface of the copper plate 120 consisting of copper or a copper alloy, and the sintering and bonding are simultaneously performed through the sintering and bonding step S 102 , and thus it is possible to simplify a producing process.
  • porous copper body is produced by using a producing facility shown in FIG. 6 .
  • the present invention is not limited thereto, and the porous copper body may be produced by using other producing facilities.
  • the copper fibers consisting of oxygen-free copper (JIS C1020) are used.
  • the present invention is not limited thereto, and pure copper such as phosphorus-deoxidized copper (JIS C1201, C1220) and tough pitch copper (JIS C1100) and a highly conductive copper alloy such as Cr copper (C18200) or Cr—Zr copper (C18150) may also be used.
  • a bonding method in which a sintered layer is formed at the bonded portion of the porous copper body and the member main body has been exemplified as a desirable method.
  • the present invention is not limited thereto, and the porous copper body and the member main body may also be bonded by using a bonding method such as various welding methods (laser welding method and resistance welding method) or a brazing method in which a brazing material having a low melting temperature is used.
  • the porous copper composite member having a structure shown in FIG. 7 is described as an example.
  • the present invention is not limited thereto, and it is also possible to employ a porous copper composite member having a structure as shown in FIG. 9 to FIG. 14 .
  • porous copper composite member 200 having a structure in which as a member main body, a plurality of copper tubes 220 are inserted into a porous copper body 210 .
  • porous copper composite member 300 having a structure in which as a member main body, a copper tube 320 curved in a U-shape is inserted into a porous copper body 310 .
  • porous copper composite member 400 having a structure in which a porous copper body 410 is bonded to an inner peripheral surface of a copper tube 420 that is a member main body.
  • porous copper composite member 500 having a structure in which a porous copper body 510 is bonded to an outer peripheral surface of a copper tube 520 that is a member main body.
  • porous copper composite member 600 having a structure in which porous copper bodies 610 are bonded to an inner peripheral surface and an outer peripheral surface of a copper tube 620 that is a member main body.
  • porous copper composite member 700 having a structure in which porous copper bodies 710 are bonded to both surfaces of a copper plate 720 that is a member main body.
  • porous copper composite member 800 having a structure in which a porous copper body 810 is bonded to an inner passage of a copper tube 820 that is a member main body.
  • porous copper composite member 900 having a structure in which a porous copper body 910 is bonded to both surfaces of a flat copper tube 920 that is a member main body.
  • Porous copper sintered bodies having a width of 30 mm, a length of 200 mm, and a thickness of 5 mm were produced by using sintering raw materials (copper fibers) shown in Table 1 in accordance with the producing method described in the above-described embodiment.
  • the diameter R, the ratio L/R of a length L to the diameter R, and the circularity C of the copper fiber to be used as a raw material were measured as follows.
  • the copper fibers to be used as the sintering raw material and the copper fibers sampled from the porous copper sintered body were respectively subjected to image analysis using a particle analyzer “Morphologi G3” manufactured by Malvern Instruments Co., Ltd., and thereby, the lengths of the copper fibers were measured, and the calculated simple average value thereof was used as the length L of the copper fiber. Using these, the ratio L/R of the length L to the diameter R was calculated.
  • Circularity C (4 ⁇ A ) 0.5 /Q
  • the true density D T (g/cm 3 ) was measured by Archimedes' principle using the precision balance, and the porosity P was calculated by the following expression.
  • the mass of the porous copper sintered body was represented as m (g), and the volume of the porous copper sintered body was represented as V (cm 3 ).
  • the obtained porous copper sintered body was processed into a test piece having a width of 10 mm, a length of 100 mm, and a thickness of 5 mm, and then the test piece was subjected to a tensile test using universal testing machines to measure the maximum tensile strength S (N/mm 2 ). Since the maximum tensile strength obtained by the measurement varies depending on an apparent density, in this example, a value (S/D A ) obtained by normalizing the maximum tensile strength S with the apparent density ratio D A was defined as a relative tensile strength.
  • the apparent density ratio D A was calculated by the following expression.
  • Comparative Example 1 in which the diameter R of the copper fiber was 0.008 mm and Comparative Example 2 in which the diameter R of the copper fiber was 1.20 mm, it was confirmed that the tensile strengths of the porous copper sintered bodies were low.
  • Comparative Example 5 in which the circularity C of the cross section of the copper fiber was 0.95, the tensile strength was low. The reason thereof is presumed to be that a shape of the cross section was close to a perfect circle and the contact between the copper fibers became a point contact.
  • Comparative Example 6 in which the shape of the cross section of the copper fiber was a star shape and the circularity C was 0.15, the tensile strength was low. The reason thereof is presumed to be that the unevenness of the surface of the copper fiber was large, and a contact point between the copper fibers was reduced.
  • the porosity was 50% or more which was high, and the tensile strength was sufficiently secured.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Composite Materials (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Powder Metallurgy (AREA)
US16/468,020 2017-01-18 2018-01-18 Copper porous body, copper porous composite member, method for producing copper porous body, and method for producing copper porous composite member Abandoned US20190381568A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2017-006749 2017-01-18
JP2017006749A JP6724801B2 (ja) 2017-01-18 2017-01-18 銅多孔質体、銅多孔質複合部材、銅多孔質体の製造方法、及び、銅多孔質複合部材の製造方法
PCT/JP2018/001370 WO2018135575A1 (fr) 2017-01-18 2018-01-18 Corps poreux en cuivre, élément composite poreux en cuivre, procédé de production de corps poreux en cuivre et procédé de production d'élément composite poreux en cuivre

Publications (1)

Publication Number Publication Date
US20190381568A1 true US20190381568A1 (en) 2019-12-19

Family

ID=62908106

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/468,020 Abandoned US20190381568A1 (en) 2017-01-18 2018-01-18 Copper porous body, copper porous composite member, method for producing copper porous body, and method for producing copper porous composite member

Country Status (7)

Country Link
US (1) US20190381568A1 (fr)
EP (1) EP3572169A4 (fr)
JP (1) JP6724801B2 (fr)
KR (1) KR20190108103A (fr)
CN (1) CN109803778A (fr)
TW (1) TW201842200A (fr)
WO (1) WO2018135575A1 (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2019176948A1 (ja) * 2018-03-12 2021-01-07 株式会社フジクラ 扁平型ヒートパイプ
EP4000710A1 (fr) * 2020-11-20 2022-05-25 Max-Planck-Gesellschaft zur Förderung der Wissenschaften e.V. Filtre
CN117637975A (zh) * 2023-12-04 2024-03-01 山东省科学院新材料研究所 一种三维多级锌负极片、水系锌离子电池电解液、水系锌离子电池

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08145592A (ja) 1994-11-16 1996-06-07 Hitachi Chem Co Ltd 伝熱部材およびその製造法
JP2000192107A (ja) * 1998-12-25 2000-07-11 Kogi Corp 多孔質金属及びその製造方法
JP3735712B2 (ja) 2002-03-12 2006-01-18 独立行政法人産業技術総合研究所 多孔質材料の作製方法及びその成形体
CN202671730U (zh) * 2012-06-15 2013-01-16 大连渡边过滤有限公司 纺丝组件
JP2015081399A (ja) * 2013-10-24 2015-04-27 Ｔｍｔマシナリー株式会社 フィルタ、及び、紡糸方法
JP6589402B2 (ja) * 2015-06-12 2019-10-16 三菱マテリアル株式会社 銅多孔質体、銅多孔質複合部材、銅多孔質体の製造方法、及び、銅多孔質複合部材の製造方法
JP6065059B2 (ja) * 2015-06-12 2017-01-25 三菱マテリアル株式会社 銅多孔質体、銅多孔質複合部材、銅多孔質体の製造方法、及び、銅多孔質複合部材の製造方法
JP2017006749A (ja) 2016-10-18 2017-01-12 株式会社藤商事 遊技機

Also Published As

Publication number Publication date
TW201842200A (zh) 2018-12-01
JP6724801B2 (ja) 2020-07-15
CN109803778A (zh) 2019-05-24
EP3572169A4 (fr) 2020-07-08
KR20190108103A (ko) 2019-09-23
JP2018115370A (ja) 2018-07-26
WO2018135575A1 (fr) 2018-07-26
EP3572169A1 (fr) 2019-11-27

Similar Documents

Publication Publication Date Title
US20190381568A1 (en) Copper porous body, copper porous composite member, method for producing copper porous body, and method for producing copper porous composite member
CN107614162B (zh) 铜多孔体、铜多孔复合部件、铜多孔体的制造方法及铜多孔复合部件的制造方法
US10532407B2 (en) Porous copper sintered material, porous copper composite part, method of producing porous copper sintered material, and method of producing porous copper composite part
US20180297118A1 (en) Porous copper body and porous copper composite part
CN107530776B (zh) 铜多孔体、铜多孔复合部件、铜多孔体的制造方法及铜多孔复合部件的制造方法
JP6589402B2 (ja) 銅多孔質体、銅多孔質複合部材、銅多孔質体の製造方法、及び、銅多孔質複合部材の製造方法
US20190076927A1 (en) Porous copper body, porous copper composite member, method for producing porous copper body, and method for producing porous copper composite member
WO2018212039A1 (fr) Corps en cuivre poreux, élément composite en cuivre poreux, procédé de production d'un corps en cuivre poreux et procédé de production d'un élément composite en cuivre poreux
US20240006617A1 (en) Nickel-chromium porous body and method of manufacturing nickel-chromium porous body
US20210262062A1 (en) Metal porous body and method for manufacturing metal porous body
JP6249060B2 (ja) 銅多孔質複合部材
JP2000247758A (ja) 熱伝導体

Legal Events

Date Code Title Description
AS Assignment

Owner name: MITSUBISHI MATERIALS CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KATO, JUN;KITA, KOICHI;SAIWAI, TOSHIHIKO;SIGNING DATES FROM 20190214 TO 20190220;REEL/FRAME:049414/0873

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION