US20190071757A1 - High-strength steel sheet and method for manufacturing same - Google Patents
High-strength steel sheet and method for manufacturing same Download PDFInfo
- Publication number
- US20190071757A1 US20190071757A1 US16/082,519 US201716082519A US2019071757A1 US 20190071757 A1 US20190071757 A1 US 20190071757A1 US 201716082519 A US201716082519 A US 201716082519A US 2019071757 A1 US2019071757 A1 US 2019071757A1
- Authority
- US
- United States
- Prior art keywords
- temperature
- less
- retained austenite
- cooling
- point
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 229910000831 Steel Inorganic materials 0.000 title claims abstract description 113
- 239000010959 steel Substances 0.000 title claims abstract description 113
- 238000004519 manufacturing process Methods 0.000 title claims description 29
- 238000000034 method Methods 0.000 title claims description 27
- 229910001566 austenite Inorganic materials 0.000 claims abstract description 135
- 230000000717 retained effect Effects 0.000 claims abstract description 127
- 229910000734 martensite Inorganic materials 0.000 claims abstract description 38
- 239000000203 mixture Substances 0.000 claims abstract description 37
- 229910000859 α-Fe Inorganic materials 0.000 claims abstract description 30
- 229910001563 bainite Inorganic materials 0.000 claims abstract description 27
- 229910052710 silicon Inorganic materials 0.000 claims abstract description 11
- 238000001816 cooling Methods 0.000 claims description 174
- 238000010438 heat treatment Methods 0.000 claims description 37
- 238000003303 reheating Methods 0.000 claims description 33
- 229910052761 rare earth metal Inorganic materials 0.000 claims description 7
- 229910052796 boron Inorganic materials 0.000 claims description 5
- 229910052804 chromium Inorganic materials 0.000 claims description 5
- 229910052802 copper Inorganic materials 0.000 claims description 5
- 229910052735 hafnium Inorganic materials 0.000 claims description 5
- 229910052750 molybdenum Inorganic materials 0.000 claims description 5
- 229910052759 nickel Inorganic materials 0.000 claims description 5
- 229910052758 niobium Inorganic materials 0.000 claims description 5
- 229910052719 titanium Inorganic materials 0.000 claims description 5
- 229910052720 vanadium Inorganic materials 0.000 claims description 5
- 229910052726 zirconium Inorganic materials 0.000 claims description 5
- 229910052742 iron Inorganic materials 0.000 claims description 4
- 239000002131 composite material Substances 0.000 claims description 3
- 239000012535 impurity Substances 0.000 abstract description 11
- 230000003247 decreasing effect Effects 0.000 description 23
- 230000009466 transformation Effects 0.000 description 23
- 230000007423 decrease Effects 0.000 description 15
- 230000000694 effects Effects 0.000 description 14
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 9
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 7
- 230000009471 action Effects 0.000 description 7
- 229910052799 carbon Inorganic materials 0.000 description 7
- 230000014759 maintenance of location Effects 0.000 description 7
- 230000015572 biosynthetic process Effects 0.000 description 6
- 239000002245 particle Substances 0.000 description 6
- 150000002910 rare earth metals Chemical class 0.000 description 6
- 238000012360 testing method Methods 0.000 description 6
- 238000005098 hot rolling Methods 0.000 description 5
- 238000005259 measurement Methods 0.000 description 5
- 239000000047 product Substances 0.000 description 5
- 238000009826 distribution Methods 0.000 description 4
- 238000001887 electron backscatter diffraction Methods 0.000 description 4
- 238000005482 strain hardening Methods 0.000 description 4
- 229910001567 cementite Inorganic materials 0.000 description 3
- 238000005097 cold rolling Methods 0.000 description 3
- 238000011156 evaluation Methods 0.000 description 3
- KSOKAHYVTMZFBJ-UHFFFAOYSA-N iron;methane Chemical compound C.[Fe].[Fe].[Fe] KSOKAHYVTMZFBJ-UHFFFAOYSA-N 0.000 description 3
- 230000007246 mechanism Effects 0.000 description 3
- 230000000630 rising effect Effects 0.000 description 3
- 229920006395 saturated elastomer Polymers 0.000 description 3
- 239000007787 solid Substances 0.000 description 3
- 238000005728 strengthening Methods 0.000 description 3
- 239000002699 waste material Substances 0.000 description 3
- 238000004458 analytical method Methods 0.000 description 2
- 238000005279 austempering Methods 0.000 description 2
- 238000004364 calculation method Methods 0.000 description 2
- 239000010960 cold rolled steel Substances 0.000 description 2
- 239000000470 constituent Substances 0.000 description 2
- 239000013078 crystal Substances 0.000 description 2
- 238000005530 etching Methods 0.000 description 2
- 239000000463 material Substances 0.000 description 2
- 230000004048 modification Effects 0.000 description 2
- 238000012986 modification Methods 0.000 description 2
- 238000001556 precipitation Methods 0.000 description 2
- 238000012545 processing Methods 0.000 description 2
- 238000007670 refining Methods 0.000 description 2
- 238000005096 rolling process Methods 0.000 description 2
- 238000009864 tensile test Methods 0.000 description 2
- 239000011573 trace mineral Substances 0.000 description 2
- 235000013619 trace mineral Nutrition 0.000 description 2
- 239000011800 void material Substances 0.000 description 2
- 244000137852 Petrea volubilis Species 0.000 description 1
- UCKMPCXJQFINFW-UHFFFAOYSA-N Sulphide Chemical compound [S-2] UCKMPCXJQFINFW-UHFFFAOYSA-N 0.000 description 1
- 238000002441 X-ray diffraction Methods 0.000 description 1
- 239000002253 acid Substances 0.000 description 1
- 229910052787 antimony Inorganic materials 0.000 description 1
- 229910052785 arsenic Inorganic materials 0.000 description 1
- 238000005266 casting Methods 0.000 description 1
- 238000009833 condensation Methods 0.000 description 1
- 230000005494 condensation Effects 0.000 description 1
- RKTYLMNFRDHKIL-UHFFFAOYSA-N copper;5,10,15,20-tetraphenylporphyrin-22,24-diide Chemical compound [Cu+2].C1=CC(C(=C2C=CC([N-]2)=C(C=2C=CC=CC=2)C=2C=CC(N=2)=C(C=2C=CC=CC=2)C2=CC=C3[N-]2)C=2C=CC=CC=2)=NC1=C3C1=CC=CC=C1 RKTYLMNFRDHKIL-UHFFFAOYSA-N 0.000 description 1
- 238000010586 diagram Methods 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 239000012467 final product Substances 0.000 description 1
- 238000005242 forging Methods 0.000 description 1
- 239000000446 fuel Substances 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 229910052747 lanthanoid Inorganic materials 0.000 description 1
- 150000002602 lanthanoids Chemical class 0.000 description 1
- 230000000670 limiting effect Effects 0.000 description 1
- 235000015250 liver sausages Nutrition 0.000 description 1
- 238000002844 melting Methods 0.000 description 1
- 230000008018 melting Effects 0.000 description 1
- 238000005272 metallurgy Methods 0.000 description 1
- 238000002156 mixing Methods 0.000 description 1
- 230000003287 optical effect Effects 0.000 description 1
- 230000036961 partial effect Effects 0.000 description 1
- 235000019362 perlite Nutrition 0.000 description 1
- 239000010451 perlite Substances 0.000 description 1
- 229910052698 phosphorus Inorganic materials 0.000 description 1
- 238000005554 pickling Methods 0.000 description 1
- 238000002360 preparation method Methods 0.000 description 1
- 239000002994 raw material Substances 0.000 description 1
- 230000009467 reduction Effects 0.000 description 1
- 230000002829 reductive effect Effects 0.000 description 1
- 230000002441 reversible effect Effects 0.000 description 1
- 229910052706 scandium Inorganic materials 0.000 description 1
- 150000003568 thioethers Chemical class 0.000 description 1
- 229910052718 tin Inorganic materials 0.000 description 1
- 229910052727 yttrium Inorganic materials 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D11/00—Process control or regulation for heat treatments
- C21D11/005—Process control or regulation for heat treatments for cooling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/0062—Heat-treating apparatus with a cooling or quenching zone
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
- C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/20—Ferrous alloys, e.g. steel alloys containing chromium with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
Definitions
- the present disclosure relates to a high-strength steel sheet usable for various applications including an automotive component, and a method for manufacturing the high-strength steel sheet.
- Patent Document 1 discloses as the high-strength steel sheet, a steel sheet that has a tensile strength of 980 to 1180 MPa and exhibits good deep drawability.
- the steel sheet is required to have not only high tensile strength and excellent deep drawability but also further excellent strength-ductility balance, high yield ratio and excellent hole expandability, i.e., a high hole expansion ratio when it is used for steel components for various application including a component for vehicles.
- each of the tensile strength, the strength-ductility balance, the yield ratio, the deep drawability, and the hole expansion ratio is required to attain a following level.
- the tensile strength is required to be 780 MPa or more.
- the steel sheet needs to have high yield strength (YS) in addition to high tensile strength (TS) in order to increase stress that can be applied to a component during usage. Further, from a viewpoint of securing collision safety and the like, it is necessary to increase the yield strength of the steel sheet.
- a product of TS and total elongation EL, TS ⁇ EL is required to be 22000 MPa % or more.
- an LDR Liting Drawing Ratio
- the hole expansion ratio 2 indicating the hole expandability is also required to be 20% or more.
- the high-strength steel sheet disclosed in Patent Document 1 has difficulty satisfying all these requirements, and a high-strength steel sheet has been demanded that is capable of satisfying all these requirements.
- Embodiments of the present invention have been made to meet these requirements, and an object of the embodiments is to provide a high-strength steel sheet that attains a high level in any of the tensile strength TS, the yield ratio YR, the product of TS and total elongation EL, TS ⁇ EL, the LDR indicating the deep drawability, and the hole expansion ratio ⁇ indicating the hole expandability, and a method for manufacturing the high-strength steel sheet.
- a high-strength steel sheet according to the embodiment of the present invention which has been capable of solving the above problems, contains, as component compositions, by mass:
- the steel structure further includes MA (martensite-austenite constituent), and the steel structure satisfies: an average circle equivalent diameter of the MA: 1.0 ⁇ m or less, an average circle equivalent diameter of the retained austenite: 1.0 ⁇ m or less, and a volume ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the whole retained austenite: 5% or more.
- MA martensite-austenite constituent
- An amount of C in the component composition is preferably 0.30% or less.
- An amount of Al in the component composition may be less than 0.10%.
- the high-strength steel sheet may further contain by mass:
- a method for manufacturing a high-strength steel sheet according to the embodiment of the present invention which has been capable of solving the above problems, is a method for manufacturing the high-strength steel sheet and includes steps A to E in this order:
- step B of rapidly cooling after the heating, from a rapid cooling start temperature T2 of 650° C. or higher to a cooling stop temperature T3a of 300 to 500° C. at an average cooling rate of 30° C./s or more and less than 200° C./s;
- the step C of performing gradual cooling after the rapid cooling in a temperature range from 300 to 500° C. at an average cooling rate of 0° C./s or more and 10° C./s or less for 10 seconds or more and less than 300 seconds;
- step D of cooling after the gradual cooling from a gradual cooling finish temperature T3b of 300° C. or higher to a cooling stop temperature T4 of 100 to 300° C. at an average cooling rate of more than 10° C./s; and the step E of reheating to a reheating temperature T5 of 300 to 500° C.
- the step C may include retaining at constant temperature in the temperature range from 300 to 500° C.
- the embodiment of the present invention it is possible to provide a high-strength steel sheet that attains a high level in any of the tensile strength TS, the yield ratio YR, the product of TS and total elongation EL, TS ⁇ EL, the hole expandability, and the deep drawability, and a method for manufacturing the high-strength steel sheet.
- FIG. 1 shows a diagram schematically illustrating a heat treatment of a manufacturing method according to an embodiment of the present invention.
- the prevent inventors have found that it is possible to obtain a high-strength steel sheet that attains a high level in any of the tensile strength TS, the yield ratio YR, the product of TS and total elongation EL, TS ⁇ EL, the hole expandability, and the deep drawability when the steel sheet has predetermined components and a steel structure.
- the present inventors have found that it is possible to achieve especially excellent deep drawability by suppressing an average particle diameter of retained austenite to a certain size or smaller while securing a certain ratio or more of relatively large retained austenite in the steel structure, and further that especially a multi-step austempering treatment is to be performed in a manufacturing step in order to obtain this steel structure.
- the embodiments of the present invention have been completed. First, the steel structure is described below.
- Ferrite is generally excellent in ductility but has a problem of being low in strength.
- an amount of ferrite is set to more than 5 area % in order to improve the ductility and obtain excellent strength-ductility balance.
- the amount of ferrite is preferably 7 area % or more, more preferably 10 area % or more.
- an excess amount of ferrite decreases the hole expandability and/or the yield ratio. Therefore, the amount of ferrite is set to 50 area % or less in order to secure an excellent hole expansion ratio ⁇ and a high yield ratio.
- the amount of ferrite is preferably 45 area % or less, more preferably 40 area % or less.
- Total of tempered martensite and bainite is set to 30 area % or more in the whole structure to be capable of attaining both high strength and high hole expandability.
- Bainite in the embodiments of the present invention refers to tempered bainite, untempered bainite and bainitic ferrite.
- the total of tempered martensite and bainite is preferably 35 area % or more.
- An upper limit of the total of tempered martensite and bainite is about 85 area %, in view of fractions of ferrite and retained austenite as other essential structures.
- Retained austenite causes, during processing such as press working, TRIP phenomenon where retained austenite transforms into martensite due to strain-induced transformation and is a structure capable of giving large elongation. Formed martensite has high hardness. Therefore, it is possible to obtain excellent strength-ductility balance. Further, it is also possible to increase the deep drawability by controlling a particle diameter distribution of retained austenite as described later.
- An amount of retained austenite is set to 10 volume % or more in order to obtain excellent strength-ductility balance especially with a TS ⁇ EL of 22000 MPa % or more and sufficiently produce an effect of improving the deep drawability by controlling a particle diameter distribution of retained austenite described later.
- the amount of retained austenite is preferably 12 volume % or more, more preferably 13 volume % or more, further preferably 14 volume % or more, still further preferably 15 volume % or more.
- An upper limit of the amount of retained austenite is around 40 volume %, in view of the component composition and the manufacturing conditions that are defined in the embodiments of the present invention, and the like.
- the MA is an abbreviation of a martensite-austenite constituent and a composite structure of martensite and austenite.
- the MA is a hard phase, and a vicinity of an interface between a parent phase and the hard phase serves as a void formation site during deformation.
- the MA having a coarser size more causes concentration of strain in the interface between the parent phase and the hard phase to easily generate fracture from the void, as a base point, formed in the vicinity of the interface between the parent phase and the hard phase. This results in a decrease of the hole expandability. Therefore, an average circle equivalent diameter of the MA is suppressed to 1.0 ⁇ m or less.
- the average circle equivalent diameter of the MA is preferably 0.8 ⁇ m or less, more preferably 0.7 ⁇ m or less.
- the average circle equivalent diameter of the MA is preferably smaller to increase the hole expandability. In view of the component composition and the manufacturing conditions that are defined in the embodiments of the present invention, however, a lower limit of the average circle equivalent diameter of the MA is around 0.2 ⁇ m.
- an area proportion of the MA including retained austenite is not especially limited, and an area proportion of retained austenite may be set to within the above range as described above.
- the amount of retained austenite is 10 volume % or more in the embodiments of the present invention, so that the MA where much of retained austenite exists may also exist by 10 area % or more.
- the present inventors have found that it is possible to achieve especially excellent deep drawability by suppressing an average particle diameter of retained austenite to a certain size or smaller while securing a certain ratio or more of relatively large retained austenite.
- reasons for this definition are described in detail.
- the present inventors have found that in order to maintain a high work hardening rate during deformation as described above, it is effective to cause strain-induced transformation over a wide stress range.
- the present inventors have focused on mixing unstable retained austenite that easily undergoes strain-induced transformation under relatively low stress, with stable retained austenite that undergoes strain-induced transformation only under high stress.
- the present inventors have studied to obtain steel structures including at predetermined amounts: relatively coarse retained austenite as the unstable retained austenite that contributes to suppressing martensite transformation in the flange portion and easily undergoes strain-induced transformation under relatively low stress in the longitudinal wall portion; and fine retained austenite as the stable retained austenite that undergoes strain-induced transformation only under high stress in the longitudinal wall portion.
- the present inventors have found that it is possible to maintain a high work hardening rate during deformation and thus exhibit excellent deep drawability by setting an average circle equivalent diameter of retained austenite to 1.0 ⁇ m or less and setting a volume ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the whole retained austenite to 5% or more.
- “relatively coarse retained austenite” is sometimes referred to as “relatively coarse retained austenite.”
- the average circle equivalent diameter of retained austenite is preferably 0.95 ⁇ m or less, more preferably 0.90 ⁇ m or less.
- a lower limit of the average circle equivalent diameter of retained austenite is around 0.40 ⁇ m, in view of the component composition and the manufacturing conditions that are defined in the embodiments of the present invention.
- the volume ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the whole retained austenite is preferably 10% or more, more preferably 15% or more.
- the volume ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more is preferably 50% or less, more preferably 40% or less.
- the average circle equivalent diameter of retained austenite, and the volume ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the whole retained austenite can be derived, as indicated in Examples described later, by preparing a phase map, using an EBSD (Electron Back Scatter Diffraction patterns) method, as a crystal analysis method with use of an SEM (Scanning Electron Microscope).
- EBSD Electron Back Scatter Diffraction patterns
- the metallographic structure of the steel sheet according to the embodiments of the present invention include, as described above, ferrite, tempered martensite, bainite, retained austenite, and the MA.
- the metallographic structure may be composed of only these structures but may also include a balance structure such as perlite within a scope that does not impair the effects of the present invention.
- C is an essential element for obtaining a desired structure such as retained austenite to secure high characteristics such as TS ⁇ EL.
- an amount of C is set to 0.15% or more.
- the amount of C is preferably 0.17% or more, more preferably 0.20% or more.
- the amount of C is set to 0.35% or less.
- the amount of C is preferably 0.33% or less, more preferably 0.30% or less.
- Si and Al respectively serve to suppress precipitation of cementite and promote formation of retained austenite.
- Si and Al are contained in an amount of 0.5% or more in total.
- the total of Si and Al is preferably 0.7% or more, more preferably 1.0% or more.
- the total of Si and Al is set to 2.5% or less, preferably 2.0% or less.
- Al may be contained in an addition amount that is the degree to which Al functions as a deoxidation element, that is, less than 0.10%.
- Al may be contained in a much amount, for example, in an amount of 0.7% or more.
- Mn is a necessary element to suppress formation of ferrite and secure tempered martensite/bainite and the like other than ferrite.
- an amount of Mn is set to 1.0% or more.
- the amount of Mn is preferably 1.5% or more, more preferably 2.0% or more.
- the amount of Mn is set to 4.0% or less, preferably 3.7% or less, more preferably 3.5% or less.
- the amount of P is set to 0.05% or less, preferably 0.03% or less.
- S inevitably exists as an impurity element.
- an amount of S is more than 0.01%, a sulfide-based inclusion such as MnS is formed that functions as an origin of breaking to decrease the hole expandability. Therefore, the amount of S is 0.01% or less, preferably 0.005% or less.
- the balance of the component composition of the high-strength steel sheet is Fe and inevitable impurities.
- the inevitable impurities trace elements such as, As, Sb and Sn are allowed to be incorporated, the trace elements being brought in depending on a situation such as a raw material, a material or manufacturing facilities.
- the “inevitable impurities” that constitute the balance are a concept other than an element whose composition range is separately defined.
- the high-strength steel sheet according to the embodiments of the present invention may further contain any other element as long as the steel sheet can retain the characteristics. Exemplified below are other elements that are experimentally considered to be selectively contained without impairing the effects of the present invention.
- Cu, Ni, Mo, Cr and B serve as elements that increase the tensile strength of the steel sheet, and are elements that stabilize retained austenite and effectively action to secure a predetermined amount of retained austenite.
- the elements are contained in a total amount of preferably 0.001% or more, more preferably 0.01% or more. When the elements are excessively contained, however, the effects of the elements are saturated to cause economical waste, so that the total amount of the elements is preferably 1.0% or less, more preferably 0.5% or less.
- the elements can be contained alone or in combination of any two or more elements selected.
- V, Nb, Ti, Zr and Hf are elements for manufacturing effects of precipitation strengthening and refining a structure and usefully action for high strengthening of the steel sheet.
- the elements are contained in a total amount of preferably 0.01% or more, more preferably 0.02% or more. When the elements are excessively contained, however, the effects of the elements are saturated to cause economical waste, so that the total amount of the elements is preferably 0.2% or less, more preferably 0.1% or less.
- the elements can be contained alone or in combination of any two or more elements selected.
- Ca, Mg and REM are elements that control a form of a sulfide in steel and effectively action to improve processability.
- the elements are contained in a total amount of preferably 0.001% or more, more preferably 0.002% or more. When the elements are excessively contained, however, the effects of the elements are saturated to cause economical waste, so that the total amount of the elements is preferably 0.01% or less and is further preferably set to 0.005% or less.
- the elements can be contained alone or in combination of any two or more elements selected. Examples of the REM include Sc, Y, lanthanoids and the like.
- the high-strength steel sheet according to the embodiments of the present invention attains a high level in any of the TS, the YR, the TS ⁇ EL, the and the LDR.
- the high-strength steel sheet according to the embodiments of the present invention is described in detail in terms of these characteristics.
- the high-strength steel sheet according to the embodiments of the present invention has a tensile strength of 780 MPa or more.
- the high-strength steel sheet has a tensile strength of preferably 880 MPa or more, more preferably 980 MPa or more.
- the strength is preferably higher, but an upper limit of the tensile strength is around 1300 MPa, in view of the component composition, the manufacturing conditions and the like of the steel sheet according to the embodiments of the present invention.
- the high-strength steel sheet according to the embodiments of the present invention has a yield ratio of 0.60 or more. Such a yield ratio together with the high tensile strength described above can realize high yield strength. As a result, a final product obtained by processing such as deep drawing is usable without deformation even if a high load is applied to it.
- the high-strength steel sheet preferably has a yield ratio of 0.65 or more. The yield ratio is preferably higher, but an upper limit of the yield ratio is around 0.75, in view of the component composition, the manufacturing conditions and the like of the steel sheet according to the embodiments of the present invention.
- the high-strength steel sheet according to the embodiments of the present invention has a TS ⁇ EL of 22000 MPa % or more.
- the high-strength steel sheet having a TS ⁇ EL of 22000 MPa % or more is capable of simultaneously having high strength and high ductility, attaining a high level of strength-ductility balance.
- the TS ⁇ EL is preferably 23000 MPa or more.
- the TS ⁇ EL is preferably higher, but an upper limit of the TS ⁇ EL is around 35000 MPa %, in view of the component composition, the manufacturing conditions and the like of the steel sheet according to the embodiments of the present invention.
- the high-strength steel sheet according to the embodiments of the present invention has a hole expansion ratio ⁇ of 20% or more. This can give excellent processability such as press formability.
- the high-strength steel sheet preferably has a hole expansion ratio ⁇ of 30% or more.
- the hole expansion ratio ⁇ is preferably higher, but an upper limit of the hole expansion ratio is around 60%, in view of the component composition, the manufacturing conditions and the like of the steel sheet according to the embodiments of the present invention.
- the deep drawability of the steel sheet is evaluated by the LDR as indicated in Examples described later.
- the high-strength steel sheet according to the embodiments of the present invention has an LDR of 2.05 or more, preferably 2.10 or more and thus has excellent deep drawability.
- the LDR is preferably higher, but an upper limit of the LDR is around 2.25, in view of the component composition, the manufacturing conditions and the like of the steel sheet according to the embodiments of the present invention.
- the high-strength steel sheet according to the embodiments of the present invention is excellent in any of the TS, the YR, the TS ⁇ EL, the and the LDR, so that the high-strength steel sheet is capable of being suitably used for steel-formed components for various application including a component for vehicles.
- the high-strength steel sheet is obtained that has the desired steel structure described above and thus has the desired characteristics described above, by performing, on an original sheet having the predetermined composition, a heating treatment including steps A to E described in detail below, especially, a multi-step austempering treatment.
- a heating treatment including steps A to E described in detail below, especially, a multi-step austempering treatment.
- the original sheet on which the heat treatment is performed there can be exemplified a hot-rolled steel sheet that has undergone hot rolling and a cold-rolled steel sheet that has further undergone cold rolling.
- Conditions of the hot rolling and the cold rolling are not especially limited.
- FIG. 1 schematically illustrating the heat treatment.
- Step A Step of Heating to Temperature T1 of (Ac 1 Point ⁇ 0.8+Ac 3 Point ⁇ 0.2) or Higher and Lower than Ac 3 Point]
- the step A corresponds to [ 2 ] in FIG. 1 .
- heating is performed to a temperature T1 of (Ac 1 point ⁇ 0.8+Ac 3 point ⁇ 0.2) or higher and lower than Ac 3 point.
- the heating temperature T1 is set to (Ac 1 point ⁇ 0.8+Ac 3 point ⁇ 0.2) or higher, preferably (Ac 1 point ⁇ 0.8+Ac 3 point ⁇ 0.2)+5° C.
- the heating temperature T1 is set to lower than Ac 3 point.
- the heating temperature T1 is preferably Ac 3 point—10° C. or lower, more preferably Ac 3 point—20° C. or lower.
- a retention time t1 in the heating temperature T1 is preferably 1 to 1800 seconds, in view of securement of the effects by the heating, productivity and the like.
- the Ac 1 and Ac 3 points are derived from following formulae (1) and (2) respectively that are described in “The Physical Metallurgy of Steels” by Leslie (published from Maruzen Co., Ltd., May 31, 1985, p. 273).
- each of the elements in the formula represents a content by mass % of the element in a steel sheet, and calculation is performed with an element that is not contained set as zero.
- the temperature may be raised at arbitrary heating rate.
- the temperature is raised from room temperature to the heating temperature T1 at an average heating rate HR1 of 1° C./s or more and 20° C./s or less.
- Step B step of cooling after heating, from rapid cooling start temperature T2 of 650° C. or higher to cooling stop temperature T3a of 300 to 500° C. at average cooling rate of 30° C./s or more and less than 200° C./s]
- the step B corresponds to [ 4 ] in FIG. 1 .
- rapid cooling is performed between a rapid cooling start temperature T2 of 650° C. or higher and a cooling stop temperature T3a of 300 to 500° C. at an average cooling rate CR2 of 30° C./s or more, thereby formation of excessive ferrite can be supressed.
- the average cooling rate CR2 is preferably 35° C./s or more, more preferably 40° C./s or more. When the average cooling rate CR2 is too high, however, excessive thermal strain is likely to be generated by sharp cooling, and thus the average cooling rate CR2 is set to less than 200° C./s, preferably 100° C./s or less.
- the rapid cooling at an average cooling rate CR2 of 30° C./s or more is started from the rapid cooling start temperature T2 of 650° C. or higher.
- the rapid cooling start temperature T2 is preferably 680° C. or higher, more preferably 700° C. or higher.
- An upper limit of the rapid cooling start temperature T2 is not especially limited and may be the heating temperature T1 or lower.
- the cooling stop temperature T3a of 300 to 500° C. is rapid cooling finish temperature at which the rapid cooling is finished and is also start temperature of gradual cooling in the step C described below.
- the temperature T3a is higher than 500° C., that is, if the rapid cooling is stopped in a high temperature range, a carbon-condensed region excessively increases to coarsen not only retained austenite but also the MA, and thus the hole expansion ratio is decreased.
- the temperature T3a is preferably 480° C. or lower, more preferably 460° C. or lower.
- the temperature T3a is lower than 300° C., that is, if the rapid cooling is performed to a low temperature range, the carbon-condensed region decreases to result in being unable to secure relatively coarse retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more, and thus the deep drawability is decreased.
- the temperature T3a is preferably 320° C. or higher, more preferably 340° C. or higher.
- an average cooling rate CR1 is not especially limited, which is employed in a temperature decrease from the heating temperature T1 to 650° C. illustrated by [ 3 ] in FIG. 1 .
- the average cooling rate CR1 there can be exemplified cooling at a relatively low average cooling rate of 0.1° C./s or more and 10° C./s or less.
- Step C step of performing gradual cooling after rapid cooling, in temperature range from 300 to 500° C. at average cooling rate of 0° C./s or more and 10° C./s or less for 10 seconds or more and less than 300 seconds after rapid cooling]
- the step C corresponds to [ 5 ] in FIG. 1 .
- a temperature range from a gradual cooling start temperature, i.e., the rapid cooling finish temperature T3a to a gradual cooling finish temperature T3b illustrated in FIG. 1 is 300 to 500° C.
- An average cooling rate from the T3a to the T3b is set to 0° C./s or more and 10° C./s or less, and a time from the T3a to the T3b, that is, a gradual cooling time t3 is set to 10 seconds or more and less than 300 seconds.
- Bainite has a lower solid solubility limit of carbon than a solid solubility limit of austenite, so that carbon exceeding the solid solubility limit is discharged. This results in forming a region of austenite where carbon is condensed around bainite. This region undergoes cooling in the step D and reheating in the step E that are described later to become relatively coarse retained austenite. Existence of this relatively coarse retained austenite enables an increase of the deep drawability as described above.
- the temperature T3a is preferably 480° C. or lower, more preferably 460° C. or lower.
- the gradual cooling finish temperature T3b is lower than 300° C., the carbon-condensed region is refined due to progress of bainite transformation at low temperature to be unable to sufficiently secure relatively coarse retained austenite, and thus the deep drawability is decreased.
- the temperature T3b is preferably 320° C. or higher, more preferably 340° C. or higher.
- the gradual cooling time t3 is set to 10 seconds or more, preferably 30 seconds or more, more preferably 50 seconds or more.
- the gradual cooling time t3 is set to less than 300 seconds, preferably 200 seconds or less, more preferably 100 seconds or less, further preferably 80 seconds or less, still further preferably 60 seconds or less.
- the average cooling rate of the gradual cooling is more than 10° C./s, sufficient bainite transformation does not occur, as a result, sufficient carbon-condensed region does not form and thus the amount of relatively coarse retained austenite becomes insufficient.
- the average cooling rate is preferably 8° C./s or less, more preferably 3° C./s or less. Retaining at an average cooling rate of 0° C./s, that is, at constant temperature may be performed. Alternatively, the cooling rate may be changed within the above range in the above temperature range, or the gradual cooling may be combined with the retaining at constant temperature.
- the gradual cooling there can be exemplified gradual cooling in a temperature range from 320 to 480° C. at an average cooling rate of 0° C./s or more and 8° C./s or less for 30 to 80 seconds. More preferably, the gradual cooling is performed in a temperature range from 340 to 460° C. at an average cooling rate of 0° C./s or more and 3° C./s or less for 50 to 60 seconds.
- Patent Document 1 it is considered that the gradual cooling is not performed but reheating after excessive cooling is carried out. As a result, in Patent Document 1, it is considered that the amount of relatively coarse retained austenite, that is, the ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more is low and thus deep drawability is inferior to that of the steel sheet of the present invention.
- Step D step of cooling after gradual heating, from gradual cooling finish temperature T3b of 300° C. or higher to cooling stop temperature T4 of 100 to 300° C. at average cooling rate of more than 10° C./s]
- the step D corresponds to [ 6 ] in FIG. 1 .
- cooling is performed from the gradual cooling finish temperature T3b of 300° C. or higher to a cooling stop temperature T4 of 100 to 300° C. at an average cooling rate CR3 of more than 10° C./s to allow a part of the carbon-condensed region to undergo martensite transformation.
- This enables refining of the remaining carbon-condensed region that has not undergone martensite transformation, and thus fine MA is obtained.
- the average cooling rate CR3 is 10° C./s or less, the carbon-condensed region outspreads more than necessary during the cooling to coarsen the MA, and thus the hole expansion ratio is decreased.
- the average cooling rate CR3 is preferably 15° C./s or more, more preferably 20° C./s or more.
- the gradual cooling finish temperature T3b is 500° C. or lower as described in the step C.
- the stop temperature T4 of the cooling at the average cooling rate CR3 is controlled in a temperature range from 100 to 300° C. to adjust an amount of remaining austenite that does not undergo martensite transformation and thus control an amount of a final amount of retained austenite.
- the cooling stop temperature T4 is preferably 120° C. or higher, more preferably 140° C. or higher.
- the cooling stop temperature T4 is set to 300° C. or lower.
- the cooling stop temperature T4 is preferably 280° C. or lower, more preferably 260° C. or lower.
- the gradual cooling finish temperature T3b is set to a cooling start temperature as illustrated by [ 6 ] in FIG. 1 .
- retaining at the cooling stop temperature T4 may be performed as illustrated by [ 7 ] in FIG. 1 or reheating treatment described later may be performed without the retaining.
- a retention time t4 is preferably set to 1 to 600 seconds. This is because the retention time t4 hardly affects the characteristics even when being long, but decreases productivity when being more than 600 seconds.
- Step E Step of Reheating to Reheating Temperature T5 of 300 to 500° C.
- the step E corresponds to [ 9 ] in FIG. 1 .
- reheating to a reheating temperature T5 of 300 to 500° C. is performed and retaining is performed at the reheating temperature T5 to discharge carbon in martensite and thus promote condensation of carbon in austenite around martensite, and austenite can be stabilized. This enables an increase in the amount of retained austenite eventually obtained.
- the reheating temperature T5 is set to 300° C. or higher, preferably 320° C. or higher, more preferably 340° C. or higher.
- the reheating temperature T5 is set to 500° C. or lower, preferably 480° C. or lower, more preferably 460° C. or lower.
- a reheating time t5 during retaining at the reheating temperature T5 is not especially limited and is, for example, 50 seconds or more, further 70 seconds or more, further 90 seconds or more.
- An upper limit of the reheating time t5 is, for example, 1200 seconds or less, further 900 seconds or less, further 600 seconds or less.
- An average heating rate HR2 is not especially limited in a temperature rising step illustrated by [ 8 ] in FIG. 1 from the cooling stop temperature T4 to the reheating temperature T5. Cooling illustrated by [ 10 ] in FIG. 1 after the reheating may be preferably performed to 200° C. or lower, for example, room temperature at an average cooling rate CR4 of 2 to 20° C./s.
- a casting material having component composition (with the balance being iron and inevitable impurities) described in Table 1 was produced by vacuum melting and then subjected to hot forging to form a sheet with a sheet thickness of 30 mm, followed by hot rolling.
- Table 1 also shows values of the Ac 1 and Ac 3 points and “0.8 ⁇ Ac 1 point+0.2 ⁇ Ac 3 point” that were calculated from the component composition.
- hot rolling the sheet that had been heated to 1200° C. was subjected to multistage rolling to have a sheet thickness of 2.5 mm. At this time, hot rolling finish temperature was set to 880° C. Then, the sheet was cooled to 600° C. at 30° C./s, inserted into a furnace heated to 600° C.
- the hot-rolled steel sheet was subjected to acid pickling to remove scale on a surface of the steel sheet and subjected to cold rolling to give a 1.4 mm cold-rolled steel sheet as an original sheet.
- This original pate was subjected to a heat treatment under conditions indicated in Tables 2-1 and 2-2 to give a sample.
- the average heating rate H2 was set to 30° C./s in the temperature rising step from the cooling stop temperature T4 to the reheating temperature T5.
- the samples obtained were evaluated for a steel structure and characteristics as described below.
- the sample was electrolytically polished, then subjected to LePera etching, observed by 3 fields (100 ⁇ m ⁇ 100 ⁇ m size/field) with an optical microscope (1000 times), and measured for an area proportion of ferrite by a point arithmetic method with 20 ⁇ 20 grating points at a grating space of 5 ⁇ m, and an average value of area proportions of ferrite was calculated.
- the value derived in the area ratio can be directly used as a value of a volume proportion (volume %).
- An area proportion of the total of tempered martensite and bainite was derived by deducting the fraction of ferrite described above and the fraction of the MA derived by a following method, that is, the total of retained austenite and martensite that has been only quenched, from the whole structure.
- the sample was electrolytically polished, then subjected to nital etching, observed by 3 fields (20 ⁇ m ⁇ 20 ⁇ m size/field) with an SEM (5000 times), and measured for an average circle equivalent diameter of the MA by drawing 20 straight lines with a length of 10 ⁇ m at arbitrary positions in a photograph, measuring length of segments of the MA that intersect with the straight lines, and calculating an average value of the length of the segments.
- the area proportion of the MA is calculated on the basis of the average circle equivalent diameter of the MA and the number of MAs observed in a field, and an average of the three fields was derived.
- the amount of retained austenite can be obtained by deriving through X-ray diffraction a diffraction intensity ratio between ferrite, bainite, tempered martensite and martensite as body-centered cubic lattices or body-centered tetragonal lattices and austenite as a face-centered cubic lattice and by calculation based on the diffraction intensity ratio.
- measurement was as follows.
- the sample was polished to a position of 1 ⁇ 4 the sheet thickness using #1000 to #1500 sand paper, and then the surface was further electrolytically polished to a depth of about 10 to 20 ⁇ m and measured using a two dimensional micro area X-ray diffractometer (RINT-RAPIDII) manufactured by Rigaku Corporation, as a X-ray diffractometer.
- RINT-RAPIDII two dimensional micro area X-ray diffractometer manufactured by Rigaku Corporation, as a X-ray diffractometer.
- the measurement was performed using a Co target, using a Co-K ⁇ ray as an X-ray source, at an output of about 40 kV-200 mA, in a 20 range from 40° to 130°.
- the average circle equivalent diameter of retained austenite, and the ratio of the amount of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the amount of the whole retained austenite are derived as described above by preparing a phase map according to an EBSD method which is a crystal analysis with use of an SEM.
- EBSD method which is a crystal analysis with use of an SEM.
- a surface of the sample was electrolytically polished, and EBSD measurement (OIM system manufactured by TexSEM Laboratories, Inc.) was performed at a position of 1 ⁇ 4 the sheet thickness by total three regions (100 ⁇ m ⁇ 100 ⁇ m size per region) at 180,000 points with one step of 0.25 ⁇ m.
- Integrated area was derived for retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more, and the ratio of the integrated area to the total area of retained austenite phases was derived to obtain the ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the whole retained austenite.
- the thus-derived ratio of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more to the whole retained austenite is an area ratio but is equivalent to a volume ratio.
- Table 3 shows results of measuring these steel structures.
- Table 3 indicates ferrite as “F,” tempered martensite and bainite as “tempered MB,” retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more as “retained ⁇ with 1.5 ⁇ m or more.”
- the sample obtained was subjected to a tensile test as indicated below to measure the yield strength YS, the tensile strength TS, and the total elongation EL, and the yield ratio YR and the TS ⁇ EL were calculated. Further, the hole expansion ratio ⁇ was measured by a method indicated below and the deep drawability was evaluated.
- test piece specified in JIS Z2201 was taken from the sample such that a direction perpendicular to the rolling direction is a longitudinal direction. Then, the test piece was subjected to a tensile test with a tensile tester under conditions of JIS Z2241 to derive the YS, the TS, the YR, the EL and the TS ⁇ EL. Then, a test piece having the TS of 780 MPa or more, the YR of 0.60 or more, and the TS ⁇ EL of 22000 MPa % or more was evaluated as having high strength, a high yield ratio, and excellent strength-ductility balance.
- the hole expansion ratio ⁇ was derived according to The Japan Iron and Steel Federation Standard JFS T1001.
- JFS T1001 The Japan Iron and Steel Federation Standard.
- the deep drawability was evaluated by the LDR.
- the LDR is derived as follows. That is, d is defined as a diameter of a cylinder obtained by cylinder drawing, and D is defined as a maximum diameter of a disk-shaped steel sheet (blank) capable of giving a cylinder without fracture in one time of deep drawing. Then, the LDR is derived from d/D.
- disk-shaped specimens with a sheet thickness of 1.4 mm and various diameters were subjected to cylinder deep drawing with a die having a punch diameter of 50 mm, a punch angle radius of 6 mm, a die diameter of 55.2 mm, and a die angle radius of 8 mm, the diameter (maximum diameter D) of a specimen that had been drawn without fracture was measured, and the d/D was derived and defined as the LDR.
- a specimen having an LDR of 2.05 or more was evaluated as having excellent deep drawability.
- any of Nos. 1, 2, 7, 11 to 16, 20, 22 to 27 and 34 to 40 have the component composition defined in the embodiments of the present invention and was produced under the defined conditions to obtain the desired steel structure, so that these exhibit not only high tensile strength and excellent deep drawability but also excellent strength-ductility balance, a high yield ratio, and excellent hole expandability, i.e., a high hole expansion ratio.
- No. 3 was manufactured by the condition of an excessively high heating temperature T1 to be unable to secure ferrite, and thus TS ⁇ EL was decreased.
- No. 4 was manufactured by the condition of an excessively high rapid cooling stop temperature, i.e., an excessively high gradual cooling start temperature T3a to give a coarse MA. This resulted in a decrease of the hole expandability.
- No. 5 was manufactured by the condition of an excessively low reheating temperature T5 to be unable to secure a certain amount or more of retained austenite and thus the TS ⁇ EL and the deep drawability were decreased.
- No. 6 was manufactured by the condition of an excessively low cooling stop temperature T4 after the cooling at the average cooling rate CR3 to be unable to secure a certain amount or more of retained austenite, and thus the TS ⁇ EL and the deep drawability were decreased.
- No. 8 was manufactured by the condition of an excessively high reheating temperature T5 to be unable to secure a certain amount or more of retained austenite, and thus the TS ⁇ EL and the deep drawability were decreased.
- No. 9 was manufactured by the condition of excessively low temperatures T3a and T3b for the gradual cooling, to be unable to secure retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more, and thus the deep drawability was decreased.
- No. 10 was manufactured by the condition of an excessively low average cooling rate CR3 after the gradual cooling to the cooling stop temperature T4 of 100 to 300° C. to coarsen the MA, and thus the hole expandability was decreased.
- No. 17 is an example of retaining at 400° C. for 300 seconds after the rapid cooling illustrated by [ 4 ] in FIG. 1 and cooling to room temperature, without performing [ 6 ] to [ 9 ] in FIG. 1 .
- the cooling at the average cooling rate CR3 and the reheating were not performed to cause no martensite transformation, and the MA and retained austenite were coarsened. This resulted in a decrease of the hole expandability.
- No. 18 is an example of rapidly cooling the original sheet from a rapid cooling start temperature of 700° C. to a stop temperature of 200° C. at an average cooling rate of 40° C. without a holding step illustrated by [ 5 ] in FIG. 1 .
- No. 19 was manufactured by the condition of a long gradual cooling time t3 to coarsen the MA, and thus the hole expandability was decreased.
- No. 21 was manufactured by the condition of a short gradual cooling time t3 to be short of the amount of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more, and thus the deep drawability was decreased.
- No. 28 had an excessively small amount of C to be short of the amount of retained austenite, and thus the TS ⁇ EL was especially decreased.
- No. 29 had an excessive amount of C to coarsen the MA and retained austenite, and thus both the deep drawability and the hole expandability were decreased.
- No. 30 was short of the amount of Si+Al to be short of the amount of retained austenite, and thus the TS ⁇ EL was decreased.
- No. 31 had an excessive amount of Si+Al to be short of tempered martensite/bainite, and the MA and retained austenite were coarsened. This resulted in a low yield ratio and a decrease of the hole expandability. No. 31, however, had a remarkably different structure from the structures defined in the embodiments of the present invention, so that retained austenite had a coarse average circle equivalent diameter but the deep drawability was secured.
- No. 32 is an example of obtaining no sufficient tempered martensite and bainite because the amount of Mn was short to excessively increase ferrite. This resulted in a decrease of the TS and the YR.
- No. 33 had an excessive amount of the Mn to be short of the amount of retained austenite with a circle equivalent diameter of 1.5 ⁇ m or more, and thus the deep drawability was decreased.
- step C includes retaining at constant temperature in the temperature range from 300 to 500° C.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Heat Treatment Of Strip Materials And Filament Materials (AREA)
Applications Claiming Priority (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016072740 | 2016-03-31 | ||
JP2016-072740 | 2016-03-31 | ||
JP2016-253902 | 2016-12-27 | ||
JP2016253902A JP6762868B2 (ja) | 2016-03-31 | 2016-12-27 | 高強度鋼板およびその製造方法 |
PCT/JP2017/006608 WO2017169329A1 (ja) | 2016-03-31 | 2017-02-22 | 高強度鋼板およびその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20190071757A1 true US20190071757A1 (en) | 2019-03-07 |
Family
ID=60044002
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/082,519 Abandoned US20190071757A1 (en) | 2016-03-31 | 2017-02-22 | High-strength steel sheet and method for manufacturing same |
Country Status (6)
Country | Link |
---|---|
US (1) | US20190071757A1 (zh) |
EP (1) | EP3438309B1 (zh) |
JP (1) | JP6762868B2 (zh) |
KR (1) | KR102184257B1 (zh) |
CN (1) | CN108779533B (zh) |
MX (1) | MX2018010467A (zh) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20210324492A1 (en) * | 2018-10-18 | 2021-10-21 | Jfe Steel Corporation | Steel sheet and method for producing same |
US20210340653A1 (en) * | 2018-12-11 | 2021-11-04 | Nippon Steel Corporation | High-strength steel plate having excellent formability, toughness and weldability, and production method of same |
Families Citing this family (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2020039485A1 (ja) * | 2018-08-20 | 2020-02-27 | 日本製鉄株式会社 | 鋼板およびその製造方法 |
WO2020080401A1 (ja) * | 2018-10-17 | 2020-04-23 | Jfeスチール株式会社 | 鋼板およびその製造方法 |
EP3845673A4 (en) * | 2018-10-17 | 2021-07-14 | JFE Steel Corporation | SHEET STEEL AND ITS MANUFACTURING PROCESS |
US20210381076A1 (en) * | 2018-10-17 | 2021-12-09 | Jfe Steel Corporation | Thin steel sheet and method for manufacturing same |
ES2939457T3 (es) * | 2018-11-30 | 2023-04-24 | Arcelormittal | Lámina de acero recocida laminada en frío con alta relación de expansión de orificios y procedimiento de fabricación de la misma |
JP6828855B1 (ja) * | 2019-03-29 | 2021-02-10 | Jfeスチール株式会社 | 鋼板およびその製造方法 |
KR102321285B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102353611B1 (ko) * | 2019-12-18 | 2022-01-20 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102321292B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102321287B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102321288B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102321295B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102348529B1 (ko) * | 2019-12-18 | 2022-01-07 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102348527B1 (ko) * | 2019-12-18 | 2022-01-07 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102321297B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102485006B1 (ko) * | 2020-12-17 | 2023-01-04 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102485009B1 (ko) * | 2020-12-17 | 2023-01-04 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102485007B1 (ko) * | 2020-12-17 | 2023-01-04 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102485013B1 (ko) * | 2020-12-17 | 2023-01-04 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102485004B1 (ko) * | 2020-12-17 | 2023-01-04 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
KR102485012B1 (ko) * | 2020-12-17 | 2023-01-04 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
JP7146127B1 (ja) | 2022-03-31 | 2022-10-03 | 株式会社神戸製鋼所 | 高強度鋼板の製造方法 |
Family Cites Families (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5151246B2 (ja) * | 2007-05-24 | 2013-02-27 | Jfeスチール株式会社 | 深絞り性と強度−延性バランスに優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板ならびにその製造方法 |
JP5369663B2 (ja) | 2008-01-31 | 2013-12-18 | Jfeスチール株式会社 | 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5883211B2 (ja) * | 2010-01-29 | 2016-03-09 | 株式会社神戸製鋼所 | 加工性に優れた高強度冷延鋼板およびその製造方法 |
JP5662902B2 (ja) * | 2010-11-18 | 2015-02-04 | 株式会社神戸製鋼所 | 成形性に優れた高強度鋼板、温間加工方法、および温間加工された自動車部品 |
JP5667471B2 (ja) * | 2011-03-02 | 2015-02-12 | 株式会社神戸製鋼所 | 温間での深絞り性に優れた高強度鋼板およびその温間加工方法 |
JP5685167B2 (ja) * | 2011-03-31 | 2015-03-18 | 株式会社神戸製鋼所 | 加工性に優れた高強度鋼板およびその製造方法 |
CN103459638B (zh) * | 2011-03-31 | 2015-07-15 | 株式会社神户制钢所 | 加工性优异的高强度钢板及其制造方法 |
JP5685166B2 (ja) * | 2011-03-31 | 2015-03-18 | 株式会社神戸製鋼所 | 加工性に優れた高強度鋼板およびその製造方法 |
US9745639B2 (en) * | 2011-06-13 | 2017-08-29 | Kobe Steel, Ltd. | High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof |
JP5480215B2 (ja) * | 2011-09-08 | 2014-04-23 | 株式会社神戸製鋼所 | 引張強さ780MPa以上の低降伏比厚肉円形鋼管用鋼板およびその製造方法、並びに引張強さ780MPa以上の低降伏比厚肉円形鋼管 |
CN104169444B (zh) * | 2012-03-30 | 2017-03-29 | 奥钢联钢铁有限责任公司 | 高强度冷轧钢板和生产这种钢板的方法 |
JP5609945B2 (ja) * | 2012-10-18 | 2014-10-22 | Jfeスチール株式会社 | 高強度冷延鋼板およびその製造方法 |
JP5632947B2 (ja) * | 2012-12-12 | 2014-11-26 | 株式会社神戸製鋼所 | 加工性と低温靭性に優れた高強度鋼板およびその製造方法 |
EP3178949B1 (en) * | 2014-08-07 | 2020-01-29 | JFE Steel Corporation | High-strength steel sheet and method for manufacturing same |
WO2016021197A1 (ja) * | 2014-08-07 | 2016-02-11 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法 |
-
2016
- 2016-12-27 JP JP2016253902A patent/JP6762868B2/ja not_active Expired - Fee Related
-
2017
- 2017-02-22 CN CN201780017681.4A patent/CN108779533B/zh not_active Expired - Fee Related
- 2017-02-22 MX MX2018010467A patent/MX2018010467A/es unknown
- 2017-02-22 KR KR1020187030749A patent/KR102184257B1/ko active IP Right Grant
- 2017-02-22 EP EP17773875.4A patent/EP3438309B1/en active Active
- 2017-02-22 US US16/082,519 patent/US20190071757A1/en not_active Abandoned
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20210324492A1 (en) * | 2018-10-18 | 2021-10-21 | Jfe Steel Corporation | Steel sheet and method for producing same |
US20210340653A1 (en) * | 2018-12-11 | 2021-11-04 | Nippon Steel Corporation | High-strength steel plate having excellent formability, toughness and weldability, and production method of same |
Also Published As
Publication number | Publication date |
---|---|
MX2018010467A (es) | 2018-11-29 |
KR102184257B1 (ko) | 2020-11-30 |
JP2017186647A (ja) | 2017-10-12 |
JP6762868B2 (ja) | 2020-09-30 |
CN108779533B (zh) | 2020-11-03 |
CN108779533A (zh) | 2018-11-09 |
EP3438309B1 (en) | 2021-05-12 |
EP3438309A4 (en) | 2019-10-09 |
KR20180125560A (ko) | 2018-11-23 |
EP3438309A1 (en) | 2019-02-06 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20190071757A1 (en) | High-strength steel sheet and method for manufacturing same | |
US11466337B2 (en) | High-strength steel sheet and method for producing same | |
CA2866130C (en) | High-strength cold-rolled steel sheet and method for manufacturing the same | |
KR102205432B1 (ko) | 강판 및 도금 강판 | |
JP6860420B2 (ja) | 高強度鋼板およびその製造方法 | |
JP6875916B2 (ja) | 高強度鋼板およびその製造方法 | |
KR101532492B1 (ko) | 성형성이 우수한 고강도 강판, 온간 가공 방법 및 온간 가공된 자동차 부품 | |
KR101609968B1 (ko) | 열간 프레스용 강판 및 프레스 성형품, 및 프레스 성형품의 제조 방법 | |
KR100778264B1 (ko) | 신장 특성 및 신장 플랜지 특성이 우수한 고장력열연강판과 그 제조방법 | |
WO2014061270A1 (ja) | 高強度冷延鋼板およびその製造方法 | |
JP2016050343A (ja) | 耐水素脆化特性に優れた超高強度冷延鋼板およびその製造方法 | |
CA2923585A1 (en) | Hot-pressing steel plate, press-molded article, and method for manufacturing press-molded article | |
US20160222483A1 (en) | Method for manufacturing press-molded article, and press-molded article | |
WO2017208759A1 (ja) | 高強度鋼板およびその製造方法 | |
JP2013185248A (ja) | 熱間プレス用鋼板およびプレス成形品、並びにプレス成形品の製造方法 | |
JP6762797B2 (ja) | 高強度鋼板およびその製造方法 | |
WO2017169329A1 (ja) | 高強度鋼板およびその製造方法 | |
JP5869924B2 (ja) | プレス成形品の製造方法およびプレス成形品 | |
JP6875914B2 (ja) | 高強度鋼板およびその製造方法 | |
JP2018090877A (ja) | 高強度鋼板およびその製造方法 | |
JP2021161479A (ja) | 鋼材およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MURATA, TADAO;MURAKAMI, TOSHIO;KAKIUCHI, ELIJAH;AND OTHERS;REEL/FRAME:046795/0363 Effective date: 20170701 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STCB | Information on status: application discontinuation |