US20150200341A1 - Manufacturing method for light-emitting device - Google Patents
Manufacturing method for light-emitting device Download PDFInfo
- Publication number
- US20150200341A1 US20150200341A1 US14/670,256 US201514670256A US2015200341A1 US 20150200341 A1 US20150200341 A1 US 20150200341A1 US 201514670256 A US201514670256 A US 201514670256A US 2015200341 A1 US2015200341 A1 US 2015200341A1
- Authority
- US
- United States
- Prior art keywords
- light
- sealing
- silicone resin
- fluorescent material
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A light-emitting device production method includes a positioning step of positioning, in a light-emitting element, a sealing member at least containing a silicone resin semi-cured at a room temperature (T0) by primary cross-linking and a fluorescent material, the silicone resin decreasing in viscosity reversibly in a temperature region between the room temperature (T0) and a temperature lower than a secondary cross-linking temperature (T1), and being totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature (T1).
Description
- This application is a continuation of U.S. application Ser. No. 14/348,742, filed Mar. 31, 2014, which is a national stage application under 35 USC 371 of International Application No. PCT/JP2012/066174, filed Jun. 25, 2012, which claims the priority of Japanese Applications No. 2011-2609369, filed Nov. 29, 2011, and 2012-019150, filed Jan. 31, 2012, the contents of which prior applications are incorporated herein by reference.
- The present invention relates to a method for producing a light-emitting device in which a fluorescent material is used.
- A light-emitting device in which an LED chip and a fluorescent material are used, the fluorescent material emitting fluorescence by being excited by light emission by the LED chip, is classified into the following known types according to how to provide the fluorescent material in a vicinity of the LED chip.
- The known types include a two-stage sealing type (Patent Literature 1) in which an
LED chip 151 is sealed by carrying out compression molding with respect to a sealingresin 153 containing afluorescent material 152, and the sealingresin 153 is sealed by further carrying out compression molding with respect to a sealingresin 154 that is transparent (see (a) of FIG. 33). - A light-emitting device of this type deteriorates in productivity since compression molding needs to be carried out two times. Further, compression molding carried out two times requires two molds, and respective shapes of the sealing
resin 153 containing thefluorescent material 152 and the sealingresin 154 are determined while thesealing resins LED chip 151 changes an amount of the sealingresin 153 containing the fluorescent material 152 (a relative thickness of the sealing resin 153) (see (b) of FIG. 33). This may cause a change in color of emitted light. Therefore, in order to obtain an unchanged color of the emitted light, it is necessary to adjust a concentration (contained amount) of thefluorescent material 152 or to change the shape of the sealingresin 153 by replacing the mold with another mold. - The known types also include a precipitation type (Patent Literature 2) in which an LED chip is sealed by carrying out compression molding with respect to a sealing resin containing a fluorescent material, and precipitating the fluorescent material contained in the sealing resin so as to spread the fluorescent material in a vicinity of the LED chip.
- This type makes it difficult to cause the fluorescent material to be precipitated and spread in a stable amount. This is (i) because it is difficult for resins for compression molding (most of which contain silicone), which are higher in viscosity than resins for transfer potting, to precipitate the fluorescent material and (ii) because a resin is cured in a short time during compression molding, so that the resin is cured before the fluorescent material is precipitated.
- The known types also include a sheet covering type in which an
LED chip 161 is sealed by carrying out compression molding with respect to atransparent sealing resin 162 and covering a vicinity of thetransparent sealing resin 162 with aresin sheet 164 containing a fluorescent material 163 (see (c) of FIG. 33). - According to this type, light emitted by the
LED chip 161 is partially reflected in an inner surface of theresin sheet 64 containing thefluorescent material 163 and returns inward, so that a loss occurs in the light. This reduces a light extraction efficiency. -
Patent Literature 3 proposes a technique, which is irrelevant to a fluorescent material, for covering an LED chip connected to a substrate with a heat-curable film (an epoxy resin composition), and sealing the LED chip by heat-curing the heat-curable film. Patent Literature 4 proposes a technique in which a sealing sheet having (i) an outermost resin layer (e.g., a polycarbodiimide layer), (ii) an optical diffusion layer containing light diffusion particles (e.g., a polycarbodiimide layer), and (iii) a resin layer having a low refractive index (e.g., an epoxy resin layer) is stacked by use of a vacuum laminator on a wiring circuit board mounted with an optical semiconductor element, so as to be pressure-molded by use of a stamper. - Note here that in order to seal an LED chip by use of silicone containing a fluorescent material, normally, a
substrate 172 is filled withsilicone 171 that is in a liquid state and contains a fluorescent material (see (a) of FIG. 34) and then anLED chip 173 is sealed by heating thesilicone 171 by use of an oven or the like (see (b) of FIG. 34). This causes a problem (i) such that a concentration of the fluorescent material contained in thesilicone 171 sensitively changes in accordance with an environment in which each process is carried out and (ii) such that a viscosity of thesilicone 171 changes in accordance with an ambient environment. - In order to solve this problem, Patent Literature 5, for example discloses a technique for molding, into sheet semi-cured silicone, liquid silicone in which a fluorescent material is mixed. According to the technique disclosed in Patent Literature 5, molding, into sheet semi-cured silicone, of liquid silicone in which a fluorescent material is mixed allows an improvement in treatment of silicone, and prevents a change in viscosity in accordance with an ambient environment.
-
Patent Literature 1 - Japanese Patent Application Publication, Tokukai, No. 2008-211205 A (Publication Date: Sep. 11, 2008)
- Patent Literature 2
- Japanese Patent Application Publication, Tokukai, No. 2006-229054 A (Publication Date: Aug. 31, 2006)
-
Patent Literature 3 - Japanese Patent Application Publication, Tokukai, No. 2009-010109 A (Publication Date: Jan. 15, 2009)
- Patent Literature 4
- Japanese Patent Application Publication, Tokukai, No. 2006-140362 A (Publication Date: Jun. 1, 2006)
- Patent Literature 5
- Japanese Patent Application Publication, Tokukai, No. 2010-159411 A (Publication Date: Jul. 22, 2010)
- However, according to the technique disclosed in Patent Literature 5, liquid silicone in which a fluorescent material is mixed is molded into sheet semi-cured silicone. Therefore, the fluorescent material, which is larger in specific gravity than silicone, flows and is precipitated in the liquid silicone, so that the fluorescent material is unevenly dispersed in a sheet obtained by the molding. Accordingly, in a case where a plurality of light-emitting devices are produced by use of this sheet, the plurality of light-emitting devices contain the fluorescent material in different amounts. This causes a blur in color of emitted light and/or a variation in characteristic among the plurality of light-emitting devices. Therefore, a conventional method has a problem such that many light-emitting devices outside a target chromaticity range are produced, so that a yield rate for products is reduced.
- The present invention has been made in view of the problem, and an object of the present invention is to provide a light-emitting device production method that allows (i) equalization of a concentration of a fluorescent material among light-emitting devices and (ii) a smaller variation in chromaticity value which variation is caused by a fluorescent material concentration and a fluorescent material contained amount.
- In order to attain the object of the present invention, a light-emitting device production method in accordance with the present invention includes: a mounting step of mounting at least one light-emitting element on a substrate; a positioning step of positioning a sealing member so that the sealing member faces an upper surface of the at least one light-emitting element mounted in the mounting step, the sealing member at least containing a silicone resin semi-cured by primary cross-linking and a fluorescent material; a melting step of melting, by heating at a temperature lower than a secondary cross-linking temperature at which the silicone resin subjected to primary cross-linking is totally cured by secondary cross-linking, the sealing member positioned in the positioning step; and a curing step of, while the sealing member melted in the melting step is in close contact with at least the upper surface of the at least one light-emitting element, heating the sealing member at a temperature equal to or higher than the secondary cross-linking temperature, the silicone resin decreasing in viscosity reversibly in a temperature region between a room temperature and the temperature lower than the secondary cross-linking temperature, and being totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature.
- According to the light-emitting device production method, a sealing member is positioned so that the sealing member faces an upper surface of the at least one light-emitting element mounted on the substrate, the sealing member at least containing a silicone resin semi-cured by primary cross-linking and a fluorescent material.
- Note here that the silicone resin decreases in viscosity reversibly in a temperature region between a room temperature and the temperature lower than the secondary cross-linking temperature, and is totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature. Therefore, a viscosity of the silicone resin can be repeatedly controlled by changing a temperature in the temperature region between the room temperature and the temperature lower than the secondary cross-linking temperature.
- Accordingly, for example, in a case where the viscosity of the silicone resin is controlled (reduced), during kneading of the fluorescent material with the silicone resin, to an extent that the kneaded fluorescent material is not precipitated, the fluorescent material can be evenly dispersed in the silicone resin.
- Hence, according to the light-emitting device production method, it is possible to obtain a sealing member in which the fluorescent material is evenly dispersed in the silicone resin. Therefore, in a case where a light-emitting element is sealed with the sealing member, it is possible to attain a light-emitting device production method that allows (i) equalization of a concentration of a fluorescent material among light-emitting devices and (ii) a smaller variation in chromaticity value which variation is caused by a fluorescent material concentration and a fluorescent material contained amount.
- As described earlier, a light-emitting device production method in accordance with the present invention includes: a mounting step of mounting at least one light-emitting element on a substrate; a positioning step of positioning a sealing member so that the sealing member faces an upper surface of the at least one light-emitting element mounted in the mounting step, the sealing member at least containing a silicone resin semi-cured by primary cross-linking and a fluorescent material; a melting step of melting, by heating at a temperature lower than a secondary cross-linking temperature at which the silicone resin subjected to primary cross-linking is totally cured by secondary cross-linking, the sealing member positioned in the positioning step; and a curing step of, while the sealing member melted in the melting step is in close contact with at least the upper surface of the at least one light-emitting element, heating the sealing member at a temperature equal to or higher than the secondary cross-linking temperature, the silicone resin decreasing in viscosity reversibly in a temperature region between a room temperature and the temperature lower than the secondary cross-linking temperature, and being totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature.
- Therefore, the present invention yields an effect of providing a light-emitting device production method that allows (i) equalization of a concentration of a fluorescent material among light-emitting devices and (ii) a smaller variation in chromaticity value which variation is caused by a fluorescent material concentration and a fluorescent material contained amount.
-
FIG. 1 is a perspective view illustrating a configuration of an appearance of a light-emitting device produced by a light-emitting device production method in accordance withEmbodiment 1. -
FIGS. 2( a) through 2(d) schematically illustrate a process in which light-emitting elements are mounted in respective cavities and which is included in a process for producing the light-emitting device illustrated inFIG. 1 . -
FIGS. 3( a) through 3(c) schematically illustrate a process in which the cavity is sealed with a sealing resin and which is included in the process for producing the light-emitting device illustrated inFIG. 1 . -
FIG. 4 is a graph showing a viscosity characteristic of a silicone resin of which a sealing resin sheet illustrated in FIG. 3(a) is made. -
FIGS. 5( a) through 5(d) are graphs each showing a viscosity state of the silicone resin in the process illustrated inFIG. 3( b). -
FIGS. 6( a) through 6(c) each schematically illustrate a state of the sealing resin sheet in a vacuum heating furnace illustrated inFIG. 3( b). -
FIG. 7 schematically illustrates a process in which a multiple cavity circuit board illustrated inFIG. 3( c) is divided and which is included in the process for producing the light-emitting device illustrated inFIG. 1 . -
FIG. 8 is a chart showing data on the light-emitting device production method in accordance withEmbodiment 1. -
FIGS. 9( a) through 9(e) schematically illustrate a method for producing the sealing resin sheet illustrated inFIG. 3( a). -
FIGS. 10( a) and 10(b) are graphs each showing a viscosity state of a silicone resin in a process illustrated inFIG. 9( a) throughFIG. 9( e). -
FIG. 11 is a cross-sectional view illustrating another method for forming, into a sheet, a kneaded resin illustrated inFIG. 9( c). -
FIG. 12 is a cross-sectional view illustrating an inner structure of a vacuum heating apparatus which is usable for production of the light-emitting device illustrated inFIG. 1 . -
FIGS. 13( a) through 13(c) schematically illustrate a process of a vacuum heating method which is applicable to the light-emitting device production method. -
FIGS. 14( a) through 14(c) schematically illustrate a cavity whose bottom is provided with a pair of through holes.FIG. 14( a) is a vertical cross-sectional view of the cavity,FIG. 14( b) is a plan view of the cavity illustrated inFIG. 14( a), andFIG. 14( c) is a transverse cross-sectional view of the cavity illustrated inFIG. 14( a). -
FIG. 15( a) is a cross-sectional view illustrating a cavity whose bottom is provided with a through hole, andFIG. 15( b) is a cross-sectional view illustrating a sealing resin sheet provided with a through hole. -
FIGS. 16( a) through 16(c) schematically illustrate a light-emitting device production method for sealing light-emitting elements by stacking two sealing resin sheets which contain a fluorescent material in different amounts. -
FIGS. 17( a) through 17(c) schematically illustrate a method for producing a light-emitting device having a rod lens. -
FIG. 18 is a cross-sectional view illustrating a press state in a vacuum heat pressing apparatus illustrated inFIG. 17( c). -
FIG. 19( a) is a perspective view illustrating a multiple cavity circuit board provided with rod lenses, andFIG. 19( b) is a perspective view illustrating a light-emitting device obtained by dividing the multiple cavity circuit board illustrated inFIG. 19( a). -
FIG. 20( a) is a perspective view illustrating a multiple cavity circuit board provided with a convex lens, andFIG. 20( b) is a perspective view illustrating a light-emitting device obtained by dividing the multiple cavity circuit board illustrated inFIG. 20( a). -
FIGS. 21( a) through 21(e) schematically illustrate a process in which a light-emitting element is mounted on a plane circuit board and which is included in a light-emitting device production process in accordance with Embodiment 2. -
FIG. 22 is a cross-sectional view illustrating a state of pressurized pressing in a vacuum heat pressing apparatus. -
FIG. 23( a) is a perspective view of the plane circuit board subjected to the pressurized pressing illustrated inFIG. 22 .FIG. 23( b) is a perspective view illustrating a light-emitting device obtained by dividing the plane circuit board illustrated inFIG. 23( a). -
FIG. 24( a) is a plan view showing an example of a light-emitting display device of a dot matrix type, andFIG. 24( b) is a cross-sectional view of the light-emitting display device illustrated inFIG. 24( a). -
FIG. 25 schematically shows an example of a method for producing the light-emitting display device illustrated in each ofFIG. 24( a) andFIG. 24( b). -
FIG. 26 is a cross-sectional view illustrating a state of pressurized pressing in a vacuum heat pressing apparatus. -
FIGS. 27( a) through 27(c) schematically illustrate a method for producing a single optical device. -
FIGS. 28( a) through 28(d) schematically illustrate a light-emitting device production method in accordance withEmbodiment 3. -
FIG. 29 is a chart showing data on the light-emitting device production method in accordance withEmbodiment 3. -
FIG. 30 schematically illustrates a process for producing sealing resin powder which is powder of a silicone resin containing a fluorescent material. -
FIGS. 31( a) through 31(c) schematically illustrate a method for producing a light-emitting device in which a sealing resin tablet is used. -
FIGS. 32( a) through 32(e) schematically illustrate a method for producing a sealing mixed powder sheet obtained by forming, into a sheet, sealing mixed powder illustrated inFIG. 28( a). -
FIG. 33 is a cross-sectional view illustrating a configuration of a conventional light-emitting device. -
FIG. 34 is a cross-sectional view illustrating a flow of a conventional light-emitting device production method. - The following description discusses, with reference to
FIGS. 1 through 20 , an embodiment related to a light-emitting device production method in accordance with the present invention. - First, the following description discusses, with reference to
FIG. 1 , a configuration of a light-emittingdevice 1 a in accordance with the present embodiment. -
FIG. 1 is a perspective view illustrating a configuration of an appearance of the light-emittingdevice 1 a produced by the light-emitting device production method in accordance with the present embodiment. According to the light-emittingdevice 1 a, acavity 12 which has a shape of a rectangular parallelepiped and opens upward is provided in a circuit board (substrate) 11 which is an MID (Molded Interconnection Device, three-dimensional injection-molded circuit board) which has a shape of a rectangular parallelepiped having a base approximately 1 mm×1 mm, and a light-emittingelement 13 such as an LED is mounted in the cavity 12 (seeFIG. 1 ). - The light-emitting
element 13 has a lower surface that is connected (die-bonded), by anelectroconductive adhesive 15, to a mountingwiring pattern 14 provided at a bottom of thecavity 12. Furthermore, the light-emittingelement 13 has an upper surface that is connected (wire-bonded), via anelectroconductive wire 17 made of, for example, a gold wire, to aconnection wiring pattern 16 provided at the bottom of thecavity 12. - The
cavity 12 of thecircuit board 11 is sealed by a sealingresin 21 made of a light-transmissive silicone resin. - Note that how to mount the light-emitting
element 13 on thecircuit board 11 is not particularly limited. The light-emittingelement 13 can be mounted on thecircuit board 11 by, for example, a flip chip method instead of a wire bonding method. - Next, the following description discusses, with reference to
FIGS. 2 through 8 , a method for producing the light-emittingdevice 1 a illustrated inFIG. 1 . -
FIGS. 2( a) through 2(d) schematically illustrate a process in which light-emittingelements 13 are mounted inrespective cavities 12 and which is included in a process for producing the light-emittingdevice 1 a illustrated inFIG. 1 . The light-emittingdevice 1 a is produced by use of a multiplecavity circuit board 10 in which thecavities 12 are provided in large numbers vertically and horizontally in a matrix pattern. Use of the multiplecavity circuit board 10 makes it is possible to simultaneously produce light-emittingdevices 1 a in large numbers. For example, the multiplecavity circuit board 10 has a thickness of 1.0 mm, and thecavities 12 have a depth of 0.6 mm. - First, according to the light-emitting device production method in accordance with the present embodiment, the mounting
wiring pattern 14 and theconnection wiring pattern 16 are provided at the bottom of each of the cavities 12 (seeFIG. 2( a)). - Next, the
electroconductive adhesive 15 is applied to the mountingwiring pattern 14 provided at the bottom of each of thecavities 12 of the multiple cavity circuit board 10 (seeFIG. 2( b)). - Subsequently, the light-emitting
element 13 is die-bonded to theelectroconductive adhesive 15 applied to the mounting wiring pattern 14 (seeFIG. 2( c)). The upper surface of the light-emittingelement 13 and theconnection wiring pattern 16 provided at the bottom of each of thecavities 12 are wire-bonded via theelectroconductive wire 17 made of, for example, a gold wire (seeFIG. 2( d)). - After the light-emitting
element 13 is thus mounted in each of thecavities 12 of the multiplecavity circuit board 10 by die bonding and wire bonding (a mounting step), thecavities 12 are sealed with a silicone resin containing a fluorescent material. -
FIGS. 3( a) through 3(c) schematically illustrate a process in which thecavities 12 are sealed with the sealingresin 21 and which is included in the process for producing the light-emittingdevice 1 a illustrated inFIG. 1 .FIG. 4 is a graph showing a viscosity characteristic of the silicone resin of which a sealing resin sheet (sealing member) 20 illustrated inFIG. 3( a) is made.FIGS. 5( a) through 5(d) are graphs each showing a viscosity state of the silicone resin in the process illustrated inFIG. 3( b). - Note that for convenience, the graphs of
FIG. 4 , andFIG. 5( a) throughFIG. 5( d) each show that the viscosity characteristic of the silicone resin changes linearly. However, a silicone resin is not necessarily limited to the silicone resin whose viscosity characteristic changes linearly. - The sealing
resin sheet 20, a surface molding release sheet (film) 31, and aweight plate 32 are stacked in this order on the multiplecavity circuit board 10 provided with thecavities 12 in each of which the light-emittingelement 13 is mounted (seeFIG. 3( a)). - Note here that the present embodiment uses the sealing
resin sheet 20 to simultaneously seal thecavities 12 with the sealingresin 21 containing a fluorescent material. The sealingresin sheet 20 is obtained by dispersing the fluorescent material in a silicone resin that is thermoplastic. The silicone resin is in a semi-cured state by being subjected to primary cross-linking, and has a predetermined viscosity. Note that the semi-cured state (B-STAGE) herein refers to a state which lies between a non-cured state (A-STAGE) and a totally-cured state (C-STAGE) and in which the silicone resin has a higher viscosity than in the non-cured state by being subjected to the primary cross-linking. - As shown in
FIG. 4 , the silicone resin has a viscosity of V0 at a room temperature T0 (see P0 inFIG. 4 ). The viscosity V0 refers to, for example, a viscosity which allows the silicone resin to maintain a sheet shape so that the sealingresin sheet 20 is easily treated at the room temperature T0. - In a case where the silicone resin is heated from the room temperature T0 to a temperature in a vicinity of a secondary cross-linking temperature T1, the viscosity of the silicone resin gradually decreases, so that the silicone resin has a viscosity of V1 immediately before a temperature of the silicone resin reaches a secondary cross-linking temperature T1 (see P1 of
FIG. 4 ). The viscosity V1 refers to a viscosity at which the silicone resin is melted to be flowable. - The change in viscosity of the silicone resin in a temperature region between the room temperature T0 and a temperature lower than the secondary cross-linking temperature T1 occurs because polymer chains in the silicone resin get entangled with or untied from each other by the Brownian motion, and the change is a heat-reversible change. Accordingly, in a case where the temperature of the silicone resin is decreased from the temperature in the vicinity of the secondary cross-linking temperature T1 to the room temperature T0, the viscosity of the silicone resin increases, and returns to the original viscosity V0 at the room temperature T0. Therefore, it is possible to repeatedly control the viscosity of the silicone resin between the viscosity V0 and the viscosity V1 by changing the temperature of the silicone resin in the temperature region between the room temperature T0 and the temperature lower than the secondary cross-linking temperature T1.
- Meanwhile, in a case where the silicone resin is heated at a temperature equal to or higher than the secondary cross-linking temperature T1, the silicone resin is subjected to secondary cross-linking, so that the viscosity of the silicone resin increases from the viscosity V1 to a viscosity V2 (see P2 in
FIG. 4 ). The viscosity V2 refers to a viscosity at which the silicone resin is totally cured. - The change in viscosity of the silicone resin at the secondary cross-linking temperature T1 is a heat-non-reversible change. Therefore, also in a case where the temperature of the silicone resin is decreased from the secondary cross-linking temperature T1 to the room temperature T0, the silicone resin does not change in viscosity, but maintains the totally-cured state (see P3 in
FIG. 4 ). - Various kinds of the fluorescent material are kneaded with the sealing
resin sheet 20 in accordance with a required optical characteristic, so that a concentration (contained amount) of the fluorescent material is controlled. In a case where the silicone resin is used, its viscosity can be controlled, provided that the silicone resin is in a state prior to the totally-cured state in which the silicone resin is totally cured by being subjected to secondary cross-linking. This makes it possible to form the sealingresin sheet 20 in which the fluorescent material is evenly dispersed (described later). - In order to cover all the
cavities 12 provided in the multiplecavity circuit board 10, the sealingresin sheet 20 is formed to be substantially identical in size to the multiplecavity circuit board 10. Furthermore, it is preferable that the sealingresin sheet 20 be formed to have a thickness of approximately 0.2 to 0.4 mm, which is smaller than a depth (0.6 mm) of thecavities 12. - In order that the sealing
resin 21 has a pearskin-finished surface, the surfacemolding release sheet 31 stacked on the sealingresin sheet 20 is configured to have a pearskin-finished surface with which the sealingresin sheet 20 is in contact. In a case where the surfacemolding release sheet 31 is used, the light-emittingdevice 1 a can have a higher light extraction efficiency. Furthermore, in a case where a shape of a surface of the surfacemolding release sheet 31 is changed, a surface of the sealingresin 21 can be processed to be various in design. Note that, in a case where no surfacemolding release sheet 31 is used, a shape of a surface of the weight plate (mold) 32 may be changed. - Next, as illustrated in
FIG. 3( b), the multiplecavity circuit board 10, the sealingresin sheet 20, the surfacemolding release sheet 31, and theweight plate 32, which are stacked, are set in avacuum heating furnace 33, and then heated and melted (a melting step). - In the melting step, as shown in
FIG. 5( a), the sealingresin sheet 20 is heated from the room temperature T0 to a temperature T4 (e.g., not lower than 80° C. and lower than 120° C.) which is in a vicinity of the secondary cross-linking temperature T1, so that the viscosity of the silicone resin is decreased to a viscosity V4 at which the silicone resin is flowable (see P4 inFIG. 5) . - The
vacuum heating furnace 33 is configured to carry out heating while causing an inner part thereof to be in a vacuum state. The sealingresin sheet 20 and the surfacemolding release sheet 31 which are provided on the multiplecavity circuit board 10 and are in the vacuum state are heated in close contact with each other while being pressed by theweight plate 32. This causes a melted silicone resin to flow into thecavities 12, which can be filled with the melted silicone resin. In this case, a melted silicone resin remaining on a surface, between therespective cavities 12, of the multiplecavity circuit board 10 also flows into thecavities 12. Accordingly, also in a case where the sealingresin sheet 20 is set to have a thickness smaller than the depth of the cavities 12 (approximately ⅗ of the depth of the cavities 12) as described earlier, thecavities 12 are almost full of the melted silicone resin. As a matter of course, the sealingresin sheet 20 may have a larger thickness. However, this case produces, in large amounts, the silicone resin and the fluorescent material which overflow from a rim of theweight plate 32 and are not used to seal thecavities 12. The silicone resin and the fluorescent material which overflow from the rim of theweight plate 32 cannot be reused, and thus need to be disposed of. Accordingly, in view of material costs of the silicone resin and the fluorescent material, it is preferable that the sealingresin sheet 20 be set to have a thickness smaller than the depth of thecavities 12 as described earlier. - The melted silicone resin, which has been filled in the
cavities 12, is totally cured by being further heated to a higher temperature (a curing step). - In this curing step, as shown in
FIG. 5( b), the sealingresin sheet 20 is heated at a temperature between the temperature T4 and the secondary cross-linking temperature T1 (e.g., not lower than 120° C. and not higher than 170° C.) (see P1 inFIG. 5( b)). According to this, as shown inFIG. 5( c), the silicone resin is subjected to secondary cross-linking, and the silicone resin is totally cured (see P2 inFIG. 5( c)). - Next, as shown in
FIG. 3( c), after the silicone resin is totally cured, the multiplecavity circuit board 10 on which the sealingresin sheet 20, the surfacemolding release sheet 31, and theweight plate 32 are stacked is taken out from thevacuum heating furnace 33, and a temperature of the silicone resin is decreased to the room temperature T0. In this case, as shown inFIG. 5( d), also in a case where the temperature decreases to the room temperature T0, the silicone resin which has been subjected to secondary cross-linking maintains the totally-cured state (see P3 inFIG. 5( d)). - Then, the
weight plate 32 and the surfacemolding release sheet 31 are removed from the multiplecavity circuit board 10 in order. This causes the light-emittingelement 13 in each of thecavities 12 to be sealed with the sealingresin 21 having the pearskin-finished surface. -
FIGS. 6( a) through 6(c) each schematically illustrate a state of the sealingresin sheet 20 in thevacuum heating furnace 33 illustrated inFIG. 3( b). The sealingresin sheet 20 maintains a sheet shape at the room temperature T0 when being set in the vacuum heating furnace 33 (seeFIG. 6( a)). - However, the heating started by the
vacuum heating furnace 33 causes the sealingresin sheet 20 to decrease in viscosity, so that the sealingresin sheet 20 is in a curved state (see FIG. 6(b)). Then, in a case where the heating is continued until the sealingresin sheet 20 has a temperature of approximately 100° C., the silicone resin melts, and flows into the cavities 12 (seeFIG. 6( c)). - In this case, since the sealing
resin sheet 20 is pressed by theweight plate 32, the melted silicone resin is evenly filled in thecavities 12 by a tension caused by the silicone resin having flowed into thecavities 12. According to the present embodiment, a heating time of approximately 30 minutes is necessary for the melted silicone resin to be filled in thecavities 12. - After the sealing
resin sheet 20 is melted and the melted silicone resin is filled in thecavities 12, the multiplecavity circuit board 10 is heated to a temperature of approximately 150° C. while being contained in the vacuumheat pressing apparatus 33. - In this case, during such a heating process, the melted silicone resin further decreases in viscosity before its temperature reaches the secondary cross-linking temperature T1. Therefore, the melted silicone resin remaining on the surface, between the
respective cavities 12, of the multiplecavity circuit board 10 flows into adjacent ones of thecavities 12. This prevents the melted silicone resin from remaining on the surface of the multiplecavity circuit board 10. Therefore, also in a case where the sealingresin sheet 20 is formed to have a thickness smaller than the depth of thecavities 12, thecavities 12 are almost full of the melted silicone resin. - The silicone resin filled in the
cavities 12 is totally cured by secondary cross-linking by being heated to a high temperature of 150° C. by thevacuum heating furnace 33. According to the present embodiment, a heating time of 30 minutes is necessary for the melted silicone resin in thecavities 12 to be subjected to secondary cross-linking and then totally cured. - As described above, the melted silicone resin can be filled in the
cavities 12 by melting the sealingresin sheet 20 in a state in which the sealingresin sheet 20 is in close contact with the surface of the surfacemolding release sheet 31. Thereafter, it is possible to form the sealingresin 21 by further heating the melted silicone resin to the secondary cross-linking temperature. -
FIG. 7 schematically illustrates a process in which the multiplecavity circuit board 10 illustrated inFIG. 3( c) is divided and which is included in the process for producing the light-emittingdevice 1 a illustrated inFIG. 1 . As illustrated inFIG. 7 , after the light-emittingelements 13 in therespective cavities 12 are sealed with the sealingresin 21, the multiplecavity circuit board 10 is divided into the cavities 12 (a dividing step). This makes it possible to obtain, in large numbers, the light-emittingdevices 1 a, in each of which the sealingresin 21 has the pearskin-finished surface. - Note that in order to produce the light-emitting
devices 1 a by use of the multiplecavity circuit board 10, the multiplecavity circuit board 10 is divided so as to have a circuit configuration in which the multiplecavity circuit board 10 has a plurality ofcavities 12 in which the light-emittingelements 13 in therespective cavities 12 are electrically connected to each other. This makes it possible to obtain a dot-matrix light-emitting device in which a large number of light-emittingelements 13 are provided in a matrix pattern. - As described earlier, the sealing
resin sheet 20 stacked on the multiplecavity circuit board 10 is formed to have a thickness of approximately 0.2 to 0.4 mm, whereas thecavities 12 have a depth of 0.6 mm. In a case where the sealingresin sheet 20 has a too large thickness, the melted silicone resin remains on the surface, between therespective cavities 12, of the multiplecavity circuit board 10 after the curing step is ended. If such a silicone resin remaining on the surface of the multiplecavity circuit board 10 is cured, light emitted by the light-emittingelement 13 may be scattered by the remaining silicone resin. Therefore, it is preferable that the sealingresin sheet 20 be configured to have a thickness smaller than the depth of thecavities 12. -
FIG. 8 is a chart showing data on the light-emitting device production method in accordance with the present embodiment.FIG. 8 also shows, as a comparative example, data obtained by a conventional casting sealing method. Note that the casting sealing method shown inFIG. 8 uses a general silicone resin whose initial state is a liquid state and which is conventionally used as described in the above Technical Problem (seeFIG. 34 ), and the casting sealing method does not use the silicone resin in accordance with the present invention which silicone resin has a viscosity characteristic shown inFIG. 4 . - The light-emitting
devices 1 a produced by a sheet resin method of the present embodiment each have a chromaticity distribution width of 3 ranks (seeFIG. 8 ). As compared with light-emitting devices (each having a chromaticity distribution width of 15 ranks) produced by the conventional casting sealing method, the light-emittingdevices 1 a produced by the sheet resin method of the present embodiment can less vary in chromaticity value (can be narrower in chromaticity distribution range). - Note here that values of “X” and “Y” shown in each of the sections of chromaticity distribution width in
FIG. 8 indicate respective X and Y chromaticity widths within a scope which specifies a given chromaticity range, the X and Y chromaticity widths being obtained when chromaticity values of the light-emitting devices mass-produced by each of the sheet resin method of the present embodiment and the conventional casting sealing method are plotted on a CIE1931 chromaticity diagram. Note also that a value of the rank (division), which value indicates the number of ranks (divisions) over which chromaticity distributions of the mass-produced light-emitting devices extend, shows that variations in chromaticity value are distributed while extending over a plurality of levels (chromaticity ranks) that are adjacent to each other in the scope. - According to the sheet resin method of the present embodiment, it is possible to reduce a range in which the light-emitting
devices 1 a vary in chromaticity value. This is because, as described earlier, it is possible to equalize fluorescent material contained amounts among the light-emittingdevices 1 a to a substantially equal amount. - The above description thus shows that, as compared with the light-emitting devices produced by the conventional casting sealing method, a light-emitting
device 1 a produced by the sheet resin method of the present embodiment has smaller values of X and Y, and a smaller value of the rank (division), so that mass-produced light-emittingdevices 1 a much less vary in chromaticity value. - Heads of the conventional casting resin method in the section of production efficiency/molding time in
FIG. 8 each indicate the number of heads of a dispenser of a fluorescent material application apparatus for use in casting, and show that the plurality ofcavities 12 can be simultaneously applied with the fluorescent material (subjected to casting sealing). Furthermore, times in that section each indicate a time required for the application of the fluorescent material layer (casting sealing) (that is, corresponding to a molding time). The time which is converted into a time per cavity 12 (light-emittingdevice 1 a) is 0.17 second/pcts in the case of 6 heads. - Meanwhile, a tact of the sheet resin method of the present embodiment indicates a time for a vacuum heat pressing process to be carried out with respect to a sheet resin (that is, corresponding to the molding time). In a case where three multiple
cavity circuit boards 10 are simultaneously subjected to vacuum heat pressing, the tact which is converted into a time per cavity 12 (light-emittingdevice 1 a) is 0.049 second/pcts. - As described above, the sheet resin method of the present embodiment makes the molding time shorter as compared with the conventional casting sealing method. This shows that the sheet resin method of the present embodiment allows an increase in production efficiency.
- The number of parts in each of the sections of amount of waste resin and fluorescent material in
FIG. 8 quantitatively indicate an amount of a waste resin and a waste fluorescent material in a case where 100 light-emitting devices are produced (that is, 100 parts of the sealingresin 21 are formed) assuming that an amount of the silicone resin and the fluorescent material each contained in the sealingresin 21 of one light-emitting device is one part, the waste resin and the waste fluorescent material each produced during a production process and then disposed of. According to the sheet resin method of the present embodiment, only an amount of the silicone resin and the fluorescent material which overflow from the rim of theweight plate 32 during the vacuum heat pressing process serves as an amount of a waste resin and a waste fluorescent material. In contrast, according to the conventional casting sealing method, precipitation of the fluorescent material in a casting machine (dispenser) causes a change over time in concentration of the fluorescent material for each casting process. Therefore, it is impossible to use all the resin containing the fluorescent material in the casting machine (normally, approximately half of the resin containing the fluorescent material is disposed of). This increases an amount of a waste resin and a waste fluorescent material. - As described above, the sheet resin method of the present embodiment further reduces the amount of the waste resin and the waste fluorescent material as compared with the conventional casting sealing method. This shows that the sheet resin method of the present embodiment is extremely economical.
- Furthermore, according to the sheet resin method of the present embodiment, the cavities are simultaneously filled with the silicone resin. This allows an increase in production efficiency and a reduction in amount of the resin and the fluorescent material which are to be disposed of in the production process.
- Next, the following description discusses, with reference to
FIGS. 9 through 11 , a method for producing the sealingresin sheet 20 which is used in the light-emitting device production method in accordance with the present embodiment. -
FIGS. 9( a) through 9(c) schematically illustrate the method for producing the sealingresin sheet 20 illustrated inFIG. 3( a).FIG. 10( a) andFIG. 10( b) are graphs each showing a viscosity state of a silicone resin in a process illustrated inFIGS. 9( a) through 9(e). - Note that for convenience, the graphs of
FIG. 10( a) andFIG. 10( b) each show that a viscosity characteristic of the silicone resin changes linearly. However, a silicone resin is not necessarily limited to the silicone resin whose viscosity characteristic changes linearly. - First, a
silicone resin 22 illustrated inFIG. 9( a) is subjected to primary cross-linking, and thesilicone resin 22 is obtained by removing, by appropriate decompression, the solvent content of a semi-cured material diluted with a solvent such as BTX (benzene, toluene or xylene). - As illustrated in
FIG. 10( a), thesilicone resin 22 is heated from the room temperature T0 to a temperature T5 (e.g., not lower than 40° C. and lower than 60° C.), so that a viscosity of thesilicone resin 22 is decreased to a viscosity V5 at which a fluorescent material can be kneaded with thesilicone resin 22 and the fluorescent material thus kneaded is not precipitated (see P5 inFIG. 10( a)). - Next, the fluorescent material and the
silicone resin 22 each measured in a predetermined amount are contained in a container, and kneaded by, for example, stirring until the fluorescent material is evenly dispersed in the silicone resin 22 (seeFIG. 9( b)). This makes it possible to obtain a kneadedresin 24, which is thesilicone resin 22 in which the fluorescent material is evenly dispersed (seeFIG. 9( c)). - Note that it is possible to use, as another method for kneading the fluorescent material and the
silicone resin 22, a widely used kneading apparatus such as a ball mill using a high-hardness material or a (vacuum heat) kneader. Such a kneading apparatus preferably includes a heating mechanism (temperature regulating mechanism) so that the fluorescent material and thesilicone resin 22 subjected to primary cross-linking can be further kneaded (the ball mill or the kneader needs to be decompressed by a vacuum apparatus). In a case where a temperature during the kneading (a temperature range lower than a secondary cross-linking temperature of the silicone resin 22) is regulated, it is possible to appropriately adjust the viscosity of the primarycross-linked silicone resin 22 to an extent that the fluorescent material is not precipitated. This makes it possible to adjust a state in which the fluorescent material is dispersed in thesilicone resin 22. - Such a kneading apparatus, which is suitable for kneading a high-viscosity resin material, can knead the fluorescent material and the
silicone resin 22 while less reducing the viscosity of thesilicone resin 22. Accordingly, it is possible to prevent the fluorescent material from being unevenly dispersed in thesilicone resin 22, so that the fluorescent material can be more evenly dispersed in thesilicone resin 22. Note that, in a case where such a kneading apparatus is used, thesilicone resin 22 with which the fluorescent material is kneaded does not necessarily have a sheet shape. However, it is only necessary that thesilicone resin 22 be appropriately processed again from an obtained shape to have a desired shape of a sealing (starting) material for sealing an LED package. - According to the another method for kneading the fluorescent material and the
silicone resin 22, thesilicone resin 22 which has been subjected to primary cross-linking and is to be introduced into the kneading apparatus may be not only in a resin state in which its viscosity is reduced but also in a powdered state. That is, a sample to be used (primary processed product) for obtaining a sealing resin form (secondary processed product) optimum for a sealing process may be produced by use of the kneading apparatus after dry-blending the fluorescent material and powder of the silicone resin 22 (the primary processed product may be obtained from a dry-blended product). Even in a case where thesilicone resin 22 is in the powdered state, the kneading apparatus includes the heating mechanism. Therefore, particles of thesilicone resin 22 which has been melted by heat are bonded, and the particles are kneaded while the fluorescent material is being mixed therewith. Note that a method for producing the light-emitting device using thesilicone resin 22 in the powdered state will be described later. - Next, as illustrated in
FIG. 9( d), the kneadedresin 24 is formed into a sheet by being pressurized by a pressurizingplate 30. Then, as shown inFIG. 10( b), a temperature of the kneadedresin 24 formed into a sheet is reduced from the temperature T5 to the room temperature T0. This makes it possible to produce the sealingresin sheet 20 in which the fluorescent material is evenly dispersed (seeFIG. 9( e)). - Note that a solvent remaining in the
silicone resin 22 is removed by decompression while the fluorescent material is being kneaded with thesilicone resin 22, or removed by drying when the kneadedresin 24 is being formed into a sheet. - Note that the kneaded
resin 24 can be formed into a sheet not only by such a press method as described above but also by various melting methods such as a T-die method, a calendar roll method, and a doctor blade method. -
FIG. 11 is a cross-sectional view illustrating another method for forming, into a sheet, the kneadedresin 24 illustrated inFIG. 9( c).FIG. 11 illustrates a process for forming the kneadedresin 24 into a sheet by the T-die method. - In a case where the kneaded
resin 24 is formed into a sheet by the T-die method, the kneadedresin 24 which is roughly ground to have a predetermined size is positioned on amold 131 provided with anozzle 132 having an opening 132 a which opens in a certain width (seeFIG. 11 ). The kneadedresin 24, which is pressurized by apressure member 139, can be formed into a sheet having a width of the opening 132 a. - Note that the width of the opening 132 a is appropriately changed in accordance with a required thickness of the sealing
resin sheet 20. - As described earlier, the light-emitting device production method in accordance with the present embodiment includes: a mounting step of mounting the light-emitting elements 13 in the respective cavities 12 provided in the multiple cavity circuit board 10; a positioning step of stacking the sealing resin sheet 20 on the multiple cavity circuit board 10 so that the sealing resin sheet 20 covers all the cavities 12 in which the respective light-emitting elements 13 are mounted, the sealing resin sheet 20 containing the silicone resin semi-cured by primary cross-linking and the fluorescent material; a melting step of, while heating the sealing resin sheet 20 at the temperature lower than the secondary cross-linking temperature T1 at which the silicone resin is totally cured by secondary cross-linking, pressurizing the sealing resin sheet 20 so that the silicone resin melted is filled in the cavities 12; and a curing step of, while the silicone resin 22 that has been melted and filled in the cavities 12 is in close contact with at least respective upper surfaces of the light-emitting elements 13, heating the sealing resin sheet 20 at a temperature equal to or higher than the secondary cross-linking temperature T1, the silicone resin decreasing in viscosity reversibly in a temperature region between the room temperature T0 and the temperature lower than the secondary cross-linking temperature T1, and being totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature T1.
- The light-emitting device production method in accordance with the present embodiment uses the silicone resin having the viscosity characteristic described earlier. This makes it possible to repeatedly control the viscosity of the silicone resin by changing the temperature of the silicone resin in the temperature region between the room temperature T0 and the temperature lower than the secondary cross-linking temperature T1.
- Accordingly, for example, in a case where the viscosity of the silicone resin is controlled (reduced), during kneading of the fluorescent material with the silicone resin, to an extent that the kneaded fluorescent material is not precipitated, the fluorescent material can be evenly dispersed in the silicone resin. Therefore, it is possible to obtain the sealing
resin sheet 20 in which the fluorescent material is evenly dispersed in the silicone resin. - Accordingly, in a case where, in order that the melted silicone resin is totally cured by secondary cross-linking while being in close contact with respective upper surfaces and side surfaces of the light-emitting
elements 13, the sealingresin sheet 20 is heated while being positioned so as to face the respective upper surfaces of the light-emittingelements 13 mounted on the multiplecavity circuit board 10, the light-emittingelements 13 can be sealed in a state in which a fluorescent material concentration (fluorescent material contained amount) is substantially equalized among thecavities 12. - Furthermore, according to the light-emitting device production method in accordance with the present embodiment, as compared with the conventional casting sealing method described earlier (a method for separately filling the
cavities 12 with a silicone resin that is in a liquid state and contains a fluorescent material), the light-emitting device production method allows the fluorescent material contained in the silicone resin, with which thecavities 12 are filled, to less vary in concentration and contained amount for each of thecavities 12. This can prevent a variation in chromaticity value among the light-emittingdevices 1 a. - Further, the light-emitting device production method in accordance with the present embodiment allows the melted silicone resin to be simultaneously filled in the
cavities 12 without using a special dispenser, a molding machine, or the like for causing the melted silicone resin to be filled in thecavities 12. This allows a remarkable increase in production efficiency of the light-emitting devices. - Therefore, according to the present embodiment, it is possible to attain a light-emitting device production method that allows (i) equalization of a concentration of a fluorescent material among light-emitting
devices 1 a and (ii) a smaller variation in chromaticity value which variation is caused by a fluorescent material concentration and a fluorescent material contained amount. - Next, the following description discusses, with reference to
FIGS. 12 through 20 , modifications of the light-emitting device production method in accordance with the present embodiment. - The present embodiment discusses a method in which the multiple
cavity circuit board 10 on which the light-emittingelements 13 are mounted, the sealingresin sheet 20, the surfacemolding release sheet 31, and theweight plate 32 are stacked and heated in a vacuum state by thevacuum heating furnace 33. Alternatively, the method may be replaced with a method that uses noweight plate 32. -
FIG. 12 is a cross-sectional view illustrating an inner structure of a vacuum heating apparatus 40 which is usable for production of the light-emittingdevice 1 a illustrated inFIG. 1 . Without using theweight plate 32, it is possible to stack and heat the multiplecavity circuit board 10, the sealingresin sheet 20, and the surfacemolding release sheet 31 by the vacuum heating apparatus (“Vacuum Laminator” manufactured by NPC Incorporated) 40 capable of simultaneously carrying out pressurization and heating in a vacuum state (seeFIG. 12 ). - According to the vacuum heating apparatus 40, an
upper chamber 41 and alower chamber 42 are separated from each other by adiaphragm rubber 43. Respective inner parts of theupper chamber 41 and thelower chamber 42 are configured to be in a vacuum state. - A
heating plate 44 is provided in thelower chamber 42. The multiplecavity circuit board 10 on which the sealingresin sheet 20 and the surfacemolding release sheet 31 are stacked is placed on theheating plate 44. - When the multiple
cavity circuit board 10 on which the sealingresin sheet 20 and the surfacemolding release sheet 31 are stacked is placed on theheating plate 44, the respective inner parts of theupper chamber 41 and thelower chamber 42 are made vacuous, and theheating plate 44 is heated, so that the sealingresin sheet 20 is melted. - Then, in a case where only the inner part of the
upper chamber 41 is exposed to air while the vacuum state of the inner part of thelower chamber 42 is maintained, the surfacemolding release sheet 31 is pressure-welded to the multiplecavity circuit board 10 by thediaphragm rubber 43. - According to this, the surface
molding release sheet 31 is pressure-welded, by thediaphragm rubber 43 and a vacuum function, to a surface of the silicone resin which is in a melted state and is filled in thecavities 12 of the multiplecavity circuit board 10. Therefore, the silicone resin totally cured can be molded to have a pearskin-finished surface while no air bubble enters the silicone resin in the melted state. Also in this case, regulation of a temperature of theheating plate 44 allows the vacuum heating apparatus 40 to carry out an operation in which the silicone resin is melted so as to be filled in thecavities 12 and then the silicone resin is totally cured by secondary cross-linking. -
FIGS. 13( a) through 13(c) schematically illustrate a process of a vacuum heating method which is applicable to the light-emitting device production method. As illustrated inFIG. 13( a) throughFIG. 13( c), a vacuumingbag 38 a connected to avacuum pump 38 d is also usable for producing the light-emittingdevice 1 a. - Specifically, first, the multiple
cavity circuit board 10 on which the sealingresin sheet 20 and the surfacemolding release sheet 31 are stacked is contained in the vacuumingbag 38 a, that is heat-resistant (seeFIG. 13( a)). - Next, after one end of a
tube 38 b is airtightly connected to an opening of the vacuumingbag 38 a (seeFIG. 13( b)), the vacuumingbag 38 a may be contained in aheating furnace 38 c to be heated while an inner part of the vacuumingbag 38 a is made vacuous by thevacuum pump 38 d (seeFIG. 13( c)). - The present embodiment discusses a method in which the sealing
resin sheet 20 is stacked on the multiplecavity circuit board 10 and heated. In this case, a pair of throughholes 12 a may be provided at the bottom of each of thecavities 12. -
FIGS. 14( a) through 14(c) each schematically illustrate acavity 12 whose bottom is provided with the pair of throughholes 12 a.FIG. 14( a) is a vertical cross-sectional view of thecavity 12,FIG. 14( b) is a transverse cross-sectional view of thecavity 12 illustrated inFIG. 14( a), andFIG. 14( c) is a plan view of thecavity 12 illustrated inFIG. 14( a). - In a case where the pair of through
holes 12 a is provided at the bottom of each of thecavities 12, air can be exhausted from thecavities 12 when an area around the multiplecavity circuit board 10 is in a vacuum state and the silicone resin of the sealingresin sheet 20 is in a melted state (seeFIG. 14( a) throughFIG. 14( c)). Therefore, it is possible to prevent an air bubble from entering the melted silicone resin which is filled in thecavities 12. Furthermore, inner surfaces of each of thecavities 12 and the sealingresin 21 can be in closer in contact with each other. - For example, in a case where the
cavities 12 each have (i) an opening having a rectangular shape of 3.0 mm×1.8 mm and (ii) a bottom having a rectangular shape of 2.2 mm×0.6 mm, thecavities 12 have a depth of 0.7 mm, and the bottom protrudes downward by 0.4 mm so as to correspond to a length of the throughholes 12 a, the pair of throughholes 12 a having a rectangular shape of 0.4 mm×0.6 mm is provided at either end in a longer-side direction of the bottom of each of thecavities 12 so as to be spaced from each other at intervals of 1.4 mm (seeFIG. 14( a) throughFIG. 14( c)). - Note that in a case where the melted silicone resin may flow from the through
holes 12 a, it is only necessary that a highly releasable sheet or plate, for example be provided below the multiplecavity circuit board 10. According to this, even if the melted silicone resin flows from the throughholes 12 a, it is possible to easily take out the multiplecavity circuit board 10 from, for example, the heating furnace while preventing the multiplecavity circuit board 10 from being in close contact with, for example, the heating plate. -
FIG. 15( a) is a cross-sectional view illustrating thecavity 12 whose bottom is provided with one throughhole 12 a, andFIG. 15( b) is a cross-sectional view illustrating the sealingresin sheet 20 provided with a throughhole 20 a. The bottom of each of thecavities 12 does not need to be provided with the pair of throughholes 12 a, but the bottom of each of thecavities 12 may be provided with the one throughhole 12 a (seeFIG. 15( a)). - Note that the through
hole 12 a may be provided not only at the bottom but also on a side surface of each of thecavities 12. Furthermore, the throughhole 12 a may have a cross-section having not only a rectangular shape but also a circular shape a triangular shape, or the like. - Further, instead of a configuration in which the bottom of each of the
cavities 12 is provided with the throughhole 12 a, the present embodiment may have a configuration in which a part of the sealingresin sheet 20 which part faces each of thecavities 12 is provided with a throughhole 20 a (seeFIG. 15( b)). Also in this case, air can be exhausted from thecavities 12 via respective throughholes 20 a provided in the sealingresin sheet 20 when an area around the multiplecavity circuit board 10 is in a vacuum state and the silicone resin of the sealingresin sheet 20 is melted. Therefore, it is possible to prevent an air bubble from entering the melted silicone resin which is filled in thecavities 12. Furthermore, inner surfaces of each of thecavities 12 and the sealingresin 21 can be in closer in contact with each other. - The present embodiment discusses a method in which the light-emitting
elements 13 are sealed with one sealingresin sheet 20. Alternatively, the light-emittingelements 13 may be sealed with a plurality of sealing resin sheets which are stacked and contain a fluorescent material in different amounts. -
FIGS. 16( a) through 16(c) schematically illustrate a light-emitting device production method for sealing the light-emittingelements 13 by using two sealingresin sheets sealing resin sheet 20A and the secondsealing resin sheet 20B which contain the fluorescent material in different amounts may be stacked, as the sealingresin sheet 20, on the multiple cavity circuit board 10 (seeFIG. 16( a)). - The first
sealing resin sheet 20A and the secondsealing resin sheet 20B are each identical in size to the multiplecavity circuit board 10 so as to cover all thecavities 12. The firstsealing resin sheet 20A, which is fitted to the multiplecavity circuit board 10, is stacked on the multiplecavity circuit board 10. - After the second
sealing resin sheet 20B is stacked on the firstsealing resin sheet 20A, the surfacemolding release sheet 31 having a pearskin-finished surface is further stacked on the secondsealing resin sheet 20B. - Next, the multiple
cavity circuit board 10 on which the firstsealing resin sheet 20A, the secondsealing resin sheet 20B, and the surfacemolding release sheet 31 are stacked is set in the vacuum heat pressing apparatus 35 (seeFIG. 16( b)). For example, a “vacuum laminate press” (trade name, manufactured by KITAGAWA SEIKI CO., LTD) is used as the vacuumheat pressing apparatus 35. - The vacuum
heat pressing apparatus 35 includes (i) aheater stand 35 a which is capable of carrying out heating and is positioned in avacuum chamber 35 c, and (ii) apress heater 35 b which is capable of carrying out heating and can be brought into contact with and separated from the heater stand 35 a. The multiplecavity circuit board 10 on which the firstsealing resin sheet 20A, the secondsealing resin sheet 20B, and the surfacemolding release sheet 31 are stacked is set on the heater stand 35 a. While the multiplecavity circuit board 10 is set on the heater stand 35 a, thevacuum chamber 35 c is decompressed to be at a pressure of 10 torr. - Next, the
press heater 35 b heated is lowered, and the multiplecavity circuit board 10 set on the heater stand 35 a, on which the firstsealing resin sheet 20A, the secondsealing resin sheet 20B, and the surfacemolding release sheet 31 are stacked, is heated by thepress heater 35 b at a temperature of approximately 100° C. while being pressurized at a pressure of 20 kg/cm2 (seeFIG. 16( c)). In this case, the heater stand 35 a located on the underside of the multiplecavity circuit board 10 is not heated. After thepress heater 35 b carries out heat pressing, thepress heater 35 b is further heated to a temperature of approximately 150° C. - Then, a pressure in the
vacuum chamber 35 c is returned to a normal pressure by releasing a decompression state in thevacuum chamber 35 c. Thereafter, the heat pressing by thepress heater 35 b is released, so that a vacuum heat pressing process carried out by the vacuumheat pressing apparatus 35 is ended. - During the vacuum heat pressing process carried out by the vacuum
heat pressing apparatus 35, the firstsealing resin sheet 20A and the secondsealing resin sheet 20B are melted, and the melted silicone resin is filled in thecavities 12, so that the melted silicone resin is totally cured by the secondary cross-linking. - Thereafter, the light-emitting devices are obtained by dividing the multiple
cavity circuit board 10 for each of thecavities 12 or every predetermined number of thecavities 12. - As described earlier, in a case where the first
sealing resin sheet 20A and the secondsealing resin sheet 20B which contain the fluorescent material in different amounts are stacked, it is possible to easily control a concentration at which the fluorescent material is dispersed in each of thecavities 12. - Note that a surface of the sealing
resin 21 may have an uneven surface by directly spraying a releasing agent to a surface of thepress heater 35 b without using the surfacemolding release sheet 31. - Further, the vacuum
heat pressing apparatus 35 may be replaced with a vacuum impregnating apparatus. In order to fill thecavities 12 with the melted silicone resin, the vacuum impregnating apparatus carries out pressurization by increasing a pressure in a chamber from a normal pressure. According to the vacuum impregnating apparatus, it is possible to easily carry out, in the impregnating apparatus, a process in which the melted silicone resin is filled in thecavities 12 by being heated under a high pressure. This allows an increase in operation efficiency. - The present embodiment discusses a method in which the surface
molding release sheet 31 is positioned on the sealingresin sheet 20. Alternatively, the surfacemolding release sheet 31 may be replaced with a lensmolding resin sheet 25. -
FIGS. 17( a) through 17(c) schematically illustrate a method for producing a light-emitting device having a rod lens.FIG. 18 is a cross sectional view illustrating a press state in the vacuumheat pressing apparatus 35 illustrated inFIG. 17( c). - The multiple
cavity circuit board 10 on which the sealingresin sheet 20 and the lensmolding resin sheet 25 are stacked (seeFIG. 17( a)) is set in the vacuum heat pressing apparatus 35 (seeFIG. 17( b)). The lensmolding resin sheet 25 is made of, for example, a high-molecular weight unsaturated polyester resin. - Note that, according to the present modification, the
cavities 12 provided in the multiplecavity circuit board 10 has a depth of 0.6 mm, the sealingresin sheet 20 has a thickness of 0.5 mm, and the lensmolding resin sheet 25 has a thickness of 1.0 mm. - The vacuum
heat pressing apparatus 35 includes alens molding mold 35 d provided on an undersurface of thepress heater 35 b. For example, thelens molding mold 35 d is configured such that a plurality of lens molding grooves (molding recesses: seeFIG. 18 ) 35 e having a semi-cylindrical shape and a radius of 0.9 mm are provided in parallel with each other so as to correspond to respective columns of thecavities 12 of the multiplecavity circuit board 10. While the multiplecavity circuit board 10 is set on the heater stand 35 a of the vacuumheat pressing apparatus 35, thevacuum chamber 35 c is decompressed to be be at a pressure of 10 torr. - Next, the
press heater 35 b heated is lowered, and the sealingresin sheet 20 and the lensmolding resin sheet 25 that are stacked on the multiplecavity circuit board 10 are heated by thepress heater 35 b at a temperature of approximately 100° C. while being pressurized at a pressure of 20 kg/cm2 (seeFIG. 17( c)). This causes the sealingresin sheet 20 and the lensmolding resin sheet 25 to be in a melted state, so that the melted silicone resin of the sealingresin sheet 20 is filled in thecavities 12, and a melted lens molding resin of the lensmolding resin sheet 25 is filled in thelens molding grooves 35 e. - After carrying out the heat pressing as described above, the
press heater 35 b further heats the sealingresin sheet 20 and the lensmolding resin sheet 25 to a temperature of 150° C. - Then, a pressure in the
vacuum chamber 35 c is returned to a normal pressure by releasing a decompression state in thevacuum chamber 35 c. Thereafter, the heat pressing by thepress heater 35 b is released, so that a vacuum heat pressing process carried out by the vacuumheat pressing apparatus 35 is ended. - According to the press process, the silicone resin filled in the
cavities 12 and the lens molding resin filled in thelens molding grooves 35 e are each cross-linked to be cured. -
FIG. 19( a) is a perspective view illustrating the multiplecavity circuit board 10 provided with rod lenses, andFIG. 19( b) is a perspective view illustrating a light-emittingdevice 1 b obtained by dividing the multiplecavity circuit board 10 illustrated inFIG. 19( a). - In a case where the silicone resin filled in the
cavities 12 and the lens molding resin filled in thelens molding grooves 35 e are cured, a plurality ofrod lenses 25 a having a semi-cylindrical shape can be provided on the multiple cavity circuit board 10 (seeFIG. 19( a)). - In a case where the multiple
cavity circuit board 10 is divided for each of thecavities 12, it is possible to obtain the light-emittingdevice 1 b in which the light-emittingelement 13 mounted in thecavity 12 of thecircuit board 11 is sealed with the sealingresin 21, on which arod lens 25 a having a semi-cylindrical shape is provided (seeFIG. 19( b)). - Note that according to the present modification, in order to prevent an air bubble from entering the melted lens molding resin during formation of the
rod lens 25 a by melting the lensmolding resin sheet 25 by use of thelens molding mold 35 d, the lensmolding resin sheet 25 preferably has a thickness larger than a radius of therod lens 25 a. Further, thelens molding mold 35 d, which does not need to be provided to thepress heater 35 b, may be used while being placed on the lensmolding resin sheet 25. - Note also that not only the
rod lens 25 a having a semi-cylindrical shape but also aconvex lens 25 b having a hemispherical shape can be formed on the sealingresin 21. -
FIG. 20( a) is a perspective view illustrating the multiplecavity circuit board 10 provided with a convex lens, andFIG. 20( b) is a perspective view illustrating a light-emittingdevice 1 c obtained by dividing the multiplecavity circuit board 10 illustrated inFIG. 20( a). - As illustrated in
FIG. 20( a),convex lenses 25 b having a hemispherical shape can be provided on therespective cavities 12 provided in the multiplecavity circuit board 10. In this case, theconvex lenses 25 b having a hemispherical shape can be formed by use of thelens molding mold 35 d provided with, for example, a plurality of lens molding recesses 35 f (seeFIG. 22) having a hemispherical shape and a radius of 0.9 mm, instead of thelens molding grooves 35 e having a semi-cylindrical shape. - According to this, in a case where the multiple
cavity circuit board 10 is divided for each of thecavities 12, it is possible to obtain the light-emittingdevice 1 c in which the light-emittingelement 13 mounted in thecavity 12 of thecircuit board 11 is sealed with the sealingresin 21, on which aconvex lens 25 b having a hemispherical shape is provided (seeFIG. 20( b)). - The following description discusses, with reference to
FIGS. 21 through 27 , a second embodiment of a light-emitting device production method in accordance with the present invention. Note that for convenience, members having functions identical to those of the respective members illustrated in the first embodiment are given respective identical reference numerals, and a description of those members is omitted here. - The light-emitting device production method in accordance with the present embodiment differs from the light-emitting device production method in accordance with
Embodiment 1 mainly in that themultiple circuit board 10 is replaced with aplane circuit board 60 having a plane surface. - First, the following description discusses, with reference to
FIGS. 21 through 23 , the light-emitting device production method in accordance with the present embodiment. -
FIGS. 21( a) through 21(e) schematically illustrate a process in which a light-emitting element is mounted on theplane circuit board 60 and which is included in the light-emitting device production process in accordance with the present embodiment. First, pairs of mountingwiring patterns 64 andconnection wiring patterns 66 are provided vertically and horizontally in a matrix pattern on theplane circuit board 60 having a plane surface (seeFIG. 21( a)). - Next, an
electroconductive adhesive 65 is applied to the mountingwiring patterns 64 provided on the plane circuit board 60 (seeFIG. 21( b)). - Subsequently, a light-emitting
element 63 is die-bonded to the electroconductive adhesive 65 (seeFIG. 21( c)). (i) An upper surface of the light-emittingelement 63 and (ii) aconnection wiring pattern 66 which is paired with a mountingwiring pattern 64 on which the light-emittingelement 63 is mounted are wire-bonded via anelectroconductive wire 67 made of, for example, a gold wire (seeFIG. 21( d)). - After the light-emitting
element 13 is thus mounted on theplane circuit board 60 by die bonding and wire bonding (a mounting step), a sealing resin sheet 26 is stacked and positioned on theplane circuit board 60 as illustrated inFIG. 21( e) (a positioning step), the sealing resin sheet 26 being provided withrecesses 26 a which are formed by embossing and in which the respective light-emittingelements 63 each connected with a corresponding mountingwiring pattern 64 and a correspondingconnection wiring pattern 66 can be contained. - The sealing resin sheet 26 is positioned on the
plane circuit board 60 so that the sealing resin sheet 26 is not in contact with the light-emittingelement 63 and theelectroconductive wire 67 and so that the pairs of the mountingwiring patterns 64 and theconnection wiring patterns 66 each provided on theplane circuit board 60 are contained in therespective recesses 26 a (seeFIG. 22 ). Further, an upper surface of the sealing resin sheet 26 is provided with protrusions that correspond to therespective recesses 26 a. This allows the sealing resin sheet 26 to have a substantially constant thickness. - The sealing resin sheet 26 is made of a silicone resin having the viscosity characteristic shown in
FIG. 4 , and is obtained by kneading a fluorescent material with a semi-cured silicone resin obtained by primary cross-linking. - After the sealing resin sheet 26 is thus positioned on the
plane circuit board 60, theplane circuit board 60 is set in a vacuum heat pressing apparatus 35 (seeFIG. 16( b)). -
FIG. 22 is a cross-sectional view illustrating a state of pressurization in the vacuumheat pressing apparatus 35. According to the present embodiment, alens molding mold 35 d provided with a plurality of lens molding recesses 35 f having a hemispherical shape is provided on an undersurface of apress heater 35 b (seeFIG. 22 ). - While the
plane circuit board 60 is set on aheater stand 35 a of the vacuumheat pressing apparatus 35, a vacuum chamber is decompressed to be at a pressure of 10 torr. In such a state, theheated press heater 35 b is lowered, and theplane circuit board 60, on which the sealing resin sheet 26 is stacked is heated by theheated press heater 35 b at a temperature of approximately 100° C. while being pressurized at a pressure of 20 kg/cm2. According to this, the silicone resin of the sealing resin sheet 26 is melted, so that the lens molding recesses 35 f of thelens molding mold 35 d can be filled with the silicone resin. Further, in a case where theplane circuit board 60 is further heated to a temperature of approximately 150° C., the silicone resin filled in the lens molding recesses 35 f can be totally cured by secondary cross-linking. - After heat pressing is carried out by the vacuum
heat pressing apparatus 35, a pressure in avacuum chamber 35 c is returned to a normal pressure by releasing a decompression state in thevacuum chamber 35 c. Thereafter, thepress heater 35 b is raised, so that a vacuum heat pressing process carried out by the vacuumheat pressing apparatus 35 is ended. -
FIG. 23( a) is a perspective view of theplane circuit board 60 subjected to the pressurized pressing illustrated inFIG. 22 .FIG. 23( b) is a perspective view illustrating a light-emitting device 1 d obtained by dividing theplane circuit board 60 illustrated inFIG. 23( a). On theplane circuit board 60 subjected to the vacuum heat pressing process, thelight emitting elements 63 are sealed with respective sealing resins 21 having a hemispherical shape (seeFIG. 23( a)). - In a case where the
plane circuit board 60 is divided for each of thelight emitting elements 63, it is possible to obtain a light-emitting device 1 d in which a light-emittingelement 63 mounted on a circuit board 61 is sealed with a sealingresin 21 of a convex lens type (seeFIG. 23( b)). - As described earlier, a light-emitting device production method in accordance with the present embodiment includes: a mounting step of mounting a plurality of light-emitting
devices 13 on theplane circuit board 60 having a plane surface; a positioning step of, in order that the light-emittingdevices 63 are contained in a respective plurality ofrecesses 26 a which are provided in the sealing resin sheet 26 and in which the respective light-emittingdevices 63 can be contained, positioning the sealing resin sheet 26 on theplane circuit board 60; a heating step of heating the positioned sealing resin sheet 26 while pressurizing the sealing resin sheet 26 via thelens molding mold 35 d provided with the lens molding recesses 35 f which face the respective light-emittingelements 63 mounted on theplane circuit board 60; and a curing step of totally curing a melted silicone resin by secondary cross-linking in the lens molding recesses 35 f. - The sealing resin sheet 26 used for the light-emitting device production method in accordance with the present embodiment is made of a silicone resin having the viscosity characteristic shown in
FIG. 4 , and is obtained by evenly dispersing the fluorescent material in the semi-cured silicone resin subjected to primary cross-linking. - Therefore, according to the present embodiment, it is possible to attain a light-emitting device production method that allows equalization, among light-emitting devices 1 d, of a concentration of the fluorescent material contained in the sealing
resin 21 of a convex lens type. - Next, the following description discusses, with reference to
FIGS. 24 through 27 , modifications of the light-emitting device production method in accordance with the present embodiment. - The present embodiment discusses a method in which the light-emitting device 1 d sealed with the sealing
resin 21 of a convex lens type is produced. However, a light-emittingdisplay device 50 of a dot matrix type can be produced by use of the light-emitting device production method in accordance with the present invention. -
FIG. 24( a) is a plan view showing an example of the light-emittingdisplay device 50 of a dot matrix type, andFIG. 24( b) is a cross-sectional view of the light-emittingdisplay device 50 illustrated inFIG. 24( a). As shown inFIG. 24( a) andFIG. 24( b), pairs of mountingwiring patterns 54 andconnection wiring patterns 56 are provided vertically and horizontally in a matrix pattern on aplane circuit board 51. - A light-emitting
element 53 is die-bonded to a mountingwiring pattern 54 via an electroconductive adhesive (not illustrated), and the light-emittingelement 53 and aconnection wiring pattern 56 are wire-bonded via anelectroconductive wire 57 made of, for example, a gold wire. Further, a plurality of lead pins 51 a are provided on a back surface of theplane circuit board 51. - Further, the
plane circuit board 51 is provided with a reflectingplate 58 provided withopenings 58 a having a circular cross section that surrounds (i) the mountingwiring pattern 54 on which the light-emittingelement 53 is mounted and (ii) theconnection wiring pattern 56 which is wire-bonded to the light-emittingelement 53 via theelectroconductive wire 57. - According to the reflecting
plate 58, theopenings 58 a each have at least an inner surface which has a reflecting function. In each of theopenings 58 a of the reflectingplate 58, the light-emittingelement 53, the mountingwiring pattern 54, and theconnection wiring pattern 56 are contained. Theopenings 58 a are sealed with the sealingresin 21 containing the fluorescent material. - Such a light-emitting
display device 50 of a dot matrix type can be produced by the following method. -
FIG. 25 schematically shows an example of a method for producing the light-emittingdisplay device 50 illustrated in each ofFIG. 24( a) andFIG. 24( b). First, as shown inFIG. 25 , the mountingwiring patterns 54 and theconnection wiring patterns 56 are provided on theplane circuit board 51. Then, the light-emittingelements 53 are die-bonded to the respective mountingwiring patterns 54 via the electroconductive adhesive (not illustrated). Further, the light-emittingelements 53 are wire-bonded to the respectiveconnection wiring patterns 56 via theelectroconductive wire 57 made of, for example, a gold wire (the mounting step). - Next, the reflecting
plate 58 is placed on theplane circuit board 51 so that the mountingwiring patterns 54 on which the respective light-emittingelement 53 are mounted and theconnection wiring patterns 56 are contained in therespective openings 58 a (a placing step). The reflectingplate 58 is made of, for example, a resin molded article having a reflecting function. - Next, a sealing
resin sheet 20 is positioned on the reflectingplate 58 so as to close all theopenings 58 a (the positioning step). The reflectingplate 58 and the sealingresin sheet 20 which are stacked on theplane circuit board 51 in this order are set in a vacuum heat pressing apparatus 35 (seeFIG. 16( b)). -
FIG. 26 is a cross-sectional view illustrating a state of pressurized pressing in the vacuumheat pressing apparatus 35. According to the vacuumheat pressing apparatus 35, afixture 35 g is placed on aheater stand 35 a that is provided in avacuum chamber 35 c, and a pressingmember 35 k is provided to a lower surface of apress heater 35 b located in an upper part of the vacuum heat pressing apparatus 35 (seeFIG. 26 ). Thefixture 35 g has afixture recess 35 h provided in a central part thereof so as to fit therein theplane circuit board 51, on which the reflectingplate 58 and the sealingresin sheet 20 are stacked. - A
bottom surface 35 n of thefixture recess 35 h is covered with release paper 35 m in advance. Theplane circuit board 51 is positioned in thefixture recess 35 h in a state in which theplane circuit board 51 is upside down, that is, the sealingresin sheet 20 is located lower than theplane circuit board 51 so as to be closer to thebottom surface 35 n. This causes the sealingresin sheet 20 to be in contact with the release paper 35 m, so that the sealingresin sheet 20, the reflectingplate 58, and theplane circuit board 51 are stacked in thefixture recess 35 h in this order from a lower part of thefixture recess 35 h. - After the
plane circuit board 51 has been positioned in thefixture recess 35 h, thevacuum chamber 35 c is decompressed to be at a pressure of 10 torr, and the heater stand 35 a is heated to a temperature of approximately 100° C. Then, thepress heater 35 b is lowered, and theplane circuit board 51 positioned in thefixture recess 35 h is pressurized in a state in which the pressingmember 35 k provided to the lower surface of thepress heater 35 b is provided between lead pins 59 provided on a back surface of the plane circuit board 51 (a melting step). In this case, the pressingmember 35 k carries out heat pressing with respect to the sealingresin sheet 20 while pressing theplane circuit board 51 at a pressure of 20 kg/cm2. Note that the heater stand 35 a is not heated in this case. - According to this, after the sealing
resin sheet 20 is heated and the melted silicone resin is filled in all theopenings 58 a of the reflectingplate 58, the heater stand 35 a is heated to a temperature of 150° C. (a curing step). - After the heat pressing is carried out, a pressure in the
vacuum chamber 35 c is returned to a normal pressure by releasing a decompression state in thevacuum chamber 35 c. Thereafter, the heat pressing carried out by the pressingmember 35 k is released, so that the vacuum heat pressing process carried out by the vacuumheat pressing apparatus 35 is ended. - After such vacuum heat pressing is ended, the silicone resin covering the
openings 58 a is totally cured. This makes it possible to produce the light-emittingdisplay device 50 which is of a dot matrix type and is illustrated in each ofFIG. 24( a) andFIG. 24( b). - According to the method for producing a light-emitting display device of a dot matrix type, it is only necessary to stack the sealing
resin sheet 20 on the reflectingplate 58 a, and it is unnecessary to carry out a special operation for fixing the reflectingplate 58. - The present embodiment discusses a method for producing a plurality of light-emitting devices 1 d by mounting a plurality of light-emitting
elements 63 on theplane circuit board 60 and simultaneously sealing the plurality of light-emittingelements 63. Alternatively, a single light-emittingdevice 1 e may be produced by use of the light-emitting device production method in accordance with the present invention. -
FIGS. 27( a) through 27(c) schematically illustrate a method for producing the single light-emittingdevice 1 e. First, a pair of a mountingwiring pattern 74 and aconnection wiring pattern 76 is provided on acircuit board 71 having a plane surface, and a light-emittingelement 73 is bonded to the mounting wiring pattern 74 (seeFIG. 27( a)). Then, the light-emittingelement 73 and the mountingwiring pattern 74 are wire-bonded via anelectroconductive wire 77 b made of, for example, a gold wire, and the light-emittingelement 73 and theconnection wiring pattern 76 are wire-bonded via anelectroconductive wire 77 a made of, for example, a gold wire (the mounting step). Further, the mountingwiring pattern 74 and theconnection wiring pattern 76 are each provided with aresin dam mechanism 78 for the melted silicone resin to remain on an upper surface of thecircuit board 71. Then, thecircuit board 71 mounted with the light-emittingelement 73 is set on aheating plate 79. A piece of the sealingresin sheet 20 which piece is obtained by dividing the sealingresin sheet 20 is positioned so as to face the upper surface of the light-emitting element 73 (the positioning step). - Next, as illustrated in
FIG. 27( b), thecircuit board 71 is heated from below by the heating plate 79 (the melting step) so as to melt the sealingresin sheet 20. - Next, while being in close contact with the upper surface and side surfaces of the light-emitting
element 73, the melted silicone resin is further heated so as to be totally cured by secondary cross-linking, so that the sealingresin 21 is formed (the curing step) (seeFIG. 27( c)). - As described earlier, according to the present modification, without using a mechanism for pressurization, it is possible to produce the light-emitting
device 1 e in a case where the piece of the sealingresin sheet 20 which piece is obtained by dividing the sealingresin sheet 20 is positioned so as to face the upper surface of the light-emittingelement 73 with which thecircuit board 71 is mounted, and the piece is heated. - Note that, in order to adjust a light distribution characteristic of the light-emitting
device 1 e, it is possible to appropriately form, on the sealingresin 21, a transparent resin layer that is, for example, dome-shaped or lens-shaped and contains no fluorescent material (such a transparent resin layer may be made of (i) a single silicone resin of which the sealingresin sheet 20 is made or (ii) another resin material). - Note also that it is possible to seal, with the piece of the sealing
resin sheet 20 which piece is obtained by dividing the sealingresin sheet 20, the light-emittingelements 13 mounted in therespective cavities 12 provided in the multiplecavity circuit board 10 illustrated inFIG. 2( a). Also in this case, it is possible to equalize the concentration of the fluorescent material among light-emitting devices by use of the pieces of the sealingresin sheet 20 which pieces are obtained by dividing the sealingresin sheet 20 in which the fluorescent material is evenly dispersed, the pieces having an equal size. - The following description discusses, with reference to
FIGS. 28 through 31 , a third embodiment of a light-emitting device production method in accordance with the present invention. Note that for convenience, members having functions identical to those of the respective members illustrated in the first and second embodiments are given respective identical reference numerals, and a description of those members is omitted here. - The light-emitting device production method in accordance with the present embodiment differs from the light-emitting device production method in accordance with
Embodiment 1 mainly in that the sealingresin sheet 20 is replaced with sealing mixed powder (a sealing member) 120 in which (i) powder of a silicone resin used for the sealingresin sheet 20 and (ii) the fluorescent material are mixed. -
FIGS. 28( a) through 28(d) schematically illustrate a light-emitting device production method in accordance with the present embodiment. First, the sealingmixed powder 120 in which powder of the silicone resin and the fluorescent material are mixed is sprinkled over (or applied to) an entire surface of a multiplecavity circuit board 10 mounted with light-emitting elements 13 (seeFIG. 28( a)), so that the entire surface of the multiplecavity circuit board 10 is covered with the sealing mixed powder 120 (seeFIG. 28( b)) (a positioning step). - The sealing
mixed powder 120, which is made of the silicone resin having the viscosity characteristic shown inFIG. 4 , is obtained by sufficiently mixing (i) powder of the silicone resin which has been subjected to primary cross-linking and is in a semi-cured state and (ii) the fluorescent material until the fluorescent material is evenly dispersed. A method for pulverizing the silicone resin is not particularly limited, but can be exemplified by, for example, a method in which a jet mill having a cooling function is used at a low temperature to grind the silicone resin into pieces having a diameter of approximately 10 μm. - Further, during preparation of the sealing
mixed powder 120 by mixing (i) powder of the silicone resin subjected to a primary cross-linking reaction and (ii) the fluorescent material, powder of the silicone resin subjected to a secondary cross-linking reaction may further be mixed. The silicone resin subjected to the secondary cross-linking reaction maintains a totally cured state also during the heating in, for example, a curing step. Therefore, in a case where powder of the silicone resin subjected to the secondary cross-linking reaction is mixed in the sealingmixed powder 120, it is possible to prevent precipitation of the fluorescent material, which precipitation may occur when the sealingmixed powder 120 filled incavities 12 is heated, so that the silicone resin subjected to the primary cross-linking reaction is in a melted state. - Next, the sealing
mixed powder 120 attached to the surface of the multiplecavity circuit board 10 is removed by causing asqueegee 36 to move along the surface of the multiplecavity circuit board 10 while thesqueegee 36 is in contact with the multiple cavity circuit board 10 (seeFIG. 28( c)). This causes thecavities 12 provided in the multiplecavity circuit board 10 to be full of the sealingmixed powder 120. In this case, an amount of the fluorescent material contained in the sealingmixed powder 120 which is filled (positioned) in thecavities 12 is substantially equalized. Note that the sealingmixed powder 120 removed from the surface of themultiple cavity circuit 10 is a non-cured resin which has been subjected to the primary cross-linking reaction and has not been subjected to the secondary cross-linking reaction. Therefore, the sealingmixed powder 120 can be collected to be reused. - After the sealing
mixed powder 120 is filled in thecavities 12, the multiplecavity circuit board 10 is provided in avacuum heating furnace 33 to be heated (seeFIG. 28( d)). When the sealingmixed powder 120 is heated to a temperature of approximately 100° C. by thevacuum heating furnace 33, powder of the silicone resin in thecavities 12 is melted, and the silicone resin thus melted is deaerated in a case where an inner part of thevacuum heating furnace 33 is made vacuous (a melting step). Thereafter, when the silicone resin is further heated to a high temperature of approximately 150° C. by thevacuum heating furnace 33, the silicone resin is cured by secondary cross-linking (the curing step). - Thereafter, the multiple
cavity circuit board 10 is divided for each of thecavities 12, it is possible to obtain a light-emitting device in which a light-emittingelement 13 in acavity 12 is sealed with a sealingresin 21. - As compared with the method that uses the piece of the sealing
resin sheet 20 which piece is obtained by dividing the sealingresin sheet 20 and that is illustrated inFIGS. 27( a) through 27(c), the light-emitting device production method in accordance with the present embodiment more easily improves evenness with which the fluorescent material is dispersed in the sealingresin 21. - This is because of the following reason. According to the light-emitting device production method in accordance with the present embodiment, since the silicone resin in a powdered state and the florescent material are mixed, the fluorescent material can be sufficiently dispersed without being influenced by a viscosity of the silicone resin, so that the fluorescent material can be more evenly dispersed in the sealing
mixed powder 120. -
FIG. 29 is a chart showing data on the light-emitting device production method in accordance with the present embodiment.FIG. 29 also shows, as comparative examples, data shown inFIG. 8 and obtained by the conventional casting sealing method and by the sheet resin method ofEmbodiment 1. - As shown in
FIG. 29 , chromaticity distribution widths for the conventional casting sealing method and the sheet resin method ofEmbodiment 1 are 15 ranks and 3 ranks, respectively, whereas a chromaticity distribution width for a powder application method of the present embodiment is 1 rank, which shows a great improvement in variation in chromaticity value. This is because of the following reason. According to the powder application method of the present embodiment, in the step of filling the sealingmixed powder 120 in the cavities 12 (the positioning step), the sealingmixed powder 120 which is unnecessary and is attached to the surface, between therespective cavities 12, of the multiplecavity circuit board 10 can be removed without having much influence on a concentration and the amount of the fluorescent material contained in the sealingmixed powder 120 filled in thecavities 12. Therefore, as compared with the other methods, the powder application method of the present embodiment makes it possible to more securely control an amount of the sealingmixed powder 120 to be filled in thecavities 12. - Note that in order to allow a further improvement in chromaticity distribution width, it is preferable that a silicone resin powder particle and a fluorescent material particle differ in particle size. According to this, an air gap is less likely to be made between powder of the silicone resin and the fluorescent material while the sealing
mixed powder 120 is being filled in thecavities 12. This allows the silicone resin obtained after the heating to have a smaller degree of volume shrinkage. - The above description thus shows that, as compared with the light-emitting devices produced by the conventional casting sealing method and the sheet resin method of
Embodiment 1, a light-emitting device produced by the powder application method of the present embodiment has smaller X and Y values, and a smaller value of the rank (division), so that light-emitting devices mass-produced by the powder application method much less vary in chromaticity value. - Amounts of a waste resin and a waste fluorescent material for the conventional casting sealing method and the sheet resin method of
Embodiment 1 are 50 parts and 10 parts, respectively, whereas an amount of a waste resin and a waste fluorescent material for the powder application method of the present embodiment is zero in principle. This is because according to the powder application method of the present embodiment, a surplus of the sealingmixed powder 120 which surplus overflows from thecavities 12 in the step of filling the sealingmixed powder 120 in thecavities 12 can be collected and reused. - As described earlier, according to the powder application method of the present embodiment, the amount of the waste resin and the waste fluorescent material is zero in principle. This shows that the powder application method of the present embodiment is extremely economical.
- As described earlier, according to the light-emitting device production method in accordance with the present embodiment, the light-emitting
elements 13 in therespective cavities 12 are sealed in a case where the sealingmixed powder 120 in which powder of the silicone resin and the fluorescent material are mixed is heated in the positioning step in a state in which the sealingmixed powder 120 is filled in thecavities 12 in which the respective light-emittingelements 13 are mounted. - According to the light-emitting device production method in accordance with the present embodiment, in a case where powder of the silicone resin and the fluorescent material are sufficiently mixed until the fluorescent material is evenly dispersed, it is possible to substantially equalize the amount of fluorescent material contained in the sealing
mixed powder 120, which is positioned in thecavities 12 in the positioning step. - Therefore, according to the present embodiment, it is possible to attain a light-emitting device production method that allows equalization of a concentration of a fluorescent material among light-emitting devices.
- Next, the following description discusses, with reference to
FIGS. 30 and 31 , modifications of the light-emitting device production method in accordance with the present embodiment. - The present embodiment discusses a method that uses the sealing
mixed powder 120 in which powder of the silicone resin powder and the fluorescent material are mixed. Alternatively, the sealingmixed powder 120 may be replaced with sealing resin powder 121 (the sealing member) made of powder of the silicone resin containing the fluorescent material. -
FIG. 30 schematically illustrates a process for producing the sealingresin powder 121 which is powder of the silicone resin containing the fluorescent material. - The sealing
resin powder 121 is powder obtained by evenly dispersing the fluorescent material in the silicone resin having the viscosity characteristic shown inFIG. 4 . As illustrated inFIG. 30 , the sealingresin powder 121 is obtained in a case where a jet mill having a cooling function is used at a low temperature to grind, into pieces having a diameter of approximately 25 μm, a kneadedresin 24, which is asilicone resin 22 in which the fluorescent material is evenly dispersed (seeFIG. 9( c)). - Also in a case where the sealing
mixed powder 120 is replaced with the sealingresin powder 121, the amount of the fluorescent material contained in the sealingresin powder 121 which is filled incavities 12 is substantially equalized. Therefore, it is possible to attain a light-emitting device production method that allows equalization of a concentration of a fluorescent material among light-emitting devices. - A
cavity 12 may be sealed with a sealing resin tablet (the sealing member) 122 which is molded into a tablet by compressing the sealingmixed powder 120 or the sealingresin powder 121. -
FIGS. 31( a) through 31(c) schematically illustrate a method for producing a light-emitting device in which the sealingresin tablet 122 is used. In this case, as illustrated inFIG. 31( a), the sealingresin tablet 122 is positioned in thecavity 12 provided in a circuit board 11 (the positioning step). The sealingresin tablet 122 is molded into a tablet by compressing the sealingmixed powder 120 illustrated inFIG. 28( a) or the sealingresin powder 121 illustrated inFIG. 30 . - Note that heating may be carried out at a low temperature in a step of compressing the sealing
mixed powder 120 or the sealingresin powder 121 into a tablet. This allows a closer contact between powder of the silicone resin and the fluorescent material and among powder particles of the silicone resin containing the fluorescent material. Therefore, the sealingmixed powder 120 or the sealingresin powder 121 can be easily integrated (formed into a tablet). - Next, as illustrated in
FIG. 31( b), the sealingresin tablet 122 is melted in a case where thecircuit board 11 is heated from below by aheating plate 79 in a state in which the sealingresin tablet 122 is positioned in the cavity 12 (the melting step). - Next, while being in close contact with an upper surface and side surfaces of a light-emitting
element 13, a melted silicone resin is further heated to a secondary cross-linking temperature T1 so as to be totally cured by secondary cross-linking (the curing step) (seeFIG. 31( c)). This allows formation of the sealingresin 21 and production of a light-emittingdevice 1 f. - As described earlier, according to the present modification, without using a mechanism for vacuumization, it is possible to produce the light-emitting
device 1 f by heating the sealingresin tablet 122 positioned in thecavity 12. - As compared with a method in which the sealing
mixed powder 120 or the sealingresin powder 121 is used as it is, the light-emitting device production method in accordance with the present modification is less likely to make a gap between powder of the silicone resin and the fluorescent material and among powder particles of the silicone resin containing the fluorescent material. This allows the silicone resin obtained after the heating to have a smaller degree of volume shrinkage. Therefore, the sealing can be carried out in accordance with a size of thecavity 12, and it is possible to reduce a variation in chromaticity value among light-emittingdevices 1 f. - Further, according to the light-emitting device production method in accordance with the present modification, it is possible to increase handleability of the sealing
mixed powder 120 and the sealingresin powder 121. - The
cavity 12 may be sealed with a sealing mixed powder sheet (the sealing resin sheet, the sealing member) 123 which is molded into a sheet by compressing the sealingmixed powder 120. -
FIGS. 32( a) through 32(e) schematically illustrate a method for producing the sealing mixed powder sheet 123 obtained by forming, into a sheet, the sealingmixed powder 120 illustrated inFIG. 28( a). - First, the sealing
mixed powder 120 is obtained by sufficiently mixing (i) powder of the silicone resin which has been subjected to primary cross-linking and is in a semi-cured state and (ii) the fluorescent material until the fluorescent material is evenly dispersed (seeFIG. 32( a)). - Next, the sealing
mixed powder 120 is introduced into a mold (seeFIG. 32( b)), and the sealingmixed powder 120 is molded into a sheet by compression molding by use of a pressurizing plate 30 (seeFIG. 32( c)). - This makes it possible to produce the sealing mixed powder sheet 123 which is molded by compressing the sealing
mixed powder 120 into a sheet (seeFIG. 32( d)). - According to such a method as described above for producing the sealing mixed powder sheet 123 (a dry blending method), no expensive kneading equipment is used that is essential to the light-emitting device production method as illustrated in
FIG. 9( a) throughFIG. 9( e) for producing the sealingresin sheet 20 by forming the kneadedresin 24 into a sheet and that has (i) a temperature regulating function for adjusting a viscosity of the silicone resin during the kneading and (ii) abrasion resistance to the fluorescent material. Therefore, it is possible to produce the sealing mixed powder sheet 123 at a low cost and in a short time. - The sealing mixed powder sheet 123 thus produced can replace the sealing
resin sheet 20 illustrated inFIG. 3( a). - Note that, it is preferable that powder of the silicone resin totally cured by secondary cross-linking be further mixed in the sealing
mixed powder 120 which is used for producing the sealing mixed powder sheet 123. The silicone resin subjected to secondary cross-linking maintains a totally cured state also during the heating in each of the melting step and the curing step. Therefore, in a case where the sealingmixed powder 120 in which powder of the silicone resin subjected to secondary cross-linking is mixed is formed into a sheet, it is possible to produce the sealing mixed powder sheet 123 that can prevent precipitation of the fluorescent material during the heating in, for example, the curing step. - Note also that the light-emitting
elements 13 may be individually sealed with pieces of the sealing mixed powder sheet 123 which pieces are obtained by dividing the sealing mixed powder sheet 123 (seeFIG. 32( e)). - As described earlier, a light-emitting device production method in accordance with the present invention includes: a mounting step of mounting at least one light-emitting element on a substrate; a positioning step of positioning a sealing member so that the sealing member faces an upper surface of the at least one light-emitting element mounted in the mounting step, the sealing member at least containing a silicone resin semi-cured by primary cross-linking and a fluorescent material; a melting step of melting, by heating at a temperature lower than a secondary cross-linking temperature at which the silicone resin subjected to primary cross-linking is totally cured by secondary cross-linking, the sealing member positioned in the positioning step; and a curing step of, while the sealing member melted in the melting step is in close contact with at least the upper surface of the at least one light-emitting element, heating the sealing member at a temperature equal to or higher than the secondary cross-linking temperature, the silicone resin decreasing in viscosity reversibly in a temperature region between a room temperature and the temperature lower than the secondary cross-linking temperature, and being totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature.
- According to the light-emitting device production method, a sealing member is positioned so that the sealing member faces an upper surface of the at least one light-emitting element mounted on the substrate, the sealing member at least containing a silicone resin semi-cured by primary cross-linking and a fluorescent material.
- Note here that the silicone resin decreases in viscosity reversibly in a temperature region between a room temperature and the temperature lower than the secondary cross-linking temperature, and is totally cured non-reversibly in a temperature region equal to or higher than the secondary cross-linking temperature. Therefore, a viscosity of the silicone resin can be repeatedly controlled by changing a temperature in the temperature region between the room temperature and the temperature lower than the secondary cross-linking temperature.
- Accordingly, for example, in a case where the viscosity of the silicone resin is controlled (reduced), during kneading of the fluorescent material with the silicone resin, to an extent that the kneaded fluorescent material is not precipitated, the fluorescent material can be evenly dispersed in the silicone resin.
- Hence, according to the light-emitting device production method, it is possible to obtain a sealing member in which the fluorescent material is evenly dispersed in the silicone resin. Therefore, in a case where a light-emitting element is sealed with the sealing member, it is possible to attain a light-emitting device production method that allows (i) equalization of a concentration of a fluorescent material among light-emitting devices and (ii) a smaller variation in chromaticity value which variation is caused by a fluorescent material concentration and a fluorescent material contained amount.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing member positioned in the positioning step is sealing mixed powder in which powder of the silicone resin subjected to primary cross-linking and the fluorescent material are at least mixed.
- According to the light-emitting device production method, in a case where powder of the silicone resin subjected to primary cross-linking and the fluorescent material are sufficiently mixed, the fluorescent material is evenly dispersed in the sealing mixed powder.
- Therefore, according to the light-emitting device production method, in a case where the sealing mixed powder is positioned in a fixed amount in the positioning step, it is possible to equalize a concentration of a fluorescent material among light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that powder of the silicone resin totally cured by secondary cross-linking is further mixed in the sealing mixed powder.
- According to the light-emitting device production method, powder of the silicone resin totally cured by secondary cross-linking is further mixed in the sealing mixed powder. The silicone resin subjected to secondary cross-linking maintains a totally cured state also during the heating in each of the melting step and the curing step. Therefore, in a case where powder of the silicone resin subjected to secondary cross-linking is contained in the sealing mixed powder, it is possible to prevent precipitation of the fluorescent material in each of the melting step and the curing step.
- Therefore, according to the light-emitting device production method, the fluorescent material can improve in state of dispersion in a light-emitting device.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing member positioned in the positioning step is a sealing resin sheet which is made of a sheet containing the fluorescent material and which at least contains the silicone resin subjected to primary cross-linking.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing resin sheet is obtained by forming, into a sheet, a kneaded resin obtained by kneading the fluorescent material with the silicone resin subjected to primary cross-linking and heated at the temperature lower than the secondary cross-linking temperature.
- According to the light-emitting device production method, in a case where the fluorescent material is kneaded with the silicone resin while the viscosity of the silicone resin is controlled to an extent that the fluorescent material is not precipitated, it is possible to obtain a kneaded resin in which the fluorescent material is evenly dispersed in the silicone resin.
- Accordingly, in a case where the sealing resin sheet obtained by forming the kneaded resin into a sheet is positioned in the positioning step, it is possible to equalize a concentration of a fluorescent material among light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing resin sheet is obtained by compressing, into a sheet, sealing mixed powder in which powder of the silicone resin subjected to primary cross-linking and the fluorescent material are at least mixed.
- According to the light-emitting device production method, the sealing resin sheet is obtained by compressing, into a sheet, sealing mixed powder in which powder of the silicone resin subjected to primary cross-linking and the fluorescent material are at least mixed. Therefore, it is possible to easily produce a sealing resin sheet without using expensive kneading equipment that is essential to the light-emitting device production method for producing the sealing resin sheet by forming the kneaded resin into a sheet and that has (i) a temperature regulating function for adjusting a viscosity of the silicone resin during the kneading and (ii) abrasion resistance to the fluorescent material.
- Therefore, according to the light-emitting device production method, it is possible to produce a sealing resin sheet at a low cost and in a short time.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that powder of the silicone resin totally cured by secondary cross-linking is further mixed in the sealing mixed powder.
- According to the light-emitting device production method, powder of the silicone resin totally cured by secondary cross-linking is further mixed in the sealing mixed powder. The silicone resin subjected to secondary cross-linking maintains a totally cured state also during the heating in, for example, the curing step. Therefore, in a case where the sealing mixed powder in which powder of the silicone resin subjected to secondary cross-linking is mixed is formed into a sheet, it is possible to produce a sealing resin sheet that can prevent precipitation of the fluorescent material during the heating in, for example, the curing step.
- Therefore, according to the light-emitting device production method, the fluorescent material can improve in state of dispersion in a light-emitting device.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing member positioned in the positioning step is sealing resin powder which is made of powder of the silicone resin subjected to primary cross-linking and which contains the fluorescent material.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing resin powder is obtained by pulverizing a kneaded resin obtained by kneading the fluorescent material with the silicone resin subjected to primary cross-linking and heated at the temperature lower than the secondary cross-linking temperature.
- According to the light-emitting device production method, in a case where the fluorescent material is kneaded with the silicone resin while the viscosity of the silicone resin is controlled to an extent that the fluorescent material is not precipitated, it is possible to obtain a kneaded resin in which the fluorescent material is evenly dispersed in the silicone resin.
- Accordingly, in a case where the sealing resin powder obtained by pulverizing the kneaded resin is positioned in a fixed amount in the positioning step, it is possible to equalize a concentration of a fluorescent material among light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that: in the mounting step, the at least one light-emitting element is mounted in a respective plurality of cavities which are provided in the substrate so as to open upward; in the positioning step, the sealing resin sheet is stacked, as the sealing member, on the substrate so as to cover all the plurality of cavities provided in the substrate; in the melting step, the melted sealing member is pressurized so as to be filled in the plurality of cavities; and in the curing step, the silicone resin subjected to primary cross-linking and contained in the sealing member which has been filled in the plurality of cavities is totally cured.
- According to the light-emitting device production method, the sealing resin sheet that is stacked, as the sealing member, on the substrate so as to cover all the plurality of cavities provided in the substrate is heated while the melted sealing member (silicone resin) is pressurized so as to be filled in the plurality of cavities. Therefore, the melted sealing member can be simultaneously filled in the plurality of cavities. Then, in a case where the silicone resin subjected to primary cross-linking and contained in the sealing member which has been filled in the plurality of cavities is totally cured, the at least one light-emitting element mounted in the respective plurality of cavities can be simultaneously sealed.
- Therefore, as compared with a method for separately filling cavities with a sealing member for each of the cavities, the light-emitting device production method allows the sealing member that is filled in the plurality of cavities to less vary in characteristic and/or amount for each of the plurality of cavities. This can prevent a variation in characteristic among light-emitting devices.
- Further, the light-emitting device production method allows the melted sealing member to be simultaneously filled in the plurality of cavities without using a special dispenser, a molding machine, or the like for causing the melted sealing member to be filled in the plurality of cavities. This allows a remarkable increase in production efficiency of the light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the plurality of cavities provided in the substrate are provided with respective through holes.
- According to the light-emitting device production method, the plurality of cavities provided in the substrate are provided with respective through holes. This promotes exhaust of air from the plurality of cavities.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing resin sheet is provided with through holes which face the respective plurality of cavities.
- According to the light-emitting device production method, the sealing resin sheet is provided with through holes which face the respective plurality of cavities. This promotes exhaust of air from the plurality of cavities.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that: in the positioning step, a surface molding release sheet having a surface provided with pearskin-finished unevenness is further stacked and positioned on the sealing resin sheet; and in the curing step, the silicone resin subjected to primary cross-linking and contained in the sealing member is totally cured while the surface molding release sheet is in contact with a surface of the sealing member which has been filled in the plurality of cavities.
- According to the light-emitting device production method, in the positioning step, a surface molding release sheet having a surface provided with pearskin-finished unevenness is stacked and positioned on the sealing resin sheet; and in the curing step, the silicone resin subjected to primary cross-linking and contained in the sealing member is totally cured while the surface molding release sheet is in contact with a surface of the sealing member which has been filled in the plurality of cavities.
- Therefore, according to the light-emitting device production method, the sealing member that is totally cured has a surface provided with pearskin-finished unevenness. Therefore, this unevenness allows an increase in light extraction efficiency of the light-emitting devices.
- Further, in a case where a surface molding release sheet having a porous paper quality is used as the surface molding release sheet of the present invention, it is possible to smoothly exhaust air from the plurality of cavities.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that: in the positioning step, a lens molding resin sheet made of a light-transmissive resin is further stacked and positioned on the sealing resin sheet; and in the melting step, the lens molding resin sheet is pressurized against the sealing resin sheet via a lens molding mold provided with at least one lens molding recess which faces the at least one light-emitting element mounted on the substrate.
- According to the light-emitting device production method, a lens molding resin sheet made of a light-transmissive resin is further stacked and positioned on the sealing resin sheet. Then, the lens molding resin sheet is pressurized against the sealing resin sheet via a lens molding mold provided with at least one lens molding recess which faces the respective plurality of cavities. This allows the at least one lens molding recess to be filled with a melted resin of the lens molding resin sheet.
- Therefore, according to the light-emitting device production method, in a case where a resin of the lens molding resin sheet is cured while the resin is filled in the at least one lens molding recess, it is possible to simultaneously produce a plurality of light-emitting devices each further including a lens.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that: in the mounting step, a plurality of light-emitting elements included in the at least one light-emitting element are mounted on the substrate which has a plane surface; in the positioning step, the sealing resin sheet which is provided with a plurality of recesses in which the respective plurality of light-emitting elements mounted on the substrate can be contained is positioned, as the sealing member, on the substrate so that the plurality of light-emitting elements are contained in the respective plurality of recesses; in the melting step, the sealing resin sheet is pressurized, via a lens molding mold provided with lens molding recesses which face the respective plurality of light-emitting elements mounted on the substrate, so as to be filled in the lens molding recesses; and in the curing step, the silicone resin subjected to primary cross-linking and contained in the sealing member which has been filled in the lens molding recesses is totally cured.
- According to the light-emitting device production method, a plurality of light-emitting elements included in the at least one light-emitting element are mounted on the substrate which has a plane surface; and the sealing resin sheet (sealing member) which is provided with a plurality of recesses in which the respective plurality of light-emitting elements mounted on the substrate can be contained is stacked and positioned on the substrate so that the plurality of light-emitting elements are contained in the respective plurality of recesses. Then, the sealing resin sheet is pressurized against the substrate via a lens molding mold provided with lens molding recesses which face the respective plurality of light-emitting elements mounted on the substrate. This allows the melted sealing member to be filled in the lens molding recesses, so that the silicone resin subjected to primary cross-linking and contained in the sealing member can be totally cured by secondary cross-linking in the lens molding recesses.
- Therefore, according to the light-emitting device production method, it is possible to simultaneously produce a plurality of light-emitting devices in each of which the sealing member is molded to be lens-shaped.
- The light-emitting device production method in accordance with the present invention is preferably arranged to further include: a placing step of placing a reflecting plate which is provided with a plurality of openings in which the at least one light-emitting elements can be contained, the plurality of openings each having at least an inner surface which has a reflecting function, wherein: in the mounting step, a plurality of light-emitting elements included in the at least one light-emitting element are mounted on the substrate which has a plane surface; in the placing step, the reflecting plate is placed on the substrate so that the plurality of light-emitting elements mounted on the substrate are contained in the respective plurality of openings; in the positioning step, the sealing resin sheet is positioned, as the sealing member, on the reflecting plate so as to cover all the plurality of openings provided in the reflecting plate placed on the substrate; in the melting step, the melted sealing member is pressurized so as to be filled in the plurality of openings; and in the curing step, the silicone resin subjected to primary cross-linking and contained in the sealing member which has been filled in the plurality of openings is totally cured.
- According to the light-emitting device production method, the sealing resin sheet serving as the sealing member is positioned on the reflecting plate so as to cover all the plurality of openings provided in the reflecting plate. Then, the melted sealing member is heated while being pressurized so as to be filled in the plurality of openings, and the silicone resin subjected to primary cross-linking and contained in the sealing member which has been filled in the plurality of openings is totally cured. This allows the melted sealing member to be simultaneously filled in the plurality of openings, so that the plurality of light-emitting elements mounted in the respective plurality of openings can be simultaneously sealed.
- Therefore, according to the light-emitting device production method, it is possible to simultaneously produce a plurality of light-emitting devices each of which has a reflecting function and has increased in efficiency with which light from a light-emitting element is used.
- Further, as compared with a method for separately filling openings with a sealing member for each of the openings, the light-emitting device production method allows the sealing member that is filled in the plurality of openings to less vary in characteristic and/or amount for each of the plurality of openings. This can prevent a variation in characteristic among light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that in the melting step, the sealing resin sheet is pressurized against the substrate with vacuum pressure.
- According to the light-emitting device production method, the sealing resin sheet is heated while being pressurized against the substrate with vacuum pressure. This allows air to be exhausted from the plurality of cavities without fail, and allows prevention of air from entering the melted silicone resin.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that a vacuum heat pressing apparatus is used to heat and pressurize the sealing resin sheet.
- According to the light-emitting device production method, a process for heating the sealing resin sheet under vacuum can be easily carried out in the vacuum heat pressing apparatus. This allows an increase in operation efficiency.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing resin sheet positioned in the positioning step includes sealing resin sheets which are stacked and contain the fluorescent material in different amounts.
- According to the light-emitting device production method, a plurality of sealing resin sheets which contain the fluorescent material in different amounts are stacked. Therefore, a change in combination of sealing resin sheets makes it possible to easily control a concentration at which the fluorescent material is dispersed.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that a vacuum impregnating apparatus is used to heat and pressurize the sealing resin sheet.
- According to the light-emitting device production method, a process for heating the sealing resin sheet at a high pressure can be easily carried out in the vacuum impregnating apparatus. This allows an increase in operation efficiency.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that: in the mounting step, the at least one light-emitting element is mounted in at least one cavity which is provided in the substrate so as to open upward; and in the positioning step, the sealing mixed powder is positioned, as the sealing member, in the at least one cavity in which the at least one light-emitting element is mounted.
- According to the light-emitting device production method, in the positioning step, the sealing mixed powder is positioned, as the sealing member, in the at least one cavity in which the at least one light-emitting element is mounted. This makes it possible to easily equalize a concentration of a fluorescent material among light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing mixed powder is compressed into a tablet.
- As compared with a method in which the sealing mixed powder is used as it is, the light-emitting device production method is less likely to make a gap between powder of the silicone resin and the fluorescent material. This allows the silicone resin obtained after the heating to have a smaller degree of volume shrinkage.
- Therefore, according to the light-emitting device production method, it is possible to further reduce a variation in chromaticity value among light-emitting devices and to increase handleability of the sealing mixed powder.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that: in the mounting step, the at least one light-emitting element is mounted in at least one cavity which is provided in the substrate so as to open upward; and in the positioning step, the sealing resin powder is positioned, as the sealing member, in the at least one cavity in which the at least one light-emitting element is mounted.
- According to the light-emitting device production method, in the positioning step, the sealing resin powder is positioned, as the sealing member, in the at least one cavity in which the at least one light-emitting element is mounted. This makes it possible to easily equalize a concentration of a fluorescent material among light-emitting devices.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that the sealing resin powder is compressed into a tablet.
- As compared with a method in which the sealing resin powder is used as it is, the light-emitting device production method is less likely to make a gap between silicone resins containing a fluorescent material. This allows the silicone resin obtained after the heating to have a smaller degree of volume shrinkage.
- Therefore, according to the light-emitting device production method, it is possible to further reduce a variation in chromaticity value among light-emitting devices and to increase handleability of the sealing resin powder.
- The light-emitting device production method in accordance with the present invention is preferably arranged such that in the melting step, the silicone resin is melted under a vacuum environment.
- According to the light-emitting device production method, in the melting step, the silicone resin is melted under a vacuum environment. This allows deaeration of the silicone resin melted in the
cavity 12. - Therefore, the light-emitting device production method allows an inner surface of the cavity and the totally cured silicone resin to be in closer contact to each other.
- The present invention is not limited to the description of the embodiments above, but may be altered by a skilled person within the scope of the claims. An embodiment based on a proper combination of technical means disclosed in different embodiments is encompassed in the technical scope of the present invention.
- For example, the present invention can be suitably used to produce light-emitting devices for use in, for example, (i) a display device and a lighting apparatus each including an LED as a light source; (ii) a backlight of, for example, a display; (iii) a signal; and (iv) a large display and an advertising sign each being used outside.
-
-
- 1 a Light-emitting device
- 1 b Light-emitting device
- 1 c Light-emitting device
- 1 d Light-emitting device
- 1 e Light-emitting device
- 1 f Light-emitting device
- 10 Multiple cavity circuit board (Substrate)
- 11 Circuit board (Substrate)
- 12 Cavity
- 12 a Through hole
- 13 Light-emitting element
- 14, 54, 64, 74 Mounting wiring pattern
- 15, 65 Electroconductive adhesive
- 16, 56, 66, 76 Connection wiring pattern
- 17, 57, 67, 77 a, 77 b Electroconductive wire
- 20 Sealing resin sheet (Sealing member)
- 20 a Through hole
- 20A First sealing resin sheet (Sealing resin sheet, Sealing member)
- 20B Second sealing resin sheet (Sealing resin sheet, Sealing member)
- 21 Sealing resin
- 24 Kneaded resin
- 25 Lens molding resin sheet
- 26 Sealing resin sheet (Sealing member)
- 26 a Recess
- 31 Surface molding release sheet
- 32 Weight plate
- 33 Vacuum heating furnace
- 35 Vacuum heat pressing apparatus
- 35 a Heater stand
- 35 b Press heater
- 35 e Lens molding groove (Lens molding recess)
- 35 h Fixture recess
- 38 a Vacuuming bag
- 38 c Heating furnace
- 38 d Vacuum pump
- 40 Vacuum heating apparatus
- 41 Upper chamber
- 42 Lower chamber
- 43 Diaphragm rubber
- 44, 79 Heating plate
- 50 Light-emitting display device (Light-emitting device)
- 51 Plane circuit board (Substrate)
- 53 Light-emitting element
- 58 Reflecting plate
- 58 a Opening
- 60 Plane circuit board (Substrate)
- 61 Circuit board (Substrate)
- 63, 73 Light-emitting element
- 120 Sealing mixed powder (Sealing member)
- 121 Sealing resin powder (Sealing member)
- 122 Sealing resin tablet (Sealing mixed powder, Sealing resin powder, Sealing member)
- 123 Sealing mixed powder sheet (Sealing resin sheet, Sealing member)
- 132 a Opening
- T0 Room Temperature
- T1 Secondary cross-linking temperature
Claims (16)
1.-25. (canceled)
26. A sealing member comprising:
at least a thermoplastic resin and a fluorescent material,
the thermoplastic resin being thermoplastic at a temperature lower than a predetermined cross-linking temperature, and being cured non-reversibly at a temperature equal to or higher than the predetermined cross-linking temperature.
27. The sealing member as set forth in claim 26 , wherein the thermoplastic resin is subjected to primary cross-linking at the temperature lower than the predetermined cross-linking temperature, and the thermoplastic resin is subjected to secondary cross-linking at the temperature equal to or higher than the predetermined cross-linking temperature.
28. The sealing member as set forth in claim 26 , wherein the predetermined cross-linking temperature is not lower than 120° C. and not higher than 170° C.
29. The sealing member as set forth in claim 26 , wherein the sealing member is a sealing sheet obtained by molding, into a sheet, the thermoplastic resin in which the fluorescent material is dispersed.
30. The sealing member as set forth in claim 29 , wherein the sealing sheet is provided with a through hole.
31. The sealing member as set forth in claim 29 , wherein the sealing sheet has a surface provided with a plurality of recesses.
32. The sealing member as set forth in claim 29 , wherein the sealing sheet has a surface provided with a plurality of protrusions.
33. The sealing member as set forth in claim 26 , wherein the sealing member is sealing powder containing at least powder of the thermoplastic resin in which the fluorescent material is dispersed.
34. The sealing member as set forth in claim 26 , wherein the sealing member is sealing powder in which at least (i) powder of the thermoplastic resin and (ii) powder of the fluorescent material are mixed.
35. The sealing member as set forth in claim 34 , wherein in the sealing powder, (i) the powder of the thermoplastic resin and (ii) the powder of the fluorescent material the sealing powder differ in particle size.
36. The sealing member as set forth in claim 33 , wherein the sealing powder is compressed into a predetermined shape.
37. The sealing member as set forth in claim 36 , wherein the predetermined shape is a tablet.
38. The sealing member as set forth in claim 36 , wherein the predetermined shape is a sheet.
39. The sealing member as set forth in claim 33 , wherein powder of the thermoplastic resin subjected to secondary cross-linking is further mixed in the sealing powder.
40. The sealing member as set forth in claim 26 , wherein the thermoplastic resin contains a solvent containing benzene, toluene, and xylene.