US20150104641A1 - Coated overhead conductor - Google Patents

Coated overhead conductor Download PDF

Info

Publication number
US20150104641A1
US20150104641A1 US14/051,080 US201314051080A US2015104641A1 US 20150104641 A1 US20150104641 A1 US 20150104641A1 US 201314051080 A US201314051080 A US 201314051080A US 2015104641 A1 US2015104641 A1 US 2015104641A1
Authority
US
United States
Prior art keywords
conductor
coating
aluminum
oxide
overhead cable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/051,080
Other languages
English (en)
Inventor
Vijay Mhetar
Cody R. DAVIS
Sathish Kumar RANGANATHAN
John OLVER
John Dillard
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Cable Technologies Corp
Emisshield Inc
Original Assignee
General Cable Technologies Corp
Emisshield Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Cable Technologies Corp, Emisshield Inc filed Critical General Cable Technologies Corp
Priority to US14/051,080 priority Critical patent/US20150104641A1/en
Priority to TW102138287A priority patent/TW201515026A/zh
Priority to ARP130103862A priority patent/AR093122A1/es
Priority to EP13895379.9A priority patent/EP3055868B1/en
Priority to BR112016007986-8A priority patent/BR112016007986B1/pt
Priority to CN201380081526.0A priority patent/CN105814648A/zh
Priority to PCT/US2013/070154 priority patent/WO2015053796A1/en
Priority to ES13895379T priority patent/ES2739040T3/es
Priority to MX2016004379A priority patent/MX2016004379A/es
Priority to CA2925856A priority patent/CA2925856C/en
Assigned to GENERAL CABLE TECHNOLOGIES CORPORATION reassignment GENERAL CABLE TECHNOLOGIES CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: RANGANATHAN, SATHISH KUMAR, DAVIS, CODY, MHETAR, VIJAY
Publication of US20150104641A1 publication Critical patent/US20150104641A1/en
Assigned to Emisshield, Inc. reassignment Emisshield, Inc. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: DILLARD, JOHN, OLVER, JOHN
Priority to US15/230,194 priority patent/US10332658B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B13/00—Apparatus or processes specially adapted for manufacturing conductors or cables
    • H01B13/06—Insulating conductors or cables
    • H01B13/16—Insulating conductors or cables by passing through or dipping in a liquid bath; by spraying
    • H01B13/165—Insulating conductors or cables by passing through or dipping in a liquid bath; by spraying by spraying
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
    • B05D7/20—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to wires
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24C—ABRASIVE OR RELATED BLASTING WITH PARTICULATE MATERIAL
    • B24C1/00—Methods for use of abrasive blasting for producing particular effects; Use of auxiliary equipment in connection with such methods
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B1/00—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors
    • H01B1/02—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors mainly consisting of metals or alloys
    • H01B1/023—Alloys based on aluminium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B1/00—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors
    • H01B1/02—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors mainly consisting of metals or alloys
    • H01B1/026—Alloys based on copper
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/002—Inhomogeneous material in general
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/02—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of inorganic substances
    • H01B3/10—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of inorganic substances metallic oxides
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B7/00—Insulated conductors or cables characterised by their form
    • H01B7/17—Protection against damage caused by external factors, e.g. sheaths or armouring
    • H01B7/29—Protection against damage caused by extremes of temperature or by flame
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B7/00—Insulated conductors or cables characterised by their form
    • H01B7/17—Protection against damage caused by external factors, e.g. sheaths or armouring
    • H01B7/29—Protection against damage caused by extremes of temperature or by flame
    • H01B7/292—Protection against damage caused by extremes of temperature or by flame using material resistant to heat
    • H—ELECTRICITY
    • H02—GENERATION; CONVERSION OR DISTRIBUTION OF ELECTRIC POWER
    • H02G—INSTALLATION OF ELECTRIC CABLES OR LINES, OR OF COMBINED OPTICAL AND ELECTRIC CABLES OR LINES
    • H02G7/00—Overhead installations of electric lines or cables
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D1/00—Processes for applying liquids or other fluent materials
    • B05D1/02—Processes for applying liquids or other fluent materials performed by spraying
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D1/00—Processes for applying liquids or other fluent materials
    • B05D1/02—Processes for applying liquids or other fluent materials performed by spraying
    • B05D1/08—Flame spraying
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D1/00—Processes for applying liquids or other fluent materials
    • B05D1/30—Processes for applying liquids or other fluent materials performed by gravity only, i.e. flow coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/002—Pretreatement
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/08—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by flames
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • B05D3/12—Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials by mechanical means
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D5/00—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures
    • B05D5/12—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures to obtain a coating with specific electrical properties
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2916—Rod, strand, filament or fiber including boron or compound thereof [not as steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2918—Rod, strand, filament or fiber including free carbon or carbide or therewith [not as steel]
    • Y10T428/292—In coating or impregnation
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2933—Coated or with bond, impregnation or core
    • Y10T428/294—Coated or with bond, impregnation or core including metal or compound thereof [excluding glass, ceramic and asbestos]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2933—Coated or with bond, impregnation or core
    • Y10T428/294—Coated or with bond, impregnation or core including metal or compound thereof [excluding glass, ceramic and asbestos]
    • Y10T428/2958—Metal or metal compound in coating

Definitions

  • the present invention relates to a surface modified overhead conductor with a coating that allows the conductor to operate at lower temperatures.
  • the amount of power a transmission line can deliver is dependent on the current-carrying capacity (ampacity) of the line.
  • the ampacity of a line is limited by the maximum safe operating temperature of the bare conductor that carries the current. Exceeding this temperature can result in damage to the conductor or the accessories of the line.
  • the conductor gets heated by Ohmic losses and solar heat and it gets cooled by conduction, convection and radiation.
  • WO 2007/034248 to Simic discloses overhead conductors coated with a spectrally selective surface coating.
  • the coating has a coefficient of heat emission (E) higher than 0.7 and coefficient of solar absorption (A) that is less than 0.3.
  • Simic also requires that the surface be white in color to have low solar absorption.
  • DE 3824608 discloses an overhead cable having a black paint coating with an emissivity greater than 0.6, preferably greater than 0.9.
  • the paint is made of a plastic (e.g. polyurethane) and black color pigment.
  • FR 2971617 discloses an electric conductor coated with a polymeric layer whose emissivity coefficient is 0.7 or more and solar absorption coefficient is 0.3 or less.
  • the polymeric layer is produced from polyvinylidene fluoride (PVDF) and a white pigment additive.
  • Both FR 2971617 and WO 2007/034248 require white coatings that are not desirable due to glare and discoloration over time.
  • Both DE 3824608 and FR 2971617 require polymeric coatings that are not desirable due to their questionable heat and wet aging characteristics.
  • US 20120074122 A1 teaches the application of high emissivity coatings, such as those found in U.S. Pat. No. 7,105,047 and U.S. Pat. No. 6,921,431, on or adjacent to heating elements within a baking oven to modify the radiating heat. Those application and patents are incorporated herein by reference.
  • the temperature of the conductor is dependent on a number of factors including the electrical properties of the conductor, the physical properties of the conductor, and the local weather conditions.
  • One way the conductor will increase in temperature is by absorbing heat from the sun due to solar radiation.
  • the amount of heat absorbed is dependent on the surface of the conductor, that is, the surface's coefficient of absorptivity (“absorptivity”).
  • absorptivity indicates that the conductor absorbs only a small amount of heat due to solar radiation.
  • emissivity emissivity
  • an object of the present invention to provide an overhead conductor that contains an emissivity agent, when tested in accordance to ANSI C119.4-2004, reduces the operating temperature of the conductor compared to the temperature of the same conductor without the emissivity agent.
  • the emissivity agent can be incorporated directly into the conductor or coated on the conductor.
  • the operating temperature is reduced by at least 5° C.
  • the overhead conductor has its surface exposed to the environment coated with a layer consisting of a high emissivity coating, such as those available from Emisshield, Inc. (Blacksburg, Va.), disposed on the exposed surface which alters the performance of the conductor surface.
  • the coating layer contains about 5% to about 30% of an inorganic adhesive, about 45% to about 92% of a filler, about 2% to about 20% of one or more emissivity agents, and optionally, about 1% to about 5% of a stabilizer.
  • the coating provides superior adhesion and flexibility on the conductor, such that it is able to resist peeling and cracking during repeated bending of the cable.
  • the conductor coating layer contains, in dry weight, about 10% to about 25% sodium silicate, about 55% to about 75% SiO 2 dry powder, about 10% to about 25% B 4 C, optionally about 0.5% to about 5.0% boron nitride dry weight, and about 0.5% to about 2% bentonite powder.
  • the dry composition can be prepared as a wet mixture by adding about 20% to about 40% deionized water on a wet basis.
  • the coating used contains, as dry weight percent, about 13% to about 15% sodium silicate, about 69% SiO 2 dry powder, about 14% to about 16% boron carbide, and about 1.0% to about 1.5% bentonite powder.
  • That dry composition can be prepared as a wet aqueous mixture having about 36% to about 38% deionized water on a wet basis.
  • the coating used contains, as dry weight percent, about 13% to about 15% sodium silicate, about 69% SiO 2 dry powder, about 13% to about 15% boron carbide dry weight, about 1.0% to about 2.0% boron nitride dry weight, and about 1.0% to about 1.5% bentonite powder.
  • That dry composition can be prepared as a wet aqueous mixture having about 36% to about 38% deionized water on a wet basis.
  • a yet further object of the present invention provides methods for coating an overhead conductor with an inorganic, flexible coating that reduces the operating temperature of the conductor compared to the temperature of the same conductor without the heat radiating agent.
  • FIG. 1 is a cross sectional view of a conductor in accordance with one embodiment of the present invention
  • FIG. 2 is a cross sectional view of a conductor in accordance with one embodiment of the present invention.
  • FIG. 3 is a cross sectional view of a conductor in accordance with one embodiment of the present invention.
  • FIG. 4 is a cross sectional view of a conductor in accordance with one embodiment of the present invention.
  • FIG. 5 is a drawing showing the test arrangement to measure the temperature of metal substrates for a given applied current
  • FIG. 6 is a drawing showing a continuous process of the present invention.
  • FIG. 7 is drawing showing a cross-section of the flooded die
  • FIG. 8 is a drawing showing a plan view of the flooded die.
  • FIG. 9 ′ is a drawing showing a cut-away view of the flooded die.
  • the present invention provides an overhead conductor that contains an outer coating that, when tested in accordance to ANSI C119.4-2004, reduces the operating temperature of the conductor compared to the temperature of the same conductor without the heat radiating agent.
  • the heat radiating agent can be incorporated directly into the conductor or coated on the conductor.
  • the operating temperature is reduced by at least 5° C.
  • the present invention provides a bare overhead conductor with a surface coating to decrease the operating temperature of the conductor without significant change to any electrical or mechanical properties, such as electrical resistance, heat aging resistance, corona, elongation at rupture, tensile strength, and modulus of elasticity for example.
  • the coating layer of the present invention contains about 5% to about 30%, preferably about 13% to about 15%, of an inorganic adhesive, about 45% to about 92%, preferably about 68% to about 69%, of a filler, about 2% to about 20%, preferably about 14% to about 17%, of one or more emissivity agents, and optionally, about 1% to about 5%, preferably about 1% to about 1.5%, of a stabilizer.
  • the coating layer is preferably less than 200 microns, more preferably less than 100 microns, most preferably less than 30 microns. But in any event, the thickness is at least 5 microns.
  • the coatings produced in accordance with the present invention are preferably non-white. Coatings appropriate for the present invention are available from Emisshield, Inc. (Blacksburg, Va.).
  • wet admixture refers to relative percentages of the composition of the thermal protective coating in solution and “dry admixture” refers to the relative percentages of the composition of the dry thermal protective coating mixture prior to the addition of water. In other words, the dry admixture percentages are those present without taking water into account.
  • Wet admixture refers to the admixture in solution (with water).
  • Weight percentage is the weight in a wet admixture
  • dry weight percentage is the weight in a dry admixture without regard to the wet weight percentages. All percentages mentioned herein are based on dry weight of the total composition, unless otherwise indicated.
  • the inorganic adhesive is preferably an alkali/alkaline earth metal silicate, which includes, but is not limited to, sodium silicate, potassium silicate, lithium silicate, calcium silicate, and magnesium silicate.
  • the preferred inorganic adhesive is sodium silicate.
  • the filler is preferably a metal oxide, which includes, but is not limited to, silicon dioxide, aluminum oxide, titanium dioxide, magnesium oxide, calcium oxide, and boron oxide.
  • the preferred filler is silicon dioxide.
  • the emissivity agent includes, but is not limited to, carbon tetraboride (boron carbide), boron nitride, silicon tetraboride, silicon carbide, molybdenum disilicide, zirconium diboride, cupric chromite, and metallic oxides, such as iron oxides, magnesium oxides, manganese oxides, copper chromium oxides, and chromium oxides, and derivatives thereof.
  • the preferred emissivity agent is boron carbide and/or boron nitride.
  • the stabilizer includes, but is not limited to, bentonite, kaolin, magnesium alumina silica clay, and stabilized zirconium oxide. Other ball clay stabilizers may be substituted herein as a stabilizer.
  • the preferred stabilizer is bentonite.
  • total solids refers to the sum of the silica and the alkali.
  • the weight ratio is a most important silicate variable. Ratio determines the product solubility, reactivity and physical properties. Ratio is either the weight or molar proportion of silica to alkali. Density is an expression of total solids and is typically determined using a hydrometer. As temperatures increase, density decreases. When solids content increases, density increases.
  • the pH is a function of silicate composition and solids concentration. The pH value of silicates does not truly reflect the alkali content of solution, due to the strong buffering capability of silica. This means the pH of a silicate solution is kept constant until almost completely neutralized. The buffering capacity of silicate solutions increases with increasing ratio of silica to alkali.
  • Emissivity agents are available from several sources. Emissivity is the relative power of a surface to emit heat by radiation, and the ratio of the radiant energy emitted by a surface to the radiant energy emitted by a blackbody at the same temperature. Emittance is the energy radiated by the surface of a body per unit area.
  • the stabilizer is bentonite powder, tabular alumina, or magnesium alumina silica clay.
  • the bentonite powder permits the present invention to be prepared and used at a later date. Preparations of the present invention without bentonite powder must be used immediately.
  • Betonite is available, for example, from American Colloid Company (Hoffman Estates, IL) as Polargel®.
  • One or more colorants may be used in the coating composition, preferably at a concentration of about 0.02 to 0.2% (by weight of the total dry composition).
  • the colorant can be organic or inorganic pigments, which includes, but are not limited to, titanium dioxide, rutile, titanium, anatine, brookite, cadmium yellow, cadmium red, cadmium green, orange cobalt, cobalt blue, cerulean blue, aureolin, cobalt yellow, copper pigments, azurite, Han purple, Han blue, Egyptian blue, malachite, Paris green, phthalocyanine blue BN, phthalocyanine green G, verdigris, viridian, iron oxide pigments, sanguine, caput mortuum, oxide red, red ochre, Venetian red, Prussian blue, clay earth pigments, yellow ochre, raw sienna, burnt sienna, raw umber, burnt umber, marine pigments (ultramarine, ultramarine green shade), zinc pigment
  • the conductor coating layer contains, in dry weight, about 10% to about 25% sodium silicate, about 55% to about 75% SiO 2 dry powder, about 10% to about 25% B 4 C, optionally about 0.5% to about 5.0% boron nitride dry weight, and about 0.5% to about 2% bentonite powder.
  • the dry composition can be prepared as a wet mixture by adding about 20% to about 40% deionized water on a wet basis.
  • the coating used contains, as dry weight percent, about 13% to about 15% sodium silicate, about 69% SiO 2 dry powder, about 14% to about 16% boron carbide, and about 1.0% to about 1.5% bentonite powder.
  • That dry composition can be prepared as a wet aqueous mixture having about 36% to about 38% deionized water on a wet basis.
  • the coating used contains, as dry weight percent, about 13% to about 15% sodium silicate, about 69% SiO 2 dry powder, about 13% to about 15% boron carbide dry weight, about 1.0% to about 2.0% boron nitride dry weight, and about 1.0% to about 1.5% bentonite powder.
  • That dry composition can be prepared as a wet aqueous mixture having about 36% to about 38% deionized water on a wet basis.
  • the coating offers a flexible coating that shows no visible cracks when bent on a mandrel of diameter of 10 inches or less.
  • the cured coating is also heat resistant and passes the same mandrel bent test after heat aging at 325° C. for a period of 1 day and 7 days.
  • FIGS. 1 , 2 , 3 , and 4 illustrate various bare overhead conductors according to various embodiments of the invention incorporating a spectrally selective surface.
  • the bare overhead conductor 100 of the present invention generally includes a core of one or more wires 110 , round-cross section conductive wires around the core 120 , and the spectrally selective surface layer 130 .
  • the core 110 may be steel, invar steel, carbon fiber composite, or any other material providing strength to the conductor.
  • the conductive wires 120 are copper, or a copper alloy, or an aluminum or aluminum alloy, including aluminum types 1350, 6000 series alloy aluminum, or aluminum-zirconium alloy, or any other conductive metal.
  • the bare overhead conductor 200 generally includes round conductive wires 210 and the spectrally selective surface layer 220 .
  • the conductive wires 210 are copper, or a copper alloy, or an aluminum or aluminum alloy, including aluminum types 1350, 6000 series alloy aluminum, or aluminum-zirconium alloy, or any other conductive metal.
  • the bare overhead conductor 300 of the present invention generally includes a core of one or more wires 310 , trapezoidal shaped conductive wires around the core 320 , and the spectrally selective surface layer 330 .
  • the core 310 may be steel, invar steel, carbon fiber composite, or any other material providing strength to the conductor.
  • the conductive wires 320 are copper, or a copper alloy, or an aluminum or aluminum alloy, including aluminum types 1350, 6000 series alloy aluminum, or aluminum-zirconium alloy, or any other conductive metal.
  • the bare overhead conductor 400 generally includes trapezoidal shaped conductive wires 410 and the spectrally selective surface layer 420 .
  • the conductive wires 410 are copper, or a copper alloy, or an aluminum or aluminum alloy, including aluminum types 1350, 6000 series alloy aluminum, or aluminum-zirconium alloy, or any other conductive metal.
  • the coating composition can be made in a High Speed Disperser (HSD), Ball Mill, Bead mill or using other techniques known in the art.
  • a HSD is used to make the coating composition.
  • the binders, dispersion medium and surfactant (if used) are taken in a High Speed Disperser and a solution is prepared.
  • the heat radiating agent, fillers, stabilizers, colorants and others additives are slowly added. Initially, a lower stirrer speed is used to remove the entrapped air and afterwards the speed is increased gradually up to 3000 rpm. The high speed mixing is performed until the desired dispersion of the fillers and other additives is achieved in the coating.
  • the dispersion medium can be water or an organic solvent.
  • organic solvents include, but are not limited to, alcohols, ketones, esters, hydrocarbons, and combinations thereof.
  • the preferred dispersion medium is water.
  • the resulting coating mixture is a suspension with a total solid content of about 40-80%, preferably about 45-55%, more preferably about 49-51%. Upon storage of this mixture, the solid particles may settle, and hence, that coating mixture needs to be stirred and may further be diluted to achieve the required viscosity before transferring in to the coating applicator.
  • the surface of the overhead conductor is prepared prior to the application of the coating composition.
  • the preparation process can be chemical treatment, pressurized air cleaning, hot water or steam cleaning, brush cleaning, heat treatment, sand blasting, ultrasound, deglaring, solvent wipe, plasma treatment, and the like.
  • the surface of the overhead conductor is deglared by sand blasting.
  • the coating mixture composition can be applied by spray gun, preferably with 10-45 psi pressure, which is controlled through the air pressure.
  • the spray gun nozzle is preferably placed perpendicular to the direction of the conductor (at approximately 90° angle) to get a uniform coating on conductor product. In specific cases, two or more guns can be used to get more efficient coatings.
  • the coating thickness and density are controlled by the admixture viscosity, gun pressure, and conductor line speed.
  • the overhead conductor temperature is preferably maintained between 10° C. to 90° C. depending on the material of the conductor.
  • the coating mixture can be applied to the overhead conductor by dipping or using a brush or using a roller.
  • the cleaned and dried conductor is dipped into the coating mixture to allow the mixture to completely coat the conductor.
  • the conductor is then removed from the coating mixture and allowed to dry.
  • the coating on the overhead conductor is allowed to dry by evaporation either at room temperature or at elevated temperatures up to 325° C.
  • the coating is dried by direct flame exposure which exposes the coating to intense, but brief (about 0.1-2 seconds, preferably about 0.5-1 second) heating.
  • the developed coating can be used for overhead conductors which are already installed and currently being used.
  • Existing conductors can be coated with a robotic system for automated or semi-automated coating.
  • the automated system functions in three steps: 1. cleaning the conductor surface; 2. applying the coating on the conductor surface; and 3. drying the coating.
  • the surface modification of the present invention can be used in bare overhead conductor accessories and bare overhead conductor electrical transmission and distribution related products and parts for temperature reduction purpose, for example, deadends/termination products, splices/joints products, conductor suspension and support products, and conductor and compression fitting repair parts. These products are commercially available from many manufacturers, such as Preformed Line Products (PLP), Cleveland, Ohio, and AFL, Duncan, S.C.
  • PLP Preformed Line Products
  • Cleveland, Ohio Cleveland, Ohio
  • AFL Duncan, S.C.
  • the coating can be applied to the conductors in several ways. It can be applied by coating the individual wires before their assembly in the bare overhead conductor. Here, it is possible to have all of the wires of the conductor coated, or more economically, only the outer most wires of the conductor coated. Alternatively, the coating can be applied only to the outer surface of the bare overhead conductor. Here, the complete outer surface or a portion thereof can be coated.
  • the coating can be applied in a batch process, a semi-batch process, or a continuous process.
  • the continuous process is preferred.
  • FIG. 6 illustrates a preferred continuous process for the present invention.
  • the conductor 112 is passed through a surface preparation process via a pretreatment unit 104 prior to the coating being applied in the coating unit 106 .
  • the conductor may be dried via a drying/curing unit 108 . Once dried, the cable is wound on a roller 110 .
  • the surface of the conductor 112 is preferably prepared by media blasting.
  • the preferred media is sand, however, glass beads, ilmenite, steel shot, could also be used.
  • the media blasting is followed by air-wiping to blow the particulate materials off the conductor 112 .
  • An air-wipe consists of jets of air blown on to the conductor 112 at an angle and in a direction opposing the direction of travel of the conductor 112 .
  • the air jets create a 360° ring of air that attaches to the circumference of the conductor 112 and wipes the surface with the high velocity of air.
  • any particles on the conductor 112 are wiped and blown back into the pretreatment unit 104 .
  • the air jet typically operates at about 60 to about 100 PSI, preferably about 70-90 PSI, more preferably about 80 PSI.
  • the air jet preferably has a velocity (coming out of the nozzles) of about 125 mph to about 500 mph, more preferably about 150 mph to about 400 mph, and most preferably about 250 mph to about 350 mph.
  • number of particles, that are greater than 10 microns in size, on the surface of the conductor are lower than 1,000 per square feet of the conductor surface, preferably less than 100 per square feet of the surface.
  • the conductor is preferably heated, e.g. by a heating oven, UV, IR, E-beam, open flame, and the like.
  • the heating can be accomplished by single or multiple units.
  • the drying/curing occurs by direct flame application.
  • the cable is passed directly through a flame to heat the cable surface to a temperature above ambient temperature.
  • High heating temperature in pretreatment allows for a lower heating temperature later in the drying/curing unit.
  • the heating should not be too severe that it affects the quality of the coating (e.g. adherence, evenness, blistering etc.).
  • it is preferable that the conductor not be heated above about 140° C., more preferably no more than about 120° C.
  • FIGS. 7-9 show a depiction of an annular shaped flooded die 200 .
  • the coating suspension is fed to the die 200 via a tube 206 .
  • the coating suspension coats the conductor 112 via opening ports in the inner surface 202 of the die 200 .
  • the flooded die 200 contains one or more, preferably two or more, more preferably four, opening ports evenly spaced around the circumference of the inner surface 202 .
  • the conductor 112 exits the flooded die, it then passes through another air wipe to remove excess coating suspension and to spread the coating evenly around the conductor.
  • the air wipe allows the coating to penetrate the grooves between the strands on the surface of the conductor. This air wipe preferably operates at the same condition as that for the air wipe in the pretreatment unit 104 .
  • the drying/curing can be accomplished by air or by using hot air of the temperature of up to 1000° C. and/or the line speed of between about 9 feet/min to about 500 feet/min, preferably about 10 feet/min to about 400 feet/min, depending on the metal alloy used in the conductor.
  • the drying process may be gradual drying, rapid drying, or direct flame application.
  • the drying or curing also can be accomplished by other techniques, like a heating oven, UV, IR, E-beam, chemical, or liquid spray and the like.
  • the drying can be accomplished by single or multiple units. It also can be vertical or horizontal or at a specific angle.
  • the drying/curing occurs by direct flame application.
  • the cable preferably passes directly through a flame to heat the cable surface to a temperature of up to about 300° C., preferably up to about 150° C.
  • the continuous process if operated for an individual strand (instead of the whole cable), preferably operates at a line speed of up to about 2500 ft/min, preferably about 9 to about 2000 ft/min, more preferably about 10 to about 500 ft/min, most preferably about 30 to about 300 ft/min.
  • the overhead conductor coating of the present invention can be used in composite core conductor designs.
  • Composite core conductors are used due to their lower sag at higher operating temperatures and higher strength to weight ratio. Reduced conductor operating temperatures due to the coating can further lower sag of the conductors and lower degradation of polymer resin in the composite. Examples for composite cores can be found, e.g., in U.S. Pat. Nos. 7,015,395, 7,438,971, and 7,752,754, which are incorporated herein by reference.
  • the coated conductor exhibits improved heat dissipation.
  • Emissivity is the relative power of a surface to emit heat by radiation, and the ratio of the radiant energy emitted by a surface to the radiant energy emitted by a blackbody at the same temperature.
  • Emittance is the energy radiated by the surface of a body per unit area. Emissivity can be measured, for example, by the method disclosed in U.S. Patent Application Publication No. 2010/0076719 to Lawry et al., which is incorporated herein by reference.
  • Exp 1 contains dry admixture of 13-15% sodium silicate, 68-69% silicon dioxide powder, 14-16% boron carbide, and 1-1.5% bentonite powder.
  • Exp 2 contains 13-15% sodium silicate, 68-69% silicon dioxide powder, 13-15% boron carbide, 1-2% boron nitride, and 1-1.5% bentonite powder.
  • Exp 3-7 contains B4C dry powder weight 12-17%, SiO2 dry powder weight 60-70%, Poly-silicate powder dry weight basis 15-20%, DI water on a wet weight basis of 20-25%.
  • the total solids content is approximately 50%.
  • Exp 8-11 are consists of B4C dry powder weight of 10-15%, TiO2 powder dry weight of 7-13%, diatomaceous earth powder dry weight of 1-5%, acrylic polymer dry weight 30-40% and DI water on a wet weight basis of 30-50%.
  • the total solids content is approximately 50%.
  • compositions are coated on sample substrates and cured.
  • the final thickness of the coating is approximately 1 mil.
  • the coated substrates are then tested for temperature reduction.
  • a current is applied through the metal substrate with a 1 mil coating thickness and an uncoated metal substrate to measure the performance improvement of the coating.
  • the test apparatus is shown in FIG. 5 and mainly consisted of a 60 Hz ac current source, a true RMS clamp-on current meter, a temperature datalog device and a timer. Testing was conducted within a 68′′ wide ⁇ 33′′ deep windowed safety enclosure to control air movement around the sample. An exhaust hood was located 64′′ above the test apparatus for ventilation.
  • the sample to be tested was connected in series with an ac current source through a relay contact controlled by a timer.
  • the timer was used to activate the current source and controlled the time duration of the test.
  • the 60 Hz ac current flowing through the sample was monitored by a true RMS clamp-on current meter.
  • a thermocouple was used to measure the surface temperature of the sample. Using a spring clamp, the tip of the thermocouple was kept firmly in contacted with the center surface of the sample. In case of measurement on coated sample, the coating was removed at the area where thermocouple made the contact with the sample to get accurate measurement of the temperature of the substrate.
  • the thermocouple temperature was monitored by a datalog recording device to provide a continuous record of temperature change.
  • Both coated cable samples were tested for temperature rise on this test set-up under identical experimental conditions.
  • the current was set at a desired level and was monitored during the test to ensure a constant current is flowing through the samples.
  • the timer was set at a desired value and the temperature datalog recording device was set to record temperature at a recording interval of one reading per second.
  • the metal component for the uncoated and coated samples was from the same source material and lot of Aluminum 1350 .
  • the finished dimensions of the uncoated sample were 12.0′′(L) ⁇ 0.50′′(W) ⁇ 0.027′′(T).
  • the finished dimensions of the coated samples were 12.0′′(L) ⁇ 0.50′′(W) ⁇ 0.029′′(T).
  • the increase in thickness and width was due to the thickness of the applied coating.
  • the temperature test data was then accessed from the datalog device and analyzed using a computer.
  • the temperature (measured in ° C.) of the coated samples as compared to uncoated sample are reported as % reduction relative to uncoated sample are shown in Tables 1 and 2.
  • Heat aging performance of the coating was carried out by placing the coated samples in an air circulating oven maintained at 325° C. for a period of 1 day and 7 days. After the heat aging was complete, the samples were placed at room temperature of 21° C. for a period of 24 hours. The samples were then bent on different cylindrical mandrels sized from higher diameter to lower diameter and the coatings were observed for any visible cracks at each of the mandrel size. The samples are bent on mandrels of diameters of 10 inches and less. The samples are reported “Pass” at the smallest mandrel size where no visible cracks are visible. The file hardness test was performed by running a series of files of known hardness over the coating. If coating is not removed by the file, then that coating is harder than the file.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Paints Or Removers (AREA)
  • Organic Insulating Materials (AREA)
  • Chemical & Material Sciences (AREA)
  • Insulated Conductors (AREA)
  • Ceramic Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Adhesives Or Adhesive Processes (AREA)
US14/051,080 2013-10-10 2013-10-10 Coated overhead conductor Abandoned US20150104641A1 (en)

Priority Applications (11)

Application Number Priority Date Filing Date Title
US14/051,080 US20150104641A1 (en) 2013-10-10 2013-10-10 Coated overhead conductor
TW102138287A TW201515026A (zh) 2013-10-10 2013-10-23 經塗敷之架空導體
ARP130103862A AR093122A1 (es) 2013-10-10 2013-10-24 Conductor aereo recubierto y metodo para hacerlo
ES13895379T ES2739040T3 (es) 2013-10-10 2013-11-14 Conductor aéreo recubierto
BR112016007986-8A BR112016007986B1 (pt) 2013-10-10 2013-11-14 Método de formação de um condutor suspenso que tem uma temperatura operacional mais baixa
CN201380081526.0A CN105814648A (zh) 2013-10-10 2013-11-14 经涂覆的架空导线
PCT/US2013/070154 WO2015053796A1 (en) 2013-10-10 2013-11-14 Coated overhead conductor
EP13895379.9A EP3055868B1 (en) 2013-10-10 2013-11-14 Coated overhead conductor
MX2016004379A MX2016004379A (es) 2013-10-10 2013-11-14 Conductor aereo revestido.
CA2925856A CA2925856C (en) 2013-10-10 2013-11-14 Coated overhead conductor
US15/230,194 US10332658B2 (en) 2013-10-10 2016-08-05 Method of forming a coated overhead conductor

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US14/051,080 US20150104641A1 (en) 2013-10-10 2013-10-10 Coated overhead conductor

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/230,194 Continuation US10332658B2 (en) 2013-10-10 2016-08-05 Method of forming a coated overhead conductor

Publications (1)

Publication Number Publication Date
US20150104641A1 true US20150104641A1 (en) 2015-04-16

Family

ID=52809927

Family Applications (2)

Application Number Title Priority Date Filing Date
US14/051,080 Abandoned US20150104641A1 (en) 2013-10-10 2013-10-10 Coated overhead conductor
US15/230,194 Active 2033-11-19 US10332658B2 (en) 2013-10-10 2016-08-05 Method of forming a coated overhead conductor

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/230,194 Active 2033-11-19 US10332658B2 (en) 2013-10-10 2016-08-05 Method of forming a coated overhead conductor

Country Status (10)

Country Link
US (2) US20150104641A1 (zh)
EP (1) EP3055868B1 (zh)
CN (1) CN105814648A (zh)
AR (1) AR093122A1 (zh)
BR (1) BR112016007986B1 (zh)
CA (1) CA2925856C (zh)
ES (1) ES2739040T3 (zh)
MX (1) MX2016004379A (zh)
TW (1) TW201515026A (zh)
WO (1) WO2015053796A1 (zh)

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170148548A1 (en) * 2014-08-07 2017-05-25 Henkel Ag & Co., Kgaa Electroceramic coating of a wire for use in a bundled power transmission cable
US20170162290A1 (en) * 2014-08-05 2017-06-08 Mee Investment Scandinavia Ab Electrical wire
US20180211746A1 (en) * 2015-07-21 2018-07-26 General Cable Technologies Corporation Electrical accessories for power transmission systems and methods for preparing such electrical accessories
US10319488B2 (en) * 2015-08-19 2019-06-11 Nkt Hv Cables Gmbh Conductor for a power transmission cable and a process for the production of the conductor
US10370514B2 (en) 2014-06-23 2019-08-06 Southwire Company, Llc UV-resistant superhydrophobic coating compositions
US10586633B2 (en) 2012-08-10 2020-03-10 General Cable Technologies Corporation Surface modified overhead conductor
WO2020053559A1 (en) * 2018-09-10 2020-03-19 Cable Coatings Limited Overhead conductor with self-cleaning coating
EP3529324A4 (en) * 2016-10-20 2020-06-10 General Cable Technologies Corporation SUSTAINABLE COATING COMPOSITIONS AND COATINGS FORMED THEREFROM
US10889727B1 (en) 2018-06-14 2021-01-12 Southwire Company, Llc Electrical cable with improved installation and durability performance
US10957468B2 (en) 2013-02-26 2021-03-23 General Cable Technologies Corporation Coated overhead conductors and methods
US11746250B2 (en) 2016-05-04 2023-09-05 General Cable Technologies Corporation Compositions and coatings formed thereof with reduced ice adherence and accumulation
US11854721B2 (en) 2022-03-28 2023-12-26 Ts Conductor Corp. Composite conductors including radiative and/or hard coatings and methods of manufacture thereof
WO2024013065A1 (fr) * 2022-07-12 2024-01-18 Centre National De La Recherche Scientifique Utilisation d'une fibre optique comprenant un revetement a base de nitrure de bore dans un procede de fabrication additive de structures ceramiques
WO2024013066A1 (fr) * 2022-07-12 2024-01-18 Centre National De La Recherche Scientifique Enduction d'une fibre notamment optique par un revetement a base de nitrure de bore
CN117524604A (zh) * 2023-11-22 2024-02-06 正泰交联电缆有限公司 一种防止聚氯乙烯护套烘干软化的电缆外护套去水装置

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3079961B1 (fr) 2018-04-05 2022-05-27 Nexans Accessoire pour cable a conductivite thermique amelioree
CN109637715A (zh) * 2019-01-16 2019-04-16 京仪股份有限公司 一种抗弯曲散热金包铜合金电缆及其制造工艺
CN110387129A (zh) * 2019-06-17 2019-10-29 东莞市明盛电气有限公司 一种硅橡胶电线生产方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5391606A (en) * 1992-07-02 1995-02-21 Nalco Chemical Company Emissive coatings for investment casting molds
WO2005005680A2 (en) * 2003-05-06 2005-01-20 Wessex Incorporated Thermal protective coating
WO2007034248A1 (en) * 2005-09-23 2007-03-29 Zdenko Simic Overhead conductor with spectrally selective surface

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2699425A (en) * 1952-07-05 1955-01-11 Motorola Inc Electroplating electrical conductors on an insulating panel
US3404031A (en) * 1963-09-03 1968-10-01 Boeing Co Emissive coating
US4588546A (en) * 1984-08-27 1986-05-13 The Goodyear Tire & Rubber Company Wire coating process
JPS6234778A (ja) * 1985-08-06 1987-02-14 Niigata Eng Co Ltd サンドブラストによる物体の加工方法
DE3824608C1 (en) * 1988-07-20 1989-08-17 Berndorf F.A.S. Freileitungen Und Aluminium Sonderprodukte Ges.M.B.H., Berndorf, At Method of equipping an overhead-line conductor for a high-voltage overhead line with a black surface layer
US5296288A (en) 1992-04-09 1994-03-22 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Protective coating for ceramic materials
EP0729158B1 (en) * 1995-02-24 2003-04-09 Sumitomo Wiring Systems, Ltd. Radiation wire
US5668072A (en) 1996-05-09 1997-09-16 Equity Enterprises High emissivity coating
DE19731625A1 (de) * 1997-03-04 1998-09-10 Volkswagen Ag Lagerwerkstoff in einem Pleuelauge
DK1124235T3 (da) 2000-02-08 2009-02-16 Gift Technologies Llc Kompositforstærket elektrisk transmissionsleder
US6921431B2 (en) 2003-09-09 2005-07-26 Wessex Incorporated Thermal protective coating for ceramic surfaces
US7438971B2 (en) 2003-10-22 2008-10-21 Ctc Cable Corporation Aluminum conductor composite core reinforced cable and method of manufacture
US20060015695A1 (en) * 2004-06-30 2006-01-19 Cochran Robert A Method of device mirroring via packetized networking infrastructure
CN200979826Y (zh) * 2006-11-30 2007-11-21 张安 电力电缆线芯包漆模具
US9011791B2 (en) 2008-04-07 2015-04-21 Emisshield, Inc. Pyrolysis furnace and process tubes
US8510075B2 (en) 2008-09-24 2013-08-13 Electric Power Research Institute, Inc. Emmissivity test instrument for overhead electrical transmission and distribution
TWI391668B (zh) 2008-11-21 2013-04-01 King Yuan Electronics Co Ltd 具有高耐電流能力之電連接導體與提高電連接導體之耐電流能力的方法
RU2386183C1 (ru) 2008-12-04 2010-04-10 Дмитрий Григорьевич Сильченков Композиционный несущий сердечник для внешних токоведущих жил проводов воздушных высоковольтных линий электропередачи и способ его производства
CN101572137B (zh) * 2009-06-05 2011-01-05 江苏中超电缆股份有限公司 电缆三层共挤交联生产线的出线润滑系统
CN201773611U (zh) * 2010-07-29 2011-03-23 上海德力西集团有限公司 易于散热的电线
US8840942B2 (en) 2010-09-24 2014-09-23 Emisshield, Inc. Food product and method and apparatus for baking
TW201220451A (en) 2010-11-08 2012-05-16 Yuh Cheng Materials Co Ltd characterized by using plasma to clean the core surface prior to coating a plating on the core
FR2971617B1 (fr) 2011-02-10 2013-02-01 Nexans Cable electrique aerien a vieillissement ameliore
CN202741376U (zh) * 2012-07-31 2013-02-20 盈锋紧固系统（无锡）有限公司 用于硬盘螺丝生产的清洗装置
US9859038B2 (en) * 2012-08-10 2018-01-02 General Cable Technologies Corporation Surface modified overhead conductor

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5391606A (en) * 1992-07-02 1995-02-21 Nalco Chemical Company Emissive coatings for investment casting molds
WO2005005680A2 (en) * 2003-05-06 2005-01-20 Wessex Incorporated Thermal protective coating
WO2007034248A1 (en) * 2005-09-23 2007-03-29 Zdenko Simic Overhead conductor with spectrally selective surface

Cited By (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10586633B2 (en) 2012-08-10 2020-03-10 General Cable Technologies Corporation Surface modified overhead conductor
US10957468B2 (en) 2013-02-26 2021-03-23 General Cable Technologies Corporation Coated overhead conductors and methods
US10370514B2 (en) 2014-06-23 2019-08-06 Southwire Company, Llc UV-resistant superhydrophobic coating compositions
US11001696B2 (en) 2014-06-23 2021-05-11 Southwire Company, Llc UV-resistant superhydrophobic coating compositions
US20170162290A1 (en) * 2014-08-05 2017-06-08 Mee Investment Scandinavia Ab Electrical wire
US9953737B2 (en) * 2014-08-05 2018-04-24 Mee Investment Scandinavia Ab Electrical wire with a central aluminum wire surrounded by at least one copper wire
US9953747B2 (en) * 2014-08-07 2018-04-24 Henkel Ag & Co. Kgaa Electroceramic coating of a wire for use in a bundled power transmission cable
US20170148548A1 (en) * 2014-08-07 2017-05-25 Henkel Ag & Co., Kgaa Electroceramic coating of a wire for use in a bundled power transmission cable
US10726975B2 (en) * 2015-07-21 2020-07-28 General Cable Technologies Corporation Electrical accessories for power transmission systems and methods for preparing such electrical accessories
US20180211746A1 (en) * 2015-07-21 2018-07-26 General Cable Technologies Corporation Electrical accessories for power transmission systems and methods for preparing such electrical accessories
EP3326176A4 (en) * 2015-07-21 2019-01-23 General Cable Technologies Corporation ELECTRICAL ACCESSORIES FOR ENERGY TRANSMISSION SYSTEMS AND METHODS FOR PREPARING THESE ELECTRICAL ACCESSORIES
US10319488B2 (en) * 2015-08-19 2019-06-11 Nkt Hv Cables Gmbh Conductor for a power transmission cable and a process for the production of the conductor
US11746250B2 (en) 2016-05-04 2023-09-05 General Cable Technologies Corporation Compositions and coatings formed thereof with reduced ice adherence and accumulation
US10836914B2 (en) 2016-10-20 2020-11-17 General Cable Technologies Corporation Durable coating compositions and coatings formed thereof
EP3529324A4 (en) * 2016-10-20 2020-06-10 General Cable Technologies Corporation SUSTAINABLE COATING COMPOSITIONS AND COATINGS FORMED THEREFROM
US10889727B1 (en) 2018-06-14 2021-01-12 Southwire Company, Llc Electrical cable with improved installation and durability performance
US11174398B2 (en) * 2018-09-10 2021-11-16 Cable Coatings Limited Overhead conductor with self-cleaning coating
WO2020053559A1 (en) * 2018-09-10 2020-03-19 Cable Coatings Limited Overhead conductor with self-cleaning coating
US11854721B2 (en) 2022-03-28 2023-12-26 Ts Conductor Corp. Composite conductors including radiative and/or hard coatings and methods of manufacture thereof
WO2024013065A1 (fr) * 2022-07-12 2024-01-18 Centre National De La Recherche Scientifique Utilisation d'une fibre optique comprenant un revetement a base de nitrure de bore dans un procede de fabrication additive de structures ceramiques
WO2024013066A1 (fr) * 2022-07-12 2024-01-18 Centre National De La Recherche Scientifique Enduction d'une fibre notamment optique par un revetement a base de nitrure de bore
FR3137911A1 (fr) * 2022-07-12 2024-01-19 Centre National De La Recherche Scientifique Enduction d’une fibre notamment optique par un revetement a base de nitrure de bore.
FR3137912A1 (fr) * 2022-07-12 2024-01-19 Centre National De La Recherche Scientifique Utilisation d’une fibre optique comprenant un revetement a base de nitrure de bore dans un procede de fabrication additive de structures ceramiques.
CN117524604A (zh) * 2023-11-22 2024-02-06 正泰交联电缆有限公司 一种防止聚氯乙烯护套烘干软化的电缆外护套去水装置

Also Published As

Publication number Publication date
CA2925856A1 (en) 2015-04-16
ES2739040T3 (es) 2020-01-28
CA2925856C (en) 2021-02-23
AR093122A1 (es) 2015-05-20
BR112016007986A8 (pt) 2020-03-17
EP3055868A4 (en) 2017-05-17
EP3055868B1 (en) 2019-05-08
EP3055868A1 (en) 2016-08-17
CN105814648A (zh) 2016-07-27
MX2016004379A (es) 2016-08-19
US20160343476A1 (en) 2016-11-24
BR112016007986B1 (pt) 2021-06-15
TW201515026A (zh) 2015-04-16
WO2015053796A1 (en) 2015-04-16
US10332658B2 (en) 2019-06-25

Similar Documents

Publication Publication Date Title
US10332658B2 (en) Method of forming a coated overhead conductor
US10586633B2 (en) Surface modified overhead conductor
US9328245B2 (en) Curable two-part coatings for conductors
US20180025809A1 (en) Electrical accessories for power transmission systems and methods for preparing such electrical accessories
US10726975B2 (en) Electrical accessories for power transmission systems and methods for preparing such electrical accessories

Legal Events

Date Code Title Description
AS Assignment

Owner name: GENERAL CABLE TECHNOLOGIES CORPORATION, KENTUCKY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MHETAR, VIJAY;DAVIS, CODY;RANGANATHAN, SATHISH KUMAR;SIGNING DATES FROM 20131017 TO 20131028;REEL/FRAME:031658/0745

AS Assignment

Owner name: EMISSHIELD, INC., VIRGINIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:OLVER, JOHN;DILLARD, JOHN;REEL/FRAME:035750/0100

Effective date: 20131121

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION