US20140338824A1 - Apparatus and method for manufacturing composite membrane - Google Patents
Apparatus and method for manufacturing composite membrane Download PDFInfo
- Publication number
- US20140338824A1 US20140338824A1 US14/280,763 US201414280763A US2014338824A1 US 20140338824 A1 US20140338824 A1 US 20140338824A1 US 201414280763 A US201414280763 A US 201414280763A US 2014338824 A1 US2014338824 A1 US 2014338824A1
- Authority
- US
- United States
- Prior art keywords
- electrolyte membrane
- roller
- thin film
- suction roller
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An electrolyte membrane with a backsheet is sent out from an electrolyte membrane unwinding roller, and is separated with its second side sucked on a suction roller by a first press roller. While the electrolyte membrane from which the backsheet has been separated is transported with the electrolyte membrane sucked and supported on the suction roller, an electrode ink is applied to a first side of the electrolyte membrane to form an electrode ink layer, which is dried by blowing hot air thereto to form a catalyst layer. Thereafter, in a state in which the outer surface of a second press roller disposed close to the suction roller is in contact with and supported on the first side of the electrolyte membrane, a support film is pressed against the second side of the electrolyte membrane by a third press roller and attached thereto to manufacture a catalyst-coated membrane.
Description
- 1. Field of the Invention
- The present invention relates to an apparatus and a method for manufacturing a composite membrane, such as a catalyst-coated membrane for a fuel cell, having a functional layer formed on a band-like thin film.
- 2. Description of the Background Art
- In recent years, fuel cells have been garnering attention as drive power sources for automobiles, household uses, mobile phones and the like. A fuel cell is a power generation system that generates electric power through electrochemical reaction between hydrogen (H2) contained in the fuel and oxygen (O2) in the air, and is characterized by high power generation efficiency and low environmental load.
- There are several types of fuel cells that vary according to the electrolytes used. One of them is a polymer electrolyte fuel cell (PEFC) that uses an ion-exchange membrane (electrolyte membrane) as the electrolyte. PEFCs are capable of operating at room temperature and can be reduced in size and weight, and therefore, they are expected to be applied to automobiles and portable devices.
- A catalyst-coated membrane (CCM) used for a polymer electrolyte fuel cell is a composite membrane having catalyst layers formed on both sides of a thin film of an electrolyte as functional layers. A gas diffusion layer and a separator are disposed on the opposite sides of the catalyst-coated membrane, and thereby, a unit cell is formed. Such a catalyst-coated membrane is made by applying, to the surface of the electrolyte membrane, an electrode ink (electrode paste) obtained by dispersing a catalyst containing platinum (Pt) in a solvent such as alcohol. However, the electrolyte membrane has the tendency of undergoing swelling and shrinkage by easily absorbing the solvent contained in the electrode ink and moisture in the atmosphere. This has posed a problem in that creases and pinholes are generated in the electrolyte membrane at the time of applying and drying the electrode ink. Generation of creases and pinholes in the electrolyte membrane leads to a reduction in the power generation performance of the fuel cell.
- To solve such a problem, Japanese Patent Application Laid-Open-No. 2001-70863 discloses a technique for transporting an electrolyte membrane while sucking the electrolyte membrane using a suction heating roller, and immediately heating and drying the electrode ink applied to the electrolyte membrane, thereby inhibiting deformation of the electrolyte membrane. Additionally, US2007/0190253 discloses a technique for spray applying an electrode ink to an electrolyte membrane that is sucked on a roller, and drying the electrode ink by heating with a roller. Furthermore, Japanese Patent Application Laid-Open No. 2011-165460 discloses suspending an electrolyte membrane having a shape-retaining film attached to its one side on a backup roller, applying a catalyst ink onto the other side of the electrolyte membrane, and also attaching a shape-retaining film to the other side of the electrolyte membrane on which a catalyst layer has been formed after the catalyst ink was dried, thereby preventing creases from being generated in the electrolyte membrane.
- However, with the techniques disclosed in Japanese Patent Application Laid-Open No. 2001-70863 and US2007/0190253, the electrode ink is applied, with the electrolyte membrane being sucked by the roller. Accordingly, although it is possible to prevent deformation due to swelling of the electrolyte membrane during coating, there is the possibility that the electrolyte membrane may undergo swelling and shrinkage caused by the absorption of the solvent of the electrode ink and the drying of the ink when the electrolyte membrane is separated from the roller after coating. Moreover, with the technique disclosed in Japanese Patent Application Laid-Open No. 2011-165460, the electrolyte membrane is simply suspended on the backup roller, and therefore, there is the possibility that the electrolyte membrane may be displaced from the shape-retaining film during coating in the case of applying an electrode ink using a solvent that undergoes a significant degree of swelling. That is, in any case, there is the possibility that the electrolyte membrane may undergo deformation during manufacture of the catalyst-coated membrane.
- The present invention is directed to an apparatus for manufacturing a composite membrane having a functional layer formed on a band-like thin film.
- According to one aspect of the present invention, the manufacturing apparatus includes a suction roller that sucks and supports the thin film on an outer surface thereof, a coating part that applies a coating liquid to one side of the thin film that is transported while being sucked and supported on the suction roller, a drying part that is provided to cover a portion of the outer surface of the suction roller and dries the coating liquid applied to the one side of the thin film to form the functional layer, and an attachment part that attaches a band-shaped first supporting member to another side of the thin film on which the functional layer is formed, the attachment part including a first roller that comes into contact with the one side of the thin film and supports the thin film while being in contact with or close to the suction roller, and being configured to attach the first supporting member to the other side of the thin film with the one side of the thin film being in contact with and supported on an outer surface of the first roller.
- During and after the application of the coating liquid, the thin film is continuously supported by the suction roller, the first roller, and the first supporting member, and it is thus possible to inhibit deformation of the thin film throughout transport during and after coating.
- Preferably, the manufacturing apparatus further includes a separation part that separates a band-shaped second supporting member from the thin film having the second supporting member attached to the one side thereof, the separation part including a third roller that separates the second supporting member with the other side of the thin film being sucked on the suction roller.
- This makes possible to inhibit deformation of the thin film throughout a series of steps of manufacturing a composite membrane.
- Preferably, the drying part is divided into a plurality of drying zones, and drying temperatures of the plurality of drying zones sequentially increase in order from an upstream side toward a downstream side in a transport direction in which the thin film is transported.
- The applied coating liquid is gradually dried, making it possible to prevent the occurrence of cracking in the functional layer due to rapid drying.
- Preferably, the drying part includes a heat-shielding zone on at least the most upstream side in the transport direction.
- This makes it possible to prevent coating failure due to leakage of heated atmosphere.
- Preferably, the manufacturing apparatus further includes an auxiliary drying part that heats the thin film to which the first supporting member is attached by the attachment part.
- This makes it possible to sufficiently dry the coating liquid.
- Preferably, the manufacturing apparatus further includes a cooling part that cools the suction roller.
- This makes it possible to prevent the suction roller from storing heat, thus preventing the coating liquid from being rapidly dried during coating.
- The present invention is also directed to a method for manufacturing a composite membrane having a functional layer formed on a band-like thin film.
- According to one aspect of the present invention, the manufacturing method includes the steps of (a) sucking and supporting the thin film on an outer surface of a suction roller, (b) applying a coating liquid to one side of the thin film that is transported while being sucked and supported on the suction roller, (c) drying the coating liquid applied to the one side of the thin film to form the functional layer, and (d) attaching a band-shaped first supporting member to another side of said thin film in a state in which the one side of said thin film on which said functional layer is formed is in contact with and supported on an outer surface of a first roller that comes into contact with the one side of said thin film and supports said thin film while being in contact with or close to said suction roller.
- During and after the application of the coating liquid, the thin film is continuously supported by the suction roller, the first roller, and the first supporting member, and it is thus possible to inhibit deformation of the thin film throughout transport during and after coating.
- Preferably, the manufacturing method further includes the step of (e) separating a band-shaped second supporting member from the thin film having the second supporting member attached to the one side thereof.
- This makes it possible to inhibit deformation of the thin film throughout a series of the steps of manufacturing a composite membrane.
- Therefore, it is an object of the present invention to inhibit deformation of a thin film throughout transport during and after coating.
- These and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
-
FIG. 1 is a perspective view showing a schematic overall configuration of a manufacturing apparatus for a composite membrane according to the present invention; -
FIG. 2 is a side view of the manufacturing apparatus ofFIG. 1 ; -
FIG. 3 is a diagram showing a configuration of a suction roller and a drying furnace; -
FIG. 4 is a front view of the suction roller and the drying furnace; -
FIG. 5 is a flowchart illustrating a procedure of manufacturing a catalyst-coated membrane performed by the manufacturing apparatus ofFIG. 1 ; -
FIG. 6 is a diagram showing how a backsheet is separated and an electrolyte membrane is sucked on a suction roller by a first press roller; -
FIG. 7 is a diagram showing a state in which an electrode ink has been intermittently applied to the electrolyte membrane; -
FIG. 8 is a cross-sectional view of the electrolyte membrane having an electrode ink intermittently applied thereto; -
FIG. 9 is a cross-sectional view of the electrolyte membrane having a catalyst layer formed thereon; -
FIG. 10 is a diagram showing how a support film is attached to the electrolyte membrane by a second press roller and a third press roller; -
FIG. 11 is a side view of a manufacturing apparatus for a composite membrane according to a second preferred embodiment; -
FIG. 12 is a cross-sectional view of an electrolyte membrane with a backsheet that has been unwound from an electrolyte membrane unwinding roller in the second preferred embodiment; -
FIG. 13 is a cross-sectional view of the electrolyte membrane having an electrode ink intermittently applied to a side opposite to the side corresponding to the catalyst layer; -
FIG. 14 is a cross-sectional view of the electrolyte membrane having catalyst layers formed on both sides; -
FIG. 15 is a cross-sectional view of the electrolyte membrane having a support film attached thereto. -
FIG. 16 is a side view of a manufacturing apparatus for a composite membrane according to a third preferred embodiment; and -
FIG. 17 is a cross-sectional view of an electrolyte membrane having a support film attached to a second side of an electrolyte membrane having catalyst layers laminated on a first side thereof. - Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the drawings.
-
FIG. 1 is a perspective view showing a schematic overall configuration of amanufacturing apparatus 1 for a composite membrane according to the present invention.FIG. 2 is a side view of themanufacturing apparatus 1 ofFIG. 1 . Themanufacturing apparatus 1 for a composite membrane is an apparatus for manufacturing a catalyst-coatedmembrane 5 for a polymer electrolyte fuel cell by applying an electrode ink (electrode paste) to the surface of anelectrolyte membrane 2, which is a band-like thin film, and drying the electrode ink to form a catalyst layer (electrode) as a functional layer on theelectrolyte membrane 2. To clarify the directional relationship,FIG. 1 and the subsequent drawings each show an XYZ Cartesian coordinate system in which the Z-axis direction is the vertical direction and the XY plane is the horizontal plane. For facilitating the understanding, the dimensions and the numbers of various components are exaggerated or simplified inFIG. 1 and the subsequent drawings. - The
manufacturing apparatus 1 includes, as its main constituent elements, aseparation part 10 that separates abacksheet 6 from theelectrolyte membrane 2, asuction roller 20 that transports theelectrolyte membrane 2 while sucking and supporting theelectrolyte membrane 2, acoating nozzle 30 that applies an electrode ink to a surface of theelectrolyte membrane 2, a dryingfurnace 40 that heats and dries the applied electrode ink, and anattachment part 50 that attaches a support film to theelectrolyte membrane 2 that has undergone the drying step. - The
separation part 10 includes a first press roller 11 (third roller). Themanufacturing apparatus 1 also includes an electrolytemembrane unwinding roller 12, anauxiliary roller 13, and abacksheet winding roller 14. The electrolytemembrane unwinding roller 12, around which theelectrolyte membrane 2 with thebacksheet 6 is wound, continuously sends out theelectrolyte membrane 2 with thebacksheet 6. - As the
electrolyte membrane 2, it is possible to use fluorine-based or hydrocarbon-based polymer electrolyte membranes that have been used thus far in an application to catalyst-coated membranes of polymer electrolyte fuel cells. For example, theelectrolyte membrane 2 may be a polymer electrolyte membrane containing perfluorocarbon sulfonic acid (e.g., Nafion (registered trademark) manufactured by USA DuPont, Flemion (registered trademark) manufactured by Asahi Glass Co. Ltd, Aciplex (registered trademark) manufactured by Asahi Kasei Corporation, and Goreselect (registered trademark) manufactured by Gore). - The
electrolyte membrane 2 described above is very thin and low in mechanical strength. Thus, theelectrolyte membrane 2 has the characteristics of easily swelling even with a small amount of moisture in the air, and also shrinking with decreasing humidity, so that it is highly likely to undergo deformation. For this reason, in the initial state, theelectrolyte membrane 2 with thebacksheet 6 is wound around the electrolytemembrane unwinding roller 12 in order to prevent deformation of theelectrolyte membrane 2. As thebacksheet 6, it is possible to use a film of a resin material having high mechanical strength and an excellent shape-retaining function, such as PEN (polyethylene naphthalate) and PET (polyethylene terephthalate). - The initial-
state electrolyte membrane 2 with thebacksheet 6, which is wound around the electrolytemembrane unwinding roller 12, has a film thickness of 5 to 30 μm and a width of approximately 300 mm at maximum. The film thickness of thebacksheet 6 is 25 to 100 μm, and the width is equal to or slightly greater than the width of theelectrolyte membrane 2. In the first preferred embodiment, thebacksheet 6 is attached to a first side of theelectrolyte membrane 2. - The
electrolyte membrane 2 with thebacksheet 6 that has been sent out from the electrolytemembrane unwinding roller 12 is suspended on theauxiliary roller 13 and is pressed against thesuction roller 20 by thefirst press roller 11. Thefirst press roller 11 is supported by a cylinder (not shown) at a position close to and spaced a predetermined interval from the outer surface of thesuction roller 20. The interval between thefirst press roller 11 and the outer surface of thesuction roller 20 is smaller than the thickness of theelectrolyte membrane 2 with thebacksheet 6. Accordingly, a second side of theelectrolyte membrane 2 is pressed against thesuction roller 20 when theelectrolyte membrane 2 with thebacksheet 6 passes between thefirst press roller 11 and thesuction roller 20. The force with which thefirst press roller 11 presses theelectrolyte membrane 2 with thebacksheet 6 against thesuction roller 20 is controlled by adjusting the interval between thefirst press roller 11 and thesuction roller 20 by the above-described cylinder. - By the
first press roller 11 pressing the second side of theelectrolyte membrane 2 against thesuction roller 20, theelectrolyte membrane 2 is sucked onto the outer surface of thesuction roller 20. At this time, thebacksheet 6 is separated from the first side of theelectrolyte membrane 2 and is wound by thebacksheet winding roller 14. That is, thefirst press roller 11 of theseparation part 10 serves to separate thebacksheet 6 from theelectrolyte membrane 2 with thebacksheet 6 and to cause theelectrolyte membrane 2 to be sucked on thesuction roller 20 by pressing theelectrolyte membrane 2 against thesuction roller 20. Thebacksheet winding roller 14 continuously winds thebacksheet 6 by being continuously rotated by a motor (not shown), and provides a constant tension to theelectrolyte membrane 2 with thebacksheet 6 that is transported from the electrolytemembrane unwinding roller 12 via theauxiliary roller 13 to thefirst press roller 11. - The
suction roller 20 is a columnar member installed such that its central axis extends along the Y-axis direction. The dimensions of thesuction roller 20 are, for example, a height (a length in the Y-axis direction) of 400 mm and a diameter of 400 to 1600 mm. Thesuction roller 20 is rotated in the direction indicated by the arrow AR2 shown inFIG. 2 by a motor (not shown) about the central axis along the Y-axis direction as the center of rotation. - The
suction roller 20 is a porous roller formed of porous carbon or porous ceramics. For example, a sintered body of alumina (Al2O3) or silicon carbide (SiC) can be used as the porous ceramics. The pore diameter of theporous suction roller 20 is 5 μm or less, and the porosity thereof is in the range of 15 to 50%. The surface roughness of the outer surface (column circumferential surface) of thesuction roller 20 is 5 μm or less in terms of Rz (maximum height), and this value is preferably as small as possible. Additionally, the total runout (fluctuations in the distance from the rotational shaft to the outer surface) of thesuction roller 20 during rotation is set to 10 μm or less. -
FIG. 3 is a diagram showing a configuration of thesuction roller 20 and the dryingfurnace 40. The top surface and/or bottom surface of thesuction roller 20 is provided with asuction port 21. Thesuction port 21 is sucked by a suction mechanism (e.g., an exhaust pump), which is not shown, and thereby, a negative pressure is applied thereto. Thesuction roller 20 is porous with a porosity of 15 to 50%. Thus, when a negative pressure is applied to thesuction port 21, a negative pressure of a predetermined value (the pressure for suction from the surrounding atmosphere to the outer surface) uniformly acts on the outer surface of thesuction roller 20 through the internal pores. For example, in the present embodiment, a negative pressure of 90 kPa or more is applied to thesuction port 21, causing a negative pressure of 10 kPa or more to uniformly act on the outer surface of thesuction roller 20. This enables thesuction roller 20 to uniformly suck theelectrolyte membrane 2 along the entire width (in the Y-axis direction). - The
suction roller 20 is also provided with a plurality of water-cooledtubes 22. The water-cooledtubes 22 are provided in a uniform arrangement density so as to circulate inside thesuction roller 20. The water-cooledtubes 22 are supplied with constant-temperature water adjusted to a predetermined temperature from a water supply mechanism (not shown). The constant-temperature water that has flowed through the inside of the water-cooledtubes 22 is discharged to a drainage mechanism (not shown). By passing the constant-temperature water through the water-cooledtubes 22, thesuction roller 20 is cooled. - Referring back to
FIGS. 1 and 2 , acoating nozzle 30 is provided so as to oppose the outer surface of thesuction roller 20. Thecoating nozzle 30 is provided on the downstream side of thefirst press roller 11 in the transport direction of theelectrolyte membrane 2 by thesuction roller 20. Thecoating nozzle 30 is a slit nozzle that includes a slit-shaped discharge port at its end (the end on the +X side). The longitudinal direction of the slit-shaped discharge port is the Y-axis direction. Thecoating nozzle 30 is provided at a position where the slit-shaped discharge port is at a predetermined interval from the outer surface of thesuction roller 20. Additionally, thecoating nozzle 30 is provided such that its position and orientation relative to thesuction roller 20 can be adjusted by a drive mechanism (not shown). - An electrode ink is supplied as a coating liquid from a coating
liquid supply mechanism 35 to thecoating nozzle 30. The electrode ink used in the present embodiment contains, for example, catalyst particles, an ion-conducting electrolyte, and a dispersion medium. The catalyst particles may be any known or commercially available catalyst particles without any particular limitations, as long as they can cause a fuel cell reaction in the anode or cathode of a polymer electrolyte fuel cell. For example, it is possible to use platinum (Pt), a platinum alloy, a platinum compound, and the like. Among them, examples of the platinum alloy include alloys of platinum with at least one selected from the group consisting of ruthenium (Ru), palladium (Pd), nickel (Ni), molybdenum (Mo), iridium (Ir), and iron (Fe), for example. In general, platinum is used as the catalyst particles for the cathode electrode ink, and any of the above-described platinum alloys is used as the catalyst particles for the anode electrode ink. - Alternatively, the catalyst particles may be so-called catalyst-supporting carbon powder in which catalyst fine particles are supported on carbon powder. The average particle diameter of the catalyst-supporting carbon is usually about 10 to 100 nm, preferably about 20 to 80 nm, most preferably about 40 to 50 nm. There is no particular limitation on the carbon powder that supports the catalyst fine particles, and examples thereof include carbon blacks such as channel black, furnace black, ketjen black, acetylene black, and lamp black, graphite, activated carbon, carbon fiber, and carbon nanotube. They may be used alone or in combination of two or more.
- A solvent is added to the above-described catalyst particles to form a paste that can be applied from the slit nozzle. As the solvent, it is possible to use water or organic solvents including, for example, alcohol-based solvents such as ethanol, n-propanol and n-butanol, ether-based solvents, ester-based solvents, and fluorine-based solvents.
- A polyelectrolyte solution having an ion-exchange group is further added to a solution obtained by dispersing the catalyst particles in the solvent. As an example, an electrode ink can be obtained by dispersing carbon black that supports 50 wt % of platinum (“TEC10E50E” manufactured by TANAKA KIKINZOKU KOGYO K.K.) in a solution of water, ethanol, propylene glycol, and polyelectrolyte (a Nafion liquid “D2020” manufactured by USA DuPont). The resultant paste mixture is supplied as an electrode ink from the coating
liquid supply mechanism 35 to thecoating nozzle 30. - The coating
liquid supply mechanism 35 includes a tank for storing the above-described electrode ink, a supply tube that openly connects the tank with thecoating nozzle 30, and an open/close valve provided to the supply tube. The coatingliquid supply mechanism 35 can continuously supply the electrode ink to thecoating nozzle 30 by keeping the open/close valve open, or can intermittently supply the electrode ink to thecoating nozzle 30 by repeatedly opening and closing the open/close valve. - The electrode ink supplied from the coating
liquid supply mechanism 35 is applied from thecoating nozzle 30 to the first side of theelectrolyte membrane 2 that is transported while being sucked and supported on thesuction roller 20. The electrode ink is continuously applied to theelectrolyte membrane 2 when the coatingliquid supply mechanism 35 continuously supplies the electrode ink, and the electrode ink is intermittently applied to theelectrolyte membrane 2 when the electrode ink is intermittently supplied. - The drying
furnace 40 is provided so as to cover a portion of the outer surface of thesuction roller 20. As shown inFIG. 3 , the dryingfurnace 40 is divided into a total of five zones, including three dryingzones zones zones suction roller 20 by using a hot air blast from a hot-air blowing part (not shown). The blast of hot air from the dryingfurnace 40 dries the electrode ink applied to the first side of theelectrolyte membrane 2. - The three drying
zones zones electrolyte membrane 2 by the suction roller 20 (clockwise on the plane ofFIG. 3 ). For example, the hot air temperature of the dryingzone 41 on the most upstream side is in the range of room temperature to 40° C., the hot air temperature of theintermediate drying zone 42 is in the range of 40 to 80° C., and the hot air temperature of the dryingzone 43 on the most downstream is in the range of 50 to 100° C. - The two heat-shielding
zones zone electrolyte membrane 2. The heat-shieldingzone 44 is provided on the upstream side of the dryingzone 41, and the heat-shieldingzone 45 is provided on the downstream side of the dryingzone 43. The two heat-shieldingzones suction roller 20 by using the exhaust gas from an air exhaust part (not shown). This can prevent the hot air blown out from the dryingzones furnace 40 to the upstream and downstream sides of thesuction roller 20 and can also prevent the solvent vapor or the like generated from the electrode ink during drying from leaking out of the dryingfurnace 40. Note that if there is at least the heat-shieldingzone 44 on the upstream side, it is possible to prevent the occurrence of coating failure caused by a hot air blast from the dryingzones coating nozzle 30 and drying the area in the vicinity of the discharge port. -
FIG. 4 is a front view of thesuction roller 20 and the dryingfurnace 40. The dryingfurnace 40 is also provided withsuction parts suction roller 20. As with the heat-shieldingzones suction parts furnace 40 in the width direction. - Referring back to
FIGS. 1 and 2 , anattachment part 50 is provided on the downstream side of the dryingfurnace 40 in the transport direction of theelectrolyte membrane 2 by thesuction roller 20. Theattachment part 50 includes a second press roller 51 (first roller) and a third press roller 52 (second roller). Thesecond press roller 51 is supported by a cylinder (not shown) at a position that is close to and spaced a predetermined interval from the outer surface of thesuction roller 20. The interval between thesecond press roller 51 and the outer surface of thesuction roller 20 is smaller than the thickness of theelectrolyte membrane 2 that has undergone the dry process (the total thickness of theelectrolyte membrane 2 and the catalyst layer). Accordingly, the first side of theelectrolyte membrane 2 that includes the catalyst layer is pressed against thesecond press roller 51 when theelectrolyte membrane 2 that has undergone the dry process passes between thesecond press roller 51 and thesuction roller 20. - The
third press roller 52 is supported by a cylinder (not shown) at a position that is close to and spaced a predetermined interval from thesecond press roller 51. The interval between thethird press roller 52 and thesecond press roller 51 is smaller than a value obtained by adding the thickness of thesupport film 7, which will be described later, to the total thickness of theelectrolyte membrane 2 and the catalyst layer. Note that thefirst press roller 11, thesecond press roller 51, and thethird press roller 52 each may be a metal roller or a resin roller having about the same width as that of thesuction roller 20. The diameters of thefirst press roller 11, thesecond press roller 51, and thethird press roller 52 may be set as appropriate. - The
manufacturing apparatus 1 is further provided with a supportfilm unwinding roller 55 and a membraneassembly winding roller 56. The supportfilm unwinding roller 55 has thesupport film 7 wound therearound, and continuously sends out thatsupport film 7. As thesupport film 7, it is possible to use a resin film having high mechanical strength and an excellent shape-retaining function such as a PEN (polyethylene naphthalate) film and a PET (polyethylene terephthalate) film. In other words, thesupport film 7 may be the same as thebacksheet 6, and thebacksheet 6 that has been separated by theseparation part 10 and wound by thebacksheet winding roller 14 may be sent out as thesupport film 7 from the supportfilm unwinding roller 55. Alternatively, thesupport film 7 may be a one-side slightly self-adhesive film obtained by applying an adhesive to one side (the side attached to the electrolyte membrane 2) of the above resin film. - The
support film 7 that has been sent out from the supportfilm unwinding roller 55 is suspended on thethird press roller 52. Meanwhile, theelectrolyte membrane 2 having the catalyst layer formed thereon after the dry process is separated from thesuction roller 20 by thesecond press roller 51 and suspended on thesecond press roller 51. Then, thesupport film 7 is pressed against and attached to the second side of theelectrolyte membrane 2 by thesecond press roller 51 and thethird press roller 52. Through this step, the catalyst-coatedmembrane 5 with thesupport film 7 is manufactured. - The catalyst-coated
membrane 5 with thesupport film 7 is wound by the membraneassembly winding roller 56. The membraneassembly winding roller 56 winds the catalyst-coatedmembrane 5 and provides a constant tension to theelectrolyte membrane 2 that is suspended on thesecond press roller 51 away from thesuction roller 20. Themanufacturing apparatus 1 includes anadditional drying furnace 49 between theattachment part 50 and the membraneassembly winding roller 56. The catalyst-coatedmembrane 5 to which thesupport film 7 has been attached by theattachment part 50 passes through theadditional drying furnace 49 before being wound by the membraneassembly winding roller 56. Any known hot air drying furnace can be used as theadditional drying furnace 49. Finish drying of the catalyst layer is carried out by the catalyst-coatedmembrane 5 with thesupport film 7 passing through the inside of theadditional drying furnace 49. - The
manufacturing apparatus 1 also includes anair jetting part 60. Theair jetting part 60 is provided between theattachment part 50 and theseparation part 10. Theair jetting part 60 includes a mechanism for jetting air toward thesuction roller 20 and a mechanism for sucking the surrounding atmosphere. The air jetted by theair jetting part 60 is cooled to about 5° C., for example. Since theair jetting part 60 is provided between theattachment part 50 and theseparation part 10, it blows air to the outer surface of thesuction roller 20 on which theelectrolyte membrane 2 is not sucked. - The outer surface of the
suction roller 20 is cooled by theair jetting part 60 blowing the cooled air to thesuction roller 20. In addition, any foreign substance adhering to the outer surface of thesuction roller 20 can be removed by theair jetting part 60 blowing air to thesuction roller 20 and sucking the surrounding atmosphere. - The
manufacturing apparatus 1 further includes acontrol part 90 that controls various mechanisms provided in the apparatus. The hardware configuration of thecontrol part 90 is the same as a commonly used computer. More specifically, thecontrol part 90 includes a CPU that performs various types of computational processing, a ROM that is a read-only memory for storing a basic program, a RAM that is a readable and writable memory for storing various types of information, and a magnetic disk for storing control software, data and the like. The various operation mechanisms provided in themanufacturing apparatus 1 are controlled by the CPU of thecontrol part 90 executing a predetermined processing program, and thereby the manufacturing process of the catalyst-coatedmembrane 5 proceeds. - Next, a description will be given of the procedure of processing performed by the
manufacturing apparatus 1 for a composite membrane that has the above-described configuration.FIG. 5 is a flowchart illustrating a procedure through which the catalyst-coatedmembrane 5 is manufactured by themanufacturing apparatus 1. The following procedure for manufacturing the catalyst-coatedmembrane 5 proceeds by thecontrol part 90 controlling various operation mechanisms of themanufacturing apparatus 1. - First, the electrolyte
membrane unwinding roller 12 unwinds theelectrolyte membrane 2 with the backsheet 6 (step S1). As described above, since theelectrolyte membrane 2 for use in polymer electrolyte fuel cells is very easily deformed with a low amount of moisture contained in the air, thebacksheet 6, which is a band-shaped resin film for shape retention, is attached to theelectrolyte membrane 2 at the stage of winding theelectrolyte membrane 2 during manufacture. Thebacksheet 6 is attached to the first side of theelectrolyte membrane 2. Theelectrolyte membrane 2 with thebacksheet 6 that has been continuously pulled out from the electrolytemembrane unwinding roller 12 is suspended on theauxiliary roller 13 and sent out to thefirst press roller 11 of theseparation part 10. - In the
separation part 10, the second side of theelectrolyte membrane 2 with thebacksheet 6 is pressed against thesuction roller 20 by thefirst press roller 11, thereby separating thebacksheet 6 and causing theelectrolyte membrane 2 to be sucked and supported by the suction roller 20 (step S2). In other words, thefirst press roller 11 separates thebacksheet 6, with the second side of theelectrolyte membrane 2 being sucked onto thesuction roller 20.FIG. 6 is a diagram showing how thebacksheet 6 is separated and theelectrolyte membrane 2 is sucked onto thesuction roller 20 by thefirst press roller 11. Thebacksheet 6 is separated from theelectrolyte membrane 2 at a position between thefirst press roller 11 and thesuction roller 20, and theelectrolyte membrane 2 is sucked onto thesuction roller 20. - The
first press roller 11 presses theelectrolyte membrane 2 against thesuction roller 20 with a force in such a range that theelectrolyte membrane 2 having low strength can be reliably sucked onto the outer surface of thesuction roller 20 without being deformed. Note that thefirst press roller 11 is installed at a position close to and spaced a predetermined interval from the outer surface of thesuction roller 20. The force with which thefirst press roller 11 presses theelectrolyte membrane 2 with thebacksheet 6 against thesuction roller 20 is adjustable by changing this interval. - The
suction roller 20 sucks the second side of theelectrolyte membrane 2. By applying a negative pressure of 90 kPa or more to thesuction port 21 of thesuction roller 20 that is formed of porous ceramics having a porosity of 15 to 50%, a negative pressure of 10 kPa or more uniformly acts on the outer surface, regardless of whether thesuction roller 20 is sucking theelectrolyte membrane 2. Accordingly, thesuction roller 20 can stably suck and support theelectrolyte membrane 2 at a fixed suction pressure, regardless of the size of the width of theelectrolyte membrane 2. Additionally, it is possible to inhibit deformation of theelectrolyte membrane 2 due to suction by thesuction roller 20. - Furthermore, since the surface roughness of the outer surface of the
suction roller 20 is 5 μm or less in terms of Rz and the pore diameter of thesuction roller 20 is 5 μm or less, a suction trace resulting from suction support is unlikely to occur in theelectrolyte membrane 2. In other words, thesuction roller 20 according to the present embodiment can stably suck and support theelectrolyte membrane 2 having fragile mechanical properties without causing deformation or a suction trace. - As shown in
FIG. 6 , thesuction roller 20 sucking and supporting theelectrolyte membrane 2 rotates about the central axis extending in the Y-axis direction as the center of rotation, and thereby, theelectrolyte membrane 2 from which thebacksheet 6 has been separated is transported while being supported on the outer surface of thesuction roller 20. On the other hand, thebacksheet 6 that has been separated from theelectrolyte membrane 2 is wound by thebacksheet winding roller 14. - Next, the electrode ink is applied from the
coating nozzle 30 to the first side of theelectrolyte membrane 2 that is transported while being sucked and supported on the suction roller 20 (step S3). The electrode ink to be applied to theelectrolyte membrane 2 of a polymer electrolyte fuel cell contains, for example, particles of a catalyst such as platinum or a platinum alloy, an ion-conducting electrolyte, and a dispersion medium. The electrode ink to be applied may be either a cathode electrode ink or an anode electrode ink. - In the present embodiment, the coating
liquid supply mechanism 35 intermittently supplies the electrode ink to thecoating nozzle 30, thereby intermittently applying the electrode ink from thecoating nozzle 30 to the first side of theelectrolyte membrane 2 that is transported while being sucked and supported on thesuction roller 20.FIG. 7 is a diagram showing a state in which the electrode ink has been intermittently applied to theelectrolyte membrane 2.FIG. 8 is a cross-sectional view of theelectrolyte membrane 2 having the electrode ink intermittently applied thereto. By intermittently ejecting the electrode ink though thecoating nozzle 30 onto theelectrolyte membrane 2 that is transported at a fixed speed while being sucked and supported on thesuction roller 20, theelectrode ink layers 8 having a constant size are discontinuously formed at predetermined intervals on the first side of theelectrolyte membrane 2 as shown inFIGS. 7 and 8 . - Since the total runout of the
suction roller 20 during rotation is 10 μm or less and the surface roughness of the outer surface of thesuction roller 20 is 5 μm or less in terms of Rz, the interval between the outer surface of therotating suction roller 20 and the slit-shaped discharge port of thecoating nozzle 30 is stable at a substantially constant value. Thus, it is possible to form uniformelectrode ink layers 8 with high precision through intermittent coating from thecoating nozzle 30. - The width of each of the
electrode ink layers 8 formed on the first side of theelectrolyte membrane 2 is defined by the width of the slit-shaped discharge port of thecoating nozzle 30. The length of each of the electrode ink layers 8 is defined by the electrode ink ejection time of thecoating nozzle 30 and the transport speed of the electrolyte membrane 2 (i.e., the rotational speed of the suction roller 20). The thickness (height) of the electrode ink layers 8 is defined by the distance between the discharge port of thecoating nozzle 30 and the first side of theelectrolyte membrane 2 as well as the ejection flow rate of the ejection electrode ink and the transport speed of theelectrolyte membrane 2. For example, the thickness is in the range of 10 to 300 μm. The electrode ink is a paste that can be applied from thecoating nozzle 30, and has a degree of viscosity that can maintain the shape of the electrode ink layers 8 on theelectrolyte membrane 2. - Then, the
electrode ink layers 8 are transported to positions opposing the dryingfurnace 40 by the rotation of thesuction roller 20 and are subjected to a dry process (step S4). The dry process of the electrode ink layers 8 is carried out by blowing hot air from the dryingfurnace 40 to the electrode ink layers 8. As a result of the hot air being blown to theelectrode ink layers 8, theelectrode ink layers 8 are heated to volatilize the solvent component and are dried. The volatilization of the solvent component causes theelectrode ink layers 8 to be dried into catalyst layers 9. Note that in the present embodiment, since theadditional drying furnace 49 is provided for the final finish drying, it is sufficient that theelectrode ink layers 8 are dried in the dryingfurnace 40 to the extent that no ink from thecatalyst layer 9 will adhere to thesecond press roller 51. -
FIG. 9 is a cross-sectional view of theelectrolyte membrane 2 having the catalyst layers 9 formed thereon. The catalyst layers 9 are electrode layers in which catalyst particles of platinum or the like are supported. The catalyst layers 9 are formed as a result of solidification of the solvent component that has been volatilized from theelectrode ink layers 8, and therefore have a thickness smaller than that of the electrode ink layers 8. The thickness of the dried catalyst layers 9 is in the range of 3 to 50 μm, for example. - The drying
furnace 40 includes the three dryingzones zone 41 located on the most upstream side through theintermediate drying zone 42 to the dryingzone 43 on the most downstream side in the transport direction of theelectrolyte membrane 2 by thesuction roller 20. If the dryingfurnace 40 is not divided into drying zones and high-temperature hot air is immediately blown to theelectrode ink layers 8 immediately after coating, theelectrode ink layers 8 will be rapidly dried, which may cause cracking in the surface. This is also the case when theelectrode ink layers 8 immediately after coating are rapidly dried with a heater built into thesuction roller 20. - In the present embodiment, the drying
furnace 40 is divided into the three dryingzones electrolyte membrane 2. That is, the dryingzone 41 on the most upstream side slightly increases the temperature of theelectrode ink layers 8 by blowing hot air having a relatively low temperature to theelectrode ink layers 8 immediately after coating. Next, theintermediate drying zone 42 gradually dries theelectrode ink layers 8 by blowing hot air having a rather high temperature. Then, the dryingzone 43 on the most downstream side strongly dries theelectrode ink layers 8 by blowing high-temperature hot air. By gradually increasing the drying temperature in this way to dry theelectrode ink layer 8 stepwise, it is possible to prevent the occurrence of cracking during the dry process. - To appropriately dry the
electrode ink layers 8 while preventing the occurrence of cracking, it is also necessary to appropriately manage the dry process time. Preferably, the dry process time is about 60 seconds, for example. The dry process time is a total time required for a singleelectrode ink layer 8 to pass through the three dryingzones suction roller 20 is 400 mm and the three dryingzones suction roller 20, the length of the dryingzones electrolyte membrane 2 may be set to 10.4 mm/sec. The transport speed of theelectrolyte membrane 2 is defined by the rotational speed of thesuction roller 20. - The drying
furnace 40 further includes the heat-shieldingzone 44 on the most upstream side and the heat-shieldingzone 45 on the most downstream side in the transport direction of theelectrolyte membrane 2. This makes it possible to prevent the hot air blown out from the dryingzones furnace 40 to the upstream and downstream sides of thesuction roller 20. As a result, it is possible to prevent unnecessarily heating of thecoating nozzle 30 located on the upstream side of the dryingfurnace 40 and theattachment part 50 located on the downstream side. - Besides the heat-shielding
zones furnace 40 is also provided with thesuction parts furnace 40 and to prevent the leakage of the vapor or the like of the solvent volatilized from theelectrode ink layers 8 during drying. - Next, the dried
catalyst layer 9 reaches theattachment part 50 by further rotation of thesuction roller 20. When theelectrolyte membrane 2 having thecatalyst layer 9 formed thereon has reached theattachment part 50, theelectrolyte membrane 2 is separated from thesuction roller 20 and suspended by thesecond press roller 51. That is, the second side of theelectrolyte membrane 2 is separated from the outer surface of thesuction roller 20, and the first side of theelectrolyte membrane 2 is brought into contact with and supported by the outer surface of the second press roller 51 (step S5). At this time, the catalyst layers 9 that have been formed on theelectrolyte membrane 2 come into contact with thesecond press roller 51. On the other hand, thesupport film 7 that has been sent out from the supportfilm unwinding roller 55 is suspended on thethird press roller 52. - The
second press roller 51 and thethird press roller 52 are provided at a predetermined interval, and the interval is smaller than the total thickness of theelectrolyte membrane 2, the catalyst layers 9, and thesupport film 7. Accordingly, thesupport film 7 is pressed against and attached to the second side of theelectrolyte membrane 2 when theelectrolyte membrane 2 and thesupport film 7 pass between thesecond press roller 51 and the third press roller 52 (step S6). -
FIG. 10 is a diagram showing how thesupport film 7 is attached to theelectrolyte membrane 2 by thesecond press roller 51 and thethird press roller 52. The second side of theelectrolyte membrane 2 wound on thesecond press roller 51 and thesupport film 7 wound on thethird press roller 52 come into contact with each other. The force with which thesupport film 7 is pressed against the second side of theelectrolyte membrane 2 at this time is defined by the interval between thesecond press roller 51 and thethird press roller 52. Since theelectrolyte membrane 2 has a certain degree of viscosity on its surface, thesupport film 7 can be attached to theelectrolyte membrane 2 by pressing thesupport film 7 against the second side of theelectrolyte membrane 2 even if thesupport film 7 is a resin film such as PEN. If thesupport film 7 is a one-side slightly self-adhesive film having an adhesive applied to one side, thesupport film 7 can be more reliably attached to theelectrolyte membrane 2. - By attaching the
support film 7 to the second side of theelectrolyte membrane 2, the catalyst-coatedmembrane 5 with thesupport film 7 is manufactured. The catalyst-coatedmembrane 5 is transported by being wound by the membraneassembly winding roller 56. In this process, the catalyst-coatedmembrane 5 with thesupport film 7 passes through the inside of theadditional drying furnace 49. Thereby, the final finish drying of the catalyst layers 9 is performed (step S7). Even if the catalyst layers 9 are not sufficiently dried in the dryingfurnace 40, the catalyst layers 9 can be reliably dried by theadditional drying furnace 49. The catalyst-coatedmembrane 5 with thesupport film 7 that has passed through theadditional drying furnace 49 is wound by the membraneassembly winding roller 56, and thereby, a series of the steps of manufacturing the catalyst-coatedmembrane 5 is completed (step S8). - In the
manufacturing apparatus 1 described above, the dryingfurnace 40 is provided so as to cover a portion of the outer surface of thesuction roller 20, and hot air is blown to the outer surface of thesuction roller 20 for drying the electrode ink layers 8. Accordingly, thesuction roller 20 formed of porous ceramics gradually stores heat and undergoes a temperature rise. When thesuction roller 20 is heated to a high temperature exceeding a predetermined value, the electrode ink applied to theelectrolyte membrane 2 from thecoating nozzle 30 is immediately heated and rapidly dried, which may cause cracking in the surfaces of the electrode ink layers 8. - For this reason, the
suction roller 20 is provided with the plurality of water-cooled tubes 22 (FIG. 3 ). Thesuction roller 20 is cooled by flowing constant-temperature water through the water-cooledtubes 22, thereby preventing thesuction roller 20 from being heated to a temperature higher than or equal to the predetermined value. However, thesuction roller 20 formed of porous ceramics may have low heat conduction. Moreover, since the dryingfurnace 40 blows hot air onto the outer surface of thesuction roller 20, it may not be possible to sufficiently suppress an increase in the temperature of the outer surface. - Even in such a case, the outer surface of the
suction roller 20 that has stored heat due to hot air from the dryingfurnace 40 can be cooled to remove heat by blowing cooling air from the air jetting part 60 (FIG. 2 ) toward the outer surface of thesuction roller 20. This makes it possible to prevent immediate heating of the electrode ink applied from thecoating nozzle 30 to theelectrolyte membrane 2. In addition, any foreign substance adhering to the outer surface of thesuction roller 20 can be removed by theair jetting part 60 blowing air to thesuction roller 20 and sucking the surrounding atmosphere. - In the first preferred embodiment, the
electrolyte membrane 2 with thebacksheet 6 is sent out from the electrolytemembrane unwinding roller 12, and thebacksheet 6 is separated, with the second side of theelectrolyte membrane 2 being sucked on thesuction roller 20 by thefirst press roller 11. Then, theelectrolyte membrane 2 is transported while being sucked and supported on thesuction roller 20, so that the electrode ink is applied to the first side of theelectrolyte membrane 2 to form theelectrode ink layers 8, which are then dried by a blast of hot air into catalyst layers 9. Thereafter, thesupport film 7 is attached to the second side of theelectrolyte membrane 2 in a state in which the outer surface of thesecond press roller 51 disposed close to thesuction roller 20 is brought into contact with and supported on the first side of theelectrolyte membrane 2. - Accordingly, the
electrolyte membrane 2, which is transported roll-to-roll from the electrolytemembrane unwinding roller 12 via thesuction roller 20 to the membraneassembly winding roller 56, is always continuously supported by some member. Specifically, in the initial state, the first side of theelectrolyte membrane 2 is supported by thebacksheet 6. When thebacksheet 6 is separated, the second side of theelectrolyte membrane 2 is supported by the outer surface of thesuction roller 20. When theelectrolyte membrane 2 is separated from thesuction roller 20 after drying of the catalyst layers 9, the first side of theelectrolyte membrane 2 is supported by thesecond press roller 51. Furthermore, in a state in which the first side of theelectrolyte membrane 2 is in contact with and supported on the outer surface of thesecond press roller 51, thesupport film 7 is attached to the second side of theelectrolyte membrane 2 and all are wound on the membraneassembly winding roller 56. - As previously described, the
electrolyte membrane 2 used in themanufacturing apparatus 1 is very thin and low in mechanical strength, and has the characteristics of easily undergoing swelling even with a small amount of moisture in the air, and also undergoing shrinkage with decreasing humidity. Therefore, theelectrolyte membrane 2 is highly likely to undergo deformation. If the electrode ink is applied to theelectrolyte membrane 2 that is not supported by any member, the solvent contained in the electrode ink will cause theelectrolyte membrane 2 to swell, and theelectrolyte membrane 2 will also undergo shrinkage when the electrode ink is dried. When the catalyst layers 9 are not sufficiently dried in the dryingfurnace 40, theelectrolyte membrane 2 may undergo swelling and shrinkage even after the dry process in the dryingfurnace 40. If theelectrolyte membrane 2 undergoes swelling and shrinkage, there is the possibility that creases and pinholes are generated in theelectrolyte membrane 2. That is, the swelling and shrinkage of theelectrolyte membrane 2 tend to occur especially after the application of the electrode ink containing the solvent, posing the problem of the generation of creases and pinholes. Generation of such creases and pinholes in theelectrolyte membrane 2 can lead to a reduction in the power generation performance of the fuel cell. - In the present embodiment, the
electrolyte membrane 2 is sucked and supported by thesuction roller 20 at the time of applying the electrode ink, and theelectrolyte membrane 2 is continuously supported by thesecond press roller 51 and thesupport film 7 even after theelectrolyte membrane 2 is subsequently separated from thesuction roller 20. Accordingly, it is possible to inhibit deformation due to swelling and shrinkage of theelectrolyte membrane 2 throughout transport after the application of the electrode ink, thus preventing the generation of creases and pinholes. As a result, it is possible to prevent a reduction in the power generation performance of a fuel cell that uses the catalyst-coatedmembrane 5 manufactured by themanufacturing apparatus 1 according to the present invention. - With the
manufacturing apparatus 1, theelectrolyte membrane 2 is always continuously supported by some member not only during and after the application of the electrode ink, but also from when theelectrolyte membrane 2 is sent out from the electrolytemembrane unwinding roller 12 until it is wound by the membraneassembly winding roller 56. Accordingly, it is possible to inhibit deformation of theelectrolyte membrane 2 due to swelling and shrinkage throughout a series of the steps of manufacturing the catalyst-coatedmembrane 5, thus preventing the generation of creases and pinholes. - Next, a second preferred embodiment of the present invention will be described. Although the catalyst layers 9 are formed by applying the electrode ink to one side of the
electrolyte membrane 2 in the first preferred embodiment, the second preferred embodiment describes a case in which the catalyst layers 9 are formed by applying the electrode ink to the opposite side of theelectrolyte membrane 2 having the catalyst layers 9 formed on one side thereof. By forming anode and cathode catalyst layers 9 on both sides of theelectrolyte membrane 2, theelectrolyte membrane 2 functions as a catalyst-coatedmembrane 5 of a polymer electrolyte fuel cell. -
FIG. 11 is a side view of amanufacturing apparatus 1 a for a composite membrane according to the second preferred embodiment. InFIG. 11 , constituent elements that are the same as those in the first preferred embodiment are denoted by the same reference numerals. Themanufacturing apparatus 1 a of the second preferred embodiment is different from themanufacturing apparatus 1 of the first preferred embodiment in that it includes animage processing unit 70. Theimage processing unit 70 is provided at any position between the electrolytemembrane unwinding roller 12 and thefirst press roller 11 of the separation part 10 (in the second preferred embodiment, at a position between theauxiliary roller 13 and the first press roller 11). Theimage processing unit 70 includes an imaging camera and an image data analyzer, and uses the imaging camera to image the surface of theelectrolyte membrane 2 that is sent out from the electrolytemembrane unwinding roller 12 and transported toward theseparation part 10. Theimage processing unit 70 performs predetermined image processing on image data obtained by imaging performed by the imaging camera and specifies positions at which the catalyst layers 9 are to be formed on theelectrolyte membrane 2. The result of the analysis by theimage processing unit 70 is transmitted to thecontrol part 90. The rest of the configuration of themanufacturing apparatus 1 a of the second preferred embodiment other than theimage processing unit 70 is the same as that of themanufacturing apparatus 1 of the first preferred embodiment. - The procedure of processing performed by the
manufacturing apparatus 1 a of the second preferred embodiment is also the same as that in the first preferred embodiment (seeFIG. 5 ). However, in the second preferred embodiment, the electrode ink is applied to the opposite side of theelectrolyte membrane 2 having thecatalyst layer 9 already formed on one side. Accordingly, an electrolyte membrane obtained by attaching thebacksheet 6 to the opposite side of theelectrolyte membrane 2 having thecatalyst layer 9 formed on one side is wound around the electrolytemembrane unwinding roller 12. For example, an electrolyte membrane that is obtained by attaching thesupport film 7 to the second side of theelectrolyte membrane 2 having thecatalyst layer 9 formed on the first side and is wound by the membraneassembly winding roller 56 in the first preferred embodiment may be directly unwound from the electrolytemembrane unwinding roller 12. Thesupport film 7 and thebacksheet 6 may be the same film, and the catalyst-coatedmembrane 5 manufactured in the first preferred embodiment may be directly used as a material that is unwound from the electrolytemembrane unwinding roller 12 in the second preferred embodiment. -
FIG. 12 is a cross-sectional view of theelectrolyte membrane 2 with thebacksheet 6 that has been unwound from the electrolytemembrane unwinding roller 12. Theelectrolyte membrane 2 has catalyst layers 9 intermittently formed on the first side thereof, and thebacksheet 6 attached to the second side thereof. Theelectrolyte membrane 2 with thebacksheet 6 that has been continuously pulled out from the electrolytemembrane unwinding roller 12 is suspended on theauxiliary roller 13 and sent out to thefirst press roller 11 of theseparation part 10. - In the process in which the
electrolyte membrane 2 is sent out from the electrolytemembrane unwinding roller 12 to theseparation part 10, the first side of theelectrolyte membrane 2 is imaged by theimage processing unit 70, and positions at which the catalyst layers 9 are to be formed on theelectrolyte membrane 2 is specified by image processing. The forming positions of the catalyst layers 9 that have been specified by theimage processing unit 70 is transmitted to thecontrol part 90. Theimage processing unit 70 images the first side of theelectrolyte membrane 2 either continuously or intermittently in a short cycle, and specifies the forming positions of all catalyst layers 9. - In the
separation part 10, the first side of theelectrolyte membrane 2 is pressed against thesuction roller 20 by thefirst press roller 11, and thereby thebacksheet 6 is separated from the second side and theelectrolyte membrane 2 is sucked and supported on thesuction roller 20. In other words, thefirst press roller 11 separates thebacksheet 6 from the second side with the first side of theelectrolyte membrane 2 being sucked on thesuction roller 20. When the catalyst-coatedmembrane 5 manufactured in the first preferred embodiment is directly used in the second preferred embodiment, theelectrolyte membrane 2 is sucked and supported on thesuction roller 20, with the front and back sides being inverted. - The
suction roller 20 on which the first side of theelectrolyte membrane 2 is sucked and supported is rotated around the central axis along the Y-axis direction as the center of rotation, and thereby theelectrolyte membrane 2 from which thebacksheet 6 has been separated is transported while being supported on the outer surface of thesuction roller 20. On the other hand, thebacksheet 6 that has been separated from theelectrolyte membrane 2 is wound by thebacksheet winding roller 14. - Next, an electrode ink is applied from the
coating nozzle 30 to the second side of theelectrolyte membrane 2 that is transported while being sucked and supported on thesuction roller 20. In the second preferred embodiment, an electrode ink of opposite polarity to that of thecatalyst layer 9 already formed on the first side of theelectrolyte membrane 2 is applied to the second side. For example, when cathode catalyst layers 9 have been formed on the first side of theelectrolyte membrane 2, an anode electrode ink is applied to the second side of theelectrolyte membrane 2. Conversely, when anode catalyst layers 9 have been formed on the first side of theelectrolyte membrane 2, a cathode electrode ink is applied to the second side of theelectrolyte membrane 2. - In the second preferred embodiment, on the basis of the result of the specification of the forming positions of the catalyst layers 9 by the
image processing unit 70, thecontrol part 90 performs coating control so that the electrode ink is intermittently applied from thecoating nozzle 30 to the second side of theelectrolyte membrane 2 at positions corresponding to the forming positions of the catalyst layers 9. Specifically, for the positioning of theelectrolyte membrane 2 in the transport direction, thecontrol part 90 controls the ejection timing of the electrode ink from thecoating nozzle 30. For the positioning of theelectrolyte membrane 2 in the width direction, thecontrol part 90 adjusts the Y-axial position of thecoating nozzle 30. -
FIG. 13 is a cross-sectional view of anelectrolyte membrane 2 having an electrode ink intermittently applied the side opposite to the side corresponding to thecatalyst layer 9. As shown inFIG. 13 , the electrode ink is applied to the second side of theelectrolyte membrane 2 at positions corresponding to the positions at which the catalyst layers 9 have been formed on the first side, and therebyelectrode ink layers 8 are formed. Note that the positions of theelectrode ink layers 8 formed on the second side of theelectrolyte membrane 2 do not necessarily have to completely correspond to the forming positions of the catalyst layers 9, and may be displaced slightly. - Then, the
electrode ink layers 8 are transported to the positions opposing the dryingfurnace 40 by rotation of thesuction roller 20, and a dry process is performed on the electrode ink layers 8. The dry process of the electrode ink layers 8 is the same as that in the first preferred embodiment, and is carried out by blowing hot air from the dryingfurnace 40 to the electrode ink layers 8. As a result of the hot air being blown to theelectrode ink layers 8, theelectrode ink layers 8 are heated to volatilize the solvent component and are thereby dried. The volatilization of the solvent component causes theelectrode ink layers 8 to be dried into catalyst layers 9. - The hot air temperatures (drying temperatures) of the three drying
zones furnace 40 sequentially increase in order from the upstream side toward the downstream side in the transport direction of theelectrolyte membrane 2 by thesuction roller 20. This allows theelectrode ink layers 8 to be dried stepwise, making it possible to prevent the occurrence of cracking during the dry process. -
FIG. 14 is a cross-sectional view of an electrolyte membrane having catalyst layers 9 formed on both sides. Catalyst layers 9 are formed on the first side of theelectrolyte membrane 2, andcatalyst layers 9 of opposite polarity are formed on the second side. The catalyst layers 9 on the second side are formed at the positions corresponding to the forming positions of the catalyst layers 9 on the first side. Accordingly, theelectrolyte membrane 2 is sandwiched between the cathode catalyst layers 9 and the anode catalyst layers 9 as shown inFIG. 14 . - Next, the dried catalyst layers 9 reach the
attachment part 50 by further rotation of thesuction roller 20. When theelectrolyte membrane 2 having the catalyst layers 9 formed on the second side has reached theattachment part 50, theelectrolyte membrane 2 is separated from thesuction roller 20 and suspended on thesecond press roller 51. That is, the first side of theelectrolyte membrane 2 is separated from the outer surface of thesuction roller 20, and the second side of theelectrolyte membrane 2 is brought into contact with and supported by the outer surface of thesecond press roller 51. Meanwhile, thesupport film 7 that has been sent out from the supportfilm unwinding roller 55 is suspended on thethird press roller 52. - When the
electrolyte membrane 2 having the catalyst layers 9 formed on both sides and thesupport film 7 pass between thesecond press roller 51 and thethird press roller 52, thesupport film 7 is pressed against and attached to the first side of theelectrolyte membrane 2.FIG. 15 is a cross-sectional view of anelectrolyte membrane 2 having thesupport film 7 attached thereto. The first side of theelectrolyte membrane 2 that is wound on thesecond press roller 51, and thesupport film 7 that is wound on thethird press roller 52 come into contact with each other. The force with which thesupport film 7 is pressed against the first side of theelectrolyte membrane 2 at this time is defined by the interval between thesecond press roller 51 and thethird press roller 52. By pressing thesupport film 7 against the first side of theelectrolyte membrane 2, thesupport film 7 is attached to the first side of theelectrolyte membrane 2 to form a catalyst-coatedmembrane 5 with thesupport film 7. Although the thickness of thecatalyst layer 9 is depicted in an exaggerated manner inFIG. 15 , thecatalyst layer 9 actually has a very small thickness of 3 to 50 μm. Thus, it is possible to appropriately attach thesupport film 7 to the first side of theelectrolyte membrane 2 over the catalyst layers 9. - The catalyst-coated
membrane 5 with thesupport film 7 passes through the inside of theadditional drying furnace 49 before being wound by the membraneassembly winding roller 56. The final finish drying of the catalyst layers 9 is performed when the catalyst-coatedmembrane 5 passes through the inside of theadditional drying furnace 49. As a result of the catalyst-coatedmembrane 5 with thesupport film 7 being wound by the membraneassembly winding roller 56, a series of the steps of manufacturing the catalyst-coatedmembrane 5 is completed. - In the second preferred embodiment as well, the
electrolyte membrane 2 is sucked and supported by thesuction roller 20 at the time of applying the electrode ink, and theelectrolyte membrane 2 is continuously supported by thesecond press roller 51 and thesupport film 7 even after theelectrolyte membrane 2 is subsequently separated from thesuction roller 20. Accordingly, it is possible to prevent deformation of theelectrolyte membrane 2 due to swelling and shrinkage throughout transport during and after the application of the electrode ink, thereby preventing the generation of creases and pinholes. As a result, it is possible to prevent a reduction in the power generation performance of a fuel cell using the catalyst-coatedmembrane 5 manufactured by themanufacturing apparatus 1 a according to the present invention. - With the
manufacturing apparatus 1 a of the second preferred embodiment, theelectrolyte membrane 2 is always continuously supported by some member not only during and after the application of the electrode ink, but also from when theelectrolyte membrane 2 is sent out from the electrolytemembrane unwinding roller 12 until it is wound by the membraneassembly winding roller 56. Accordingly, it is possible to inhibit deformation of theelectrolyte membrane 2 due to swelling and shrinkage throughout a series of the steps of manufacturing the catalyst-coatedmembrane 5, thus preventing the generation of creases and pinholes. - Next, a third preferred embodiment of the present invention will be described. In the third preferred embodiment, the electrode ink is applied twice to one side of the
electrolyte membrane 2 and a dry process is performed.FIG. 16 is a side view of amanufacturing apparatus 1 b for a composite membrane according to the third preferred embodiment. InFIG. 16 , constituent elements that are the same as those in the first preferred embodiment are denoted by the same reference numerals. Themanufacturing apparatus 1 b of the third preferred embodiment is different from themanufacturing apparatus 1 of the first preferred embodiment in that it includes twocoating nozzles - The
coating nozzle 30 and the coatingliquid supply mechanism 35 of themanufacturing apparatus 1 b are the same as those in the first preferred embodiment. Themanufacturing apparatus 1 b of the third preferred embodiment further includes thecoating nozzle 130. Thecoating nozzle 130 is provided on the downstream side of thecoating nozzle 30 in the transport direction of theelectrolyte membrane 2 by thesuction roller 20 so as to divide the dryingfurnace 40. In other words, dryingfurnaces 40 are provided on the front and rear sides of thecoating nozzle 130. For example, one of the three drying zones of the dryingfurnace 40 may be disposed on the upstream side of thecoating nozzle 130, and the other two drying zones may be disposed on the downstream side of thecoating nozzle 130. - The configurations of the
coating nozzle 130 and the coatingliquid supply mechanism 135 are respectively the same as those of thecoating nozzle 30 and the coatingliquid supply mechanism 35. That is, thecoating nozzle 130 is a slit nozzle including a slit-shaped discharge port at its end. The coatingliquid supply mechanism 135 includes a tank for storing the electrode ink and an open/close valve, and supplies the electrode ink to thecoating nozzle 130. The rest of the configuration of themanufacturing apparatus 1 b of the third preferred embodiment other than the twocoating nozzles manufacturing apparatus 1 of the first preferred embodiment. - The procedure of processing performed by the
manufacturing apparatus 1 b of the third preferred embodiment is generally the same as that in the first preferred embodiment. First, thebacksheet 6 is separated from the first side of theelectrolyte membrane 2 with the second side being sucked by thesuction roller 20, and the first intermittent application of the electrode ink from thecoating nozzle 30 to the first side of theelectrolyte membrane 2, which is transported while being sucked and supported on thesuction roller 20, is performed. This step is identical to that of the first preferred embodiment. - Then, the
electrode ink layers 8 are transported to positions opposing the upstream drying furnace 40 (the dryingfurnace 40 on the upstream side of the coating nozzle 130) by rotation of thesuction roller 20, and a dry process is performed on theelectrode ink layers 8 formed by the first application of the electrode ink. In this dry process, theelectrode ink layers 8 may not be completely dried, and may be dried to such an extent that the surface does not stick to the hand when examined by touch. - In the third preferred embodiment, the second intermittent application of the electrode ink from the
coating nozzle 130 is further performed on theelectrode ink layers 8 that have been formed on the first side of theelectrolyte membrane 2 by the first application of the electrode ink. Thereby, two layers of theelectrode ink layers 8 are formed on the first side of theelectrolyte membrane 2. - The two-layered
electrode ink layers 8 formed on the first side of the twoelectrolyte membrane 2 are transported to positions opposing the downstream drying furnace 40 (the dryingfurnace 40 on the downstream side of the coating nozzle 130) by rotation of thesuction roller 20, and a dry process is performed on the electrode ink layers 8. By blowing hot air to theelectrode ink layers 8 from the dryingfurnace 40, theelectrode ink layers 8 are heated to volatilize the solvent component and are thereby dried. The volatilization of the solvent component causes theelectrode ink layers 8 to be dried into two-layered catalyst layers 9 laminated one above the other. - Thereafter, the dried catalyst layers 9 reach the
attachment part 50 by further rotation of thesuction roller 20, and thesupport film 7 is pressed against and attached to the second side of theelectrolyte membrane 2. This step is the same as that in the first preferred embodiment.FIG. 17 is a cross-sectional view of anelectrolyte membrane 2 obtained by attaching thesupport film 7 to the second side of theelectrolyte membrane 2 having the catalyst layers 9 laminated on the first side. As with the first preferred embodiment, thesupport film 7 is attached to the first side of theelectrolyte membrane 2 by pressing thesupport film 7 against the first side of theelectrolyte membrane 2, and thereby, a catalyst-coatedmembrane 5 with thesupport film 7 is manufactured. - Then, the catalyst-coated
membrane 5 with thesupport film 7 passes through the inside of theadditional drying furnace 49 before being wound by the membraneassembly winding roller 56. The final finish drying of the laminated catalyst layers 9 is performed when the catalyst-coatedmembrane 5 passes through theadditional drying furnace 49. As a result of the catalyst-coatedmembrane 5 with thesupport film 7 being wound by the membraneassembly winding roller 56, a series of the steps of manufacturing the catalyst-coatedmembrane 5 is completed. - In the third preferred embodiment as well, the
electrolyte membrane 2 is sucked and supported by thesuction roller 20 at the time of applying the electrode ink, and theelectrolyte membrane 2 is continuously supported by thesecond press roller 51 and thesupport film 7 even after theelectrolyte membrane 2 is thereafter separated from thesuction roller 20. Accordingly, it is possible to inhibit deformation of theelectrolyte membrane 2 due to swelling and shrinkage throughout transport during and after the first application of the electrode ink, thus preventing the generation of creases and pinholes. As a result, it is possible to prevent a reduction in the power generation performance of a fuel cell using the catalyst-coatedmembrane 5 manufactured by themanufacturing apparatus 1 b according to the present invention. - With the
manufacturing apparatus 1 b of the third preferred embodiment, theelectrolyte membrane 2 is always continuously supported by some member not only during and after the application of the electrode ink, but also from when theelectrolyte membrane 2 is sent out from the electrolytemembrane unwinding roller 12 until it is wound by the membraneassembly winding roller 56. Accordingly, it is possible to inhibit deformation of theelectrolyte membrane 2 due to swelling and shrinkage throughout a series of the steps of manufacturing the catalyst-coatedmembrane 5, thus preventing the generation of creases and pinholes. - Although preferred embodiments of the present invention have been described above, various modifications other than the above-described preferred embodiments may be made to the invention without departing from the spirit or essential characteristics thereof. For example, the above-described preferred embodiments describe the case in which the
first press roller 11 and thesecond press roller 51 are each installed at a position close to and spaced a predetermined interval from the outer surface of thesuction roller 20, but these rollers may be disposed in contact with the outer surface of thesuction roller 20. Similarly, thethird press roller 52 may be disposed in contact with thesecond press roller 51. Even if these rollers are disposed in contact with each other, theelectrolyte membrane 2 is always continuously supported by some member from when it is sent out from the electrolytemembrane unwinding roller 12 until it is wound by the membraneassembly winding roller 56. It is therefore possible to inhibit deformation of theelectrolyte membrane 2 due to swelling and shrinkage. However, when the rollers are disposed in contact with each other, a stronger force will act on theelectrolyte membrane 2 and the catalyst layers 9 than in the above-described preferred embodiments. - Although the drying
furnace 40 is provided with the three dryingzones furnace 40 sequentially increase in order from the upstream side toward the downstream side in the transport direction of theelectrolyte membrane 2 by thesuction roller 20. - Alternatively, a heat-shielding zone similar to that in the above-described preferred embodiments may be provided at a position between adjacent drying zones. Doing so can prevent the blasts of hot air blown out from the adjacent drying zones from mutually interfering with each other.
- When the catalyst layers 9 are sufficiently dried by the drying
furnace 40, theadditional drying furnace 49 may not necessarily be installed. - Although the drying
furnace 40 dries theelectrode ink layer 8 by blowing hot air, theelectrode ink layer 8 may be dried using, for example, a far-infrared heater instead. - In place of the
air jetting part 60, an adhesive roller or a brush that adsorbs a foreign substance may be provided so as to be in contact with the outer surface of thesuction roller 20. Alternatively, it is possible to provide a mechanism for removing a foreign substance by applying ultrasonic waves to the outer surface of thesuction roller 20. - Cooling water may be passed through the inside of
second press roller 51 so that the outer surface of thesuction roller 20 is cooled to remove heat by heat conduction from thesuction roller 20 to thesecond press roller 51. - The
manufacturing apparatus 1 a of the second preferred embodiment may be used to specify the positions of the catalyst layers 9 formed on one side of theelectrolyte membrane 2, an additional electrode ink may be applied to those catalyst layers 9, and a dry process may be performed. Doing so makes it possible to manufacture a catalyst-coatedmembrane 5 havingcatalyst layers 9 laminated thereon in the same manner as in the third preferred embodiment. - The manufacturing technique according to the present invention is not limited to the applications for the manufacture of the catalyst-coated
membrane 5 of a fuel cell, and is also applicable to the manufacture of a composite membrane for forming a functional layer on any other types of thin films. In particular, the manufacturing technique according to the present invention can be suitably used for manufacturing a composite membrane having a functional layer formed on a thin film, by applying a coating liquid containing a solvent to a thin film that easily undergoes deformation due to swelling and shrinkage such as theelectrolyte membrane 2 described above. - While the invention has been shown and described in detail, the foregoing description is in all aspects illustrative and not restrictive. It is therefore understood that numerous modifications and variations can be devised without departing from the scope of the invention.
Claims (18)
1. An apparatus for manufacturing a composite membrane having a functional layer formed on a band-like thin film, comprising:
a suction roller that sucks and supports said thin film on an outer surface thereof;
a coating part that applies a coating liquid to one side of said thin film that is transported while being sucked and supported on said suction roller;
a drying part that is provided to cover a portion of the outer surface of said suction roller and dries said coating liquid applied to the one side of said thin film to form said functional layer; and
an attachment part that attaches a band-shaped first supporting member to another side of said thin film on which said functional layer is formed, said attachment part including a first roller that comes into contact with the one side of said thin film and supports said thin film while being in contact with or close to said suction roller, and being configured to attach said first supporting member to the other side of said thin film with the one side of said thin film being in contact with and supported on an outer surface of said first roller.
2. The apparatus for manufacturing a composite membrane according to claim 1 , wherein
said attachment part includes a second roller that, while being in contact with or close to said first roller, presses said first supporting member against the other side of said thin film that is in contact with and supported on the outer surface of said first roller.
3. The apparatus for manufacturing a composite membrane according to claim 2 , further comprising
a separation part that separates a band-shaped second supporting member from said thin film having said second supporting member attached to the one side thereof, said separation part including a third roller that separates said second supporting member with the other side of said thin film being sucked on said suction roller.
4. The apparatus for manufacturing a composite membrane according to claim 1 , wherein
said drying part is divided into a plurality of drying zones, and
drying temperatures of said plurality of drying zones sequentially increase in order from an upstream side toward a downstream side in a transport direction in which said thin film is transported.
5. The apparatus for manufacturing a composite membrane according to claim 4 , wherein
said drying part includes a heat-shielding zone on at least the most upstream side in said transport direction.
6. The apparatus for manufacturing a composite membrane according to claim 1 , further comprising
an auxiliary drying part that heats said thin film to which said first supporting member is attached by said attachment part.
7. The apparatus for manufacturing a composite membrane according to claim 1, wherein
said coating part includes a slit nozzle provided with a slit-shaped discharge port.
8. The apparatus for manufacturing a composite membrane according to claim 1 , further comprising
a cooling part that cools said suction roller.
9. The apparatus for manufacturing a composite membrane according to claim 1 , further comprising
a jetting part that blows air to the outer surface of said suction roller.
10. The apparatus for manufacturing a composite membrane according to claim 1 , wherein
said coating part performs intermittent coating in which the coating liquid is intermittently applied to said thin film.
11. The apparatus for manufacturing a composite membrane according to claim 3 , wherein
said attachment part attaches said second supporting member separated by said separation part as said first supporting member, to the other side of said thin film.
12. The apparatus for manufacturing a composite membrane according to claim 1 , wherein
said thin film is an electrolyte membrane for a fuel cell, and
said coating liquid is an electrode paste.
13. A method for manufacturing a composite membrane having a functional layer formed on a band-like thin film, comprising the steps of:
(a) sucking and supporting said thin film on an outer surface of a suction roller;
(b) applying a coating liquid to one side of said thin film that is transported while being sucked and supported on said suction roller;
(c) drying said coating liquid applied to the one side of said thin film to form said functional layer; and
(d) attaching a band-shaped first supporting member to another side of said thin film in a state in which the one side of said thin film on which said functional layer is formed is in contact with and supported on an outer surface of a first roller that comes into contact with the one side of said thin film and supports said thin film while being in contact with or close to said suction roller.
14. The method for manufacturing a composite membrane according to claim 13 , wherein,
in said step (d), said first supporting member is pressed against and attached to the other side of said thin film by a second roller, said thin film being in contact with and supported on the outer surface of said first roller.
15. The method for manufacturing a composite membrane according to claim 14 , further comprising the step of
(e) separating a band-shaped second supporting member from said thin film having said second supporting member attached to the one side thereof.
16. The method for manufacturing a composite membrane according to claim 13 , wherein,
in said step (b), intermittent coating in which the coating liquid is intermittently applied to said thin film is performed.
17. The method for manufacturing a composite membrane according to claim 15 , wherein,
in said step (d), said second supporting member separated in said step (e) is attached to the other side of said thin film as said first supporting member.
18. The method for manufacturing a composite membrane according to claim 13 , wherein
said thin film is an electrolyte membrane for a fuel cell, and
said coating liquid is an electrode paste.