US20140165422A1 - Monofilament Footwear Lining - Google Patents

Monofilament Footwear Lining Download PDF

Info

Publication number
US20140165422A1
US20140165422A1 US14/103,454 US201314103454A US2014165422A1 US 20140165422 A1 US20140165422 A1 US 20140165422A1 US 201314103454 A US201314103454 A US 201314103454A US 2014165422 A1 US2014165422 A1 US 2014165422A1
Authority
US
United States
Prior art keywords
upper assembly
layer
laminate
inner lining
footwear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/103,454
Other languages
English (en)
Inventor
Martin Pfister
Andrea Giupponi
Jens Heidenfelder
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WL Gore and Associates GmbH
WL Gore and Associates SRL
Original Assignee
WL Gore and Associates GmbH
WL Gore and Associates SRL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WL Gore and Associates GmbH, WL Gore and Associates SRL filed Critical WL Gore and Associates GmbH
Assigned to W. L. GORE & ASSOCIATES GMBH reassignment W. L. GORE & ASSOCIATES GMBH ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HEINDENFELDER, JENS, PFISTER, MARTIN
Assigned to W. L. GORE & ASSOCIATI, S.r.l. reassignment W. L. GORE & ASSOCIATI, S.r.l. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: GIUPPONI, ANDREA
Publication of US20140165422A1 publication Critical patent/US20140165422A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B7/00—Footwear with health or hygienic arrangements
    • A43B7/12—Special watertight footwear
    • A43B7/125—Special watertight footwear provided with a vapour permeable member, e.g. a membrane
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B1/00—Footwear characterised by the material
    • A43B1/02—Footwear characterised by the material made of fibres or fabrics made therefrom
    • A43B1/04—Footwear characterised by the material made of fibres or fabrics made therefrom braided, knotted, knitted or crocheted
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B1/00—Footwear characterised by the material
    • A43B1/06—Footwear characterised by the material made of wood, cork, card-board, paper or like fibrous material 
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/0205—Uppers; Boot legs characterised by the material
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/02—Uppers; Boot legs
    • A43B23/06—Waterproof legs
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B23/00—Uppers; Boot legs; Stiffeners; Other single parts of footwear
    • A43B23/07—Linings therefor
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B7/00—Footwear with health or hygienic arrangements
    • A43B7/12—Special watertight footwear
    • A—HUMAN NECESSITIES
    • A43—FOOTWEAR
    • A43B—CHARACTERISTIC FEATURES OF FOOTWEAR; PARTS OF FOOTWEAR
    • A43B9/00—Footwear characterised by the assembling of the individual parts
    • A43B9/12—Stuck or cemented footwear
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
    • B29D35/00—Producing footwear
    • B29D35/10—Producing footwear having preformed soles or heels joined on to preformed uppers using a moulding technique, e.g. by feeding or injecting plastics material between the parts to be joined
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04B—KNITTING
    • D04B21/00—Warp knitting processes for the production of fabrics or articles not dependent on the use of particular machines; Fabrics or articles defined by such processes
    • D04B21/14—Fabrics characterised by the incorporation by knitting, in one or more thread, fleece, or fabric layers, of reinforcing, binding, or decorative threads; Fabrics incorporating small auxiliary elements, e.g. for decorative purposes
    • D04B21/16—Fabrics characterised by the incorporation by knitting, in one or more thread, fleece, or fabric layers, of reinforcing, binding, or decorative threads; Fabrics incorporating small auxiliary elements, e.g. for decorative purposes incorporating synthetic threads
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2403/00—Details of fabric structure established in the fabric forming process
    • D10B2403/02—Cross-sectional features
    • D10B2403/021—Lofty fabric with equidistantly spaced front and back plies, e.g. spacer fabrics
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2501/00—Wearing apparel
    • D10B2501/04—Outerwear; Protective garments
    • D10B2501/043—Footwear

Definitions

  • the present invention relates to an upper assembly for a waterproof, water vapor permeable footwear article, and to a waterproof, water permeable footwear article comprising such upper assembly.
  • the functional layer has been covered by at least one additional inner liner facing towards the interior of the footwear during use.
  • the additional inner liner provides for improved visual appearance and also for better comfort to the wearer of the footwear in use.
  • Such inner liners are made of materials, e.g. textile materials, leather, or polymeric materials, being soft and able to take up moisture in order to enhance comfort.
  • Such inner liners are also very often thick to improve comfort and take up of moisture.
  • Typical inner liners are made of all kinds of fabric like woven fabric, knit fabric, or non-woven fabric made of multifilament yarns having wicking characteristics in order to absorb moisture produced by the foot of the wearer.
  • Inner liners are also made of leather, polymeric “artificial leather”, or non-woven fabric.
  • inner liner fabrics are also often combined with foam or nonwoven layer to increase thickness and provide cushioning and stand.
  • An example for a fabric used as an inner liner in footwear articles is a non-woven material sold under the name “Cambrelle”.
  • inner liners are thick and heavy to provide abrasion resistance and durability.
  • a number of footwear applications use a three layer laminate having a functional layer embedded between two textile layers.
  • the textile layer facing inwards is a liner as described above.
  • the additional textile layer facing outwards is a mesh.
  • Footwear liners in the form of a three layer and/or a two layer laminate are mostly hanging loose within the upper assembly and are fixed only along the upper edge of the upper assembly, or are fixed discontinuously to the upper material forming an outer shell of the upper assembly, e.g. by using adhesive dots.
  • US 2011/0179677 A1 discloses an article of footwear having a hybrid upper construction including a superior compartment and an inferior compartment.
  • the superior compartment includes a laminate composed of an innermost layer (closest to the food) and at least one polymeric film layer.
  • the polymeric film layer is made of a vapor permeable, waterproof polymeric film attached to the outer side of the innermost layer. In one embodiment the polymeric film layer is sandwiched between the innermost layer and an outer layer.
  • the innermost layer is made of a lightweight material that provides comfort and breathability to the user when the user's foot comes in contact with the innermost layer during normal use and wear of the article of footwear.
  • This material may include a nonwoven fabric, a knit fabric or woven fabric made of multifilament yarn, such as rayon, nylon, and/or polyester yarn.
  • the innermost layer is made of a 170 g/m 2 hydrophilic nylon, texturized polyester knit.
  • US 2004/0216332 A1 discloses a waterproof, vapor permeable footwear construction having an upper assembly with an upper and a layer of textile material forming an upper layer located underneath the upper next to the foot of the wearer of the footwear.
  • fabrics made up with multifilament yarns can be utilized for the upper layer including woven, nonwoven and knit fabrics, e.g. a warp knit fabric.
  • warp knit fabrics include an abrasive resistant polyester and nylon combination fabric sold under the trademark ECLIPSE 100HTM, a lightweight nylon fabric sold under the trademark ECLIPSE 400HTM, and a three bar knit fabric.
  • vapor permeability of the materials used and reduced thickness of the layers to increase heat loss and reduce weight is of utmost importance.
  • waterproofness and high durability are additional requirements that typically restrict achievable vapor permeability of such footwear.
  • the requirement of durability typically also implies constraints with respect to achievable weight reduction. This applies the more in case of footwear to be used during strenuous activities in harsh environments, as is the case for footwear for military, civil defense, fire fighting or similarly demanding applications, for example.
  • an upper assembly for a waterproof, water vapor permeable footwear article comprises a laminate including a waterproof, water vapor permeable functional layer, and an inner lining layer directly attached to the functional layer on an inner side of the functional layer.
  • the inner lining layer is a knitted or woven fabric made with monofilaments.
  • Knits as used herein, also include nettings, grid monofilaments and braids.
  • Inner side refers to the side of the functional layer facing towards the foot of the user.
  • the functional layer is sometimes also referred to as a barrier layer, in view of its function to prevent entry of moisture, in the form of liquid water or of other liquids, into the interior of the footwear.
  • Monofilaments refer to filaments or fibers made of one single filament only.
  • a monofilament thus does not have an inner structure in form of twisted of braided filaments, but rather is made of a single string of material.
  • the monofilament has the configuration of a single homogeneous string of the polymer material. Such single string may be formed e.g. by extrusion. Due to its homogeneous structure and absence of any inner structure, moisture, e.g.
  • water vapor and/or liquid water, and/or any other liquids may be taken up by the monofilament only on a molecular scale, i.e by incorporation of water molecules or liquid molecules into the molecular structure of the monofilament material.
  • the ability of the monofilament to take up moisture will depend on molecular characteristics of the material the monofilament is made from. Different from multifilaments, there are no inner structures, like voids or capillars, which may increase water absorption capability of the monofilament.
  • Such upper assembly as well as a footwear article using such upper assembly, has turned out to be lightweight and highly water vapor permeable. Still, a footwear article using such upper assembly may be fully waterproof and durable. Particularly, such footwear article may have the capability of re-drying quickly after it has become wet on the inside.
  • the inner lining layer may be made up of monofilaments having a water absorption rate of less than 40% according to the “Bundesmann test” as described in DIN EN 29685 (1991).
  • the monofilaments may have a water absorption rate of even less than 30%, or even of less than 25%, according to DIN EN 29685 (1991).
  • the monofilaments may have a water absorption rate of 20% to 35% according to DIN EN 29685.
  • Water absorption rate refers to a water absorption rate of the monofilaments as measured using a laminate made up of the functional layer (e.g. an ePTFE functional layer as described below) and the inner lining layer made up of monofilaments. In such laminate the functional layer serves as a carrier for the inner lining layer. Water absorption is measured on the side of the inner lining layer in an experimental setup as described in detail in DIN EN 29685 (1991).
  • the functional layer e.g. an ePTFE functional layer as described below
  • the inner lining layer made up of monofilaments.
  • Water absorption is measured on the side of the inner lining layer in an experimental setup as described in detail in DIN EN 29685 (1991).
  • the inner lining layer used for the upper assembly provides for a particularly low water absorption by the inner lining layer.
  • the inner lining layer has a knit and/or woven configuration formed of monofilaments interlaced with each other to form loops, meshes and/or interstices between weft and warp yarns.
  • the inner lining layer creates a large number of interstices in between the monofilaments.
  • the monofilaments themselves do not significantly take up moisture.
  • the interstices formed in the inner lining layer may be relatively large, and thus do not provide for significant capillary function. Rather, moisture is transported through the interstices formed by the inner lining layer towards the functional layer.
  • the inner lining layer may be lightweight. In some embodiments the inner lining layer may have a textile weight of not more than 130 g/m 2 . The textile weight of the inner lining layer may even be not more than 100 g/m 2 , or even be not more than 90 g/m 2 . In some embodiments, the textile weight of the inner lining layer may be in the range of 40 g/m 2 to 130 g/m 2 .
  • the laminate made up of the inner lining layer and the functional layer, optionally also including an outer textile layer may be lightweight, and thus highly breathable.
  • the laminate may have a weight of less than 200 g/m 2 , particularly less than 170 g/m 2 , particularly of less than 150 g/m 2 , particularly of 170 g/m 2 to 90 g/m 2 .
  • Such embodiments provide for a most lightweight, but still durable footwear laminate including a functional layer. Breathability of the laminate is increased while weight can be reduced up to 20% compared to conventional functional layer laminates used in footwear industry.
  • the upper assembly may comprise an outer shell.
  • the laminate described herein may be attached to an inner side of such outer shell.
  • the laminate may be directly attached to the outer shell using a discontinuous adhesive.
  • the outer shell may be made from any material as used for conventional breathable uppers in the footwear industry, e.g. leather. Such material may be selected to achieve a desired visual appearance, abrasion resistance or the like.
  • laminates including a functional layer and an inner lining layer as described above may have a dry-out time of less than one hour, particularly of less than 30 minutes, particularly of 20 minutes, particularly of 15 minutes to 45 minutes. Dry-out time is measured according to the test described below.
  • the inner lining layer may have a high wet abrasion resistance of more than 100000 cycles Martindale, measured as described in EN-ISO 20344:2004. Even wet abrasion resistances of more than 200000 cycles Martindale (EN-ISO 20344:2004), more than 300000 cycles or even more than 400000 cycles Martindale (EN-ISO 20344:2004) may be achieved. In some particular embodiments the wet abrasion resistance may be 300000 to 450000 cycles Martindale (EN-ISO 20344:2004). Compared to conventional inner linings used for footwear, e.g. as prescribed by EN 20345 requiring 51.200 cycles Martindale for heel counter linings in protective footwear, the abrasion resistance is improved by 600%, or even more.
  • the inner lining layer may be a warp knit, particularly a three bar warp knit.
  • a three bar warp knit as a result of the particular way it is manufactured using three sets of guide bars arranged in three different planes in thickness direction of the fabric, is relatively thick and thus abrasion resistant.
  • such fabric may have a knit structure including relatively large interstices or meshes.
  • a three bar warp knit fabric made up with monofilaments has turned out to be both abrasion resistant and highly vapor permeable.
  • different materials may be used for the monofilaments depending on particular characteristics. Monofilaments may be used with each the guide bars of the warp knit.
  • Embodiments including both monofilaments and multifilaments typically will have inferior re-dry characteristics than embodiments where the inner lining layer is made up using monofilaments exclusively.
  • the inner lining layer may be a singular knitted fabric.
  • Singular knitted fabrics have a regular and simple knitting pattern, e.g. a simple “right/left” pattern of meshes. Such knits are relatively elastic and stretchable.
  • the inner lining layer may be made of monofilaments of any material of the group consisting of polyamide, like polyamide 6 or polyamide 6.6, and polyester, and combinations thereof.
  • polyamide like polyamide 6 or polyamide 6.6, and polyester, and combinations thereof.
  • Such polymer materials have highly non-absorbent molecular structure with respect to water vapor, water, or other liquids, thus they allow relatively low water absorption rates if provided in the form of monofilaments.
  • the thickness of the monofilament inner lining layer may be from dtex 10/f1 up to dtex 300/f1.
  • a currently preferred thickness is dtex 20/f1.
  • the laminate further may comprise an outer textile layer attached to an outer side of the functional layer.
  • the outer textile layer may have the configuration of a mesh supporting the functional layer and/or improving adherence of the laminate to an outer shell of the upper assembly, if provided.
  • “Outer side of the functional layer” refers to that side of the functional layer facing away from the foot in use.
  • the laminate may extend around the upper side of the foot.
  • the laminate may cover the inner side of an upper or outer shell of the footwear wrapping around the side and upper parts of the foot.
  • the laminate may also, but not necessarily has to, cover the underside of the foot, e.g. in the form of a lining covering an inner side of an insole which extends below the foot.
  • Such lining may have a sock-like configuration typically referred to a “bootie”, or may be a composite bag like structure of an inner upper lining covering the inner side of the upper and an inner insole lining connected, alone or together with the insole, to the bottom edges of the inner upper lining.
  • Using monofilaments for the inner lining layer provides for the possibility of seam sealing the laminates without using a primer at all. This is a unique benefit, as two pieces of inner lining material may be bonded and sealed to each other, e.g. using stitches and sealing tape, using ultrasonic bond/weld, heat bond/weld, and the like techniques without use of an additional primer.
  • two pieces of laminates each having an inner lining layer made up with, or from, monofilaments can be seam sealed with respect to each other, e.g. using stitches and sealing tape, using ultrasonic bond/weld, heat bond/weld, and the like techniques, without application of any additional preparatory techniques, like primers.
  • This characteristic of an inner lining layer made up with, or from, monofilaments simplifies production of a footwear article considerably, thus making production particularly easy and convenient.
  • the inner layer of the laminate may be the innermost layer of the upper assembly, i.e. the layer closest to the foot. In such configuration, the inner layer will be in direct contact with the foot of the person wearing the footwear and thus determine comfort.
  • the upper assembly further may comprise an outer shell, the laminate being attached to an inner side of the outer shell.
  • outer shell may be made of any material as used for conventional footwear uppers, and may be selected according to a desired visual appearance and/or abrasion resistance of the footwear. “Inner side” refers to that side of the outer shell facing towards the foot.
  • the upper laminate may be directly attached (bonded) to the inner side of the outer shell in a breathable manner over the whole surface of the inner side of the outer shell.
  • the upper assembly described above may be used in construction of a footwear article.
  • Such footwear article may include an upper assembly as describe above and a sole in communication with the upper assembly.
  • the sole may be cemented to the upper assembly, or injected to the upper assembly.
  • Other configuration for attaching a prefabricated sole to the upper assembly, like high frequency welding or stitching, are conceivable as well.
  • a footwear article may be provided having a whole boot moisture vapor transmission rate of 7 g/hr or greater, particularly of 8.75 g/hr or greater, particularly of 8 to 9.5 g/hr.
  • footwear article using an upper assembly may be waterproof according to the Dynamic Water Penetration Test set out below. It has been shown that such footwear article may successfully fulfil more than 100000 flex cycles, particularly more than 300000 flex cycles, in some embodiments even more than 500,000 flex cycles of the Dynamic Water Penetration Test.—E.g. in some particular embodiments between 350000-1000000 flex cycles may be fulfilled successfully, i.e. without significant entry of water into the interior of the shoe (see ISO 20344:2011),
  • the term “functional material” refers to materials which are both waterproof and water vapor permeable. Such materials are typically provided in laminar configuration, thus forming layers or sheets. Exemplary of such a functional material is a microporous, expanded polytetrafluoroethylene membrane material available from W. L. Gore and Associates GmbH, Putzbrunn, Germany, under the trade name GORE-TEX(R). Other functional materials have also been developed and are well known in the art.
  • Functional materials are often provided in form of laminates where at least one layer made of functional material is laminated together with at least one additional layer.
  • Laminates in footwear industry are comprised of at least two layers, e.g in the form of a two layer laminate including a functional layer supported on a textile layer.
  • three layer laminates may be used having a functional layer sandwiched in between two water vapor permeable, but not necessarily waterproof, fabric layers.
  • Such laminates may also have a discontinuous adhesive applied to the functional layer on one or both sides in order to adhere the functional layer to an outer shell or to an inner lining material, like leather, in a separate step.
  • “Functional” materials or “functional” layers often are referred to as “barrier” materials or layers.
  • the term “knit fabric” refers to any fabric or textile having a configuration with at least one yarn or thread turned into consecutive rows of loops, called loopstitches. As each row progresses, a new loop is pulled through an existing loop. The active loopstitches are held on a needle until another loop can be passed through them.
  • a fabric In the process of knitting a fabric is formed by the intermeshing of loops of yarn or yarns. Each yarn follows a meandering path, called course, thus forming loops symmetrically to the meandering path of the yarn. When one loop is drawn through another, loopstitch is formed. Loopstitches may be formed in horizontal (weft knitting) or vertical direction (warp knitting). A sequence of loopstitches in which each stitch is suspended front the next is called a wale.
  • Weft knitting is a method of forming a fabric in which the loops are made in horizontal way from a single yarn, and intermeshing of loops takes place in a crosswise direction, i.e. the wales are perpendicular to the course of the yarn.
  • Weft knitting may be knit using only one yarn, or using a multiplicity of yarns.
  • Warp knitting is a method of fabric forming in which the loops are made in a vertical way along the length of the fabric from each warp yarn, and intermeshing of loops takes place in a lengthwise direction.
  • the wales and courses run parallel.
  • One yarn is required for each wale, thus numerous ends of yarns are being fed simultaneously to individual needles placed in a lateral direction.
  • Knits as used herein also includes nettings, grid monofils and braids.
  • Woven fabric refers to a fabric formed by weaving. Weaving is a process of fabric forming by the interlacement of warp and weft yarns. Both warp and weft yarns run essentially straight and parallel to each other, either lengthwise (warp) or crosswise (weft). Woven fabric only stretches diagonally on the bias directions (between the warp and weft directions), unless the threads are elastic.
  • Non-woven fabric refers to a fabric-like material, such as felt, which is neither woven nor knitted.
  • Non-woven fabric is made from fibres, bonded together by chemical, mechanical, heat or solvent treatment.
  • Non-woven fabric unless densified or reinforced by a backing, typically lacks mechanical strength.
  • Water vapor permeability may be expressed by water vapor transmission resistance (RET)
  • RET water vapor transmission resistance
  • the water vapor transmission resistance (RET) is a specific material property of sheet-like structures or composites which determines the latent evaporation heat flux through a given area of the sheet-like structure or composite, under a constant partial pressure gradient.
  • RET is measured by the Hohenstein skin model, of the Be reliesphysio striges Institute (Apparel Physiology Institute] e.V. Hohenstein. The Hohenstein skin model is described in ISO 11092:1993.
  • Waterproofness may be expressed by a dynamic footwear water penetration test carried out according to ISO 20344:2011. This test method is intended to provide a means of evaluating the degree of water resistance of footwear. The method is applicable to all types of footwear, particularly shoes and boots.
  • the footwear is secured in a flexing machine with water at a defined level above the featherline (i.e. the edge between the sole and upper).
  • the footwear is flexed at a constant rate and inspected at predefined intervals for water penetration.
  • the flexing machine comprises, at each testing station:
  • the total wetted area inside the footwear shall be not greater than 3 cm 2 when tested in accordance with either of:
  • the rain unit creates rain defined by water volume, drop size and distance of rain unit to test samples. The test runs for 10 minutes.
  • Test I The water absorption (Test I) of the fabric and/or laminate are measured according to the following method:
  • the Bundesmann rain test (DIN EN 29685) may be used to determine dry-out time as follows:
  • the wet abrasion Martindale test is a test to check the abrasion resistance of footwear linings, i.e. the innermost textile side adjacent to the foot, according to EN ISO 20344:2004, 6.12.
  • Such test involves abrading circular test pieces on a reference abradant, under a specified pressure, with a cyclic planar motion on the form of a Lissajous figure.
  • the resistance to abrasion is assessed by subjecting the test piece to a defined number of cycles at which point it shall not exhibit any holes.
  • test is continued until either a hole forms in the test piece or the intende number of cycles have been performed (see below). If the fabric sample has a hole, it is only necessary to take account of holes in the base fabric. A hole should only be considered as a hole when it extends through the full thickness of the layer constituting the wear surface. This is assessed by the naked eye.
  • EN ISO 20345 specifies abrasion requirements for linings of different components of footwear, under dry and wet conditions, as follows:
  • MVTR Whole Boot Moisture Vapor Transmission Rate
  • the boot breathability test shall be designed to indicate the Moisture Vapor Transmission Rate (MVTR) through the boot by means of a difference in concentration of moisture vapor between the interior and the exterior environment.
  • MVTR Moisture Vapor Transmission Rate
  • the external test environment control system shall be capable of maintaining 23 (+ ⁇ 1) C and 50%+ ⁇ 2% relative humidity throughout the test duration.
  • the weight scale shall be capable of determining weight of boots filled with water to an accuracy of (+ ⁇ 0.01) gram.
  • the water holding bag shall be flexible so that it can be inserted into the boot and conform to the interior contours; it must be thin enough so that folds do not create air gaps; it must have much higher MVTR than the footwear product to be tested; and it must be waterproof so that only moisture vapor contacts the interior of the footwear product rather than liquid water.
  • the internal heater for the boot shall be capable of controlling the temperature of the liquid water uniformly in the boot to 35 (+ ⁇ 1) C.
  • the boot plug shall be impervious to both liquid water and water vapor.
  • Each boot shall be tested in accordance with the method described above.
  • the average whole boot MVTR from the 5 boots tested shall be greater than 3.5 grams/hour to satisfy the breathability standard.
  • FIG. 1 is a perspective and cross-sectional view of a waterproof, vapor permeable footwear article.
  • FIG. 2 is a schematic cross-sectional view of the footwear article shown in FIG. 1 .
  • FIG. 3 a,b are a schematic views showing an inner liner in form a three bar warp knit made of monofilaments from its two opposite “right” and “left” sides.
  • FIG. 4 is a schematic view showing an inner liner in form a woven made of monofilaments.
  • FIG. 1 shows a waterproof breathable footwear article 10 .
  • the footwear article 10 includes an upper assembly 12 and a sole 18 .
  • sole 18 is made of polymer material, e.g. polyurethane.
  • sole 18 may have a composite structure made of various sole layers or elements, like midsole, outsole, or further layers to improve comfort or stablilization characteristics.
  • the sole 18 may even include an outsole made of leather.
  • Sole 18 may be a prefabricated sole assembly which is joined to the upper assembly 12 , e.g. by cementing or direct injection molding.
  • sole 18 may be formed by direct injection molding of polymer material, e.g polymer material forming an outsole, to the upper assembly 12 .
  • the upper assembly 12 includes an outer shell 14 , an upper laminate 16 and an insole 28 .
  • the upper laminate 16 is composed of an inner lining layer 24 (closest to foot), a functional layer 22 , and an outer textile layer 26 (furthest from foot).
  • the outer textile layer 26 is disposed directly to the inner side of outer shell 14 .
  • the outer textile layer 26 may be made of typical shoe upper materials, like leather. In such cases, no separate outer shell 14 need be provided.
  • the functional layer 22 is often referred to as “barrier layer” in view of one of its functions, namely to prevent entry of moisture (water or other liquids).
  • the outer shell 14 may be made of any vapor permeable material us used for footwear uppers, e.g. leather, and/or a robust vapor permeable fabrics material.
  • outer shell 14 may include a woven fabric, a knit fabric, a nonwoven fabric, leather, synthetic leather, perforated rubber, polymer mesh, a discontinuous pattern of non-breathable material, the like, or combinations thereof.
  • Outer shell 14 may also include a protective cover constructed of a variety of materials including, but not limited to, leather, woven fabric, knit fabric, synthetic leather, perforated rubber, polymer mesh, a discontinuous pattern of non-breathable material, nonwoven fabric, the like, or combinations thereof.
  • the protective cover Regardless of the type of material used for the protective cover, it should be of sufficient durability to protect the upper laminate 16 during normal use of the footwear article and breathable enough to maintain comfort within the shoe.
  • the type of material utilized for the outer shell 14 will be selected such as to provide sufficient abrasion resistance to the upper assembly 12 , to provide adequate protection for the wearer of the article of footwear.
  • Protective cover is optional and may be omitted where outer shell 14 itself provides for sufficient protection of upper laminate 16 and the wearer's foot.
  • the functional layer 22 may comprise a film.
  • the film may include polymeric materials such as fluoropolymers, polyolefins, polyurethanes, and polyesters.
  • Suitable polymers may comprise resins that can be processed to form porous or microporous membrane structures.
  • polytetrafluoroethylene (PTFE) resins that can be processed to form stretched porous structures are suitable for use herein.
  • PTFE resins can be stretched to form microporous membrane structures characterized by nodes interconnected by fibrils when expanded according to the process taught in patents such as in U.S. Pat. No. 3,953,566, U.S. Pat. No. 5,814,405, or U.S. Pat. No. 7,306,729.
  • expanded PTFE fluoropolymer films are made from PTFE resins according to U.S. Pat. No. 6,541,589, having comonomer units of polyfluorobutylethylene (PFBE).
  • PFBE polyfluorobutylethylene
  • microporous expanded PTFE (ePTFE) fluoropolymers can comprise PTFE having from about 0.05% by weight to about 0.5% by weight of comonomer units of PFBE based upon the total polymer weight.
  • the film includes ePTFE having a microstructure characterized by nodes interconnected by fibrils, wherein the pores of the porous film are sufficiently tight so as to provide liquidproofness and sufficiently open to provide properties such as water vapor transmission, and/or penetration by coatings of colorants and oleophobic compositions.
  • the porous membranes it is desirable for the porous membranes to have an average median flow pore size of less than or equal to about 400 nm to provide water resistance, and a median flow pore size greater than about 50 nm for colorization. This may be accomplished by compounding a PTFE resin which is suited to produce a node and fibril microstructure upon stretching.
  • the resin can be blended with an aliphatic hydrocarbon lubricant extrusion aid such as a mineral spirit.
  • the compounded resin may be formed into a cylindrical pellet and paste extruded by known procedures into a desired extrudable shape, preferably a tape or membrane.
  • the article can be calendared to the desired thickness between rolls and then thermally dried to remove the lubricant.
  • the dried article is expanded by stretching in the machine and/or transverse directions, for example, according to the teachings of U.S. Pat. No. 3,953,566, 5,814,405, or 7,406,729, to produce an expanded PTFE structure characterized by a series of nodes which are interconnected by fibrils.
  • the ePTFE article is then amorphously locked by heating the article above the crystalline melt point of PTFE, for example between about 343° C.-375° C.
  • the ePTFE may be covered by a film of hydrophilic material, particularly polyurethane, as described in U.S. Pat. No. 4,194,041.
  • the upper laminate 16 has the configuration of a three-layer laminate with the functional layer 22 forming the middle layer of such three layer laminate.
  • An outer textile layer 26 of the upper laminate 16 faces towards the inner side of the outer shell 14 .
  • the outer textile layer is made of a knit fabric.
  • the upper laminate 16 further comprises an inner lining layer 26 provided on the inner side of the functional layer 22 .
  • the inner lining layer 26 is the innermost layer of the upper assembly, i.e. the layer closest to the foot of the wearer in use. In such position, the inner lining layer 26 is directly exposed to any sweat produced by the wearer's foot.
  • the inner lining layer 24 is desirably made from a lightweight material that provides comfort and breathability to the user when the user's foot comes into contact with the inner lining layer 24 during normal use and wear of the article of footwear 10 .
  • a lightweight material that provides comfort and breathability to the user when the user's foot comes into contact with the inner lining layer 24 during normal use and wear of the article of footwear 10 .
  • Such materials may include, but are not limited to, a knit fabric (see FIG. 3 a / 3 b ), or woven fabric (see FIG. 4 ).
  • the inner lining layer 24 is made from at least one monofilament 32 , i.e. made from at least one filament or fiber made of one single filament only.
  • monofilament 32 i.e. made from at least one filament or fiber made of one single filament only.
  • ply/twisted/braided yarns, or threads are used to produce fabrics.
  • a monofilament is made as a homogeneous piece of material, and therefore does not have an inner structure in form of twisted of braided filaments. Rather, a monofilament has the configuration of a single string of material.
  • such monofilament may be made by extruding a polymer material in the form of a thin filament or string. Such monofilament will have the configuration of a single homogeneous string of the polymer material.
  • an inner lining layer 24 can be provided which has a relatively low water absorption capability.
  • the at least one monofilament 32 is made of polyamide which is a polymer material known to have a relatively low affinity to take up water molecules.
  • the characteristic of the inner lining layer 24 not to have an affinity to absorb water or liquids may be even enhanced by providing the inner lining layer 24 in a configuration having relatively large interstices formed in between the at least one monofilament 32 .
  • Such configuration may be provided by a knit fabric, as shown in FIG. 3 a / 3 b , or by a woven fabric as shown in FIG. 4 .
  • an inner lining layer 24 in the configuration of a singular knitted three bar warp knit, as shown in FIG. 3 a / 3 b has been proven to combine the characteristics of relatively low water or liquid absorption capability with high durability.
  • an inner lining with a configuration as described above and shown in FIGS. 3 a / 3 b and 4 is lightweight, and thus also is highly vapor permeable. Using such fabric as the inner lining layer in a footwear article does not impair comfort, as sweat is transported to the functional layer efficiently, and transported towards outside via the functional layer.
  • FIGS. 3 a and 3 b show in an enlarged schematic view a singular knitted, three bar warp knit fabric. Such fabric has turned to be a highly suitable material for forming the inner lining layer 24 .
  • FIG. 3 a shows the singular knitted, three bar warp knit fabric in a view towards its “right” material side
  • FIG. 3 b shows the same singular knitted, three bar warp knit fabric in a view towards its “left” material side.
  • the warp knit structure made of a multiplicity of monofilament yarns in FIG. 3 a / 3 b yarns 32 a , 32 b , 32 c , 32 d are designated exemplary) is clearly visible.
  • Each yarn is a monofilament yarn made of polyamide 6.
  • a warp-knitted shoe liner fabric of a three-bar construction has a three-dimensional character in the fabric's thickness dimension with a lapping pattern of elongated coursewise underlaps at the fabric's technical back which, in use, is to be oriented to face inwardly of the interior foot-receiving area of the shoe.
  • a three bar warp knit is manufactured using three guide bars on the knitting machine. The three guide bars carry out lapping movements in a specific feed of the monofilament yarn. This leads to three layers of yarn, in particular monofilament yarn like PA 6 22 f1, overlapping each other and being connected to each other.
  • the textile weight of the inner lining layer 24 may be between 50 g/m 2 and 130 g/m 2 . In some embodiments the textile weight of the inner lining layer is not more than 130 g/m 2 .
  • the inner lining layer may be very thin, in particular if made from mechanically durable material and provided in a mechanically durable configuration like a suitable knit or woven made of tear resistant polymer.
  • Thickness of the inner lining layer 24 may be less than 1.5 mm, or even less than 1 mm.
  • the inner lining layer may have a thickness in a range of 1-0.5 mm, particularly at around 0.8 mm.
  • a footwear article 10 with such upper assembly 12 can be used in warm climate conditions, e.g. in deserts or tropical regions, despite the fact it is provided with a waterproof and water vapour permeable functional layer 22 .
  • the upper assembly 12 may be provided with a functional layer 22 of highly vapor permeable configuration.
  • a particular advantage of using an inner lining layer 24 as described above in a footwear article 10 is that such footwear article may have the capability of re-drying quickly after it has become wet on the inside.
  • Neither the inner lining layer 24 nor the functional layer 22 attached to it do absorb significant amounts of water or other liquids. Thus, such water or other liquids may be desorbed relatively fast and efficiently by simply turning the footwear article 10 upside down, by shaking and air dry, and/or by possible heating up.
  • the layers of the upper laminate 16 may be joined together utilizing a variety of methods.
  • One such method includes utilizing adhesives.
  • the adhering to form the upper laminate 16 can be effected either with adhesive which has been applied in continuous form, i.e., over the whole area, or with adhesive which has been applied discontinuously, i.e. with gaps.
  • Water-vapor-permeable adhesive is used in the case of a continuous adhesive layer being applied.
  • a discontinuous adhesive layer for example applied in powder, dot, net or matrix form, it is possible to use an adhesive which is not inherently water-vaporpermeable. Powdered adhesive may be desirable due to its low cost and the ease of adjusting adhesive laydowns. In this case, water vapor permeability is maintained by only a fraction of the surface of the layer being covered with adhesive.
  • the adhesive layer can be a layer of thermo-activatable adhesive. If this thermo-activatable adhesive is used for manufacturing a laminate 16 from which footwear is manufactured the activation of the laminating adhesive can be affected by a heating device either applied from the inside or from the outside of the shoe.
  • the individual layers of the upper laminate 16 may be laminated together utilizing ultrasonic bond, a seam seal, a heat bond, or the like.
  • the upper laminate 16 and the outer shell 14 may be laminated together utilizing adhesive as described above, or alternatively using ultrasonic bond, a seam seal, a heat bond, or the like.
  • An upper laminate 16 was made having a three layer configuration, as follows:
  • Such laminate was additionally provided with
  • the three layers a), b) and c) were laminated together using a discontinuous hot melt adhesive.
  • the adhesive layer d) is formed on the outer textile layer.
  • the thickness of the upper laminate 16 was 0.49 mm.
  • the weight of the upper laminate was 144 g/m 2 .
  • the upper laminate had an RET of about 4.5 m 2 Pa/W.
  • the upper laminate 16 was also tested for abrasion resistance utilizing the Abrasion Resistance Test described above.
  • the laminate fulfilled the wet abrasion rate requirement of 300000 cycles Martindale (EN-ISO 20344:2004).
  • the upper laminate 16 was also tested for water absorption rate and re-dry time according to the methods described above. The results are listed in Table 1 below.
  • the upper laminate 16 was bonded to an outer shell 14 made of leather/textile combination. Adhesion was obtained by fitting the upper laminate 16 and the outer shell 14 onto a hot aluminium last and pressing the stack of layers together using a silicon rubber shape or a 360° membrane press. The arrangement of outer shell 14 and upper laminate 16 was such that the adhesive layer of the upper laminate 16 was in direct contact with the inside of the outer shell 14 . Temperature of the last was set so as to activate the adhesive layer during the pressing process.
  • the laminate obtained in the procedure described above i.e. including the outer shell 14 and the upper laminate 16
  • the last had the form of a boot.
  • An insole board 28 was attached to the underside of the last by staples, tape or adhesive dots.
  • the stack formed by outer shell 14 and upper laminate 16 bonded together was wrapped around the last, and the outer shell/upper laminate stack was pulled over the toe region of the last.
  • the toe region of the outer shell/upper laminate stack was then attached to the insole board 28 using a hot melt adhesive that was applied automatically by the lasting machine.
  • a second lasting machine was then used to complete the lasting of the side and heel areas of the upper assembly 12 .
  • a sole unit 18 was applied according to any of the following constructions: (i) Cemented sole, by cementing a prefabricated outsole to the bottom of the upper assembly 12 , or (ii) Injected sole, by direct injection of sole material to the bottom of the upper assembly 12 .
  • the bottom of the upper assembly 12 was sealed using a Hot Melt PU adhesive applied in the total surface of the bottom of the upper assembly 12 , and then pressed with a hydraulic system press to guarantee perfect adhesion of the hot melt.
  • the exceeded lining was completely sealed creating the waterproofness of the footwear bottom.
  • the prefabricated outsole was then attached to the bottom of the upper assembly 12 and pressed onto the bottom of the upper assembly 12 in the sole press.
  • the sole press was configured in a standard setup used for sole attachment.
  • the finished article of footwear 10 was allowed to cool and the last was removed from the article of footwear 10 , as described in WO 00/44252.
  • the upper assembly 12 was fitted onto a last and closed in the bottom by an insole 28 , as described above.
  • the lasted upper assembly 12 was placed in a mold of a direct injection machine.
  • the mold was closed around the upper assembly 12 such that the bottom of the upper assembly formed the top side of the mold.
  • Hot liquid PU material was injected into the mold such as to fill the mold and seal the bottom side of the upper assembly 12 , thereby forming a seal with the exceeded part of the upper laminate 16 and creating the outsole 18 .
  • the penetration of the polyurethane into the structure of the exceeding upper laminate 16 was creating the complete waterproofness of the footwear bottom.
  • An upper laminate 16 was made having a three layer configuration, as follows:
  • the three layers were laminated together using a discontinuous adhesive pattern.
  • the thickness of the laminate 16 was 0.72 mm.
  • the weight of the laminate was 240 g/m 2 .
  • the RET of the laminate was about 6 m 2 Pa/W according to the Hohenstein skin model method described above.
  • the laminate was also tested for abrasion resistance utilizing the Abrasion Resistance Test described above.
  • the laminate was measured to fulfil the wet abrasion rate requirement of 51000 cycles Martindale (EN-ISO 20344:2004).
  • the laminate was also tested for water absorption rate and re-dry time according to the methods described above. The results are listed in Table 1.
  • An upper laminate 16 was made having a four layer configuration, as follows:
  • the three layers were laminated together using a discontinuous adhesive pattern
  • the thickness of the laminate 16 was 2.2 mm.
  • the weight of the laminate was 344 g/m 2 .
  • the RET of the laminate was about 15 m 2 Pa/W according to the Hohenstein skin model method described above.
  • the laminate was also tested for abrasion resistance utilizing the Abrasion Resistance Test described above.
  • the laminate fulfilled a wet abrasion rate of 50000 cycles Martindale (EN-ISO 20344:2004).
  • the laminate was also tested for water absorption rate and re-dry time according to the tests described above. The results are listed in Table 1.

Landscapes

  • Engineering & Computer Science (AREA)
  • Health & Medical Sciences (AREA)
  • Epidemiology (AREA)
  • General Health & Medical Sciences (AREA)
  • Public Health (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Textile Engineering (AREA)
  • Footwear And Its Accessory, Manufacturing Method And Apparatuses (AREA)
  • Knitting Of Fabric (AREA)
  • Woven Fabrics (AREA)
US14/103,454 2012-12-14 2013-12-11 Monofilament Footwear Lining Abandoned US20140165422A1 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP12197311.9A EP2742820B1 (de) 2012-12-14 2012-12-14 Monofilamentschuhfutter
EP12197311.9 2012-12-14

Publications (1)

Publication Number Publication Date
US20140165422A1 true US20140165422A1 (en) 2014-06-19

Family

ID=47602932

Family Applications (1)

Application Number Title Priority Date Filing Date
US14/103,454 Abandoned US20140165422A1 (en) 2012-12-14 2013-12-11 Monofilament Footwear Lining

Country Status (10)

Country Link
US (1) US20140165422A1 (de)
EP (1) EP2742820B1 (de)
JP (1) JP5902663B2 (de)
KR (1) KR101680417B1 (de)
CN (1) CN103859700B (de)
CA (1) CA2835559C (de)
DK (1) DK2742820T3 (de)
ES (1) ES2538095T3 (de)
PL (1) PL2742820T3 (de)
RU (1) RU2599713C2 (de)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130232825A1 (en) * 2012-03-07 2013-09-12 W. L. Gore & Associates, Inc. Stretchable Insole
US8959959B1 (en) * 2014-02-03 2015-02-24 Nike, Inc. Knitted component for an article of footwear including a full monofilament upper
CN108593776A (zh) * 2018-06-08 2018-09-28 中冶建筑研究总院有限公司 一种测量短切纤维弹性模量的装置与方法
US20190021444A1 (en) * 2015-05-28 2019-01-24 Brooks Sports, Inc. Shoe constructions having upper assemblies with independently movable booties and decoupled sole assemblies
US20200008529A1 (en) * 2018-07-03 2020-01-09 Under Armour, Inc. Article with Thermally Bonded Ribbon Structure and Method of Making
US10758007B2 (en) 2018-07-03 2020-09-01 Under Armour, Inc. Article with thermally bonded ribbon structure and method of making
WO2021183476A1 (en) * 2020-03-13 2021-09-16 Piana Nonwovens, LLC. Vertically lapped nonwoven in footwear
US20220095744A1 (en) * 2019-02-01 2022-03-31 W. L. Gore & Associates Gmbh Waterproof breathable footwear
US20220400807A1 (en) * 2019-10-14 2022-12-22 W. L. Gore & Associates Gmbh Footwear Upper

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016086993A (ja) * 2014-10-31 2016-05-23 アキレス株式会社 通気性靴
CN105729919A (zh) * 2014-12-12 2016-07-06 三六一度(中国)有限公司 一种防水透气鞋类面料的加工方法
WO2017016593A1 (en) * 2015-07-28 2017-02-02 W.L. Gore & Associates Gmbh Footwear assembly
ITUB20152773A1 (it) 2015-08-03 2017-02-03 Geox Spa Calzatura impermeabile e traspirante
US10165822B2 (en) * 2015-10-21 2019-01-01 W. L. Gore & Associates, Inc. Insulated footwear articles
WO2017088099A1 (zh) * 2015-11-23 2017-06-01 北京东石联合贸易有限公司 耐热防水透气材料及透气性防水硫化橡胶鞋
KR101686896B1 (ko) * 2016-08-31 2016-12-15 허민수 양모섬유를 이용한 신발 및 신발의 제조에 이용되는 갑피의 제조방법
FR3082103B1 (fr) 2018-06-08 2020-08-28 Decathlon Sa Procede de fabrication d'une chaussure, et chaussure susceptible d'etre obtenue par ledit procede

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120233882A1 (en) * 2011-03-15 2012-09-20 NIKE. Inc. Article Of Footwear Incorporating A Knitted Component

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SE392582B (sv) 1970-05-21 1977-04-04 Gore & Ass Forfarande vid framstellning av ett porost material, genom expandering och streckning av en tetrafluoretenpolymer framstelld i ett pastabildande strengsprutningsforfarande
US4194041A (en) 1978-06-29 1980-03-18 W. L. Gore & Associates, Inc. Waterproof laminate
KR890001484A (ko) * 1987-07-08 1989-03-27 존 에스. 캠벨 방 수 화
JPH055Y2 (de) * 1987-08-14 1993-01-05
JP2631927B2 (ja) * 1991-11-18 1997-07-16 アキレス株式会社 胛被材一体のライニング及びこれを使用したスラッシュ成形靴の製造方法並びにスラッシュ成形靴
US5505011A (en) * 1992-11-24 1996-04-09 Bleimhofer; Walter Waterproof breathable footwear with extended inside liner layer
DE4443002C2 (de) * 1994-12-02 1999-02-18 Gore W L & Ass Gmbh Schutzschuh
US5814405A (en) 1995-08-04 1998-09-29 W. L. Gore & Associates, Inc. Strong, air permeable membranes of polytetrafluoroethylene
JPH11276201A (ja) * 1998-03-26 1999-10-12 Toyo Kako Kk インナーブーツ
AU3277300A (en) 1999-01-29 2000-08-18 W.L. Gore & Associates Gmbh Footwear with sealed functional layer and method for producing same
US6541589B1 (en) 2001-10-15 2003-04-01 Gore Enterprise Holdings, Inc. Tetrafluoroethylene copolymer
US7055267B2 (en) 2003-04-30 2006-06-06 Bha Technologies, Inc. Waterproof footwear construction
EP2198820B1 (de) 2004-07-30 2013-06-26 Hill-Rom Services, Inc. Patientenliege mit motorisierter einstellbarer Breite
US7306729B2 (en) 2005-07-18 2007-12-11 Gore Enterprise Holdings, Inc. Porous PTFE materials and articles produced therefrom
JP5179231B2 (ja) * 2008-03-18 2013-04-10 日本ゴア株式会社 ランニングシューズ
DE102008027856A1 (de) * 2008-06-11 2009-12-24 W. L. Gore & Associates Gmbh Schuh mit Belüftung im unteren Schaftbereich und dafür verwendbares luftdurchlässiges Abstandsgebilde
DE202008009455U1 (de) * 2008-06-20 2009-08-06 W. L. Gore & Associates Gmbh Sohleneinheit für Schuhwerk
EP2238850B1 (de) * 2009-04-10 2014-08-13 Geox S.p.A. Wasserdichter und dampfdurchlässiger Schuh
DK2298100T3 (en) * 2009-08-28 2014-12-15 Geox Spa Steam permeable shoes
US8296970B2 (en) 2009-09-29 2012-10-30 W. L. Gore & Associates, Inc. Waterproof breathable footwear having hybrid upper construction
PL2322710T3 (pl) * 2009-11-09 2015-05-29 Gore W L & Ass Gmbh Tekstylny artykuł kompozytowy

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120233882A1 (en) * 2011-03-15 2012-09-20 NIKE. Inc. Article Of Footwear Incorporating A Knitted Component

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130232825A1 (en) * 2012-03-07 2013-09-12 W. L. Gore & Associates, Inc. Stretchable Insole
US8959959B1 (en) * 2014-02-03 2015-02-24 Nike, Inc. Knitted component for an article of footwear including a full monofilament upper
US9072335B1 (en) * 2014-02-03 2015-07-07 Nike, Inc. Knitted component for an article of footwear including a full monofilament upper
US9803299B2 (en) 2014-02-03 2017-10-31 Nike, Inc. Knitted component for an article of footwear including a full monofilament upper
US10555582B2 (en) * 2015-05-28 2020-02-11 Brooks Sports, Inc. Shoe constructions having upper assemblies with independently movable booties and decoupled sole assemblies
US20190021444A1 (en) * 2015-05-28 2019-01-24 Brooks Sports, Inc. Shoe constructions having upper assemblies with independently movable booties and decoupled sole assemblies
CN108593776A (zh) * 2018-06-08 2018-09-28 中冶建筑研究总院有限公司 一种测量短切纤维弹性模量的装置与方法
US20200008529A1 (en) * 2018-07-03 2020-01-09 Under Armour, Inc. Article with Thermally Bonded Ribbon Structure and Method of Making
US10758007B2 (en) 2018-07-03 2020-09-01 Under Armour, Inc. Article with thermally bonded ribbon structure and method of making
US10786043B2 (en) * 2018-07-03 2020-09-29 Under Armour, Inc. Article with thermally bonded ribbon structure and method of making
US20220095744A1 (en) * 2019-02-01 2022-03-31 W. L. Gore & Associates Gmbh Waterproof breathable footwear
US20220400807A1 (en) * 2019-10-14 2022-12-22 W. L. Gore & Associates Gmbh Footwear Upper
WO2021183476A1 (en) * 2020-03-13 2021-09-16 Piana Nonwovens, LLC. Vertically lapped nonwoven in footwear
US11684121B2 (en) 2020-03-13 2023-06-27 Piana Nonwovens, LLC. Vertically lapped nonwoven in footwear

Also Published As

Publication number Publication date
CN103859700A (zh) 2014-06-18
RU2013155663A (ru) 2015-06-20
PL2742820T3 (pl) 2015-10-30
CN103859700B (zh) 2016-09-21
ES2538095T3 (es) 2015-06-17
KR20140077837A (ko) 2014-06-24
EP2742820B1 (de) 2015-03-18
EP2742820A1 (de) 2014-06-18
CA2835559A1 (en) 2014-06-14
DK2742820T3 (en) 2015-06-08
CA2835559C (en) 2016-11-08
RU2599713C2 (ru) 2016-10-10
JP2014117610A (ja) 2014-06-30
KR101680417B1 (ko) 2016-11-28
JP5902663B2 (ja) 2016-04-13

Similar Documents

Publication Publication Date Title
EP2742820B1 (de) Monofilamentschuhfutter
JP6077623B2 (ja) ハイブリッドなアッパー構造部を有する防水性、かつ、通気性の靴
US20130291293A1 (en) Integrated Stretch Padded Laminate and Footwear
WO2009058720A1 (en) Articles of footwear
CA3082849A1 (en) Multilayer textile assembly for use in footwear
US20220095744A1 (en) Waterproof breathable footwear
US20240057710A1 (en) Waterproof and breathable footwear
US20240057718A1 (en) Waterproof and water vapour permeable footwear
WO2024042556A1 (en) Waterproof and water vapour-permeable footwear articles
CN114585509A (zh) 纺织复合材料和鞋

Legal Events

Date Code Title Description
AS Assignment

Owner name: W. L. GORE & ASSOCIATES GMBH, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:PFISTER, MARTIN;HEINDENFELDER, JENS;SIGNING DATES FROM 20140306 TO 20140317;REEL/FRAME:032607/0357

Owner name: W. L. GORE & ASSOCIATI, S.R.L., ITALY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:GIUPPONI, ANDREA;REEL/FRAME:032607/0741

Effective date: 20140331

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION