US20140080393A1 - Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain - Google Patents

Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain Download PDF

Info

Publication number
US20140080393A1
US20140080393A1 US14/110,991 US201214110991A US2014080393A1 US 20140080393 A1 US20140080393 A1 US 20140080393A1 US 201214110991 A US201214110991 A US 201214110991A US 2014080393 A1 US2014080393 A1 US 2014080393A1
Authority
US
United States
Prior art keywords
abrasive
nonwoven
agglomerates
particles
binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/110,991
Other languages
English (en)
Inventor
Bret W. Ludwig
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to US14/110,991 priority Critical patent/US20140080393A1/en
Assigned to 3M INNOVATIVE PROPERTIES COMPANY reassignment 3M INNOVATIVE PROPERTIES COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: LUDWIG, BRET W.
Publication of US20140080393A1 publication Critical patent/US20140080393A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
    • B24D3/20—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially organic
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
    • B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
    • B24D3/20—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially organic
    • B24D3/28—Resins or natural or synthetic macromolecular compounds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
    • B24D11/00—Constructional features of flexible abrasive materials; Special features in the manufacture of such materials
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/413—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties containing granules other than absorbent substances
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/58—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives
    • D04H1/64—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by applying, incorporating or activating chemical or thermoplastic bonding agents, e.g. adhesives the bonding agent being applied in wet state, e.g. chemical agents in dispersions or solutions

Definitions

  • Nonwoven abrasive articles generally have a nonwoven web (e.g., a lofty open fibrous web), abrasive particles, and a binder material (commonly termed a “binder”) that bonds the fibers within the nonwoven web to each other and secures the abrasive particles to the nonwoven web.
  • a binder material commonly termed a “binder”
  • nonwoven abrasive articles include nonwoven abrasive hand pads such as those marketed by 3M Company of Saint Paul, Minn. under the trade designation “SCOTCH-BRITE”.
  • nonwoven abrasive articles include convolute abrasive wheels and unitized abrasive wheels.
  • Nonwoven abrasive wheels typically have abrasive particles distributed through the layers of nonwoven web bonded together with a binder that bonds layers of nonwoven webs together, and likewise bonds the abrasive particles to the nonwoven web.
  • Unitized abrasive wheels have individual discs of nonwoven web arranged in a parallel fashion to form a cylinder having a hollow axial core.
  • convolute abrasive wheels have a nonwoven web that is spirally wound about and affixed to a core member.
  • nonwoven abrasive articles while using them on a work piece are import performance attributes. For some applications, reducing the resulting surface roughness (finish) on the work piece while maintaining or even increasing the cut of the nonwoven abrasive article in use is very desirable. It was surprisingly found that nonwoven abrasive articles according to the present invention exhibit significant improvements in the surface finish, as evaluated according to the test methods disclosed, when compared to alternative nonwoven abrasive articles as shown in the Examples.
  • the flexible bound agglomerates of formed abrasive particles produced a finer finish than nonwoven abrasive articles made using the identical formed abrasive particles that were not agglomerated.
  • agglomerating the formed abrasive particles would only increase the life of the abrasive article, and the resulting finish would be identical to non-agglomerated abrasive particles having the identical size.
  • the invention resides in a nonwoven abrasive article comprising a nonwoven web; agglomerates comprising formed ceramic abrasive particles bound together by a first flexible binder; and a second binder binding the agglomerates to the nonwoven fiber web.
  • FIG. 1 is a perspective view of an exemplary nonwoven abrasive article according to the present invention
  • FIG. 2 is a perspective schematic view of an exemplary convolute abrasive wheel according to one aspect of the present invention.
  • FIG. 3 is a perspective schematic view of an exemplary unitized abrasive wheel according to another aspect of the present invention.
  • FIG. 4 is a photomicrograph of one embodiment of an abrasive agglomerate made from formed abrasive particles.
  • FIG. 5 is a photomicrograph of another embodiment of an abrasive agglomerate made from formed abrasive particles.
  • FIG. 6 is a photomicrograph of another embodiment of an abrasive agglomerate made from formed abrasive particles.
  • cur means hardening a material, either by drying (i.e., evaporation of solvent), polymerizing (e.g., providing a sufficient degree of chain extension of the curable polyurethane prepolymer), or cooling a molten material.
  • the term “flexible binder” means that the cured binder material has a modulus of elasticity such that the cured binder material is able to bend a significant amount without breaking unlike a phenolic binder which would break.
  • the modulus of elasticity can be less than 28,000; or less than 25,000 or less than 23,000 psi as tested by ASTM D882.
  • suitable flexible binders include those of polyurethane, polyurea, polyisoprene, polybutadiene, polychloroprene, butyl rubber, styrene-butadiene copolymer, and nitrile rubber.
  • formed ceramic abrasive particle means an abrasive particle having at least a partially replicated shape.
  • Non-limiting processes to make formed abrasive particles include shaping the precursor ceramic abrasive particle in a mold having a predetermined shape to make shaped ceramic abrasive particles, extruding the precursor ceramic abrasive particle through an orifice having a predetermined shape, printing the precursor ceramic abrasive particle though an opening in a printing screen having a predetermined shape, or embossing the precursor ceramic abrasive particle into a predetermined shape or pattern.
  • Non-limiting examples of formed ceramic abrasive particles include shaped ceramic abrasive particles, such as triangular plates as disclosed in U.S.
  • the term “mineral” means abrasive particles or a mixture of abrasive particles and filler.
  • exemplary abrasive articles according to the present invention including lofty open nonwoven abrasive articles (e.g., webs and sheets), unitized abrasive wheels, and convolute abrasive wheels, may be manufactured through processes that include steps such as, for example, coating a curable composition, typically in slurry form, on a nonwoven web.
  • the curable composition comprises: a curable polyurethane prepolymer; an effective amount of an amine curative; at least one of a cationic surfactant, anionic surfactant, fluorinated nonionic surfactant, or silicone-based nonionic surfactant; and a dipodal aminosilane.
  • the nonwoven web is typically compressed (i.e., densified) relative to nonwoven webs used in lofty open nonwoven fiber articles.
  • Nonwoven webs suitable for use in the aforementioned abrasive articles are well known in the abrasives art.
  • the nonwoven web comprises an entangled web of fibers.
  • the fibers may comprise continuous fiber, staple fiber, or a combination thereof.
  • the nonwoven web may comprise staple fibers having a length of at least about 20 millimeters (mm), at least about 30 mm, or at least about 40 mm, and less than about 110 mm, less than about 85 mm, or less than about 65 mm, although shorter and longer fibers (e.g., continuous filaments) may also be useful.
  • the fibers may have a fineness or linear density of at least about 1.7 decitex (dtex, i.e., grams/10000 meters), at least about 6 dtex, or at least about 17 dtex, and less than about 560 dtex, less than about 280 dtex, or less than about 120 dtex, although fibers having lesser and/or greater linear densities may also be useful. Mixtures of fibers with differing linear densities may be useful, for example, to provide an abrasive article that upon use will result in a specifically preferred surface finish. If a spunbond nonwoven is used, the filaments may be of substantially larger diameter, for example, up to 2 mm or more in diameter.
  • the nonwoven web may be manufactured, for example, by conventional air laid, carded, stitch bonded, spun bonded, wet laid, and/or melt blown procedures.
  • Air laid nonwoven webs may be prepared using equipment such as, for example, that available under the trade designation “RANDO WEBBER” commercially available from Rando Machine Company of Cincinnati, N.Y.
  • Nonwoven webs are typically selected to be suitably compatible with adhering binders and abrasive particles while also being processable in combination with other components of the article, and typically can withstand processing conditions (e.g., temperatures) such as those employed during application and curing of the curable composition.
  • the fibers may be chosen to affect properties of the abrasive article such as, for example, flexibility, elasticity, durability or longevity, abrasiveness, and finishing properties.
  • Examples of fibers that may be suitable include natural fibers, synthetic fibers, and mixtures of natural and/or synthetic fibers.
  • Examples of synthetic fibers include those made from polyester (e.g., polyethylene terephthalate), nylon (e.g., hexamethylene adipamide, polycaprolactam), polypropylene, acrylonitrile (i.e., acrylic), rayon, cellulose acetate, polyvinylidene chloride-vinyl chloride copolymers, and vinyl chloride-acrylonitrile copolymers.
  • suitable natural fibers include cotton, wool, jute, and hemp.
  • the fiber may be of virgin material or of recycled or waste material, for example, reclaimed from garment cuttings, carpet manufacturing, fiber manufacturing, or textile processing.
  • the fiber may be homogenous or a composite such as a bicomponent fiber (e.g., a co-spun sheath-core fiber).
  • the fibers may be tensilized and crimped, but may also be continuous filaments such as those formed by an extrusion process. Combinations of fibers may also be used.
  • the nonwoven fiber web Prior to impregnation with the curable composition, the nonwoven fiber web typically has a weight per unit area (i.e., basis weight) of at least about 50 grams per square meter (gsm), at least about 100 gsm, or at least about 200 gsm; and/or less than about 400 gsm, less than about 350 gsm, or less than about 300 gsm, as measured prior to any coating (e.g., with the curable composition or optional pre-bond resin), although greater and lesser basis weights may also be used.
  • basis weight i.e., basis weight
  • the fiber web prior to impregnation with the curable composition, typically has a thickness of at least about 5 mm, at least about 6 mm, or at least about 10 mm; and/or less than about 200 mm, less than about 75 mm, or less than about 30 mm, although greater and lesser thicknesses may also be useful.
  • prebond resin serves, for example, to help maintain the nonwoven web integrity during handling, and may also facilitate bonding of a urethane binder to the nonwoven web.
  • prebond resins include phenolic resins, urethane resins, hide glue, acrylic resins, urea-formaldehyde resins, melamine-formaldehyde resins, epoxy resins, and combinations thereof
  • the amount of prebond resin used in this manner is typically adjusted toward the minimum amount consistent with bonding the fibers together at their points of crossing contact. If the nonwoven web includes thermally bondable fibers, thermal bonding of the nonwoven web may also be helpful to maintain web integrity during processing.
  • Useful abrasive particles for incorporating into the agglomerates of the invention are formed ceramic abrasive particles and, in particular, shaped ceramic abrasive particles.
  • Shaped ceramic abrasive particles were prepared according to the disclosures of co-pending U.S. Patent Publication 2010/0151196.
  • the shaped ceramic abrasive particles were prepared by shaping alumina sol gel from, for example, equilateral triangle-shaped polypropylene mold cavities of side length 0.054 inch (1.37 mm) and a mold depth of 0.012 inch (0.3 mm). After drying and firing, such resulting shaped ceramic abrasive particles comprised triangular plates that were about 570 micrometers (longest dimension) and would pass through a 30-mesh sieve.
  • inventive articles may also contain conventional (e.g., crushed) abrasive particles.
  • conventional abrasive particles for blending with the shaped ceramic abrasive particles include any abrasive particles known in the abrasive art.
  • Exemplary useful abrasive particles include fused aluminum oxide based materials such as aluminum oxide, ceramic aluminum oxide (which may include one or more metal oxide modifiers and/or seeding or nucleating agents), and heat-treated aluminum oxide, silicon carbide, co-fused alumina-zirconia, diamond, ceria, titanium diboride, cubic boron nitride, boron carbide, garnet, flint, emery, sol-gel derived abrasive particles, and mixtures thereof
  • the abrasive particles may be in the form of, for example, individual particles, agglomerates, composite particles, and mixtures thereof.
  • the conventional abrasive particles may, for example, have an average diameter of at least about 0.1 micrometer, at least about 1 micrometer, or at least about 10 micrometers, and less than about 2000, less than about 1300 micrometers, or less than about 1000 micrometers, although larger and smaller abrasive particles may also be used.
  • the conventional abrasive particles may have an abrasives industry specified nominal grade.
  • Such abrasives industry accepted grading standards include those known as the American National Standards Institute, Inc. (ANSI) standards, Federation of European Producers of Abrasive Products (FEPA) standards, and Japanese Industrial Standard (JIS) standards.
  • Exemplary ANSI grade designations include: ANSI 4, ANSI 6, ANSI 8, ANSI 16, ANSI 24, ANSI 36, ANSI 40, ANSI 50, ANSI 60, ANSI 80, ANSI 100, ANSI 120, ANSI 150, ANSI 180, ANSI 220, ANSI 240, ANSI 280, ANSI 320, ANSI 360, ANSI 400, and ANSI 600.
  • Exemplary FEPA grade designations include P8, P12, P16, P24, P36, P40, P50, P60, P80, P100, P120, P150, P180, P220, P320, P400, P500, 600, P800, P1000, and P1200.
  • Exemplary JIS grade designations include HS8, JI512, JI516, JI524, JI536, JI546, JI554, JI560, JI580, JIS100, JIS 150, JIS 180, JI5220, JIS 240, JI5280, JI5320, JI5360, JI5400, JI5400, JI5600, J15800, JIS1000, J151500, J152500, J154000, J156000, J158000, and JIS10000.
  • the inventive agglomerates comprise a first flexible binder.
  • suitable flexible binders include those of polyurethane, polyurea, polyisoprene, polybutadiene, polychloroprene, butyl rubber, styrene-butadiene copolymer, and nitrile rubber.
  • a typical flexible binder for preparation of agglomerates comprising formed ceramic abrasive particles is a polyurethane binder.
  • useful urethane prepolymers include polyisocyanates and blocked versions thereof.
  • blocked polyisocyanates are substantially unreactive to isocyanate reactive compounds (e.g., amines, alcohols, thiols, etc.) under ambient conditions (e.g., temperatures in a range of from about 20° C. to about 25° C.), but upon application of sufficient thermal energy the blocking agent is released, thereby generating isocyanate functionality that reacts with the amine curative to form a covalent bond.
  • Useful polyisocyanates include, for example, aliphatic polyisocyanates (e.g., hexamethylene diisocyanate or trimethylhexamethylene diisocyanate); alicyclic polyisocyanates (e.g., hydrogenated xylylene diisocyanate or isophorone diisocyanate); aromatic polyisocyanates (e.g., tolylene diisocyanate or 4,4′-diphenylmethane diisocyanate); adducts of any of the foregoing polyisocyanates with a polyhydric alcohol (e.g., a diol, low molecular weight hydroxyl group-containing polyester resin, water, etc.); adducts of the foregoing polyisocyanates (e.g., isocyanurates, biurets); and mixtures thereof.
  • aliphatic polyisocyanates e.g., hexamethylene diisocyanate or trimethylhexamethylene diis
  • polyisocyanates include, for example, those available under the trade designation “ADIPRENE” from Chemtura Corporation, Middlebury, Connecticut (e.g., “ADIPRENE L 0311”, “ADIPRENE L 100”, “ADIPRENE L 167”, “ADIPRENE L 213”, “ADIPRENE L 315”, “ADIPRENE L 680”, “ADIPRENE LF 1800A”, “ADIPRENE LF 600D”, “ADIPRENE LFP 1950A”, “ADIPRENE LFP 2950A”, “ADIPRENE LFP 590D”, “ADIPRENE LW 520”, and “ADIPRENE PP 1095”); polyisocyanates available under the trade designation “MONDUR” from Bayer Corporation, Pittsburgh, Pa.
  • AIRTHANE and “VERSATHANE” from Air Products and Chemicals, Allentown, Pa.
  • AIRTHANE APC-504 e.g., “AIRTHANE PST-95A”, “AIRTHANE PST-85A”, “AIRTHANE PET-91A”, “AIRTHANE PET-75D”, “VERSATHANE STE-95A”, “VERSATHANE STE-P95”, “VERSATHANE STS-55”, “VERSATHANE SME-90A”, and “VERSATHANE MS-90A”).
  • polyisocyanates such as, for example, those mentioned above may be blocked with a blocking agent according to various techniques known in the art.
  • blocking agents include ketoximes (e.g., 2-butanone oxime); lactams (e.g., epsilon-caprolactam); malonic esters (e.g., dimethyl malonate and diethyl malonate); pyrazoles (e.g., 3,5-dimethylpyrazole); alcohols including tertiary alcohols (e.g., t-butanol or 2,2-dimethylpentanol), phenols (e.g., alkylated phenols), and mixtures of alcohols as described.
  • ketoximes e.g., 2-butanone oxime
  • lactams e.g., epsilon-caprolactam
  • malonic esters e.g., dimethyl malonate and diethyl malonate
  • pyrazoles
  • Exemplary useful commercially-available blocked polyisocyanates include those marketed by Chemtura Corporation under the trade designations “ADIPRENE BL 11”, “ADIPRENE BL 16”, “ADIPRENE BL 31”, and blocked polyisocyanates marketed by Baxenden Chemicals, Ltd., Accrington, England under the trade designation “TRIXENE” (e.g., “TRIXENE BL 7641”, “TRIXENE BL 7642”, “TRIXENE BL 7772”, and “TRIXENE BL 7774”).
  • TRIXENE e.g., “TRIXENE BL 7641”, “TRIXENE BL 7642”, “TRIXENE BL 7772”, and “TRIXENE BL 7774”.
  • the amount of urethane prepolymer present in the curable composition is in an amount of from 10 to 40 percent by weight, more typically in an amount of from 15 to 30 percent by weight, and even more typically in an amount of from 20 to 25 percent by weight based on the total weight of the curable composition, although amounts outside of these ranges may also be used.
  • Suitable amine curatives include aromatic, alkyl-aromatic, or alkyl polyfunctional amines, preferably primary amines.
  • useful amine curatives include 4,4′-methylenedianiline; polymeric methylene dianilines having a functionality of 2.1 to 4.0 which include those known under the trade designations “CURITHANE 103”, commercially available from the Dow Chemical Company, and “MDA-85” from Bayer Corporation, Pittsburgh, Pa.; 1,5-diamine-2-methylpentane; tris(2-aminoethyl) amine; 3-aminomethyl-3,5,5-trimethylcyclohexylamine (i.e., isophoronediamine), trimethylene glycol di-p-aminobenzoate, bis(o-aminophenylthio)ethane, 4,4′-methylenebis(dimethyl anthranilate), bis(4-amino-3-ethylphenyl)methane (e.g., as marketed under the
  • the amine curative should be present in an amount effective (i.e., an effective amount) to cure the blocked polyisocyanate to the degree required by the intended application; for example, the amine curative may be present in a stoichiometric ratio of curative to isocyanate (or blocked isocyanate) in a range of from 0.8 to 1.35; for example, in a range of from 0.85 to 1.20, or in a range of from 0.90 to 0.95, although stoichiometric ratios outside these ranges may also be used.
  • the curable composition will include at least one organic solvent (e.g., isopropyl alcohol or methyl ethyl ketone) to facilitate coating of the curable composition on the nonwoven fiber web, although this is not a requirement.
  • the curable composition may be mixed with and/or include one or more additives.
  • additives include fillers, plasticizers, surfactants, lubricants, colorants (e.g., pigments), bactericides, fungicides, grinding aids, and antistatic agents.
  • the curable composition (including any solvent that may be present) is coated onto the nonwoven fiber web in an amount of from 1120 to 2080 gsm, more typically 1280-1920 gsm, and even more typically 1440-1760 gsm, although values outside these ranges may also be used.
  • Filler materials other than conventional abrasive particles may be blended with shaped ceramic abrasive particles in the inventive agglomerates.
  • useful fillers for this invention include metal carbonates (such as calcium carbonate, calcium magnesium carbonate, sodium carbonate, magnesium carbonate), silica (such as quartz, glass beads, glass bubbles and glass fibers), silicates (such as talc, clays, montmorillonite, feldspar, mica, calcium silicate, calcium metasilicate, sodium aluminosilicate, sodium silicate), metal sulfates (such as calcium sulfate, barium sulfate, sodium sulfate, aluminum sodium sulfate, aluminum sulfate), gypsum, vermiculite, sugar, wood flour, aluminum trihydrate, carbon black, metal oxides (such as calcium oxide, aluminum oxide, tin oxide, titanium dioxide), metal sulfites (such as calcium sulfite), thermoplastic particles (such as polycarbonate, polyetherimide,
  • the filler may also be a salt such as a halide salt.
  • halide salts include sodium chloride, potassium cryolite, sodium cryolite, ammonium cryolite, potassium tetrafluoroborate, sodium tetrafluoroborate, silicon fluorides, potassium chloride, magnesium chloride.
  • metal fillers include, tin, lead, bismuth, cobalt, antimony, cadmium, iron and titanium.
  • Other miscellaneous fillers include sulfur, organic sulfur compounds, graphite, lithium stearate and metallic sulfides.
  • the size of the agglomerates have a maximum diameter (if generally spherical) or a maximum side edge length (if generally cylindrical, ovoid, or other geometric shape) ranging from 0.8 mm to 5 mm, or 1.4 mm to 4 mm, or 1.8 to 3 mm and may be spherical, ovoid, cylindrical, pyramidal, conical or any multi-sided Platonic solid (tetrahedron, octahedron, etc.).
  • the ratio of the formed abrasive particle size (measuring the edge length of the formed abrasive particles) divided by the agglomerate size (measuring the maximum diameter or maximum side edge length of the agglomerate) is 0.0033 to 0.5 (approximately 300 to 2 formed abrasive particles across the agglomerate), or 0.01 to 0.33 (approximately 100 to 3 formed abrasive particles across the agglomerate), or 0.05 to 0.25 (approximately 20 to 4 formed abrasive particles across the agglomerate).
  • filler particles conventional crushed abrasive particles or diluents
  • they have an average particle size less than that of the formed ceramic abrasive particles, or the ratio of the filler particle size (maximum diameter) divided by the formed abrasive particles size (measuring the maximum diameter or maximum side edge length of the agglomerate) is 0.001 to 1.0, or 0.003 to 0.5, or 0.01 to 0.1.
  • Typical inventive agglomerates can comprise no more than 30 weight percent (wt. %) first flexible binder, no more than 20 wt. % first flexible binder, no more than 15 wt. % first flexible binder, or even no more than 10 wt.
  • Typical inventive agglomerates comprise at least 50 wt. % formed ceramic abrasive particles.
  • the formed ceramic abrasive particle content is 50 wt. % to 98 wt. %, 75 wt. % to 96 wt. %, or 80 wt. % to 94 wt. %;
  • the resin content is 2 wt. % to 20 wt. %, 4 wt. % to 10 wt. %, or 5 wt. % to 8 wt. %;
  • the filler particle content is 0 wt. % to 40 wt. %, 10 wt. % to 35 wt. %, or 15 wt. % to 30 wt. %. It is understood the above ranges for the various properties can be combined or selected in any manner to specify the agglomerate's attributes.
  • the nonwoven abrasive web is prepared by adhering the agglomerates of the invention to a nonwoven web with a curable second binder.
  • the coating weight for the abrasive agglomerates may depend, for example, on the particular second binder used, the process for applying the abrasive agglomerates, and the size of the abrasive agglomerates.
  • the coating weight of the abrasive agglomerates on the nonwoven web may be at least 200 grams per square meter (g/m), at least 600 g/m, or at least 800 g/m; and/or less than 2000 g/m, less than about 1600 g/m, or less than about 1200 g/m, although greater or lesser coating weights may be also be used.
  • Second binders useful for adhering the agglomerates to the nonwoven fiber web are known in the art and are selected according to the final product requirements.
  • Typical binders include those comprising polyurethane, phenolic, acrylate, and blends of phenolic and acrylate.
  • Useful polyurethane binder materials and their precursors for adhering agglomerates to nonwoven web have been described herein above.
  • Phenolic materials are useful binder precursors because of their thermal properties, availability, cost, and ease of handling.
  • Resole phenolics have a molar ratio of formaldehyde to phenol of greater than or equal to one, typically between 1.5:1.0 to 3.0:1.0.
  • Novolac phenolics have a molar ratio of formaldehyde to phenol of less than 1.0:1.0.
  • Examples of commercially available phenolics include those known by the trade names DUREZ and VARCUM from Occidental Chemicals Corp.; RESINOX from Monsanto; AROFENE from Ashland Chemical Co. and AROTAP from Ashland Chemical Co.
  • Emulsions of crosslinked acrylic resin particles may also find utility in the present invention.
  • Some binder precursors include a phenolic mixed with a latex.
  • latexes include materials containing acrylonitrile butadiene, acrylics, butadiene, butadiene-styrene, and combinations thereof.
  • These latexes are commercially available from a variety of different sources and include those available under the trade designations RHOPLEX and ACRYLSOL commercially available from Rohm and Haas Company, FLEXCRYL and VALTAC commercially available from Air Products & Chemicals Inc., SYNTHEMUL, TYCRYL, and TYLAC commercially available from Reichold Chemical Co., HYCAR and GOODRITE commercially available from B. F. Goodrich, CHEMIGUM commercially available from Goodyear Tire and Rubber Co., NEOCRYL commercially available from ICI, BUTAFON commercially available from BASF, and RES commercially available from Union Carbide.
  • Nonwoven abrasive articles of the invention may take any of a variety of conventional forms.
  • FIG. 1 shows a nonwoven abrasive article 100 comprising a nonwoven web; agglomerates comprising formed ceramic abrasive particles bound together by a first flexible binder; and a second binder binding the agglomerates to the nonwoven fiber web.
  • FIGS. 4-6 show abrasive agglomerates comprising shaped ceramic abrasive particles and a first flexible binder.
  • the shaped ceramic abrasive particles comprises triangular plates as seen.
  • Nonwoven abrasive articles are in the form of wheels.
  • Nonwoven abrasive wheels are typically in the form of a disc or right cylinder having dimensions that may be very small, e.g., a cylinder height on the order of a few millimeters or very large, e.g., a meter or more, and a diameter which may be very small, e.g., on the order of a few centimeters, or very large, e.g., tens of centimeters.
  • Wheels typically have a central opening for support by an appropriate arbor or other mechanical holding means to enable the wheels to be rotated in use. Wheel dimensions, configurations, means of support, and means of rotation are all well known in the art.
  • Convolute abrasive wheels may be provided, for example, by winding the nonwoven web that has been impregnated with the curable composition under tension around a core member (e.g., a tubular or rod-shaped core member) such that the impregnated nonwoven layers become compressed, and then curing the curable composition to provide, in one embodiment, a polyurethane binder binding the abrasive agglomerates to the layered nonwoven web and binding layers of the layered nonwoven web to each other.
  • a core member e.g., a tubular or rod-shaped core member
  • layered nonwoven fiber web 210 coated with binder binding the abrasive agglomerates to the layered nonwoven fiber web and binding layers of the layered nonwoven fiber web to each other is spirally disposed around and affixed to core member 230 .
  • convolute abrasive wheels may be dressed prior to use to remove surface irregularities, for example, using methods known in the abrasive arts.
  • An exemplary unitized abrasive wheel is shown in FIG. 3 , and can be provided, for example, by layering the impregnated above-provided nonwoven web 310 (e.g., as a layered continuous web or as a stack of sheets) compressing the nonwoven layers, curing the curable composition (e.g., using heat), and die cutting the resultant abrasive article to provide a unitized abrasive wheel having a hollow axial core 320 .
  • the layers are typically compressed to form a bun having a density that is from 1 to 20 times that of the density of the layers in their non-compressed state.
  • the bun is then typically subjected to heat molding (e.g., for from 2 to 20 hours) at elevated temperature (e.g., at 135° C.), typically depending on the urethane prepolymer and bun size.
  • SAP2 Shaped ceramic abrasive particles of about 550 micrometers (longest dimension) and passing through a 35-mesh sieve, prepared according to the teachings of U.S. patent application Ser. No. 12/337,075.
  • Agglomerated binder solutions for the Examples were prepared by mixing components as described below.
  • Agglomerate precursor compositions included mineral (abrasive particles with optional fillers) and binder mixed by hand with a spatula.
  • Agglomerates prepared with AR1, AR2, and AR4 were 94 wt. % mineral based on solids content.
  • Agglomerates prepared with AR3 were 90 wt. % mineral based on solids content.
  • a stainless steel putty knife was used to force an agglomerate precursor composition into the cavities of 15 cm by 86 cm sheets of microreplicated polypropylene tooling.
  • the tooling had total thickness of 2.2 mm, a plurality of precisely-shaped, microreplicated cavities 4.0 mm square and 1.6 mm deep separated by walls 1.5 mm thick.
  • the tooling was prepared from a corresponding master roll generally according to the procedure of U.S. Pat. No. 6,076,248 to Hoopman et al.
  • Filled sheets of polypropylene tooling were heated in a forced air oven to cure the agglomerates.
  • Urethane agglomerates were cured for 20 minutes at 260° F. (127° C.).
  • Phenolic agglomerates were cured at 200° F. (91° C.) for 90 minutes followed by 16 hours at 215° F. (102° C.).
  • Agglomerates containing free radical cured resins were cured for 30 minutes at 280° F. (138° C.).
  • the cured agglomerates were removed from the tooling by ultrasonic energy. More particularly, the backside of the tooling was pulled, under tension, across the forward edge of an ultrasonic horn tapered to a single edge.
  • the horn was oscillated at a frequency of 19,100 HZ at amplitude of about 130 micrometers.
  • the horn was composed of 6-4 titanium and was driven with a 900 watt 184 V Branson power source coupled with a 2:1 Booster 802 piezoelectric converter. Examples of the resulting abrasive agglomerates are shown in FIG. 4 .
  • abrasive particles 3000 grams was thoroughly mixed with 250 grams of AR1 producing a friable, tacky agglomerate precursor composition.
  • the agglomerate precursor composition was processed into abrasive agglomerate particles with the aid of a size reduction machine obtained under the trade designation “QUADRO COMIL” (“Model #197”, Quadro Engineering Incorporated, Waterloo, Ontario, Canada). Details of the operation of the size reduction machine can be found in WO 02/32832 A1 to Culler et.al.
  • the premix was forced through the 75 mil (1.9 mm) circular openings of a conical screen using an impeller driven at a range of 50 rpm to 3500 rpm.
  • the filamentary shaped agglomerate precursor particle separates and falls by gravity to an aluminum collection pan.
  • a mono- or bi-layer of precursor particles were collected in a pan, which was then placed in an oven set to 320° F. (160° C.) for 15 minutes in order to cure the binder resin.
  • the abrasive agglomerate particles were size-reduced by running them once through the size reduction machine (“QUADRO COMIL”) set up with a conical screen pierced by 95 mil (2.4 mm) round holes. The size-reduced particles were sieved on a 14-mesh (1400 micron) screen. Those particles retained on the screen were used to produce unitized abrasive wheels.
  • FIG. 5 An example of the abrasive agglomerate is shown in FIG. 5 .
  • Agglomerates of abrasive grain, or abrasive grain and fillers were produced by applying drops of AR4 to beds of mineral one to two centimeters in thickness. Drops were produced by feeding the solution through a blunt-tipped 22-guage hypodermic needle supported in a vertical position approximately seven centimeters above the mineral bed. The resin droplets wicked into the mineral beds within 10 seconds of application, wetting a volume of material dependent upon the surface area of the mineral or mineral/filler blends. The agglomerates were cured at 302° F. (150° C.) for 30 minutes and then sieved from the non-agglomerated mineral, which was recycled back into the agglomerate forming process.
  • AR2 was dripped onto the mineral or mineral/filler bed in a similar manner and cured at 200° F. (91° C.) for 90 minutes followed by 16 hours at 215° F. (102° C.).
  • Individual agglomerates weighed between 0.033 and 0.076 grams and contained from twelve to four percent resin by weight.
  • An example of the resulting abrasive agglomerate is show in FIG. 6 .
  • a nonwoven web was formed on an air laid fiber web forming machine, available under the trade designation “RANDO-WEBBER” from the Rando Machine Corporation of Ard, N.Y.
  • the fiber web was formed from 70 denier nylon crimp set fiber with a staple length of one and one-half inches (available from E. I. du Pont de Nemours & Company, Wilmington, Delaware).
  • the weight of the web was approximately 105 grams per square meter (gsm), and the thickness was approximately 0.4 inches (10 mm).
  • the web was conveyed to a horizontal, two-roll coater, where a pre-bond resin was applied at a wet add-on weight of 89 gsm.
  • the pre-bond resin had the following composition (all percentages relative to component weight): 54.1% BL16, 19.9% K450S, 26% PMA.
  • the pre-bond resin was cured to a non-tacky condition by passing the coated web through a convection oven at 330° F. (166° C.) for 4.5 minutes, yielding a pre-bonded, nonwoven web of approximately 6 mm thickness and having a basis weight of 168 gsm.
  • Unitized abrasive wheels were prepared from the pre-bonded nonwoven web as follows. A 9-inch (23-cm) square section was cut from the prebonded nonwoven web and saturated with one of two wheel adhesives. Wheel adhesive one (WA1) was 44% BL16, 16.4% K-450S, 15.8% PMA, 7% MP-22VF, 6% phenoxy, 9.9% kaolin, and 0.4% D-1122. Wheel adhesive two (WA2) was 60.8% Phenolic, 31.2% water, 7.4% SR511, and 0.6% D-1122.
  • Wheel adhesive one was 44% BL16, 16.4% K-450S, 15.8% PMA, 7% MP-22VF, 6% phenoxy, 9.9% kaolin, and 0.4% D-1122.
  • Wheel adhesive two (WA2) was 60.8% Phenolic, 31.2% water, 7.4% SR511, and 0.6% D-1122.
  • the saturated prebonded web was then passed through the nip of a roll coater having 4-inch (10-cm) diameter rubber rolls of 85-Shore A durometer hardness to remove excess resin until the desired resin add-on weight of 0.49 ⁇ 0.035 oz (14 ⁇ 1 g) for WA1 or 0.60 ⁇ 0.035 oz (17 ⁇ 1 g) for WA2 was obtained.
  • a roll coater having 4-inch (10-cm) diameter rubber rolls of 85-Shore A durometer hardness to remove excess resin until the desired resin add-on weight of 0.49 ⁇ 0.035 oz (14 ⁇ 1 g) for WA1 or 0.60 ⁇ 0.035 oz (17 ⁇ 1 g) for WA2 was obtained.
  • multiple passes through the nip at 11 fpm (3.35 mpm) under pressures of 10-21 psi (69-145 kPa) were required to reach the target weight.
  • seven sections of pre-bonded web were coated in the above manner. The coated sections of prebonded web were placed in a forced air
  • Stacks containing WA1 (urethane) were left in the press, set at 260° F. (127° C.), for 30 minutes.
  • Stacks containing WA2 (phenolic) were left in the press, set at 200° F. (93° C.), for five hours.
  • WA1 urethane
  • WA2 phenolic
  • the slab After removal from the oven, the slab was cooled to room temperature, and an 8.0-inch (20-cm) diameter unitized abrasive wheel with a 1.25-inch (3.2-cm) center hole was die cut from it using a SAMCO SB-25 swing beam press manufactured by Deutsche vernier Schuhmaschinen GmbH & Co., Frankfurt, Germany.
  • a pre-weighed, 0.25 inch (6.4 mm)-thick unitized abrasive wheel to be tested was mounted in a vertical orientation on the arbor of a mechanically driven, variable speed lathe adjusted to generate a surface speed at the wheel's edge of approximately 3500 feet (1065 meters) per minute.
  • the edge of a 0.0625 inch (1.59 mm)-thick, two-inch by eleven-inch (5.08-cm by 27.9-cm) cold rolled carbon steel or T304 stainless steel panel held horizontally at the height of the arbor was plunged into the rotating edge of the wheel with approximately 5 pounds (22.2 Newtons) of force for 20 seconds.
  • the amount of material removed from the panel during the test sequence was designated as the “cut” and was defined as the difference between the weight of the panel before and after the test sequence.
  • the amount of material removed from the wheel during the test sequence was designated as the “wear” and was defined as the difference between the weight of the wheel before and after the test sequence.
  • Finish samples were produced by placing the 6.4 mm-thick wheels on a back stand and adjusting the speed to produce a surface speed of approximately 3500 feet (1065 meters) per minute.
  • the faces of 0.0625 inch (1.59 mm)-thick, two-inch by eleven-inch (5.08-cm by 27.94-cm) cold rolled carbon steel or T304 stainless steel panels were abraded while applying roughly five pounds (22.2 Newtons) of pressure.
  • a 4-inch (10.2-cm) length of panel was finished by passing the panel over the wheel eight times, stepping roughly 0.25 inch (6.4 mm) between passes and moving the panel approximately 2 inches (5.04 cm) per second. Finish was measured using a Perthometer PRK profilometer (Feinpruf GmbH; Gottingen, Germany). Ten measurements were taken on each surface. The high and low values were discarded and the remaining eight data points averaged.
  • Films for modulus measurements were prepared by placing 16 grams of AR1 on a circular stainless steel form with a diameter of 5.5 inches (14 cm) and a side wall 0.12 inch (3 mm) high. Samples were placed in a forced air oven set at 180° F. (82° C.) for one hour to drive off the majority of solvent. The oven was then set at 260° F. (127° C.) for two hours to complete curing. The resulting films, approximately 0.027 in (0.69 mm) thick, were removed from the steel form.
  • Urethane-bound unitized abrasive wheels were prepared according to the procedures set forth above in the sections on Preparation of Agglomerates and Unitized Abrasive Wheel Preparation, using the components reported in Table 1.
  • the unitized abrasive wheels were tested according to the Unitized Abrasive Wheel Performance Test and Unitized Abrasive Wheel Finish Testing. Results are reported in Table 2.
  • Comparative Examples G through L the cut and wear data were not collected because the smaller abrasive particle size resulted in very low cut. Comparative Examples G through L are presented to show the comparative finishes obtained.
  • Phenolic-bound unitized abrasive wheels were prepared according to the procedures set forth above in the sections Preparation of Agglomerates and Unitized Abrasive Wheel Preparation, using the ingredients reported in Table 3. The unitized abrasive wheels were tested according to the Unitized Abrasive Wheel Performance Test and Unitized Abrasive Wheel Finish Testing. Results are reported in Table 4.
  • the modulus of AR1 was measured according to the procedure in the section on Measurement of Resin Modulus above.
  • Urethane bound unitized wheels containing agglomerates bound by a variety of free radical cured resins were produced according to the procedures set forth above in the sections Preparation of Agglomerates and Unitized Abrasive Wheel Preparation, using the ingredients reported in Table 5.
  • the unitized abrasive wheels were tested according to the Unitized Abrasive Wheel Finish Testing. Results are reported in Table 6.
  • Examples 8 and 9 and examples Z and AA were prepared to demonstrate the effect of filler on the finish produced by agglomerates of precisely shaped grain.
  • Urethane bound unitized abrasive wheels were prepared according to the procedures set forth above in the sections Preparation of Agglomerates and Unitized Abrasive Wheel Preparation, using the ingredients reported in Table 7. The unitized abrasive wheels were tested according to the Unitized Abrasive Wheel Performance Test and Unitized Abrasive Wheel Finish Testing. Results are reported in Table 8.
  • results show the addition of fillers (particles other than formed ceramic abrasive particles) in the flexible binder agglomerates of formed ceramic abrasive particles results in a finer finish.
  • Examples 10 and 1 l were prepared to demonstrate that the unexpected improved finish result is independent of the method of agglomerate production.
  • Urethane bound unitized abrasive wheels were prepared according to the procedures set forth above in the sections Preparation of Agglomerates and Unitized Abrasive Wheel Preparation, using the variables reported in Table 9. The unitized abrasive wheels were tested according to the Unitized Abrasive Wheel Performance Test and Unitized Abrasive Wheel Finish Testing. Results are reported in Table 10.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Textile Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Dispersion Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Polishing Bodies And Polishing Tools (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
US14/110,991 2011-04-14 2012-03-29 Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain Abandoned US20140080393A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US14/110,991 US20140080393A1 (en) 2011-04-14 2012-03-29 Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201161475350P 2011-04-14 2011-04-14
US14/110,991 US20140080393A1 (en) 2011-04-14 2012-03-29 Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain
PCT/US2012/031086 WO2012141905A2 (fr) 2011-04-14 2012-03-29 Article abrasif non tissé contenant des agglomérats liés à un élastomère de grain abrasif façonné

Publications (1)

Publication Number Publication Date
US20140080393A1 true US20140080393A1 (en) 2014-03-20

Family

ID=47009912

Family Applications (1)

Application Number Title Priority Date Filing Date
US14/110,991 Abandoned US20140080393A1 (en) 2011-04-14 2012-03-29 Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain

Country Status (10)

Country Link
US (1) US20140080393A1 (fr)
EP (1) EP2697416B1 (fr)
JP (1) JP6000333B2 (fr)
KR (1) KR20140024884A (fr)
CN (1) CN103476979B (fr)
BR (1) BR112013026334A2 (fr)
ES (1) ES2633316T3 (fr)
PL (1) PL2697416T3 (fr)
RU (1) RU2013145788A (fr)
WO (1) WO2012141905A2 (fr)

Cited By (44)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8840694B2 (en) 2011-06-30 2014-09-23 Saint-Gobain Ceramics & Plastics, Inc. Liquid phase sintered silicon carbide abrasive particles
US8840696B2 (en) 2012-01-10 2014-09-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US8986409B2 (en) 2011-06-30 2015-03-24 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles including abrasive particles of silicon nitride
US9017439B2 (en) 2010-12-31 2015-04-28 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9074119B2 (en) 2012-12-31 2015-07-07 Saint-Gobain Ceramics & Plastics, Inc. Particulate materials and methods of forming same
US9200187B2 (en) 2012-05-23 2015-12-01 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US9238768B2 (en) 2012-01-10 2016-01-19 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US9242346B2 (en) 2012-03-30 2016-01-26 Saint-Gobain Abrasives, Inc. Abrasive products having fibrillated fibers
US9440332B2 (en) 2012-10-15 2016-09-13 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9457453B2 (en) 2013-03-29 2016-10-04 Saint-Gobain Abrasives, Inc./Saint-Gobain Abrasifs Abrasive particles having particular shapes and methods of forming such particles
US9517546B2 (en) 2011-09-26 2016-12-13 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles including abrasive particulate materials, coated abrasives using the abrasive particulate materials and methods of forming
US9566689B2 (en) 2013-12-31 2017-02-14 Saint-Gobain Abrasives, Inc. Abrasive article including shaped abrasive particles
US9604346B2 (en) 2013-06-28 2017-03-28 Saint-Gobain Cermaics & Plastics, Inc. Abrasive article including shaped abrasive particles
US9676981B2 (en) 2014-12-24 2017-06-13 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle fractions and method of forming same
US9707529B2 (en) 2014-12-23 2017-07-18 Saint-Gobain Ceramics & Plastics, Inc. Composite shaped abrasive particles and method of forming same
US9765249B2 (en) 2011-12-30 2017-09-19 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
US9771507B2 (en) 2014-01-31 2017-09-26 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US9783718B2 (en) 2013-09-30 2017-10-10 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US9803119B2 (en) 2014-04-14 2017-10-31 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US9902045B2 (en) 2014-05-30 2018-02-27 Saint-Gobain Abrasives, Inc. Method of using an abrasive article including shaped abrasive particles
US9914864B2 (en) 2014-12-23 2018-03-13 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US9938440B2 (en) 2015-03-31 2018-04-10 Saint-Gobain Abrasives, Inc./Saint-Gobain Abrasifs Fixed abrasive articles and methods of forming same
WO2018081246A1 (fr) 2016-10-25 2018-05-03 3M Innovative Properties Company Agglomérat abrasif vitrifié façonné à particules abrasives façonnées, articles abrasifs et procédés associés
US10106714B2 (en) 2012-06-29 2018-10-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US10196551B2 (en) 2015-03-31 2019-02-05 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US20190202032A1 (en) * 2016-07-01 2019-07-04 3M Innovative Properties Company Nonwoven abrasive article including abrasive particles
WO2019167022A1 (fr) 2018-03-01 2019-09-06 3M Innovative Properties Company Aggloméré abrasif siliceux façonné comportant des particules abrasives façonnées, articles abrasifs, et procédés associés
WO2020021457A1 (fr) 2018-07-23 2020-01-30 3M Innovative Properties Company Articles comprenant un support en polyester et une couche d'apprêt, et procédés associés
US10557067B2 (en) 2014-04-14 2020-02-11 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10563105B2 (en) 2017-01-31 2020-02-18 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10655038B2 (en) 2016-10-25 2020-05-19 3M Innovative Properties Company Method of making magnetizable abrasive particles
US10711171B2 (en) 2015-06-11 2020-07-14 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10759024B2 (en) 2017-01-31 2020-09-01 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10865148B2 (en) 2017-06-21 2020-12-15 Saint-Gobain Ceramics & Plastics, Inc. Particulate materials and methods of forming same
US10947432B2 (en) 2016-10-25 2021-03-16 3M Innovative Properties Company Magnetizable abrasive particle and method of making the same
US11027397B2 (en) 2016-12-23 2021-06-08 Saint-Gobain Abrasives, Inc. Coated abrasives having a performance enhancing composition
US11072732B2 (en) 2016-10-25 2021-07-27 3M Innovative Properties Company Magnetizable abrasive particles and abrasive articles including them
US11230653B2 (en) 2016-09-29 2022-01-25 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11253972B2 (en) 2016-10-25 2022-02-22 3M Innovative Properties Company Structured abrasive articles and methods of making the same
US11607776B2 (en) 2016-07-20 2023-03-21 3M Innovative Properties Company Shaped vitrified abrasive agglomerate, abrasive articles, and method of abrading
US11718774B2 (en) 2016-05-10 2023-08-08 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
US11794307B2 (en) 2017-04-28 2023-10-24 3M Innovative Properties Company Large denier nonwoven fiber webs
US11926019B2 (en) 2019-12-27 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles and methods of forming same
US11959009B2 (en) 2016-05-10 2024-04-16 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9073179B2 (en) 2010-11-01 2015-07-07 3M Innovative Properties Company Laser method for making shaped ceramic abrasive particles, shaped ceramic abrasive particles, and abrasive articles
CA2847807C (fr) 2011-09-07 2019-12-03 3M Innovative Properties Company Procede d'abrasion d'une piece a travailler
CN104114664B (zh) 2011-12-30 2016-06-15 圣戈本陶瓷及塑料股份有限公司 形成成型研磨颗粒
PL2797716T3 (pl) 2011-12-30 2021-07-05 Saint-Gobain Ceramics & Plastics, Inc. Kompozytowe ukształtowane cząstki ścierne i sposób ich formowania
MX350057B (es) 2012-04-04 2017-08-25 3M Innovative Properties Co Partículas abrasivas, método para producir partículas abrasivas y artículos abrasivos.
KR102146313B1 (ko) 2012-10-31 2020-08-21 쓰리엠 이노베이티브 프로퍼티즈 컴파니 성형 연마 입자, 그의 제조 방법, 및 그를 포함하는 연마 용품
MX2015011535A (es) * 2013-03-04 2016-02-05 3M Innovative Properties Co Articulo abrasivo no tejido que contiene particulas abrasivas conformadas.
US10414023B2 (en) 2013-03-29 2019-09-17 3M Innovative Properties Company Nonwoven abrasive articles and methods of making the same
KR102305255B1 (ko) * 2014-08-27 2021-09-28 쓰리엠 이노베이티브 프로퍼티즈 컴파니 연마 용품을 제조하는 방법 및 연마 용품
BR112017007263A2 (pt) * 2014-10-07 2017-12-19 3M Innovative Properties Co ?artigo abrasivo texturizado e métodos relacionados?
KR20170091663A (ko) 2014-12-01 2017-08-09 쓰리엠 이노베이티브 프로퍼티즈 컴파니 수분 배리어 층을 갖는 부직포 연마 휠
CN106112836A (zh) * 2016-06-27 2016-11-16 宁夏中卫大河精工机械有限责任公司 一种超硬集聚粒磨料及由其制作而成的超硬珩磨油石
CN106965101B (zh) * 2017-04-06 2019-01-08 湖北明仁研磨科技股份有限公司 一种砂纸基材抗裂处理方法
US11642756B2 (en) 2017-07-14 2023-05-09 3M Innovative Properties Company Abrasive article with anionic water solubilizing material and method of making
EP3829816A1 (fr) * 2018-07-30 2021-06-09 3M Innovative Properties Company Articles de polissage autonomes

Citations (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1953983A (en) * 1928-02-07 1934-04-10 Carborundum Co Manufacture of rubber bonded abrasive articles
US3982359A (en) * 1968-06-21 1976-09-28 Roc A.G. Abrasive member of bonded aggregates in an elastomeric matrix
US4459779A (en) * 1982-09-16 1984-07-17 International Business Machines Corporation Fixed abrasive grinding media
US5201916A (en) * 1992-07-23 1993-04-13 Minnesota Mining And Manufacturing Company Shaped abrasive particles and method of making same
US5562745A (en) * 1994-03-16 1996-10-08 Minnesota Mining And Manufacturing Company Abrasive articles, methods of making abrasive articles, and methods of using abrasive articles
US5692950A (en) * 1996-08-08 1997-12-02 Minnesota Mining And Manufacturing Company Abrasive construction for semiconductor wafer modification
US5942015A (en) * 1997-09-16 1999-08-24 3M Innovative Properties Company Abrasive slurries and abrasive articles comprising multiple abrasive particle grades
US6186866B1 (en) * 1998-08-05 2001-02-13 3M Innovative Properties Company Abrasive article with separately formed front surface protrusions containing a grinding aid and methods of making and using
US6383238B1 (en) * 1999-08-17 2002-05-07 Mitsubishi Materials Corporation Resin bonded abrasive tool
US6390890B1 (en) * 1999-02-06 2002-05-21 Charles J Molnar Finishing semiconductor wafers with a fixed abrasive finishing element
US6478977B1 (en) * 1995-09-13 2002-11-12 Hitachi, Ltd. Polishing method and apparatus
US20030205003A1 (en) * 2000-03-23 2003-11-06 Carman Lee A. Vitrified bonded abrasive tools
US20040144037A1 (en) * 2002-11-06 2004-07-29 Carter Christopher J. Abrasive articles and method of making and using the articles
US20040185754A1 (en) * 2003-03-20 2004-09-23 Adefris Negus B Abrasive article with agglomerates and method of use
US20060156634A1 (en) * 2002-07-26 2006-07-20 3M Innovative Properties Company Method of using abrasive product
US7108587B2 (en) * 2004-05-03 2006-09-19 3M Innovative Properties Company Backup shoe for microfinishing and methods
US20070026754A1 (en) * 2003-04-25 2007-02-01 Carmen Martin Rivera Scouring material
US20070037501A1 (en) * 2005-08-11 2007-02-15 Saint-Gobain Abrasives, Inc. Abrasive tool
US20070298240A1 (en) * 2006-06-22 2007-12-27 Gobena Feben T Compressible abrasive article
US20080127572A1 (en) * 2006-12-04 2008-06-05 3M Innovative Properties Company Nonwoven abrasive articles and methods of making the same
WO2010040472A2 (fr) * 2008-10-10 2010-04-15 Center For Abrasives And Refractories Research & Development C.A.R.R.D. Gmbh Agglomérats de grains abrasifs, leur procédé de fabrication et leur utilisation pour la fabrication d’abrasifs
US20100092746A1 (en) * 2008-10-14 2010-04-15 Jean-Marie Coant Nonwoven material containing benefiting particles and method of making
US20120227333A1 (en) * 2009-12-02 2012-09-13 Adefris Negus B Dual tapered shaped abrasive particles

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1752612C2 (de) * 1968-06-21 1985-02-07 Roc AG, Zug Schleifkörper
DE2813258C2 (de) * 1978-03-28 1985-04-25 Sia Schweizer Schmirgel- & Schleifindustrie Ag, Frauenfeld Schleifkörper
US5366523A (en) 1992-07-23 1994-11-22 Minnesota Mining And Manufacturing Company Abrasive article containing shaped abrasive particles
US5372620A (en) 1993-12-13 1994-12-13 Saint Gobain/Norton Industrial Ceramics Corporation Modified sol-gel alumina abrasive filaments
EP0912294B1 (fr) * 1996-05-03 2003-04-16 Minnesota Mining And Manufacturing Company Articles abrasifs en non-tisse
DE19727104C2 (de) * 1997-06-26 2000-07-20 Ver Schmirgel & Maschf Flexibler Schleifkörper und Verfahren zu seiner Herstellung
US5984998A (en) 1997-11-14 1999-11-16 American Iron And Steel Institute Method and apparatus for off-gas composition sensing
US6056794A (en) * 1999-03-05 2000-05-02 3M Innovative Properties Company Abrasive articles having bonding systems containing abrasive particles
US6352567B1 (en) * 2000-02-25 2002-03-05 3M Innovative Properties Company Nonwoven abrasive articles and methods
WO2002032832A1 (fr) * 2000-10-16 2002-04-25 3M Innovative Properties Company Procede de fabrication de particules agglomerees abrasives, et articles abrasifs fabriques a partir de celles-ci
CN1490347A (zh) * 2002-10-18 2004-04-21 廉长江 一种聚氨酯胶软体砂轮磨盘
US6802878B1 (en) * 2003-04-17 2004-10-12 3M Innovative Properties Company Abrasive particles, abrasive articles, and methods of making and using the same
EP1838497B1 (fr) * 2004-12-30 2016-07-13 3M Innovative Properties Company Article abrasif et procedes de fabrication
WO2009039348A1 (fr) * 2007-09-19 2009-03-26 Rotter Martin J Tampons de nettoyage avec filaments abrasifs et agent antimicrobien
US8123828B2 (en) 2007-12-27 2012-02-28 3M Innovative Properties Company Method of making abrasive shards, shaped abrasive particles with an opening, or dish-shaped abrasive particles
WO2009085841A2 (fr) 2007-12-27 2009-07-09 3M Innovative Properties Company Particules abrasives formées fracturées, article abrasif les utilisant, et leur procédé de fabrication
US10137556B2 (en) 2009-06-22 2018-11-27 3M Innovative Properties Company Shaped abrasive particles with low roundness factor
US8142891B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Dish-shaped abrasive particles with a recessed surface
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
US8142532B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with an opening
JP5525546B2 (ja) 2008-12-17 2014-06-18 スリーエム イノベイティブ プロパティズ カンパニー 溝を有する成形された研磨粒子

Patent Citations (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1953983A (en) * 1928-02-07 1934-04-10 Carborundum Co Manufacture of rubber bonded abrasive articles
US3982359A (en) * 1968-06-21 1976-09-28 Roc A.G. Abrasive member of bonded aggregates in an elastomeric matrix
US4459779A (en) * 1982-09-16 1984-07-17 International Business Machines Corporation Fixed abrasive grinding media
US5201916A (en) * 1992-07-23 1993-04-13 Minnesota Mining And Manufacturing Company Shaped abrasive particles and method of making same
US5562745A (en) * 1994-03-16 1996-10-08 Minnesota Mining And Manufacturing Company Abrasive articles, methods of making abrasive articles, and methods of using abrasive articles
US6478977B1 (en) * 1995-09-13 2002-11-12 Hitachi, Ltd. Polishing method and apparatus
US5692950A (en) * 1996-08-08 1997-12-02 Minnesota Mining And Manufacturing Company Abrasive construction for semiconductor wafer modification
US5942015A (en) * 1997-09-16 1999-08-24 3M Innovative Properties Company Abrasive slurries and abrasive articles comprising multiple abrasive particle grades
US6186866B1 (en) * 1998-08-05 2001-02-13 3M Innovative Properties Company Abrasive article with separately formed front surface protrusions containing a grinding aid and methods of making and using
US6390890B1 (en) * 1999-02-06 2002-05-21 Charles J Molnar Finishing semiconductor wafers with a fixed abrasive finishing element
US6383238B1 (en) * 1999-08-17 2002-05-07 Mitsubishi Materials Corporation Resin bonded abrasive tool
US20030205003A1 (en) * 2000-03-23 2003-11-06 Carman Lee A. Vitrified bonded abrasive tools
US20060156634A1 (en) * 2002-07-26 2006-07-20 3M Innovative Properties Company Method of using abrasive product
US20040144037A1 (en) * 2002-11-06 2004-07-29 Carter Christopher J. Abrasive articles and method of making and using the articles
US20040185754A1 (en) * 2003-03-20 2004-09-23 Adefris Negus B Abrasive article with agglomerates and method of use
US20070026754A1 (en) * 2003-04-25 2007-02-01 Carmen Martin Rivera Scouring material
US7108587B2 (en) * 2004-05-03 2006-09-19 3M Innovative Properties Company Backup shoe for microfinishing and methods
US20070037501A1 (en) * 2005-08-11 2007-02-15 Saint-Gobain Abrasives, Inc. Abrasive tool
US20070298240A1 (en) * 2006-06-22 2007-12-27 Gobena Feben T Compressible abrasive article
US20080127572A1 (en) * 2006-12-04 2008-06-05 3M Innovative Properties Company Nonwoven abrasive articles and methods of making the same
WO2010040472A2 (fr) * 2008-10-10 2010-04-15 Center For Abrasives And Refractories Research & Development C.A.R.R.D. Gmbh Agglomérats de grains abrasifs, leur procédé de fabrication et leur utilisation pour la fabrication d’abrasifs
US20110183142A1 (en) * 2008-10-10 2011-07-28 Center For Abrasive And Refractories Research & Development C.A.R.R.D. Ghmbh Abrasive grain agglomerates, process for the production thereof and the use thereof for producing abrasives
US20100092746A1 (en) * 2008-10-14 2010-04-15 Jean-Marie Coant Nonwoven material containing benefiting particles and method of making
US20120227333A1 (en) * 2009-12-02 2012-09-13 Adefris Negus B Dual tapered shaped abrasive particles

Cited By (86)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9017439B2 (en) 2010-12-31 2015-04-28 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US8986409B2 (en) 2011-06-30 2015-03-24 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles including abrasive particles of silicon nitride
US9598620B2 (en) 2011-06-30 2017-03-21 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles including abrasive particles of silicon nitride
US8840694B2 (en) 2011-06-30 2014-09-23 Saint-Gobain Ceramics & Plastics, Inc. Liquid phase sintered silicon carbide abrasive particles
US9303196B2 (en) 2011-06-30 2016-04-05 Saint-Gobain Ceramics & Plastics, Inc. Liquid phase sintered silicon carbide abrasive particles
US9517546B2 (en) 2011-09-26 2016-12-13 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles including abrasive particulate materials, coated abrasives using the abrasive particulate materials and methods of forming
US11453811B2 (en) 2011-12-30 2022-09-27 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
US9765249B2 (en) 2011-12-30 2017-09-19 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
US10428255B2 (en) 2011-12-30 2019-10-01 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
US11649388B2 (en) 2012-01-10 2023-05-16 Saint-Gobain Cermaics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US11142673B2 (en) 2012-01-10 2021-10-12 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US9238768B2 (en) 2012-01-10 2016-01-19 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US10364383B2 (en) 2012-01-10 2019-07-30 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US9567505B2 (en) 2012-01-10 2017-02-14 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US11859120B2 (en) 2012-01-10 2024-01-02 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having an elongated body comprising a twist along an axis of the body
US10106715B2 (en) 2012-01-10 2018-10-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US9771506B2 (en) 2012-01-10 2017-09-26 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US8840696B2 (en) 2012-01-10 2014-09-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9676980B2 (en) 2012-01-10 2017-06-13 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9242346B2 (en) 2012-03-30 2016-01-26 Saint-Gobain Abrasives, Inc. Abrasive products having fibrillated fibers
US9688893B2 (en) 2012-05-23 2017-06-27 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US10000676B2 (en) 2012-05-23 2018-06-19 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US9200187B2 (en) 2012-05-23 2015-12-01 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US9428681B2 (en) 2012-05-23 2016-08-30 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US10106714B2 (en) 2012-06-29 2018-10-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having particular shapes and methods of forming such particles
US11154964B2 (en) 2012-10-15 2021-10-26 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US11148254B2 (en) 2012-10-15 2021-10-19 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US10286523B2 (en) 2012-10-15 2019-05-14 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9440332B2 (en) 2012-10-15 2016-09-13 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9676982B2 (en) 2012-12-31 2017-06-13 Saint-Gobain Ceramics & Plastics, Inc. Particulate materials and methods of forming same
US9074119B2 (en) 2012-12-31 2015-07-07 Saint-Gobain Ceramics & Plastics, Inc. Particulate materials and methods of forming same
US10668598B2 (en) 2013-03-29 2020-06-02 Saint-Gobain Abrasives, Inc./Saint-Gobain Abrasifs Abrasive particles having particular shapes and methods of forming such particles
US11590632B2 (en) 2013-03-29 2023-02-28 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US10179391B2 (en) 2013-03-29 2019-01-15 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US9457453B2 (en) 2013-03-29 2016-10-04 Saint-Gobain Abrasives, Inc./Saint-Gobain Abrasifs Abrasive particles having particular shapes and methods of forming such particles
US9604346B2 (en) 2013-06-28 2017-03-28 Saint-Gobain Cermaics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10563106B2 (en) 2013-09-30 2020-02-18 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US9783718B2 (en) 2013-09-30 2017-10-10 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and methods of forming same
US9566689B2 (en) 2013-12-31 2017-02-14 Saint-Gobain Abrasives, Inc. Abrasive article including shaped abrasive particles
US11091678B2 (en) 2013-12-31 2021-08-17 Saint-Gobain Abrasives, Inc. Abrasive article including shaped abrasive particles
US10597568B2 (en) 2014-01-31 2020-03-24 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US9771507B2 (en) 2014-01-31 2017-09-26 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US11926781B2 (en) 2014-01-31 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US9803119B2 (en) 2014-04-14 2017-10-31 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11891559B2 (en) 2014-04-14 2024-02-06 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US10557067B2 (en) 2014-04-14 2020-02-11 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US9902045B2 (en) 2014-05-30 2018-02-27 Saint-Gobain Abrasives, Inc. Method of using an abrasive article including shaped abrasive particles
US11926780B2 (en) 2014-12-23 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US9914864B2 (en) 2014-12-23 2018-03-13 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US11608459B2 (en) 2014-12-23 2023-03-21 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US9707529B2 (en) 2014-12-23 2017-07-18 Saint-Gobain Ceramics & Plastics, Inc. Composite shaped abrasive particles and method of forming same
US10351745B2 (en) 2014-12-23 2019-07-16 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US9676981B2 (en) 2014-12-24 2017-06-13 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle fractions and method of forming same
US10196551B2 (en) 2015-03-31 2019-02-05 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11472989B2 (en) 2015-03-31 2022-10-18 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US9938440B2 (en) 2015-03-31 2018-04-10 Saint-Gobain Abrasives, Inc./Saint-Gobain Abrasifs Fixed abrasive articles and methods of forming same
US10358589B2 (en) 2015-03-31 2019-07-23 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11643582B2 (en) 2015-03-31 2023-05-09 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US10711171B2 (en) 2015-06-11 2020-07-14 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11879087B2 (en) 2015-06-11 2024-01-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11718774B2 (en) 2016-05-10 2023-08-08 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
US11959009B2 (en) 2016-05-10 2024-04-16 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
US20190202032A1 (en) * 2016-07-01 2019-07-04 3M Innovative Properties Company Nonwoven abrasive article including abrasive particles
US11607776B2 (en) 2016-07-20 2023-03-21 3M Innovative Properties Company Shaped vitrified abrasive agglomerate, abrasive articles, and method of abrading
US11230653B2 (en) 2016-09-29 2022-01-25 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US10655038B2 (en) 2016-10-25 2020-05-19 3M Innovative Properties Company Method of making magnetizable abrasive particles
US11253972B2 (en) 2016-10-25 2022-02-22 3M Innovative Properties Company Structured abrasive articles and methods of making the same
US11478899B2 (en) 2016-10-25 2022-10-25 3M Innovative Properties Company Shaped vitrified abrasive agglomerate with shaped abrasive particles, abrasive articles, and related methods
WO2018081246A1 (fr) 2016-10-25 2018-05-03 3M Innovative Properties Company Agglomérat abrasif vitrifié façonné à particules abrasives façonnées, articles abrasifs et procédés associés
US11072732B2 (en) 2016-10-25 2021-07-27 3M Innovative Properties Company Magnetizable abrasive particles and abrasive articles including them
US10947432B2 (en) 2016-10-25 2021-03-16 3M Innovative Properties Company Magnetizable abrasive particle and method of making the same
CN109890564A (zh) * 2016-10-25 2019-06-14 3M创新有限公司 具有成形磨粒的成形玻璃化磨料团聚物、磨料制品和相关方法
US11027397B2 (en) 2016-12-23 2021-06-08 Saint-Gobain Abrasives, Inc. Coated abrasives having a performance enhancing composition
US10759024B2 (en) 2017-01-31 2020-09-01 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11427740B2 (en) 2017-01-31 2022-08-30 Saint-Gobain Ceramics & Plastics, Inc. Method of making shaped abrasive particles and articles comprising forming a flange from overfilling
US10563105B2 (en) 2017-01-31 2020-02-18 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11932802B2 (en) 2017-01-31 2024-03-19 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles comprising a particular toothed body
US11549040B2 (en) 2017-01-31 2023-01-10 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles having a tooth portion on a surface
US11794307B2 (en) 2017-04-28 2023-10-24 3M Innovative Properties Company Large denier nonwoven fiber webs
US10865148B2 (en) 2017-06-21 2020-12-15 Saint-Gobain Ceramics & Plastics, Inc. Particulate materials and methods of forming same
WO2019167022A1 (fr) 2018-03-01 2019-09-06 3M Innovative Properties Company Aggloméré abrasif siliceux façonné comportant des particules abrasives façonnées, articles abrasifs, et procédés associés
US20210002533A1 (en) * 2018-03-01 2021-01-07 3M Innovative Properties Company Shaped siliceous abrasive agglomerate with shaped abrasive particles, abrasive articles, and related methods
US12006464B2 (en) * 2018-03-01 2024-06-11 3M Innovative Properties Company Shaped siliceous abrasive agglomerate with shaped abrasive particles, abrasive articles, and related methods
WO2020021457A1 (fr) 2018-07-23 2020-01-30 3M Innovative Properties Company Articles comprenant un support en polyester et une couche d'apprêt, et procédés associés
US11945076B2 (en) 2018-07-23 2024-04-02 3M Innovative Properties Company Articles including polyester backing and primer layer and related methods
US11926019B2 (en) 2019-12-27 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles and methods of forming same

Also Published As

Publication number Publication date
JP6000333B2 (ja) 2016-09-28
ES2633316T3 (es) 2017-09-20
JP2014514173A (ja) 2014-06-19
EP2697416A4 (fr) 2014-10-01
EP2697416B1 (fr) 2017-05-10
RU2013145788A (ru) 2015-05-20
CN103476979B (zh) 2016-01-06
PL2697416T3 (pl) 2017-09-29
WO2012141905A3 (fr) 2012-12-27
WO2012141905A2 (fr) 2012-10-18
BR112013026334A2 (pt) 2016-12-27
CN103476979A (zh) 2013-12-25
EP2697416A2 (fr) 2014-02-19
KR20140024884A (ko) 2014-03-03

Similar Documents

Publication Publication Date Title
US20140080393A1 (en) Nonwoven abrasive article containing elastomer bound agglomerates of shaped abrasive grain
US6352567B1 (en) Nonwoven abrasive articles and methods
US5928070A (en) Abrasive article comprising mullite
US5919549A (en) Abrasive articles and method for the manufacture of same
US10625400B2 (en) Nonwoven abrasive article containing formed abrasive particles
EP2106329B1 (fr) Articles abrasifs non tissés et leurs procédés de réalisation
KR20130038912A (ko) 부직포 연마 휠
US20240042578A1 (en) Large denier nonwoven fiber webs
MXPA97002111A (en) Mix abrasive products
US20190202032A1 (en) Nonwoven abrasive article including abrasive particles
CN110869167A (zh) 具有水增溶性阴离子材料的磨料制品及其制造方法
JP2003523837A (ja) 不織布研磨物品および製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: 3M INNOVATIVE PROPERTIES COMPANY, MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:LUDWIG, BRET W.;REEL/FRAME:031380/0393

Effective date: 20130910

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION