US20100110612A1 - Electrode for energy storage device - Google Patents
Electrode for energy storage device Download PDFInfo
- Publication number
- US20100110612A1 US20100110612A1 US12/445,294 US44529407A US2010110612A1 US 20100110612 A1 US20100110612 A1 US 20100110612A1 US 44529407 A US44529407 A US 44529407A US 2010110612 A1 US2010110612 A1 US 2010110612A1
- Authority
- US
- United States
- Prior art keywords
- current collector
- electrode
- energy storage
- storage device
- voids
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims the benefit of U.S. provisional application No. 60/852,459, filed by Linda Zhong and Xiaomei Xi on 17 Oct. 2006, which is hereby incorporated by reference as though fully set forth herein.
- The present invention relates generally to the field of energy storage devices. More particularly, the present invention relates to current collectors and electrodes for energy storage devices.
- Energy storage devices that are used to power modern technology are numerous. Such energy storage devices include capacitors, batteries, and fuel cells. With each type of device are associated positive and negative characteristics. Based on these characteristics, decisions are made as to which device is more suitable for use in a particular application. Overall performance of a device is an important characteristic that can make or break a decision as to whether a particular type of device is used.
- Many energy storage device configurations comprise the formation a stack or roll of electrode layers. This roll or stack of electrode layers is impregnated with an electrolyte and placed within a sealed container with electrical terminals connected to respective electrodes.
- Double-layer capacitors, also referred to as ultracapacitors and super-capacitors, are one type of energy storage device. Double-layer capacitors are able to store more energy per unit weight and unit volume than capacitors made with traditional technology. Double-layer capacitors store electrostatic energy in a polarized electrode/electrolyte interface layer. Double-layer capacitors include two electrodes, which are separated from contact by a porous separator. The separator prevents an electronic (as opposed to an ionic) current from shorting the two electrodes. Both the electrodes and the porous separator are immersed in an electrolyte, which allows flow of the ionic current between the electrodes and through the separator. At the electrode/electrolyte interface, a first layer of charged species is formed, and a second layer is charged species is formed in a solvent dipole (hence, the name “double-layer” capacitor).
- Improvements in impregnation and performance of electrodes used in energy storage devices, such as batteries, fuel cells, and double layer capacitors, is provided.
- An energy storage device comprising a current collector disposed adjacent to an electrode is provided. The current collector comprises a plurality of voids extending through the current collector to allow electrolyte and ions of the electrolyte to flow through the current collector to the adjacent electrode to impregnate the electrode and to shorten ion travel distance preventing or reducing localized electrolyte starvation within an energy storage device.
- In one embodiment, the current collector comprises a ratio of a surface area of a solid surface of the current collector to a total surface area of the current collector is at least about fifty percent. In another embodiment, the current collector comprises a ratio of a surface area of a solid surface of the current collector to a total surface area of the current collector is at least about eighty percent. In one example, the ratio of a solid surface of the current collector to a total surface area of the current collector is at least about ninety percent.
- In another embodiment, the plurality of voids of the current collector is formed without substantially reducing a surface area of a conductive material of the current collector. The plurality of voids, for example, may comprise a plurality of perforations and/or a plurality of slits extending through the thickness of the current collector.
- In one embodiment, a double layer capacitor comprises an electrode comprising a solid current collector and a porous electrode. The solid current collector comprises a plurality of voids extending through a thickness of the current collector.
- A method of preparing an electrode and current collector product is also provided. The method comprises providing an electrode; providing a current collector; disposing the current collector adjacent to the electrode; and creating a plurality of voids extending through a thickness of the current collector without reducing a surface area of the current collector by more than about fifty percent. In one embodiment, the plurality of voids are formed without reducing a surface area of the current collector disposed adjacent to the electrode by no more than about forty percent. In another embodiment, the plurality of voids are formed without reducing a surface area of the current collector disposed adjacent to the electrode by no more than about thirty percent, no more than about twenty percent, or no more than about ten percent. In one embodiment, the operation of creating a plurality of voids comprises perforating the current collector. In another embodiment, the operation of creating a plurality of voids comprises slitting the current collector. In yet another embodiment, the operation of creating comprises punching out portions of the current collector.
-
FIG. 1 is a block diagram illustrating a process for making a particle based energy storage device. -
FIG. 2 illustrates an apparatus used for forming one or more energy device structure. -
FIG. 3 illustrates an apparatus used to bond an electrode film to a current collector. -
FIG. 4 a illustrates an electrode. -
FIG. 4 b illustrates a jellyroll. -
FIG. 5 illustrates a jellyroll inserted into an open end of a housing. -
FIG. 6 illustrates capacitance vs. number of full charge/discharge charge cycle tests of a prior artenergy storage device 5 and anenergy storage device 6. -
FIG. 7 illustrates an embodiment of a current collector comprising a plurality of perforations extending through a thickness of the current collector. -
FIG. 8 illustrates an embodiment of a current collector comprising a plurality of slits extending through a thickness of the current collector. -
FIG. 9 , for example, shows two embodiments of pin patterns that may be used with a perforator. -
FIG. 10 shows one example of a perforator roll. - Reference will now be made in detail to embodiments of the invention that are illustrated in the accompanying drawings. Wherever possible, same or similar reference numerals are used to refer to same or similar steps and/or elements used therein.
- As the number of electrode layers of an energy storage device increases, different factors can affect performance of the energy storage device. One factor is the ability of the stack or roll of electrode layers to be impregnated with electrolyte. As the dimensions of a stack or roll of electrode layers increases, adequate impregnation becomes more difficult to achieve. Energy storage devices often include a solid layer, such as a current collector foil that runs substantially a length and a width of an electrode of an energy storage cell.
- In order to impregnate the electrode of the energy storage cell, the electrolyte follows an impregnation path through the cell. In a jelly roll configuration of an energy storage cell, for example, a solid current collector within the roll may prevent the electrolyte from reaching sections of the electrodes except through one or both of the longitudinal ends of the cell. The electrolyte thus impregnates the electrodes of the cell by traveling through the end(s) of the cell. Sometimes such a tortuous impregnation path results in dry locations of the electrode where electrolyte does not impregnate the entire electrode. The longer path also affects ion migration within the electrolyte during charge—discharge cycles and can lead to localized electrolyte starvation where ions are trapped and cannot migrate to certain areas of the electrode.
- While a mesh wire current collector may allow electrolyte to flow through the current collector to impregnate an electrode, the mesh wire of the current collector provides a significant increase in equivalent series resistance (ESR) due to the decrease in surface area of the collector making contact with the electrode. Thus, electrons within the electrode must travel farther within a less conductive electrode than if the current collector covered more of the surface area of the adjacent electrode.
- In addition, as the energy storage devices cycle through charge—discharge cycles, ions of electrolyte located within small locations in or near the electrodes may migrate away from active materials of the electrodes. The migration of these ions away from a particular region of the electrode may leave a region of the electrolyte with fewer ions than desired. Such a shortage of ions may lead to a condition of local electrolyte starvation. Local electrolyte starvation will lead to a decrease in capacity of an energy storage device. In a double layer capacitor, for example, electrolyte starvation may contribute to a decrease in capacitance or a “capacitance fade.”
- Providing voids extending through a substantially solid current collector improves impregnation and shortens ion travel distance to prevent or reduce localized electrolyte starvation within an energy storage device.
- Although particular embodiments are described including improved impregnation and performance of electrodes in double-layer capacitors, those skilled in the art will identify from this disclosure that these principles also find applicability with capacitors, batteries, fuel cells, hybrid cells, and other types of energy storage devices that utilize stacked or rolled electrodes.
-
FIG. 1 , described below, provides merely one example of an electrode film and a process for forming that electrode film that may be used in combination with a current collector having a plurality of voids extending through a thickness of the current collector to allow electrolyte to pass through the current collector. The film described with reference toFIG. 1 , for example, can be used in a double layer capacitor. Other types of electrode film both for double layer capacitors and other energy storage devices are contemplated and would be recognized by one of ordinary skill in the art after reviewing this disclosure. In addition, other processing methods may be used. - Referring now to
FIG. 1 , a block diagram illustrating an example of one type of process for making a particle based film for an energy storage device is shown. The process shown inFIG. 1 begins by blending activatedcarbon particles 12 andbinder 16 together. Optionally,conductive particles 14 may also be blended together with the activatedcarbon particles 12 and thebinder 16. The activatedcarbon particles 12, conductive particles 14 (where used), and thebinder 16 may be blended together with or without any processing aides or additives, such as used in coating or extruding processes (hereafter referred throughout as “processing additive” and “additive”), including without limitation: added solvents, liquids, lubricants, plasticizers, and the like. - Where no processing additives are used, for example, dry activated carbon, dry binder, and dry conductive carbon (where used) can be combined and processed dry without any additives that may later need to be removed (e.g., via a drying step). In other embodiments, such processing additives may be added to the activated carbon, binder, and conductive particles (where used). In such embodiments, for example, it will be understood by those skilled in the art that electrode films may be made by extrusion, coating and other processes known to those skilled in the art. While such additives can be utilized in the manufacture of an electrode for an energy storage device, the operating lifetime, and maximum operating voltage of the energy storage device may become reduced, for example, because of undesirable chemical interactions that may occur between residues of the additive(s) and a subsequently used electrolyte.
- In one embodiment,
dry binder 16 refers to particles of an inert dry binder. In one embodiment,conductive particles 14 comprise at least one of dry conductive graphite particles, an electrically conductive polymer, a metal powder, or the like. In one embodiment,binder 16 comprises a fibrillizable flouropolymer, for example, polytetrafluoroethylene (PTFE) particles. Other possible fibrillizable binders include ultra-high molecular weight polypropylene, polyethylene, co-polymers, polymer blends, and the like. It is understood that other active materials, binder, and optional conductive materials may also be used. In one embodiment, particular mixtures of activatedcarbon particles 12,conductive particles 14, andbinder 16 comprise about 50% to 99% activated carbon, about 0% to 30% conductive carbon, and/or about 1% to 50% binder weight. In a more particular embodiment, particle mixtures include about 80% to 90% activated carbon, about 0% to 15% conductive carbon, and about 3% to 15% binder weight. In other embodiments, one or more of the particles may comprise, for example, carbon, graphite, intercalated carbon, conductive carbon, catalyst impregnated carbon, metal, metal oxide, manganese dioxide, thermoplastic, homo and copolymers, olefinic oxides, rubbers, butadiene rubbers, nitrile rubbers, polyisobutylene, poly(vinylesters), poly(vinylacetates) polyacrylate, fluorocarbon polymers, non-fibrillizable binder, thermoset particles, radiations set particles, thermoplastic, and/or other particles. Suitable particles are available from a variety of sources as would be known to those skilled in the art. - In
step 18, particles of activated carbon, conductive carbon, and binder provided byrespective operations carbon 12, the conductive particles 14 (where used), and thebinder 16 without any processing additives or may include any dry or wet processing additives. In one embodiment, for example, dry activatedcarbon particles 12, dryconductive particles 14, anddry binder 16 are blended for 1 to 10 minutes in a V-blender that is equipped with a high intensity mixing bar, until a uniform dry mixture is formed. Those skilled in the art will identify that blending time can vary based on batch size, materials, particle size, densities, as well as other properties. With reference to blendingoperation 18, in one embodiment, particle size reduction and classification can be carried out as part of the blendingstep 18, or prior to the blendingstep 18. Size reduction and classification may improve consistency and repeatability of the resulting blended mixture and, consequently, of the quality of the electrode films and electrodes fabricated from the dry blended mixture. - In
operation 20 the blended particles undergo an application of impact and shear force. The particles are then fed inoperation 22, and are calendered inoperation 24 to provide a film. The film is bonded to a current collector (as described in further below) in operation 26. - Referring now to
FIG. 2 , and preceding Figures as needed, there is seen one example of an apparatus used for forming one or more film for use as an electrode that may be incorporated into an energy storage device. In one embodiment, dry blended particles (such as fromstep 22 inFIG. 1 ) are provided to adevice 41, which compacts and/or calenders the particles to form them into a dry film. The compacting and/or calendaring function provided bydevice 41 can be achieved by a roll-mill, calendar, a belt press, a flat plate press, and the like, as well as others known to those skilled in the art. Thus, although shown in a particular configuration, those skilled in the art will understand that variations and other embodiments ofdevice 41 could be provided to achieve one or more of the benefits and advantages described herein, which should be limited only by the claims that follow. In one embodiment, a resulting compacteddry film 34 exits from a first roll-mill 32 and may become self-supporting after only one compacting pass through the roll-mill 32. - Particular dry films may comprise, for example, lengths of any desired length, thickness between about 10 μm to 2 mm, and widths from on the order to meters to 10 mm or smaller. In one embodiment, a width is about 30 mm and a thickness is about 150 μm. The ability to provide a self-supporting film differs from that of some films where folding/kneading steps and/or multiple compacting/calendering steps are used to strengthen films to give them the tensile strength needed for subsequent handling and processing. Because a dry film provided herein can be sufficiently self-supporting after one pass through a roll-
mill 32, it can easily and quickly be formed into a long integral continuous sheet, which can be rolled for subsequent use in a commercial scale manufacture process. A dry film can be formed as a self-supporting sheet that is limited in length only by the capacity of the rewinding equipment. Thus, compared to some prior art additive based films, which are described as non-self supporting and/or as small finite area films, the dry self-supporting films described herein are more economically suited for large scale commercial manufacture. - The
dry film 34 can be separated from the roll-mill 32 using a doctor blade, or the edge of a thin strip of plastic, or other separation material, including metal or paper. Once the leading edge of thedry film 34 is separated, the weight of the self-supporting dry film and film tension can act to separate any remaining exitingdry film 34 from the roll-mill 32. The self-supportingdry film 34 can be fed through atension control system 36 into another set ofrollers 38. Therollers 38 may further compact and densify thedry film 34. Additional calendering steps 40 can be used to further reduce the dry film's thickness and to increase tensile strength. A slittingmachine 44 may then be used to cut the current collector to a desired width before it is wound onto astorage roll 48. - The process shown in
FIG. 2 is merely one example of a process for providing a film for use as an electrode of an energy storage device, such as a battery, fuel cell, or double layer capacitor. Other methods of providing films for electrodes may also be used. For example, a slurry including activated carbon, a conductive material (where used), a binder, and a processing additive may be coated onto a substrate (e.g., a current collector or sacrificial layer) and dried to form the film. In another example, a mixture including activated carbon, conductive material (where used), binder, and a processing additive may be extruded into a film for use as an electrode. - Referring to
FIG. 3 , and preceding Figures as needed, there is seen an apparatus used to bond an electrode film to a current collector. Instep 28, adry film 34 is bonded to an electricallyconductive collector 50. In one embodiment,collector 50 may have deposited thereon one or more layer of adhesive. In one embodiment, thecollector 50 may comprise a foil. In some embodiments, the current collector may comprise an etched or unetched foil or sheet of conductive material or a roughened or unroughened foil or sheet of conductive material. In one embodiment, thecurrent collector 50 comprises a thickness of about 30 microns. Material with other thickness is also within the scope of the invention. Materials with other thickness may also be used. In one embodiment, thecurrent collector 50 comprises aluminum or copper. Those skilled in the art will recognize that if the electrochemical potential allows, the other metals could also be used as acollector 50. - In one embodiment, a
current collector 50 and two dry film(s) 34 are fed from storage rolls 48 into a heated roll-mill 52 such that thecurrent collector 50 is positioned between two self-supportingdry films 34. In one embodiment, thecurrent collector 50 may be pre-heated by aheater 79. In one embodiment, a roll-mill 52 temperature at the nip of the roll is between 100° C. and 300° C. In one embodiment, the nip pressure is selected between 50 pounds per linear inch (PLI) and 1000 PLI. Eachdry film 34 becomes calendered and bonded to a side of thecurrent collector 50. In one embodiment, the resultingdry electrode 54 can be S-wrapped over chill rolls 56 to set thedry film 34 onto thecollector 50. - The
dry electrode 54 can then be collected onto anotherstorage roll 58.Tension control systems 51 can also be employed by the system shown inFIG. 3 . It is identified that other means, methods, and setups for bonding of electrode films to a current collector can be used to form electrodes, as are known to those skilled in the art. For example, in other embodiments, a prior art additive-based electrode film could be bonded to acurrent collector 50. Additive-based electrode films include those made by coating, extrusion, and other processes known to those skilled in the art. -
FIG. 3 further shows aperforator 60 located between the chill rolls 56 and thestorage roll 58. In this embodiment, theperforator 60 perforates the combined electrode andcurrent collector structure 54. Theperforator 60 may, however, be disposed in any other location of the process shown inFIG. 3 . For example, theperforator 60 may be used to perforate the current collector before it is combined with a film electrode (e.g., before it is wound onroll 48, after a coating step, or betweenroll 48 and the heated roll-mill 52). In such an embodiment, the current collector is perforated with the electrode film remaining intact. In another embodiment, theperforator 60 may be used to perforate the combined electrode andcurrent collector structure 54 between the heated roll-mill 52 and the chill rolls 56 or after it has been wound onto thestorage roll 58. - In one embodiment, the
perforator 60 comprises needles having a diameter of approximately 0.78 mm that are arranged in a pattern having a density of about 100 pins per square inch.FIG. 9 , for example, shows twoembodiments FIG. 10 shows one example of aperforator roll 60 a that may be used in theperforator 60 ofFIG. 3 . In one embodiment, the perforator perforates thecurrent collector 50 without substantially diminishing the surface area of the current collector available for contact with the electrode film in order to not substantially increase the equivalent series resistance of the electrode. In one embodiment, the perforation of the current collector results in little or no material being removed from the current collector. In this embodiment, perforations formed in the current collector allow electrolyte and ions to move through the perforations of the current collector but maintain all or at least substantially the same surface are of the current collector available for contact with the adjacent electrode film. Thus, the equivalent series resistance of the electrode and current collector is not increased substantially. - Although a mesh or screen current collector or a current collector with a substantial portion of its surface area removed (e.g., by removing substantial portions of the current collector by punching) may provide for openings through which an electrolyte may flow, such a current collector will provide an increased equivalent series resistance (ESR) because electrons from a portion of the electrode must travel farther through the higher-resistance electrode film to reach an available conductive surface of the current collector.
- In another embodiment, a slitter may be used to slit the
current collector 50 either by itself or in combination with one or more electrode film disposed adjacent to the current collector. Again, a slit in the electrode provides a path for electrolyte and ions to move through the current collector without substantially decreasing the surface area of the current collector available for electrical contact with the electrode film. Any number of patterns or locations of slits may be used to slit the current collector. - In yet another embodiment, voids in the
current collector 50 may be created by other methods, such as by punching relatively small holes in thecurrent collector 50 either by itself or in combination with one or more electrode film disposed adjacent to the current collector. In this embodiment, the surface area of the remaining current collector available for electrical contact with an adjacent electrode is at least fifty percent of the total surface area of the current collector disposed adjacent to the electrode before the holes are punched. In other embodiments, the surface area of the remaining current collector available for electrical contact with an adjacent electrode is at least sixty percent, seventy percent, or eighty percent of the total surface area of the current collector before the holes are punched. In another embodiment, the surface area of the remaining current collector available for electrical contact with an adjacent electrode is at least ninety percent of the total surface area of the current collector before the holes are punched. In yet another embodiment, the surface area of the remaining current collector available for electrical contact with an adjacent electrode is at least ninety-five percent of the total surface area of the current collector before the holes are punched. In another embodiment, the surface area of the remaining current collector available for electrical contact with an adjacent electrode is at least ninety nine percent of the total surface area of the current collector before the holes are punched. - Again, the availability of the remaining conductive surface area of the current collector adjacent to an electrode provides a path for electrolyte and ions to move through the current collector without decreasing the surface area of the current collector available for electrical contact with the electrode film so far as to increase the equivalent series resistance (ESR) of the combined electrode and current collector structure beyond an acceptable point. In one embodiment, for example, the voids formed in the current collector reduce a surface area of a current collector disposed adjacent to an electrode by no more than about fifty percent. In another embodiment, the voids formed in the current collector reduce a surface area of a current collector disposed adjacent to an electrode by no more than about thirty five percent. In yet another embodiment, the voids formed in the current collector reduce a surface area of a current collector disposed adjacent to an electrode by no more than about twenty percent.
- Referring now to
FIG. 4 a, and preceding Figures as needed, structures of an example electrode of an energy storage device, such as a battery, fuel cell, or double layer capacitor are shown. InFIG. 4 a, there are shown cross-sections of fourelectrode films 36, which are bonded to a respectivecurrent collector 50. First surfaces of each of thefilms 36 are coupled to respective surfaces of acurrent collector 50 to form atop electrode 54 andbottom electrode 54. In one embodiment, an electrode includes a top andbottom separator 70. In one embodiment, bonding ofelectrode films 36 to a respective current collector may be enhanced by use of anintermediate adhesive layer 55. In one embodiment,separators 70 may comprise a porous electrically insulating layer or film or paper sheet of about 30 microns in thickness. Separators with other thickness and other material may also be used. In one embodiment, a combination of current collectors, separators, and electrode films disclosed herein is formed into a configuration know by those skilled in the art as a jellyroll. - Referring now to
FIG. 4 b, a jellyroll is shown. In one embodiment, sheets of structures shown inFIG. 4 b are positioned one on top of another and rolled into ajellyroll 1200 type structure such that onecollector 50 extends from one end of the jellyroll and anothercollector 50 extends from an opposing end. The extending ends of thecollectors 50 provide contact points where electrical contact may be made with the jellyroll. - Referring now to
FIG. 5 , and preceding Figures as needed, during manufacture, ajellyroll 1200 made according to one or more of the embodiments disclosed herein is inserted into an open end of ahousing 2000. An insulator (not shown) is placed along a top periphery of thehousing 2000 at the open end, and acover 2002 is placed on the insulator. During manufacture, thehousing 2000, insulator, and cover 2002 may be mechanically curled together to form a tight fit around the periphery of the now sealed end of the housing, which after the curling process is electrically insulated from the cover by the insulator. When disposed in thehousing 2000, respective exposedcollector extensions 1202 ofelectrode 1200 make internal contact with the bottom end of thehousing 2000 and thecover 2002. In one embodiment, external surfaces of thehousing 2000 orcover 2002 may include or be coupled to standardized connections/connectors/terminals to facilitate electrical connection to the rolledelectrode 1200 within thehousing 2000. Contact betweenrespective collector extensions 1202 and the internal surfaces of thehousing 2000 and thecover 2002 may be enhanced by welding, soldering, brazing, conductive adhesive, or the like. In one embodiment, a welding process may be applied to the housing and cover by an externally applied laser welding process. In one embodiment, thehousing 2000,cover 2002, andcollector extensions 1202 comprise substantially the same metal, for example, aluminum. An electrolyte suitable for a desired application or performance characteristic can be added through a filling/sealing port (not shown) to the sealedhousing 1200. After impregnation and sealing, a finished product may, thus, made ready for sale and/or subsequent use. - Referring now to
FIG. 6 , there are seen a graph illustrating capacitance vs. number of full charge/discharge charge cycle tests of anenergy storage device 5 that uses a solid current collector without voids extending through the current collector, and anenergy storage device 6 that uses a current collector including a plurality of slits extending through a thickness of the current collector in order to allow electrolyte and ion movement through the current collector (as shown below inFIG. 8 ). - Those skilled in the art will identify that energy storage devices are typically derated to reflect performance degradation that occurs during initial first use or burn-in. For example, in the prior art, after a first 10000 cycles or so of use, the performance of a 2900 Farad capacitor may become degraded such that it may be able to provide only 2600 Farads of capacitance. Consequently, manufacturers of what would initially be a 2900 Farad double-layer capacitor typically have to rate such capacitors as a nominal 2600 Farads. Such derating of energy storage devices undesirably implicates that performance, manufacturing costs, and/or profits may be needlessly wasted.
- With further reference to
FIG. 6 , an initial capacitance ofdevices devices prior art device 5, and for approximately 12,000 cycles for thedevice 6. As shown, thedevice 5 experienced a drop of about 17% in capacitance over 12,000 full charge cycles, whereasdevice 6 experienced only a drop of about 12% in capacitance. - Referring now to
FIG. 7 , there is seen an embodiment of acurrent collector 50A for use in an energy storage device comprising a plurality ofperforations 62. Thecurrent collector 50A comprises a thickness, a width, and a length. The perforations in thecurrent collector 50A extend through the thickness of thecurrent collector 50A. Theperforations 62 may, for example, be arranged along the width and/or the length of thecurrent collector 50A. In one embodiment, theperforations 62 are formed during or after formation of thecurrent collector 50A, as could be implemented by those skilled in the art. The perforations may also be formed before or after thecurrent collector 50A is combined with at least one electrode film. In one embodiment, theperforations 62 may be formed by cutting or punching (e.g., by perforator needles) through thecurrent collector 50A. In one embodiment, theperforations 62 may be formed by mechanical contact forces as applied by an instrument, or non-mechanically, as by application of a beam of energy. In one embodiment, theperforations 62 may comprise other geometries, for example, circular, oval, elongated, and the like. In one embodiment, theperforations 62 are spaced at equal intervals along the collector length and/or width. In one embodiment, theperforations 62 are spaced at unequal intervals along the length and/or width. In one embodiment, theperforations 62 are centrally disposed between a width of, and along a length of, the collector. In one embodiment, the voids are disposed across the entire surface of thecurrent collector 50A. In one embodiment, one or more of theperforations 62 may be formed after or during calendaring of an electrode film onto the collector. In one embodiment, theperforations 62 are formed in a collector after an electrode film is formed on, or bonded to, a current collector, in which case it is understood that correspondingperforations 62 could, thus, be formed in the electrode film as well. - Referring now to
FIG. 8 , an embodiment of acurrent collector 50B including a plurality ofslits 64 is shown. InFIG. 8 , thecurrent collector 50B comprises a thickness, a width, and a length. In one embodiment, thecurrent collector 50B comprises a plurality ofslits 64 formed by makingslits 64 through the thickness and along the length of thecurrent collector 50B. In one embodiment, the slits are formed by mechanical slitting (e.g., by mechanical contact) or by non-mechanical cutting (e.g., by application of a beam of energy). In one embodiment, theslits 64 are formed during or after formation of thecurrent collector 50B, as could be implemented by those skilled in the art. In one embodiment, theslits 64 are spaced at equal intervals along the collector length and/or width of thecurrent collector 50B. In one embodiment, the voids are spaced at unequal intervals along the length and/or width of thecurrent collector 50B. In one embodiment, theslits 64 are centrally disposed between a width of, and along a length of, the collector. In one embodiment, theslits 64 are disposed across the entire surface of the collector. In one embodiment, one or more of theslits 64 may be formed after or during calendaring of an electrode film onto the collector. In one embodiment, theslits 64 are formed in the current collector after an electrode film is formed on, or bonded to, a collector, in which case it is understood that corresponding slits 64 could, thus, be formed in the electrode film as well. - As described above with respect to
FIG. 6 , a certain amount of capacitance drop is experienced during the first 12,000 cycles of use of adouble layer capacitor 5 including a solid current collector not having a plurality of voids extending through the current collector. The inventors have identified that, at least in part, such capacitance drop is due to unequal distribution of electrolyte within the structures of a jellyroll (i.e. local electrolyte starvation). It has been identified that after 12000 cycle testing of acapacitor 5, when the capacitor is opened, and electrode films used in the manufacture of the capacitor are viewed, many areas of dryness on the electrode films can be visually identified. Such dryness indicates that electrolyte has not sufficiently penetrated within the structures of the capacitor. In the case of a jellyroll type capacitor cell, when electrolyte is introduced within a housing to impregnate the jellyroll, it is desired that electrolyte become evenly distributed within the jellyroll. Without a plurality of voids in a current collector, the impregnation typically occurs by diffusion of electrolyte that starts at the ends of the jellyroll that have exposed collectors, and then inward between the layers of wound electrode films and towards a centermost point within jellyroll. Because the electrode film layers are typically wound under tension, it is identified that the spacing between successive wound electrode layers is reduced. It is identified that as the spacing between layer decreases, adequate diffusion and transport of electrolyte therebetween becomes more difficult to achieve. As well, as a jellyroll diameter and/or width is increased, as when increased capacitance is desired, the distance that electrolyte needs to traverse to achieve complete impregnation of a jellyroll also increases, which further hinder diffusion or transport of electrolyte within a jellyroll. - Improved impregnation of electrode films of energy storage devices is provided. One or more voids formed through a current collector allows for electrolyte to more easily find a path to fully impregnate electrode films and other structures that comprise an electrode. In addition, the plurality of voids formed through the current collector provides for more electrolyte and ion transport per unit of time during cycled use of an energy storage device. In addition to impregnation of electrolyte that may occur through ends an electrode and then through layers of the electrode, impregnation may also occur through surfaces of the current collector. In the case of a jellyroll type electrode design, as well as with flat or stacked electrode designs that are known to those skilled in the art, electrolyte impregnation may, thus, be made to occur through surfaces of an electrode, not just through its ends. For example, after introduction within a housing, electrolyte may diffuse through a plurality of voids formed in a radially outermost portion of a collector and, thereafter, one or more other voids. In this manner, the voids provide a shorter path over which electrolyte diffusion or transport can occur to impregnate electrode structures within a jellyroll. The voids may also provide more paths for impregnation. Shorter and more paths for diffusion and impregnation path implicates that impregnation of one or more electrode structures may occur more quickly and more thoroughly. More efficient and rapid transport reduces in starvation of electrolyte within an energy storage device and, thus, reduces initial capacitance drop that is experienced when such energy storage device is used in a cycled manner. Referring back to
FIG. 6 , there is seen that for adevice 6 that comprises a plurality of slit type voids formed along a collector of a jellyroll type electrode, an initial capacitance drop that is experienced over a first 12000 cycles of use is only about 12%. As compared to thecapacitor 5 without the plurality of voids in the current collector, the reduced capacitance drop means that less capacitor material need be used in anticipation of a nominally specified capacitance, or for a given housing volume, a nominally specified capacitance can be greater. - Thus, the particular systems and methods shown and described herein in detail are capable of attaining the above described objects and advantages of the invention. However, the descriptions and drawings presented herein represent some, but not all, embodiments that have been practiced or that are broadly contemplated. For example, products, structures, and methods that are disclosed may comprise configurations, variations, and dimensions other than those disclosed. In one embodiment, an electro-chemical device made according to principles described herein may comprise two different electrode films that differ in composition and/or dimension (i.e. asymmetric electrodes). Housing and electrode designs may be implemented in coin-cell type, clamshell type, flat or stacked prismatic type, and cylindrical type geometries, as well as others as are known to those skilled in the art. For a particular type of housing, it is understood that appropriate geometrical changes to the embodiments described herein may be needed, but that such changes would be within the scope of those skilled in the art. The present invention should be therefore limited only by the appended claims.
Claims (25)