US20060219786A1 - Marker for coded electronic article identification system - Google Patents

Marker for coded electronic article identification system Download PDF

Info

Publication number
US20060219786A1
US20060219786A1 US11/095,559 US9555905A US2006219786A1 US 20060219786 A1 US20060219786 A1 US 20060219786A1 US 9555905 A US9555905 A US 9555905A US 2006219786 A1 US2006219786 A1 US 2006219786A1
Authority
US
United States
Prior art keywords
marker
coded
strips
coded marker
strip
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/095,559
Other languages
English (en)
Inventor
Ryusuke Hasegawa
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Metglas Inc
Original Assignee
Metglas Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Metglas Inc filed Critical Metglas Inc
Priority to US11/095,559 priority Critical patent/US20060219786A1/en
Assigned to METGLAS, INC. reassignment METGLAS, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HASEGAWA, RUSUKE
Assigned to METGLAS, INC. reassignment METGLAS, INC. RECORD TO CORRECT THE NAME OF THE ASSIGNOR ON THE ASSIGNMENT DOCUMENT PREVIOUSLY RECORD ON REEL 016443, FRAME 0168. THE CORRECT NAME OF THE ASSIGNOR IS HASEGAWA RYUSUKE. Assignors: RYUSUKE, HASEGAWA
Assigned to METGLAS, INC. reassignment METGLAS, INC. CORRECTED COVER SHEET TO CORRECT THE EXECUTION DATE, PREVIOUSLY RECORDED AT REEL/FRAME 016838/0482 (ASSIGNMENT OF ASSIGNOR'S INTEREST) Assignors: HASEGAWA, RYUSUKE
Priority to TW101128803A priority patent/TWI480567B/zh
Priority to TW095110950A priority patent/TWI377507B/zh
Priority to PCT/US2006/011839 priority patent/WO2006107739A2/en
Priority to EP06740152A priority patent/EP1872299B1/en
Priority to KR1020077021146A priority patent/KR100990989B1/ko
Priority to AT06740152T priority patent/ATE535880T1/de
Priority to ES06740152T priority patent/ES2378560T3/es
Priority to CN2006800102314A priority patent/CN101151620B/zh
Priority to JP2008504410A priority patent/JP4778551B2/ja
Publication of US20060219786A1 publication Critical patent/US20060219786A1/en
Priority to US11/607,993 priority patent/US7320433B2/en
Priority to HK08108205.6A priority patent/HK1117618A1/xx
Abandoned legal-status Critical Current

Links

Images

Classifications

    • G—PHYSICS
    • G06—COMPUTING; CALCULATING OR COUNTING
    • G06K—GRAPHICAL DATA READING; PRESENTATION OF DATA; RECORD CARRIERS; HANDLING RECORD CARRIERS
    • G06K19/00—Record carriers for use with machines and with at least a part designed to carry digital markings
    • G06K19/06—Record carriers for use with machines and with at least a part designed to carry digital markings characterised by the kind of the digital marking, e.g. shape, nature, code
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/14—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys
    • H01F1/147—Alloys characterised by their composition
    • H01F1/153—Amorphous metallic alloys, e.g. glassy metals
    • H01F1/15308—Amorphous metallic alloys, e.g. glassy metals based on Fe/Ni
    • G—PHYSICS
    • G06—COMPUTING; CALCULATING OR COUNTING
    • G06K—GRAPHICAL DATA READING; PRESENTATION OF DATA; RECORD CARRIERS; HANDLING RECORD CARRIERS
    • G06K19/00—Record carriers for use with machines and with at least a part designed to carry digital markings
    • G06K19/06—Record carriers for use with machines and with at least a part designed to carry digital markings characterised by the kind of the digital marking, e.g. shape, nature, code
    • G06K19/06187—Record carriers for use with machines and with at least a part designed to carry digital markings characterised by the kind of the digital marking, e.g. shape, nature, code with magnetically detectable marking
    • G06K19/06196—Constructional details
    • G—PHYSICS
    • G06—COMPUTING; CALCULATING OR COUNTING
    • G06K—GRAPHICAL DATA READING; PRESENTATION OF DATA; RECORD CARRIERS; HANDLING RECORD CARRIERS
    • G06K7/00—Methods or arrangements for sensing record carriers, e.g. for reading patterns
    • G06K7/08—Methods or arrangements for sensing record carriers, e.g. for reading patterns by means detecting the change of an electrostatic or magnetic field, e.g. by detecting change of capacitance between electrodes
    • G—PHYSICS
    • G08—SIGNALLING
    • G08B—SIGNALLING OR CALLING SYSTEMS; ORDER TELEGRAPHS; ALARM SYSTEMS
    • G08B13/00—Burglar, theft or intruder alarms
    • G08B13/02—Mechanical actuation
    • G08B13/14—Mechanical actuation by lifting or attempted removal of hand-portable articles
    • G—PHYSICS
    • G08—SIGNALLING
    • G08B—SIGNALLING OR CALLING SYSTEMS; ORDER TELEGRAPHS; ALARM SYSTEMS
    • G08B13/00—Burglar, theft or intruder alarms
    • G08B13/22—Electrical actuation
    • G08B13/24—Electrical actuation by interference with electromagnetic field distribution
    • G08B13/2402—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting
    • G08B13/2405—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting characterised by the tag technology used
    • G08B13/2408—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting characterised by the tag technology used using ferromagnetic tags
    • G—PHYSICS
    • G08—SIGNALLING
    • G08B—SIGNALLING OR CALLING SYSTEMS; ORDER TELEGRAPHS; ALARM SYSTEMS
    • G08B13/00—Burglar, theft or intruder alarms
    • G08B13/22—Electrical actuation
    • G08B13/24—Electrical actuation by interference with electromagnetic field distribution
    • G08B13/2402—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting
    • G08B13/2405—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting characterised by the tag technology used
    • G08B13/2414—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting characterised by the tag technology used using inductive tags
    • G08B13/2417—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting characterised by the tag technology used using inductive tags having a radio frequency identification chip
    • G—PHYSICS
    • G08—SIGNALLING
    • G08B—SIGNALLING OR CALLING SYSTEMS; ORDER TELEGRAPHS; ALARM SYSTEMS
    • G08B13/00—Burglar, theft or intruder alarms
    • G08B13/22—Electrical actuation
    • G08B13/24—Electrical actuation by interference with electromagnetic field distribution
    • G08B13/2402—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting
    • G08B13/2428—Tag details
    • G08B13/2437—Tag layered structure, processes for making layered tags
    • G—PHYSICS
    • G08—SIGNALLING
    • G08B—SIGNALLING OR CALLING SYSTEMS; ORDER TELEGRAPHS; ALARM SYSTEMS
    • G08B13/00—Burglar, theft or intruder alarms
    • G08B13/22—Electrical actuation
    • G08B13/24—Electrical actuation by interference with electromagnetic field distribution
    • G08B13/2402—Electronic Article Surveillance [EAS], i.e. systems using tags for detecting removal of a tagged item from a secure area, e.g. tags for detecting shoplifting
    • G08B13/2428—Tag details
    • G08B13/2437—Tag layered structure, processes for making layered tags
    • G08B13/2442—Tag materials and material properties thereof, e.g. magnetic material details
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/14—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys
    • H01F1/147—Alloys characterised by their composition
    • H01F1/153—Amorphous metallic alloys, e.g. glassy metals
    • H01F1/15391—Elongated structures, e.g. wires
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F41/00—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties
    • H01F41/02—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets
    • H01F41/0206—Manufacturing of magnetic cores by mechanical means
    • H01F41/0213—Manufacturing of magnetic circuits made from strip(s) or ribbon(s)
    • H01F41/0226—Manufacturing of magnetic circuits made from strip(s) or ribbon(s) from amorphous ribbons

Definitions

  • the present invention relates to ferromagnetic amorphous alloy ribbon and to a marker for use in an electronic article identification system, the marker including a plurality of rectangular strips based on an amorphous magnetostrictive material that vibrates in an alternating magnetic field mechanically at multiple resonant frequencies, whereby the magnetomechanical effect of the marker is effectively utilized for encoding and decoding purposes.
  • the present invention is also directed to an electronic identification system utilizing such a marker.
  • Magnetostriction of a magnetic material is a phenomenon in which a dimensional change takes place upon application of an external magnetic field on the magnetic material.
  • the material is termed “positive-magnetostrictive”.
  • a material is “negative-magnetostrictive”, the material shrinks upon its magnetization.
  • a magnetic material vibrates when it is in an alternating magnetic field.
  • ⁇ E effect is commonly known as ⁇ E effect, which is described, for example, in “Physics of Magnetism” by S.
  • the marker in such systems is a strip, or a plurality of strips, of known length of a ferromagnetic material, packaged with a magnetically harder ferromagnet (material with a higher coercivity) that provides a static field termed as biasing field to establish peak magneto-mechanical coupling.
  • the ferromagnetic marker material is preferably an amorphous alloy ribbon, since the efficiency of magneto-mechanical coupling in the alloys is very high.
  • the mechanical resonance frequency, f r is determined essentially by the length of the alloy ribbon and the biasing field strength, as the above Equation (1) indicates.
  • amorphous ferromagnetic materials were considered in the U.S. Pat. No. 4,510,490 for coded identification systems based on magnetomechanical resonance described above and included amorphous Fe—Ni—Mo—B, Fe—Co—B—Si, Fe—B—Si—C and Fe—B—Si alloys.
  • a commercially available amorphous Fe—Ni—Mo—B based METGLAS®2826MB alloy was used extensively until accidental triggering, by a magnetomechanical resonance marker, of other systems based on magnetic harmonic generation/detection. This occurs because a magnetomechanical resonance marker used at that time sometimes exhibited non-linear BH characteristics, resulting in generation of higher harmonics of the exciting field frequency.
  • the present invention includes a marker with encoding and decoding capability and an electronic identification system utilizing the marker.
  • a coded surveillance system having a magnetomechanical marker was taught in U.S. Pat. No. 4,510,490, but the number of constituent marker strips was limited due to a limited space available in a marker, thus limiting the universe of encoding and decoding capability using such a marker.
  • coded electronic article identification system a marker is needed in which the number of marker strips is increased considerably without sacrificing the performance as a coded marker in an electronic article identification system having encoding and decoding capability, hereinafter termed “coded electronic article identification system.”
  • a soft magnetic material is included in a marker of an electronic identification system based on magnetomechanical resonance.
  • a marker material with enhanced overall magnetomechanical resonance properties is fabricated from an amorphous alloy ribbon so that a multiple of marker strips are housed in a coded marker.
  • a soft magnetic material in a ribbon form having magnetomechanical resonance capability is cast on a rotating substrate, as taught in the U.S. Pat. No.4,142,571.
  • the as-cast ribbon width is wider than the predetermined width for a marker material, the said ribbon is slit to said predetermined width.
  • the ribbon thus processed is cut into ductile, rectangular amorphous metal strips having different lengths to fabricate a magnetomechanical resonance marker using a plurality of said strips with at least one semi-hard magnet strip which provides a bias static magnetic field.
  • a coded electronic article identification system utilizes a coded marker of the present invention.
  • the system has an article interrogation zone in which a magnetomechanical marker of the present invention is subject to an interrogating magnetic field with varying frequencies, the signal response to the interrogating magnetic field excitation being detected by a receiver having a pair of antenna coils situated in the article interrogation zone.
  • a coded marker of a magnetomechanical resonant electronic article identification system adapted to resonate mechanically at preselected frequencies, comprising: a plurality of ductile magnetostrictive strips cut to predetermined lengths from amorphous ferromagnetic alloy ribbons that have curvatures along a ribbon length direction and exhibit magnetomechanical resonance under alternating magnetic field excitations with a static bias field, the strips having a magnetic anisotropy direction perpendicular to a ribbon axis, wherein at least two of the strips are adapted to be magnetically biased to resonate at a single, different one of the preselected frequencies.
  • a radius of curvature of the marker strip curvatures is less than 100 cm.
  • encoding is carried out by cutting an amorphous magnetostrictive alloy ribbon having its magnetic anisotropy direction perpendicular to ribbon axis to a rectangular strip with a predetermined length having a length-to-width aspect ratio greater than 3.
  • the strips have a strip width ranging from about 3 mm to about 15 mm.
  • the strips have a slope of resonance frequency versus bias field ranging from about 4 Hz/(A/m) to about 14 Hz/(A/m).
  • the strips have a length greater than about 18 mm when a strip width is 6 mm.
  • the strips have a magnetomechanical resonance frequency less than about 120,000 Hz.
  • the amorphous ferromagnetic alloy ribbons have a saturation magnetostriction between about 8 ppm and about 18 ppm and a saturation induction between about 0.7 tesla and about 1.1 tesla.
  • an amorphous ferromagnetic alloy of the amorphous ferromagnetic alloy ribbons has a composition of one of: Fe 40.6 Ni 40.1 Mo 3.7 B 15.1 Si 0.5 , Fe 41.5 Ni 38.9 Mo 4.1 B 15.5 , Fe 41.7 Ni 39.4 Mo 3.1 B 15.8 , Fe 40.2 Ni 39.0 Mo 3.6 B 16.6 Si 0.6, Fe 39.8 Ni 39.2 Mo 3.1 B 17.6 C 0.3 , Fe 36.9 Ni 41.3 Mo 4.1 B 17.8 , Fe 35.6 Ni 42.6 Mo 4.0 B 17.9, Fe 40 Ni 38 Mo 4 B 18 , or Fe 38.0 Ni 38.8 Mo 3.9 B 19.3 .
  • the coded marker comprises at least two marker-strips with different lengths.
  • coded marker comprises five marker-strips with different lengths.
  • the coded marker has a magnetomechanical resonance frequency between about 30,000 and about 130,000 Hz.
  • the coded marker has an electronic identification universe containing up to about 1800 and about 115 million separately identifiable articles for a coded marker with two and five marker strips, respectively.
  • the coded marker has an electronic identification universe containing more than 115 million separately identifiable articles.
  • the strips have a magnetomechanical resonance frequency less than about 120,000 Hz.
  • an electronic article identification system has a capability of decoding coded information of a coded marker.
  • the system comprises one of: a pair of coils emitting an AC excitation field aimed at the coded marker to form an interrogation zone; a pair of signal detection coils receiving coded information from the coded marker; an electronic signal processing device with an electronic computer with a software to decode information coded on the coded marker; or an electronic device identifying the coded marker, wherein the coded marker is adapted to resonate mechanically at preselected frequencies, wherein the coded marker comprises a plurality of ductile magnetostrictive strips cut to predetermined lengths from amorphous ferromagnetic alloy ribbons that have curvatures along a ribbon length direction and exhibit magnetomechanical resonance under alternating magnetic field excitations with a static bias field, the strips having a magnetic anisotropy direction perpendicular to a ribbon axis, wherein at least two of the strips are adapted to be magnetically biased to resonate at a
  • a radius of curvature of the marker strip curvatures is between about 20 cm and about 100 cm.
  • FIG. 1A illustrates a side view of a strip cut from an amorphous alloy ribbon in accordance with an embodiment of the present invention and having a bias magnet
  • FIG. 1B illustrates a view of a conventional strip with a bias magnet
  • FIG. 2 illustrates magnetomechanical resonance characteristics of a single strip marker in accordance with an embodiment of the present invention and magnetomechanical resonance characteristics of a conventional single strip marker, showing resonance frequency as a function of bias field;
  • FIG. 3 illustrates resonance signals of a single strip marker in accordance with an embodiment of the present invention and resonance signals of a conventional strip marker, showing resonance signal amplitudes as a function of a bias field;
  • FIG. 4 illustrates a BH loop taken at 60 Hz on a marker strip of an embodiment of the present invention having a length of approximately 38 mm, a width of approximately 6 mm and a thickness of about 28 ⁇ m;
  • FIG. 5A illustrates a comparison of a physical profile of an embodiment of a magnetomechanical resonant marker in accordance with embodiments of the present invention
  • FIG. 5B illustrates a comparison of a conventional marker, utilizing two marker-strips with different lengths in both cases
  • FIG. 6A illustrates magnetomechanical resonance characteristics of a marker having two strips with different lengths of an embodiment of the present invention
  • FIG. 6B illustrates magnetomechanical resonance characteristics of a conventional marker having two strips with different lengths
  • FIG. 7 illustrates a resonance signal profile near the lower resonance frequency region of FIG. 6A ;
  • FIG. 8 illustrates a resonance signal profile near the upper resonance frequency region of FIG. 6A ;
  • FIGS. 9-1 and 9 - 2 illustrate a marker of an embodiment of the present invention, in which three strips with different lengths are housed;
  • FIG. 10 illustrates magnetomechanical resonance characteristics of a marker having three strips with different lengths of an embodiment of the present invention
  • FIG. 11 illustrates magnetomechanical resonance characteristics of a marker having five strips with different lengths of an embodiment of the present invention.
  • FIG. 12 illustrates a coded electronic article identification system in accordance with an embodiment of the present invention.
  • a marker material with enhanced overall magnetomechanical resonance properties is fabricated from an amorphous ferromagnetic alloy ribbon so that a multiple of marker strips are housed in a coded marker, wherein at least two of the strips are adapted to be magnetically biased to resonate mechanically at a single, different one of a plurality of preselected frequencies.
  • a magnetic material in a ribbon form having magnetomechanical resonance capability is cast on a rotating substrate, as taught in the U.S. Pat. No. 4,142,571.
  • the ribbon width is wider than the predetermined width for a marker material, the ribbon is slit to the predetermined width.
  • the ribbon thus processed is cut into ductile, rectangular amorphous metal strips having different lengths to fabricate a magnetomechanical resonance marker using a plurality of the strips with at least one semi-hard magnet strip which provides a bias static magnetic field.
  • the amorphous ferromagnetic alloy utilized to form a ribbon for the marker strip has a composition of one of: Fe 40.6 Ni 40.1 Mo 3.7 B 15.1 Si 0.5 , Fe 41.5 Ni 38.9 Mo 4.1 B 15.5 , Fe 41.7 Ni 39.4 Mo 3.1 B 15.8 , Fe 40.2 Ni 39.0 Mo 3.6 B 16.6 Si 0.6 , Fe 39.8 Ni 39.2 Mo 3.1 B 17.6 C 0.3 , Fe 36.9 Ni 41.3 Mo 4.1 B 17.8 , Fe 35.6 Ni 42.6 Mo 4.0 B 17.9 , Fe 40 Ni 38 Mo 4 B 18 , or Fe 38.0 Ni 38.8 Mo 3.9 B 19.3 .
  • an amorphous alloy ribbon with a chemical composition similar to a chemical composition of a commercially available amorphous magnetostrictive METGLAS®2826MB ribbon was cast in accordance with the invention described in the U.S. Pat. No. 4,142,571.
  • the cast amorphous alloy had a saturation induction of about 0.88 Tesla and a saturation magnetostriction of about 12 ppm.
  • the ribbon had widths of about 100 mm and about 25 mm, and its thickness was about 28 ⁇ m.
  • the ribbon was then slit into narrower ribbons with different widths.
  • the slit ribbon then was cut into ductile, rectangular strips having a length ranging from about 15 mm to about 65 mm.
  • FIG. 1A illustrates the physical appearance of a marker strip 10 of an embodiment of the present invention
  • FIG. 1B illustrates the physical appearance of a conventional strip 20 produced in accordance with a complex heat-treatment method disclosed in the U.S. Pat. No. 6,299,702.
  • magnetic flux lines 11 are more closed in a resonance marker-bias strip configuration of an embodiment of the present invention than the magnetic flux lines 21 of a conventional strip, as is illustrated in FIG. 1B .
  • FIG. 2 compares the resonance frequency as a function of bias field for a single strip marker 830 of an embodiment of the present invention and the resonance frequency of a conventional strip 831 .
  • FIG. 2 indicates that the resonance frequency change as a function of bias field is about the same for both cases.
  • FIG. 3 A comparison of the resonance response between the two cases is illustrated in FIG. 3 , in which V 0 is the response signal amplitude when the exciting field is turned off, and V 1 is the signal amplitude at 1 msec after the termination of the exciting field.
  • V 0 is the response signal amplitude when the exciting field is turned off
  • V 1 is the signal amplitude at 1 msec after the termination of the exciting field.
  • V 3 indicates that the ratio of V 1 /V 0 at these maximum points is higher for a resonance marker strip of an embodiment of the present invention than for a conventional marker strip, illustrating that signal retention of a marker strip of an embodiment of the present invention is better than in a conventional marker strip, thus enhancing the effectiveness of the present coded electronic identification system.
  • Table I summarizes a comparison of parameters critical for the performance of a marker strip as a magnetomechanical resonator between representative conventional marker strips and examples from the marker strips of an embodiment of the present invention. It is noted that the performance of the marker strips of an embodiment of the present invention is close to, or superior to, the performance of a conventional marker strips. All of the marker strips of an embodiment of the present invention in Table I are acceptable for use as markers of the embodiment of the present invention.
  • Table I contains data for a marker strip width of about 6 mm which is presently widely used. It is one aspect of the present invention to provide marker strips with widths different than about 6 mm. Marker strips with different widths were slit from the same ribbon used in Table I, and their magnetomechanical resonance characteristics were determined. The results are summarized in Table II. The resonance signal voltages, V 0 max and V 1 max decreased with decreasing width as expected. Decrease in the characteristic field values, H b0 and H b1 with decreasing width is due to demagnetizing effects. Thus, a bias field magnet must be selected accordingly.
  • a marker with a smaller width is suited for a smaller article identification area, whereas a marker with a larger width is suited for a larger article identification area because resonance signals are larger from larger marker strips, as Table II indicates. Since the resonance frequency depends primarily on the strip length, as Equation (1) indicates, the strip width change does not affect the resonance frequency of the article identification system used.
  • Table II shows the magnetomechanical resonance characteristics of marker strips of an embodiment of the present invention with strip height h, as defined in FIG. 1A and with different strip widths.
  • the definitions for V 0 max , H b0 , V 1 max and df r ldH b were the same as in Table I.
  • the length l of the strips were all about 38 mm.
  • a radius of curvature for each marker strip was calculated from h and l.
  • the resonance frequency of each strip was about 58 kHz.
  • Another aspect of the present invention is to provide a variety of available markers operated under different conditions.
  • magnetomechanical resonance characteristics were varied by changing the chemical composition of the amorphous magnetic alloy ribbon from which marker strips were produced.
  • the chemical compositions of the alloys examined are listed in Table III in which values of the saturation induction and magnetostrictions for the alloys are given.
  • the results of the magnetomechanical resonance properties of these alloys are given in Table IV below.
  • Table III shows examples of magnetostrictive amorphous alloys with their compositions, saturation inductions, B s , and saturation magnetostrictions, ⁇ s , for magnetomechanical resonance markers of an embodiment of the present invention.
  • TABLE III Magnetostrictive Amorphous Alloy Saturation Saturation Alloy Marker Chemical Composition Induction Magnetostriction No.
  • Table IV shows the magnetomechanical resonance characteristics of marker strips having different chemical compositions listed in Table III of an embodiment of the present invention with strip height h as defined in FIG. 1A .
  • the definitions for V 0 max , H b0 , V 1 max and df r ldH b were the same as in Table I.
  • the lengths l of the strips were all about 38 mm.
  • a radius of curvature for each marker strip was calculated from h and l.
  • the resonance frequency of each strip was about 58 kHz.
  • magnetomechanical resonance characteristics were determined for marker strips of an embodiment of the present invention with different lengths, l.
  • the width and thickness of each strip were about 6 mm and about 28 ⁇ m, respectively.
  • the resonance frequency, f r and time constant, ⁇ are defined in Equations (1) and (2), respectively.
  • the definitions of V 0 max , H b0 , V 1 max , H b1 and df r ldH b were the same as in Table 1.
  • Marker height h is defined in FIG. 1 , and a radius of curvature each strip was calculated using h and l.
  • the direction of magnetic anisotropy which is the direction of easy magnetization in a marker strip must be essentially perpendicular to the strip's length direction.
  • FIG. 4 depicts a BH loop taken at 60 Hz using a measurement method of Example 3 on an approximately 38 mm long strip from Table V above.
  • the shape of the BH loop shown in FIG. 4 is typical of the BH behavior of a magnetic strip in which the average direction of the magnetic anisotropy is perpendicular to strip's length direction.
  • a consequence of the magnetization behavior of a marker strip of an embodiment of the present invention shown in FIG. 4 is the absence of higher harmonics generation in the strip when the strip is placed in an AC magnetic field.
  • the system “pollution problem” as mentioned in the “Background of the Invention” section is minimized.
  • a higher harmonic signal from the marker strip of FIG. 4 was compared with that of a marker strip of an electronic article surveillance system based on magnetic harmonic generation/detection. The results of this comparison are given in Table VI below.
  • a magnetic higher harmonics signal comparison was made between a marker strip of an embodiment of the present invention and a marker strip based on Co-based METGLAS®2714A alloy, which is widely used in an electronic article surveillance system based on a magnetic harmonic generation/detection system.
  • the strip size was the same for both cases and was approximately 38 mm long and approximately 6 mm wide.
  • the fundamental excitation frequency was 2.4 kHz and the 25 th harmonic signals were compared by using a harmonic signal detection method of Example 4.
  • a negligibly small harmonic signal from a marker of an embodiment of the present invention does not trigger an electronic article surveillance system based on magnetic harmonic generation/detection.
  • Two marker-strips of an embodiment of the present invention with different lengths were selected randomly from a number of strips as characterized in Tables I, II, IV and V and were mounted on top of each other, and a marker was made as indicated by strip 110 and strip 111 in FIG. 5A .
  • the two marker-strips with different lengths are housed in a hollow area between non-magnetic outside casing 100 and 101 .
  • a bias magnet 120 is attached on the outside surface of a casing 101 .
  • a marker configuration for two conventional marker-strips is shown by strip 210 and strip 211 in FIG. 5B , in which a planar area available for the two strips is the same as that for the two strips of FIG. 5A .
  • Numerals 200 , 201 and 220 in FIG. 5B correspond to items 100 , 101 and 120 in FIG. 5A , respectively.
  • FIG. 6A The magnetomechanical resonance behavior of a two-strip marker of an embodiment of the present invention corresponding to FIG. 5A is shown in FIG. 6A for a marker containing an approximately 20 mm strip and an approximately 57 mm strip from Table V, and the magnetomechanical resonance behavior of a conventional two-strip marker prepared in accordance with the '490 patent, which corresponds to FIG. 5B , is shown in FIG. 6B using two strips with lengths of approximately 20 mm and approximately 57 mm. It is clear from FIGS. 6A-6B that overall signal amplitudes from the two marker-strips of an embodiment of the present invention are considerably higher than the overall signal amplitudes from the two conventional marker-strips.
  • the signal amplitude V 0 (illustrated in FIG. 6A ) from the longer sized strip of an embodiment of the present invention is about 280% higher than its corresponding value V 0 (illustrated in FIG. 6B ) for the longer sized conventional marker strip of FIG. 5B .
  • the strip of an embodiment of the present invention generates a higher signal amplitude V 1 (illustrated in FIG. 6A ) by 370% than the signal amplitude V 1 (illustrated in FIG. 6B ) of its corresponding conventional marker strip.
  • An enlarged resonance amplitude profile near the lower resonance frequency, f r 38,610 Hz shown in FIG.
  • FIG. 7 shows the width of the magnetomechanical resonance, defined as the width in frequency at the point where the amplitude becomes 1 ⁇ 2 that of the peak amplitude, is about 420 Hz.
  • the signal amplitude has a frequency width of about 660 Hz as shown in FIG. 8 .
  • This frequency width hereinafter termed resonance line width, is used to determine the minimum resonance frequency separation between the two adjacent resonance frequencies for two marker strips with slightly different lengths.
  • FIG. 9-1 illustrates a marker of an embodiment of the present invention which contains three marker-strips, 311 , 312 and 313 , with different lengths which were randomly selected from Tables I, II and IV above.
  • the cavity space 302 between the two outside casings 300 and 301 is to accommodate the marker strips, 311 , 312 and 313 , of the embodiment of the present invention, and numeral 330 indicates a bias magnet which is attached on the outside surface of casing 301 .
  • the magnetomechanical resonance characteristics of the marker with three strips having lengths of about 25 mm, about 38 mm and about 52 mm and a width of about 6 mm are shown in FIG. 10 . It noted in FIG. 6A and FIG.
  • marker strip width and thickness are about 6 mm and about 28 ⁇ m, respectively.
  • the resonance signals V 0 max and V 1 max given in Table VII are significant enough to be detected in an electronic article identification system in accordance with embodiments of the present invention.
  • f r resonance frequency
  • l strip length
  • Equation (1) the variability of the resonance frequency caused by the tolerance in cutting ribbon to a predetermined length is determined as follows.
  • the marker strip cutting tolerance achievable with a commercially available ribbon cutter is determined by comparing the nominal or targeted strip length and the actual length given in Table V.
  • the strip having a length of 18.01 mm in Table V had a targeted strip length of 18 mm, resulting in a cutting tolerance of 0.01 mm.
  • the frequency variability ⁇ f r due to strip length variability was calculated, which ranged from about 3 Hz for shorter strips to about 400 Hz for longer strips. Since the resonance line width for a longer strip is about 400 Hz, as indicated in FIG. 7 and is about 700 Hz for a shorter strip, as indicated in FIG.
  • the minimum frequency separation which is discernable in an electronic article identification system in accordance with embodiments of the present invention is determined as about 800 Hz.
  • a resonance frequency separation of 2 kHz which is more than twice that of the minimum discernable resonance frequency separation, was selected to determine the number of identifiable articles in a selected universe.
  • the resonance frequency covered with the marker strips listed in Table V ranged from about 34,000 Hz to about 120,000 Hz, covering a resonance frequency span of approximately 86,000 Hz.
  • the number of electronically identifiable articles becomes 43 when a marker has only one strip, which increases to about 1800, 74000, 2.96 million and 115.5 million in a given universe when a marker with two, three, four and five marker strips, respectively, with different lengths of an embodiment of the present invention is utilized in a coded electronic article identification system in accordance with the present invention.
  • the number of the identifiable or coded articles is further increased by either adding more marker strips and/or changing the level of bias field in a marker.
  • a coded marker 501 as described above is effectively utilized in an electronic article identification system in accordance with embodiments of the present invention, as is illustrated in FIG. 12 .
  • An article to be identified 502 carrying a coded marker 501 of an embodiment of the present invention is placed in an interrogation zone 510 in FIG. 12 , which is flanked by a pair of interrogation coils 511 .
  • the coils 511 emit an AC magnetic field fed by an electronic device 512 consisting of a signal generator 513 and an AC amplifier 514 with varying frequencies, which is controlled by an electronic circuit box 515 for its on-off operation, aiming at the article 502 to be identified.
  • the electronic circuit box 515 switches on the interrogation AC field frequency sweeping from the lowest frequency to the highest frequency, the range of which depends on the marker's predetermined frequency range.
  • a resonance signal from a coded marker of an embodiment of the present invention 501 is detected in a pair of signal receiving coils 516 , resulting in a resonance signal profile as exemplified in FIG. 11 .
  • the signal profile thus obtained by means of a signal detector 517 is stored in a computer 518 which is programmed to identify the resonance frequency sequences encoded in a coded marker 501 of an embodiment of the present invention.
  • the computer 518 sends signal reporting results of the identification to an identifier 519 and to the electronic circuit box 515 for resetting the system.
  • a coded marker in accordance with embodiments of the present invention may be deactivated by demagnetizing the bias magnet in the marker after article 502 exits the interrogation zone 510 .
  • the coded electronic article identification system provided above is used to identify an article by sweeping an AC excitation field with varying frequency. In certain cases, delayed identification is desired, which can be accomplished by tracking V 1 as depicted in FIG. 3 , FIG. 5 ( a ), FIG. 10 and FIG. 11 . Electronically this is accomplished by programming the computer 517 in FIG. 12 to process V 1 as a function of the sweeping frequency.
  • a slit ribbon was cut into ductile and rectangular strips with a conventional metal ribbon cutter.
  • the curvature of each strip was determined optically by measuring the height, h, of the curved surface over the strip length, l, as defined in FIG. 1A .
  • the magnetomechanical performance was determined in a set-up in which a pair of coils supplying a static bias field and the voltage appearing in a signal detecting coil compensated by a bucking coil was measured by a voltmeter and an oscilloscope. The measured voltage therefore is detecting-coil dependent and indicates a relative signal amplitude.
  • the exciting AC field was supplied by a commercially available function generator and an AC amplifier. The signal voltage from the voltmeter was tabulated and a commercially available computer software was used to analyze and process the data collected.
  • a commercially available DC BH loop measurement equipment was utilized to measure magnetic induction B as a function of applied field H.
  • an exciting coil-detecting coil assembly similar to that of Example 4 was used and output signal from the detecting coil was fed into an electronic integrator. The integrated signal was then calibrated to give the value of the magnetic induction B of a sample. The resultant B was plotted against applied field H, resulting in an AC BH loop. Both AC and DC cases, the direction of the applied field and the measurement was along marker strips' length direction.
  • a marker strip prepared in accordance with Example 1 was placed in an exciting AC field at a predetermined fundamental frequency and its higher harmonics response was detected by a coil containing the strip.
  • the exciting coil and signal detecting coil were wound on a bobbin with a diameter of about 50 mm.
  • the number of the windings in the exciting coil and the signal detecting coil was about 180 and about 250, respectively.
  • the fundamental frequency was chosen at 2.4 kHz and its voltage at the exciting coil was about 80 mV.
  • the 25th harmonic voltages from the signal detecting coil were measured.
  • a radius of curvature of the marker strip curvatures may be less than about 100 cm, or between about 20 cm and about 100 cm.
  • encoding is carried out by cutting an amorphous magnetostrictrive alloy ribbon having its magnetic anisotropy direction perpendicular to ribbon axis to a rectangular strip with a predetermined length having a length-to-width ratio greater than 3.
  • the strips have a strip width ranging from about 3 mm to about 15 mm.
  • the strips have a slope of resonance frequency versus bias field ranging from about 4 Hz/(A/m) to about 14 Hz/(A/m).
  • the strips have a length greater than about 18 mm when a strip width is 6 mm.
  • the strips have a magnetomechanical resonance frequency less than about 120,000 Hz.
  • the amorphous ferromagnetic alloy ribbons have a saturation magnetostriction between about 8 ppm and about 18 ppm and a saturation induction between about 0.7 tesla and about 1.1 tesla.
  • the coded marker comprises at least two marker-strips with different lengths. Where selected, the coded marker comprises five marker-strips with different lengths.
  • the coded marker has a magnetomechanical resonance frequency between about 30,000 and about 130,000 Hz.
  • the coded marker has an electronic identification universe containing up to about 1800 and about 115 million separately identifiable articles for a coded marker with two and five marker strips, respectively.
  • the coded marker has an electronic identification universe containing more than 115 million separately identifiable articles.
  • a coded marker of a magnetomechanical resonant electronic article identification system adapted to resonate mechanically at preselected frequencies, comprises a plurality of ductile magnetostrictive strips cut to predetermined lengths from amorphous ferromagnetic alloy ribbons that have curvatures along a ribbon length direction and exhibit magnetomechanical resonance under alternating magnetic field excitations with a static bias field, the strips having a magnetic anisotropy direction perpendicular to a ribbon axis, wherein at least two of the strips are adapted to be magnetically biased to resonate at a single, different one of the preselected frequencies.
  • an electronic article identification system has a capability of decoding coded information of a coded marker.
  • the coded marker is adapted to resonate mechanically at preselected frequencies
  • the coded marker comprises a plurality of ductile magnetostrictive strips cut to predetermined lengths from amorphous ferromagnetic alloy ribbons that have curvatures along a ribbon length direction and exhibit magnetomechanical resonance under alternating magnetic field excitations with a static bias field, the strips having a magnetic anisotropy direction perpendicular to a ribbon axis, and wherein at least two of the strips are adapted to be magnetically biased to resonate at a single, different one of the preselected frequencies.
  • the electronic article identification system comprises one of: a pair of coils emitting an AC excitation field aimed at the coded marker to form an interrogation zone; a pair of signal detection coils receiving coded information from the coded marker; an electronic signal processing device with an electronic computer with a software to decode information coded on the coded marker; or an electronic device identifying the coded marker.
  • the electronic article identification system may identify an article having the coded marker attached thereto.

Landscapes

  • Physics & Mathematics (AREA)
  • Engineering & Computer Science (AREA)
  • General Physics & Mathematics (AREA)
  • Electromagnetism (AREA)
  • Automation & Control Theory (AREA)
  • Computer Security & Cryptography (AREA)
  • Power Engineering (AREA)
  • Theoretical Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Dispersion Chemistry (AREA)
  • Computer Vision & Pattern Recognition (AREA)
  • Artificial Intelligence (AREA)
  • Manufacturing & Machinery (AREA)
  • Burglar Alarm Systems (AREA)
  • Geophysics And Detection Of Objects (AREA)
  • Radar Systems Or Details Thereof (AREA)
  • Machine Tool Sensing Apparatuses (AREA)
  • Inspection Of Paper Currency And Valuable Securities (AREA)
US11/095,559 2005-04-01 2005-04-01 Marker for coded electronic article identification system Abandoned US20060219786A1 (en)

Priority Applications (12)

Application Number Priority Date Filing Date Title
US11/095,559 US20060219786A1 (en) 2005-04-01 2005-04-01 Marker for coded electronic article identification system
TW101128803A TWI480567B (zh) 2005-04-01 2006-03-29 用於編碼電子物件識別系統之標誌
TW095110950A TWI377507B (en) 2005-04-01 2006-03-29 Marker for coded electronic article identification system
JP2008504410A JP4778551B2 (ja) 2005-04-01 2006-03-31 コード化電子商品識別システム用マーカ
CN2006800102314A CN101151620B (zh) 2005-04-01 2006-03-31 用于编码电子物品识别系统的标记器
ES06740152T ES2378560T3 (es) 2005-04-01 2006-03-31 Marcador codificado para sistema electrónico de identificación de artículos
EP06740152A EP1872299B1 (en) 2005-04-01 2006-03-31 Coded marker for electronic article identification system
PCT/US2006/011839 WO2006107739A2 (en) 2005-04-01 2006-03-31 Marker for coded electronic article identification system
KR1020077021146A KR100990989B1 (ko) 2005-04-01 2006-03-31 코딩된 전자 물품 식별 시스템용 마커
AT06740152T ATE535880T1 (de) 2005-04-01 2006-03-31 Codierter markierer für ein elektronisches artikelidentifikationssystem
US11/607,993 US7320433B2 (en) 2005-04-01 2006-12-04 Marker for coded electronic article identification system
HK08108205.6A HK1117618A1 (en) 2005-04-01 2008-07-24 Marker for coded electronic article identification system

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US11/095,559 US20060219786A1 (en) 2005-04-01 2005-04-01 Marker for coded electronic article identification system

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US11/607,993 Continuation-In-Part US7320433B2 (en) 2005-04-01 2006-12-04 Marker for coded electronic article identification system

Publications (1)

Publication Number Publication Date
US20060219786A1 true US20060219786A1 (en) 2006-10-05

Family

ID=37069122

Family Applications (2)

Application Number Title Priority Date Filing Date
US11/095,559 Abandoned US20060219786A1 (en) 2005-04-01 2005-04-01 Marker for coded electronic article identification system
US11/607,993 Expired - Fee Related US7320433B2 (en) 2005-04-01 2006-12-04 Marker for coded electronic article identification system

Family Applications After (1)

Application Number Title Priority Date Filing Date
US11/607,993 Expired - Fee Related US7320433B2 (en) 2005-04-01 2006-12-04 Marker for coded electronic article identification system

Country Status (10)

Country Link
US (2) US20060219786A1 (ja)
EP (1) EP1872299B1 (ja)
JP (1) JP4778551B2 (ja)
KR (1) KR100990989B1 (ja)
CN (1) CN101151620B (ja)
AT (1) ATE535880T1 (ja)
ES (1) ES2378560T3 (ja)
HK (1) HK1117618A1 (ja)
TW (2) TWI480567B (ja)
WO (1) WO2006107739A2 (ja)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008021730A2 (en) * 2006-08-07 2008-02-21 Gadonniex Dennis M Electronic article surveillance marker
CN101882492A (zh) * 2010-06-21 2010-11-10 北京四海诚明科技有限公司 半硬磁材料、制备方法及其用途
US8579203B1 (en) 2008-12-19 2013-11-12 Dynamics Inc. Electronic magnetic recorded media emulators in magnetic card devices
CN103903510A (zh) * 2012-12-29 2014-07-02 鸿富锦精密工业（深圳）有限公司 声磁标签
TWI593944B (zh) * 2013-05-09 2017-08-01 Ｔｈｋ股份有限公司 線性編碼器裝置及基準位置檢測方法

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20090004949A (ko) * 2006-07-26 2009-01-12 넥스트 가부시키가이샤 자기 마커 및 그 제조 장치
WO2010082195A1 (en) 2009-01-13 2010-07-22 Vladimir Manov Magnetomechanical markers and magnetostrictive amorphous element for use therein
KR101025822B1 (ko) * 2009-06-11 2011-03-30 한국조폐공사 전자기 밴드갭 패턴의 보안코드 인식장치
US8366010B2 (en) * 2011-06-29 2013-02-05 Metglas, Inc. Magnetomechanical sensor element and application thereof in electronic article surveillance and detection system
US10325439B2 (en) 2015-07-03 2019-06-18 Custom Security Industries, Inc. Article identification reader, marker element for article identification and method of article identification

Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4142571A (en) * 1976-10-22 1979-03-06 Allied Chemical Corporation Continuous casting method for metallic strips
US4510490A (en) * 1982-04-29 1985-04-09 Allied Corporation Coded surveillance system having magnetomechanical marker
US4510489A (en) * 1982-04-29 1985-04-09 Allied Corporation Surveillance system having magnetomechanical marker
US5495231A (en) * 1995-04-13 1996-02-27 Alliedsignal Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US5539380A (en) * 1995-04-13 1996-07-23 Alliedsignal Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US5628840A (en) * 1995-04-13 1997-05-13 Alliedsignal Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US6073845A (en) * 1995-12-19 2000-06-13 Canon Denshi Kabushiki Kaisha Recording medium on which information is recorded in intermittent pattern, and method of and apparatus for reproducing the information
US6093261A (en) * 1995-04-13 2000-07-25 Alliedsignals Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US6095416A (en) * 1998-02-24 2000-08-01 Privicom, Inc. Method and device for preventing unauthorized use of credit cards
US6187112B1 (en) * 1995-04-13 2001-02-13 Ryusuke Hasegawa Metallic glass alloys for mechanically resonant marker surveillance systems
US6299702B1 (en) * 1997-11-12 2001-10-09 Vacuumschmelze Gmbh Method of annealing amorphous ribbons and marker for electronic article surveillance
US6359563B1 (en) * 1999-02-10 2002-03-19 Vacuumschmelze Gmbh ‘Magneto-acoustic marker for electronic article surveillance having reduced size and high signal amplitude’
US7088247B2 (en) * 2000-10-02 2006-08-08 Vacuumschmelze Gmbh Amorphous alloys for magneto-acoustic markers having reduced, low or zero cobalt content, and associated article surveillance system
US7205897B2 (en) * 2005-03-01 2007-04-17 Sap Aktiengesellschaft Product flow based auto-ID infrastructure

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS58219677A (ja) * 1982-06-03 1983-12-21 アイデンテイテツク　コ−ポレ−シヨン 磁気機械的マ−カ−をもつコ−ド化された監視システム
EP0565583B1 (en) * 1991-01-04 1997-04-09 Scientific Generics Limited Remotely readable data storage devices and apparatus
TW198154B (ja) * 1991-08-20 1993-01-11 Allied Signal Inc
US5495230A (en) * 1994-06-30 1996-02-27 Sensormatic Electronics Corporation Magnetomechanical article surveillance marker with a tunable resonant frequency
US5469140A (en) * 1994-06-30 1995-11-21 Sensormatic Electronics Corporation Transverse magnetic field annealed amorphous magnetomechanical elements for use in electronic article surveillance system and method of making same
US5969612A (en) * 1998-07-06 1999-10-19 Sensormatic Electronics Corporation Stabilizing the position of an active element in a magnetomechanical EAS marker
DE69939064D1 (de) * 1998-08-14 2008-08-21 3M Innovative Properties Co Anwendungen für radiofrequenzidentifikationssysteme
US7065440B2 (en) 2004-01-22 2006-06-20 Trimble Navigation, Ltd Method and apparatus for steering movable object by using control algorithm that takes into account the difference between the nominal and optimum positions of navigation antenna

Patent Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4142571A (en) * 1976-10-22 1979-03-06 Allied Chemical Corporation Continuous casting method for metallic strips
US4510490A (en) * 1982-04-29 1985-04-09 Allied Corporation Coded surveillance system having magnetomechanical marker
US4510489A (en) * 1982-04-29 1985-04-09 Allied Corporation Surveillance system having magnetomechanical marker
US5650023A (en) * 1995-04-13 1997-07-22 Allied Signal Inc Metallic glass alloys for mechanically resonant marker surveillance systems
US5539380A (en) * 1995-04-13 1996-07-23 Alliedsignal Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US5628840A (en) * 1995-04-13 1997-05-13 Alliedsignal Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US5495231A (en) * 1995-04-13 1996-02-27 Alliedsignal Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US6093261A (en) * 1995-04-13 2000-07-25 Alliedsignals Inc. Metallic glass alloys for mechanically resonant marker surveillance systems
US6187112B1 (en) * 1995-04-13 2001-02-13 Ryusuke Hasegawa Metallic glass alloys for mechanically resonant marker surveillance systems
US6073845A (en) * 1995-12-19 2000-06-13 Canon Denshi Kabushiki Kaisha Recording medium on which information is recorded in intermittent pattern, and method of and apparatus for reproducing the information
US6299702B1 (en) * 1997-11-12 2001-10-09 Vacuumschmelze Gmbh Method of annealing amorphous ribbons and marker for electronic article surveillance
US6095416A (en) * 1998-02-24 2000-08-01 Privicom, Inc. Method and device for preventing unauthorized use of credit cards
US6359563B1 (en) * 1999-02-10 2002-03-19 Vacuumschmelze Gmbh ‘Magneto-acoustic marker for electronic article surveillance having reduced size and high signal amplitude’
US7088247B2 (en) * 2000-10-02 2006-08-08 Vacuumschmelze Gmbh Amorphous alloys for magneto-acoustic markers having reduced, low or zero cobalt content, and associated article surveillance system
US7205897B2 (en) * 2005-03-01 2007-04-17 Sap Aktiengesellschaft Product flow based auto-ID infrastructure

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008021730A2 (en) * 2006-08-07 2008-02-21 Gadonniex Dennis M Electronic article surveillance marker
WO2008021730A3 (en) * 2006-08-07 2008-05-15 Dennis M Gadonniex Electronic article surveillance marker
US8579203B1 (en) 2008-12-19 2013-11-12 Dynamics Inc. Electronic magnetic recorded media emulators in magnetic card devices
CN101882492A (zh) * 2010-06-21 2010-11-10 北京四海诚明科技有限公司 半硬磁材料、制备方法及其用途
CN103903510A (zh) * 2012-12-29 2014-07-02 鸿富锦精密工业（深圳）有限公司 声磁标签
US20140183270A1 (en) * 2012-12-29 2014-07-03 Hon Hai Precision Industry Co., Ltd. Acoustic magnetic tag
TWI593944B (zh) * 2013-05-09 2017-08-01 Ｔｈｋ股份有限公司 線性編碼器裝置及基準位置檢測方法

Also Published As

Publication number Publication date
ES2378560T3 (es) 2012-04-13
US7320433B2 (en) 2008-01-22
CN101151620A (zh) 2008-03-26
TW200701091A (en) 2007-01-01
CN101151620B (zh) 2012-08-01
WO2006107739A3 (en) 2007-06-21
EP1872299A4 (en) 2010-08-18
KR100990989B1 (ko) 2010-11-01
KR20070118084A (ko) 2007-12-13
WO2006107739A2 (en) 2006-10-12
TW201300816A (zh) 2013-01-01
TWI480567B (zh) 2015-04-11
ATE535880T1 (de) 2011-12-15
HK1117618A1 (en) 2009-01-16
JP4778551B2 (ja) 2011-09-21
EP1872299A2 (en) 2008-01-02
EP1872299B1 (en) 2011-11-30
TWI377507B (en) 2012-11-21
JP2008535104A (ja) 2008-08-28
US20070080226A1 (en) 2007-04-12

Similar Documents

Publication Publication Date Title
EP1872343B1 (en) Marker for coded electronic article identification system
US7320433B2 (en) Marker for coded electronic article identification system
JP2008545175A5 (ja)
US20030168124A1 (en) Method of annealing amorphous ribbons and marker for electronic article surveillance
KR19980703801A (ko) 기계적 공진마아커 감시시스템용 금속 유리질합금
JP2010529551A (ja) 磁気機械共鳴装置のためのアモルファス合金組成物およびそれを含むｅａｓマーカー
US20100259391A1 (en) Electronic Article Surveillance Marker
US8366010B2 (en) Magnetomechanical sensor element and application thereof in electronic article surveillance and detection system
KR19980703802A (ko) 기계적 공진마아커 감시시스템용 금속 유리질합금
KR100576075B1 (ko) 기계적 공진마커 감시시스템을 위한 금속유리합금
O’Handley Magnetic materials for EAS sensors
KR100478114B1 (ko) 기계적공진마커감시시스템을위한금속유리합금

Legal Events

Date Code Title Description
AS Assignment

Owner name: METGLAS, INC., SOUTH CAROLINA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HASEGAWA, RUSUKE;REEL/FRAME:016443/0168

Effective date: 20050331

AS Assignment

Owner name: METGLAS, INC., SOUTH CAROLINA

Free format text: RECORD TO CORRECT THE NAME OF THE ASSIGNOR ON THE ASSIGNMENT DOCUMENT PREVIOUSLY RECORD ON REEL 016443, FRAME 0168. THE CORRECT NAME OF THE ASSIGNOR IS HASEGAWA RYUSUKE.;ASSIGNOR:RYUSUKE, HASEGAWA;REEL/FRAME:016838/0482

Effective date: 20050401

AS Assignment

Owner name: METGLAS, INC., SOUTH CAROLINA

Free format text: CORRECTED COVER SHEET TO CORRECT THE EXECUTION DATE, PREVIOUSLY RECORDED AT REEL/FRAME 016838/0482 (ASSIGNMENT OF ASSIGNOR'S INTEREST);ASSIGNOR:HASEGAWA, RYUSUKE;REEL/FRAME:017204/0590

Effective date: 20050531

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION