US20060060510A1 - High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product - Google Patents

High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product Download PDF

Info

Publication number
US20060060510A1
US20060060510A1 US10/943,756 US94375604A US2006060510A1 US 20060060510 A1 US20060060510 A1 US 20060060510A1 US 94375604 A US94375604 A US 94375604A US 2006060510 A1 US2006060510 A1 US 2006060510A1
Authority
US
United States
Prior art keywords
alumina
weight percent
catalyst composition
range
angstroms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/943,756
Other languages
English (en)
Inventor
Opinder Bhan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US10/943,756 priority Critical patent/US20060060510A1/en
Priority to KR1020077008519A priority patent/KR20070057945A/ko
Priority to ES05796545T priority patent/ES2383378T3/es
Priority to CA2580451A priority patent/CA2580451C/en
Priority to CNA2005800349670A priority patent/CN101076399A/zh
Priority to RU2007114294/04A priority patent/RU2377067C2/ru
Priority to BRPI0515365-4A priority patent/BRPI0515365A/pt
Priority to EP05796545A priority patent/EP1789182B1/en
Priority to PCT/US2005/033248 priority patent/WO2006034073A1/en
Priority to JP2007532522A priority patent/JP5036542B2/ja
Priority to DK05796545.1T priority patent/DK1789182T3/da
Priority to AT05796545T priority patent/ATE555849T1/de
Publication of US20060060510A1 publication Critical patent/US20060060510A1/en
Priority to ZA200702000A priority patent/ZA200702000B/xx
Priority to US13/558,056 priority patent/US8618015B2/en
Priority to US14/082,687 priority patent/US9540573B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G45/00—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds
    • C10G45/02—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing
    • C10G45/04—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used
    • C10G45/06—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used containing nickel or cobalt metal, or compounds thereof
    • C10G45/08—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used containing nickel or cobalt metal, or compounds thereof in combination with chromium, molybdenum, or tungsten metals, or compounds thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
    • B01J21/02—Boron or aluminium; Oxides or hydroxides thereof
    • B01J21/04—Alumina
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/74—Iron group metals
    • B01J23/755—Nickel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
    • B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J23/85—Chromium, molybdenum or tungsten
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
    • B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J23/85—Chromium, molybdenum or tungsten
    • B01J23/88—Molybdenum
    • B01J23/882—Molybdenum and cobalt
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
    • B01J27/14—Phosphorus; Compounds thereof
    • B01J27/186—Phosphorus; Compounds thereof with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J27/188—Phosphorus; Compounds thereof with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium with chromium, molybdenum, tungsten or polonium
    • B01J27/19—Molybdenum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/08—Heat treatment
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G45/00—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds
    • C10G45/02—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing
    • C10G45/04—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J23/24—Chromium, molybdenum or tungsten
    • B01J23/28—Molybdenum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/74—Iron group metals
    • B01J23/75—Cobalt
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
    • B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J23/85—Chromium, molybdenum or tungsten
    • B01J23/88—Molybdenum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/61—Surface area
    • B01J35/615—100-500 m2/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/63—Pore volume
    • B01J35/635—0.5-1.0 ml/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/63—Pore volume
    • B01J35/638—Pore volume more than 1.0 ml/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/64—Pore diameter
    • B01J35/647—2-50 nm
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/66—Pore distribution
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
    • C10G2300/10—Feedstock materials
    • C10G2300/1037—Hydrocarbon fractions
    • C10G2300/1048—Middle distillates
    • C10G2300/1055—Diesel having a boiling range of about 230 - 330 °C
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
    • C10G2300/20—Characteristics of the feedstock or the products
    • C10G2300/201—Impurities
    • C10G2300/202—Heteroatoms content, i.e. S, N, O, P
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G2400/00—Products obtained by processes covered by groups C10G9/00 - C10G69/14
    • C10G2400/04—Diesel oil

Definitions

  • This invention relates to a catalyst and process for the manufacture of a hydrocarbon product having a low sulfur concentration.
  • the invention further relates to a high activity hydrodesulfurization catalyst, a method of making such high activity hydrodesulfurization catalyst, and a process for manufacturing diesel distillate product having a low sulfur concentration using the high activity hydrodesulfurization catalyst.
  • a conventional hydrodesulfurization process employed to reduce the concentration of organosulfur compounds contained in a hydrocarbon feedstock is typically carried out by contacting the hydrocarbon feedstock with a hydrotreating catalyst in the presence of hydrogen and at an elevated temperature and pressure.
  • a typical hydrotreating catalyst contains a group 6 metal component, such as molybdenum, and a group 9 or group 10 component, such as cobalt or nickel, supported on a refractory oxide support.
  • U.S. Pat. No. 3,669,904 discloses a method of making a gas oil hydrodesulfurization catalyst prepared from a precursor mixture of mildly calcined boehmite and uncalcined boehmite.
  • the disclosed method addresses certain of the disadvantages and limitations with the use of technical grade boehmite in forming extruded pellets for use in making certain catalysts.
  • the gamma alumina pellets are made by mixing a mildly calcined technical grade boehmite with uncalcined technical grade boehmite and an extrusion aid followed by forming a pellet that is calcined.
  • U.S. Pat. No. 3,853,789 discloses a method of making a mechanically strong alumina extrudate that may be used as a catalyst carrier.
  • the extrudate is prepared by mixing with water specific proportions of gamma alumina powder having a certain particle size and alumina monohydrate (boehmite) having a certain particle size to form an extrudable paste from which an extrudate is formed.
  • the extrudate is dried and then heat-treated at temperatures of 1150 to 1250° F.
  • U.S. Pat. No. 4,066,574 discloses a catalyst for use in the hydrodesulfurization of a heavy oil feedstock.
  • the catalyst is an alumina support that is impregnated with Group VIB and Group VIII metals or metal compounds.
  • the alumina support has a specific pore structure that provides for certain desired catalyst properties.
  • the alumina support is made by mixing water and a strong mineral acid with amorphous or crystalline hydrate alumina powder to form a paste that is extruded.
  • the density of the extrudate may be controlled by the addition of ammonium hydroxide to the extrudable paste.
  • the extrudate is calcined at a temperature of 500° F. to 1600° F.
  • the support has at least 70 volume percent of its pore volume in pores having a diameter between 80 and 150 Angstroms and less than 3 volume percent of its pore volume in pores having a diameter above 1000 Angstroms.
  • U.S. Pat. No. 4,089,811 discloses a method of making an alumina catalyst support by calcining alpha alumina monohydrate (boehmite) at a temperature of from about 800° F. to 900° F. to form calcined alumina containing gamma alumina and mixing the calcined alumina with water to form a wetted alumina.
  • the wetted alumina at a pH of from 6 to 12.5 is heated to a temperature of from 190° F. to 250° F. for from 8 to 24 hours to convert the calcined alumina to beta alumina trihydrate. Maintaining the calcination temperature within the range of 800 to 900° F. is important to achieve the desired results.
  • the calcined alumina contains at least about 80% gamma alumina with the remaining portion of the alumina being substantially entirely alpha alumina monohydrate.
  • U.S. Pat. No. 4,271,042 discloses a desulfurization catalyst that comprises a hydrogenation catalytic component composited with gamma alumina that contains dispersed delta and/or theta phase alumina.
  • the catalyst is prepared by precalcining gamma alumina or boehmite at a temperature of from 1600° F. to 2000° F. to induce the formation of delta and/or theta phase alumina.
  • the resulting powder is then mixed with alpha alumina monohydrate (boehmite) and formed into pellets or extrudates that are calcined at a temperature of from 900° F. to 1400° F. to form a catalyst support consisting of an intimate mixture of gamma alumina with delta and/or theta phase alumina.
  • the catalyst support may be composited with the hydrogenation component.
  • U.S. Pat. No. 5,300,217 discloses a hydroprocessing catalyst that comprises a hydrogenation component supported on a porous, amorphous refractory oxide containing delta alumina.
  • the finished catalyst contains greater than 5 weight percent delta alumina.
  • the amorphous, porous refractory oxide support material is prepared by extruding a precursor of the desired support, such as a refractory gel, followed by calcination of the extrudate. To obtain the desired delta-gamma alumina combination for the support, it is precalcined, prior to impregnation with the hydrogenation component, at a temperature above about 900° F. and preferably above 1800° F.
  • an object of the invention to provide an improved catalyst for use in processes for the manufacture of a distillate product having a low concentration of sulfur.
  • Another object of the invention is to provide a process for making low sulfur distillate product.
  • a catalyst composition that comprises a shaped support material having incorporated therein a catalytic hydrogenation component wherein the shaped support material is a calcined alumina having a material absence of aluminum hydroxide and a material absence of crystalline transitional phase of alumina other than gamma alumina.
  • the catalyst composition comprises a calcined impregnated shaped support, wherein the shaped support of the impregnated shaped support comprises, prior to its impregnation and calcination, at least 90 weight percent alumina that is in the crystalline transitional phase of gamma-alumina, less than 5 weight percent alumina that is in the crystalline transitional phase of delta-alumina, and less than 5 weight percent alumina that is in the crystalline transitional phase other than gamma-alumina, and wherein the shaped support has incorporated therein a hydrogenation catalytic component thereby providing the impregnated shaped support, and wherein the impregnated shaped support is calcined.
  • a method of making a catalyst composition useful in the manufacture of a low sulfur distillate product includes providing a shaped support, having a material absence of aluminum hydroxide and a material absence of crystalline transitional phase of alumina, comprising gamma-alumina, and incorporating therein a catalytic component to thereby provide an intermediate, and calcining the intermediate to thereby provide the catalyst composition.
  • Another embodiment of the inventive method of making the catalyst composition includes forming a shaped particle comprising at least 90 weight percent, exclusive of water, boehmite, and calcining the shaped particle under a controlled temperature condition to convert the boehmite of the shaped particle to gamma-alumina.
  • the controlled temperature condition is controlled to within a calcination temperature range of from about 850° F. and 950° F. so that essentially all of the boehmite of the shaped particle is converted to a crystalline transitional phase of alumina but less than a material amount of the boehmite of the shaped particle is converted to a crystalline transitional phase other than gamma-alumina to thereby provide a calcined shaped particle.
  • the calcined shaped particle is impregnated with a hydrogenation catalytic component to thereby provide an impregnated calcined shaped particle that is calcined to thereby provide the catalyst composition.
  • In accordance with yet another invention is a process for manufacturing a low sulfur distillate product by contacting under hydrodesulfurization conditions a middle distillate hydrocarbon feedstock having a high sulfur concentration with the aforedescribed catalyst or a catalyst made by the aforedescribed method and yielding a low sulfur middle distillate product having a low sulfur concentration.
  • FIG. 1 presents the X-ray diffraction spectrum for a shaped support calcined at a calcination temperature of 750° F.
  • FIG. 2 presents the X-ray diffraction spectrum for a shaped support calcined at a calcination temperature of 850° F.
  • FIG. 3 presents the X-ray diffraction spectrum for a shaped support calcined at a calcination temperature of 900° F.
  • FIG. 4 presents plots of the reaction temperature required for the desulfurization of a diesel feed stock under certain test conditions to yield a diesel product having a 10 ppm sulfur concentration as a function of catalyst age for an inventive catalyst and for a comparative catalyst.
  • FIG. 4 presents a contour plot with each contour line representing a single sulfur concentration of a desulfurized middle distillate product resulting from the use of a catalyst made by an embodiment of the inventive method which uses a carefully controlled heat treatment of the catalyst support followed by a carefully controlled heat treatment of the impregnated heat treated catalyst support.
  • a novel catalyst composition has been discovered that has a particularly high activity when used in the hydrodesulfurization of a hydrocarbon distillate feed stock, such as, for example, diesel oil, that has a high concentration of sulfur or sulfur compounds such as organosulfur compounds.
  • This catalyst composition can provide for significantly improved diesel desulfurization activity when compared to other known hydrodesulfurization catalyst compositions. It is especially useful in the manufacture of an ultra-low sulfur diesel product that has a sulfur concentration of less than 15 parts per million (ppm) and even less than 10 ppm or less than 8 ppm.
  • the inventive high activity catalyst composition is a supported catalyst in which a hydrogenation component is supported on a specially made shaped support that comprises gamma ( ⁇ ) alumina.
  • This shaped support can have a material absence of the transition alumina phases of delta ( ⁇ ) alumina, theta ( ⁇ ) alumina and kappa ( ⁇ ) alumina.
  • the shaped support further can have a material absence of aluminum hydrate, and it can even further have a material absence of aluminum hydrate and transition alumina phases other than gamma alumina.
  • the shaped support of the inventive catalyst composition can comprise gamma alumina and have a material absence of aluminum hydroxide and forms of transitional crystalline phases of alumina other than gamma alumina.
  • the shaped support upon or into which is incorporated the hydrogenation catalytic component, has a material absence of the transitional crystalline phases of alumina, such as, for example, alpha ( ⁇ ) alumina, delta ( ⁇ ) alumina, eta ( ⁇ ) alumina, kappa ( ⁇ ) alumina, and theta ( ⁇ ) alumina, and additionally, a material absence of aluminum hydroxide, such as, for example, alpha mono aluminum monohydrate (boehmite).
  • alumina such as, for example, alpha ( ⁇ ) alumina, delta ( ⁇ ) alumina, eta ( ⁇ ) alumina, kappa ( ⁇ ) alumina, and theta ( ⁇ ) alumina
  • aluminum hydroxide such as, for example, alpha mono aluminum monohydrate (boehmite).
  • a particularly important aspect of the inventive method for preparing the catalyst composition includes the use of certain starting materials and the formation of a shaped particle that is heat treated under carefully controlled temperature and heat treatment conditions so as to provide a heat treated shaped particle having the desired composition required for forming the final catalyst composition having high activity when used for the desulfurization of a distillate feed stock.
  • the controlled heat treatment of the shaped particle is followed by the incorporation of the catalytic component into the heat treated shaped particle and a second carefully controlled temperature and heat treatment step.
  • the starting material used in preparing the shaped support particle of the catalyst composition is selected from among aluminum hydroxides, which are also referred to by those skilled in the art and herein as alumina hydrate or hydrated alumina, that when prepared and treated in accordance with the particular features of the inventive preparation method will provide a heat treated support particle and catalyst composition having a high hydrodesulfurization activity.
  • aluminum hydroxides are commercially available, but the preferred aluminum hydroxide for use in preparing the shaped support particle is alpha alumina monohydrate, which is also referred to as boehmite, having the chemical formula ⁇ -AlO(OH).
  • the starting boehmite material used in the preparing the shaped support particle is in the form of a powder, and it is particularly desirable for the boehmite material to be a high purity boehmite with more than 98 percent and even more than 99 percent of the boehmite material being in the form of alpha alumina monohydrate. It is also desirable for the boehmite material to contain less than small amounts of impurities, such as, silicon dioxide (SiO 2 ), iron oxide (Fe 2 O 3 ) and alkali (Na 2 O) and alkaline earth (MgO) metals.
  • impurities such as, silicon dioxide (SiO 2 ), iron oxide (Fe 2 O 3 ) and alkali (Na 2 O) and alkaline earth (MgO) metals.
  • the silicon dioxide should be present in the boehmite material at a concentration of less than 200 ppm, and, preferably, less than 150 ppm. But, typically, the silicon dioxide may be present in the range of from 80-130 ppm.
  • the iron oxide should be present in the boehmite material at a concentration of less than 200 ppm, but, typically, the concentration may be present in the range of from 50 to 150 ppm.
  • the alkali metal should be present at a concentration of less than 50 ppm, but, typically, it may be present in the range of from 5 to 40 ppm.
  • the shaped support of the starting material may be formed by any suitable method known to those skilled in the art; provided, that a shaped particle of the starting support material can be subsequently heat treated in accordance with the invention to provide a heat treated shaped support particle having the necessary properties of the invention.
  • suitable method known to those skilled in the art; provided, that a shaped particle of the starting support material can be subsequently heat treated in accordance with the invention to provide a heat treated shaped support particle having the necessary properties of the invention.
  • known shaping methods include tableting, pelletizing, and extrusion methods.
  • the starting aluminum hydroxide material is mixed with water and, if required, a suitable acid compound, in proportions and in a manner so as to form an extrudable paste suitable for extruding through an extrusion die to thereby form an extrudate.
  • the weight ratio of aluminum hydroxide-to-water mixed together to form the extrudable paste is in the range of from 0.1:1 to 10:1, but, more typically, the weight ratio of aluminum hydroxide-to-water is in the range of from 0.5:1 to 5:1.
  • the preferred weight ratio of aluminum hydroxide-to-water used to form the extrudable paste is in the range of from 0.75:1 to 3:1, and, most preferred, it is in the range of from 1:0 to 2:0.
  • the acid compound added to the mixture of aluminum hydroxide and water can be any suitable acid that assists in the formation of a suitable extrudable paste, and it is generally used to control the pH of the mixture to within the range of from 3 to 7. Strong mineral acids, such as nitric acid, may be used, but the preferred acid is acetic acid.
  • the formed extrudate used as the shaped support particle of the invention may have any cross-sectional shape such as cyclinderical shapes, polylobal shapes or any other suitable shape.
  • a typical size of extrudate has a cross-sectional diameter in the range of from about 1/10 inch to 1/32 inch and a length-to-diameter ratio in the range of from 2:1 to 5:1.
  • the preferred shape is a tri-lobe.
  • the shaped support particle prefferably substantially entirely comprise aluminum hydroxide, exclusive of the water content.
  • the preferred form of the aluminum hydroxide is boehmite, and especially preferred is high purity boehmite.
  • the shaped particle will comprise at least 90 weight percent aluminum hydroxide, wherein the weight percent is based upon the dry weight of the shaped support particle, i.e., the weight percent is based on the total weight of the shaped support particle exclusive of the weight of the water contained in the shaped support particle. It is preferred, however, for the shaped particle to comprise at least 95 weight percent aluminum hydroxide, and, most preferred, the shaped particle can comprise at least 98 weight percent aluminum hydroxide.
  • the shaped support particle is then heat treated under treatment conditions that include the careful control of the temperature conditions so as to assure that the resulting heat treated shaped support particle does not contain undesirable amounts of delta alumina and theta aluminum and, even, other phases of alumina; and, preferably, so as to assure that essentially all the aluminum hydrate is converted to an alumina phase, which is preferably the gamma alumina phase. Therefore, the heat treatment temperature is controlled during the heat treatment of the shaped particle to within a specific temperature range to give a heat treated shaped particle having a material absence of the transition alumina phases of delta ( ⁇ ) alumina, eta ( ⁇ ) alumina, theta ( ⁇ ) alumina and kappa ( ⁇ ) alumina.
  • the carefully controlled heat treatment of the shaped support it further can have a material absence of aluminum hydroxide, and even a material absence of aluminum hydroxide and a material absence of transition alumina phases other than gamma alumina.
  • the temperature at which the heat treatment is conducted is controlled to within a narrow range and for a heat treatment time period so as to provide the heat treated shaped particle that has the properties as described herein.
  • the temperature during the heat treatment be can controlled to within the range of from about 850° F. to about 950° F. for a heat treatment time period in the range of from about 0.5 hours to about 72 hours or even a longer time period as is required to provide the necessary conversion of the starting aluminum hydroxide material to the desired alumina phase. More specifically, the controlled temperature condition is controlled so that the heat treatment temperature does not exceed 940° F.
  • the controlled heat treatment temperature should not exceed 920° F., and, most preferred, the controlled heat treatment temperature should not exceed 910° F.
  • the controlled heat treatment temperature should exceed 850° F., and, preferably, the controlled heat treatment temperature should exceed 875° F. Most preferably, the controlled heat treatment temperature should exceed 890° F.
  • the relevant component is not present therein in an amount that significantly affects the ultimate catalytic properties of the final catalyst composition of the invention. It is believed that the significant presence of various phases of alumina other than gamma alumina and of aluminum hydrate in the heat treated shaped particle used to make the final catalyst composition can have a negative impact on the diesel hydrodesulfurization activity of the final catalyst composition. Thus, while small amounts of the alumina phases other than gamma alumina and of aluminum hydrate may be present in the heat treated shaped particle used in the preparation of the final catalyst composition, such amounts should be insignificant so that they do not materially negatively affect the activity of the final catalyst.
  • less than 5 weight percent of the alumina of the heat treated shaped particle is in a crystalline alumina phase other than gamma alumina, such as the alumina phases of delta alumina, theta alumina, eta alumina, kappa alumina and alpha alumina, and preferably less than 2 weight percent, and, most preferably, less than 1 weight percent, of the alumina of the heat treated shaped particle is in a crystalline transitional phase other than gamma alumina.
  • the heat treated shaped particle contain a material absence of aluminum hydroxide. Therefore, a substantial portion of the aluminum hydroxide contained in the shaped particle prior to its heat treatment should be converted by the heat treatment to a crystalline phase of alumina, preferably, gamma alumina.
  • the heat treated shaped particle thus, should contain an insubstantial amount of aluminum hydroxide, for instance, less than 5 weight percent based on the total weight of the heat treated shaped particle.
  • the heat treated shaped particle contains less than 2 weight percent, and, most preferably, less than 1 weight percent aluminum hydroxide.
  • the heat treated shaped particle has a specific pore structure including a characteristic median pore diameter, total pore volume and pore size distribution.
  • the median pore diameter of the heat treated shaped particle is in the range of from about 70 angstroms to 120 angstroms, but, preferably, the median pore diameter is in the range of from 80 angstroms to 110 angstroms. More preferably, the median pore diameter of the heat treated shaped particle is in the range of from 90 angstroms to 100 angstroms.
  • the total pore volume of the heat treated shaped particle is generally in the range of from about 0.5 cubic centimeters per gram (cc/gram) to about 1.1 cc/gram.
  • the total pore volume is in the range of from 0.6 cc/gram to 1 cc/gram, and, most preferably, from 0.7 cc/gram to 0.9 cc/gram.
  • the percentage of the total pore volume contained in the pores of the heat treated shaped particle having a pore diameter less than 80 angstroms is less than 25 percent and, among these pores, less than 3 percent of the total pore volume of the heat treated shaped particle is in the pores having a diameter smaller than 50 angstroms.
  • the pores having a diameter between 80 angstroms to 350 angstroms more than 70 percent of the total pore volume of the heat treated shaped particle is contained in such pores. It is preferred, however, for at least 75 percent, and, most preferred, at least 80 percent, of the total volume to be in the pores having a diameter between 80 to 350 angstroms. Less than 3 percent of the total pore volume of the heat treated shaped particle is in the pores having a pore diameter greater than 350 angstroms.
  • the references herein to the pore size distribution and pore volume of the alumina support material are to those properties as determined by mercury penetration porosimetry.
  • the measurement of the pore size distribution of the alumina support material is by any suitable measurement instrument using a contact angle of 140° with a mercury surface tension of 474 dyne/cm at 25° C.
  • the catalytic components are incorporated into the heat treated shaped particle, which is thereafter subjected to a second heat treatment, again, under carefully controlled heat treatment conditions so as to assure that an insignificant amount of the alumina support is converted to undesirable crystalline alumina phases.
  • Any suitable means or method may be used to incorporate the catalytic components into the heat treated shaped particle, but any of the known impregnation methods, such as, spray impregnation, soaking, multi-dip procedures, and incipient wetness impregnation methods, are preferred.
  • the catalytic components include hydrogenation catalytic components such as those selected from Group 6 of the IUPAC Periodic Table of the Elements (e.g.
  • chromium Cr
  • molybdenum Mo
  • tungsten W
  • Groups 9 and 10 of the IUPAC Periodic Table of the Elements e.g. cobalt (Co) and nickel (Ni)
  • Phosphorus (P) is also a desired catalytic component.
  • the catalytic components may be incorporated into the heat treated shaped particle using one or more impregnation solutions containing one or more of the catalytic components.
  • the preferred impregnation solution is an aqueous solution of the desired catalytic component or precursor thereof.
  • a Group 9 or 10 metal Group 9 or 10 metal acetates, carbonates, nitrates, and sulfates or mixtures of two or more thereof may be used, with the preferred compound being a metal nitrate such as nitrates of nickel or cobalt.
  • a salt of the Group 6 metal which may be a precursor of the metal oxide or sulfide, may be used in the impregnation solution.
  • concentration of the metal compounds in the impregnation solution is selected so as to provide the desired metal concentration in the final catalyst composition of the invention.
  • concentration of the metal compound in the impregnation solution is in the range of from 0.01 to 100 moles per liter.
  • the amounts of catalytic metal compound and, if desired, phosphorous compound, incorporated or impregnated into the heat treated shaped particle is such that when the impregnated, heat treated shaped particle is subsequently subjected to a heat treatment, the final catalyst composition of the invention has the desired concentrations of the catalytic components.
  • the amount of Group 6 metal contained in the final catalyst composition generally should be in the range of from about 3 to about 30, preferably from 4 to 27, and, most preferably, from 5 to 20 weight percent, calculated as a Group 6 metal trioxide and based on the total weight of the final catalyst composition inclusive of the catalytic components.
  • the amount of Group 9 or 10 metal contained in the final catalyst composition generally should be in the range of from about 0.01 to about 10, preferably from 0.1 to 8, and, most preferably, from 1 to 6 weight percent, calculated as a Group 9 or 10 metal monoxide and based on the total weight of the final catalyst composition inclusive of the catalytic components. If the final catalyst contains a phosphorous component, it is present at a concentration in ther range of from about 0.01 to about 5 weight percent, calculated as phosphorous.
  • the heat treatment of the impregnated heat treated shaped particle, as in the heat treatment of the shaped particle, is also conducted under carefully controlled heat treatment temperature conditions so as to assure that an insignificant portion of the alumina therein is converted to the undesirable crystalline transitional phases of alumina.
  • one embodiment of the invention includes the combined use of specific heat treatment conditions for each of the two heat treatment steps to provide the final catalyst having unexpectedly better middle distillate hydrodesulfurization catalytic performance. It has been found that an unexpected improvement in the desulfurization performance of the final catalyst is achieved when the temperature conditions of the second heat treatment step shifted to somewhat higher temperatures than those used in the first heat treatment step.
  • a final catalyst having especially good middle distillate desulfurization properties is obtained when the temperature range of the first heat treatment step to yield the heat treated particle is, as discussed above, from about 850° F. to about 950° F. and the temperature range of the second heat treatment step to yield the final catalyst is from about 870° F. to about 1000° F.
  • a preferred temperature range at which the second heat treatment step is conducted is from 880° F. to 990° F., and, most preferred, from 900° F. to 980° F.
  • the second heat treatment step is conducted for a time period necessary to provide the desired final catalyst composition and can generally be in the range of from about 0.5 hours to about 72 hours.
  • the upper limit for the temperature for the second heat treatment step should be no more than about 35° C. (63° F.) above the upper temperature limit of the first heat treatment step, and, preferably, it is no more than 30° C. (54° F.). Most preferably, the upper temperature limit for the second heat treatment step in which the impregnated heat treated shaped particle is heat treated is no more than 25° C. (45° F.) of the upper temperature limit of the first heat treatment step.
  • the final catalyst composition i.e., the impregnated heat treated shaped particle that itself has been heat treated, has a specific pore structure including a characteristic median pore diameter, total pore volume and pore size distribution.
  • the median pore diameter of the final catalyst composition is in the range of from about 80 angstroms to 110 angstroms, but, preferably, the median pore diameter is in the range of from 85 angstroms to 105 angstroms. More preferably, the median pore diameter of the final catalyst composition is in the range of from 90 angstroms to 100 angstroms.
  • the total pore volume of the final catalyst composition is generally in the range of from about 0.6 cubic centimeters per gram (cc/gram) to about 1.1 cc/gram.
  • the total pore volume is in the range of from 0.65 cc/gram to 1 cc/gram, and, most preferably, from 0.7 cc/gram to 0.9 cc/gram.
  • the percentage of the total pore volume contained in the pores of the final catalyst composition having a pore diameter less than 80 angstroms is less than 25 percent and, among these pores, less than 3 percent of the total pore volume of the final catalyst composition is in the pores having a diameter smaller than 50 angstroms.
  • the pores having a diameter between 80 angstroms to 350 angstroms more than 70 percent of the total pore volume of the final catalyst composition is contained in such pores. It is preferred, however, for at least 75 percent, and, most preferred, at least 80 percent, of the total volume to be in the pores having a diameter between 80 to 350 angstroms. Less than 3 percent of the total pore volume of the final catalyst composition is in the pores having a pore diameter greater than 350 angstroms.
  • the catalyst composition of the invention is particularly suitable for use in a process for the hydrodesulfurization of a middle distillate hydrocarbon feed stock, having a concentration of sulfur or sulfur compounds, in order to make a low sulfur middle distillate hydrocarbon product. More specifically, the catalyst composition may be used in a process for the manufacture of an ultra-low sulfur diesel product having a sulfur concentration of less than 15 ppm, preferably, less than 10 ppm, and, most preferably, less than 8 ppm.
  • the middle distillate hydrocarbon feed stock as referred to herein is intended to include refinery hydrocarbon streams having boiling temperatures at atmospheric pressure in the range of from about 140° C. (284° F.) to about 410° C. (770° F.). These temperatures are approximate initial and final boiling temperatures of the middle distillate.
  • Examples of the refinery streams intended to be included within the meaning of middle distillate hydrocarbon include straight run distillate fuels boiling in the referenced boiling range, such as, kerosene, jet fuel, light diesel oil, heating oil, and heavy diesel oil, and the cracked distillates, such as FCC cycle oil, coker gas oil, and hydrocracker distillates.
  • the preferred feedstock of the inventive process is a middle distillate boiling in the diesel boiling range of from about 140° C. (284° F.) to about 400° C. (752° F.).
  • the sulfur concentration of the middle distillate feedstock can be a high concentration, for instance, being in the range of upwardly to about 2 weight percent of the middle distillate feedstock based on the weight of elemental sulfur and the total weight of the middle distillate feedstock inclusive of the sulfur compounds.
  • the middle distillate feedstock of the inventive process has a sulfur concentration in the range of from 0.01 wt. % (100 ppm) to 1.8 wt. % (18,000 ppm). But, more typically, the sulfur concentration is in the range of from 0.1 wt. % (1000 ppm) to 1.6 wt. % (16,000 ppm), and, most typically, from 0.18 wt. % (1800 ppm) to 1.1 wt.
  • the final catalyst of the invention may be employed as a part of any suitable reactor system that provides for the contacting of the catalyst with the middle distillate feedstock under suitable hydrodesulfurization reaction conditions that include the presence of hydrogen and an elevated total pressure and temperature.
  • suitable reactor systems can include fixed catalyst bed systems, ebullating catalyst bed systems, slurried catalyst systems, and fluidized catalyst bed systems.
  • the preferred reactor system is that which includes a fixed bed of the inventive final catalyst composition contained within a reactor vessel equipped with an reactor feed inlet means, such as a feed inlet nozzle, for introducing the feedstock into the reactor vessel, and a reactor effluent outlet means, such as an effluent outlet nozzle, for withdrawing the reactor effluent or the low sulfur distillate product from the reactor vessel.
  • the hydrodesulfurization reaction temperature is generally in the range of from about 200° C. (392° F.) to 420° C. (788° F.).
  • the preferred hydrodesulfurization reaction temperature is in the range of from 260° C. (500° F.) to 400° C. (752° F.), and, most preferred, from 320° C. (608° F.) to 380° C. (716° F.). It is recognized that one of the unexpected features of the use of the inventive catalyst composition is that it has a higher hydrodesulfurization activity than certain conventional catalysts, and, thus, will in general provide for a comparatively lower process temperature than such conventional catalysts.
  • the inventive process generally operates at a hydrodesulfurization reaction pressure in the range of from about 100 psig to about 2000 psig, preferably, from 275 psig to 1500 psig, and, most preferably, from 290 psig to 1000 psig.
  • the flow rate at which the distillate feedstock is charged to the reaction zone of the inventive process is generally such as to provide a liquid hourly space velocity (LHSV) in the range of from about 0.1 hr ⁇ 1 upwardly to about 10 hr ⁇ 1 .
  • LHSV liquid hourly space velocity
  • weight average space velocity means the numerical ratio of the rate at which the distillate feedstock is charged to the reaction zone of the process in volume per hour divided by the volume of catalyst composition contained in the reaction zone to which the distillate feedstock is charged.
  • the preferred LHSV is in the range of from 0.1 hr ⁇ 1 to 250 hr ⁇ 1 , and, most preferred, from 0.5 hr ⁇ 1 to 5 hr ⁇ 1 .
  • the hydrogen treat gas rate is the amount of hydrogen charged to reaction zone with the distillate feedstock.
  • the amount of hydrogen relative to the amount of distillate hydrocarbon feedstock charged to the reaction zone is in the range upwardly to about 10,000 cubic meters hydrogen per cubic meter of distillate hydrocarbon feedstock.
  • the desulfurized middle distillate product yielded from the process of the invention has a low or reduced sulfur concentration relative to the high sulfur concentration of the middle distillate feedstock.
  • One particularly advantageous aspect of the inventive process is that it is capable of more economically providing for a deeply desulfurized diesel product or an ultra low sulfur diesel product.
  • the low sulfur middle distillate product can have a sulfur concentration that is less than 25 ppm.
  • the ultra low sulfur diesel product can have a sulfur concentration that is less than 15 ppm.
  • the low sulfur middle distillate product and ultra low sulfur diesel product has a sulfur concentration of less than 10 ppm, and, most preferably, less than 8 ppm.
  • This Example 1 describes the preparation of the alumina support used in the making of the final catalyst composition of the invention.
  • the alumina support was calcined at various calcination temperatures in order to determine the effect that calcination temperature has on the properties of the calcined support used to make the final catalyst composition of the invention and upon the catalytic performance of the final catalyst composition of the invention.
  • the shaped support was prepared first by dissolving 150 parts by weight Ni(NO 3 ) 2 ⁇ 6H 2 O in 52 parts by weight deionized water with heating to form a nickel nitrate solution.
  • the nickel nitrate solution was mixed with 3000 parts by weight (on dry basis) of wide pore alumina and 30 parts by weight Superfloc 16 extrusion aid using a muller mixer.
  • the components were mixed for a sufficient period of time to provide an extrudable paste.
  • the resulting paste was extruded through 1.3 mm extrusion dies to form extrusion particles of the shaped support.
  • a 700 gram sample of the shaped support was calcined at a temperature of 750° F. in a muffle furnace for a time period of two hours to thereby provide a calcined shaped support (Sample A).
  • a 700 gram sample of the shaped support was calcined at a temperature of 900° F. in a muffle furnace for a time period of two hours to thereby provide a calcined shaped support (Sample C).
  • Table 1 Presented in Table 1 are certain of the physical properties of the calcined samples described above. Presented in Table 2 is the pore size distribution as determined by mercury porosimetry of the calcined samples. TABLE 1 Various properties of the samples of shaped support calcined at different temperatures. Pore Diameter Calcination Temperature ( ⁇ ) 750° F. (399° C.) 850° F. (454° C.) 900° F.
  • FIGS. 1, 2 and 3 each presents the X-ray diffraction spectrum for each of the samples of shaped support calcined at the different temperatures (i.e., Sample A, Sample B and Sample C).
  • the spectrum of Sample C indicates that it has no significant amount of boehmite present; however, the spectra for Samples A ( FIG. 1 ) and B ( FIG. 2 ) indicate that they both contain a significant amount of boehmite.
  • the spectrum of Sample C indicates that it is predominantly gamma alumina with little, if any, amounts of other phases of alumina being present.
  • Example 2 describes the preparation of catalyst compositions using the calcined samples described in Example 1. These catalyst compositions were used in the hydrodesulfurization activity tests presented in the following Example 3.
  • the catalyst compositions were prepared by impregnating the samples of Example 1 with an impregnation solution followed by drying the impregnated samples and calcination of the dried, impregnated samples.
  • the impregnation solution was prepared by combining within a container vessel 34 parts by weight molybdenum trioxide (MoO 3 ), 8 parts by weight of 86.1% phosphoric acid (H 3 PO 4 ), and 77 parts by weight deionized water. The mixture was heated to 180° F. followed by the addition of 9 parts by weight cobalt hydroxide (Co(OH) 2 ). The solution was then heated to 212° F. followed by the addition of 4 parts by weight citric acid monohydrate. The container was then covered and the solution was heated until it became clear. The container was then uncovered and the solution was heated to reduce the volume thereof.
  • MoO 3 molybdenum trioxide
  • H 3 PO 4 86.1% phosphoric acid
  • deionized water 77 parts by weight deionized water.
  • This Example 3 describes the experimental procedure used to measure the performance of certain catalyst compositions prepared as described in the above Examples 1 and 2 in the hydrodesulfurization of a diesel feedstock having a high concentration of sulfur (1.6 wt. %).
  • a laboratory stainless steel isothermal tube reactor having a nominal diameter of 3 ⁇ 4 inch, was packed with a 100 cc volume of the relevant catalyst.
  • the catalyst was presulfided by adding 68 grams of TNPS to 1000 grams of the feedstock.
  • the feed was introduced to the reactor at a rate so as to provide an LHSV of 1 hr ⁇ 1 , and hydrogen was introduced at a rate of 19.6 liters/hr.
  • the reactor temperature was ramped up over a 5 hour period to 400° F. and held at 400° F. for a period of 4 hours. Thereafter, the temperature was ramped up to 650° F. over a 4 hour period and then held at 650° F. for two hours.
  • the feedstock used was a straight run gas oil containing 1.6 weight percent sulfur having ASTM D2887 distillation as presented in the following Table 3.
  • the reactor was operated at a pressure of 300 psig, the feed rate was adjusted to provide a liquid hourly space velocity of 0.5, and the hydrogen gas feed rate was 1200 standard cubic feed per barrel of feed (based at 60° F.).
  • the reactor temperature was adjusted so as to provide an ultra low sulfur diesel product having a sulfur concentration of 10 ppmw.
  • FIG. 4 presents plots of the reaction temperature required for the desulfurization of the gas oil feedstock to yield a product having a sulfur concentration of 10 ppmw as a function of the age for a representative inventive catalyst and for a comparative catalyst.
  • the inventive catalyst demonstrates a significantly higher hydrodesulfurization activity than does the comparative catalyst by requiring a lower hydrodesulfurization temperature, which in some cases is as much as 20° F. to 30° F. lower.
  • Example 4 describes, in general, the approach used to develop a prediction model for predicting the sulfur concentration of a desulfurized middle distillate feedstock obtained using various catalysts prepared generally in accordance with the method as described in Example 2.
  • contour plot of FIG. 5 A graphical representation of the results of this study is presented in the contour plot of FIG. 5 .
  • the X-axis of the contour plot is the temperature at which the support material used in the preparation of the final catalyst was calcined, and the Y-axis is the temperature at which the impregnated calcined support material was calcined.
  • Each contour line represents a sulfur concentration of the desulfurized middle distillate feedstock resulting from the use of a final catalyst composition prepared using the inventive two-step heat treatment method at the two different calcination temperatures.
  • the contour lines are a best fit of a number of data points used to generate the contour plot.
  • the best performing catalysts are those prepared using a support material calcined at a calcination temperature in the range of from about 850° F. to 1000° F., which the calcined support material has been impregnated, dried and calcined at a temperature in the range of from about 880° F. to 1000° F.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • General Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Catalysts (AREA)
  • Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
US10/943,756 2004-09-17 2004-09-17 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product Abandoned US20060060510A1 (en)

Priority Applications (15)

Application Number Priority Date Filing Date Title
US10/943,756 US20060060510A1 (en) 2004-09-17 2004-09-17 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
EP05796545A EP1789182B1 (en) 2004-09-17 2005-09-15 Method of making a high activity hydrodesulfurization catalys
PCT/US2005/033248 WO2006034073A1 (en) 2004-09-17 2005-09-15 A high activity hydrodesulfurization catalyst, a method of making said catalyst, and a process for manufacturing an ultra-low sulfur middle distillate fuel
CA2580451A CA2580451C (en) 2004-09-17 2005-09-15 A high activity hydrodesulfurization catalyst, a method of making said catalyst, and a process for manufacturing an ultra-low sulfur middle distillate fuel
CNA2005800349670A CN101076399A (zh) 2004-09-17 2005-09-15 高活性加氢脱硫催化剂、制备所述催化剂的方法和生产超低硫中间馏分燃料的方法
RU2007114294/04A RU2377067C2 (ru) 2004-09-17 2005-09-15 Высокоактивный катализатор гидрообессеривания, способ его изготовления и способ получения среднего топливного дистиллята с ультранизким содержанием серы
BRPI0515365-4A BRPI0515365A (pt) 2004-09-17 2005-09-15 catalisador de hidrodessulfurização de alta atividade, método de preparação do referido catalisador, e processo de preparação de um combustìvel destilado médio com teor ultrabaixo de enxofre
KR1020077008519A KR20070057945A (ko) 2004-09-17 2005-09-15 고도 활성 수첨탈황 촉매, 이 촉매의 제조방법 및 초저황중간 증류 연료의 제조방법
ES05796545T ES2383378T3 (es) 2004-09-17 2005-09-15 Método de obtención de catalizadores de hidrodesulfuración de elevada actividad
JP2007532522A JP5036542B2 (ja) 2004-09-17 2005-09-15 高活性水素化脱硫触媒、前記触媒の製造方法、および超低硫黄中間留分燃料の製造方法
DK05796545.1T DK1789182T3 (da) 2004-09-17 2005-09-15 Fremgangsmåde til fremstilling af højaktiv hydro-afsvovlingskatalysator
AT05796545T ATE555849T1 (de) 2004-09-17 2005-09-15 Verfahren zur herstellung eines hochaktiven hydro-entschwefelungs-katalysators
ZA200702000A ZA200702000B (en) 2004-09-17 2007-03-07 A high activity hydrodesulfurization catalyst, a method of making said catalyst, and a process for manufacturing an ultra-low sulfur distillate fuel
US13/558,056 US8618015B2 (en) 2004-09-17 2012-07-25 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US14/082,687 US9540573B2 (en) 2004-09-17 2013-11-18 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US10/943,756 US20060060510A1 (en) 2004-09-17 2004-09-17 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/558,056 Division US8618015B2 (en) 2004-09-17 2012-07-25 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product

Publications (1)

Publication Number Publication Date
US20060060510A1 true US20060060510A1 (en) 2006-03-23

Family

ID=35431248

Family Applications (3)

Application Number Title Priority Date Filing Date
US10/943,756 Abandoned US20060060510A1 (en) 2004-09-17 2004-09-17 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US13/558,056 Expired - Lifetime US8618015B2 (en) 2004-09-17 2012-07-25 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US14/082,687 Expired - Lifetime US9540573B2 (en) 2004-09-17 2013-11-18 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product

Family Applications After (2)

Application Number Title Priority Date Filing Date
US13/558,056 Expired - Lifetime US8618015B2 (en) 2004-09-17 2012-07-25 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US14/082,687 Expired - Lifetime US9540573B2 (en) 2004-09-17 2013-11-18 High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product

Country Status (13)

Country Link
US (3) US20060060510A1 (ru)
EP (1) EP1789182B1 (ru)
JP (1) JP5036542B2 (ru)
KR (1) KR20070057945A (ru)
CN (1) CN101076399A (ru)
AT (1) ATE555849T1 (ru)
BR (1) BRPI0515365A (ru)
CA (1) CA2580451C (ru)
DK (1) DK1789182T3 (ru)
ES (1) ES2383378T3 (ru)
RU (1) RU2377067C2 (ru)
WO (1) WO2006034073A1 (ru)
ZA (1) ZA200702000B (ru)

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050133416A1 (en) * 2003-12-19 2005-06-23 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20060234877A1 (en) * 2005-04-11 2006-10-19 Bhan Opinder K Systems, methods, and catalysts for producing a crude product
US20080083650A1 (en) * 2006-10-06 2008-04-10 Bhan Opinder K Methods for producing a crude product
WO2009039020A1 (en) * 2007-09-18 2009-03-26 Shell Oil Company Process for the deep desulfurization of heavy pyrolysis gasoline
US20100155301A1 (en) * 2008-12-18 2010-06-24 Ifp Hydrodemetallization and hydrodesulphurization catalysts, and use in a single formulation in a concatenated process
US20100155293A1 (en) * 2008-12-18 2010-06-24 Ifp Hydrocracking process including switchable reactors with feedstocks containing 200 ppm by weight - 2% by weight of asphaltenes
US7745369B2 (en) 2003-12-19 2010-06-29 Shell Oil Company Method and catalyst for producing a crude product with minimal hydrogen uptake
US20110226671A1 (en) * 2003-12-19 2011-09-22 Opinder Kishan Bhan Method for producing a crude product
WO2012174094A1 (en) 2011-06-14 2012-12-20 Shell Oil Company Aqueous catalyst sulfiding process
US20130309574A1 (en) * 2012-05-16 2013-11-21 Shin-Etsu Chemical Co., Ltd. Silicon oxide particles, making method, lithium ion secondary battery, and electrochemical capacitor
US8618015B2 (en) 2004-09-17 2013-12-31 Shell Oil Company High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US10118158B2 (en) 2013-04-17 2018-11-06 Shell Oil Company Process and catalyst for the hydrotreatment of a heavy hydrocarbon feedstock
US10533141B2 (en) 2017-02-12 2020-01-14 Mag{tilde over (e)}mã Technology LLC Process and device for treating high sulfur heavy marine fuel oil for use as feedstock in a subsequent refinery unit
US10604709B2 (en) 2017-02-12 2020-03-31 Magēmā Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil from distressed heavy fuel oil materials
US20220033657A1 (en) * 2018-10-03 2022-02-03 Sasol (Usa) Corporation Aluminas and Methods for Producing Same
US11788017B2 (en) 2017-02-12 2023-10-17 Magëmã Technology LLC Multi-stage process and device for reducing environmental contaminants in heavy marine fuel oil
US12025435B2 (en) 2017-02-12 2024-07-02 Magēmã Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil
US12071592B2 (en) 2017-02-12 2024-08-27 Magēmā Technology LLC Multi-stage process and device utilizing structured catalyst beds and reactive distillation for the production of a low sulfur heavy marine fuel oil

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2998488B1 (fr) * 2012-11-29 2015-02-06 Ifp Energies Now Catalyseur d hydrotraitement a partir d alumine gel et methode de preparation d un tel catalyseur
JP6284403B2 (ja) * 2014-03-27 2018-02-28 Ｊｘｔｇエネルギー株式会社 炭化水素油の水素化脱硫触媒
KR101702208B1 (ko) * 2015-02-17 2017-02-14 한밭대학교 산학협력단 연료 전지용 탈황 흡착 촉매 및 그 제조 방법
SG11201806008PA (en) 2016-02-01 2018-08-30 Jgc Catalysts & Chemicals Ltd Hydrogenation treatment catalyst for hydrocarbon oil, method for producing the same, and hydrogenation treatment method
CN105833879B (zh) * 2016-05-03 2018-06-26 中国石油天然气股份有限公司 一种加氢处理催化剂及其制备方法和应用
WO2022147407A1 (en) * 2020-12-29 2022-07-07 Saint-Gobain Ceramics & Plastics, Inc. Ceramic article and methods of making the same

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3669904A (en) * 1970-05-28 1972-06-13 Air Prod & Chem Particles featuring gamma alumina
US3853789A (en) * 1971-03-26 1974-12-10 J Warthen Preparation of macroporous alumina extrudates
US4066574A (en) * 1973-08-09 1978-01-03 Chevron Research Company Hydrocarbon hydrotreating catalyst composition
US4089811A (en) * 1976-11-01 1978-05-16 Texaco Inc. Preparation of catalyst support
US4145316A (en) * 1977-12-27 1979-03-20 Exxon Research & Engineering Co. Preparation of catalysts of predetermined pore size distribution and pore volume
US4271042A (en) * 1977-12-20 1981-06-02 Mobil Oil Corporation Process for demetalation and desulfurization of petroleum oils
US4879265A (en) * 1982-08-19 1989-11-07 Union Oil Company Of California Hydroprocessing catalyst and phosphorous and citric acid containing impregnating solution
US4891350A (en) * 1986-10-27 1990-01-02 Rhone-Poulenc Chimie Catalyst supports and process for their preparation
US5300217A (en) * 1992-04-14 1994-04-05 Union Oil Company Of California Hydroprocess utilizing a delta alumina-supported nickel and molybdenum catalyst

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4440956A (en) * 1982-10-25 1984-04-03 The Dow Chemical Company Selective hydrogenation of acetylenes in the presence of butadiene and catalyst used in the hydrogenation
DE3861642D1 (de) * 1987-07-02 1991-02-28 Sumitomo Metal Mining Co Katalysator zur wasserstoffbehandlung von kohlenwasserstoffen und methode zu dessen herstellung.
DE68926764T2 (de) * 1988-08-19 1996-10-31 Sumitomo Metal Mining Co Kohlenwasserstoffbehandlungskatalysatoren und Verfahren zu deren Herstellung
GB9010075D0 (en) * 1990-05-04 1990-06-27 Shell Int Research Process for the preparation of alumina based extrudates
JP2920255B2 (ja) * 1990-05-21 1999-07-19 住友金属鉱山株式会社 水素化脱硫触媒
JP2900771B2 (ja) 1992-11-18 1999-06-02 住友金属鉱山株式会社 炭化水素油の水素化処理触媒の製造方法
JPH07155597A (ja) * 1993-12-02 1995-06-20 Sumitomo Metal Mining Co Ltd アルミナ触媒担体の製造方法
JP3504984B2 (ja) * 1994-09-19 2004-03-08 日本ケッチェン株式会社 重質炭化水素油の水素化脱硫脱金属触媒
CN1105681C (zh) * 1998-01-30 2003-04-16 日本能源株式会社 假勃姆石及其制备方法
JP2003230837A (ja) * 1998-06-24 2003-08-19 Cosmo Oil Co Ltd 軽油の水素化処理触媒及び軽油の水素化処理方法
TWI248809B (en) 2003-08-06 2006-02-11 Hitachi Ltd Automatic urine disposal device and urine receptacle used therefor
US20060060510A1 (en) 2004-09-17 2006-03-23 Bhan Opinder K High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3669904A (en) * 1970-05-28 1972-06-13 Air Prod & Chem Particles featuring gamma alumina
US3853789A (en) * 1971-03-26 1974-12-10 J Warthen Preparation of macroporous alumina extrudates
US4066574A (en) * 1973-08-09 1978-01-03 Chevron Research Company Hydrocarbon hydrotreating catalyst composition
US4089811A (en) * 1976-11-01 1978-05-16 Texaco Inc. Preparation of catalyst support
US4271042A (en) * 1977-12-20 1981-06-02 Mobil Oil Corporation Process for demetalation and desulfurization of petroleum oils
US4145316A (en) * 1977-12-27 1979-03-20 Exxon Research & Engineering Co. Preparation of catalysts of predetermined pore size distribution and pore volume
US4879265A (en) * 1982-08-19 1989-11-07 Union Oil Company Of California Hydroprocessing catalyst and phosphorous and citric acid containing impregnating solution
US4891350A (en) * 1986-10-27 1990-01-02 Rhone-Poulenc Chimie Catalyst supports and process for their preparation
US5300217A (en) * 1992-04-14 1994-04-05 Union Oil Company Of California Hydroprocess utilizing a delta alumina-supported nickel and molybdenum catalyst

Cited By (83)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7807046B2 (en) 2003-12-19 2010-10-05 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US20090178953A1 (en) * 2003-12-19 2009-07-16 Opinder Kishan Bhan Systems, methods, and catalysts for producing a crude product
US20050133415A1 (en) * 2003-12-19 2005-06-23 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20050139520A1 (en) * 2003-12-19 2005-06-30 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20050139518A1 (en) * 2003-12-19 2005-06-30 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20050155908A1 (en) * 2003-12-19 2005-07-21 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20050167328A1 (en) * 2003-12-19 2005-08-04 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20050167326A1 (en) * 2003-12-19 2005-08-04 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20050167325A1 (en) * 2003-12-19 2005-08-04 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20110226671A1 (en) * 2003-12-19 2011-09-22 Opinder Kishan Bhan Method for producing a crude product
US7955499B2 (en) 2003-12-19 2011-06-07 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US7959796B2 (en) 2003-12-19 2011-06-14 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US20090206005A1 (en) * 2003-12-19 2009-08-20 Opinder Kishan Bhan Systems, methods, and catalysts for producing a crude product
US20050133418A1 (en) * 2003-12-19 2005-06-23 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US8475651B2 (en) 2003-12-19 2013-07-02 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US8137536B2 (en) 2003-12-19 2012-03-20 Shell Oil Company Method for producing a crude product
US7780844B2 (en) 2003-12-19 2010-08-24 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US7745369B2 (en) 2003-12-19 2010-06-29 Shell Oil Company Method and catalyst for producing a crude product with minimal hydrogen uptake
US20090283444A1 (en) * 2003-12-19 2009-11-19 Opinder Kishan Bhan Systems, methods, and catalysts for producing a crude product
US20090288987A1 (en) * 2003-12-19 2009-11-26 Opinder Kishan Bhan Systems, methods, and catalysts for producing a crude product
US8764972B2 (en) 2003-12-19 2014-07-01 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US20050133416A1 (en) * 2003-12-19 2005-06-23 Bhan Opinder K. Systems, methods, and catalysts for producing a crude product
US20090308791A1 (en) * 2003-12-19 2009-12-17 Opinder Kishan Bhan Systems, methods, and cataylsts for producing a crude product
US20090288989A1 (en) * 2003-12-19 2009-11-26 Opinder Kishan Bhan Systems, methods, and catalysts for producing a crude product
US9540573B2 (en) 2004-09-17 2017-01-10 Shell Oil Company High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US8618015B2 (en) 2004-09-17 2013-12-31 Shell Oil Company High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
US7678264B2 (en) 2005-04-11 2010-03-16 Shell Oil Company Systems, methods, and catalysts for producing a crude product
US20060234877A1 (en) * 2005-04-11 2006-10-19 Bhan Opinder K Systems, methods, and catalysts for producing a crude product
US20080083655A1 (en) * 2006-10-06 2008-04-10 Bhan Opinder K Methods of producing a crude product
US20090188836A1 (en) * 2006-10-06 2009-07-30 Opinder Kishan Bhan Methods for producing a crude product
US20090057197A1 (en) * 2006-10-06 2009-03-05 Opinder Kishan Bhan Methods for producing a crude product
WO2008060779A2 (en) 2006-10-06 2008-05-22 Shell Oil Company Methods for producing a crude product
WO2008045755A1 (en) 2006-10-06 2008-04-17 Shell Oil Company Methods for producing a crude product
WO2008045758A1 (en) 2006-10-06 2008-04-17 Shell Oil Company Systems and methods for producing a crude product and compositions thereof
WO2008045757A2 (en) 2006-10-06 2008-04-17 Shell Oil Company Methods for producing a crude product
WO2008045760A1 (en) 2006-10-06 2008-04-17 Shell Oil Company Methods for producing a crude product and compositions thereof
US20080087575A1 (en) * 2006-10-06 2008-04-17 Bhan Opinder K Systems and methods for producing a crude product and compositions thereof
US7749374B2 (en) 2006-10-06 2010-07-06 Shell Oil Company Methods for producing a crude product
US20080087578A1 (en) * 2006-10-06 2008-04-17 Bhan Opinder K Methods for producing a crude product and compositions thereof
WO2008045749A2 (en) 2006-10-06 2008-04-17 Shell Oil Company Methods for producing a crude product
WO2008045750A2 (en) 2006-10-06 2008-04-17 Shell Oil Company Methods of producing a crude product
WO2008045753A2 (en) 2006-10-06 2008-04-17 Shell Oil Company Systems for treating a hydrocarbon feed
US20080085225A1 (en) * 2006-10-06 2008-04-10 Bhan Opinder K Systems for treating a hydrocarbon feed
US20080083650A1 (en) * 2006-10-06 2008-04-10 Bhan Opinder K Methods for producing a crude product
US20100288679A1 (en) * 2007-09-18 2010-11-18 Paul Benjerman Himelfarb Process for the deep desulfurization of heavy pyrolysis gasoline
WO2009039020A1 (en) * 2007-09-18 2009-03-26 Shell Oil Company Process for the deep desulfurization of heavy pyrolysis gasoline
EP3395929A1 (en) 2007-09-18 2018-10-31 Shell Internationale Research Maatschappij B.V. Process for the deep desulfurization of heavy pyrolysis gasoline
US8163167B2 (en) 2007-09-18 2012-04-24 Shell Oil Company Process for the deep desulfurization of heavy pyrolysis gasoline
US8394262B2 (en) 2008-12-18 2013-03-12 IFP Energies Nouvelles Hydrodemetallization and hydrodesulphurization catalysts, and use in a single formulation in a concatenated process
EP2255873A3 (fr) * 2008-12-18 2011-03-30 IFP Energies nouvelles Catalyseurs d'hydrodémétallation et d'hydrodésulfuration et mise en oeuvre dans un procédé d'enchaînement en formulation unique
FR2940143A1 (fr) * 2008-12-18 2010-06-25 Inst Francais Du Petrole Catalyseurs d'hydrodemetallation et d'hydrodesulfuration et mise en oeuvre dans un procede d'enchainement en formulation unique
US20100155293A1 (en) * 2008-12-18 2010-06-24 Ifp Hydrocracking process including switchable reactors with feedstocks containing 200 ppm by weight - 2% by weight of asphaltenes
US20100155301A1 (en) * 2008-12-18 2010-06-24 Ifp Hydrodemetallization and hydrodesulphurization catalysts, and use in a single formulation in a concatenated process
US9523049B2 (en) 2008-12-18 2016-12-20 IFP Energies Nouvelles Hydrocracking process including switchable reactors with feedstocks containing 200 ppm by weight—2% by weight of asphaltenes
CN101822994A (zh) * 2008-12-18 2010-09-08 Ifp公司 加氢脱金属和加氢脱硫催化剂,以及在级联过程中的单个配制剂中的使用
WO2012174094A1 (en) 2011-06-14 2012-12-20 Shell Oil Company Aqueous catalyst sulfiding process
US20130309574A1 (en) * 2012-05-16 2013-11-21 Shin-Etsu Chemical Co., Ltd. Silicon oxide particles, making method, lithium ion secondary battery, and electrochemical capacitor
CN103427075A (zh) * 2012-05-16 2013-12-04 信越化学工业株式会社 硅氧化物颗粒及制作方法、锂离子二次电池以及电化学电容器
US9281129B2 (en) * 2012-05-16 2016-03-08 Shin-Etsu Chemical Co., Ltd. Silicon oxide particles, making method, lithium ion secondary battery, and electrochemical capacitor
US9553309B2 (en) 2012-05-16 2017-01-24 Shin-Etsu Chemical Co., Ltd. Silicon oxide particles, making method, lithium ion secondary battery, and electrochemical capacitor
US10118158B2 (en) 2013-04-17 2018-11-06 Shell Oil Company Process and catalyst for the hydrotreatment of a heavy hydrocarbon feedstock
US10563132B2 (en) 2017-02-12 2020-02-18 Magēmā Technology, LLC Multi-stage process and device for treatment heavy marine fuel oil and resultant composition including ultrasound promoted desulfurization
US11441084B2 (en) 2017-02-12 2022-09-13 Magēmā Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil
US10533141B2 (en) 2017-02-12 2020-01-14 Mag{tilde over (e)}mã Technology LLC Process and device for treating high sulfur heavy marine fuel oil for use as feedstock in a subsequent refinery unit
US10584287B2 (en) 2017-02-12 2020-03-10 Magēmā Technology LLC Heavy marine fuel oil composition
US10604709B2 (en) 2017-02-12 2020-03-31 Magēmā Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil from distressed heavy fuel oil materials
US10655074B2 (en) 2017-02-12 2020-05-19 Mag{hacek over (e)}m{hacek over (a)} Technology LLC Multi-stage process and device for reducing environmental contaminates in heavy marine fuel oil
US10836966B2 (en) 2017-02-12 2020-11-17 Magēmā Technology LLC Multi-stage process and device utilizing structured catalyst beds and reactive distillation for the production of a low sulfur heavy marine fuel oil
US11136513B2 (en) 2017-02-12 2021-10-05 Magëmä Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil from distressed heavy fuel oil materials
US11203722B2 (en) 2017-02-12 2021-12-21 Magëmä Technology LLC Multi-stage process and device for treatment heavy marine fuel oil and resultant composition including ultrasound promoted desulfurization
US12071592B2 (en) 2017-02-12 2024-08-27 Magēmā Technology LLC Multi-stage process and device utilizing structured catalyst beds and reactive distillation for the production of a low sulfur heavy marine fuel oil
US11345863B2 (en) 2017-02-12 2022-05-31 Magema Technology, Llc Heavy marine fuel oil composition
US10563133B2 (en) 2017-02-12 2020-02-18 Magëmä Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil
US11447706B2 (en) 2017-02-12 2022-09-20 Magēmā Technology LLC Heavy marine fuel compositions
US11492559B2 (en) 2017-02-12 2022-11-08 Magema Technology, Llc Process and device for reducing environmental contaminates in heavy marine fuel oil
US11530360B2 (en) 2017-02-12 2022-12-20 Magēmā Technology LLC Process and device for treating high sulfur heavy marine fuel oil for use as feedstock in a subsequent refinery unit
US11560520B2 (en) 2017-02-12 2023-01-24 Magēmā Technology LLC Multi-stage process and device for treatment heavy marine fuel oil and resultant composition and the removal of detrimental solids
US11788017B2 (en) 2017-02-12 2023-10-17 Magëmã Technology LLC Multi-stage process and device for reducing environmental contaminants in heavy marine fuel oil
US11795406B2 (en) 2017-02-12 2023-10-24 Magemä Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil from distressed heavy fuel oil materials
US11884883B2 (en) 2017-02-12 2024-01-30 MagêmãTechnology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil
US11912945B2 (en) 2017-02-12 2024-02-27 Magēmā Technology LLC Process and device for treating high sulfur heavy marine fuel oil for use as feedstock in a subsequent refinery unit
US12025435B2 (en) 2017-02-12 2024-07-02 Magēmã Technology LLC Multi-stage device and process for production of a low sulfur heavy marine fuel oil
US20220033657A1 (en) * 2018-10-03 2022-02-03 Sasol (Usa) Corporation Aluminas and Methods for Producing Same

Also Published As

Publication number Publication date
ES2383378T3 (es) 2012-06-20
RU2007114294A (ru) 2008-10-27
ATE555849T1 (de) 2012-05-15
JP2008513201A (ja) 2008-05-01
WO2006034073A1 (en) 2006-03-30
DK1789182T3 (da) 2012-07-23
BRPI0515365A (pt) 2008-07-22
CA2580451A1 (en) 2006-03-30
KR20070057945A (ko) 2007-06-07
US20120292231A1 (en) 2012-11-22
JP5036542B2 (ja) 2012-09-26
RU2377067C2 (ru) 2009-12-27
EP1789182B1 (en) 2012-05-02
US20140076783A1 (en) 2014-03-20
CN101076399A (zh) 2007-11-21
US8618015B2 (en) 2013-12-31
EP1789182A1 (en) 2007-05-30
US9540573B2 (en) 2017-01-10
ZA200702000B (en) 2008-08-27
CA2580451C (en) 2014-07-08

Similar Documents

Publication Publication Date Title
US9540573B2 (en) High activity hydrodesulfurization catalyst, a method of making a high activity hydrodesulfurization catalyst, and a process for manufacturing an ultra-low sulfur distillate product
EP1347832B1 (en) Hydroprocessing catalyst and use thereof
CA2360121C (en) Hydroprocessing catalyst and use thereof
US10118158B2 (en) Process and catalyst for the hydrotreatment of a heavy hydrocarbon feedstock
US10676680B2 (en) Catalyst for the hydrotreatment of a heavy hydrocarbon feedstock
EP2864042A1 (en) Improved resid hydrotreating catalyst containing titania
US4665048A (en) Catalyst suitable for hydrotreating
US9724677B2 (en) Selenium-containing hydroprocessing catalyst, its use, and method of preparation
US4716140A (en) Hydrotreating catalysts prepared from hydrogels
KR101976224B1 (ko) 수소화처리 촉매 및 이러한 촉매의 제조 방법 및 사용 방법
US4880523A (en) Process for hydrotreating hydrocarbon feeds

Legal Events

Date Code Title Description
STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION