TWI759341B - 樹脂組成物、含樹脂組成物之卡片用樹脂薄片及多層薄片 - Google Patents
樹脂組成物、含樹脂組成物之卡片用樹脂薄片及多層薄片 Download PDFInfo
- Publication number
- TWI759341B TWI759341B TW106135443A TW106135443A TWI759341B TW I759341 B TWI759341 B TW I759341B TW 106135443 A TW106135443 A TW 106135443A TW 106135443 A TW106135443 A TW 106135443A TW I759341 B TWI759341 B TW I759341B
- Authority
- TW
- Taiwan
- Prior art keywords
- resin composition
- resin
- mass
- sheet
- aliphatic polyester
- Prior art date
Abstract
本發明係為實現具有高耐久性及耐熱性的同時，亦能保持其透明性，易加工性亦優良之樹脂組成物，以及使用該樹脂組成物形成之卡片用樹脂薄片，及多層薄片。 上述之課題，係藉由含有2質量%以上且未滿9質量%之脂肪族聚酯化合物及聚碳酸酯樹脂之樹脂組成物而解決。
Description
[0001] 本發明係關於一種具有高耐久性及耐熱性的同時，亦易於加工之樹脂組成物、使用其製造之卡片用樹脂薄片，及多層薄片。
[0002] 一直以來，樹脂膜被使用於ID卡片、電子護照(e-passport)，以及非接觸型IC卡片等中。作為此種樹脂膜的材料，舉例而言，使用聚氯乙烯(PVC)，及聚對苯二甲酸乙二酯類之PET-G等，已廣為人知。 [0003] 又，作為各種卡片用之樹脂組成物，使用聚酯樹脂組成物亦為人熟知(參照專利文獻1)。於專利文獻1中，已揭示含有以PET為主要成分之聚酯樹脂，及芳香族聚碳酸酯樹脂之聚酯樹脂組成物。 [先前技術文獻] [專利文獻] [0004] [專利文獻1] 日本特開2002-97361號公報
[發明所欲解決之課題] [0005] 使用PVC及PET-G等作為卡片用之樹脂組成物的情況下，由於這些樹脂的耐久性及耐熱性並不一定足夠，因此卡片的機械強度將可能成為一項問題。 [0006] 又，於專利文獻1中記載，上述聚酯樹脂組成物係具有耐熱性及耐衝撃性等優點。然而，這樣的聚酯樹脂組成物其透明性較差，使得其印刷部的解析度低下。 [用以解決課題之手段] [0007] 本發明人等，為了解決上述課題而反覆進行積極檢討的結果，發現含有聚碳酸酯之所定的樹脂組成物，其具有高耐久性及耐熱性的同時，亦能保持其透明性，易加工性亦優，而完成本發明。 亦即，本發明係關於以下所示之樹脂化合物、使用聚碳酸酯樹脂組成物所形成之卡片用樹脂薄片，以及多層薄片。 [0008] (1)一種樹脂組成物，其係包含2質量%以上且未滿9質量%之脂肪族聚酯化合物及聚碳酸酯樹脂。 (2)如上述(1)記載之樹脂組成物，其係具有雷射標示性。 (3)如上述(1)記載之樹脂組成物，其玻璃轉移溫度為100~135℃。 (4)如上述(1)~(3)中任一項記載之樹脂組成物，前述脂肪族聚酯化合物中，其係至少包含內酯化合物作為構成單體。 (5)如上述(4)記載之樹脂組成物，其中前述內酯化合物係包含ε-聚己內酯。 (6)如上述(5)記載之樹脂組成物，其中前述內酯化合物係包含主要構成單體為ε-己內酯之聚己內酯。 (7)如上述(1)~(6)中任一項記載之樹脂組成物，其係以樹脂組成物全體之質量為基準，含有3質量%以上，5質量%以下之脂肪族聚酯化合物。 (8)如上述(1)~(7)中任一項記載之樹脂組成物，其中前述脂肪族聚酯化合物之重量平均分子量為10000~90000。 (9)如上述(1)~(8)中任一項記載之樹脂組成物，其係以樹脂組成物全體之質量為基準，含有90質量%以上之聚碳酸酯樹脂。 (10)如上述(1)~(9)中任一項記載之樹脂組成物，其中，前述樹脂組成物係以樹脂組成物全體之質量為基準，更進一步含有10~30質量%之白色顏料。 (11)如上述(1)~(10)中任一項記載之樹脂組成物，其中前述樹脂組成物係更進一步含有雷射呈色劑。 (12)如上述(11)記載之樹脂組成物，其中前述雷射呈色劑係含有碳黑及金屬氧化物的粒子中之至少一者。 (13)如上述(12)記載之樹脂組成物，其中前述金屬氧化物係由下述式(I)表示，
(式(I)中、M為至少一種選自釓及釹之金屬、x為滿足0.001＜x＜0.5之關係之值、y為滿足1＜y＜2.5之關係之值)。 (14)如上述(11)~(13)中任一項記載之樹脂組成物，前述樹脂組成物係以前述樹脂組成物之質量為基準含有0.0001~0.2質量%之前述雷射呈色劑。 (15)一種卡片用樹脂薄片，其係具有包含如上述(1)~(14)中任一項記載之樹脂組成物之層。 (16)如上述(15)記載之卡片用樹脂薄片，其中具有嵌入之天線晶片。 (17)如上述(15)或(16)記載之卡片用樹脂薄片，其係雷射標示卡片用。 (18)一種多層薄片，其係具有兩片以上之積層樹脂薄片之多層薄片，其特徵在於，其至少一層包含上述(1)~(14)中任一項記載之樹脂組成物。 (19)如上述(18)記載之多層薄片，前述多層薄片係進一步含有包含選自由PET-G、聚碳酸酯、PCT-G、PCT及上述至少兩種類以上之混合物所組成之群組之至少一個的樹脂薄片。 [發明的效果] [0009] 本發明之樹脂組成物，包含脂肪族聚酯化合物及聚碳酸酯樹脂，於薄片狀加工時，亦不容易破損，耐衝擊性佳，特別是對於彎曲疲勞具有高耐久性。進一步而言，本發明之樹脂組成物，係具優異的耐熱性及透明性，同時亦容易進行藉由加熱之加工。如上述，本發明之具有優良性質之樹脂組成物，特別適合用於作為卡片用樹脂薄片及多層薄片之材料，例如，適於ID卡片、電子護照(e-passport)，及非接觸型IC卡片等之製造。 [0010] 又，由於本發明之樹脂組成物，與藉由其他樹脂形成之膜，特別是PET-G膜等以聚酯樹脂作為主成分而形成之膜之接著性亦佳，因此亦適用於含有這些膜之積層體之製造。
[0012] 以下對於本發明之實施態樣予以詳細說明。但本發明不受以下實施態樣的任何限定，在本發明之目的的範圍內可加以適當變更來實施。 [0013] [樹脂組成物] 本發明之樹脂組成物，係包含2質量%以上且未滿9質量%之脂肪族聚酯化合物，及聚碳酸酯樹脂。關於脂肪族聚酯化合物及聚碳酸酯樹脂之種類等，係如同後述內容，於樹脂組成物中脂肪族聚酯化合物之含量，較佳為3質量%以上且未滿9質量%，更佳為3質量%以上，7質量%以下，特佳為3質量%以上，5質量%以下。 藉此，本發明之樹脂組成物，由於含有具優異耐久性及耐熱性、高透明性之聚碳酸酯樹脂作為主成分，因此具有這些優異的特徵。進而，本發明之樹脂組成物，係含有詳細如後述之脂肪族聚酯化合物之指定含量，故易加工性亦優。 [0014] 本發明之樹脂組成物之玻璃轉移溫度，較佳為100℃~135℃，更佳為105℃~130℃，特佳為110℃~128℃。特別是，由樹脂組成物之易加工性之觀點來看，玻璃轉移溫度為128℃以下，較佳為120℃以下。 [0015] ＜脂肪族聚酯化合物＞ 於本發明之樹脂組成物中含有之脂肪族聚酯化合物，係含有內酯化合物作為其構成單體者。脂肪族聚酯化合物中，作為其構成單體，可含有上述化合物中之複數種類，亦可僅含有其中任一種類。 脂肪族聚酯化合物係於上述化合物中，較佳含有內酯化合物作為單體。於此，構成脂肪族聚酯化合物之全單體中，較佳係70莫耳%以上使用內酯化合物，更佳為，90莫耳%以上使用內酯化合物。 並且，作為脂肪族聚酯化合物之單體之內酯化合物，係包含ε-己內酯、β-丙酸內酯、δ-戊內酯等。脂肪族聚酯化合物之單體，係可含有這些內酯化合物中之複數種類，亦可僅使用其中之任一種類。 [0016] 又，作為脂肪族聚酯化合物之單體之上述內酯化合物中，較佳係使用ε-己內酯。於此，內酯化合物中，較佳係70莫耳%以上使用ε-己內醯胺，更佳係90莫耳%以上使用ε-己內酯。 如此，脂肪族聚酯化合物之主要構成單體較佳為含有係ε-己內酯之聚己內酯，更佳為，作為脂肪族聚酯化合物，使用單體僅為ε-己內酯之聚己內酯。又，所謂主要構成單體，係為佔構成單體全體之50莫耳%以上。 [0017] 脂肪族聚酯化合物之重量平均分子量較佳為10,000~90,000。更佳為，脂肪族聚酯化合物之重量平均分子量為10,000~60,000，特佳為10,000~未滿40,000。 [0018] ＜聚碳酸酯樹脂＞ 本發明之樹脂組成物中含有之聚碳酸酯樹脂，若為於分子主鏈中，含有碳酸酯鍵結-[O-R-OCO]-單元(其中R為脂肪族基、芳香族基，或含有脂肪族基及芳香族基兩者者，更進一步為具有直鏈構造或分支構造者)者，則無特別限制，然而，特別地，較佳為使用以下之聚碳酸酯。 亦即，具有雙酚A骨架之聚碳酸酯。 [0019] 作為聚碳酸酯樹脂之重量平均分子量，較佳為20,000~60,000，更佳為23,000~55,000。特佳為25,000~50,000。 又，作為聚碳酸酯樹脂之玻璃轉移溫度，較佳為120~160(℃)，更佳為130~155(℃)。 具有上述範圍內之重量平均分子量或玻璃轉移溫度之聚碳酸酯樹脂，對於樹脂組成物之高耐熱性及耐衝擊性之實現具有貢獻。 [0020] 又，樹脂組成物，其較佳係以樹脂組成物全體之質量為基準，含有90質量%以上之聚碳酸酯樹脂。更佳為，樹脂組成物，係以樹脂組成物全體之質量為基準，含有脂肪族聚酯化合物之93質量%以上之聚碳酸酯樹脂，特佳為含有95質量%以上之聚碳酸酯樹脂。 [0021] ＜白色顔料＞ 樹脂組成物亦可進一步含有白色顏料。如此含有白色顏料之樹脂組成物，適合使用於白色薄片，例如，作為形成ID卡片等之含有天線之芯層之白色薄片之材料。作為白色顏料，係可使用氧化鈦、滑石、高嶺土、黏土、雲母等，較佳為使用氧化鈦。 [0022] 白色顏料之含量，係以樹脂組成物全體之質量為基準，較佳為10~30質量%，更佳為13~25質量%，特佳為15~20質量%。 [0023] ＜雷射呈色劑＞ 樹脂組成物，亦可進一步含有雷射呈色劑。如此含有雷射呈色劑之樹脂組成物，例如，適合使用作為特別需要防止篡改之卡片中，藉由標記處理使印字變為可能之雷射標示薄片(雷射標示層)之材料。作為雷射呈色劑，係可使用碳黑、摻銻氧化錫、鉍氧化物類呈色劑等，較佳係使用碳黑。 又，作為金屬氧化物類之雷射呈色劑，較佳為鉍氧化物類呈色劑，作為金屬成分，除了鉍以外，更佳為含有釹或釓之鉍氧化物類呈色劑。 例如，作為雷射呈色劑之金屬氧化物，較佳係以下述式(I)表示者。
(式(I)中，M為至少一種選自釓及釹之金屬。x為滿足0.001＜x＜0.5之關係之值，較佳為滿足0.01＜x＜0.3之關係之值。y為滿足1＜y＜2.5之關係之值，較佳為滿足1.5＜y＜2.1關係之值)。 [0024] 雷射呈色劑之含量，係以樹脂組成物全體之質量為基準，較佳為0.0001~0.2質量%，更佳為0.0005~0.15質量%，特佳為0.001~0.1質量%。 例如，以碳黑作為雷射呈色劑使用之狀況，碳黑之含量，係以樹脂組成物全體之質量為基準，較佳為1~100質量ppm (0.0001~0.01質量%)，更佳為未滿40質量ppm，例如為5~35質量ppm。又，以上述之金屬氧化物類之粒子作為雷射呈色劑使用之狀況，雷射呈色劑之含量，例如，以樹脂組成物全體之質量為基準，為50~5000質量ppm (0.005~0.5質量%)，較佳為80~3000質量ppm，更佳為100~2000質量ppm。關於雷射呈色劑，使用具有使屬於雷射波長之1064nm之光線難以穿透，再加上特異地使波長在500nm附近之光線難以通過之性質之雷射呈色劑，能賦予其驚人的雷射標示性能。例如，上述之雷射呈色劑，即使僅微量存在於樹脂組成物，仍可能實現清晰印字之效果。作為實現這樣效果的雷射呈色劑，舉例可為上述之碳黑，及含有鉍氧化物者。 [0025] ＜樹脂組成物之添加物＞ 樹脂組成物，除了上述之成分以外，亦可含有以下之添加劑。亦即，係為至少一種選自由熱穩定劑、抗氧化劑、阻燃劑、阻燃助劑、紫外線吸收劑、脫模劑及著色劑所成之群組之添加劑等。 又，在不顯著損害所求之諸物特性之前提下，亦可添加抗靜電劑、螢光增白劑、防霧劑、流動性改良劑、可塑劑、分散劑、抗菌劑等。 [0026] 惟，有機磷化合物，例如，關於偶磷氮阻燃劑，若於樹脂組成物中過剩添加，則利用該樹脂組成物所形成之薄片之耐久性之低下將可能發生。為此，使樹脂組成物中有機磷化合物之含量較佳係控制在例如未滿2000質量ppm，磷之含量較佳係控制在例如未滿100質量ppm。 [0027] 又，作為抗靜電劑，有機磺酸磷鹽，例如，將含有烷基苯磺酸磷鹽之物質添加於樹脂組成物時，由於分子量低，有使得卡片成形後之耐久性顯著低下之可能性。故，如此，有較佳係避免添加對於卡片用樹脂薄片之性能有不良影響之添加劑之情況。 此外，於將玻璃碎片等，或含有苯基之矽油等之液體之添加劑添加於樹脂組成物之情況，亦可能會產生卡片成形後之耐久性低下的問題。特別是，添加玻璃碎片時，亦可能會產生樹脂組成物之外觀(透明性)之低下的問題。因此，有較佳係避免使用這些添加劑之情況。 [0028] [卡片用樹脂薄片] 本發明之樹脂用組成物，如同上述內容，由於其具有優良耐熱性及耐久性的同時，亦易於加工，因此適合作為卡片用樹脂薄片之材料使用。亦即，使用本發明之樹脂用組成物之卡片用之薄片，例如，可製造嵌入天線晶片之薄片，或雷射標示薄片。 [0029] 使用本發明之樹脂用組成物之薄片之製造步驟中，作為將樹脂組成物層狀(薄片狀)加工之方法，可採用一直以來之手法。例如藉由擠出成型、鑄造成型之方法。 作為擠出成型之例子，舉例可為將本發明之樹脂用組成物之小顆粒、碎片或粉末於擠出機溶解、捏合後，由T字模等擠出，所得之半熔融狀之薄片以軋輥一邊加壓一邊冷卻、固化而形成薄片之方法。 [0030] [多層薄片] 本發明之多層薄片，係為具有兩片以上之積層之熱可塑性樹脂薄片者，其中至少一層，係包含本發明之樹脂組成物。更具體而言，使用本發明之樹脂用組成物形成之薄片，例如，可製造如以上述卡片用之薄片複數積層之多層薄片(積層體)卡片。 作為本發明之多層薄片之較佳型態，舉例可為，熱可塑性樹脂薄片(樹脂薄片)之至少一層係含有一種選自由PET-G、聚碳酸酯、PCT-G、PCT，及至少上述2種類之混合物(合金)所組成之群組。亦即，作為熱可塑性樹脂薄片(樹脂薄片)之較佳具體例，舉例可為以PET-G薄片、聚碳酸酯(PC)樹脂薄片、PCT-G薄片、PCT薄片或以這些樹脂之任2種類之合金作為主成分之薄片。特別是，作為上述之合金，較佳為PC樹脂與PET-G樹脂之合金。 又，使用含有聚碳酸酯之本發明之樹脂用組成物形成之薄片，例如，上述之天線晶片嵌入之薄片，及雷射標示薄片，不僅與被積層之其他聚碳酸酯樹脂薄片之接著性優異，與上述PET-G薄片及PC樹脂與PET-G樹脂之合金之薄片之接著性亦優異。 [0031] 作為構成多層薄片之熱可塑性樹脂薄片(樹脂薄片)，亦可進一步使用聚碳酸酯/聚酯薄片(含有聚碳酸酯及聚酯中任一之樹脂的薄片)。 PET-G薄片，係以含有聚對苯二甲酸乙二酯類的PET-G樹脂(PETG樹脂)，亦即，以對苯二甲酸單元為主的二羧酸單元、乙二醇單元，及以環己烷二甲醇單元(1,4-環己烷二甲醇單元)為主的二醇單元之聚酯而形成之薄片。又，例如，對苯二甲酸單元係以莫耳基準計，佔有二羧酸單元總含量的50%以上，乙二醇係以莫耳基準計，佔有二醇單元總含量(乙二醇單元及環己烷二甲醇單元合計)的50%以上。 又，作為熱可塑性樹脂薄片之材料，其他的聚對苯二甲酸乙二酯類之樹脂，例如，亦可使用PCT-G樹脂 (PCTG樹脂)及PCT樹脂。 PCT-G樹脂亦由於為含有以對苯二甲酸單元為主的二羧酸單元、乙二醇單元，及以環己烷二甲醇單元(1,4-環己烷二甲醇單元)為主的二醇單元之聚酯者，環己烷二甲醇單元係以莫耳基準計，佔有二醇單元總含量(乙二醇單元及環己烷二甲醇單元合計)的50%以上，以此觀點來看與PET-G樹脂相異。 又，PCT樹脂 (聚亞環己基･二亞甲基･對苯二甲酸酯樹脂)係含有以對苯二甲酸單元為主的二羧酸單元，及以環己烷二甲醇單元(1,4-環己烷二甲醇單元)為主的二醇單元之聚酯，不含乙二醇單元。 上述之使用聚對苯二甲酸乙二酯類之樹脂而形成之薄片，亦即，PET-G薄片、PCT-G薄片以及PCT薄片，係與聚碳酸酯樹脂薄片之接著性(相容性)佳，故適合用於與聚碳酸酯樹脂薄片形成之積層體。 又，聚碳酸酯/聚酯薄片係含有聚碳酸酯及聚酯之聚合物合金(混合物)之薄片，作為聚碳酸酯，係可使用與本發明之樹脂用組成物中含有之聚碳酸酯樹脂相同者，作為聚酯，係可使用上述之脂肪族聚酯化合物、聚對苯二甲酸乙二酯類之PETG樹脂、PCTG樹脂，及PCT樹脂等。亦即，作為多層薄片中含有之熱可塑性樹脂薄片之材料，較佳係可使用含有上述之聚碳酸酯樹脂、PETG樹脂、PCTG樹脂、PCT樹脂，及脂肪族聚酯中之至少兩種以上之聚合物合金。 [0032] 作為多層薄片之具體例，舉例可為如圖1所示之ID卡片10。ID卡片10係含有第1表層12、第2表層14、第1雷射標示層16、第2雷射標示層18、第1芯層20，及第2芯層22之積層體。 第1表層12及第2表層14為無色透明，於第1雷射標示層16，及第2雷射標示層18中，藉由雷射光L之照射而進行印字係為可能。第1芯層20，及第2芯層22係白色顔料，故為白色，第1芯層20中，天線晶片24係嵌入其中。對應天線晶片24所接收之由外部而來的電磁波，IC晶片(圖中未示出)之信息因而被覆寫。 於這些層中之任一層，皆可能使用本發明之樹脂用組成物。特別是，藉由使用本發明之樹脂用組成物形成之第1表層12，及第2表層14，可製造表面耐久性及耐熱性優良之ID卡片10。 又，藉由含有雷射呈色劑之本發明之樹脂用組成物，亦可形成雷射標示性優良之第1雷射標示層16，及第2雷射標示層18。 [實施例] [0033] 以下，參照實施例更進一步具體地說明本發明。然而，本發明並不限於以下的實施例，在不脫離本發明的主旨的範圍內，可任意地變更而實施本發明。 [0034] ＜玻璃轉移溫度的測定＞ 樹脂之玻璃轉移溫度(Tg)係使用示差掃描熱量分析儀(股)日立High-Tech Science製之EXSTAR DSC 7020(DSC)進行測定。測定係於氮氣環境下，於樹脂成分溶融之溫度(270℃)，以15℃/min進行升溫，30℃為止以20℃/min進行冷卻後，再度以15℃/min進行昇溫(2nd run)。由所得之DSC曲線，依據起點法求得玻璃轉移溫度。 [0035] ＜與PETG膜之接著性＞ 與各實施例及比較例之樹脂組成物之PETG膜之接著性，係皆使用以下列方式作成之試料進行評價。 試料之作成 使用測定對象之樹脂組成物作成50μm之膜，並使其與使用PETG(S2008：SK Chemicals公司製)同樣地作成之100μm之膜貼合。於此經兩層貼合之測定對象膜之上下面，分別以兩片為0.5mm的SUS板、1mm的矽橡膠片、100μm的SUS板、0.78mm的鐵氟龍(註冊商標)薄片之四片積層板將之夾住。亦即，於測定對象之樣品膜側之其中之一積層板的鐵氟龍片，係以於測定對象膜之PETG膜側，與另一積層板的鐵氟龍片各自連接的狀態，以2片上述的積層板將測定對象膜夾住。而後，在測定對象膜之上下以2片積層板夾住之狀態下，更進一步，以衝壓機的一對衝壓板將2片積層板各自之最外側配置之0.5mm SUS板夾住，使用空壓式加熱衝壓(IMC-1839型：井元製作所製)，以120℃、空氣壓力0.2 MPa、進行60秒之壓製而作成積層體。 ＜接著性評價＞ 將作成之積層體，以自動立體測圖儀(AGS-X：島津製作所製)安裝於膠帶剝離試驗裝置，進行將測試對象之樹脂組成物之50μm之膜由PETG之100μm之膜上剝離之剝離試驗(以剝離速度152.4mm/min，90°進行剝離試驗)，其接著性係如下述內容進行評價。 膜無法剝離：非常良好 剝離力20N/50mm以上：良好 剝離力未達20N/50mm：差 [0036] ＜耐久性＞ 各實施例及比較例之樹脂組成物的耐久性，係如下述內容進行評價。使用對象樹脂組成物作成厚0.78 mm之卡片，使用IC卡片彎曲、扭轉測試儀((股)東洋精機製作所製)實施卡片彎曲試驗，測定卡片發生破損為止之彎曲次數。卡片彎曲次數之測定，係遵循JIS X6305-1進行，依據彎曲次數之數值如下述內容進行評價。 未滿1000次：差 1000次以上且未滿3000次：良好 3000次以上：非常良好 [0037] ＜透明性＞ 各實施例及比較例之樹脂組成物的透明性，係如下述內容進行評價。使用測定對象樹脂組成物形成厚0.3 mm之膜，使用霧度計(村上色彩技術研究所製HM-150)測定Haze值，其透明係性係如下述內容進行評價。Haze值之測定，係遵循JIS K 7136進行。 Haze值：5%以上：差 Haze值：1%以上，未滿5%：良好 Haze值：未滿1%：非常良好 [0038] ＜黑色度＞ 測試片之作成 於詳細內容如後述之實施例4~7及比較例6~13之膜上實施雷射標示加工，黑色度係如下述內容進行評價。首先，使用測定對象之樹脂組成物，形成含有碳黑或金屬氧化物、厚0.1mm之雷射標示膜。再使用前述測定對象樹脂組成物中，不含有碳黑及金屬氧化物之樹脂組成物形成0.1mm之覆蓋膜。進而，於覆蓋膜成形時使用之樹脂組成物中，將氧化鈦(RESINO COLOR工業(股)製「white DCF-T-17007」)以全體之15wt%之含量添加而作成之樹脂組成物，使用其形成厚0.2mm之白芯膜。 將作成之膜，以覆蓋膜、雷射標示膜、白芯膜之順序貼合。將此3層貼合之測定對象膜之上下，分別以兩片為0.5mm的SUS板、1mm的矽橡膠片、100μm的SUS板、0.78mm的鐵氟龍(註冊商標)薄片之四片積層板將之夾住。亦即，於測定對象膜之覆蓋膜側之其中之一積層板的鐵氟龍片，係以於測定對象膜之白芯膜側，與另一積層板的鐵氟龍片各自連接的狀態，以2片上述的積層板將測定對象夾住。而後，在測定對象膜之上下以2片積層板夾住之狀態下，更進一步，以衝壓機的一對衝壓板將2片積層板各自之最外側配置之0.5mm SUS板夾住，使用空壓式加熱衝壓(IMC-1839型：井元製作所製)，以160℃、空氣壓力0.2 MPa、進行60秒之壓製而作成積層體。 使用雷射標式裝置(ROFIN-BAASEL製「EasyMark IV-E10」)，於壓製而得到之積層體，由其覆蓋膜層側起以以下之照射條件實施雷射標示。印字部使用分光濃度計(X-Rite(股)製「X-Rite 504」)測定，得到之最大值作為其黑色度。 雷射標示條件
[0039] ＜雷射呈色性之評價＞ 將黑色度之值為閾值之1.70以上之實施例或比較例之雷射呈色性判定為「良好」，以黑色度之值未達閾值之實施例或比較例作為「差」之評價。又，關於不含碳黑及金屬氧化物、不具有雷射標示性之實施例及比較例，其雷射呈色性以「無」評價。 [0040] ＜樹脂組成物的製造＞ 實施例1~3及比較例1~5之樹脂組成物，以下述之方法製造。亦即，如同下述，於表1以省略方式表示之樹脂中，分別添加表1所示之含量之聚己內酯(聚ε-己內酯：重量平均分子量：10000)、偶磷氮阻燃劑((股)伏見製藥所製「Rabitoru(註冊商標)FP-110」)，獲得均一的樹脂組成物。 [0041] 實施例4~7及比較例6~13之樹脂組成物，以下述之方法製造。亦即，如同下述，於表1以省略方式表示之樹脂中，分別以表1所示之含量之聚己內酯(聚ε-己內酯：重量平均分子量：10000)、碳黑(卡博特公司製「MONARCH(註冊商標)800」)、金屬氧化物(東罐Material Technology(股)製「42-920A」)添加並攪拌，獲得均一的樹脂組成物。 又，下述表1所示之樹脂中，分別以表1所示之含量之聚己內酯(perstorp公司製Capa(註冊商標)6800：重量平均分子量80,000)及上述碳黑，添加並攪拌，製造實施例8之樹脂組成物。 此外，上述金屬氧化物(「42-920A」)，係三氧化鉍Bi2
O3
與三氧化釹 Nd2
O3
之混合物，具體而言，其係含有98~99質量%之Bi2
O3
，以及0.3~1.0質量%之Nd2
O3
程度之混合物。 (PC) 雙酚A型芳香族聚碳酸酯樹脂 (三菱化學工程塑料(股)製「Iupilon(註冊商標)E-2000」、熱變形溫度(玻璃轉移溫度)150℃) (PETG) 改質聚對苯二甲酸乙二酯樹脂 (SK Chemicals製「SKYGREEN(註冊商標)S2008」、熱變形溫度(玻璃轉移溫度)80℃) (PC/PETG合金) 上述(PC)與(PETG)之50：50(重量比)之混合物 [0042] ＜測試片(薄片)之製造＞ 使用實施例1~7及比較例1~13之樹脂組成物，以下述之方法製造測試片之薄片。首先，使用由桶直徑32mm、螺旋之L/D=31.5之雙軸擠出機而成之T字模溶融擠出機，以排出量20 kg/h、螺旋旋轉數200 rpm，使寬度300 mm之薄片成形。實施例1~7、比較例2、4~9、11，及13之汽缸.模頭溫度各自設定為280℃，於比較例1、3、10，及12之汽缸．模頭溫度各自設定為260℃。又，作為薄片，係製造表面兩面為鏡面者。為評價上述之接著性、耐久性，及透明性，各樹脂組成物係分別形成50μm (0.05 mm)、100μm (0.1 mm)、300μm (0.3mm)、780μm (0.78mm)之具有4種厚度的膜，以實施上述各項測定。
[0043]10‧‧‧ID卡片(多層薄片)12‧‧‧第1表層14‧‧‧第2表層16‧‧‧第1雷射標示層18‧‧‧第2雷射標示層20‧‧‧第1芯層22‧‧‧第2芯層24‧‧‧天線晶片
[0011] [圖1] 表示多層薄片(ID卡片)之具體例之斷面圖。
Claims (16)
- 一種樹脂組成物，其係包含2質量%以上且未滿9質量%之脂肪族聚酯化合物，及聚碳酸酯樹脂，其中，前述樹脂組成物係以前述樹脂組成物之質量為基準更進一步含有0.0001~0.2質量%之雷射呈色劑。
- 如請求項1之樹脂組成物，其玻璃轉移溫度為100~135℃。
- 如請求項1或2之樹脂組成物，前述脂肪族聚酯化合物中，其係至少包含內酯化合物作為構成單體。
- 如請求項3之樹脂組成物，其中前述內酯化合物係包含ε-聚己內酯。
- 如請求項4之樹脂組成物，其中前述內酯化合物係包含主要構成單體為ε-己內酯之聚己內酯。
- 如請求項1或2之樹脂組成物，其係以樹脂組成物全體之質量為基準，含有3質量%以上，5質量%以下之脂肪族聚酯化合物。
- 如請求項1或2之樹脂組成物，其中前述脂肪族聚酯化合物之重量平均分子量為10000~90000。
- 如請求項1或2之樹脂組成物，其係以樹脂組成物全體之質量為基準，含有90質量%以上之聚碳酸酯樹脂。
- 如請求項1或2之樹脂組成物，其中，前述樹脂組成物係以樹脂組成物全體之質量為基準，更進一步含有10~30質量%之白色顏料。
- 如請求項1之樹脂組成物，其中前述雷射呈色劑係含有碳黑及金屬氧化物的粒子中之至少一者。
- 如請求項10之樹脂組成物，其中前述金屬氧化物係由下述式(I)表示，Bi(1-x)MxOy．．．(I)(式(I)中、M為至少一種選自釓及釹之金屬、x為滿足0.001<x<0.5之關係之值、y為滿足1<y<2.5之關係之值)。
- 一種卡片用樹脂薄片，其係具有包含如請求項1~11中任一項之樹脂組成物之層。
- 如請求項12之卡片用樹脂薄片，其中具有嵌入之天線晶片。
- 如請求項12或13之卡片用樹脂薄片，其係雷射標示卡片用。
- 一種多層薄片，其係具有兩片以上之積層樹脂薄片之多層薄片，其特徵在於，其至少一層包含請求項1~11中任一項之樹脂組成物。
- 如請求項15之多層薄片，前述多層薄片係進一步含有包含選自由PET-G、聚碳酸酯、PCT-G、PCT及上述至少兩種類以上之混合物所組成之群組之至少一個的樹脂薄片。