CN109963908B - 树脂组合物、包含树脂组合物的卡片用树脂片和多层片 - Google Patents
树脂组合物、包含树脂组合物的卡片用树脂片和多层片 Download PDFInfo
- Publication number
- CN109963908B CN109963908B CN201780062607.4A CN201780062607A CN109963908B CN 109963908 B CN109963908 B CN 109963908B CN 201780062607 A CN201780062607 A CN 201780062607A CN 109963908 B CN109963908 B CN 109963908B
- Authority
- CN
- China
- Prior art keywords
- resin composition
- resin
- sheet
- mass
- cards
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明旨在实现具有高的耐久性和耐热性、并且保持透明性的同时加工容易性也优异的树脂组合物、以及使用该树脂组合物所形成的卡片用树脂片和多层片。上述课题是通过含有2质量%以上且低于9质量%的脂肪族聚酯化合物、和聚碳酸酯树脂的树脂组合物来解决的。
Description
技术领域
本发明涉及具有高的耐久性和耐热性、并且加工也容易的树脂组合物、使用其所制造的卡片用树脂片和多层片。
背景技术
一直以来,在ID卡、电子护照和非接触型IC卡等中,使用着树脂膜。作为这样的树脂膜的材料,已知例如使用聚氯乙烯(PVC)和聚对苯二甲酸乙二醇酯系的PET-G等。
另外,作为各种卡片用的树脂组合物,还已知使用聚酯树脂组合物(参照专利文献1)。在专利文献1中,公开了包含以PET为主要成分的聚酯树脂和芳香族聚碳酸酯树脂的聚酯树脂组合物。
现有技术文献
专利文献
专利文献1:日本特开2002-97361号公报
发明内容
发明所要解决的课题
在作为卡片用的树脂组合物,使用PVC和PET-G等的情况下,由于这些树脂的耐久性和耐热性不一定充分,所以卡片的机械强度会成为问题。
另外,在专利文献1中,记载了上述聚酯树脂组合物的耐热性和耐冲击性等优异。然而,这样的聚酯树脂组合物的透明性差,会使印刷部分的分辨率降低。
用于解决课题的方法
本发明的发明人为了解决上述课题,反复进行了深入研究,结果发现包含聚碳酸酯的规定的树脂组合物具有高的耐久性和耐热性,并且在保持透明性的同时,加工容易性也优异,从而完成了本发明。
即,本发明涉及以下所示的树脂组合物、使用聚碳酸酯树脂组合物所形成的卡片用树脂片和多层片。
(1)一种树脂组合物,其含有聚碳酸酯树脂、和2质量%以上且低于9质量%的脂肪族聚酯化合物。
(2)如上述(1)所述的树脂组合物,其具有激光打标性能。
(3)如上述(1)所述的树脂组合物,玻璃化转变温度为100~135℃。
(4)如上述(1)~(3)中任一项所述的树脂组合物,其中,上述脂肪族聚酯化合物至少包含内酯化合物作为结构单体。
(5)如上述(4)所述的树脂组合物,其中,上述内酯化合物包含ε-聚己内酯。
(6)如上述(5)所述的树脂组合物,其中,上述内酯化合物包含主要结构单体为ε-己内酯的聚己内酯。
(7)如上述(1)~(6)中任一项所述的树脂组合物,其中以树脂组合物整体的质量为基准,含有3质量%以上5质量%以下的脂肪族聚酯化合物。
(8)如上述(1)~(7)中任一项所述的树脂组合物,其中,上述脂肪族聚酯化合物的重均分子量为10000~90000。
(9)如上述(1)~(8)中任一项所述的树脂组合物,其中以树脂组合物整体的质量为基准,含有90质量%以上的聚碳酸酯树脂。
(10)如上述(1)~(9)中任一项所述的树脂组合物,其中,上述树脂组合物中还含有以树脂组合物整体的质量为基准,10~30质量%的白色颜料。
(11)如上述(1)~(10)中任一项所述的树脂组合物,上述树脂组合物还含有激光显色剂。
(12)如上述(11)所述的树脂组合物,其中,上述激光显色剂包含炭黑和金属氧化物的颗粒中的至少一者。
(13)如上述(12)所述的树脂组合物,其中,上述金属氧化物由下述通式(I)所示。
Bi(1-x)MxOy···(I)
(式(I)中,M为选自钆和钕中的至少1种金属,x为满足0.001<x<0.5的关系的值,y为满足1<y<2.5的关系的值。)
(14)如上述(11)~(13)中任一项所述的树脂组合物,其中,上述树脂组合物含有以上述树脂组合物的质量为基准,0.0001~0.2质量%的上述激光显色剂。
(15)一种卡片用树脂片,其具有包含上述(1)~(14)中任一项所述的树脂组合物的层。
(16)如上述(15)所述的卡片用树脂片,其具有嵌入式天线-芯片。
(17)如上述(15)或(16)所述的卡片用树脂片,其用于激光打标卡片。
(18)一种多层片,其为具有二张以上的叠层的树脂片的多层片,其至少一层包含上述(1)~(14)中任一项所述的树脂组合物。
(19)如上述(18)所述的多层片,其中,上述多层片还具有包含选自PET-G、聚碳酸酯、PCT-G、PCT和它们的至少2种的混合物中的任意一种的树脂片。
发明的效果
本发明的树脂组合物包含脂肪族聚酯化合物和聚碳酸酯树脂,在加工成片状时也不易破裂,耐冲击性优异,特别是对于弯曲疲劳具有高的耐久性。此外,本发明的树脂组合物的耐热性和透明性也优异,并且利用加热的加工也容易。如上所述,具有优异的性质的本发明的树脂组合物特别适合作为卡片用树脂片和多层片的材料使用,例如适于制造ID卡片、电子护照和非接触型IC卡片等。
另外,本发明的树脂组合物与由其他树脂形成的膜、特别是PET-G膜等以聚酯树脂为主成分所形成的膜的粘接性也优异,因此也适于制造包含这些膜的叠层体。
附图说明
图1是表示多层片(ID卡片)的具体例的剖面图。
具体实施方式
以下,详细说明本发明。此外,本发明并不限定于以下的实施方式,能够在具有发明的效果的范围内任意地变更实施。
[树脂组合物]
本发明的树脂组合物包含2质量%以上且低于9质量%的脂肪族聚酯化合物、和聚碳酸酯树脂。关于脂肪族聚酯化合物和聚碳酸酯树脂的种类等如后所述,树脂组合物中的脂肪族聚酯化合物的含量更优选为3质量%以上且低于9质量%,更优选为3质量%以上7质量%以下,特别优选为3质量%以上5质量%以下。
这样,本发明的树脂组合物的耐久性和耐热性优异,含有具有高透明性的聚碳酸酯树脂为主成分,因此具有这些优异的特征。此外,本发明的树脂组合物包含规定量的详细内容后述的脂肪族聚酯化合物,因此加工容易性也优异。
本发明的树脂组合物的玻璃化转变温度优选为100℃~135℃,更优选为105℃~130℃,更加优选为110℃~128℃。特别是从树脂组合物的加工容易性的观点,玻璃化转变温度为128℃以下,优选为120℃以下。
<脂肪族聚酯化合物>
本发明的树脂组合物所含的脂肪族聚酯化合物包含内酯化合物作为结构单体。脂肪族聚酯化合物可以包含上述的化合物中的多种,也可以包含任意一种作为结构单体。
脂肪族聚酯化合物在上述的化合物中,优选包含内酯化合物作为单体。其中,构成脂肪族聚酯化合物的全部单体中,优选使用70摩尔%以上的内酯化合物,更优选使用90摩尔%以上的内酯化合物。
而且,作为脂肪族聚酯化合物的单体的内酯化合物包含ε-己内酯、β-丙内酯、δ-戊内酯等。脂肪族聚酯化合物的单体可以包含这些内酯化合物中的多种,也可以仅使用任意一种。
另外,作为脂肪族聚酯化合物的单体的上述的内酯化合物中,优选使用ε-己内酯。其中,内酯化合物中,优选使用70摩尔%以上的ε-己内酯,更优选使用90摩尔%以上的ε-己内酯。
这样脂肪族聚酯化合物优选包含主要结构单体为ε-己内酯的聚己内酯,更优选作为脂肪族聚酯化合物,使用单体仅为ε-己内酯的聚己内酯。此外,主要结构单体是指占到结构单体整体的50摩尔%以上的结构单体。
脂肪族聚酯化合物的重均分子量优选为10,000~90,000。更优选脂肪族聚酯化合物的重均分子量为10,000~60,000,特别优选为10,000~低于40,000。
<聚碳酸酯树脂>
本发明的树脂组合物所含的聚碳酸酯树脂只要在分子主链中包括包含碳酸酯键的-[O-R-OCO]-单元(R包含脂肪族基、芳香族基、或脂肪族基和芳香族基的双方,进而具有直链结构或支链结构),就没有特别限定,特别优选使用以下的聚碳酸酯。
即具有双酚A骨架的聚碳酸酯。
作为聚碳酸酯树脂的重均分子量,优选为20,000~60,000,更优选为23,000~55,000。更加优选为25,000~50,000。
另外,作为聚碳酸酯树脂的玻璃化转变温度,优选为120~160(℃),更优选为130~155(℃)。
具有上述的范围内的重均分子量或玻璃化转变温度的聚碳酸酯树脂有助于实现树脂组合物的高的耐热性和耐冲击性。
另外,树脂组合物优选以树脂组合物整体的质量为基准,含有90质量%以上的聚碳酸酯树脂。更优选为树脂组合物以树脂组合物整体的质量为基准,含有脂肪族聚酯化合物的93质量%以上的聚碳酸酯树脂,特别优选含有95质量%以上的聚碳酸酯树脂。
<白色颜料>
树脂组合物可以还含有白色颜料。这样包含白色颜料的树脂组合物适合作为白色片、例如、形成包含ID卡片等的天线的芯层的白色片的材料使用。作为白色颜料,可以使用氧化钛、滑石、高岭土、粘土、云母等,优选使用氧化钛。
白色颜料的含量,以树脂组合物整体的质量为基准,优选为10~30质量%,更优选为13~25质量%,更加优选为15~20质量%。
<激光显色剂>
树脂组合物可以还含有激光显色剂。这样包含激光显色剂的树脂组合物例如适合作为在特别需要防篡改的卡片中能够利用打标处理进行印字的激光打标片(激光打标层)的材料使用。作为激光显色剂,可以使用炭黑、掺锑氧化锡、铋氧化物系显色剂等,优选使用炭黑。
另外,作为金属氧化物系的激光显色剂,优选铋氧化物系显色剂,更优选作为金属成分,在铋以外还含有钕或钆的铋氧化物系显色剂。
例如,作为为激光显色剂的金属氧化物,优选下述式(I)所示的物质。
Bi(1-x)MxOy···(I)
(式(I)中,M为选自钆和钕中的至少1种金属。x为满足0.001<x<0.5的关系的值,优选为满足0.01<x<0.3的关系的值。y为满足1<y<2.5的关系的值,优选为满足1.5<y<2.1的关系的值。)
激光显色剂的含量,以树脂组合物整体的质量为基准,优选为0.0001~0.2质量%,更优选为0.0005~0.15质量%,更加优选为0.001~0.1质量%。
例如,在作为激光显色剂使用炭黑的情况下,炭黑的含量以树脂组合物整体的质量为基准,优选为1~100质量ppm(0.0001~0.01质量%),更优选为低于40质量ppm,例如为5~35质量ppm。另外,在上述的金属氧化物系的颗粒作为激光显色剂使用的情况下,激光显色剂的含量例如以树脂组合物整体的质量为基准,为50~5000质量ppm(0.005~0.5质量%),优选为80~3000质量ppm,更优选为100~2000质量ppm。关于激光显色剂,使用具有除了难以透过作为激光的波长的1064nm的光以外,还特异性地难以通过波长为500nm附近的光的性质的激光显色剂,对激光打标性能赋予了令人预料不到的效果。例如,上述的激光显色剂即使在树脂组合物中含有极少的量,也能够实现能够清晰的印刷的效果。作为实现这样的效果的激光显色剂,可以列举包含上述的炭黑和铋氧化物的物质。
<树脂组合物的添加物>
树脂组合物除了含有上述成分以外,还可以含有以下的添加剂。即,为选自热稳定剂、抗氧化剂、阻燃剂、阻燃助剂、紫外线吸收剂、脱模剂和着色剂中的至少1种添加剂等。
另外,只要不明显损害所希望的各项物性,也可以添加抗静电剂、荧光增白剂、防雾剂、流动性改良剂、增塑剂、分散剂、抗菌剂等。
只是关于有机磷化合物、例如、磷腈阻燃剂等,如果在树脂组合物中过剩地添加,则存在产生使用树脂组合物形成的片的耐久性降低的可能性。因此,优选将树脂组合物中的有机磷化合物的含量抑制到例如低于2000质量ppm,将磷的含量抑制到例如低于100质量ppm。
另外,作为抗静电剂,如果在树脂组合物中添加包含有机磺酸鏻盐、例如、烷基苯磺酸鏻盐的抗静电剂,则由于分子量低,所以存在使卡片成型后的耐久性明显降低的可能性。因此,如上所述,有时优选避免添加会对卡片用树脂片的性能产生不良影响的添加剂。
进而,在树脂组合物中添加玻璃薄片等或含苯基的硅油等液体的添加剂的情况下,也会产生卡片成型后的耐久性降低的问题。特别是如果添加玻璃薄片,则还会产生树脂组合物的外观(透明性)变差的问题。因此,有时也优选避免使用这些添加剂。
[卡片用树脂片]
本发明的树脂组合物如上所述,耐热性和耐久性优异,并且加工容易,因此适合作为卡片用树脂片的材料使用。即使用本发明的树脂组合物,能够制造卡片用的片例如嵌有天线-芯片的片、或激光打标片。
在使用本发明的树脂组合物的片的制造工序中,作为将树脂组合物加工成层状(片状)的方法,可以采用现有的方法。例如为利用挤出成型、浇铸成型的方法。
作为挤出成型的例子,可以列举将本发明的树脂组合物的粒料、薄片或粉末用挤出机熔融、混炼后,从T模等挤出,将所得到的半熔融状的片一边用辊夹压,一边冷却、固化而形成片的方法。
[多层片]
本发明的多层片具有二张以上的叠层的热塑性树脂片,其至少一层包含本发明的树脂组合物。更具体而言,使用本发明的树脂组合物所形成的片例如能够将上述的卡片用的片多个叠层,来制造作为多层片(叠层体)的卡片。
作为本发明的多层片的优选方式,例如、热塑性树脂片(树脂片)的至少一层包含选自PET-G、聚碳酸酯、PCT-G、PCT、和它们的至少2种的混合物(合金)中的任意一种。即,作为热塑性树脂片(树脂片)的优选的具体例,可以列举PET-G片、聚碳酸酯(PC)树脂片、PCT-G片、PCT片或者以这些树脂的任意2种的合金为主成分的片。特别是作为上述的合金,优选PC树脂与PET-G树脂的合金。
另外,使用含有聚碳酸酯的本发明的树脂组合物所形成的片、例如嵌入有上述天线-芯片的片和激光打标片不仅与所叠层的其他聚碳酸酯树脂片的粘接性优异,而且与上述的PET-G片、及PC树脂和PET-G树脂的合金的片的粘接性也优异。
作为构成多层片的热塑性树脂片(树脂片),还可以使用聚碳酸酯/聚酯片(含有聚碳酸酯和聚酯的任意种的树脂的片)。
PET-G片是由聚对苯二甲酸乙二醇酯系的PET-G树脂(PETG树脂)、即包含以对苯二甲酸单元为主的二元羧酸单元、以乙二醇单元和环己烷二甲醇单元(1,4-环己烷二甲醇单元)为主的二醇单元的聚酯所形成的片。其中,对苯二甲酸单元例如占到以摩尔基准计的全部二元羧酸单元的50%以上,乙二醇占到以摩尔基准计的全部二醇单元(乙二醇单元和环己烷二甲醇单元的合计)的50%以上。
另外,作为热塑性树脂片的材料,也可以使用其他的聚对苯二甲酸乙二醇酯系的树脂、例如、PCT-G树脂(PCTG树脂)和PCT树脂。
PCT-G树脂虽然也是包含以对苯二甲酸单元为主的二元羧酸单元、包含以乙二醇单元和环己烷二甲醇单元(1,4-环己烷二甲醇单元)为主的二醇单元的聚酯,但在环己烷二甲醇单元占到以摩尔基准计的全部二醇单元(乙二醇单元和环己烷二甲醇单元的合计)的50%以上的方面与PET-G树脂不同。
另外,PCT树脂(聚(对苯二甲酸亚环已基-二亚甲酯)树脂)是包含以对苯二甲酸单元为主的二元羧酸单元、以及以环己烷二甲醇单元(1,4-环己烷二甲醇单元)为主的二醇单元的聚酯,不含乙二醇单元。
使用上述的聚对苯二甲酸乙二醇酯系的树脂所形成的片、即、PET-G片、PCT-G片和PCT片与聚碳酸酯树脂片的粘接性(相容性)优异,适合用于与聚碳酸酯树脂片的叠层体。
另外,聚碳酸酯/聚酯片是包含聚碳酸酯和聚酯的聚合物合金(混合物)的片,作为聚碳酸酯,能够使用与本发明的树脂组合物所含的聚碳酸酯树脂同样的聚碳酸酯,作为聚酯,可以使用上述的脂肪族聚酯化合物、聚对苯二甲酸乙二醇酯系的PETG树脂、PCTG树脂、和PCT树脂等。即,作为多层片所含的热塑性树脂片的材料,可以使用包含上述的聚碳酸酯树脂、PETG树脂、PCTG树脂、PCT树脂和脂肪族聚酯的至少2种以上的聚合物合金。
作为多层片的具体例,可以列举图1所示的ID卡片10。ID卡片10为包含第一表层12、第二表层14、第一激光打标层16、第二激光打标层18、第一芯层20和第二芯层22的叠层体。
第一表层12和第二表层14无色透明,在第一激光打标层16和第二激光打标层18中,能够利用照射激光L进行印字。第一芯层20和第二芯层22包含白色颜料,因此为白色,在第一芯层20中嵌入有天线-芯片24。根据天线-芯片24所接受的来自外部的电磁波,IC芯片(未图示)的信息被重写。
在这些任意一个层中,都能够使用本发明的树脂组合物。特别是通过使用本发明的树脂组合物形成第一表层12和第二表层14,能够制造表面的耐久性和耐热性优异的ID卡片10。
另外,利用含有激光显色剂的本发明的树脂组合物,也能够形成激光打标性能优异的第一激光打标层16和第二激光打标层18。
实施例
以下,表示实施例对本发明进行更加具体的说明。只是本发明并不限定于以下的实施例,能够在不脱离本发明的主旨的范围内任意变更地实施。
<玻璃化转变温度的测定>
树脂的玻璃化转变温度(Tg)使用差示热扫描量热分析计日立高新技术公司制的EXSTAR DSC 7020(DSC)测定。在测定中,在氮气氛下以15℃/min升温至树脂成分熔融的温度(270℃),以20℃/min冷却到30℃后,再次以15℃/min升温(2nd run)。从所得到的DSC曲线利用起始点法求出玻璃化转变温度。
<与PETG膜的粘接性>
各实施例及比较例的树脂组合物的与PETG膜的粘接性利用如下制成的试样进行评价。
试样的制成
使用作为测定对象的树脂组合物制作50μm的膜,与使用PETG(S2008:SKChemicals公司制)同样制成的100μm的膜重叠。将重叠它们这2层得到的测定对象膜的上下用2张叠层板夹住,该叠层板是0.5mm的SUS板、1mm的硅胶片、100μm的SUS板、0.78mm的特氟隆(注册商标)片的4张叠层板。即,1个叠层板的特氟隆片与测定对象膜的样品膜侧接触,另一个叠层板的特氟隆片与测定对象膜的PETG膜侧接触的方式,用上述的2张叠层板夹住测定对象膜。然后,在测定对象膜的上下夹入2张叠层板的状态下,再利用加压机的一对加压板,夹住配置在2张叠层板的各自最外侧的0.5mmSUS板,使用空压式加热加压机(IMC-1839型:井元制作所制),以120℃、空气压力0.2MPa加压60秒钟,制成叠层体。
<粘接性评价>
将制成的叠层体利用AUTOGRAPH(AGS-X:岛津制作所制)安装于胶粘带剥离试验装置,对作为测定对象的树脂组合物的50μm的膜进行从PETG的100μm的膜撕下的剥离试验(以剥离速度152.4mm/min、90°剥离试验),如下评价粘接性。
膜不能剥离:非常良好
剥离力20N/50mm以上:良好
剥离力低于20N/50mm:差
<耐久性>
如下评价各实施例和比较例的树脂组合物的耐久性。使用对象树脂组合物制成厚度0.78mm的卡片,使用IC卡片弯曲·扭转试验机((株)东洋精机制作所制)实施卡片弯曲试验,测定直到卡片发生开裂的弯曲次数。卡片弯曲次数的测定根据JIS X6305-1进行,利用次数的数值如下进行评价。
低于1000次:差
1000次以上且低于3000次:良好
3000次以上:非常良好
<透明性>
各实施例和比较例的树脂组合物的透明性如下评价。使用测定对象树脂组合物将厚度0.3mm的膜成型,使用雾度计(村上色彩技术研究所制HM-150)测定雾度(Haze)值,如下评价透明性。雾度值的测定根据JIS K 7136进行。
雾度值:5%以上:差
雾度值:1%以上且低于5%:良好
雾度值:低于1%:非常良好
<黑色度>
试验片制成
对详细内容后述的实施例4~7和比较例6~13的膜实施激光打标加工,如下评价黑色度。首先,使用测定对象的树脂组合物,将含有炭黑或金属氧化物的厚度0.1mm的激光打标膜成型。另外,使用不含上述测定对象树脂组合物中的炭黑和金属氧化物的树脂组合物,成型0.1mm的覆盖(overlay)膜。进而在覆盖膜成型中使用的树脂组合物中添加氧化钛(RESINOCOLOR工业(株)制“White DCF-T-17007”)使其作为整体达到15wt%,使用制成的树脂组合物,成型厚度0.2mm的白色芯膜。
将制成的膜以覆盖膜、激光打标膜、白色芯膜的顺序重叠。将它们这3层重叠得到的测定对象膜的上下用2张叠层板夹住,该叠层板是0.5mm的SUS板、1mm的硅胶片、100μm的SUS板、0.78mm的特氟隆(注册商标)片的4张叠层板。即,以1个叠层板的特氟隆片接触测定对象膜的覆盖膜侧,另一个叠层板的特氟隆片接触测定对象膜的白色芯膜侧的方式,用上述的2张叠层板夹住测定对象膜。然后,在测定对象膜的上下被2张叠层板夹着的状态下,再利用加压机的一对加压板,夹住配置在2张叠层板各自的最外侧的0.5mmSUS板,使用空压式加热加压机(IMC-1839型:井元制作所制),以160℃、空气压力0.2MPa加压60秒钟,制成叠层体。
使用激光打标装置(Rofin-baasel制“EasyMarIV-E10”),在利用加压得到的叠层体从覆盖膜层侧在以下的照射条件下实施激光打标。利用分光浓度计(Xrite(株)制“X-Rite504”)测定印字部,将所得到的值的最大值作为黑色度。
激光打标条件
扫描速度(Scan Speed):1,000mm/s
输出能量(Output Energy):21~30A
脉冲频率(Pulse Frequency):10~100kHz
<激光显色性的评价>
将黑色度的值为阈值1.70以上的实施例或比较例评价为激光显色性判定“良好”、将黑色度的值低于阈值的实施例或比较例评价为“差”。此外,对于不含炭黑和金属氧化物且不具有激光打标性能的实施例和比较例,激光显色性评价为“无”。
<树脂组合物的制造>
如下制造实施例1~3和比较例1~5的树脂组合物。即,在如下所述表1中以缩写表示的树脂中,将聚己内酯(聚ε-己内酯:重均分子量:10000)、磷腈阻燃剂((株)伏见制药所制“Rabitle(注册商标)FP-110”)、以表1中分别所示的含量添加,得到均匀的树脂组合物。
如下制造实施例4~7和比较例6~13的树脂组合物。即,在如下所述表1所示的树脂中,将聚己内酯(聚ε-己内酯:重均分子量:10000)、炭黑(Cabot Corporation制“MONARCH(注册商标)800”)、金属氧化物(Tokan Material Technology Co.,Ltd.制“42-920A”)以表1中分别所示的含量添加,并搅拌,得到均匀的树脂组合物。
另外,在下述表1所示的树脂中将聚己内酯(Perstorp公司制CAPA(注册商标)6800:重均分子量80,000)和上述炭黑以表1中分别所示的含量添加并搅拌,制造实施例8的树脂组合物。
此外,上述金属氧化物(“42-920A”)是三氧化铋Bi2O3和三氧化钕Nd2O3的混合物,具体而言,是包含98~99质量%的Bi2O3和0.3~1.0质量%左右的Nd2O3的混合物。
(PC)
双酚A型芳香族聚碳酸酯树脂
(三菱工程塑料株式会社制“Iupilon(注册商标)E-2000”、热变形温度(玻璃化转变温度)150℃)
(PETG)
改性聚对苯二甲酸乙二醇酯树脂
(SK Chemicals制“SKYGREEN(注册商标)S2008”、热变形温度(玻璃化转变温度)80℃)
(PC/PETG合金)
上述(PC)与(PETG)的50:50(重量比)的混合物
<试验片(片)的制造>
使用实施例1~7和比较例1~13的树脂组合物,如下制造试验片的片。首先,使用包括料筒直径32mm、螺杆的L/D=31.5的双螺杆挤出机的T模熔融挤出机,以排出量20kg/h、螺杆转速200rpm形成宽度300mm的片。料筒、模头温度在实施例1~7、比较例2、4~9、11和13中设定为280℃,在比较例1、3、10和12中设定为260℃。另外,作为片,制造表面的两面为镜面的片。为了评价上述的粘接性、耐久性和透明性,对每个各树脂组合物,形成具有50μm(0.05mm)、100μm(0.1mm)、300μm(0.3mm)、780μm(0.78mm)的4个厚度的膜,实施上述的各测定。
[表1]
符号说明
10 ID卡片(多层片)
12 第一表层
14 第二表层
16 第一激光打标层
18 第二激光打标层
20 第一芯层
22 第二芯层
24 天线-芯片
Claims (13)
1.一种树脂组合物,其特征在于:
含有93质量%以上97质量%以下的聚碳酸酯树脂、和3质量%以上7质量%以下的脂肪族聚酯,
所述树脂组合物含有以所述树脂组合物整体的质量为基准,0.0001~0.2质量%的激光显色剂,
而且,所述树脂组合物含有作为激光显色剂的炭黑,
所述炭黑的含量以所述树脂组合物整体的质量为基准,为1~100质量ppm,
所述脂肪族聚酯为聚ε-己内酯,
根据JIS K 7136测定的所述树脂组合物的雾度值小于5%,
所述树脂组合物所有组分含量之和不超过100质量%。
2.如权利要求1所述的树脂组合物,其特征在于:
所述树脂组合物具有激光打标性能。
3.如权利要求1所述的树脂组合物,其特征在于:
所述树脂组合物的玻璃化转变温度为100~135℃。
4.如权利要求1~3中任一项所述的树脂组合物,其特征在于:
以树脂组合物整体的质量为基准,含有3质量%以上5质量%以下的脂肪族聚酯。
5.如权利要求1~3中任一项所述的树脂组合物,其特征在于:
所述脂肪族聚酯的重均分子量为10000~90000。
6.如权利要求1~3中任一项所述的树脂组合物,其特征在于:
以树脂组合物整体的质量为基准,含有95质量%以上97质量%以下的聚碳酸酯树脂。
7.如权利要求1所述的树脂组合物,其特征在于:
所述激光显色剂还含有金属氧化物的颗粒。
8.如权利要求7所述的树脂组合物,其特征在于:
所述金属氧化物由下述通式(I)所示,
Bi(1-x)MxOy···(I)
式(I)中,M为选自钆和钕中的至少1种金属,x为满足0.001<x<0.5的关系的值,y为满足1<y<2.5的关系的值。
9.一种卡片用树脂片,其特征在于:
所述卡片用树脂片具有包含权利要求1~8中任一项所述的树脂组合物的层。
10.如权利要求9所述的卡片用树脂片,其特征在于:
所述卡片用树脂片具有嵌入式天线-芯片。
11.如权利要求9或10所述的卡片用树脂片,其特征在于:
所述卡片用树脂片用于激光打标卡片。
12.一种多层片,其特征在于:
其为具有二张以上的经过叠层的树脂片的多层片,其中的至少一层包含权利要求1~8中任一项所述的树脂组合物。
13.如权利要求12所述的多层片,其特征在于:
所述多层片还具有包含选自PETG、聚碳酸酯、PCTG、PCT和它们的至少2种的混合物中的任意一种的树脂片。