TW462955B - Infrared and ultraviolet radiation absorbing blue glass composition - Google Patents
Infrared and ultraviolet radiation absorbing blue glass composition Download PDFInfo
- Publication number
- TW462955B TW462955B TW086107212A TW86107212A TW462955B TW 462955 B TW462955 B TW 462955B TW 086107212 A TW086107212 A TW 086107212A TW 86107212 A TW86107212 A TW 86107212A TW 462955 B TW462955 B TW 462955B
- Authority
- TW
- Taiwan
- Prior art keywords
- glass
- weight
- patent application
- scope
- item
- Prior art date
Description
經濟部中央標準局員工消費合作社印裂 462955 A7 _B7__ 五、發明説明（1 ) 發明背景 1.發明領域 本發明係有關於一種適用於建築及汽車嵌裝用途之吸收 紅外光及紫外光輻射之藍色鈉-鈣-矽玻璃组合物。該玻璃應 具有主波長爲約4 8 5至4 9 1毫微米及色純度爲约3至1 8 %。 該玻璃也可與平板玻璃製造方法相容。 2A.技術考慮 吸收紅外光及紫外光輻射之有色玻璃基質具有各式各樣 用途。特定言之，此種玻璃建築師可用於嵌裝建築物，車 輛設計師可用作爲汽車窗。除了提供美觀愉悦顏色外，這 些玻璃也可提供較之習用透明玻璃增強之太陽性能。 不同的物質可加至玻璃中以提供所要顏色及光譜性能。 例如，一般都是加入鐵，姑，錄，栖及欽（只舉一些）以提供 所要顏色組合物。由於加入物質是爲改變顏色及增強太陽 性能，故必須謹愼保持該特定用途所需之可視光透過率及 顏色。也應記住的是，改變玻璃之厚度即會影響這些光譜 性質，故特定厚度時具有可接受顏色及性能之特定組合物 ，在不同厚度時可能不被接受。 提供極優光譜性能的一種特別之藍色組合物己揭示於美 國專利第4,792,536號（頒予Pecoraro等人）。採用該專利之商 業產物有PPG工業公司出售的商標名SOLEXTRA®及 AZURITE®。此一玻璃在組成中併含適量之鐵，且相當大部 份的玻璃都呈亞鐵狀態，以FeO表示。特定言之，玻璃組 合物包括基本鈉-鈣-矽组合物，且進一步包括0.45至1重量 -4-
本紙張尺度適用中國國家標隼（CNS ) A4規格（210X297公H ------.---—裝-----1訂------線 (請先聞讀背面之注意事項再填寫本頁) !462955 A7 B7 五、發明説明（2 ) %總鐵（以F e 2 Ο 3表示）。總鐵中至少有3 5 %爲亞鐵狀態。這 些玻璃之主波長由約486至489毫微米，而色純度則自約8 至1 4 %。從製造之觀點而言，製造該專利所揭示具有高亞 鐵與總鐵比之玻璃，如本技藝所熟知，或許需作與習用玻 璃溶解作業一般不相關連的另外製程考慮。然而，由於此 產物普受接受，使用習用破璃熔解製造技術能製造具類似 顏色及增強光譜之玻璃，將是有利的。 2 B .相關專利 美國專利弟3,652,303號（頒予Janakirama Rao)揭示一種藍 色吸熱玻璃，其併含低量鐵並使用錫將相當部份的鐵轉化 並保持爲亞鐵態，而特定言之，80%以上的鐵保持亞鐵態。 美國專利第4,866,010及5,070,〇48號（頒予Boulos等人）揭 示著色劑部份主要由鐵及鈷所組成並進一步包括鎳及/或硒 之藍色玻璃组合物。這些玻璃之主波長爲482毫微米±1毫 微米，而色純度爲1 3 % ± 1 %。 美國專利第5,013,487及5,069,826(頒予Cheng)揭示包括鐵 ，欽，錫及鋅爲著色劑之藍色玻璃組合物。這些玻璃之主 波長自485至494毫微米，而色純度爲5至9%。 經濟部中央標準局員工消費合作社印製 ^—1' ^—^1 - - I I ^—^1 I I - - ^1 (請先閲讀背面之注意事項再填寫本頁) 美國專利第5,344,798號（頒予Morimoto等人)揭示一種包括 鐵、鈽、鈦、鋅、鈷及錳的藍色玻璃組合物。這些玻璃之 主波長爲495至505毫微米，而色純度爲5至9%。 發明概述 rn - t -i . 本發明提供一種使用鈉-鈣-矽玻璃基底組合物，另加鐵及 鈷作爲吸收太陽輻射之物質及著色劑之藍色玻璃。特定言 本紙張尺度適用中國國家標準（CNS ) A4規格（2丨ox 297公嫠） 462955 A7 B7 五、發明説明（3 ) 之，該藍色玻璃包含約〇.53至K1重量％總鐵，較佳約〇6 至0.85重量％及約5至40 PPM CoO、較佳約15至3〇 ppM ，且透光率爲至少5 5 %。若需要，該组合物可包含高達約 1 00 PPM Cr；!〇3。本發明之玻璃之氧化還元比維持於约 0.25至0.35之間’較佳約0.28至0.33之間。玻璃顏色之特 徵爲主波長（DW)爲約485至491毫微米，及色純度（pe, excitation Purity)爲約3至18%。在本發明之一特定具想例 中。玻璃之顏色之特徵爲主波長在約487至489毫微米之間 ，而在厚度爲約0.084至0.126吋時之色純度爲約3至8%， 在厚度爲約0.1 2 6至0 . 1 8 9吋時之色純度爲約5至1 2 %，及 在厚度爲約0.189至0.315吋時之色純度爲約10至18 %。 發明之詳細説明 本發明之基底玻璃組合物爲商用鈉-鈣·矽玻璃，其特徵如 (請先聞讀背而之注意事項存填寫本筲) .装_ 訂 經濟部中央標隼局貝工消費合作社印製 重量％ Si02 66 至 75 Na20 1 0至20 CaO 5至1 5 Mg〇 0至5 A 1 2 0 3 0至5 K20 0至5 如此處所用，全部"重量％，•値皆以最終玻璃組合物之總重 爲準。 線·' 462955 A7 B7 經濟部中央標準局負工消費合作社印製 五、發明説明（4 ) 在此基底玻璃中，本發明加入鐵及鈷及視情況鉻形式之 吸收紅外光及紫外光物質及著色劑。如此處所揭示，鐵係 以F e 2 0 3及F e 0表示，鈷係以C 〇 0表示及鉻係以C r 2 0 3表示 。應了解的是，此處所揭示的玻璃組合物可包含小量之其 他物質，例如熔解及淨化助劑，掉入物質或雜質。應進一 步了解的是，在本發明之一具體例中，可加入小量之另外 物質以使玻璃發色及/或改進其太陽性能，此將在稍後作更 詳細的説明。 玻璃組合物中的氧化鐵具有若干功用。氧化鐵，Fe203， 是一種很好的紫外光輕射吸收劑，在玻璃中作爲黃色著色 劑。氧化亞鐵，F e 0，是一種很好的紅外光輻射吸收劑， 在玻璃中作爲藍色著色劑。鐵在此處所揭示玻璃中的總存 在量係根據標準分析習慣以Fe203表示，但此並不暗示全部 的鐵實際上都是Fe203之形式。同樣地，亞鐵狀態的鐵量係 以FeO表示，既使其實際上並不以FeO存在於玻璃内。爲了 反映此處所揭示玻璃組合物中亞鐵與正鐵的相對量，氧化 還元” 一詞應意指亞鐵狀態之鐵量（以F e 〇表示）除以總鐵量（ 以F e2 0 3表示）=再者，除非另有註明，本發明書中的"總鐵 "一詞應意指以F e2 03表示之總鐵，” f e 2 0 3，'一詞應意指以 Fe2〇3表示之正鐵狀態之鐵，而，_Fe〇，__詞應意指以Fe〇表 示之亞鐵狀態的鐵。 C 〇 0係用作爲玻璃之藍色著色劑及弱紅外光輻射吸收劑 。可加入CI*2 03賦予玻璃組合物綠色組份。此外，咸信鉻也 可提供一些紫外光輻射吸收。鐵，即氧化正鐵與亞鐵，及 本紙張尺度適用中國國家標準（CNS ) A4規格（210XM7公董） 裝------^-訂------線 (請先閲讀背面之注意事項再填寫本頁} 462955 經濟部中央標準局員工消費合作社印製 A7 B7 —'' " ' '' -五、發明説明（5 ) 鈷，及視情況鉻含量間需有適當平衡才能獲得具有所要藍 色及光學性質之玻璃。 本發明之玻璃可用連續式大規模商用熔解設備熔解及淨 化，並以浮式法形成各種厚度的平板玻璃板；浮式法係用 一池的溶融金屬，通常爲錫，支撑熔融玻璃，一邊形成帶 狀一邊冷卻。應了解的是，由於在熔融錫上形成玻璃之故 ，相當量的氧化錫會侵入玻璃與錫接觸的一面的表面部份 。一般而言，一片浮式玻璃在玻璃與錫接觸過的表面下前 數微米内，Sn02濃度爲至少0.05重量％。 雖然較佳爲，此處所揭示的玻璃，如本技藝所熟知，應 使用習用，頂部燒火連續設備製造，但該玻璃也可使用多 段熔解設備製造，如美國專利第4,381,934號（頒予Kunkle等 人），第4,792,536號（頒予Pecoraro等人）及第4,886,539號（頒 予Cerutti等人）所揭示。若需要，可在玻璃製造設備之熔 解及/或形成階段中使用攪拌裝置以使玻璃均質化而製得具 最高光學品質之玻璃。 表1及5將説明具體使用本發明原則之玻璃組合物之實例 °PA1，PA2及PA3代表先前技藝藍色玻璃，實例1至14爲 試驗溶解物，而實例15至25爲由一玻璃顏色產生的電腦模 擬組合物及P P G工業公司所發展的光學性能電腦模型。僅 實例1至14之鐵及鈷部份列在表1中。表5進一步包括實例 1 5至2 5之鉻含量，表2至4及6至8則分別列出表1所示實例 1至1 4之光譜性質及表5所示實例1 5至2 5之光譜性質，基準 厚度分別爲0.089吋(2.3毫米），0.154吋(3.9毫米）及0.223吋（5.5 (請先閎讀背面之注意事項再填寫本頁) 丨裝. 訂 線 本紙張尺度適用中國國家標準（CNS ) A4規格（210X 297公釐） 462955 經濟部中央標準局—工消費合作社印黎 A7 ______B7 五、發明説明（6 ) 毫米）。至於表2至4提供之數據，透光率（Luminous transmittance, LTA)係使用 C · I. E . 2。觀察器及 C . I · E .標準 光源"A "之加重因數在波長範園3 8 0至7 7 0毫微米内測量。 太陽透過率（S olar transmittance，LTS)係在波長範圍380至 77〇毫微米内測量，使用C.I.E. 2°觀察器及ASTM 891-87 指定的加重因數。玻璃顏色，以主波長（DW)及色純度（Pe) 表示，係使用2 °觀察器之C . I. E .標準光源，，C ’，，依照ASTM E308-90確立的程序測量。太陽紫外光總透過率（tota丨s〇lar ultraviolet transmittance, TSUV)係在波長範圍 300至 400 毫 微米内測量，太陽紅外光總透過率（total solar infrared transmittance，TSIR)係在波長範圍720至2000毫微米内測量 ’而太陽能總透過率（total solar energy transmittance, TSET)則係在波長範圍300至2000毫微米内測量。TSUV， T SIR及T S E T透過率數據，如本技藝所知，係使用巴利蒙 (Parry Moon)空氣質量2·0直接太陽照射度數據計算，並使 用梯形定律積分。遮陰係數（Shading Coefficient, SC) —樣 本太陽熱總獲量與公稱3毫米厚（1/8吋）透明玻璃基準太陽 熱總獲量之比一係使用自勞儉斯柏克莱（Lawrence Berkeley) 實驗室購得之視窗4.1(Window4.1)電腦程式計算。表6至8 所呈現模擬组合物之光譜性質係根據相同波長範圍及計算 程序。 樣本製備 實例1至5 -表1所列實例1至5之資訊係根據於試驗用實驗 室熔解物，其具有約略以下基本配料組份： -9- 本紙張尺度適用中國國家標準（CNS) A4規格（2IOX297公釐） ----.--'---------ir------^ (請先閲讀背面之注意事項再填寫本頁) Α7 Β7
500克 162.8克 42克 121克 2.5克 按需要 按需要 Δ 6 2955 五、發明説明（7 ) 砂 純碱 石灰石 白雲石 芒硝 紅丹 CO3O4 每一熔解物中都加入煤炭控制氧化還原。製備熔解物時 ，將各原料秤出並置入混合機中拌合。然後，將—半的料 放入耐火氧化矽坩堝中並加熱至2650 T (1454 °C)30分鐘。 剩下的料然後再加至坩堝中並加熱至2650°F(1454°C)1 1/2小 時。接著，將熔融玻璃倒入水中碎裂，烘乾後再加熱至 2 6 5 0 T ( 1 4 5 4 °C ) 1小時。然後，再將熔融玻璃倒入水中第 二次碎裂，烘乾後再加熱至2650°F( 1454°C)2小時，然後 ，將熔融玻璃自坩堝倒出並予以徐冷。 實例6至9 -表1所列實例6至9之資訊係根據於試驗用實驗 室熔解物，其具有約略以下基本配料組份： 裳------訂^------線 f請先閑讀背面之注意事項再填寫本頁} 經濟部中央標準局員工消費合作社印製 砂 260.4 克 純碱 82.3 克 石灰石 22.1 克 白雲石 62·5 克 石膏 1.68 至 3.39 克 C 0 3 〇 4 0.0081 克 紅丹 按需要 -10· 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐> 462955 A7 B7 經濟部中央標準扃員工消費合作社印製 五、發明説明（
SoLex玻璃碎 按需要 將含碳原料加至配料中以控制氧化還原水準，例如美國 專利第4,551，161號（頒予Savolskis等人）所揭示。s〇LEX®破 璃係PPGX業公司出售的綠色鈉冬梦玻璃，其用於汽車嵌 裝用且一般具總鐵量爲約〇,52重量％及卜〇含量爲約〇 ^ 3 重量％。在製備熔解物時，將原料秤出並置入混合機中拌合 。然後將該配料放入耐火氧化矽坩堝中並加熱至26〇〇下 ( 1 427°C)90分鐘。然後，自坩堝倒出熔融玻璃，並予以徐 冷0 實例1 0至1 4 -表1所列實例i至丨4之資訊係根據於試驗用 實驗室熔解物，其具有約略以下基本配料組份： SOLEX®玻璃碎 3〇〇〇克 按需要 C〇3°4 按需要 將石墨加至每一熔解物中以控制氧化還元。在製備熔解 物時，將各原料秤出並置入混合機中拌合。然後將拌料置 於销-10%鈀坩堝中並加熱至265〇T( 1 454°C)2小時。接著 ’將溶融玻璃倒入水中碎裂，烘乾後再加熱至265(rF (1 4 5 4 C ) 1小時。然後’再將溶融玻璃倒入水中第二次碎裂 ’烘乾後再加熱至2 7 00T ( 1 4 82 °C)2小時。然後，自坩堝 倒出熔融玻璃並予以徐冷。 玻璃组合物之化學分析係使用理學（RIGAKU)3370-X射線 勞光分光光度計測定。F e0含量係使用光譜分析或濕式化 學技術測定’如本技藝所熟知。玻璃之光譜特徵係以徐冷 -11 本紙張尺度適用中國國家標準（CNS > A4規格（210 X 297公釐） .--^---—裝------訂-------線 (請先閱讀背面之注意事項再填寫本頁) 462955 A7 B7
Si02 Na20 K20 CaO MgO AI2O3 五、發明説明（9 樣本使用柏金-愛瑪（Perkin-Elmer)閑木大9 UV/VIS/NIR分光 光度計，在玻璃強化或長期暴露於紫外光輻射之前測定； 強化或暴露於紫外光輻射，如以下所討論，會影響光譜性質 以下係表1所揭示玻璃之代表性基本氧化物： 72.4至74重量〇/0 12.9至13.7重量％ 0.042 至 0.056 重量 ％ 8.2至9.1重量％ 3.5至3.9重量％ 0.14至0.2重量％ 預料表5中電腦產生之玻璃組合物之基本氧化物組份將類 似0 雖然不包括在表1内，實例1至14亦包含約5至1〇 PPM 〇2〇3，這些水準被認爲是掉入及/或殘餘水準，很可能是由 批原料或玻璃製造設備引入玻璃组合物中。此外，實例1， 3 5及10-13包含高達約39 PPM Mn〇2，此量也被認爲是掉 入及/或殘餘水準。實例2及14未經分析Mn〇2。再者，實例6 至9分別包含228，262，284及354 PPM Μη02。咸信這麼高 的]^11〇2含量係由於製造樣本時所用特定玻璃碎所致。表$ 中電腦產生之實例15-18，20及22-25係模擬成包含3〇 PPM Μη02。實例19及21在組成上與實例2〇類似，但彼等 分別不含Μη02及含3〇〇 PPM Mn〇2。Mn〇2曾用於幫助控 制玻璃組合物中的氧化還原。在本發明所揭示之玻璃組合 物中，咸信高達約0.1重量％Mn〇2之存在並不會影響玻璃之 顏色及性能。 -12- 本紙诔尺度適用中國國家標準（CNS ) A4規格（2ι〇χ297公釐 ---------裝------訂L------線 (請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製 462955 A7 五、發明説明（10 ) 經濟部中央標準局員工消費合作社印製 實例14 1 0,721 0.418 { 0.472 0.226 0.3132 實例13 0.648 0.209 0.323、! LO f'J 實例12 ,0.628 0.409 0.199 0.3171 OJ (N Φ 實例11 ：0,603 0.391 0.197 0.3241 實例10 ,0.598 0.409 0.172 0.2382 tN 0.749 0.516 1 — 1 0,198 ! 0.212 0.2712 丨 0.2832 〇) 實例8 0.730 實例7 0.726 ； I 0.202 ! 0.27S2 1 實例6 0.G68 1 0.455 0,1 94 0.2902 <D 實例5 0.308 .0,532 0.251 I 0.31 r1 卜 ίΝ 實例4 ,0.777 0.543 0.208 0.2682 OJ ' CQ 1 實例U 0.732 0.咖 I |〇.231 0.3131 〇 實例2 0.737 0.475 0.3232 實例1| 0.631 0.465 ； 0.196 0.2S81 in r-* ΡΑ 3 0,475 0,333 0.123 0.2592 lO to ΡΑ 2 0.44S 丨 0.336 0,100 I !〇.224j ；_ £ 2 0.379 Γ〇,73 0.097 0.2562 | 總鐵（Wt.%l [Fe203 Fe〇 fwt.%) I乾化還原 ICoO (PPM)' j ----.—.---丨^-------------^ (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) Α4規格（210Χ297公釐） 462955
7 7 A B 經濟部中央標準局員工消費合作社印製 五、發明説明（η ) I [η d S ο ο 2 駟 卜 α； 卜 Ο σ3 Γ、 〇 d CD 卜 00 CO 吋 d to 00 K oo 寸 ui 卜 r- d σ> 卜1 卜 — σ> 卜 tN CD <J) — 寸 CO d CO CO O) 寸 00 〇 00 d 知 卜 00 1^ ω σί 卜 O) 〇i CO in (D 寸 to — CD ΙΟ 卜· CO rt LD ω d τ 恥 C0 σί 卜 寸 ό CO 卜 c6 <D 00 ώ 寸 CD - CD 卜· CO 计 CO ω d ο 卜 CN d 00 00 Γ0 CO €0 κ 寸 寸 ci CO c〇 卜· 00 寸 LD (N 00 d £ q 卜· 卜 CO cd 卜 τ— iT> 寸 σί co to ¢6 lf> 〇 (X> 寸 卜 寸· 卜 d 〇c Φ LO 卜 \— 卜 CO tr> in ο t~ 寸 q 卜' LO 寸 α> 00 寸 Ο LO 卜 卜 d 卜 和 〇 卜 CN cd 卜 00 lO to 00 σί CO 00 to to CO σ> CO 寸 ① r- 卜 ό CO 00 Γ- CD 〇i 卜 O) 〇ΐ LD Γ0 Ol ¢0 ^ LO 卜 σί oo 寸 ΙΩ CO 卜 d 〇 u> CO (Ό 卜 €0 CD LO Τ— CD CO 00 ιό U) ΙΟ 00 寸 CO Lf) CO r^ d 寸 寸 ιτ> 卜 cd LO K LD CN (N 寸 卜 LO eg 卜* CO 寸 寸 LO CO 卜 d CN 卜 寸 O'J f、 CD 00 ID If) <N 寸 LO 03 If) oi 00 00 寸 00 (D 卜‘ d <N 吋 CD 卜 r、 卜 CD Ο) LO Γ0 CO 吋 iri LO CO CO -寸 CD in CO r- d ί： η σ> 卜 d 00 CM 5 q K 寸 O) t—* ω 卜 CO 00 dh 03 C9 5 d S < Η w 'j Ϊ > ⑺ l·- £X U) 卜 g te ω H E <: 6 g QJ Q_ CJ ⑺ -14- I---.--.---1策-----!.^l------^ (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（2ίΟΧ 297公釐） 462955 五、發明説明（12 ) 經濟部中央標準局員工消費合作杜印製 實例14 | 67.6 69,6 43.2 21.4 ：42.8 487.6 r**- oi — 0.65 實例13 1 69.4 71.2. I 51.4 ! 27.2 46.9 I 487.1 co 00 0.69 :實例12 1 70.6 ! 72.3 52.3 I 28.8 48.3 487.3 I 卜 0.70 實例11 71.5 73.2 r 53.3 I 29.1 48.9 | 487.5 7.4 i 0.70 實例10 71.2 |_72』 53,5 30.2 49.4 I 487.1 7.7 0.71 : 實例9 | 68.1 70.0— _ L 45.5 , 22.0 C9 寸 488.9 τ~~ CO 0.65 I 實例s 1 66.4 63.3 43.4 23.4 43.2 I_ 「488.3 ---1 8.4 0.65 實例7 1 68.1 69.9 44.2 22.4 43.1 489.2 ___ί Γ ；7.8 0.65 實例6 70.6 72.5 '49.0 I 20.2 1' 43.0 489.6 7-7 ^ 0.65 1 實例_'5 65.0 66.9- 44.9 '21.6 1 41.8 4S7.3 i 9.5 | _I 0.64 1實例4 | 65.7 1 67.6 46.4 I 24·6 I 4-3.9 487.0 0.66 實例3 68.3 I 70.2 47.2 ί 24.8 44.9 488.0 5 0.67 , 實例2 1 丨 67.1 69,2 49.0 ] I 20.1 j 41.9 487.6 in O) I 0.64 j 5 71.5 73.2 50.4 29.4 ] 48.8 488.5 卜 (Ω 0.70 LTA (%)] LTS (%) 丁SUV (%) TSIR (%) TSET (%) DW (πγτί) Pe (%l (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（210 X 297公慶） 462955
7 7 A B 五、發明説明（13 ) δ.ο 蛵濟部中央標準局員工消費合作社印製 寸 CN 卜 ¢0 (D CD 〇 卜 Ο) LO 5 ό 寸 \— o 00 K 00 寸 ΓΟ r~* in d 實例13 61.5 - 63.3 43.0 I 16.3 I 37.4 487.0 00 t t~~ 1 0.60 C1 〇 CN Ο to CO <N o CN 09 IX) 卜- 00 卜 O) T~~ iO 私 CO CD 寸 — C9 o i i ? <N 寸 τ— cn 寸 <D (N -J： CD UQ oi 卜 CO 寸 d to CD CD 寸ι — ,^ — d 〇 CQ 〇 寸 00 o CD σ> CO CO ΙΟ 00 6 i£> OT a CO 和: (〇 CD 寸 1 吋 — d CO <N CD Ά— CO CO 寸 卜 O) <X) rJ ri oi CO 吋 T- in o 私 LO CO r> T— CO s- CO ω o 寸 04 LO o to 卜’ o' 寸 CO CO 488 <N u) ΓΟ X— CO T- o 卜 CN 寸 00 1 4S9.1 I 1- Γ ΙΟ ci oi ΙΟ c4 CO T~* 駟 LO <O Γ0 τ— ro d 〇 CO 寸 廿 CO CO ID CD 00 id d d 勺： 0) 00 寸 d ID <〇 i〇 寸 T*- CO K~^ d 丨實例S ! CD 寸 σ> 00 CO 1~~ 寸 <D ui 00 ID r— oi 00 寸 CO LO LO in ·» CO t— CO T— d 寸 00 1~ CN| τ- t— 00 ^ _ 00 CD 〇> 寸 — <〇 CO 寸 CO lO LD ιο Γ0 r·- 01 T~ d 實例3 T*·- 寸 寸 00 计 G) CD CD d 〇j 00 寸- in 卜 00 寸 r^· ID CD CO CO <— CO x— 6 實例2 | CD (N 计 CD 00 tn 00 LO 1™ CO o 6 t— CN Γ0 Γ ΟΟ 寸 Γ0 T-~ ID o 實例1 6^.2 | 66.3 41.9 13.1 39.3 .4884 CD CT) 0.62 g < 卜 LTS (%) ! TSUV (%} g cn g 卜 LU CO Ε 5 ① o _.l h" a α_ w -16- ---.--.----------L------ά. (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（2ΪΟΧ297公釐） 462955 五、發明説明（w) 經濟部中央樣隼局員工消費合作杜印製 m r) ¥ 〇 〇 r— X- σι 〇 卜 d 〇J in CO d CO d {〇 o ID 寸 (N 〇 〇 τ— ο ο 卜 ό o r- CM ό o 卜 £N d 〇 tO Ip； 〇 σ> 6 ο 00 in ό 00 〇〇, CM 6 CO ό 00 T— s r·'* LT) 03 'Ο 卜 CO LO d in LO CM 〇 o 〇 r〇 d LO <N LO -(N Ο ό CO 寸 d CO 〇 (N 6 o a) CN d ID 駟 〇 ν— 〇· 廿 d CD 〇 CN d 〇 σ> <N d LD ο r™ ό t- CO 寸 6 CO 〇 <N d 〇 σ> cn 6 LO «>〇 τ ;私 CO 00 CD ό CD lh 寸: o 卜 _ o iN d o 〇 CO 6 o CN LO 卜 知 ο ιο CD d ω 寸 ό (N C〇 t— d 〇 CO CN d UQ CO s ο 〇 CO d § d 吋 1~~ d o σ) CN d to Oi s »rv r-^ 〇 CO in d CN 寸 cn ό o 卜 T ό 〇 iN CO d ΙΩ tN in § ♦-* & 〇 fvj ιϊί 如： ? o i O- 〇 o 〇 5 6 r> 〇 6 (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（21 OX2?7公嫠） 462955 A7 B7 五、發明説明（〗5 ) 駟ti-s^w^ir(日日 rcir6800 經濟部中央標準局員工消費合作社印製 實例24 !實例25 71.S | 73.5 - 52.8 1 26.7 | :47.5 | 489.1 6.7 0.69 i 72.7 1.74.1 52.9 | 3Γ3.2 | 35.3 | 52.9 ! 52.7 | 487.5 5.4 I 6.1 0.73 | 0,73 i 實例23 76.0 77.3 56.7 488.8 * r» ri "^7 75.9 77,2 ! 57.0 - co 55.1 488.2 5.2 0.75 實例21 : 78.6 79.7 59.9 | 44,0 | 60.0 488.8 | I 4.0 i 0.79 ' 實例20 78.6 79.7 60,0 44,0 i 60.0 488.6 T— 寸 0.79 實例ιί] 78.6 79.7 60:0 44.0 60.0 488.6 4.1 0.79 實例15tl實例t6 1實例17!實例181 78.6 I 79.7 60.8 44.0 60.0 488.8 4.3 0.79 78,6 I 76.6 I 77.7 61.1 47.8 CO '一 CD l 487.3 4.8 0.81 r 79,7 62.7 49.2 62.9 488.5 4.0 I 0,82 ' 79,5 1 80.5 1__________ 65,5 50.0 63.9 486.4 4Λ 0,83 LTA i%) | LTS (%) TSUV (%) TSIR (%) TSET (%) DW (nm) I jPe (%) u if) ! I - .^ϋ · - - il^i I I — I - - 1^1. — ml lr^—、一DJt-i n J^i p L (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） 462955 A7 B7 五、發明説明（16 ) 經濟部中央標準局員工消費合作社印製 «η (N to d CD 〇 Γ0 CD 寸 d 寸 卜 ^— T— CO cn 00 00 寸 04 X— T— Lf) d ¥ 卜 s 卜 CO CD o CO 00 r·" CD 00 ro CO 〆 00 寸 气 d r— CD d ¥ ΙΟ to CO CD CO CD iri 寸 CD CD Ά— in oi CO 卜 od CO 寸 t— CD 04 CO d LO -to CO 寸 CO <D o d T" LO — 吋 〇 α> CO 寸 CD CX) 寸 CD d <N 恥 {D d 卜 T (N 卜 CN σ)· 寸 计 cw 03 CD 寸 CD 00 00 吋 σ> CD 00 CD d LO ό 卜 CNi <N CO σί 寸 寸 CD 00 <ό 寸 in 03 00 吋 〇 卜’ CO CO d 〇> 私 LO 〇 cM 〇i 卜 crj 寸 寸 CD OJ 00 <ή 寸 in CO CO 寸 o CO CD d CO ，.冢 (D 0 co- 〇J 卜 09 ό ur> C0 tD Csi €0 CO 寸 CM od ex? 寸 (N 00 CD d 卜 1 1 *ϊΓ* 叶 <D 〇> CD 卜· ό ΙΟ CO d CO 00 卜* 寸 Τ'" κ CO 寸 CNi 00 O) CO ό 恥 LO d r- T— OJ 卜 卜 CN t〇 00 r— CO 00 ? CO 00 00 寸 00 CD r— r- d 1〇 σ> t— CO CO 卜 CM tD to to rsi CO LO <N CD 00 寸 tn CM 卜 o < Hj g CO 卜 」 g > D CO 1~ g cc w i— 2 Η* UJ XD 1- E S ί Q ? ω Q_ o ω (請先閲讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐> 4 6 2955 A7 B7 五、發明説明（17 輙超lr^w^El:(iln.s)t£3ro 經濟部中央標準局員工消費合作社印製 to ίΝ ? 卜 d ΪΓ> ID CO to — " CO t—； ir> 00 in CN CO 00 00 寸 卜 ui —1 o LD d ο ur> CO 寸* ID in r"~ 寸 σ> OJ cri <N T*~ 寸· n IT) d σ> 卜'· ιο d (D to CO CM 00 CO 6 CO <〇 CO TO 00 CN — l〇 in 6 r4 (N ，卜 ID t— d CD r^ ό in d t— CO OJ CO CD 00 寸 CD CNJ r— to LO d »—* CO CN CD <J> CO to d 寸 to iri ^— co 卜 in 00 00 计 00 O) o CD d 00 CNJ CD 〇 in co CO d 寸 CD Ln 1~ CO co 寸 00 CO 寸 o d τ— o CD 0 0-1 — 私 00 CN CD 〇 LD CD 00 d 寸 ω LO T— CO 卜- C9 寸 οό 00 寸 q d T" 〇 CD d CO 冢 CD oi CD 5 to CD 吋 in ir> \— co 〇 00 CO 寸 CO d r- 〇 CD 6 卜 1—« ΤΓ» σ) 00 ID o 5 <N 〇i 计 0D CO τ— 03 CO ο 00 寸 CD T-τ— τ— CD d oo <N CD 00 CO LQ 寸 T— o CN o o 寸 CN οό 00 寸 卜 oi CQ CD d r—· 5 {〇 寸 (D CD CO ' CD Lil 〇5 寸 O) 6 OJ to r— 寸 ο CO 00 寸 卜 d 1— 寸 CD 6 < H ? c/> H O'- > Z) in l·- ? DC to \- g fc CO h- E g Q g 〇 C/3 I 裝 .—訂 I線 {請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家榇準（CNS ) A4規格（210 X 297公釐） 經濟部中央標準局員工消費合作社印製 462955 A7 _B7_ 五、發明説明（IS ) 請參閲表1至8，本發明提供一種使用標準鈉-鈣·矽玻璃 基底组合物’另加鐵及钴，及視情況鉻，作爲吸收紅外光 及紫外光輕射物質及著色劑之藍色玻璃。特定言之，玻璃 之紅外光及紫外光輻射吸收及著色劑部份包含約〇 . 5 3至1 . 1 重量％總鐵，較佳約〇 . 6 0至0.8 5重量％總鐵及約5至4 0 PPM CoO，較佳約15至30 PPM CoO。此外，該組合物 可包含高達100 PPM Cr203，較佳25至50 PPM。該玻璃 之氧化還原爲約0.25至0.35，較佳約0.28至0.33，及透光 率（LTA)爲至少55 %。在本發明中，主要的是，玻璃之主 波長要在約485至491毫微米之間，較佳約487至489毫微 米之間，及色純度要在約3至約1 8 %。應了解的是，色純度 視玻璃厚度而定。因此，較佳爲本發明之玻璃，厚度爲約 0.084至0.126吋（2.1至3.2毫米）時，Pe爲約3至8°/。；厚度 爲約0.126至0·189吋（3.2至4.9毫米）時，Pe爲約5至12 % •’及厚度爲約0.189至0.315对（4·9至8毫米）時，Pe爲約 1 0 至 1 8 %。 此處所揭示並以浮式法製成之玻璃組合物一般板厚度係 自約1毫米至10毫米。供車輛嵌裝用時，具有此處所揭示組 成之玻璃板，其厚度較佳在0.071至0.197吋（1.8至5毫米） 範圍内。預期使用單層玻璃時，玻璃將強化，例如汽車侧 窗或後窗用時’而使用多層時，玻璃將徐冷並使用熱塑性 接著劑膠合，例如汽車擋風玻璃，其係由兩片徐冷玻璃使 用聚乙烯丁搭中間膜膠合而成。此外，當此玻璃使用於機 動車輛之特選部份時，例如擋風玻璃及前門窗及—些情後 -21 - ^紙張適用中關家標準（CNS) A4規格（21()><297公楚 --- ----.-----—装-------ir^-------^ (請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作杜印裂 462955 A7 _____B7 五、發明説明（19 ) 窗時’玻璃之L Τ A需要至少7 0 %。此外，本發明所揭示玻 璃組合物之T S U V應不大於6 0 %，較佳不大於5 〇 % ; τ SIR 應不大於約3 5 %，較佳不大於約3 〇 % ;及τ S E T應不大於約 55%，較佳不大於約50% ;皆以厚度約〇 154吋而言。 在建築物嵌裝用途上，對於玻璃之太陽透過率（LTS， Solar transmittance)—般都無法律規定；然而，在本發明而 5 ’玻璃較佳具有LTS爲約60至70%，較佳約63至67%， 及遮陰係數爲不大於約0.70，較佳不大於約0.65% ;皆以 厚度約0.223吋而言。 預期玻璃之光譜性質在玻璃強化及進一步長期曝露於紫 外光輻射-通稱曝晒-後會改變。特定言之，預估此處所揭示 玻璃組合物經強化及曝曬後會使L τ A，L T S及T SIR降低約 0 5至1 % ’使T S U V降低約1至2 % ’及使T S E T降低約1至 1_5%。因此’在本發明一具體例中，玻璃組合物具有特選 光譜性質’其最初在先前討論之所要範圍外，而在強化及/ 或曝曬則在所要範園内。 也應了解的是’由於光及太陽透過率（LTA及LTS)會因 這些情況而降低，故爲了保持透過率在所要最低水準以上 ，製造後之玻璃之最初LTA或LTS必須足夠高，俾歸因於 強化及曝晒之任何損失都不會使透過率降至不可接受程度。 如早先所討論，其他物質也可加至此處所揭示玻璃组合 物中，以進一步降低紅外光及紫外光輻射透過及/或控控制 玻璃顏色。鉻及錳之加入，先前已討論過。預想以下物質 也可加至此處所揭示含鐵及鈷之鈉-鈣-矽玻璃中： -22- 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） .-----—裝------ 訂-------0 (請先閲讀背面之注意事項再填寫本頁) 462955 A7 ____B7 五、發明説明（)
S η 0 2 0至約2.0重量％ Ce02 〇至約1.0重量〇/0 Ti〇2 0至約0.5重量〇/〇 ZnO 0至約0.5重量％ Nd203 0至約0.5重量％ Mo03 0 至約 1 0 0 P P Μ V2〇5 0至約7 5 Ρ Ρ Μ NiO 0至約10 PPM Se 0至約3 PPM 如應了解的是’可對玻璃之基本組份作調整，以促使這 些另外物質產生任何著色及/或氧化還原影響力。 熟諳此技藝者所知的其他變異都可在不偏離隨附申請專 利範圍所界定本發明之範園下進行。 ----.-----1¾衣-----ίιτ^-------線 {請先閲讀背面之注意事項再填寫本頁) 經濟部中央標率局員工消費合作社印製 - 3 2 本紙張尺度適用中國國家標车（CNS ) Α4規格（2 [ Ο X 297公釐）
Claims (1)
- 4綦总&55號專利申請案 中文申請專利範圍修正本(90年9月) 六、申請專利範圍 1. 一種藍色、吸收紅外光及紫外光輻射之玻璃組合物，其 基底玻璃部份包含： Si02 66至75重量％ Na20 10至20重量°/〇 CaO 5至15重量％ MgO 0至5重量％ AI2O3 0至5重量％ K20 0至5重量％ 及其吸收太陽輻射及著色劑部份主要係由以下所组成 總鐵 0.53至1.1重量％ CoO 5 至 40 PPM C r 2 0 3 0 至 100 PPM 該玻璃之氧化還原為0.25至0.35，透光率之最小值為55% ，及顏色之特徵為主波長在485至491毫微米範圍内而色 純度為3至18%。 2. 根據申請專利範圍第1項之組合物，其中總鐵濃度為0.6 至0.85重量％及氧化還原為0.28至0.33。 3. 根據申請專利範圍第2項之組合物，其中CoO濃度為自15 至 30 PPM β 4. 根據申請專利範圍第3項之組合物，其中玻璃之顏色之特 徵為主波長在487至489毫微米之範圍内，而色純度在厚度 為0.084至0.126吋時為3至8%，色純度在厚度為0.126至 0.189吋時為5至12%，及色純度在厚度為0.189至0.315吋 時為10至18%。 本紙張尺度適用中國國家搮準(CNS) Α4规格(210X297公爱:) A B c D 462955 六、申請專利範圍 5. 根據申請專利範圍第4項之組合物，其中玻璃之透光率為 70%或更大& 6. 根據申請專利範圍第4項之组合物，其中玻璃之太陽透過 率為60至70%，而遮陰係數為〇?〇或以下。 7. 根據申請專利範圍第1項之組合物，其中c〇〇濃度為自15 至 30 PPM。 8. 根據申請專利範圍第1項之組合物，其中濃度為自25 至 50 PPM。 9. 根據申請專利範圍第1項之組合物’其申玻璃之透光率為 70%或更大* 10-根據申請專利範圍第9項之組合物，其中玻璃之太陽紫外 光總透過率為60°/。或更少，太陽紅外光總透過率為35%或 更少及太陽能總透過率為55%或更少；皆以厚度〇. 154付 而言。 11. 根據申請專利範圍第10項之組合物，其中玻璃之太陽紫 外光總透過率為50%或更少，太陽紅外光總透過率為3〇% 或更少及太陽能總透過率為50%或更少；皆以厚度〇. 154 吋而言。 12. 根據申請專利範圍第1項之组合物，其中玻璃之太陽透過 率為60至70%及遮陰係數為〇.7〇或以下；皆以厚度為0.223 叶而言。 13. 根據申請專利範圍第12項之組合物，其中玻璃之太陽透 過率為63至67%及遮陰係數為0.65或以下；皆以厚度為 0.023付而言》 本紙張尺度速用中B曲家標準(CNS) A4規格(210 X 297公) 462955 έβ C8 DS 六、申請專利範圍 14. 根據申請專利範圍第1項之組合物，其中玻璃之顏色之特 徵為主波長在487至489毫微米之範圍内。 15. 根據申請專利範圍第1項之組合物，其中玻璃之顏色之特 徵為色純度在厚度為0.084至0.126吋時為3至8%，色純度 在厚度為0.126至0.189吋時為5至12%，及色純度在厚度為 0.189 至0.315 吋時為 10至 18%。 16. —種自申請專利範圍第1項之組合物製成之玻璃板。 17. 根據申請專利範圍第16項之玻璃板，其中玻璃板之厚度 為介於1.8至10毫米之間。 18. —種藍色、吸收紅外光及紫外光輻射之玻璃组合物，其 基底玻璃部份包含： Si〇2 66至75重量％ Na20 10至20重量％ CaO 5至15重量％ MgO 0至5重量％ AI2O3 0至5重量％ κ20 0至5重量％ 及其太陽輻射吸收及著色劑部份主要係由以下所組成 總鐵 0.53至1.1重量％ CoO 5 至 40 PPM Sn02 0至2.0重量％ Ce02 0至1.0重量％ Ti02 0至0.5重量％ ZnO 0至0·5重量％ -3- 本紙張尺度適用中B 8家揉準(CNS) A4规格(210X297公釐) A BCD 4 6 2955 六、申請專利範園 Nd203 0至0.5重量°/〇 Μη02 0至0.1重量％ Mo03 0 至 100 PPM Cr203 0 至 100 PPM V205 0 至 75 PPM NiO 0 至 10 PPM Se 0 至 3 PPM 該玻璃之氧化還原為0.25至0.35，透光率為55%至100%， 及顏色之特徵為主波長在485至491毫微米範圍内而色純度 為3至18% β 19.根據申請專利範圍第18項之組合物，其中玻璃顏色之特 徵為主波長在487至489毫微米之範圍内，而色純度在厚度 為0.084至0.126吋時為3至8%，色純度在厚度為0.126至 0.189吋時為5至12%，及色純度在厚度為0.189至0.315吋 時為10至18°/。。 -4- 本紙張·尺度逋用中8 8家搮準(CMS) A4规格(210 x 297公A) 5·28補充I δ!月-R 申請日期 86. 05. 28 案 號 86107212 類 別 Γ.....Μ專利 發明 名稱 中文 説明書 吸收紅外光與紫外光輻射之藍色玻璃組合物 英文 INFRARED AND ULTRAVIOLET RADIATION ABSORBING BLUE GLASS COMPOSITION 姓 名 1. 賴瑞傑希莉斯泰克 2. 大衛爾哈金斯 發明 國 籍 1-2均美國 裝 住 '居所 1 美國賓州拜德福市佛德街1046號第233號郵箱 2.美國賓州吉伯森尼亞市歐拜伯卡路261號 訂 姓 名 (名稱） 美商片片堅俄亥俄州工業公司 線 經"部智^:^4"0工消"入〇作社印製 申請人 國 籍 吴國 住、居所 (事務所） 代表人 姓 名 美國俄亥俄州克利夫蘭市西143大道街3800號 莉塔，柏格斯卓 本紙張尺度遍用中國國家標準（CNS ) Λ4規格（210X29?公釐）4綦总&55號專利申請案 中文申請專利範圍修正本(90年9月) 六、申請專利範圍 1. 一種藍色、吸收紅外光及紫外光輻射之玻璃組合物，其 基底玻璃部份包含： Si02 66至75重量％ Na20 10至20重量°/〇 CaO 5至15重量％ MgO 0至5重量％ AI2O3 0至5重量％ K20 0至5重量％ 及其吸收太陽輻射及著色劑部份主要係由以下所组成 總鐵 0.53至1.1重量％ CoO 5 至 40 PPM C r 2 0 3 0 至 100 PPM 該玻璃之氧化還原為0.25至0.35，透光率之最小值為55% ，及顏色之特徵為主波長在485至491毫微米範圍内而色 純度為3至18%。 2. 根據申請專利範圍第1項之組合物，其中總鐵濃度為0.6 至0.85重量％及氧化還原為0.28至0.33。 3. 根據申請專利範圍第2項之組合物，其中CoO濃度為自15 至 30 PPM β 4. 根據申請專利範圍第3項之組合物，其中玻璃之顏色之特 徵為主波長在487至489毫微米之範圍内，而色純度在厚度 為0.084至0.126吋時為3至8%，色純度在厚度為0.126至 0.189吋時為5至12%，及色純度在厚度為0.189至0.315吋 時為10至18%。 本紙張尺度適用中國國家搮準(CNS) Α4规格(210X297公爱:)