TW440591B - Coating composition forming porous mineral coatings for buildings comprising an aqueous emulsion - Google Patents
Coating composition forming porous mineral coatings for buildings comprising an aqueous emulsion Download PDFInfo
- Publication number
- TW440591B TW440591B TW085102290A TW85102290A TW440591B TW 440591 B TW440591 B TW 440591B TW 085102290 A TW085102290 A TW 085102290A TW 85102290 A TW85102290 A TW 85102290A TW 440591 B TW440591 B TW 440591B
- Authority
- TW
- Taiwan
- Prior art keywords
- group
- coating composition
- alkyl
- silicon
- patent application
- Prior art date
Description
9 1 ^ 經濟部中央標準局員工消费合作社印製 五、 發明説明 (1 ) 1 I 本 發 明 相 關 於 用 作 防 水 多 孔 性 礦 質 建 築 材 料 之 有 微 矽 1 1 化 合 物 水 性 乳 化 液 f 而 且 亦 相 關 於 使 用 乳 化 液 以 製 備 防 水 1 I 建 築 材 料 之 方 法 〇 請 先 1 1 使 用 有 機 矽 化 合 物 水 性 乳 化 液 以 保 護 建 築 物 V 主 要 由 閲 讀 1 [ 於 ; 對 水 及 污 物 之 優 良 浸 漬 性 9 其 與 環 境 之 相 容 性 及 其 在 之 1 注 I 生 理 上 之 可 接 受 性 Ο 意 1 美 國 專 利 US -A -4 ,7 57 ,1 06 中 曾 述 及 用 一 含 有 銨 基 之 聚 項 再 1 填 1 有 機 矽 氧 烷 及 含 有 環 氣 基 之 聚 有 機 矽 氧 院 之 水 性 乳 化 液 對 寫 本 "} 中 性 礦 質 建 築 材 料 之 浸 漬 作 用 〇 因 銨 基 受 到 中 和 作 用 且 乳 頁 1 1 化 作 用 破 壞 > 對 鹼 性 建 築 材 料 之 防 水 功 能 減 弱 〇 所 以 聚 有 1 I 機 矽 氣 院 幾 不 能 穿 入 建 築 材 料 〇 1 1 含 有 樹 脂 狀 具 有 院 氧 基 之 聚 有 機 矽 氣 烷 作 為 有 效 成 1 訂 1 I 分 之 乳 化 液 » 可 撤 底 穿 入 多 孔 性 建 築 材 料 i 使 其 具 有 良 好 之 表 面 疏 水 性 0 但 緻 密 之 建 築 材 料 僅 表 面 獲 得 保 護 且 歴 時 1 1 短 暫 0 1 I 雖 然 院 基 院 氧 基 矽 院 之 水 乳 液 可 徹 底 穿 入 建 築 材 料 » 1 1 線 1 但 在 儲 存 期 間 則 不 安 定 〇 歐 洲 專 利 EP -A -340 8 16 曾 述 及 烷 基 院 氣 基 矽 院 之 缓 衝 乳 化 液 在 儲 存 期 間 安 定 , 但 (持 別 是 1 I 在 中 性 建 築 材 料 内 ) 沉 澱 速 率 太 慢 9 所 以 防 水 性 差 0 1 1 美 國 專 利 US -A -5 ,091 ,002 中 掲 示 含 有 樹 脂 狀 具 有 1 I 烷 氧 基 之 聚 有 機 矽 氣 烷 及 烷 基 烷 氧 基 矽 烷 作 為 有 效 成 分 之 1 1 乳 化 液 Ο 該 等 乳 化 液 係 儲 存 安 定 性 與 表 面 防 水 作 用 間 之 折 1 I 衷 産 物 〇 1 I 先 前 習 知 之 乳 化 液 9 因 不 3 含 具 有 銨 基 之 聚 有 Utit 饿 砂 氧 院 1 1 1 1 1 1 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) 經濟部中央標率局員工消費合作社印製 44 0 5 9 1 A7 87 五、發明説明(2 ) ,其經稀釋者之儲存安定性較差且其初期對水之耐力不會 令人滿意。 本發明之目的在提供:儲存安定之有機矽化合物水性 乳化液,以形成防水多孔性礦質建築材料及建築塗料;以 及製備防水多孔性礦質建築材料及建築塗料之方法,該方 法尤其對中性及鹽基性建築材料及建築塗料特別有效。 本發明提供一水性乳化液,其中包括下列諸成分: (A) 選自
Ul) Cl - c2(D -烷基-c2 - c6 -烷氣基矽烷及 (A2)含有烷氣基之有機聚矽氧烷, (B) 有機聚矽氣烷,除其他有機矽氣烷單元外更含有矽氣 烷單元(該等矽氣烷單元具有矽磺-鍵結基,該等矽碳 -鍵結基含有鹽基性氮),但該有機聚矽氣烷之胺值至 少為0 . 0 1 ,及 (C )乳化劑。 最好,該等Cl - c2[)-烷基-c2 - c6 -烷氣基矽烷 U1)具有1個或2値相同或不同、未經取代或鹵素-取代, 矽-磺鍵結單價 Ci - C2Q -烷基及其餘諸基傺相同或不同 c2 - C6 -烷氣基。甲氣基矽烷水解速率太快且妨礙足夠 之儲存安定性。
Cl - c2C)-烷基之實例是:甲基、乙基、正-丙基、 異-丙基、正-丁基、異-丁基、第三级-丁基、正-戊基、 異-戊基、新-戊基、第三级-戊基;己基,例如:正-己基; 庚基,例如:正-庚基;辛基,例如:正-辛基及異-辛基, -4 - 本紙張尺度適用中國國家榇隼(CNS > A4規格(210 X 297公釐) 一{請先閣讀背面之注意事項再填寫本頁) 訂 魄 A7 B7 440591 五、發明説明(3 ) -請先閲讀背面之注意事項再填寫本頁) 例如:2,2,4 -三甲基戊基;’壬基,例如:正一壬基;癸基, 例如:正-癸基及十二基,例如:正-十二基;環烷基,例 如:環戊基、環己基、4 -乙基環己基、環庚基、正-IS基及 申基環己基。 鹵素取代之4 - C2()-烷基之實例是:由氟、氣、溴 及碘原子取代之烷基,例如:3,3,3 -三氟正-丙基,2,2,2, 2',2',2_-六氟異丙基及七氟異丙基。 未經取代之4 - C12 -烷基特別合意。 1 C2 - C6 -烷氣基之實例是:乙氣基、正-丙氧基、異 -丙氧基、正-丁氣基、異·丁氣基、第二级-丁氧基、第三 级-丁氣基;戊氧基,例如:正-戊氣基及己氣基,例如: 正-己氣基。其中乙氣基特別合意。 烷氣基可能由鹵原子取代,但並不合意。 該乳化液可能含有一種含有烷氣基之有機聚矽氧烷( A2)或由多種有機聚矽氣烷形成之混合物。有機聚矽氣烷 中可能更含有羥基以輔助對建築材料之黏合作用。 有機聚矽氧烷(A2)之合意黏度最大為2000公厘2 /秒, 如此在實施圬工時可在多孔性表面上形成待佳之分佈。 經濟部中央標準局員工消費合作社印製 最合意之有機聚矽氣烷(A2)係包括具有化學通式(I ) 之單元者
RxSi(OR1)y(〇H)z〇4_x_y_z (工) "~2 其中 -5 - 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) 4 4 05 9 1 A7 B7 五、發明説明(4 ) β 偽相同或不同之單價、·未經取代或經鹵素取代、矽硕 -鍵結之q - C2Q -烴基, -(請先閱讀背面之注意事項再填寫本頁) 是 例 實 之 基 0 有 列 所 上 之如 20 基 烯 乙 代 取-5 素正 鹵 、 及基 基丙 烷烯 之 20 己
基間 苯 、 如鄰 例如 ,例 基., 芳基 ;芳 基烷 0 ; 宿基 正M 基聯 烯、 乙 1例 3 (A,及 院基基 氧烯烷 矽,環 聚基基 機烷烯 對 苯及 及基 基苯 M甲 、二 基 、 萘基 、苯 基甲 苯- 基 烷' 芳C1 ; 之 基代 苯取 乙經 基 ί卞 如 例 苯 及 基 烷 未 中 其 〇 基 乙 苯 一 ο β 意 及合 * -=1 特 基 a 經濟部中央標準局負工消費合作社印製 與 接 直 由 可 基 R 分 〇 部意 ,合 示不 顯並 曾但 未 〇 中代 式取 通子 學原 化氫 述之 上結 然鍵 雖子 原 矽 基 丁 及 基
基, 乙级 、三 基第 甲及 :基 是丁 例-實 之 基 Ti R 第 级 正 基 正戊 - 基正 異例 ', 基基 丙戊 至 4 ο 。為 意值 合均 別平 特意 基合 乙之 以y 中Ιο 其1. ,至 基.9 己10 - 為 正值 :均 如平 例意 , 合 基之 己
X
至 ο ο 為 值 均 平 意 合 之 Z R1 % 相 同或 不同之 t3D 早 價 Cl C6 _院基 t X 係 0、 1、 2或3 , 平 均 為 0 . 8至1 .δ , y % 0, K 2或3, 平 均 為 0 . 01至 2 . 0及 Z 偽 0、 1 > 2或3 , 平 均 為 0 . 0至0 * 5 〇 但 X S y、 及z之 和 至 多 為 3 . 5 〇 在 25 C溫 度下, 有 機 聚 矽 氣烷 U2)之 黏 度 以1 0公厘2 / 秒至 50 ,0 0 0 公 厘2 /秒 為 佳 9 尤 以50 公厘2 / 秒 至 5 , 0 0 0公厘2 /秒更佳。 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) 44059 1 A7 B7 五、發明説明(5 ) 有機聚矽氣烷(A2)之寅例是由甲基三氣矽烷及(假若 需要)一種Ci - C8 -烷基三氣矽烷或(假若需要)苯基三氣 矽烷在水中與乙醇反應所得者,例如:具有下列實驗式之 #機聚矽氣烷: CH3Si (OC2H5)0.8。以或 C6H5Si(0C2H5)〇.72 。 合意有機聚矽氣烷(Β)僳包括具有化學通式(H)之單 元者: R2aR3b(。只4)cSiO^-a—b-c R2 偽相同或不同之單價、未經取代或經齒素取代、砂碳 -鍵結之Ci - C2Q -烴基,其中無鹽基性氪, R3 傷相同或不同之單價、未經取代或經鹵素取代、矽碩 -鍵結之Cl - c3(3 -烴基,其中含有鹽基性氪, R4 可相同或不同,且可能是氫原子或Ci - C6 -烷基·, a 僳 0、1、2或 3, b 你0、1、2或3,平均至少為0.05,及 c 傷 0、 1、2或 3, 經濟部中央標隼局員工消費合作社印製 -(請先閲讀背面之注意事項再填寫本頁) 但a、b及C之和小於或等於3且有機聚矽氣烷(B)之胺值 至少為0 . 0 1。 胺值傷中和1公克有機聚矽氣烷(B)所需1當量濃度 鹽酸之毫升數。有機聚矽氣烷(B)之胺值以至少0.1為佳, 但以至少0.2較佳,且至多8為佳,但以至多4較佳。 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) A7 B7
(I 44 05 9 1 五、發明説明( R2基之實例及合意實例與上述R基者相同。其中特別 合意者是甲基及異辛基。 最好,有一烴基(尤其一甲基)與每個具有鍵結氫原子 乏矽原子鍵結。 R3基最好是一個具有化學通式U )之基 R52NR6· 其中 R5 可相同或不同,且换一値氫原子或一單價,未經取代 或業經取代之Cl - c1Q烴基或一 q - c1G1 -氨基烴基及 R6 係一兩價C i - C15 -烴基。 R5基之實例,除上述R基之烴基實例外,並有氨基取 代之烴基,例如:氨基烷基,其中以氨基乙基恃別合意。 最好,在具有化學通式U)之基内,每個氮原子至少 與一摘氫原子實施鍵結。 R6基最好是一®具有1至10個碩原子(尤其1至4値碩 原子更桂)之兩價烴基,其中以正-伸丙基特別合意。 R6基之實例是:亞甲基、伸乙基、伸丙基、伸丁基、 伸環己基、伸十八基、伸苯基及伸丁烯基。 合意之R3基實例是 H2N(CH2)3-, h2n(ch2)2nh(ch2)2-, h2n(ch2)2nh(ch2)3-, H2N(CH2)2-/ h3cnh(ch2)3-, 本紙浪尺度適用中國國家標準(CNS ) A4規格(2丨0X297公釐) -----------)------訂------气—. -(請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局貞工消費合作社印製 A7 B7 44 059 1 五、發明説明(7 ) C2H5NH(CH2) 3-,
h3cnh(ch2)2”, ' I C2K5NH(CH2)2-, ;; h2n(ch2)4-, q H2N(CH2)5-/ i ΐ hcnhch2ch2)3-/ C4K9NK(CH2)2NH(CH2)2* i 環-CgHiiNH(CH2)3-' i 環-CgHuNHiCHA-, 1 (CH3)2N(CH2)3-, ' (CH3)2N(CH2)2-, (C2H5)2N(CH2)3-及. (C2H5).2N(CH2)2- · 所有烷基R1之實例亦適用於R6基。 R4基之實例及合意實例與上述R1基者相同。其中甲基 及乙基特別合意。 a之平均值以0至2為合意,尤以0至1.8特別合意。 b之平均值以0.1至0.6為合意,尤以0.15至0.30待別 A音 口 芯 〇 c之平均值以0至0.8為合意,尤以0.01至0.6特別合 思0 在2 5 π溫度下,有機聚矽氧烷(Β )之黏度以5至5 0 0 0公 厘2 /秒為佳,尤以1 0 0至3 0 0 0公厘2 /秒更佳。 有機聚矽氣烷(Β)可以習知之方式製備,例如:將具有 氨官能基之矽烷與含有烷氧基及/或羥基且無鹽基性氮之 有機聚矽氧烷實施平衡作用或縮合作用。 本紙浪尺度適用中國國家標準(CNS ) Λ4規格(2! Ο X 297公釐) -(請先閱讀背面之注意事項再填寫本頁) 11Τ 經濟部中央標準局負工消費合作社印製 4 4 059 1 A7 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明 (£ I 1 I 該 等 水 性 乳 化 液 含 有 — 本 身 業 經 習 知 之 乳 化 劑 (C )0 1 1 特 別 適 宜 之 陰 離 子 型 乳 化 劑 是 ; 1 1 . 硫 酸 烷 基 酯 1 特 別 是 鏈 長 為 8 至 1 8 値 碳 原 子 者 > 硫 酸 請 先 ί 1 基 及 烷 芳 基 醚 酯 » 其 疏 水 基 内 具 有 8 至 1 8個 碩 原 子 且 具 聞 讀 背 1 1 有 1 至 4 0锢 環 氣 乙 院 或 環 氣 丙 院 CET 早 元 者 0 面 之 1 注 1 2 . 磺 酸 酯 S 特 別 是 具 有 8 至 1 8値 磺 原 子 之 磺 酸 院 基 酯 , 意 事 1 具 有 8 至 18 値 磺 原 子 之 磺 酸 烷 芳 基 酯 氣 基 乙 磺 酸 酯 % 磺 項 再 1 填 1 酸 基 丁 二 酸 與 早 元 醇 或 具 有 4 至 15値 碩 原 子 之 烷 基 酚 (假 寫 本 ϊ 若 需 要 9 該 等 醇 或 院 基 酚 亦 可 用 1 至 40値 環 氣 乙 院 HtT 早 元 予 頁 1 1 以 乙 氣 化 )所形成之酯或單酯。 1 I 3 . 院 基 Λ 芳 基 % 烷 芳 基 或 芳 烷 基 内 具 有 8 至 20 値 碩 原 子 I I 之 羧 酸 之 鹸 金 屣 鹽 及 銨 鹽 〇 1 訂 1 I 4 . 磷 酸 之 部 分 酯 及 其 鹼 金 屬 及 銨 鹽 9 特 別 是 其 有 機 基 内 具 有 8 至 20個 碩 原 子 之 磷 酸 烷 基 酯 及 院 芳 基 酯 , 其 烷 基 1 ! 或 院 芳 基 内 具 有 8 至 20 痼 磺 原 子 且 具 有 1 至 40 緬 環 氧 乙 院 ί I C3P 元 之 m 酸 烷 基 或 烷 芳 基 醚 酯 〇 1 1 特 別 適 宜 之 非 離 子 型 乳 化 劑 是 : 5 . 聚 乙 烯 醇 9 其 中 仍 含 有 5 至 50¾ (以 8 至 20¾較佳) 之 乙 i I 酸 乙 烯 基 酯 早 元 > 且 其 聚 合 度 為 500至 3000〇 1 1 6 . 烷 基 多 乙 二 醇 醚 > 尤 以 具 有 8 至 4 0個 環 氣 乙 院 αα 早 元 及 1 ί 具 有 8 至 20 個 m 原 子 之 烷 基 者 較 為 合 溶、 〇 \ 1 7 . 院 基 芳 基 多 乙 二 醇 醚 > 尤 以 具 有 8 至 4 0個 環 氧 乙 早 1 1 元 及 烷 基 及 芳 基 内 具 有 8 至 20値 磺 原 子 者 較 為 合 意 0 1 8 . 環 氣 乙 烷 / 環 氣 丙 烷 嵌 段 共 聚 物 尤 以 具 有 8 至 40 個 1 1 1 - 10 - 1 1 1 本紙張尺度適用中國國家標準(CNS ) A4规格(210 X 297公釐) 440591 A7 B7 經濟部中央標準局員工消費合作社印製 五、 發明説明 (ί 1 1 I 璟 氧 乙 院 或 環 氣 丙 烷 (3d 早 元 者 較 為 合 思 0 1 1 9 . 具 有 8 至 22個 磺 原 子 之 烷 基 之 烷 胺 與 環 氣 乙 烷 或 環 氣 二 i I 丙 烷 實 施 加 成 作 用 之 生 成 物 0 請 先 1 1 鬩 I 10 爭 具 有 6 至 24個 碳 原 子 之 脂 肪 酸 0 讀 背 1 I 1 1 . 具 有 化 學 通 式 R %u π _ •0- 1 之 院 基 高 聚 醏 > 其 中 % —- 面 之 ί 注 [ 直 線 型 或 分 枝 型 飽 和 或 不 飽 和 具 有 平 均 8 至 24個 碳 原 意 事 1 子 之 烷 基 » 且 Z 傜 一 低 聚 甘 基 3 其 中 具 有 平 均 0 = 1 至 10 項 再 1 I 個 己 醋 或 戊 醣 DD 早 元 或 其 混 合 物 〇 寫 本 ) I 12 天 然 材 料 及 其 衍 生 物 J 例 如 卵 磷 脂 羊 毛 脂 皂 素 頁 1 I > m 維 素 , 其 毎 個 烷 基 具 有 高 達 4 値 碳 原 子 之 m 維 素 院 基 [ I 醚 及 羧 基 烷 基 缕 維 素 〇 1 1 13 - 含 有 極 性 基 之 直 線 塑 有 概 (聚) 矽 氧 烷 ί 特 別 是 含 有 具 i 訂 有 高 達 24個 碩 原 子 之 烷 氣 基 及 / 或 髙 達 40 個 環 氧 乙 院 及 / 1 I 或 環 氣 丙 院 基 者 0 1 i 特 別 適 宜 之 陽 離 子 型 乳 化 劑 是 1 I 14 • 具 有 8 至 24個 磺 原 子 之 第 一 级 、 第 二 级 及 第 三 级 脂 肪 1 胺 與 乙 酸 硫 酸 鹽 酸 及 磷 酸 所 形 成 之 鹽 類 〇 15 * 第 四 级 院 基 銨 鹽 及 院 基 苯 銨 鹽 , 持 別 是 其 烷 基 具 有 6 1 I 至 24個 磺 原 子 者 1 尤 其 該 等 鹵 化 物 硫 酸 鹽 m 酸 鹽 及 乙 1 1 酸 鹽 〇 1 1 16 * 院 基 毗 錠 鹽 院 基 眯 唑 銳 鹽 及 烷 基 Q咢 唑 m 鹽 ) 尤 其 其 1 r 烷 基 具 有 高 逹 1 8悃 m 原 子 者 * 持 別 是 該 等 化 物 硫 酸 鹽 [ 1 % m 酸 鹽 及 乙 酸 鹽 0 1 1 待 別 適 宜 之 兩 性 型 乳 化 劑 是 1 1 1 - 11 1 1 1 本纸張尺度適用中國國家標準(CNS ) A4現格(210X2?7公釐〉 440591 A7 經濟部中央標準局負工消費合作社印製 五 *發明説明 (1〇 ) 1 1 I 1Ί r 長 鍵 經 取 代 之 氨 基 酸. 9 例如 Ν - 烷 基 -二( 氨 基 乙 基) 1 1 I 甘 胺 酸 或 H- 院 基 -2 -氨基丙酸鹽。 1 | 18 . 内 鹽 9 例 如 具 有 一 c8 - C18 ~醒基之N -( 3- 醯 基 ·*. tv Μ 胺 請 ▲ 1 i 基 丙 基 )- N , Η - 一 甲 基 銨 鹽 及 院 基眯 唑 耕 内 鹽 〇 閲 讀 1 背 1 合 意 之 乳 化 劑 傺 非 離 子 型 乳化 劑 9 特 別 是 上 述 第 9 項 之 1 述 第 注 1 内 烷 胺 與 環 氣 乙 烷 或 環 氣 丙 烷 之加 成 生 成 物 , 上 1 1項 意 事 1 内 之 烷 基 高 聚 簾 +·+ 甘 及 上 述 第 5 項内 之 聚 乙 烯 醇 〇 持 別 a 意 項 再 1 1 之 聚 乙 烯 醇 仍 含 有 5 至 20¾ (以 1 0至 15¾更佳) 之 乙 酸 乙 烯 酯 寫 本 1 } αα 早 元 , 且 其 聚 合 度 以 50 0 至 3 0 0 0 為 佳 1 尤 以 1200 至 2 0 00 更 頁 1 1 佳 0 1 I 水 性 乳 化 液 内 成 分 (A)及(B)之 總 量 以 1 至 80¾ 重 量 bb 為 1 i 佳 , 以 10 至 7 5 3;重置比較佳, 尤以30至70¾ 重 量 bb 最 佳 0 1 訂 1 成 分 (C )佔成分(A ) 及 (B )總量之比例以0 .1 至 30 % 重 里 fcb 為 佳 1 尤 以 佔 2 至 1 〇 a;重量比更佳。 1 1 該 等 乳 化 液 更 可 含 有 常 用 之填 料 及 增 稠 劑 * 尤 其 增 強 1 I 性 填 料 » 亦 即 其 BET 低 溫 W* 吸 附法 測 定 之 表 面 積 大 於 50平 1 1 方 公 尺 /公克之填料, 例如: 熱解矽石, 沉澱矽石及BET 表 線 ' 面 積 大 矽 -鋁混合氣化物。 細粉狀矽石特別適宜。 可能 ί 僅 使 用 一 種 填 料 或 使 用 至 少 兩 種填 料 之 混 合 物 〇 填 料 佔 成 1 1 分 (A)及(B ) 總 量 之 bb 例 至 多 為 5¾重 量 fcb 9 但 以 2¾ 重 量 比 為 I 1 佳 0 1 1 該 等 乳 化 液 内 亦 可 含 有 缓 衝物 質 藉 以 穩 定 酸 驗 度 在 5 I ! 至 8 之 間 t 在 該 範 圍 内 院 基 三 院氧 矽 院 對 水 解 作 用 之 抗 力 E i 甚 強 〇 適 世 之 緩 衝 物 質 均 偽 有 機及 •fitr Μ 機 酸 及 鹽 基 (其 對 乳 1 1 I - 12 ] 1 1 本纸浪尺度適用中國國家標準(CNS ) A4規格(21 OX 297公釐) 44059 1 A7 B7 經濟部中央標準局負工消費合作社印製 五、 發明説明(] 0 | 化 液 之 其 他 組 成 分 不 起 化 學 反 脾 ,/U·、 ) 9 尤 其 羧 酸 酸 \ 碩 1 1 I 酸 及 硫 酸 等 之 鹼 金 屬 鹼 土 金 屬 及 銨 之 鹽 類 〇 其 中 特 別 合 — ! Τ =tV, 思 者 係 磺 酸 鈉 酸 氮 鈉 磷 酸 氫 鈉 及 一 乙 酸 與 氨 水 溶 液 請 1 1 混 合 物 〇 緩 衝 物 質 使 用 量 佔 成 分 (A)及(B)總 量 之 bh 例 以 鬩 讀 背 1 1 至 多 3¾重 量 bb 為 佳 I 尤 以 1尤重 量 比 更 佳 〇 之 1 除 上 述 紐 成 分 外 > 該 等 乳 化 劑 可 更 含 有 殺 真 菌 劑 注 意 1 1 殺 細 菌 劑 除 藻 劑 、 殺 徹 生 物 劑 香 料 腐 蝕 抑 制 劑 及 防 項 再 1 泡 沫 劑 作 為 添 加 劑 〇 添 加 劑 使 用 量 佔 成 分 (A)及(B)總 量 之 寫 1 ί bh 例 以 至 多 2¾重 量 比 為 佳 尤 以 0 . 5¾重 里 比 更 佳 〇 頁 1 | 本 發 明 水 性 乳 化 劑 傜 藉 製 備 水 性 乳 化 劑 之 習 用 方 法 製 1 I 得 0 合 意 之 方 式 是 :開始時先將部分之水與乳化劑(C )加以 1 1 混 合 , 再 將 成 分 (B)及最後成分(A)予以 乳 化 f 直 至 一 黏 著 i 訂 1 油 相 形 成 隨 後 將 其 餘 之 水 乳 化 進 去 * 以 形 成 一 低 黏 箸 乳 化 液 〇 另 外 亦 可 能 先 將 成 分 (A )及(Β )加以 混 合 » 再 將 其 加 1 ! 入 乳 化 劑 與 水 之 乳 化 液 内 0 混 合 工 作 最 好 在 壓 力 乳 化 機 > 1 I 膠 體 粉 碎 機 或 尤 其 威 廉 斯 教 授 所 述 之 高 速 靜 子 -轉子攪拌 1 1 裝 置 内 實 施 〇 本 發 明 亦 提 供 Η~- 製 造 防 水 多 孔 性 礦 質 建 築 材 料 及 建 築 1 1 塗 料 之 方 法 * 其 中 包 括 使 用 上 述 水 性 乳 化 液 以 處 理 建 築 材 [ 1 料 及 建 築 塗 料 1 | 本 發 明 亦 提 供 一 製 造 可 形 成 多 孔 性 礦 質 建 築 塗 料 之 防 1 1 水 塗 料 組 成 物 之 方 法 » 其 中 包 括 將 塗 料 組 成 物 與 上 述 水 性 1 | 乳 化 液 加 以 混 合 之 工 作 〇 i 該 等 乳 化 液 Μ 用 於 防 水 礦 質 建 築 材 料 , 例 如 : 天 然 或 1 1 | - 13 * 1 1 1 本紙張尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) 44 05 9 '1 A7 B7 經濟部中央標準局負工消費合作社印製
五、 發明説明(] ί2) I I | 人 造 石 材 > 混 凝 土 水 泥 石 灰 -i 少石磚及多孔性混凝土, I I 坭 土 礦 質 建 築 材 料 例 如 : 磚 ♦ 作 為 對 石 苷 塗 泥 具 有 防 A I I 水 及 (假若需要)黏箸作 用 之 添 加 物 用 於 建 築 塗 料 * 例 如 請 先 I I 礦 質 油 漆 聚 矽 氧 樹 脂 乳 化 油 漆 及 塗 泥 、 矽 酸 鹽 分 散 油 閱 讀 背 I I 漆 、 乳 化 液 油 漆 \ 槙 充 塗 料 增 強 組 成 物 及 底 漆 0 尤 其 在 面 之 I 作 建 築 塗 料 組 成 物 之 案 例 中 9 先 期 耐 雨 強 度 獲 得 改 進 0 >王 意 事 I ! 該 等 乳 化 液 亦 適 用 於 防 水 細 粉 狀 無 機 材 料 * 例 如 珠 項 再 I I 岩 > 蛭 石 及 熱 雄 緣 材 料 0 俱 寫 本 I } 該 等 乳 化 液 特 別 適 用 於 防 水 礦 質 黏 合 (尤 以 水 泥 黏 合 頁 \ I 者 更 佳 ) 之 m 維 型 建 築 材 料 t 該 等 缴 維 包 括 天 然 m 維 或 合 I | 成 m 維 〇 適 當 之 天 然 m 維 曰 疋 礦 質 m 維 i 例 如 LXJ 石 绒 Λ 石 英. I 或 陶 瓷 m 維 或 植 物 m 維 , 例 如 m 維 素 〇 舉 例 言 之 , 適 當 I 訂 之 合 成 缕 雄 是 玻 璃 m 維 \ 聚 合 物 m 維 及 碳 m 維 〇 將 乳 化 液 I I 使 用 於 防 水 水 泥 黏 合 纖 維 素 m 維 既 分 待 別 合 意 0 舉 例 m 之 I I 7 該 等 m 維 素 m 维 可 能 是 黃 麻 椰 子 或 大 麻 之 維 或 來 白 I I 紙 張 硬 紙 板 或 廢 紙 之 m 雄 0 I I 該 等 乳 化 液 適 宜 以 散 體 形 式 使 甩 > 亦 即 將 乳 化 液 添 峻 \ 加 於 — 水 硬 之 混 合 物 S 以 便 於 凝 固 前 以 産 生 成 分 » 或 於 凝 \ I 固 後 使 成 分 能 夠 防 水 〇 I I 在 其 用 作 防 水 劑 及 (假若需要)黏合劑 之 前 本 發 明 之 I I 乳 化 液 可 用 水 加 以 稀 釋 0 將 成 分 (A)及(B)之 總 含 量 稀 釋 至 I i U重 量 比 對 凝 固 後 建 築 材 料 之 表 面 浸 漬 有 利 〇 I I 除 另 有 表 示 外 t 在 下 列 諸 實 驗 例 中 1 所 有 份 數 及 百 分 I | 數 均 為 重 量 比 0 除 另 有 表 示 外 下 列 諸 實 驗 例 均 偽 在 環 I I I — 14 - I I I 本紙張尺度適用中國國家標準(CNS > A4規格(210X 297公釐) 經濟部中央標準局員工消費合作社印製 440591 A7 B7 五、發明説明(13) 境大氣壓力(亦邸約0·10百萬帕斯卡)、室溫(亦即約20t!) 或無需加熱或冷卻,在室溫下將反應物集結在一起所産生 之溫度下實施。下列諸實驗例中所提及之黏度均慑指在溫 k25O之情況下所呈現者。該等乳化劑之固體含量乃除水 外所有水分之總和。 實驗例 所用成分(A)偽: H1:異-辛基三乙氧矽烷 H2:具有實驗式 CH3Si (0C2 H5 )0,8 Ου之有機聚矽氣烷. 其平均分子量約為6 5 0公克/莫耳,黏度約為2 0公厘2 / 秒。 H3:高黏度液體甲基聚矽氧樹脂,其中包括 CH3Si 03/2單 元,約20%莫耳比之(〇3)23丨02/2單元及約10%莫耳比 之 C2H5Si03/g單元,其分子量約為5 00 0公克/莫耳。 H4:粉狀甲基聚矽氧樹脂,其中包括CH3Si 03/2單元,約3¾ 莫耳比之(CH3 )2 S〖〇2/2單元及約4¾莫耳比之C2 H5 S i 03/2 單元,其分子童約為5000公克/莫耳及軟化點約為50 t: 0 所用分子(B)係: N1:在有氣氧化鉀存在之情況下,α,ω-二羥基甲基聚矽 氣烷(其每齒終端單元具有一矽-鍵結羥基)與Ν(-2-氨 基乙基)-3 -氨基丙基三甲氣基矽烷之縮合生成物,其 胺值約為0.3,在溫度25T時之黏度約為1500公厘2/ 秒,殘留甲氣基含量低於5¾莫耳比(以初始存在於N( -15 - 本紙張尺度適用中國國家榡準(CNS ) A4規格(210X 297公嫠) -----------)----—-Iΐτ------ Α請先½讀背面之注意事項再填窝本頁) Α7 Γ 44 05 9 1 Β7 五、發明説明(14 ) -2 -氨基乙基)-3 -氛基丙基三甲氣基矽烷中之甲氣基 為基準)。 *(請先閑讀背面之注意事項再填寫本頁〕 N2:類似於N1之縮合生成物,但其胺值約為0.6,其在溫 度25它時之黏度約為2000公厘2 /秒。 N3:在有氫氧化鉀存在之情況下,H2與N(-2 -氨基乙基)-3 -氨基丙基三甲氧基矽烷之縮合生成物,其胺值約為 3.0,其在溫度251畤之黏度約為500公厘2 /秒,殘留 甲氣基含量低於5%莫耳比(以初始存在於N(-2 -氨基乙 基)-3-氨基丙基三甲氣基矽烷中之甲氣基為基準。 所用成分(C)偽: E1:傑納敏200,荷西斯特公司出品,法蘭克福,偽硬脂胺 與環氣乙烷反應之生成物。 E2:格魯科旁225,漢克爾公司出品,杜塞道夫,一脂肪醇 c8 - c1C)醏苷水溶液。 E3:多烯醇W 25/140,瓦克化學公司,慕尼黑,僳一聚乙 烯醇,其聚合度約為1600且仍含有11至14¾之乙醯氧 伸乙烷單元。 本發明乳化液之製備: 經濟部中央標準局員工消费合作杜印製 本發明水性乳化液之製備程序是:首先將部分水與乳 化割加以混合並乳化氨官能基聚矽氣烷,其次為矽烷及/ 或聚矽氣樹脂。首先述及之混合工作及乳化作用僳在威廉 斯教授所述之快速靜子-轉子攪拌器内實施。該等組成物 如下列表I中所示。
表I -16 - 本纸浪尺度適用中國國家樣準(CNS ) Λ4規格(210X297公釐) 經濟部令央標準局員工消費合作社印製 4405 9 1 A7 B7 五、發明説明(15 ) 乳化液 矽烷或聚 矽氣樹脂 [S;重量比] 氨基聚 矽氣烷 [3:重量比] 乳化劑 [%重量比] 水 [%重量比] 固體含量 [%重量比] EM 1 Η 1/66.5 A 1/3.5 E 1/0.7 29.3 70.7 EH 2 Η 1/34 A 2/34 E 1/2 30 70 EM 3 Η 1/3.5 A 1/66.5 E 1/4 26 74 EH 4 Η 2/43 A 1/28 E 1/2.9 26.1 73.9 EH 5 Η 2/61.2 A 1/6.8 E 1/2 30 70 EM 6 Η 3/23 A 3/23 £ 2/2 + E 3/2 50 50 EM 7 Η 1/32.4+ Η 4/8.1 A 2/4.5 E 1/1.3+ E 2/3.7 50 50 EH 8 Η 1/54 A 1/6 E 1/0.5+ E 2/2.7 36.8 63.2 EM 9 Η 1/6 A 1/54 E 1/1 + E 2/3 36 64 EM 10 Ή 2/6,8 A 1/61.2 E 2/2. E 3/1 29 71 (請先閲讀背面之注意事項再填寫本頁) 訂 -17-本紙張尺度適用中國國家揉準(CNS ) A4規格(210 X 297公釐) A7 B7 五、發明説明() 在50¾溫度下儲存14天之後,乳化液EM1至EM10均無 丰目分離現象,另在室溫下儲存6個月之後同樣無相分離現 象。所以該等乳化液儲存安定。 ' 值得注意之一點是:當乳化液EM1至EM10之稀釋品( 具有約1至10¾有效含量)塗被在礦質表面時,水之結珠效 應甚佳。經處理過之表面,測得之接觸角大於90° 。 非本發明乳化液之裝製: 非本發明乳化液之製備方法與本發明乳化液者相似。 該等紐成物如下列表I所示。
表I 乳化液 矽烷或聚 氨基聚 乳化劑 水 固體含量 矽氣樹脂 矽氣烷 重量比] [3;重量比] [3!重量比] U重量比] [X重童比] CE 1 Η 1/60 - E 1/0.5+ 36.8 63.2 E 2/2.7 CE 2 異-辛基甲氣 - E 1/0.5+ 36.8 63.2 基矽烷/60 E 2/2.7 CE 3 異-辛基甲氧 A 1/6 E 1/0.5+ 36.8 63.2 基矽烷/54 E 2/2.7 經濟部中央標準局—工消費合作社印製 i(請先闊讀背面之注意事項再填寫本頁) 實驗例1 :用於多孔性礦質建築材料之防水組成物 "18 本紙張尺度適用中國國家標準(CMS )八4規格(210X297公釐) Α4〇δ91 Α7 經濟部中央標準局員工消費合作社印製 Β7五、發明説明(17) 用水將本發明乳化液及非本發明乳化液稀釋至如下列 表Μ所示之固體含量。 在用於多孔性礦質建築材料之前,在50Τ:溫度下,將 永發明乳化液及非本發明乳化液儲存1 4天並用目視加以評 估。下列表Μ内所示符號代表之意義為: + + + :無明顯變化 + + :輕微凝聚(凝稠),經搖動則可逆 + :強烈凝聚(凝稠),經搖動則可逆 ~ :由於聚結作用産生不可逆之相分離。 在室溫下將該等乳化液儲存6掴月導致同樣變化。 用刷子將該等乳化液塗被在塗有礦質油漆(矽酸鹽油 漆「結晶」,凱慕法班公司,迪道夫)之石灰-砂石磚上。 在室溫下儲存14天之後,將經塗裨及防水處理之石灰-砂 石磚之變色程度加以評估,並藉量測接觸角以評估滴在上 面之水之結珠效應。接觸角大於90°表示結珠效應佳,接 觸角小於90°表示結珠效應差。所得結果如下列表3R所示。 將固化之混凝土試驗試樣浸入乳化液歴時1分鐘。在 室溫下儲存14天之後,試樣破裂。表面上疏水區之厚度表 示貫穿深度。混凝土之水分吸收量隨貫穿深度而下降,同 時混凝土之疏水性則增強。所得結果如下列表Μ所示。 用刷子將該等乳化液塗被在石灰-砂石磚上。在室溫 下儲存14天之後,依照德國工業標準52167量剷水分吸收 葆數以評估水分吸收量。I#之值小於0.1公斤/公尺2 X 秒1/2表示水分吸收童極低。 -1 9 - -(請先閲讀背面之注意事項再填寫本頁) 訂 -气 本紙張尺度適用中國國家標準(CNS > Α4規格(210 X 297公釐) 4.4 05 9 1 A7 B7 五、發明説明(is) 表瓜 經濟部中央標準局員工消費合作社印製 别浓/ 孔1G肢/ |固體含量 儲存安定性 變色程度 結珠效應 貫穿深度 w值 /接觸角 公斤/公尺2x秒1/2 EH 1, 70.7 +++ 無 甚佳/120° 7公厘 EH 1, 20 + + + 甚佳/140° 4公厘 0.053公斤/公尺2x秒V2 EM 8, 63.2 + + + 無 甚佳/110° 6公厘 EM 8, 50 +++ 無 甚佳/110° 6公厘 EH 8, 20 ++ + 無 甚佳/115° 4公厘 0.060公斤/公尺2x ?#/2 EH 8, 10 +++ Jhrt m 甚佳/128° 2公厘 EH 8, 5 +十+ 無 甚佳/140° 1公厘 CE 1, 63.2 + + 無 無/0° 6公厘 CE 1, 20 - 無 無/0° 4公厘 0.23公斤/公尺2χί#/2 CE 2, 63.2 + 強烈 無/50° < 1公厘 CE 2, 20 - 輕撤 無/60° < 1公厘 0.38公斤/公尺2χ ?#/2 CE 3, 63.2 + 強烈 甚佳/110° < 1公厘 CE 3, 20 + 輕徹 甚佳/120° < 1公厘 0.35公斤/公尺2X秒1/2 實驗例2 :礦質建 築材料 上礦質塗 料所用 之防水性底漆 將稀釋至固體含量為10¾重量比之乳化液EM2塗被在石 灰-砂石磚上,其.使用量為400公克/平方公尺。在室溫下 -20- 本紙乐尺度適用中國國家標準(CNS ) A4規格(2t〇X297公釐) (請先鬩讀背面之注意事項再填寫本頁)
-IT 440591 A7 B7 五、發明説明(19 儲存14天之後,用類似於實驗例1之方法,量測經防水處 理之石灰-纱石磚之下列諸性能: 結珠效應: 甚佳 接觸角 : 130° 貫穿深度: 3公厘 w值 : 0 . 07 3公斤/公尺2 X秒1/2
Sd值 : 0.02公尺 該S d值係依照德國工業標準5 2 6 1 5量測者,S d值小於 0.1公尺表示水蒸氣之穿透性高,Sd值大於0.1公尺表示水 蒸氣之不穿透性降低。 經儲存14天之石灰-砂石磚,依照德國工業標準1 8 3 6 3 塗以聚氣樹脂乳化液油漆(有機樹脂之含量不超過有機聚 矽氣烷之含量)。之後依照國際標準組織4624測定塗層之 黏著拉力強度為2.8牛頓/公厘2。若不用10¾濃度之乳化液 E M2施以防水底漆處理,經測得石灰-砂石磚上聚矽氧樹脂 油漆之黏著拉力強度僅為1.5牛頓/公厘2。 經濟部中央標準局員工消費合作杜印製 經稀釋達固體含量為10¾重童比之乳化液EM7,在50Ό 溫度下儲存14天之後,並無顯著變化。隨後用刷子將該稀 釋之乳化液塗被在塗有2公厘厚易碎石灰-水泥塗泥之纖維 水泥上,並於室溫下儲存14天。 經測得未經處理之石灰-水泥塗泥之w值為1 . 3公斤/公 尺 人請先閱讀背面之注意事項再填寫本頁)
2 X秒W 經如此施以防水處理之石灰-水泥塗泥,其性能如下: 結珠效應: 甚佳 -21 - 本紙張尺度適用中國國家標準(CNS > A4規格(2!0X297公釐) 440591 A7 B7 五、發明説明(2 0 ) 接觸角 : 1253 貫穿溁度: 2公厘 W值 : 0 . 0 68公斤/公尺2 X秒1/2 * 塗被10¾濃度之EM7之後,石灰-水泥塗泥之表面強度 獲致顯著改進。 ^ 經如此處理過之底材可塗以如實驗例3之聚矽氣樹脂 乳化液油漆。經用Q-UV快速耐候試驗1000小時之後,所有 如此塗被之配製品均未發生塗層剝落或任何變色現象,但 仍保持甚佳之結珠效應。 實驗例3 :用於水性房屋油漆及塗泥之防水黏合劑 Η將依照德國工業標準18363製備之聚矽氧樹脂乳化 液油漆及聚矽氧樹脂塗泥加以檢査。該等塗料組成物僳屬 於一個組群,在該組群中,有機樹脂之含量不超過有機聚 矽氣烷之含量。 於塗被後,傳統之聚矽氣樹脂油漆及塗泥起初在一段 時間内(「洗脫期j )仍具有一相對高之水分趿收容童且此 正可限制對耐候性(例如:雨水)之初始抗力。 經濟部中央標隼局員工消費合作杜印製 <請先鬩讀背面之注意事項再填寫本頁) 經由下列示範可發現:本發明乳化液如何賦予屋外油 漆以先期雨水抗力。 乳化液油漆製備工作之實施僳使用一高速混合器。首 先將配方所需之水分置入混合容器内。添加顔料助濕劑。 繼而添加填料及顔料並予以預行分散,歴時約5分鐘。當 顔料及填料黏聚物業經碎裂之後,將防水乳化液攪入並與 整個混合物加以分散,歴時再5分鐘。最後一步,添加一 -22 - 本紙張尺度適用中國國家橾準(CNS ) Α4規格(210 X 297公釐) A7 \ 44·05 9 1 B7 五、發明説明(21) 聚合物乳化液並攪拌1分Μ直至均勻地分散。隨後利用一 增稠劑將如此製得之乳化液油漆調整至加工稠度。 配方 210.7份重量比之水 8.4份重量比之多磷酸鈉溶液(10¾濃度之水溶液) 1.4份重量比之顔料助濕劑(以聚丙烯酸為基準) 70.2份重量比之滑石(粒徑20撤米) 70. 2份重量比之沉澱碩酸鈣(平均粒徑0.3徹米) 140. 4份重量比之磺酸鈣(方斛石型填料,平均粒徑5微 米) 140. 4份重量比之碩酸鈣(方斛石型瑱料,平均粒徑15徹 米) 140.4份重量比之二氣化鈦,金紅石型 140. 4份重童比之防水乳化液 56.2份重量比之苯乙烯/丙稀酸酯乳化液f 50%濃度水 溶液(聚合物乳化液) 21.3份重童比之増稠劑(羥基乙基纖維素,2.5¾濃度水 溶液) 1000.0份重量比 試驗 將依照上述方法及上述配方製得之房屋油漆加以檢査 ,以測定其水分吸牧量。在此試驗中,建築材料之吸收作 用或建築材料/塗料複合条統之吸收作用將加以童測。毛 -23 - 本紙乐尺度適用中國國家標準(CNS ) A4規格(210X 297公釐) -請先閱讀背面之注意事項再填寫本頁)
'1T 經濟部中央標準局員工消費合作社印製 44059 1 A7 B7 經濟部中央標隼局員工消费合作社印製 五、發明説明(22 ) 細水分吸收量之童測方法曾在德國工業標準52617中述及。 此處所用方法之實施乃依照上述程序之簡短試驗。所用油 漆底材僳石灰-砂石磚盤(115 X 70 X 20公厘,表面積為 0.008平方公尺)。為塗被油漆底材,將6.5公克倒在表面 上作為第一層塗層,並用一扁平刷子將其均勻攤開,同時 各側面亦加以塗被。經過2 4小時一段時間後,再塗被第二 層塗層。油漆使用量為4.5公克。經塗被之試驗試樣,首 先在室溫下儲存2 4小時,隨後在5 0 1C溫度下儲存2 4小時。 為作進一步之調理,在室溫下再儲存24小時。 將如此製得之試驗試樣置入盤碟中,該等盤碟均襯有 泡沫塑料且以適當之方式充以水,因而經塗漆之表面始終 與飽含水分之泡沫塑料表面有所接觸。隨時間變化(在2、 6及24小時之後)量測增加之重量並與未經處理之試驗試樣 作一比較。 參考註釋 依照所述試驗方法將未經處理之試驗試樣施以水中儲 存 鍺存時間[小時] 水分吸收量[公斤/公尺2 ] 2 2.98 6 3.01 2 4 3.1 本發明房屋油漆 在上述配方中,本發明之乳化液ΕΜ4、ΕΜ5或ΕΜ6,未 經稀釋,傺用作防水乳化液,其使用量如配方中所示。水 -2 4 - 本紙張尺度適用中國國家標準(CNS Μ4規格(2丨Ο X 297公釐) -請先鬩讀背面之注意事項再填寫本頁) 訂 " 五、發明説明(23: A7 B7
分吸收量之測試結果如表IV所示: 表IV 声時間(小時) 水分吸 收量[公斤 /公尺2 ] ΕΜ4 ΕΗ5 ΕΗ6 2 0.15 0.10 0.20 6 0.25 0.20 0.35 24 0.33 0.33 0.45 非本發明房屋油漆 製備一種依照該配方之油漆:不使用防水乳化液,首 先將一聚矽氣樹脂[其平均組成為(ch3 )U2 S i (o)li38 (oh)〇<m ,其黏度經添加4 5份重量比之溶劑石腦油而調整為2 Ο 5 Ο毫 帕斯卡•秒(23Τ)]分散於水中,再使用8.4份重量比之聚 環氣乙烷-烷胺作為乳化劑予以乳化。隨後將無機組成分 等加以分散。 水分吸收量[公斤/公尺2 ] 0.40 2.90 3.10 。經過該第二次儲存,其 •(請先閱讀背面之注意事項再填寫本頁) 訂 經濟部中央標率局員工消費合作社印製 儲存時間[小時] 2 6 24 隨後將該試樣再儲存在水中 量測結果如下: 儲存時間[小時] 水分吸收量[公斤/公尺2 2 6 24 0.10 0.25 0.50 25 - 本紙張尺度適用中國國家標準(CNS ) Α4規格(210 X 297公釐) " AV- A7 440591 B7 五、發明説明(24 ) 實驗例4 :用於水性高填料房屋油漆及塗泥之防水添加物 此處所看到之材料係髙镇料、低黏合劑、毛細水分吸 收童髙之房屋油漆,例如:矽酸鹽分散液油漆及塗泥、以 芬散液為主之髙填料塗料、石灰分散液油漆、填料油漆及 增強組成物、礦質油漆、礦質塗泥、石灰油漆等。塗料中 顔料之體積濃度通常超過50S:。藉實驗例3内所述簡短試 驗法測定,於24小時之後,上述塗料組成物之水分吸收里 通常至少為3公斤/公尺2。 於下列表V所示塗料組成物内,添加僅U重量比之本 發明未稀釋乳化液作為防水添加劑,可急劇減低毛細水吸 牧量。水分吸收量係依照德國工業標準5261?對石灰-砂石 磚作簡短試驗而測定者。
表V Λ讀先簡讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製 塗料組成物 水分吸收量[公斤/公尺2] 1¾重量比之添加童 矽酸鹽分散液油漆 6.4 - 0,28 EM 3 消石灰塗泥 7.4 - 0.35 EM 9 填料乳化液油漆 3.4 (顔料體積濃度=70) 0.62 EM 10 -26- 本紙張尺度適用中國國家標準(CNS ) Α4規格(210X 297公釐)
Claims (1)
- 經濟部智慧財產局員Η消費合作社印製 1· 一種製借多孔性礦質建築塗料用塗料組成物,選自礦 質油漆、聚矽氧樹脂乳化油漆及塗泥、矽酸鹽分散油漆、 乳化油漆、填料塗料、加強組成物及含有水性乳化液之底 漆,包括 ⑷選自 (Al) Cr c2(r烷基-C2- (V烷氧基矽烷及 (A2)含有烷氧基之有機聚矽氧烷, (B) 有機聚矽氧烷,除其他有機矽氧烷單元外更含有矽氧 烷單元(該等矽氧烷單元具有矽碳-鍵結基,該等矽碳-鍵結基含有鹽基性氮>,但該有機聚矽氧烷之胺值至少 為0·〇1,及 (C) 乳化劑。 2·如申請專利範圍第1項之塗料組成物,其中Cr C20-烷基-C2-C6烷氧基矽烷(Al>具有1個或2個相同或不同, 未經取代或經鹵素取代、矽碳-鍵結之單價CVCm--烷基, 其餘之基係相同或不同之C2-C6-烷氧基。 3·如申請專利範園第1項之塗料组成物,其中有機聚矽 氧烷(A2)係由具有化學通式(I)之單元所組成 R^Si (OR1)y(0H^ z°4-x-y~z ⑴ 2 其中 R 係相同或不同之單價、未經取代或經鹵素取代、矽碳 -鍵結之CV c2。-烴基, 27 ^--_------------------訂------- !線 I'— (請先閱讀背面之注意事項再ii;本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 440591 I _____ D8 ____ 六、申請專利範圍 Rl係相同或不同之單價CrCV烷基, x 係〇、1、2或3,平均為0.8至1.8, y 係〇、1、2或3,平均為0·01至2·0及 ζ 係〇、1、2或3,平均為0·0至0.5。 但X、y、及Ζ之和至多為3.5。 4.如申請專利範圍第1項之塗料組成物,其中有機聚矽 氧烷(B)係由具有化學通式(π)之單元所組成 R2 匕(〇r4 ) iO 4 — a-b-C 7 2 (H) R2係相同或不同之單償、未經取代或經鹵素取代、矽碳 3 _鍵結之CrC^-烴基,其中無鹽基性氮, R3係相同或不同之單價、未經取代或經_素取代、矽碳 -鍵結之cv <:2〇-烴基,其中含有鹽基性氮, R4可相同或不同’且可能是氣原子或ei_C6_烷基, a 係 〇、1、2 或 3, b係0、1、2或3,平均至少為〇.os,及 c 係 〇、1、2 或 3, 但a、b及c之和小於或等於3且有機聚矽氧烷(B)之胺 值至少為0.01。 5·如申請專利範圍第4項之塗料組成物,其中R3基係一 具有化學通式(皿)之基 R52NRe- (瓜) __ 28 本紙張尺度適用中國國家標準(CNS)A4 ^格(210 ---- (請先閱讀背面之注意事項再垆.·.本頁) I. -線_ 經濟部智慧財產局員工消費合作社印製 f 440591 A8 B8 C8 D8 經濟部智慧財產局員工消費合作社印製 六、申請專利範圍 其中 R5可相同或不同,且係一個氫原子或一單價,未經取代 或業經取代之cv c1(r烴基或一 c1(r氨基烴基 及 R6係一兩價Cls-烴基。 6. 如申請專利範圍第1項之塗料組成物,其中有機聚砍 氧烷(B)在25°C時之點度為5至5〇〇〇公厘V秒》 7. 如申請專利範圍第1項之塗料組成物,其十乳化劑(c) 係選自: 聚乙稀醇(該等聚乙稀醇仍含有5至50%之乙酸乙烯基_ 單元),且其聚合度為500至3000 , 具有8至22個礙原子之烷基之烷胺與環氧乙烷或環氧丙 炫實施加成作用之生成物及 具有化學通式R*-0-Ze之烷基高聚醣苷,其中r*係一直 線型或分枝型、飽和或不飽和、具有平均8至24個碳原子 之烷基,且Z係一低聚醣苷基,其中具有平均〇=1至1〇 個己醣或戊糖單元或其混合物。 8·如申請專利範圍第1項之塗料組成物,其中乳化劑(c) 之比例佔成分(A)及(B)總量之〇_1至30%重量比。 9. 一種對塗料組成物實施防水處理以製備多孔性礦質建 築塗料之方法,其t包括塗料組成物與如申請專利範圍第 1、2、3、4、5、6、7或8項之水性乳化液之混合作用。 29 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) -.It n η-----------------訂----— I!線 1' (請先閱讀背面之注意事項再产^本頁} S貧s iffifff審 公告本j 申請曰期 案 號 8 5 1 0 2 2/6 0 類 別 (以上各櫊由本局填註) /vr A4 C4 44C591 黍1專利説明書 發明 -、S名稱 中 文 製備多孔性礦質建築塗料用之塗料組成物 英文 Coating composition forming porous mineral coatings for buildings comprising an aqueous emulsion 姓 名 國 籍 發明 創作> 住、居所 姓 名 (名稱) 德 μ li毒|讓_幕套-屋讀霧1杂¥號 德商·瓦克化學公司 經濟部中^'標準扃員工消費合作社印^ 三、申請人 國 籍 德國 德國慕尼黑市漢斯—賽德-廣場四號 (事務所) 代表人 姓 名 I響希漢iMii査博士 本紙張尺度適用中國國家樣準(CNsIa4規格(210X29?公嫠)經濟部智慧財產局員Η消費合作社印製 1· 一種製借多孔性礦質建築塗料用塗料組成物,選自礦 質油漆、聚矽氧樹脂乳化油漆及塗泥、矽酸鹽分散油漆、 乳化油漆、填料塗料、加強組成物及含有水性乳化液之底 漆,包括 ⑷選自 (Al) Cr c2(r烷基-C2- (V烷氧基矽烷及 (A2)含有烷氧基之有機聚矽氧烷, (B) 有機聚矽氧烷,除其他有機矽氧烷單元外更含有矽氧 烷單元(該等矽氧烷單元具有矽碳-鍵結基,該等矽碳-鍵結基含有鹽基性氮>,但該有機聚矽氧烷之胺值至少 為0·〇1,及 (C) 乳化劑。 2·如申請專利範圍第1項之塗料組成物,其中Cr C20-烷基-C2-C6烷氧基矽烷(Al>具有1個或2個相同或不同, 未經取代或經鹵素取代、矽碳-鍵結之單價CVCm--烷基, 其餘之基係相同或不同之C2-C6-烷氧基。 3·如申請專利範園第1項之塗料组成物,其中有機聚矽 氧烷(A2)係由具有化學通式(I)之單元所組成 R^Si (OR1)y(0H^ z°4-x-y~z ⑴ 2 其中 R 係相同或不同之單價、未經取代或經鹵素取代、矽碳 -鍵結之CV c2。-烴基, 27 ^--_------------------訂------- !線 I'— (請先閱讀背面之注意事項再ii;本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐)