TW202244303A - 保形且平滑之氮化鈦層及其形成方法 - Google Patents

保形且平滑之氮化鈦層及其形成方法 Download PDF

Info

Publication number
TW202244303A
TW202244303A TW111110614A TW111110614A TW202244303A TW 202244303 A TW202244303 A TW 202244303A TW 111110614 A TW111110614 A TW 111110614A TW 111110614 A TW111110614 A TW 111110614A TW 202244303 A TW202244303 A TW 202244303A
Authority
TW
Taiwan
Prior art keywords
tin
precursor
exposure
thin film
flow rate
Prior art date
Application number
TW111110614A
Other languages
English (en)
Chinese (zh)
Inventor
趙賢哲
金海英
佈生 Ｂ 聶
Original Assignee
美商尤金納斯股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US17/547,086 external-priority patent/US20220172988A1/en
Application filed by 美商尤金納斯股份有限公司 filed Critical 美商尤金納斯股份有限公司
Publication of TW202244303A publication Critical patent/TW202244303A/zh

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45557—Pulsed pressure or control pressure
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C23C16/30—Deposition of compounds, mixtures or solid solutions, e.g. borides, carbides, nitrides
    • C23C16/34—Nitrides
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/4401—Means for minimising impurities, e.g. dust, moisture or residual gas, in the reaction chamber
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/4401—Means for minimising impurities, e.g. dust, moisture or residual gas, in the reaction chamber
    • C23C16/4408—Means for minimising impurities, e.g. dust, moisture or residual gas, in the reaction chamber by purging residual gases from the reaction chamber or gas lines
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45523—Pulsed gas flow or change of composition over time
    • C23C16/45525—Atomic layer deposition [ALD]
    • C23C16/45527—Atomic layer deposition [ALD] characterized by the ALD cycle, e.g. different flows or temperatures during half-reactions, unusual pulsing sequence, use of precursor mixtures or auxiliary reactants or activations
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
    • C23C16/455—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating characterised by the method used for introducing gases into reaction chamber or for modifying gas flows in reaction chamber
    • C23C16/45523—Pulsed gas flow or change of composition over time
    • C23C16/45525—Atomic layer deposition [ALD]
    • C23C16/45553—Atomic layer deposition [ALD] characterized by the use of precursors specially adapted for ALD
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer
    • H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic Table or AIIIBV compounds with or without impurities, e.g. doping materials
    • H01L21/28—Manufacture of electrodes on semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/268
    • H01L21/283—Deposition of conductive or insulating materials for electrodes conducting electric current
    • H01L21/285—Deposition of conductive or insulating materials for electrodes conducting electric current from a gas or vapour, e.g. condensation
    • H01L21/28506—Deposition of conductive or insulating materials for electrodes conducting electric current from a gas or vapour, e.g. condensation of conductive layers
    • H01L21/28512—Deposition of conductive or insulating materials for electrodes conducting electric current from a gas or vapour, e.g. condensation of conductive layers on semiconductor bodies comprising elements of Group IV of the Periodic Table
    • H01L21/28556—Deposition of conductive or insulating materials for electrodes conducting electric current from a gas or vapour, e.g. condensation of conductive layers on semiconductor bodies comprising elements of Group IV of the Periodic Table by chemical means, e.g. CVD, LPCVD, PECVD, laser CVD
    • H01L21/28562—Selective deposition
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/70—Manufacture or treatment of devices consisting of a plurality of solid state components formed in or on a common substrate or of parts thereof; Manufacture of integrated circuit devices or of parts thereof
    • H01L21/71—Manufacture of specific parts of devices defined in group H01L21/70
    • H01L21/768—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics
    • H01L21/76838—Applying interconnections to be used for carrying current between separate components within a device comprising conductors and dielectrics characterised by the formation and the after-treatment of the conductors
    • H01L21/76841—Barrier, adhesion or liner layers
    • H01L21/76843—Barrier, adhesion or liner layers formed in openings in a dielectric

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Computer Hardware Design (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Power Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Vapour Deposition (AREA)
  • Electrodes Of Semiconductors (AREA)
  • Internal Circuitry In Semiconductor Integrated Circuit Devices (AREA)
TW111110614A 2021-03-22 2022-03-22 保形且平滑之氮化鈦層及其形成方法 TW202244303A (zh)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US202163164219P 2021-03-22 2021-03-22
US63/164,219 2021-03-22
US17/547,086 US20220172988A1 (en) 2019-10-08 2021-12-09 Conformal and smooth titanium nitride layers and methods of forming the same
US17/547,086 2021-12-09

Publications (1)

Publication Number Publication Date
TW202244303A true TW202244303A (zh) 2022-11-16

Family

ID=83396089

Family Applications (1)

Application Number Title Priority Date Filing Date
TW111110614A TW202244303A (zh) 2021-03-22 2022-03-22 保形且平滑之氮化鈦層及其形成方法

Country Status (4)

Country Link
JP (1) JP2024511050A (ja)
KR (1) KR20230172494A (ja)
TW (1) TW202244303A (ja)
WO (1) WO2022204663A1 (ja)

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6221174B1 (en) * 1999-02-11 2001-04-24 Applied Materials, Inc. Method of performing titanium/titanium nitride integration
KR20110084275A (ko) * 2008-10-27 2011-07-21 어플라이드 머티어리얼스, 인코포레이티드 삼원 화합물의 기상 증착 방법
JP2011168881A (ja) * 2010-01-25 2011-09-01 Hitachi Kokusai Electric Inc 半導体装置の製造方法及び基板処理装置
JP6118197B2 (ja) * 2013-07-02 2017-04-19 東京エレクトロン株式会社 成膜方法

Also Published As

Publication number Publication date
KR20230172494A (ko) 2023-12-22
JP2024511050A (ja) 2024-03-12
WO2022204663A1 (en) 2022-09-29

Similar Documents

Publication Publication Date Title
TW201920740A (zh) 用於填充基材表面上的間隙特徵的方法和相關的半導體元件結構
TW201920736A (zh) 通過迴圈沉積過程在基材的介電表面上沉積鉬金屬膜的方法和相關的半導體元件結構
KR100261017B1 (ko) 반도체 장치의 금속 배선층을 형성하는 방법
KR20190101497A (ko) 루테늄 도핑에 의한 증진된 코발트 내응집성 및 갭 충전 성능
TW202129843A (zh) 以氮化鈦為主之保形薄膜及其形成方法
US20230395369A1 (en) Smooth titanium nitride layers and methods of forming the same
TW201908510A (zh) 包含鈦、矽及氮的多區域擴散阻障
Kim et al. Remote plasma enhanced atomic layer deposition of titanium nitride film using metal organic precursor (C12H23N3Ti) and N2 plasma
TW202244303A (zh) 保形且平滑之氮化鈦層及其形成方法
TW202240006A (zh) 保形且平滑之氮化鈦層及其形成方法
US20220216060A1 (en) Conformal and smooth titanium nitride layers and methods of forming the same
TW202229641A (zh) 氣相沉積組件、氮化矽沉積方法、及形成半導體裝置之方法
US20220172988A1 (en) Conformal and smooth titanium nitride layers and methods of forming the same
US11482413B2 (en) Conformal and smooth titanium nitride layers and methods of forming the same
CN117355631A (zh) 保形且平滑的氮化钛层及其形成方法
TW202307249A (zh) 以氮化鈦矽為主之保形薄膜及其形成方法
CN117378032A (zh) 保形的氮化钛硅基薄膜及其形成方法
Jung et al. Thermal stability of N2–H2 plasma-treated metal-organic-vapor-deposition TiN in a W/TiN/Ti/Si system