TW202129967A - 製造具有多個量子井之半導體結構 - Google Patents

製造具有多個量子井之半導體結構 Download PDF

Info

Publication number
TW202129967A
TW202129967A TW109134955A TW109134955A TW202129967A TW 202129967 A TW202129967 A TW 202129967A TW 109134955 A TW109134955 A TW 109134955A TW 109134955 A TW109134955 A TW 109134955A TW 202129967 A TW202129967 A TW 202129967A
Authority
TW
Taiwan
Prior art keywords
layer
semiconductor
layers
stack
semiconductor alloy
Prior art date
Application number
TW109134955A
Other languages
English (en)
Inventor
史蒂文 艾弗拉德 菲利普斯 克萊
彼得 約翰內斯 阿德里安納斯 瑟斯
Original Assignee
荷蘭商智慧光電控股公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 荷蘭商智慧光電控股公司 filed Critical 荷蘭商智慧光電控股公司
Publication of TW202129967A publication Critical patent/TW202129967A/zh

Abstract

實例係關於一種製造具有多個量子井之一半導體結構之方法。該方法包括：提供一基板，該基板包括具有一第一晶格常數之一種二元半導體化合物；沈積至少在該基板上之一第一層及與該第一層接觸之一第二層，以在該基板上形成實質上平面半導體層之一第一堆疊，為一第一半導體合金之該第一層包括InP，為一第二半導體合金之該第二層包括InP；與該第一堆疊接觸地沈積具有該第一晶格常數之一種二元半導體化合物之一第三層；沈積至少在該第三層上之一第四層及與該第四層接觸之一第五層，以在該第三層上形成實質上平面半導體層之一第二堆疊，該第四層包括包含InP之一第三半導體合金，該第五層包括包含InP之一第四半導體合金。

Description

製造具有多個量子井之半導體結構
本揭露一般而言係關於一種製造具有多個量子井之一半導體結構之方法。
量子井通常用於半導體結構中以提供電子侷限。例如，在光電子裝置中，量子井用於調諧電子帶隙，藉此調諧被發射(在發射器之情況下)或被吸收(在吸收器之情況下)之光子之能量(或頻率)。
在諸多應用中，可以藉由在一堆疊中提供多個量子井來增強一量子井之效應。在一發射器(諸如一雷射)之情況下，此可以增加發射器中受激發射之速率，而在一吸收器之情況下，可以增加吸收速率。
用於光電子裝置之一通常商用材料平台係磷化銦(InP)，其允許將光學主動和被動功能整合到所謂的光子積體電路(PIC)中。
期望提供一種製造具有多個量子井之一半導體結構之更可靠方法。
本揭露之一個態樣提供了一種製造具有多個量子井之一半導體結構之方法。該方法包括：提供一基板，該基板包括具有一第一晶格常數之一種二元半導體化合物；沈積至少在該基板上之一第一層及與該第一層接觸之一第二層，以在該基板上形成實質上平面半導體層之一第一堆疊，為一第一半導體合金之該第一層包括InP，為一第二半導體合金之該第二層包括InP；與該第一堆疊接觸地沈積具有該第一晶格常數之一種二元半導體化合物之一第三層；沈積至少在該第三層上之一第四層及與該第四層接觸之一第五層，以在該第三層上形成實質上平面半導體層之一第二堆疊，該第四層包括包含InP之一第三半導體合金，該第五層包括包含InP之一第四半導體合金。
本揭露之另一態樣提供了一種具有多個量子井之半導體結構。該半導體結構包括：一基板，該基板包括具有一第一晶格常數之一種二元半導體化合物；在該基板上之實質上平面半導體層之一第一堆疊，該第一堆疊包括至少在該基板上之一第一層及與該第一層接觸之一第二層，為一第一半導體合金之該第一層包括InP，為一第二半導體合金之該第二層包括InP；與該第一堆疊接觸之一第三層，為一種二元半導體化合物之該第三層具有該第一晶格常數；及在該第三層上之實質上平面半導體層之一第二堆疊，該第二堆疊包括至少在該第三層上之一第四層及與該第四層接觸之一第五層，該第四層包括包含InP之一第三半導體合金，該第五層包括包含InP之一第四半導體合金。
本揭露進一步提供了一種包括一半導體結構之電致吸收調變器或電致折射調變器。
本文描述之實例係關於製造半導體結構之方法。特定言之但非排他地，其等係關於製造具有多個量子井之半導體結構。
如下文將詳細說明，至少在具有包括InP之量子井之一半導體結構之實例中，本文描述之實例提供了一種改良型半導體結構。因此，此一結構可減少透射穿過該結構之光之散射，可增加發光部分中之受激發射速率，且可增加光吸收部分中之吸收速率。此允許一更高效的光電子裝置，且因此允許一更高效的PIC。
圖1係以一常見方式圖解說明根據實例之製造具有多個量子井之一半導體結構之一方法100之一流程圖。下面參考圖5描述一對應實例半導體結構。
在方塊102處，提供一基板。該基板包括具有一第一晶格常數之一種二元半導體化合物。
例如，該基板可為一InP基板。即，該基板主要包括InP。基板可為純InP (在可接受的純度容限範圍內)，或者可包括其他材料，諸如摻雜劑或雜質，其中該材料包括至少99%的InP。例如，該基板被摻雜有一摻雜劑材料，使得該基板可被視為n摻雜的，或者該基板被摻雜有一摻雜劑材料，使得該基板可被視為p摻雜的。
在方塊104處，方法100包括沈積至少：在基板上之一第一層及與第一層接觸之一第二層，以在基板上形成實質上平面半導體層之一第一堆疊。第一層係包括InP之一第一半導體合金，且第二層係包括InP之一第二半導體合金。
第一堆疊包括複數個層。第一堆疊中之層數小於一臨限層數，超過該臨限層數，堆疊中之一或多個層將展現一缺陷。第一堆疊之製造包括穿插地沈積若干層第一半導體合金以及對應層數之第二半導體合金。如下面參考圖3所描述，至少在某些實例中，特定地在其中第一層和第二層包括InP之實例中，隨著半導體之一數目之增加，在第一堆疊之半導體層中出現缺陷之一趨勢上升。
藉由認為該等層實質上係平面的，設想例如將該等層沈積在基板上，使得該等層中之每一者之上表面與在其上沈積有第一層之基板之表面平行。
在某些實例中，在第一層被沈積成與基板接觸之意義上，第一層係在基板上。在其他實例中，第一層係在基板上，因為其由基板支撐但不直接與基板接觸。例如，存在一或多個中間層，諸如不包括InP之材料，諸如砷化銦鋁(InAlAs)。
作為與本文中使用之術語「在...上」有關之一般性評論，被指定為與一層(諸如下伏層)接觸之一層與該層直接接觸；而被指定為在一層(諸如一下伏層)上之一層可與該層直接接觸或者可由該層支撐，其中該等層之間有一或多個中間層(諸如為不包括InP之一材料的層)。
在某些實例中，該等層中之每一者實質上跨基板之整個表面區域(例如，基板之被其中正製造半導體之一反應器之一晶圓夾具夾持之區域除外)沈積。
圖2係包括包含InP之多個(總共32個)量子井之一半導體結構之掃描電子顯微照片；在此實例中，量子井由磷化砷鎵銦(InGaAsP)之薄層形成，該等薄層經配置以藉由晶格常數與基板之晶格常數匹配而不發生應變。如圖2中所示，生長包括InP之諸多連續半導體量子井會導致半導體結構之層中產生形態缺陷，如下所述，此可表現為半導體之一或多層中之明顯非平面性(例如，起伏)。此等缺陷可導致無法進行磊晶生長，或者導致併入有半導體結構之裝置中之裝置故障，此限制可在該結構中生長之量子井之數目。
如圖2中所示，自剖面看，起伏表現在結構之層中。此等起伏可能不會存在於經處理結構之表面處，該表面仍可能展現一平面表面；例如，此可能係歸因於沈積在半導體結構之層上(例如，以形成一電接觸)之一InP層之平面化效應。
因此，發明人已經瞭解，當使用InP製造多個量子井時，會出現一問題，就目前而言，該問題在使用其他半導體材料平台製造多個量子井時並未出現。發明人判定，取決於處理條件(例如，壓力和溫度)，當在一堆疊中生長超過大約16個量子井時，觀察到缺陷。
因此，在某些實例中，第一半導體合金及第二半導體合金中之每一者之層數大於8且小於16，使得第一堆疊中之總層數小於32。
相反地，圖3係包括不包含InP之36個量子井之一半導體結構之一掃描電子顯微照片；在此實例中，量子井係由砷化鎵鋁銦(InAlGaAs)形成。如所示，圖2中所示之量子井係實質上平面的；儘管可使用含InP之量子井製造更多量子井而不會形成如圖2中所示之缺陷。
為了解決上文參考圖2描述之問題，在方塊106處，與第一堆疊接觸地沈積包括具有第一晶格常數之一種二元半導體材料之一第三層。例如，在基板係InP之情況下，第三層亦可為InP。
此後，在方塊108處，方法100包括沈積至少：與第三層接觸之一第四層及與第四層接觸之一第五層，以在第三層上形成實質上平面半導體層之一第二堆疊。第四層包括包含InP之一第三半導體合金，且第五層包括包含InP之一第四半導體合金。
如熟習此項技術者將瞭解，根據本文描述之實例，可使用各種技術來沈積半導體材料層。此等技術可包含化學氣相沈積技術，諸如金屬有機氣相磊晶(MOVPE)或分子束磊晶(MBE)。
圖4係根據實例之一半導體結構400之一圖式。根據上文參考圖1描述之方法來製造半導體結構。
半導體結構400包括在其上生長有量子井之一基板402。
半導體結構400包含量子井之一第一堆疊404。第一堆疊404包括一第一半導體合金406與一第二半導體合金408之多個交替層。如上文參考圖1之方塊104描述，為第一半導體合金406之一第一層被沈積在基板402上，且為第二半導體合金408之一第二層被沈積成與為第一半導體合金406之第一層接觸。藉由在用於沈積第一半導體合金406之沈積製程與用於沈積第二半導體合金408之沈積製程之間交替來製造多個量子井。
由於上述原因，第一堆疊404包括少於32層。即，第一堆疊包括少於16層第一半導體合金406及少於16層第二半導體合金408。
在某些實例中，第一半導體合金406及第二半導體合金408中之每一者包括一種三元半導體合金或一種四元半導體合金。例如，第一半導體合金406及第二半導體合金408中之每一者包括InGaAsP，其中磷化銦(InP)、砷化鎵(GaAs)、砷化銦(InAs)及磷化鎵(GaP)之相對量在第一半導體合金406與第二半導體合金408之間係不同的。第一半導體合金406及第二半導體合金408中之每一者可被摻雜(例如，p摻雜或n摻雜)。
儘管在某些實例中設想第一半導體合金406及第二半導體合金408中之每一者不發生應變(例如，一個層之晶格常數與其中該層所接觸之層匹配)，但期望選擇引入應變之晶格常數以例如對半導體結構400之光學吸收或發射屬性改性。
在某些實例中，第一半導體合金406及第二半導體合金408中之每一者之層小於15奈米(nm)。
一第三層410與第一堆疊404接觸地沈積。第三層410係一個二元半導體，其之一晶格常數實質上等於基板402之一晶格常數，如上面參考圖1之方塊106所描述的。「實質上相等」意味著引入第三層410不意圖引發應變。
第三層410之厚度可在4 nm至100 nm之範圍內。
包含具有實質上等於基板402之晶格常數之一晶格常數之一第三半導體層410意味著在製造第三層410之前可在不修改製造反應器或不對反應器之製程條件(諸如溫度或壓力)進行任何修改之情況下執行製造製程(例如，圖2之方法)。在實例中，此可使得易於整合到現有製造製程中。
此外，僅添加二元半導體材料之一單個薄層對半導體結構400之整體電光屬性之影響可忽略不計，且因此併入有半導體結構400之裝置之效能不會因包含第三層410而受到不利影響。
量子井之一第二堆疊412與第三層410接觸地沈積。第二堆疊412包括一第三半導體合金414與一第四半導體合金416之多個交替層。如上文參考方塊108所述，為第三半導體合金414之一層沈積在第三層410上，且為第四半導體合金416之一層沈積在與第三層410接觸地沈積之第三半導體合金414之層上。藉由在用於沈積第三半導體合金414之沈積製程與用於沈積第四半導體合金416之沈積製程之間交替來製造多個量子井。
由於上述原因，第二堆疊412亦包括少於32層。即，第一堆疊包括少於16層第一半導體合金406及少於16層第二半導體合金408。
在某些實例中，第三半導體合金414及第四半導體合金416中之每一者包括一種三元半導體合金或一種四元半導體合金。例如，第三半導體合金414及第四半導體合金416中之每一者包括InGaAsP，其中磷化銦(InP)、砷化鎵(GaAs)、砷化銦(InAs)及磷化鎵(GaP)之相對量在第三半導體合金與第四半導體合金(414、416)之間係不同的。第三半導體合金414及第四半導體合金416中之每一者可被摻雜(例如，p摻雜或n摻雜)。
儘管設想在某些實例中第三半導體合金414及第四半導體合金416中之每一者不發生應變(例如，一個層之晶格常數與相鄰層匹配)，但可能期望選擇引入應變之晶格常數以例如對半導體結構400之光學吸收或發射屬性改性。
在某些實例中，可重複參考圖1之方塊106及108描述之製程，以進一步增加半導體結構400中之量子井之數目。
儘管在圖4中所示之實例中，第一堆疊404與第二堆疊412具有相等數目之層，使得第三層410在整體堆疊之中心，但在其他實例中，第一堆疊404與第二堆疊412具有不同數目之量子井層。即，第三層410可在半導體結構400內之其他地方，而不一定在量子井層之確切中間。例如，在包括25個量子井層之半導體結構400中，可在已經製造9個量子井之後沈積第三層410，且可在第三層410上方製造16個量子井。
圖5係包括包含InP之24個量子井之一半導體結構之一掃描電子顯微照片；在此實例中，量子井由磷化砷鎵銦(InGaAsP)之薄層形成，該等薄層經配置以藉由晶格常數與基板之晶格常數匹配而不發生應變。上述第三層410可識別為大約在較暗帶(對應於量子井結構)之一堆疊之中心之亮帶。如圖2中所示，引入第三層410 (其係一材料之一單個薄層)使得能夠在諸如圖2中所示之缺陷存在之前顯著地增加可在半導體結構中製造之含InP之量子井層之數目。因此，上文參考圖1描述之方法提供了一種簡單有效的方法以允許生長包含InP之量子井之更厚堆疊。
例如，藉由增加半導體中之光學侷限，增加重複磊晶量子井層之一堆疊之總厚度可能係有用的。例如，可產生一更有效的電致吸收或電致折射調變器，此乃因電致吸收和電致折射調變器之效率與光學侷限有關。
以上實例應被理解為說明性實例。應當理解，關於任何一個實例描述之任何特徵皆可單獨使用，或者與所描述之其他特徵結合使用，且亦可與任何其他該等實例或者任何其他該等實例之任一組合之一或多個特徵結合使用。此外，在不背離隨附申請專利範圍之範疇之情況下，亦可採用上面未描述之等效物及修改。
100:方法 102:方塊 104:方塊 106:方塊 108:方塊 400:半導體結構 402:基板 404:第一堆疊 406:第一半導體合金 408:第二半導體合金 410:第三層/第三半導體層 412:第二堆疊 414:第三半導體合金 416:第四半導體合金
圖1係圖解說明根據實例之製造具有多個量子井之一半導體結構之一方法之一流程圖； 圖2係具有多個含InP之量子井之一半導體結構之一掃描電子顯微照片，其展示了所得結構中之缺陷； 圖3係具有不含InP之多個量子井之一半導體結構之一掃描電子顯微照片； 圖4係根據實例之一半導體結構之一示意圖；及 圖5係根據實例之具有多個含InP之量子井之一半導體結構之一掃描電子顯微照片。
100:方法
102:方塊
104:方塊
106:方塊
108:方塊

Claims (20)

  1. 一種製造具有多個量子井之一半導體結構之方法，該方法包括： 提供一基板，該基板包括具有一第一晶格常數之一種二元半導體化合物； 沈積至少： 在該基板上之一第一層，為一第一半導體合金之該第一層包括InP，及 與該第一層接觸之一第二層，為一第二半導體合金之該第二層包括InP， 以在該基板上形成實質上平面半導體層之一第一堆疊； 與該第一堆疊接觸地沈積具有該第一晶格常數之一種二元半導體化合物之一第三層； 沈積至少： 在該第三層上之一第四層，該第四層包括包含InP之一第三半導體合金，及 與該第四層接觸之一第五層，該第五層包括包含InP之一第四半導體合金， 以在該第三層上形成實質上平面半導體層之一第二堆疊。
  2. 如請求項1之方法，其中該第一堆疊包括複數個層，該複數個層包括該第一層及該第二層，其中該第一堆疊中之一總層數小於一臨限層數，超過該臨限層數，該第一堆疊之一或多個層將展現一缺陷。
  3. 如請求項1或請求項2之方法，其中該第一堆疊包括複數個層，該複數個層包括該第一層及該第二層，且在不包括該第三層且該第一堆疊包括額外層之情況下，將存在至少該第一堆疊之一個層展現一缺陷之一趨勢。
  4. 如請求項2至請求項3中任一項之方法，其中該缺陷係以下至少一者：平面性中之一或多個起伏或不規則性。
  5. 3或4之方法，其中該第三層至少部分地消除該趨勢，使得該第二堆疊實質上不含該缺陷。
  6. 如請求項2至請求項5中任一項之方法，其中該第一堆疊包括少於32層。
  7. 如前述請求項中任一項之方法，其中存在以下至少一者： 該第三半導體合金與該第一半導體合金實質上相同，或者 該第四半導體合金與該第二半導體合金實質上相同。
  8. 如前述請求項中任一項之方法，其中該第一半導體合金、該第二半導體合金、該第三半導體合金和該第四半導體合金中之每一者分別係一種三元半導體合金或一種四元半導體合金中之一者。
  9. 如前述請求項中任一項之方法，其中該第一半導體合金、該第二半導體合金、該第三半導體合金和該第四半導體合金中之每一者係InGaAsP，其中InP、GaAs、InAs及GaP之相對量在該第一半導體合金與該第二半導體合金之間及在第三半導體合金與該第四半導體合金之間係不同的。
  10. 如請求項2至請求項9中任一項之方法，其中該第二堆疊包括複數個層，其中該第二堆疊中之一層數等於該第一堆疊中之層數。
  11. 如前述請求項中任一項之方法，其中該第三層係InP。
  12. 如前述請求項中任一項之方法，其中該基板係InP。
  13. 如前述請求項中任一項之方法，其中該第三層之一厚度大於4 nm。
  14. 如前述請求項中任一項之方法，其中該第三層之一厚度小於100 nm。
  15. 如前述請求項中任一項之方法，其中該第一層與該基板接觸。
  16. 一種具有多個量子井之半導體結構，該半導體結構包括： 一基板，該基板包括具有一第一晶格常數之一種二元半導體化合物； 該基板上之實質上平面半導體層之一第一堆疊，該第一堆疊包括至少： 在該基板上之一第一層，為一第一半導體合金之該第一層包括InP，及 與該第一層接觸之一第二層，為一第二半導體合金之該第二層包括InP； 與該第一堆疊接觸之一第三層，為一種二元半導體化合物之該第三層具有該第一晶格常數；及 在該第三層上之實質上平面半導體層之一第二堆疊，該第二堆疊包括至少： 在該第三層上之一第四層，該第四層包括包含InP之一第三半導體合金，及 與該第四層接觸之一第五層，該第五層包括包含InP之一第四半導體合金。
  17. 如請求項16之半導體結構，其中該基板係InP。
  18. 如請求項16或請求項17之半導體結構，其中該第三層之一厚度大於4 nm。
  19. 如請求項16至請求項18中任一項之半導體結構，其中該第三層之一厚度小於100 nm。
  20. 一種電致吸收調變器或電致折射調變器，其包括請求項16至請求項19中任一項之半導體結構。
TW109134955A 2019-10-23 2020-10-08 製造具有多個量子井之半導體結構 TW202129967A (zh)