TW202106861A - 一種液晶組合物及液晶顯示器件 - Google Patents
一種液晶組合物及液晶顯示器件 Download PDFInfo
- Publication number
- TW202106861A TW202106861A TW109125327A TW109125327A TW202106861A TW 202106861 A TW202106861 A TW 202106861A TW 109125327 A TW109125327 A TW 109125327A TW 109125327 A TW109125327 A TW 109125327A TW 202106861 A TW202106861 A TW 202106861A
- Authority
- TW
- Taiwan
- Prior art keywords
- liquid crystal
- iii
- general formula
- crystal composition
- carbon atoms
- Prior art date
Abstract
本發明提供一種液晶組合物及液晶顯示器件,所述液晶組合物包含至少一種通式I所示化合物、至少一種通式II所示化合物、至少一種選自通式III-1~III-3所示化合物、至少一種通式IV所示化合物以及至少一種通式V所示化合物;通過同時使用多種二噁烷類單體並與其他單體的搭配使用,使得該液晶組合物具有高對比度、同時提升穿透率,改善低溫存儲穩定性,適用於小折射率各向異性、大介電各向異性的液晶體系,可以滿足現在對液晶顯示器的低電壓驅動需求,適用於ECB等小折射率的顯示模式。
Description
本發明屬於液晶材料領域,涉及一種液晶組合物及液晶顯示器件。
液晶顯示器(Liquid Crystal Display,LCD)因其體積小、重量輕、功耗低且顯示品質優異而獲得了飛速發展,特別在可擕式電子資訊產品中獲得廣泛的應用。隨著用於可擕式電腦、辦公應用、視頻應用的液晶螢幕尺寸的增加,液晶顯示器能夠用於大螢幕顯示並最終替代了陰極射線管的顯示器(Cathode Ray Tube,CRT)。液晶主要用於液晶顯示器件中的電介質,因通過施加電壓可以改變這類物質的光學性能。因此液晶材料必須具有良好的化學和熱穩定性,以及良好的對電場和電磁輻射的穩定性等。
相對於傳統的顯示器件和顯示材料,液晶顯示材料具有明顯的優點:驅動電壓低、功耗微小、可靠性高、顯示信息量大、彩色顯示、無閃爍、對人體無危害、生產過程自動化、成本低廉、可以製成各種規格和類型的液晶顯示器,便於攜帶等。由於這些優點,液晶顯示技術對顯示顯像領域產生了深刻影響,促進了微電子技術和光電資訊技術的發展。液晶材料憑藉其良好的光學性能和光電效應,在諸多顯示場合獲得了廣泛應用。
二噁烷類化合物是液晶單體中的一類優質單體,在液晶領域得到廣泛應用,但現有技術依然存在一些尚待解決的技術問題,如K值小,對比度不足,穿透率不足,低溫存儲不穩定等問題。
本發明對液晶材料做進一步改進從而獲得一些全新的性能優勢,研發出一種高對比度、同時提升穿透率,改善低溫存儲穩定性,適用於小折射率各向異性、大介電各向異性液晶體系的液晶組合物,可以滿足現有技術對液晶顯示器的低電壓驅動要求,適用於ECB等顯示模式。
為解決現有技術中存在的技術問題,本發明提供一種液晶組合物及液晶顯示器件,所述液晶組合物具有高對比度、同時提升穿透率,改善低溫存儲穩定性,適用於小折射率各向異性、大介電各向異性液晶體系的液晶組合物,可滿足液晶顯示器的低電壓驅動要求,適用於ECB等的顯示模式。
為達上述技術效果,本發明採用以下技術方案:
本發明目的之一在於提供一種液晶組合物,所述液晶組合物包含至少一種通式I所示化合物、至少一種通式II所示化合物、至少一種選自通式III-1~III-3所示化合物、至少一種通式IV所示化合物以及至少一種通式V所示化合物;I;II;III-1;III-2;III-3;IV;以及V;
其中,所述R1
~R2
和R12
分別獨立地為氫原子、環丙基、環丁基、環戊基、含有1-7個碳原子的烷基、含有1-7個碳原子的烷氧基、含有2-7個碳原子的烯基或含有2-7個碳原子的烯氧基;所述R4
-R11
分別獨立地為氫原子、鹵代或未鹵代的含有1-7個碳原子的烷基、鹵代或未鹵代的含有1-7個碳原子的烷氧基、鹵代或未鹵代的含有2-7個碳原子的烯基、或鹵代或未鹵代的含有1-7個碳原子的烯氧基;
所述環A0
、環B0
、環A1
和環B1
分別獨立地為1,4-亞環己基或1,3-二噁烷基,且環A0
和B0
不相同,環A1
和B1
中至少一個為1,3-二噁烷基;所述環A3
-A5
、環B2
-B5
、環C3
-C4
以及環D4
分別獨立地為1,4-亞環己基、1,4-亞環己烯基、1,4-亞苯基或至少一個氫原子被鹵原子取代的1,4-亞苯基;
所述Z0
和Z1
分別獨立地為單鍵或亞乙基;所述Z2
為單鍵、亞乙基、亞甲氧基或二氟醚基;所述Z4
-Z6
分別獨立地為單鍵、酯基、亞乙基、亞甲氧基、亞乙烯基、鹵代亞乙基或鹵代亞乙烯基;所述Z7
和Z8
分別獨立地為單鍵、亞乙基或亞乙烯基;
所述L1
-L3
分別獨立地為氫原子或氟原子;
所述Y為氟原子、三氟甲基或三氟甲氧基;
m=0或1;
n=1或2,當n為2時,環B5
相同或不同。
本發明中,含1~7個碳原子的烷基可以是碳原子數為1、2、3、4、5、6、7的直鏈或支鏈烷基;
含1~7個碳原子的烷氧基可以是碳原子數為1、2、3、4、5、6、7的直鏈或支鏈烷氧基;
含2~7個碳原子的烯基可以是碳原子數為2、3、4、5、6、7的直鏈或支鏈烯基;
含2~7個碳原子的烯氧基可以是碳原子數為2、3、4、5、6、7的直鏈或支鏈烯氧基。
鹵代或未鹵代的含1~7個碳原子的烷基可以是鹵代或未鹵代的碳原子數為1、2、3、4、5、6、7的直鏈或支鏈烷基;
鹵代或未鹵代的含1~7個碳原子的烷基可以是鹵代或未鹵代的碳原子數為1、2、3、4、5、6、7的直鏈或支鏈烷氧基;
鹵代或未鹵代的含2~7個碳原子的烷基可以是鹵代或未鹵代的碳原子數為2、3、4、5、6、7的直鏈或支鏈烯基;
鹵代或未鹵代的含2~7個碳原子的烷基可以是鹵代或未鹵代的碳原子數為2、3、4、5、6、7的直鏈或支鏈烯氧基。
相對於現有技術,本發明提供的液晶組合物同時使用了多種二噁烷類單體,並與雙環己烷類等其他單體的搭配使用,通過調配液晶組合物中各組分的比例,使得該組合物體系出現了一些全新的性能優勢:改善暗態顯示,提高對比度,同時提升穿透率,改善低溫性能,可獲得更好的低溫存儲性能;本發明提供的液晶組合物適用於小折射率各向異性、大介電各向異性的液晶體系,又可以滿足技術發展中對於低電壓驅動的迫切需求,可應用於ECB等顯示模式。
作為本發明優選的技術方案,所述液晶組合物包含:占液晶組合物總重量1-20%的所述通式I的化合物,占液晶組合物總重量1-30%的所述通式II的化合物,占液晶組合物總重量1-40%的所述通式III-1~III-3的化合物,占液晶組合物總重量15-60%的所述通式IV的化合物,占液晶組合物總重量1-50%的所述通式V的化合物。
其中,通式I所示化合物的質量分數可以是2%、5%、8%、10%、12%、15%或18%等,通式II所示化合物的質量分數可以是2%、5%、8%、10%、12%、15%、18%、20%、22%、25%、28%等,通式III-1~3所示化合物的質量分數可以是5%、10%、15%、18%、20%、22%、25%、28%、30%、35%、38%等,通式IV所示化合物的質量分數可以是18%、20%、25%、30%、35%、40%、45%、50%或55%等,通式V所示化合物的質量分數可以是5%、8%、10%、15%、20%、25%、30%、35%、40%、45%或48%等,但並不僅限於所列舉的數值,該數值範圍內其他未列舉的數值同樣適用。
作為本發明優選的技術方案,所述通式II的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:II-1;II-2;II-3;II-4;II-5;II-6;II-7;II-8;II-9;II-10;II-11;II-12;或II-13;
其中,所述R2
具有與上述相同的限定範圍。
作為本發明優選的技術方案,所述通式II的化合物選自通式II-1至通式II-12中的任意一種或至少兩種的組合。
更優選地,所述通式II的化合物選自通式II-1、通式II-4、通式II-6、通式II-7、通式II-9、通式II-11和通式II-12中的任意一種或至少兩種的組合。
作為本發明優選的技術方案,所述通式III-1的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-1-1;III-1-2;III-1-3;或III-1-4;
其中,所述R4
和R5
具有與上述相同的限定範圍。
更優選地,III-1的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-1-1-1;III-1-1-2;III-1-1-3;III-1-1-4;III-1-1-5;或III-1-2-1;
其中,R4
為含1~7個碳原子的烷基、含1~7個碳原子的烷氧基、或含2~7個碳原子的烯基;R5
為含1~7個碳原子的烷基或含1~7個碳原子的烷氧基。
優選地,所述通式III-2的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-2-1;III-2-2;III-2-3;III-2-4;III-2-5;III-2-6;III-2-7;III-2-8;III-2-9;III-2-10;或III-2-11;
其中,所述R6
和R7
具有與上述相同的限定範圍。
其中,通式III-2-1更優選地具有如下結構中的任意一種或至少兩種的組合:III-2-1-1;III-2-1-2;III-2-1-3;III-2-1-4;III-2-1-5;或III-2-1-6;
其中,所述R6
和R7
各自獨立地為含1~7個碳原子的烷基或含1~7個碳原子的烷氧基。
通式III-2-2更優選地具有如下結構中的任意一種或至少兩種的組合:III-2-2-1;III-2-2-2;III-2-2-3;III-2-2-4;III-2-2-5;III-2-2-6;或III-2-2-7;
其中,所述R6
和R7
各自獨立地為含1~7個碳原子的烷基或含1~7個碳原子的烷氧基。
優選地,所述通式III-3的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-3-1;III-3-2;III-3-3;III-3-4;III-3-5;或III-3-6;
其中,所述R8
和R9
具有與上述相同的限定範圍。
作為本發明優選的技術方案,所述通式IV的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:IV-1;IV-2;IV-3;IV-4;或IV-5;
其中,R10
-R11
分別獨立地為含1~7個碳原子的烷基、含1~7個碳原子的烷氧基。
作為本發明優選的技術方案,所述通式V的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:V-1;V-2;V-3;V-4;V-5;V-6;V-7;V-8;V-9;V-10;V-11;V-12;V-13;V-14;V-15;V-16;V-17;V-18;或V-19;
其中,所述R12
具有與上述相同的限定範圍。
作為本發明的技術方案,所述液晶組合物還包含至少一種式VI所示化合物:VI;
其中,所述R13
為氫原子、環丙基、環丁基、環戊基、含1~7個碳原子的烷基、含1~7個碳原子的烷氧基、含2~7個碳原子的烯基或含2~7個碳原子的烯氧基;
所述A6
和B6
分別獨立地為1,4-亞環己基、1,4-亞環己烯基、1,4-亞苯基、至少一個氫原子被鹵原子取代的1,4-亞苯基、1,3-二噁烷基或四氫吡喃-2,5-二基;
所謂Z7
為單鍵、亞乙基或亞乙烯基;
所述L4
和L5
分別獨立地為氫原子或氟原子,所述L6
為氫原子或甲基;
所述Y1
為氟原子、三氟甲基或三氟甲氧基;
o為1或2,當o為2時,環B6
相同或不同。
作為本發明優選的技術方案,所述通式VI的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:VI-1;VI-2;VI-3;VI-4;VI-5;VI-6;VI-7;VI-8;VI-9;VI-10;VI-11;VI-12;VI-13;VI-14;VI-15;VI-16;VI-17;VI-18;或VI-19。
其中,所述R13
表示含1~7個碳原子的烷基、含1~7個碳原子的烷氧基、含2~7個碳原子的烯基或含2~7個碳原子的烯氧基。
優選地,所述液晶組合物中式VI所示化合物的質量分數為0~35%,如0%、1%、5%、10%、15%、20%、25%或30%等,但並不僅限於所列舉的數值,該數值範圍內其他未列舉的數值同樣適用。
本發明目的之二在於提供一種液晶顯示器件,所述液晶顯示器件包括上述的液晶組合物。
本發明中,各液晶分子中的代碼的具體含義如表1所示。
表1
基團的單元結構 | 代碼 | 基團名稱 |
C | 1,4-亞環己基 | |
C(N) | 1-氰基-1,4-亞環己基 | |
P | 1,4-亞苯基 | |
I | 茚滿-2,5-二基 | |
G | 2-氟-1,4-亞苯基 | |
U | 2,6-二氟-1,4-亞苯基 | |
W | 2,3-二氟-1,4-亞苯基 | |
P(F,Cl) | 2-氯-3-氟-1,4-亞苯基 | |
A | 四氫吡喃-2,5-二基 | |
D | 1,3-二氧六環-2,5-二基 | |
Q或1(2F)O | 二氟醚基 | |
-CH2 CH2 - | 2 | 亞乙基 |
-CH2 O- | 1O | 亞甲氧基 |
-O- | O | 氧取代基 |
-F | F | 氟取代基 |
-CH=CH- | V | 烯基 |
-C≡C- | T | 炔基 |
V(2F) | 二氟烯基 | |
-COO- | E | 酯基 |
-CN | N | 氰基 |
-Cn H2n+1 或-Cm H2m+1 | n或m | 烷基 |
與現有技術相比,本發明至少具有以下有益效果:
本發明提供一種液晶組合物及液晶顯示器件,所述液晶組合物具有高對比度、同時提升回應速度和穿透率,改善低溫存儲穩定性的液晶組合物,可以滿足液晶顯示器的低電壓驅動要求,適用於ECB等小折射率的顯示模式。
為便於理解本發明,本發明列舉實施例如下。本領域技術人員應該明瞭,所述實施例僅僅是幫助理解本發明,不應視為對本發明的具體限制。
以如下結構式的化合物為例對其結構代碼進行說明:,該結構式如果用表1所示代碼表示,則可以表達為nCPPm,代碼中n表示左端烷基的碳原子數,例如n為3,即表示該烷基為-C3
H7
,代碼中C表示環己烷基,P表示苯基,m表示右端烷基的碳原子數,例如m為2,即表示該烷基為-C2
H5
。
以下實施例中測試專案的簡寫代號如下:
Cp 清亮點(向列相-各向同性相的轉變溫度,℃)
Δn 光學各向異性(589 nm,25℃)
Δε 介電各向異性(1 KHz,25℃)
K11
展曲彈性常數
K22
扭曲彈性常數
K33
彎曲彈性常數
LTS 低溫存儲穩定性
T(穿透率) 光線穿過液晶前後的光強之比。
其中,光學各向異性使用阿貝折光儀在鈉光燈(589 nm)光源下、25℃測試得。
Δε=ε‖
-ε⊥
,其中,ε‖
為平行於分子軸的介電常數,ε⊥
為垂直於分子軸的介電常數,測試條件:25℃、1 KHz、測試盒為TN90型,盒厚7 μm。
K11
、K22
、K33
是使用LCR儀和反平行摩擦盒,測試液晶的C-V曲線計算所得,測試條件:7 μm反平行摩擦盒,V=0.1~20 V;
T(穿透率)測試條件:使用DMS 505測試液晶的V-T(穿透率)曲線,測試盒採用正性3.5μm IPS cell,V=0~20V。
實施例1
本實施例提供一種液晶組合物,其具體組成以及性能參數如表2所示。
表2
液晶分子 | 質量分數/% | 性能參數 | |
2DCUF | 2 | △n | 0.105 |
3DCUF | 2 | Cp | 88 |
3D2CUF | 3 | K11 | 12.8 |
3CDPUF | 5 | K22 | 7.6 |
4CDPUF | 5 | K33 | 14 |
3CD2PUF | 5 | △ε | 6 |
3CPO1 | 8 | T(穿透率) | 13.70% |
3CPO2 | 8 | LTS | -30℃下存儲7天,不析晶 |
1PP2V | 8 | ||
VCCP1 | 8 | ||
3CPP2 | 6 | ||
3CCV | 20 | ||
3CCV1 | 10 | ||
3PGPF | 5 | ||
4PGPF | 5 |
實施例2
本實施例提供一種液晶組合物,其具體組成以及性能參數如表3所示。
表3
液晶分子 | 質量分數/% | 性能參數 | |
2CDUF | 2 | △n | 0.09 |
3CDUF | 3 | Cp | 82 |
4CDUF | 3 | K11 | 12.6 |
3CDPUF | 5 | K22 | 7.4 |
4CDPUF | 3 | K33 | 13.8 |
3CD2PUF | 5 | △ε | 5.7 |
3CPO1 | 5 | T(穿透率) | 13.60% |
1PP2V | 6 | LTS | -30℃下存儲7天,不析晶 |
VCCP1 | 4 | ||
3CPP2 | 3 | ||
3CCV | 41 | ||
3CCV1 | 11 | ||
3PGPF | 5 | ||
4PGPF | 4 |
實施例3
本實施例提供一種液晶組合物,其具體組成以及性能參數如表4所示。
表4
液晶分子 | 質量分數/% | 性能參數 | |
3DCUF | 5 | △n | 0.095 |
3C2DUF | 2 | Cp | 85 |
3D2CUF | 2 | K11 | 12.4 |
3DPUF | 1 | K22 | 7.3 |
2DCPUF | 2 | K33 | 14.4 |
3DCPUF | 2 | △ε | 4.9 |
4DCPUF | 2 | T(穿透率) | 13.80% |
3D2C2PUF | 4 | LTS | -30℃下存儲7天,不析晶 |
1PP2V | 8 | ||
3CCP2 | 5 | ||
3CCV | 50 | ||
3CCV1 | 10 | ||
3PGPF | 4 | ||
4PGPF | 3 |
實施例4
本實施例提供一種液晶組合物,其具體組成以及性能參數如表5所示。
表5
液晶分子 | 質量分數/% | 性能參數 | |
2DCUF | 2.5 | △n | 0.092 |
3DCUF | 2 | Cp | 82 |
3D2CUF | 2 | K11 | 13.7 |
3CDPUF | 5.5 | K22 | 8.3 |
3CD2PUF | 5.5 | K33 | 14.4 |
VCCP1 | 6 | △ε | 7 |
3CPP2 | 9 | T(穿透率) | 14.30% |
3CCV | 48.5 | LTS | -40℃下存儲7天,不析晶 |
3PGPF | 2 | ||
4PGPF | 4 | ||
6CPUF | 8 | ||
3PGUQUF | 1.5 | ||
4PGUQUF | 1.5 | ||
5PGUQUF | 2 |
實施例5
本實施例提供一種液晶組合物,其具體組成以及性能參數如表6所示。
表6
液晶分子 | 質量分數/% | 性能參數 | |
2CDUF | 2.5 | △n | 0.086 |
3DCUF | 3 | Cp | 84 |
3D2CUF | 2 | K11 | 14.7 |
3D2CPUF | 4 | K22 | 8.2 |
3C2D2PUF | 3 | K33 | 16.6 |
3CDPUF | 5.5 | △ε | 8.9 |
2DC1OPGF | 2 | T(穿透率) | 14.40% |
2DC1OPUF | 2 | LTS | -30℃下存儲7天,不析晶 |
3CPO1 | 8 | ||
3CCP2 | 8.5 | ||
VCCP1 | 7 | ||
3CCV | 38.5 | ||
6CPUF | 7 | ||
4PGUQUF | 2.5 | ||
5PGUQUF | 2 | ||
3D2PUQUF | 2.5 |
實施例6
本實施例提供一種液晶組合物,其具體組成以及性能參數如表7所示。
表7
液晶分子 | 質量分數/% | 性能參數 | |
2CDUF | 5.5 | △n | 0.078 |
3CDUF | 6 | Cp | 88 |
5C2DUF | 6 | K11 | 14.3 |
3D2CPUF | 4 | K22 | 8.5 |
3CDPUF | 3 | K33 | 15.7 |
3D2PPUF | 4 | △ε | 11.6 |
3CPO1 | 6.5 | T(穿透率) | 15.20% |
3CCEPC3 | 4 | LTS | -40℃下存儲7天,不析晶 |
3CCEPC4 | 4.5 | ||
5CC3 | 5 | ||
4CC3 | 7 | ||
3CC3 | 6 | ||
2CCUF | 5.5 | ||
3CCUF | 3 | ||
3CCQUF | 14 | ||
3PUQUF | 8 | ||
3PGUQPOCF3 | 3 | ||
4PGUQPOCF3 | 2 | ||
2CDUQUF | 3 |
實施例7
本實施例提供一種液晶組合物,其具體組成以及性能參數如表8所示。
表8
液晶分子 | 質量分數/% | 性能參數 | |
2CDUF | 5 | △n | 0.078 |
5CDUF | 5 | Cp | 85 |
3CDPUF | 2 | K11 | 13.8 |
3CCEP3 | 4 | K22 | 7.8 |
3CCEC5 | 5 | K33 | 17.4 |
3CCECC3 | 2.5 | △ε | 9.2 |
3CCV | 18.5 | T(穿透率) | 14.60% |
2CCGF | 5 | LTS | -40℃下存儲7天,不析晶 |
3CCGF | 5 | ||
5CCGF | 4.5 | ||
2CCUF | 5 | ||
3CCUF | 5 | ||
5CCUF | 6 | ||
3C2CUF | 6 | ||
4C2CUF | 6.5 | ||
3CCGUF | 5 | ||
3D2PUQUF | 6 | ||
4D2PUQUF | 4 |
實施例8
本實施例提供一種液晶組合物,其具體組成以及性能參數如表9所示。
表9
液晶分子 | 質量分數/% | 性能參數 | |
3CDUF | 3 | △n | 0.09 |
3DCUF | 4 | Cp | 95 |
3D2CPUF | 4 | K11 | 13.1 |
4D2CPUF | 4 | K22 | 7.9 |
VCCP1 | 5.5 | K33 | 18.3 |
3CCEPC3 | 4 | △ε | 10.4 |
3CCV | 20 | T(穿透率) | 14.50% |
3CCV1 | 6 | LTS | -40℃下存儲7天,不析晶 |
5CCV | 9 | ||
3CPUF | 8.5 | ||
2CCUF | 6 | ||
3CCUF | 6 | ||
5CCUF | 4 | ||
3CCPUF | 4 | ||
4CCPUF | 4 | ||
3D2PUQUF | 4 | ||
4D2PUQUF | 4 |
實施例9
本實施例提供一種液晶組合物,其具體組成以及性能參數如表10所示。
表10
液晶分子 | 質量分數/% | 性能參數 | |
2DCUF | 5 | △n | 0.08 |
5DCUF | 5 | Cp | 91 |
2C2D2PUF | 6 | K11 | 13.2 |
3C2D2PUF | 5.5 | K22 | 7.7 |
2CDPUF | 5 | K33 | 17.7 |
3CDPUF | 5 | △ε | 9.6 |
3CCEP3 | 3 | T(穿透率) | 14.40% |
3CC1OC5 | 3 | LTS | -40℃下存儲7天,不析晶 |
3CCEPC2 | 3 | ||
3CCEPC3 | 3 | ||
3CCV | 21 | ||
3CPUF | 2 | ||
2CCUF | 10 | ||
3CCUF | 8 | ||
3C2CUF | 8 | ||
4C2CUF | 7.5 |
實施例10
本實施例提供一種液晶組合物,其具體組成以及性能參數如表11所示。
表11
液晶分子 | 質量分數/% | 性能參數 | |
2CDUF | 5.5 | △n | 0.081 |
3CDUF | 6 | Cp | 100 |
5CDUF | 6 | K11 | 12.3 |
2CDPUF | 5 | K22 | 7.3 |
3CDPUF | 3 | K33 | 18.2 |
2CD2PUF | 6 | △ε | 11.4 |
3CD2PUF | 5.5 | T(穿透率) | 15.00% |
3DC1OPGF | 5 | LTS | -40℃下存儲7天,不析晶 |
3CPO1 | 2.5 | ||
3CCEPC3 | 5 | ||
3CCEPC4 | 4.5 | ||
5CC3 | 5 | ||
4CC3 | 8 | ||
3CCO3 | 6 | ||
3CCGF | 7.5 | ||
4CCGF | 6 | ||
5CCGF | 5 | ||
2CCUF | 5.5 | ||
3CCUF | 3 |
對比例1
本對比例提供一種液晶組合物,其具體組成以及性能參數如表12所示。
表12
液晶分子 | 質量分數/% | 性能參數 | |
2CDUF | 3 | △n | 0.098 |
3CDUF | 3 | Cp | 82 |
4CDUF | 2 | K11 | 11.7 |
2DCUF | 1.5 | K22 | 7.1 |
3C2DUF | 4 | K33 | 13.2 |
3CPO1 | 10 | △ε | 3.2 |
3CPO2 | 10 | T(穿透率) | 12.80% |
1PP2V | 8 | LTS | -20℃下存儲7天,析晶 |
VCCP1 | 9 | ||
3CPP2 | 5 | ||
3CCV | 23 | ||
3CCV1 | 11.5 | ||
3PGPF | 5 | ||
4PGPF | 5 |
通過實施例1-10和對比例1的對比可知,本發明的液晶組合物具有較大的K值,穿透率和對比度有明顯提升,同時低溫互溶性也有所提升,改善了低溫存儲性能。
申請人聲明,本發明通過上述實施例來說明本發明的詳細工藝設備和工藝流程,但本發明並不局限於上述詳細工藝設備和工藝流程,即不意味著本發明必須依賴上述詳細工藝設備和工藝流程才能實施。所屬技術領域的技術人員應該明瞭,對本發明的任何改進,對本發明產品各原料的等效替換及輔助成分的添加、具體方式的選擇等,均落在本發明的保護範圍和公開範圍之內。
Claims (10)
- 一種液晶組合物,其特徵在於: 該液晶組合物包含至少一種通式I所示化合物、至少一種通式II所示化合物、至少一種選自通式III-1~III-3所示化合物、至少一種通式IV所示化合物以及至少一種通式V所示化合物;I;II;III-1;III-2;III-3;IV;以及V; 其中,R1 ~R2 和R12 分別獨立地為氫原子、環丙基、環丁基、環戊基、含有1-7個碳原子的烷基、含有1-7個碳原子的烷氧基、含有2-7個碳原子的烯基或含有2-7個碳原子的烯氧基;所述R4 -R11 分別獨立地為氫原子、鹵代或未鹵代的含有1-7個碳原子的烷基、鹵代或未鹵代的含有1-7個碳原子的烷氧基、鹵代或未鹵代的含有2-7個碳原子的烯基、或鹵代或未鹵代的含有1-7個碳原子的烯氧基; 環A0 、環B0 、環A1 和環B1 分別獨立地為1,4-亞環己基或1,3-二噁烷基,且環A0 和B0 不相同,環A1 和B1 中至少一個為1,3-二噁烷基;所述環A3 -A5 、環B2 -B5 、環C3 -C4 以及環D4 分別獨立地為1,4-亞環己基、1,4-亞環己烯基、1,4-亞苯基或至少一個氫原子被鹵原子取代的1,4-亞苯基; Z0 和Z1 分別獨立地為單鍵或亞乙基;Z2 為單鍵、亞乙基、亞甲氧基或二氟醚基;Z4 -Z6 分別獨立地為單鍵、酯基、亞乙基、亞甲氧基、亞乙烯基、鹵代亞乙基或鹵代亞乙烯基;Z7 和Z8 分別獨立地為單鍵、亞乙基或亞乙烯基; L1 -L3 分別獨立地為氫原子或氟原子; Y為氟原子、三氟甲基或三氟甲氧基; m=0或1; n=1或2,當n為2時,環B5 相同或不同。
- 如請求項1所述之液晶組合物,其中,通式I的化合物占液晶組合物總重量的1-20%,通式II的化合物占液晶組合物總重量的1-30%,通式III-1~III-3的化合物占液晶組合物總重量的1-40%,通式IV的化合物占液晶組合物總重量的15-60%,通式V的化合物占液晶組合物總重量的1-50%。
- 如請求項1至4中任一項所述之液晶組合物,其中,通式III-1的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-1-1;III-1-2;III-1-3;或III-1-4; 其中,R4 和R5 具有與請求項1-4相同的限定範圍; 通式III-2的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-2-1;III-2-2;III-2-3;III-2-4;III-2-5;III-2-6;III-2-7;III-2-8;III-2-9;III-2-10;或III-2-11; 其中,R6 和R7 具有與請求項1-4相同的限定範圍; 通式III-3的化合物為具有如下結構的化合物中的任意一種或至少兩種的組合:III-3-1;III-3-2;III-3-3;III-3-4;III-3-5;或III-3-6; 其中,R8 和R9 具有與請求項1-4相同的限定範圍。
- 如請求項1至7中任一項所述之液晶組合物,其中,該液晶組合物還包含至少一種通式VI所示化合物:VI 其中,R13 為氫原子、環丙基、環丁基、環戊基、含1~7個碳原子的烷基、含1~7個碳原子的烷氧基、含2~7個碳原子的烯基或含2~7個碳原子的烯氧基; 環A6 和環B6 分別獨立地為1,4-亞環己基、1,4-亞環己烯基、1,4-亞苯基、至少一個氫原子被鹵原子取代的1,4-亞苯基、1,3-二噁烷基或四氫吡喃-2,5-二基; Z7 為單鍵、亞乙基或亞乙烯基; L4 和L5 分別獨立地為氫原子或氟原子,L6 為氫原子或甲基; Y1 為氟原子、三氟甲基或三氟甲氧基; o為1或2,當o為2時,環B6 相同或不同。
- 一種液晶顯示器件,其特徵在於:該液晶顯示器件包括請求項1-9中任一項所述之液晶組合物。