TW201510142A - 用於偏振板的黏合劑膜、包括其的偏振板和包括其的光學顯示器 - Google Patents

用於偏振板的黏合劑膜、包括其的偏振板和包括其的光學顯示器 Download PDF

Info

Publication number
TW201510142A
TW201510142A TW103128619A TW103128619A TW201510142A TW 201510142 A TW201510142 A TW 201510142A TW 103128619 A TW103128619 A TW 103128619A TW 103128619 A TW103128619 A TW 103128619A TW 201510142 A TW201510142 A TW 201510142A
Authority
TW
Taiwan
Prior art keywords
weight
adhesive film
polarizing plate
group
vinyl monomer
Prior art date
Application number
TW103128619A
Other languages
English (en)
Other versions
TWI617639B (zh
Inventor
Won Kim
Yi-Eun Kim
Yoo-Jin Suh
Seung-Jun Lee
Ha-Yun Cho
In-Cheon Han
Original Assignee
Samsung Sdi Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Samsung Sdi Co Ltd filed Critical Samsung Sdi Co Ltd
Publication of TW201510142A publication Critical patent/TW201510142A/zh
Application granted granted Critical
Publication of TWI617639B publication Critical patent/TWI617639B/zh

Abstract

本文揭示了包括由式1表示的官能基的用於偏振板的黏合劑膜、包括其的偏振板以及包括其的光學顯示器。 □

Description

用於偏振板的黏合劑膜、包括其的偏振板和包括其的光學顯示器 相關申請案的交互引用
2013年8月22日向韓國智慧財產局提申的韓國專利申請案10-2013-0099973，標題為“用於偏振板的黏合劑膜、包括其的偏振板以及包括其的光學顯示器”，的全部內容藉由引用合併於此。
發明領域
本發明涉及一種用於偏振板的黏合劑膜、包括其的偏振板以及包括其的光學顯示器。
發明背景
偏振板包括以一定方向配置的含有碘化合物或二向色性材料的偏振器。偏振板包括在偏振器的兩個表面上的保護膜(如三乙醯纖維素(TAC))以保護偏振器。
通常，偏振板具有以下結構：在該結構中保護膜堆疊在偏振器上且黏合劑層插入其間。由於環境變化，在保護膜與偏振器之間的介面處或在保護膜與黏合於保護膜的另一構件之間的介面處產生應力，並且由於應力造成的光彈性雙折射改變了保護膜的相位延遲。特別地，由於在 螢幕末端處的每個構件的尺寸變化比在其中心部分處的更大，所以螢幕有可能在其末端處經受顯著的漏光。
在近期生產更大尺寸和更高亮度的圖像顯示器的趨勢下，由於從光源放熱，圖像顯示器的內部溫度趨於上升。此外，由於薄的圖像顯示器(諸如液晶顯示器和有機EL顯示器)更廣泛地被用於各種目的，將薄的圖像顯示器用於諸如高溫和高濕的惡劣環境中。因此，在環境變化時，在螢幕末端處的漏光有可能更明顯。
在相關技術中，日本專利公開案2000-352619A建議使用具有小的絕對光彈性係數的透明保護膜以便減少延遲變化。
發明概要
本發明的一個方面提供用於偏振板的黏合劑膜，所述黏合劑膜即使在高溫或高濕的惡劣使用條件下仍具有優異的改善漏光能力並且呈現優異的耐久性和可靠性。
根據本發明的一個方面，用於偏振板的黏合劑膜可包括由式1表示的官能基：
(其中*、A、B、R2和n如在詳細描述中所定義。)
根據本發明的另一個方面，偏振板可包括如上文所述的黏合劑膜。
根據本發明的再一個方面，光學顯示器可包括如上文所述的偏振板。
10‧‧‧偏振器
20‧‧‧第一光學膜
30‧‧‧第二光學膜
40‧‧‧黏合劑層
100‧‧‧偏振板
110‧‧‧面板
、、©、、‧‧‧指示亮度測量點
圖1是根據本發明的一個實施方式的偏振板的截面圖。
圖2是根據本發明的一個實施方式的光學顯示器的截面圖。
圖3顯示面板上漏光的測量位置。
較佳實施例之詳細說明
將參考附圖詳細地描述本發明的實施方式。應理解，本發明不限於下列實施方式並且可以不同方式實施。在附圖中，為了清晰起見將忽略與描述不相關的部分。相似的組分在整篇說明書中將由相似的附圖標記表示。
根據本發明的一個方面，用於偏振板的黏合劑膜可包括由式1表示的官能基：
(其中*表示結合位點；A為C1至C20脂族烴基；B為-O-、-S-、C1至C20脂族烴基或單鍵；R2為C1至C20脂族烴基；且n是1至5的整數。)
在一個實施方式中，A可為C1至C10脂族烴基，具體而言為直鏈或支鏈C1至C10伸烷基，更具體而言為直鏈或支鏈C1至C5伸烷基；B可為-O-或-S-；且R2可為C1至C10脂族烴基，具體而言為直鏈或支鏈C1至C10烷基，更具體而言為直鏈或支鏈C1至C5烷基。
在一個實施方式中，由式1表示的官能基可由式1-1表示：
(其中*和n如在式1中定義。)
由於用於偏振板的黏合劑膜包括由式1表示的官能基，所以黏合劑膜可抑制漏光並且在高溫和高濕下呈現優異的耐久性和可加工性。在一個實施方式中，由式1或式1-1表示的官能基在黏合劑膜中的含量可為10重量%(wt%)至99wt%，具體而言為50wt%至95wt%，更具體而言為80wt%至95wt%。在該範圍內，可有效實現具有低光彈性係數的黏合劑層，從而抑制漏光。在一個實施方式中，如在23℃和在590nm的波長處測量的，用於 偏振板的黏合劑膜可具有-120×10-12m2/N至120×10-12m2/N例如-115×10-12m2/N至-1×10-12m2/N的光彈性係數。在該範圍內，黏合劑膜可抑制偏振板的漏光。
用於偏振板的黏合劑膜可具有大於0μm至100μm或以下，例如1μm至50μm，具體而言為5μm至30μm的厚度。在該範圍內，黏合劑膜可應用於偏振板。
用於偏振板的黏合劑膜可用於使多個光學膜彼此黏合或用於將偏振板黏合至面板，並且光學膜可包括保護膜或延遲膜。
用於偏振板的黏合劑膜可黏合於在附著至偏振器的光學膜中的具有低光彈性係數的光學膜。在一個實施方式中，光學膜在23℃和在590nm的波長處可具有0.1×10-12m2/N至100×10-12m2/N的光彈性係數。如上所述，雖然根據本發明的用於偏振板的黏合劑膜黏合於具有低光彈性係數的光學膜，但是黏合劑膜在用於液晶顯示器時也可防止漏光。
黏合劑膜可由黏合劑組合物形成，所述黏合劑組合物包括具有由式1表示的官能基的(甲基)丙烯酸共聚物。例如，黏合劑膜可藉由乾燥和/或老化黏合劑組合物來製備。老化可包括熱固化、UV固化或在35℃貯存1小時至1週，而並不局限於此。例如，可藉由將黏合劑組合物塗覆在離型膜(例如，聚對苯二甲酸乙二酯膜)上，然後在25℃至50℃乾燥和固化來製備黏合劑膜。
(甲基)丙烯酸共聚物
由於(甲基)丙烯酸共聚物在其側鏈包括由式1表 示的官能基，(甲基)丙烯酸共聚物在被包括於黏合劑層中時可抑制漏光，並且可實現在高溫和高濕下呈現優異的耐久性以及可加工性的偏振板。在一個實施方式中，(甲基)丙烯酸共聚物可為單體混合物的共聚物，所述單體混合物包括由式2表示的單體：
(其中A為C1至C20脂族烴基；B為-O-、-S-、C1至C20脂族烴基或單鍵；R2為C1至C20脂族烴基；R1為氫或甲基；且n是1至5的整數。)
由於(甲基)丙烯酸共聚物包括由式2表示的單體，所以黏合劑膜可藉由改善光學性能來抑制漏光，並且可確保黏結力。
由式2表示的單體在單體混合物或(甲基)丙烯酸共聚物中的含量可為50wt%至100wt%，具體而言為50wt%至96wt%，更具體而言為75wt%至95wt%。在該範圍內，可有效實現具有低光彈性係數的黏合劑層。由式2表示的單體可藉由典型方法合成，或可為可商購的。
在一個實施方式中，單體混合物可包括75wt%至95wt%的由式2-1表示的單體：
(甲基)丙烯酸共聚物可為單體混合物的共聚 物，所述單體混合物包括由式2表示的單體、含有烷基的乙烯基單體、含有羧酸基的乙烯基單體、含有羥基的乙烯基單體、含有雜環的乙烯基單體、含有芳基的乙烯基單體、含有脂環基的乙烯基單體和含有醯胺基的乙烯基單體中的至少一種。
含有烷基的乙烯基單體可形成用於偏振板的黏 合劑膜的結構，並且可包括具有直鏈或支鏈C1至C20烷基的(甲基)丙烯酸酯。例如，含有烷基的乙烯基單體可包括以下的至少一種：(甲基)丙烯酸甲酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸丙酯、(甲基)丙烯酸正丁酯、(甲基)丙烯酸叔丁酯、(甲基)丙烯酸異丁酯、(甲基)丙烯酸戊酯、(甲基)丙烯酸己酯、(甲基)丙烯酸2-乙基己酯、(甲基)丙烯酸庚酯、(甲基)丙烯酸辛酯、(甲基)丙烯酸異辛酯、(甲基)丙烯酸壬酯、(甲基)丙烯酸癸酯和(甲基)丙烯酸十二烷基酯，而並不局限於此。其等可單獨或以其組合使用。
含有烷基的(甲基)丙烯酸單體在(甲基)丙烯酸共 聚物中的含量可為0.1wt%至30wt%，具體而言為0.1wt%至20wt%，更具體而言為1wt%至15wt%。在該範圍內， 黏合劑膜可呈現耐久性所必需的黏結力。
含有羧酸基的乙烯基單體為(甲基)丙烯酸單體 並且可包括(甲基)丙烯酸或β-羧乙基(甲基)丙烯酸酯，而並不局限於此。其等可單獨或以其組合使用。
含有羧酸基的(甲基)丙烯酸單體在(甲基)丙烯酸 共聚物中的含量可為0.001wt%至10wt%，具體而言為0.001wt%至5wt%。在該範圍內，黏合劑膜可在苛刻條件下抑制脫離或起泡的同時獲得可再剝離性。在一個實施方式中，含有羧酸基的(甲基)丙烯酸單體在(甲基)丙烯酸共聚物中的含量可為0.005wt%至1wt%，或例如0.007wt%至0.05wt%。
含有羥基的乙烯基單體可為(甲基)丙烯酸酯單 體並且可為含有C2至C20烷基、C5至C20環烷基、或C6至C20芳基的在其末端或在其任何其它位置具有羥基的(甲基)丙烯酸酯。例如，含有羥基的乙烯基單體可包括(甲基)丙烯酸2-羥乙酯、(甲基)丙烯酸2-羥丙酯、(甲基)丙烯酸2-羥丁酯、(甲基)丙烯酸4-羥丁酯、(甲基)丙烯酸6-羥己酯、單(甲基)丙烯酸1,4-環己烷二甲醇酯、(甲基)丙烯酸1-氯-2-羥丙基酯、單(甲基)丙烯酸二乙二醇酯、單(甲基)丙烯酸1,6-己二醇酯、三(甲基)丙烯酸季戊四醇酯、五(甲基)丙烯酸二季戊四醇酯、單(甲基)丙烯酸新戊二醇酯、三羥甲基丙烷二(甲基)丙烯酸酯、三羥甲基乙烷二(甲基)丙烯酸酯、2-羥基-3-苯氧基丙基(甲基)丙烯酸酯、(甲基)丙烯酸4-羥基環戊酯、(甲基)丙烯酸4-羥基環己酯或單(甲基)丙烯酸環己烷二甲醇 酯，而並不局限於此。其等可單獨或以其組合使用。
含有羥基的(甲基)丙烯酸單體在(甲基)丙烯酸共 聚物中的含量可為0.1wt%至10wt%，具體而言為0.1wt%至1wt%，更具體而言為0.5wt%至1wt%。在該範圍內，黏合劑膜可在苛刻條件下抑制脫離或起泡的同時獲得可再剝離性。
含有雜環的乙烯基單體可為具有雜原子(例如， 氮、氧和硫中的至少一種)的含有C2至C10脂族或脂環族的飽和的或不飽和雜環的單體、或含有C4至C20芳族雜環的單體。例如，含有雜環的乙烯基單體可包括丙烯醯基啉。 含有雜環的乙烯基單體在(甲基)丙烯酸共聚物中的含量可選地為10wt%以下，例如5wt%以下。在該範圍內，黏合劑膜可呈現改善的耐久性、可靠性和良好的可再加工性。
含有醯胺基的乙烯基單體可包括丙烯醯胺和甲 基丙烯醯胺。其等可單獨或以其組合使用。含有醯胺基的(甲基)丙烯酸單體在(甲基)丙烯酸共聚物中的含量可為0.1wt%至10wt%，具體而言為0.1wt%至1wt%，更具體而言為0.5wt%至1wt%。在該範圍內，黏合劑膜可在苛刻條件下抑制起泡。
含有芳基的乙烯基單體可包括含有C6至C20芳基 或C7至C21芳烷基的(甲基)丙烯酸酯。在一個實施方式中，含有芳基的乙烯基單體可包括(甲基)丙烯酸苯酯、或(甲基)丙烯酸苄酯等。含有芳基的(甲基)丙烯酸單體的含量可任選地為14wt%以下，具體而言為0.1wt%至14wt%，更具體而 言為1wt%至14wt%。在該範圍內，可獲得具有合適光彈性係數以用於抑制漏光的黏合劑層。
在一個實施方式中，(甲基)丙烯酸共聚物可為單 體混合物的共聚物，所述單體混合物包括：50wt%至96wt%的由式2表示的單體；0.1wt%至30wt%的含有烷基的乙烯基單體；0.001wt%至10wt%的含有羧酸基的乙烯基單體；0.1wt%至10wt%的含有羥基的乙烯基單體；和0.1wt%至10wt%的含有醯胺基的乙烯基單體。
在另一個實施方式中，(甲基)丙烯酸共聚物可為 混合物的共聚物，所述混合物包括：50wt%至96wt%的由式2表示的單體；0.1wt%至20wt%的含有烷基的乙烯基單體；0.001wt%至10wt%的含有羧酸基的乙烯基單體；0.1wt%至10wt%的含有羥基的乙烯基單體；和0.1wt%至14wt%的含有芳基的乙烯基單體。
(甲基)丙烯酸共聚物可具有200,000g/mol至 2,000,000g/mol，例如800,000g/mol至1,000,000g/mol的重量平均分子量。在該範圍內，黏合劑組合物可在塗覆時確保外部外觀，並且可在藉由乾燥和老化被附著至偏振膜後抑制外觀缺陷(諸如脫離和起泡)。
(甲基)丙烯酸共聚物可具有2至15，例如3至12的 多分散指數(PDI)。在該範圍內，黏合劑組合物可在塗覆時確保外部外觀，並且可在藉由乾燥和老化被附著至偏振膜後抑制外觀缺陷(諸如脫離和起泡)。
(甲基)丙烯酸共聚物可具有-75℃至30℃，例如 -55℃至0℃，且在一個實施方式中具有-50℃至-10℃的玻璃化轉變溫度。在該範圍內，用於偏振板的黏合劑膜可為偏振板提供應力弛豫並且呈現與玻璃改善的黏結力，從而在提供高抗收縮性的同時使漏光最小化。
(甲基)丙烯酸共聚物可在25℃具有3,000cPs至 5,000cPs的黏度。在該範圍內，黏合劑組合物可呈現改善的可塗布性。
(甲基)丙烯酸共聚物可藉由溶液聚合、光聚合、 本體聚合或乳液聚合來製備，而並不局限於此。例如，(甲基)丙烯酸共聚物可藉由在50℃至140℃的聚合溫度下進行溶液聚合來製備。
聚合起始劑可包括偶氮類化合物起始劑，諸如偶氮二異丁腈或偶氮二環己腈；和/或典型起始劑，包括諸如過氧化苯甲醯或乙醯基過氧化物等的過氧化物。
基於100重量份的含有烷基的乙烯基單體，起始劑的含量可為0.01重量份至10重量份。在該範圍內，共聚物可被充分聚合。
在聚合時，溶劑可包括乙酸乙酯和甲乙酮中的至少一種，而並不局限於此。
以固含量計，(甲基)丙烯酸共聚物在黏合劑組合物中的含量可為70wt%至99.5wt%例如90wt%至99.5wt%。在該範圍內，黏合劑組合物可具有形成塗膜的優點，並允許黏合劑組分均勻分佈。
用於偏振板的黏合劑組合物可進一步包括交聯 劑和矽烷偶聯劑中的至少一種。
交聯劑
交聯劑可被包括於用於偏振板的黏合劑組合物中，並因此改善黏合劑膜的交聯度，從而穩定黏合劑膜的結構。在一個實施方式中，交聯劑可包括異氰酸酯、環氧基樹脂、氮丙啶、三聚氰胺、胺、醯亞胺、碳二醯亞胺和醯胺交聯劑中的至少一種。
異氰酸酯交聯劑可包括甲苯二異氰酸酯、2,4-甲苯二異氰酸酯、2,6-甲苯二異氰酸酯、氫化三氯乙烯二異氰酸酯、同種型二異氰酸酯(isoform diisocyanate)、1,3-二甲苯二異氰酸酯、1,4-二甲苯二異氰酸酯、二苯基甲烷-4,4-二異氰酸酯、1,3-二異氰醯甲基環己烷、四甲基二甲苯二異氰酸酯、1,5-萘二異氰酸酯、六亞甲基二異氰酸酯、2,2,4-三甲基六亞甲基二異氰酸酯、2,4,4-三甲基六亞甲基二異氰酸酯、三羥甲基丙烷改質的甲苯二異氰酸酯、三羥甲基丙烷改質的甲代伸苯基二異氰酸酯、甲苯二異氰酸酯與三羥甲基丙烷的加成物、二甲苯二異氰酸酯與三羥甲基丙烷的加成物、三苯基甲烷三異氰酸酯、或亞甲基雙三異氰酸酯等，而並不局限於此。其等可單獨或以其組合使用。
以固含量計，交聯劑在黏合劑組合物中的含量可為0.1wt%至20wt%，例如0.1wt%至9wt%。在該範圍內，黏合劑組合物可呈現優異的耐久性、可靠性和其組分和性能的隨時間較小的變化。
矽烷偶聯劑
矽烷偶聯劑可被包括於用於偏振板的黏合劑膜 中以改善與液晶顯示面板的黏結力。矽烷偶聯劑可為本領域技術人員已知的典型矽烷偶聯劑。例如，矽烷偶聯劑可包括含有環氧結構的矽化合物，諸如3-縮水甘油氧基丙基三甲氧基矽烷、3-縮水甘油氧基丙基甲基二甲氧基矽烷、2-(3,4-環氧環己基)乙基三甲氧基矽烷等；含有可聚合的不飽和基團的矽化合物，諸如乙烯基三甲氧基矽烷、乙烯基三乙氧基矽烷、(甲基)丙烯醯氧基丙基三甲氧基矽烷等；含有胺基的矽化合物，諸如3-胺基丙基三甲氧基矽烷，N-(2-胺基乙基)-3-胺基丙基三甲氧基矽烷，N-(2-胺基乙基)-3-胺基丙基甲基二甲氧基矽烷等；和3-氯丙基三甲氧基矽烷，而並不局限於此。例如，矽烷偶聯劑可為含有環氧結構的矽烷偶聯劑。
以固含量計，矽烷偶聯劑在黏合劑組合物中的含 量可為0.1wt%至10wt%，例如0.1wt%至5wt%。在該範圍內，黏合劑組合物可呈現優異的與液晶面板的黏結力，並且(甲基)丙烯酸共聚物可呈現優異的貯存穩定性。
用於偏振板的黏合劑組合物可進一步包括溶劑。溶劑可包括甲乙酮，而並不局限於此。
用於偏振板的黏合劑組合物可進一步包括典型的添加劑，諸如UV吸收劑、或抗氧化劑等，從而在防止由於光或氧造成的損害的同時改善黏合劑膜的壽命。
用於偏振板的黏合劑組合物可用作壓敏黏合劑(PSA)的材料。具體而言，黏合劑組合物可用作用於將偏振 板附著至面板(例如液晶顯示面板)的PSA黏合劑。此外，用於偏振板的黏合劑組合物還可用作用於在偏振板中附著多個光學膜的黏合劑，所述偏振板包括多個保護膜。
根據本發明的另一個方面，偏振板可包括如上文 所述的黏合劑膜。在一個實施方式中，偏振板可包括偏振器、在偏振器的下表面上形成的光學膜，和在光學膜下表面上形成的黏合劑層。光學膜可包括保護膜或延遲膜。偏振板可進一步包括在偏振器的上表面上的光學膜。如本文所用的，參考附圖來定義術語諸如"上表面"和"下表面"。因此，應理解，術語"上表面"可與術語"下表面"交換使用。
黏合劑層可包括用於偏振板的上述黏合劑膜或 用於偏振板的黏合劑組合物的固化產物。光學膜可在23℃和在590nm的波長處具有0.1×10-12m2/N至100×10-12m2/N的光彈性係數。
偏振板在附著至面板(例如液晶顯示面板)時可在抑制漏光方面具有優異的改善，並在高溫和高濕條件下呈現優異的耐久性。在一個實施方式中，偏振板可具有0至0.4，例如0至0.1的漏光值(△L)，如由等式1表示：[等式1]△L=[(a+b+d+e)/4]/c-1
(其中a、b、d和e為其上堆疊有偏振板的面板的每側中點處的亮度，並且c為在其上堆疊有偏振板的面板的中心位點處的亮度)。
較小的△L表示較低的漏光度。
在測量漏光時，偏振板可在85℃的高溫條件下留 置250小時，或在60℃和90% RH的耐濕熱條件放置250小時，並在25℃留置1小時。
圖1為根據本發明的一個實施方式的偏振板的截 面圖。參照圖1，偏振板可包括偏振器10、在偏振器10的上表面上形成的第一光學膜20；在偏振器10的下表面上形成的第二光學膜30；和在第二光學膜30的下表面上形成的黏合劑層40。黏合劑層40可堆疊在液晶顯示面板的一個表面上(未示出)。
偏振器可為藉由拉伸含有偏振組分(諸如碘等) 的聚乙烯醇樹脂膜而製備的膜。聚乙烯醇樹脂可包括聚乙烯醇、聚乙烯縮甲醛、聚乙烯縮醛或乙烯-醋酸乙烯酯共聚物等的皂化產物。
偏振器可具有例如10μm至30μm的厚度，而並 不局限於此。
第一光學膜和第二光學膜可包括保護膜和延遲 膜中的至少一種。保護膜可黏合於偏振器的兩個表面以保護偏振器。為此，保護膜可選自諸如三乙醯纖維素的纖維素膜、聚碳酸酯膜、包括聚對苯二甲酸乙二酯的聚酯膜等。 各保護膜可以單層或多層堆疊。保護膜可具有20μm至80μm的厚度。
對於延遲膜，可沒有限制地使用任何膜，只要該 膜通常用於偏振板並且具有相位延遲功能。例如，延遲膜可為由烯烴膜製備的膜，所述烯烴膜包括環烯烴聚合物 (COP)膜、丙烯酸膜、纖維素膜或聚碳酸酯膜。延遲膜可具有10μm至100μm，例如10μm至60μm的厚度。在該範圍內，延遲膜可提供光學補償並且在用於偏振板時呈現圓偏振。
第一光學膜和第二光學膜可藉由黏合層堆疊在偏振器上。黏合層可由水基黏合劑、或壓敏黏合劑等形成。
偏振板可進一步包括堆疊在第二光學膜的一個表面上的另一光學膜。
根據本發明的再一個方面，光學顯示器可包括如上文所述的偏振板。
在一個實施方式中，光學顯示器可為，例如液晶顯示器和OLED顯示器。
圖2為根據本發明的一個實施方式的光學顯示器的截面圖。參照圖2，光學顯示器可包括面板110(例如，液晶顯示面板)和在面板110的上側上形成的偏振板100。偏振板還可在面板的下側上形成。
在下文，將參考一些實施例更詳細地描述本發明。然而，應注意到，該等實施例僅為了舉例說明而提供，並且不以任何方式被解釋為限制本發明。
製備例1：(甲基)丙烯酸共聚物的製備
在1L的4頸燒瓶中放入50g乙酸乙酯(EAc)、10g甲乙酮(MEK)、95g丙烯酸2-(2-乙氧基乙氧基)乙酯(EOEOEA)、0.01g丙烯酸(AA)、0.7g甲基丙烯酸2-羥乙酯(2-HEMA)、0.6g丙烯醯胺(AM)和3.7g丙烯酸丁酯(n-BA)， 接著將燒瓶加熱至70℃，然後將燒瓶保持在70℃。將0.06g作為偏振起始劑的偶氮二異丁腈溶解於20g乙酸乙酯中，並加入燒瓶中。在65℃進行反應3小時，接著將170g甲乙酮加入燒瓶中，然後將燒瓶冷卻至40℃，從而製備在25℃具有4,400cPs的黏度的丙烯酸共聚物。
製備例2至6：(甲基)丙烯酸共聚物的製備
除了EOEOEA、AA、2-HEMA、AM、n-BA和丙烯酸苄酯(BzA)的量分別根據表1修改之外，以與製備例1相同的方式製備(甲基)丙烯酸共聚物。
用於實施例和比較例的組分的詳情如下。
(A)(甲基)丙烯酸共聚物：在製備例中製備的(甲基)丙烯酸共聚物。
(B)交聯劑：三羥甲基丙烷改質的甲代伸苯基二異氰酸 酯(Colonate-L,Nippon Polyurethane Industry Co.,Ltd.)，其為異氰酸酯交聯劑
(C)矽烷偶聯劑：3-縮水甘油氧基丙基三甲氧基矽烷(KBM-403,Shin-Etsu Chemical Co.,Ltd.)
實施例1至4和比較例1至2
將(甲基)丙烯酸共聚物、交聯劑和矽烷偶聯劑以表2中列出的量(單位：重量份)加入用作溶劑的18重量份的甲乙酮中，接著在25℃下攪拌30分鐘，從而製備用於偏振板的黏合劑組合物。
關於下列性能評價所製備的用於偏振板的黏合劑組合物或由黏合劑組合物製備的用於偏振板的黏合劑膜。結果示於表3中。
(1)光彈性係數：夾緊黏合劑膜樣品(尺寸：2cm×2cm×1,000μm，寬度×長度×厚度)的兩端，在施加應力(5N至15N)至樣品的同時在23℃和在590nm的波長處使用光譜型橢偏儀(M-220,JASCO Co.,Ltd.)測量在樣品中心處的延遲，從而由應力和延遲的函數的斜率計算樣品的光彈性係數。
(2)耐久性和可靠性：將包括由黏合劑組合物製備的黏合劑層(厚度：20μm)的各偏振板(100mm×175mm，寬度×長度)附著至玻璃基板的兩個表面，並且對偏振板施加4kg/cm2至5kg/cm2的壓力以製備樣本。此處，為了不產生起泡或污染，在潔淨室中製備樣本。對於所製備的樣本，藉由將樣本在60℃和90% RH的條件下留置500小時、隨後觀察樣本是否經受起泡或剝落來評價耐濕熱性。在評價前將 樣本在25℃留置1小時，然後用裸眼或顯微鏡觀察。藉由將樣本在85℃留置500小時，接著觀察樣本是否經受起泡或剝落來評價耐熱性。評價標準如下。
O：無起泡或剝落
△：輕微起泡或剝落
X：起泡或剝落
(3)漏光：使用與耐久性和可靠性評價中相同的偏振板評價漏光。使用背光單元評價在暗室中是否漏光。將塗覆黏合劑膜的偏振板(400mm×200mm，寬度×長度)附著至玻璃基板的兩個表面(410mm×210mm×0.7mm，寬度×長度×厚度)，以使偏振板的光軸彼此垂直。將所製備的樣本在60℃留置500小時(耐熱條件)或在50℃和90% RH留置500小時(耐濕熱條件)，然後在使用之前於25℃留置1小時或更長時間。在操作使用樣品的液晶顯示器後，使用亮度測定儀(RISA,Hiland Co.,Ltd.)以1m的高度測量在顯示面板的前側處的亮度。
具體而言，測量面板的中心區域處的亮度(c)以及在出現漏光的面板邊緣處的亮度(a)、(b)、(d)和(e)。如圖3中所示，分別在面板的每側的四個中點處以及在面板的中心處放置亮度測量點。此處，面板的每側與具有0.5cm直徑的用於亮度測量的圓形的圓周相連。在圖3中，、、©、和指示亮度測量點。根據下列等式1定量漏光度(△L)。較低的△L值表示更好的漏光特性，其根據下列標準來評價。
<等式1> △L=[(a+b+d+e)/4]/c-1
(其中a、b、d和e是在分別對應於圖3的亮度測量點的a、b、d和e處測量的亮度，並且c是在中心c處的亮度)
O：在用裸眼觀察時亮度無差異(不能識別漏光)
△：在用裸眼觀察時亮度有輕微差異
X：在用裸眼觀察時亮度有顯著差異
如表3中所示，根據本發明的用於偏振板的黏 合劑膜呈現良好的耐久性和可靠性，並且在漏光方面具有優異的改善。相反地，比較例1的黏合劑膜(不包括由式2表示的單體)與根據本發明的黏合劑膜相比，呈現更低的耐久性和可靠性，並且在漏光方面無改善。而且，比較例2的黏合劑膜(包括含有芳基的單體，但不包括由式2表示的單體)由於其難以聚合而具有低分子量，並且由於高Tg而幾乎不呈現黏結力，且由此不呈現耐久性和可靠性。
10‧‧‧偏振器
20‧‧‧第一光學膜
30‧‧‧第二光學膜
40‧‧‧黏合劑層
100‧‧‧偏振板

Claims (19)

  1. 一種用於偏振板的黏合劑膜，包含由式1表示的官能基： 其中*表示結合位點；A為C1至C20脂族烴基；B為-O-、-S-、C1至C20脂族烴基或單鍵；R2為C1至C20脂族烴基；且n是1至5的整數。
  2. 如請求項1之黏合劑膜，其中該官能基由式1-1表示： 其中*和n如在式1中所定義。
  3. 如請求項1之黏合劑膜，其中該官能基在該黏合劑膜中的含量為10wt%至99wt%。
  4. 如請求項1之黏合劑膜，其中如在23℃和在590nm的波長處測量，該黏合劑膜具有-120×10-12m2/N至120×10-12m2/N的光彈性係數。
  5. 如請求項1之黏合劑膜，其中該黏合劑膜由包含(甲基)丙烯酸共聚物的組合物形成，該(甲基)丙烯酸共聚物包含由式2表示的單體： 其中A為C1至C10脂族烴基；B為-O-、-S-、C1至C10脂族烴基或單鍵；R2為C1至C10脂族烴基；R1為氫或C1至C5烷基；且n是1至5的整數。
  6. 如請求項5之黏合劑膜，其中該由式2表示的單體在該(甲基)丙烯酸共聚物中的含量為50wt%至100wt%。
  7. 如請求項5之黏合劑膜，其中該(甲基)丙烯酸共聚物包含該由式2表示的單體、含有烷基的乙烯基單體、含有羧酸基的乙烯基單體、含有羥基的乙烯基單體和含有醯胺基的乙烯基單體的混合物的共聚物。
  8. 如請求項7之黏合劑膜，其中該混合物包含：50wt%至96wt%的該由式2表示的單體；0.1wt%至30wt%的該含有烷基的乙烯基單體；0.001wt%至10wt%的該含有羧酸基的乙烯基單體；0.1wt%至10wt%的該含有羥基的乙烯基單體；和0.1wt%至10wt%的該含有醯胺基的乙烯基單體。
  9. 如請求項7之黏合劑膜，其中該混合物進一步包含含有芳基的乙烯基單體。
  10. 如請求項9之黏合劑膜，其中該混合物包含：50wt%至96wt%的該由式2表示的單體；0.1wt%至20wt%的該含有烷基的乙烯基單體；0.001wt%至10wt%的該含有羧酸基的乙烯基單體；0.1wt%至10wt%的該含有羥基的乙烯基單體；0.1wt%至10wt%的該含有醯胺基的乙烯基單體；和0.1wt%至14wt%的該含有芳基的乙烯基單體。
  11. 如請求項5之黏合劑膜，其中該組合物進一步包含交聯劑和矽烷偶聯劑中的至少一種。
  12. 如請求項11之黏合劑膜，其中該交聯劑包含異氰酸酯交聯劑。
  13. 如請求項11之黏合劑膜，其中該矽烷偶聯劑包含環氧結構。
  14. 如請求項11之黏合劑膜，其中以固含量計，該組合物包含70wt%至99.5wt%的該共聚物、0.1wt%至20wt%的該交聯劑和0.1wt%至10wt%的該矽烷偶聯劑。
  15. 如請求項1之黏合劑膜，其中該黏合劑膜具有大於0μm至100μm或以下的厚度。
  16. 一種偏振板，包含：一偏振器；一在該偏振器的下表面上形成的光學膜；以及一在該光學膜的下表面上形成的如請求項1至15中任一項之用於偏振板的黏合劑膜。
  17. 如請求項16之偏振板，進一步包含：一在該偏振器的上 表面上形成的光學膜。
  18. 如請求項16之偏振板，其中該偏振板具有0至0.4的漏光值△L，該漏光值如等式1所表示：[等式1]△L=[(a+b+d+e)/4]/c-1其中a、b、d和e為其上堆疊有偏振板的面板的每側中點處的亮度，並且c為其上堆疊有偏振板的面板的中心位點處的亮度。
  19. 一種光學顯示器，包含如請求項16之偏振板。
TW103128619A 2013-08-22 2014-08-20 用於偏振板的黏合劑膜、包括其的偏振板和包括其的光學顯示器 TWI617639B (zh)