SU986896A1 - Composition for coating construction products

Info

Publication number: SU986896A1
Application number: SU813271724A
Authority: SU
Inventors: Петр Иванович Боженов; Владимир Иванович Хренов
Original assignee: Ленинградский Ордена Трудового Красного Знамени Инженерно-Строительный Институт
Priority date: 1981-03-31
Filing date: 1981-03-31
Publication date: 1983-01-07

Description

(54) КОМПОЗИЦИЯ ДЛЯ ПОКРЫТИЯ СТРОИТЕЛЬНЫХ ИЗДЕЛИЙ(54) COMPOSITION FOR COATING CONSTRUCTION PRODUCTS

Изобретение относитс к промышленности строительных материалов и .может быть использовано дл производства цвет ных строительных изделий: автоклавного кирпича, бетонных изделий, асбесто-це- ментных изделий и др. Известна композици дл покрыти строительных изделий, включающа вес.ч стирол 40-60, бутадиен 5-35, 1О-35 насыщенные эфиры, пигменты и воду 1 Наиболее близкой к предложенной по технической сущности и достигаемому результату вл етс композици дл покрыти строительных изделий 2 , вклю чающа стирол, перекись бензола и гидравлическое в жущее - цветной портланд . цемент - при следующем соотношении компонентов, мас.%: Стирол 14-78 Перекись бензоила 1-2 Цветной 2О-86 портландцемент Однако известные композиции не обеспечивают достаточную прочность покрыти .. Целью изобретени вл етс повьпие- ние твердости покрыти . Цель достигаетс тем, что покрыти строительных изделий, включающа стирол, перекись бензоила и гидравлическое в жущее , в качестве последнего содержит маломагнезиальную известь и дополнительно горно-обогатительного комбин а та с содержанием 85% диопсида и пигмент при следующем соотнощении компонентов, мае. %: Стирол .36-83 Перекись бензоила1-2 Малом 1гнезиальна известь3-2О Отход горно-обогатительного комбината с содержанием 85% диопсида1О-35 Пигмент2-8 3986 Введение отхода горно-обогатитепьного комбината с содержанием 85% диопсида ( Са g912. Ой) и маломагнезиальной извести в количестве, соответствующем коэф. фициенту основности 1,05-1,15, позвол ет получить в услови51х повьапенных а емператур пара в автоклаве нар5Шу со смешанными гидросиликатами калыш и магни гидросиликаты кальци , вступают во взаимодействие с мономером с образог ванием сложных соединений. Композицию готов т следующим обраОтход горно-обогатительного комбизшта с содержанием 85% диопсида измель чают совместно с маломагнезиальной известью и пигментом. Полученную смесь объедин ют со стиролом и перекисью бензоила . Композицию в виде суспензии нанос т 20 The invention relates to the building materials industry and can be used for the production of colored building products: autoclaved bricks, concrete products, asbestos-cement products, etc. The known composition for coating building products, including weight.h styrene 40-60, butadiene 5-35, 1O-35 saturated esters, pigments and water 1 Closest to the proposed technical essence and the achieved result is a composition for coating building products 2, including styrene, benzene peroxide and hydraulic cement is - color portland. cement - in the following ratio of components, wt.%: Styrene 14-78 Benzoyl peroxide 1-2. Colored ISO-86 Portland cement. However, the known compositions do not provide sufficient strength to the coating. The aim of the invention is to increase the hardness of the coating. The goal is achieved by the fact that coatings of building products, including styrene, benzoyl peroxide and hydraulic sticking, as the latter contain low-magnesia lime and additionally an ore-dressing plant with a content of 85% diopside and pigment in the following ratio of components, May. %: Styrene .36-83 Benzoyl peroxide1-2 Low 1 mg lime3-2O Waste from a mining and processing plant with a content of 85% diopse1O-35 Pigment2-8 3986 Introduction of a waste from an mining and enrichment combine with a content of 85% diopside (Ca g912 Oi) magnesia lime in an amount corresponding to the coefficient. The basicity of 1.05-1.15, which allows to obtain under the conditions of steam vapor temperature in an autoclave with calis and magnesium hydrosilicates of calcium with mixed hydrosilicates, interacts with the monomer to form complex compounds. The composition is prepared as follows: Mining and processing plant with a content of 85% diopside is ground together with low magnesia lime and pigment. The mixture obtained is combined with styrene and benzoyl peroxide. The suspension composition is applied 20.

тонким слоем на поверхность сьфца иa thin layer on the surface of syftsa and

Адгези , баллыAdhesion points

Твердость, мн/м Блеск, %Hardness, mn / m Gloss,%

таблице.the table.

1111111111

ISO 154 164 154 146 25 24 222020 4 вергают автоклавной обработке или греву в течение 4 ч при . Готов т четьфе смеси с содержанием коментов , мае. %: 2 3 1 69,5 56 Стирол83 Стирол Перекись 1,5 1,0 1,0 бензоила ЛА.аломагне- зиальна 8 20 известь Отход горнообогатительного комбината с содержанием 85% 10 20 30 35 диопсида Пигмент Результаты испытаний известного и полученных составов представлены вISO 154 164 154 146 25 24 222020 4 are autoclaved or heated for 4 hours at. Ready to mix mixture containing komenty, May. %: 2 3 1 69.5 56 Styrene83 Styrene Peroxide 1.5 1.0 1.0 benzoyl LA.malomagnesial 8 20 lime Waste from the ore-dressing plant with a content of 85% 10 20 30 35 diopside Pigment The test results of the known and obtained compositions are presented at

Claims

Claim

A composition for coating construction products, including styrene, benzoyl peroxide and a hydraulic binder, characterized in that, in order to increase the hardness of the coating, it contains low-magnesium lime and additionally waste from a mining and processing plant as a hydraulic binder. with a content of 85% diopside and pigment in the following ratio, May. %: fifty