SU986898A1 - Composition for applying coatings to construction products - Google Patents

Composition for applying coatings to construction products Download PDF

Info

Publication number
SU986898A1
SU986898A1 SU813289769A SU3289769A SU986898A1 SU 986898 A1 SU986898 A1 SU 986898A1 SU 813289769 A SU813289769 A SU 813289769A SU 3289769 A SU3289769 A SU 3289769A SU 986898 A1 SU986898 A1 SU 986898A1
Authority
SU
USSR - Soviet Union
Prior art keywords
composition
lime
pigment
construction products
mineral filler
Prior art date
Application number
SU813289769A
Other languages
Russian (ru)
Inventor
Петр Иванович Боженов
Николай Федорович Федоров
Владимир Иванович Хренов
Сергей Владимирович Семенов
Original Assignee
Ленинградский Ордена Трудового Красного Знамени Инженерно-Строительный Институт
Ленинградский Ордена Октябрьской Революции И Ордена Трудового Красного Знамени Технологический Институт Им.Ленсовета
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ленинградский Ордена Трудового Красного Знамени Инженерно-Строительный Институт, Ленинградский Ордена Октябрьской Революции И Ордена Трудового Красного Знамени Технологический Институт Им.Ленсовета filed Critical Ленинградский Ордена Трудового Красного Знамени Инженерно-Строительный Институт
Priority to SU813289769A priority Critical patent/SU986898A1/en
Application granted granted Critical
Publication of SU986898A1 publication Critical patent/SU986898A1/en

Description

(54) КОМПОЗИЦИЯ ДЛЯ НАНЕСЕНИЯ ПОКРЫТИЯ НА СТРОИТЕЛЬНЫЕ ИЗДЕЛИЯ(54) COMPOSITION FOR COATING CONSTRUCTION PRODUCTS

1one

Изобретение относитс  к строительным материалам и может быть использовано дл  производства цветных строительньЬгс изделий:, цветного силикатного кирпича, цветного керамического кирпича, цветных бетонных и асбесто-цементных изделий. Известна композици  дл  нанесени  бесшовных покрытий 1 , включающа , мае. %:The invention relates to building materials and can be used for the production of colored building products: colored silicate bricks, colored ceramic bricks, colored concrete and asbestos-cement products. A known composition for the application of seamless coatings 1, including May. %:

Фурфурол-ацетоновый мономер35-36Furfural-acetone monomer35-36

Отвердитель7-8Hardener 7-8

Наполнитель52-55Filler52-55

Концентрат органического вещества кукерситовогоConcentrate of organic matter kukersitovogo

сланца1-6slate 1-6

Наиболее близкой к изобретению по технической сущности и достигаемому результату  вл етс  композици  дл  на- :несени  покрыти  на строительные изде- ли  С 2 t включающа  мае. %: Фурфурол-ацетоновый мономер16Closest to the invention to the technical essence and the achieved result is a composition for: carrying a coating on C 2 t building products, including May. %: Furfural-acetone monomer16

22

Бензолсульфокислота4Benzenesulfonic acid4

Кварцевый песок8ОQuartz sand 8O

Покрыти , получаемые из известных композиций, обладают недостаточной адгезией , твердостью и блеском.Coatings obtained from known compositions have insufficient adhesion, hardness and gloss.

Цель изобретени  - повышение адгезии , твердости и блеска покрыти .The purpose of the invention is to increase the adhesion, hardness and gloss of the coating.

Цель достигаетс  тем, что композици  дл  нанесени  покрыти  на строитель10 ные издели , включающа  фурфуролсодер- жащее св зующее и минеральный наполнитель , содержит в качестве фурфуролсодержащего св зующего фурфураль этилен, в качестве минерального наполнител  - мо15 лотый фосфорный шлак к дополнительно известь и пигмент при следующем соот ноще 1ни компонентов, мае. %:The goal is achieved by the fact that the composition for coating construction products, including furfural-containing binder and mineral filler, contains, as furfural-containing binder, furfural ethylene, as mineral filler - young phosphorus slag to additionally lime and pigment with the following ratio But 1 components, May. %:

Фурфуральэтилен12-80Furfural ethene12-80

Молотый фосфорный 20 щлак, 15-77Ground phosphate 20 shlak, 15-77

Известь 3,5-6,5Lime 3,5-6,5

Пигмент1,5-4,5 .Pigment 1.5-4.5.

Фурфуральэтилен представл ет собой продукт синтеза поливинилового спирта 36Se и фур(|урола, химический состав фсюфорнего шлака, мае. %: SiO. 41,74; 1,99; РеаОэ 0,17;СаО 46, Mg-0 4,60; S0% 0,44; 0,58; P205l,20, П.П.П, - остальное. Введение молотого фосфорного шлака, обладающего повьпиенной белизной совместно с кальциевой известью позвол ет в услови х гидротермальной обработки получить на шероховатой поверхности гидросиликаты калыш  с высокими механическими свойствами и, соответственно, адгезией к подложке. В качестве материала подложки строительного издели  могут быть использованы силикатный кирпич, асбесто-цементные издели ,  чеистый бетон и др. Композицию Л тов т следующим образом . 84 Совместно измельчают фосфорный шлак, известь и пигмент (коэффициент основности смеси 1,11) затем ввод т фурфуральэтилен и 10% воды по весу композиции . Композицию нанос т тонким слоем на поверхность сырца и подвергают автоклавной обработке или прогреву. Конкретные примеры выполнени  и фкзико- еханические свойства образцов еде„ь, в. табл. 1 и 2 соогветсгвен° Предлагаема  композици  нар ду с повышением твердости и адгезии покрыти  позвол ет улучшить его декоративные свойства. Таблица 1Furfural Ethylene is a product of the synthesis of 36Se polyvinyl alcohol and fur (| urol, chemical composition of phosphorus slag, May.%: SiO. 41.74; 1.99; ReaOe 0.17; CaO 46, Mg-0 4.60; S0 % 0.44; 0.58; P205l, 20, PPP, the rest. The introduction of ground phosphoric slag, which has white lime along with calcium lime, allows, under hydrothermal treatment conditions, to obtain on the rough surface silicate silicates with high mechanical properties and, accordingly, adhesion to the substrate. As a substrate material for a building product, Silicate bricks, asbestos-cement products, cellular concrete, etc. shall be used. The composition is as follows: 84 Phosphoric slag, lime and pigment are crushed together (the basicity ratio of the mixture is 1.11) then furfuralletile and 10% of water are added by weight of the composition The composition is applied with a thin layer on the surface of the raw material and subjected to autoclave treatment or heating. Specific examples of the performance and the physical-mechanical properties of the samples of food, c. tab. 1 and 2 co-opt. ° The proposed composition, along with an increase in hardness and adhesion of the coating, improves its decorative properties. Table 1

12 40 Фурфуральэтилен 77 54 Молотый фосфорный шлак 6,5 4,0 Кальциева  известь 4,5 2,0 ФурфуролацетоноБый мономер „ Бензолсульфокислота Кварцевьй песок12 40 Furfural Ethylene 77 54 Ground Phosphoric Slag 6.5 4.0 Calcium Lime 4.5 2.0 Furfurol Acetate Monomer “Benzene Sulfonic Acid Quartz Sand

Оптимальное соотношение компонентов.The optimal ratio of components.

ТабЯйиа2 80 20,5 60,510 80 15 70 33,578 16,5 89,5 3 ,5 5,5 4,57,5 3,0 6,0 1,5 4,О 1,54,5 О,5 4,5 . ---16 „ 4 --- Tabajaia2 80 20.5 60.510 80 15 70 33.578 16.5 89.5 3, 5 5.5 4.57.5 3.0 6.0 1.5 4, O 1.54.5 O, 5 4.5 . --- 16 „4 ---

6 76 7

8 (контрольный)8 (control)

Claims (2)

9 (прототип) Формула изобретени  Композици  дл  нанесени  покрыти  на cTpOHTejibHbie издели , включающа  фурфуролсодержащее св зующее и минеральный наполнитель, отличающа с  тем, что, с целью повьипени  25 адгезии, твердости и блеска локрыти , она содержиг в качестве фурфуролсодержащего св зующего фур(|уральэтилен, в качестве минерального наполнител  - молотый фосфорный шлак и дополнительно зо известь и пигмент при следующем состношении компонентов, мае. %:9 (prototype) Formula composition of the invention for coating cTpOHTejibHbie article comprising furfurolsoderzhaschee binder and a mineral filler, characterized in that, in order povipeni 25, adhesion, hardness and gloss lokryti it soderzhig as furfurolsoderzhaschego binder waggons (| uraletilen , as a mineral filler - ground phosphoric slag and additionally lime and pigment with the following composition of components, May.%: Продолжение таблицы 2Continuation of table 2 19 2О19 2O 15 18 п № ны 19 Фурфуральэтилен 12-80 Молотый фосфорный 15-77 Известь 3,5-6,5 Пигмент 1,5-4,5 Источники информации, ин тые во внимание при экспертизе 1.Авторское свидетельство 358297, кл. С 04 В 25/04, 1971. 15 18 n No. 19 19 Furfurallethine 12-80 Ground Phosphorus 15-77 Lime 3.5-6.5 Pigment 1.5-4.5 Sources of information that are taken into account in the examination 1.Certificate of certificate 358297, cl. From 04 To 25/04, 1971. 2.Соломатов В. И. Полимерцемен- бетоны и растворы. Стройиздат, М., 67, с. 145 (прототип).2. Solomatov V. I. Polymer cement-concretes and mortars. Stroyizdat, M., 67, p. 145 (prototype).
SU813289769A 1981-03-31 1981-03-31 Composition for applying coatings to construction products SU986898A1 (en)