SU1031939A1 - Mortar for coating concrete products - Google Patents
Mortar for coating concrete products Download PDFInfo
- Publication number
- SU1031939A1 SU1031939A1 SU813383351A SU3383351A SU1031939A1 SU 1031939 A1 SU1031939 A1 SU 1031939A1 SU 813383351 A SU813383351 A SU 813383351A SU 3383351 A SU3383351 A SU 3383351A SU 1031939 A1 SU1031939 A1 SU 1031939A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- coating
- concrete products
- asbestos
- mortar
- mineral additive
- Prior art date
Abstract
СТРОИТЕЛЬНЫЙ РАСТВОР ДЛЯ ПОKKflVlR БЕТОНШХ ИЗДЕЛИЙ, включак ций цемент, песок, минеральную добавку, асбестит и органический клей, о т личающ-ийс тем, что, с целые повышени адгезии и трещиностойкости покрыти , он дополнительно содержит известь гашенную, в качестве минераль кой добавки - молотый ваграночный граншлак, а в качестве органического кле натриевую соль карбоксиметилцеллюлозы при след укхцем соотношении компонентов, мае. %.t Цемент10-20 Песок45-66 Молотый ваграночный граншлак 1-2 Асбестит7-10 Натриева соль карбок§ симетилцеллюлозы1-3 Известь га шенна 10-20CONSTRUCTION SOLUTION FOR POKKflVlR CONCRETE PRODUCTS, inclusions of cement, sand, mineral additive, asbestos and organic glue, which is due to the fact that, with the whole increase in adhesion and crack resistance of the coating, it additionally contains slaked lime as a mineral additive, ground cupola slag, and as organic glue carboxymethylcellulose sodium salt with the following ratio of components, May. % .t Cement10-20 Sand45-66 Ground cupola slag 1-2 Asbestos 7-10 Sodium salt of carboxymethyl methylcellulose 1-3 Lime per shenna 10-20
Description
СОWITH
со со соwith so with so
Изобретение относитс к строитель вМ , материалам, в частности к состаijjaM строительных растворов« используемых дл покрыти стеновых панелей и блоков.The invention relates to the builder of construction materials, materials, in particular, the construction mortars used for coating wall panels and blocks.
Известен строительный раствор дл отделки бетонных изделий, включающий f11, мае.%Known mortar for finishing concrete products, including f11, may.%
Цемент19 0-47,0Cement19 0-47,0
Песок47, 0-74,0Sand47, 0-74.0
Гипс0,25-2,0Gypsum 0.25-2.0
Активна минеральна добайка0 ,25-2,0Mineral mineral active, 25-2.0
Пигмент0,25-2,0Pigment 0.25-2.0
Казеиноцементный клей0,15-4,0Caseino-cement glue 0,15-4,0
Наиболее близким к предлагаемому по технической сущности и достигаемому результату вл етс строительный раствор дл покрыти бетонных из целий , .включающий f2, кг: Портландцемент М-40033 Микроасбест33 Мел технический26 Клей казеиновый3 Эмульси поливинилацетатна 50%-на или латекс СКС-бО 4 Недостатками растворов вл ютс недостаточные адгези и трещиностойкрсть покрыти .The closest to the proposed technical essence and the achieved result is a mortar for coating concrete of the target, including f2, kg: Portland cement M-40033 Microasbest33 Technological chalk26 Casein glue3 Polyvinyl acetate emulsion 50% or SCS-latex 4 Solutions of impurities insufficient adhesion and crack resistance of the coating.
Цель изобретени - повышение адгезии и трещиностойкости покрыти .The purpose of the invention is to increase the adhesion and crack resistance of the coating.
Поставленна цель достигаетс тем, что строительный раствор дл покрыти бетонных изделий, включанадий цеент , песок, минеральную добавку, асбестит и органический клей, содерит дополнительно известь гашенную, качестве минеральной добавки - моотый ваграночный грашлак, а в каестве органического кле - натриеую соль карбоксиМетилцеллюлозы при ледующем соотношении компонентов, ае.%:The goal is achieved by the fact that a mortar for coating concrete products, including cement, sand, mineral additive, asbestos and organic glue, additionally contains lime of slaked cupola grape slag, and as organic glue - sodium carboxymethylcellulose with the following the ratio of components, ae.%:
Цемент10-20Cement10-20
Песок45-66Sand45-66
Молотый ваграночный граншлак1-2 Асбестит 7-10 Натриева соль карбоксиметилцеллюлозы1-3Ground cupola slab1-2 Asbestos 7-10-10 Sodium carboxymethylcellulose salt 1-3
Известь гашенна 10-20Slaked lime 10-20
Молотый ваграночный граншлак литейного цеха имеет следующий состав, мас,%: МдО ,0; SiO,;35,6-44,2) СаО 14,9-36,3; МпО 1,9-16,4 FjO 1,0-11,1 А12 Оз- остальное.Ground cupola slag foundry has the following composition, wt.%: MDO, 0; SiO; 35.6-44.2) CaO 14.9-36.3; MpO 1.9-16.4 FjO 1.0-11.1 A12 Oz - the rest.
Асбестит представл ет собой продукт обогащени асбестовых руд, содержащих минерал - хризотил-асбест, который вл етс гидросиликатом магни ,Asbestos is an enrichment product for asbestos ores containing the mineral, chrysotile asbestos, which is magnesium hydrosilicate,
Химический состав асбеста соответствует теоретической формуле ЗМдО «СЗЮ 2Н2О. Дл приготовлени раствора смешивают цемент М-400 с известью гашенной в соотношении 1:1 по массе. Строительный раствор готоь т в смесителе СБ-43, куда загружают сухие компоненты и тщательно перемешивают . Воду ввод т в строительный раствор до получени водов жущего отношени 0,42. Затем раствор под давлением 2-3 атм нанос т с помощью писто .летного распылител на поверхность чеистого бетонного издели . Толщина покрыти после трехфазового нанесени раствора составл ет 6 мм.The chemical composition of asbestos corresponds to the theoretical formula ZMdO “SZYu 2N2O. To prepare the solution, cement M-400 is mixed with hydrated lime in a 1: 1 ratio by weight. The mortar is prepared in the SB-43 mixer, where the dry ingredients are loaded and mixed thoroughly. Water is introduced into the mortar until a water ratio of 0.42 is obtained. Then the solution under pressure of 2-3 atm is applied with a spray gun to the surface of the cellular concrete product. The thickness of the coating after the three phase application of the solution is 6 mm.
Конкретные примеры выполнени и физико-механические показатели приве- дены в таблицах 1 и 2.Specific examples of performance and physico-mechanical parameters are given in Tables 1 and 2.
Таблична 1Table 1
Количественное содержание Quantitative content
Компоненкомпонентов , мае.%: тыComponent components, May.%: You
40 Цемент 10 20 14,5 12,5 13,540 Cement 10 20 14.5 12.5 13.5
14,5 12,5 13,5 10 20 59,5 666414.5 12.5 13.5 10 20 59.5 6664
65 4565 45
1,5 I 22 871.5 I 22 87
10 10 3310 10 33
Таблица 2table 2
Примечёнив} Noting}
Предлагаемый строительный раствор :позвол ет получить покрытие с повышенной адгезией и трециностойксютыо.The proposed mortar: allows you to get a coating with increased adhesion and tretsinotoksyutyuto.
чт6 дает возможное-л : увеличить долговечность бетонного издели на 14-16%.. Адгезию покрыти к поверхности бетона определ ют мёФЬ, дои отрыва покрыти после 14 дней хранени при 18: 2jOfC; и влажности 60%, а устойчивость к разрыву по . не в бетоне - методом раст жени покрыти при изгибе образца до образовани в изделии.cht6 gives a possible l: increase the durability of the concrete product by 14-16%. Adhesion of the coating to the surface of the concrete is determined by MEAT, before the separation of the coating after 14 days of storage at 18: 2jOfC; and humidity 60%, and resistance to rupture by. not in concrete — by stretching a specimen by bending the specimen before it forms in the product.
Claims (1)