SU903331A1 - Binder - Google Patents
Binder Download PDFInfo
- Publication number
- SU903331A1 SU903331A1 SU802933029A SU2933029A SU903331A1 SU 903331 A1 SU903331 A1 SU 903331A1 SU 802933029 A SU802933029 A SU 802933029A SU 2933029 A SU2933029 A SU 2933029A SU 903331 A1 SU903331 A1 SU 903331A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- portland cement
- agloporite
- granulated blast
- fine ground
- roads
- Prior art date
Description
Изобретение относитс к строительным материалам и может быть использовано дл обработки крупнообломочных и песчаных грунтов и каменных мат.ериалов при строительстве автомобильных дорог. Известно в жущее, содержащее портландцемеНт и активные минеральные добавки 1. Наиболее близким к изобретению в л етс в жущее 2 дл строительств автомобильных дорог, состо щее из следуюпдах компонентов, мас.%: Портландцемент 15-29 Тонкомолотый аглопорит 71-85 Недостатком такого в жущего вл етс сравнительно высокое содержание портландцемента и, соответственно, повышенна стоимость. Цель изобретени -.снижение расхр да портландцемента при сохранении свойств в жущего. Поставленна цель достигаетс тем что в жущее, включающее портландцемент и -тонкомолотый аглопорит, допол нительно содержит гранулированный до енный шлак при следующем соотношении компонентов, мас.% Портландцемент 5-10 Гранулированный доменный шлак15-20 Тонкомолотый аглопоритОстальное Примеры осуществлени изобретени . Используют портландцемент, аглопорит и Гранулированный доменный шлак, тонкомолотые до удельной поверхности 3000 и 5000 . Готов т растворные смеси 1:3 (в жущее - Вольский песок) и образцы методом прессовани под давлением 15,0 МПа при оптимальной влажности. Образцы хра-« н т в услови х воздушно-влажного твердени и испытыбают на прочность , в 28-суточном возрасте. Результаты испытаний приведены в таблица №1. Как видно из таблицы, содержание, в в жущем в качестве тонкомолотого до SNA 5000 компонента смеси аглопорита 70-80 мас.% и гранулированного доменного шлака 15-20 мас.% обеспечивает получение предела прочности при 100ilO na 39033314 сжатии в пределах 50-10 Па держание портландцемента по сравнеи одновременно снижает со- нию с извнстным в жущим.The invention relates to building materials and can be used for treating coarse and sandy soils and stone materials in the construction of roads. It is known to be stingy, containing Portland cement and active mineral additives 1. The closest to the invention is stranded 2 for the construction of roads, consisting of the following components, wt%: Portland cement 15-29 Fine agloporite 71-85 The disadvantage of this stitching is a relatively high content of portland cement and, accordingly, an increased cost. The purpose of the invention is to reduce the dissolution of Portland cement while maintaining the properties of a binder. This goal is achieved by the fact that the holding, including Portland cement and finely ground agloporite, additionally contains granulated reclaimed slag in the following ratio of components, wt% Portland cement 5-10 Granulated blast furnace slag15-20 Fine ground aglospinalum. Use Portland cement, agloporite and granulated blast furnace slag, fine ground to a specific surface of 3000 and 5000. Prepare mortar mixes of 1: 3 (in the slant - Volsky sand) and samples by pressing under pressure of 15.0 MPa at optimum humidity. Samples are stored in air-wet conditions and are tested for strength at 28 days of age. The test results are shown in Table 1. As can be seen from the table, the content, in the component of the mixture of agloporite 70–80 wt. Keeping Portland cement at the same time reduces sedation to imitated cement.
Claims (2)