SU386870A1 - METHOD OF MANUFACTURING OF FARFORO-FAYANS PRODUCTS - Google Patents
METHOD OF MANUFACTURING OF FARFORO-FAYANS PRODUCTSInfo
- Publication number
- SU386870A1 SU386870A1 SU1679467A SU1679467A SU386870A1 SU 386870 A1 SU386870 A1 SU 386870A1 SU 1679467 A SU1679467 A SU 1679467A SU 1679467 A SU1679467 A SU 1679467A SU 386870 A1 SU386870 A1 SU 386870A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- products
- drying
- carried out
- manufacturing
- fayans
- Prior art date
Description
1one
Изобретение относитс к керамической промышленности и может быть использовано при изготовлении фарфоро-фа нсовых изделий.The invention relates to the ceramics industry and can be used in the manufacture of porcelain and faences.
Известны два способа изготовлени фарфоро-фа нсовых изделий: метод пластического формовани и метод лить . В обоих случа х используют гипсовые формы, позвол ющие также осуществл ть процесс суплки при Температуре не более 60°С. В гипсовых формах производ т предварительную и окончательную сушку, после чего издели извлекают из них и направл ют на досушку.There are two known methods for making porcelain-façade products: plastic molding and casting. In both cases, plaster molds are used, which also allow the process of addition to be performed at a temperature of not more than 60 ° C. In the plaster molds, preliminary and final drying is carried out, after which the products are removed from them and sent for drying.
После предварительной сушки издели , извлеченные из форм, вторично подвергают тепловой обработке дл удалени влаги. Затем на специальных керамических подставках издели направл ют «а обжиг.After pre-drying, the articles removed from the molds are again heat treated to remove moisture. Then, on special ceramic coasters, the products are directed and burned.
Цель изобретени - интенсифицировать технологический процесс.The purpose of the invention is to intensify the process.
Это достигаетс тем, что сушку и первичный обжиг заготовки осуществл ют непосредственно в формах, в которых издели формуют . Кроме того, формование, сушку и первичный обжиг заготовки осуществл ют в форме Из массы на основе шлакоситалла и глины.This is achieved in that the drying and primary firing of the preform are carried out directly in the molds in which the articles are molded. In addition, the molding, drying and primary firing of the billet are carried out in the form of a mass based on slakositall and clay.
Предлагаемый способ осуществл етс следующим образом.The proposed method is carried out as follows.
Фарфоро-фа нсовые издели имеют сложную геометрическую конфигурацию. Формование изделий производ т в сложные формы, изготовленные из массы, содержащей Щлакоситалл 50-90% и огнеупорную глину 10-50%. Эти формы обладают необходимой всасываюш ,ей способностью и высокой механической прочностью. Отформованные пластическим методом или шликерным литьем издели подвергают сушке в форме при температуре до 200°С.Porcelain-faissa products have a complex geometric configuration. Products are molded into complex shapes made from a mass containing 50–90% Shlacocosital and 10–50% refractory clay. These forms have the necessary absorption, ability and high mechanical strength. Molded by plastic method or slip casting the product is dried in the mold at a temperature of up to 200 ° C.
Затем эти формы с издели ми поступают на первичный обжиг, температура которого 750- 800°С. Зачистку изделий производ т после первичного обжига. Последующие операции ведут по обычной технологии изготовлени фарфоро-фа нсовых изделий.Then, these forms with products come to primary calcination, the temperature of which is 750-800 ° C. The stripping of the products is made after the primary roasting. Subsequent operations are carried out according to the usual technology of manufacturing porcelain-façade products.
Предмет изобретенийSubject of inventions
Claims (2)