SU1377253A1 - Method of producing metal-glass articles - Google Patents
Method of producing metal-glass articles Download PDFInfo
- Publication number
- SU1377253A1 SU1377253A1 SU853927608A SU3927608A SU1377253A1 SU 1377253 A1 SU1377253 A1 SU 1377253A1 SU 853927608 A SU853927608 A SU 853927608A SU 3927608 A SU3927608 A SU 3927608A SU 1377253 A1 SU1377253 A1 SU 1377253A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- glass
- metal
- glass articles
- producing metal
- heat treatment
- Prior art date
Description
Изобретение относитс к формированию проходных изол торов и их соединений с металлической арматурой в корпусах микросхем.This invention relates to the formation of bushing insulators and their connections with metal fittings in microcircuit cases.
Целью изобретени вл етс повышение качества проходных изол торов.The aim of the invention is to improve the quality of bushing insulators.
Изготовление проходных изол торов осуществл ют следующим образом.The manufacture of bushing insulators is carried out as follows.
Выводы и основани собирают в специальную пресс-форму со строго заданным и отвечакицим требуемой конструкции корпуса объемом, затем методом лить под давлением (3-4 атм) места соединени металлических деталей заполн ют шликером при. 65-70°С, т.е. формируют внешний вид проходного изол тора . При этом шликер подаетс в требуемые места под давлением, в результате уменьшаетс веро тность образовани незаполненных объемов, вследствие чего повьш1аетс надежност корпуса.Conclusions and bases are assembled into a special mold with a strictly defined volume and volume of the required body design, then the method of casting under pressure (3-4 atm) of the junction of metal parts is filled with a slip at. 65-70 ° C, i.e. form the appearance of the bushing. In this case, the slip is supplied to the required places under pressure, as a result, the probability of the formation of unfilled volumes is reduced, as a result of which the body becomes more reliable.
Шликер может быть приготовлен из 87 мае.% .стекл нного порошка, размолотого в шаровой мельнице в течение 16 ч, 12,5 мас.% парафина и 0,5 мае.% олеиновой кислоты.The slip can be prepared from 87% by weight of glass powder ground in a ball mill for 16 hours, 12.5% by weight of paraffin and 0.5% by weight of oleic acid.
После охлаждени сформированного узла последний подвергают термообработке дл удалени технологической св зки.After cooling the formed unit, the latter is heat treated to remove the process binder.
При последующей термообработке провод т формирование спа , а также геометрических размеров проходного изол тора . Удаление св зки производ т на воздухе при постепенном подъёме температуры от комнатной до температуры спекани черепка, которую выбирают на 20-30 С выше температуры начала разм гчени примен емого стекла Спаивание стекла с металлом ведут при 970-990 С, при этом геометрические размеры проходного изол тора сов даютс без строго заданного объема, что позвол ет отказатьс от применени графитовых кассет.During the subsequent heat treatment, the spa is formed as well as the geometric dimensions of the bushing insulator. Binding is removed in air with a gradual rise in temperature from room temperature to the sintering temperature of the shard, which is chosen 20-30 ° C above the temperature of the beginning of softening of the glass used. Soldering the glass with metal is carried out at 970-990 ° C, while Tori are given without a strictly specified volume, which allows refusing the use of graphite cassettes.
00
5five
00
5five
Пример 1. Выводы и основание из ковара подвергают обезжириванию и травлению. Производ т сборку их в специальную разъемную форму, затем методом лить под давлением 4 атм заполн ют основание шликером на основе стекла С 52-1 при 65-70 С, Затем изол торы извлекают из формы, помещают в адсорбент (А1,0) и на воздухе в интервале температур 20-600 С подвергают термообработке. Скорость подъема температуры 30 /ч. Спаивание изол торов осуществл ют в конвейерной печи СК-11 в среде азота при 990 С с вьщержкой в зоне максимальной температуры 15 мин. Спаивание провод т в металлических кассетах дл фиксации выводов.Example 1. Conclusions and the basis of Kovar is subjected to degreasing and etching. They are assembled into a special split mold, then the base is cast with a pressure of 4 atm. The base is filled with a C 52-1 glass slip at 65-70 ° C. Then the insulators are removed from the mold, placed in an adsorbent (A1.0) and air in the temperature range of 20-600 C is subjected to heat treatment. Temperature rise rate 30 / h. Insulators are soldered in a CK-11 conveyor furnace in a nitrogen atmosphere at 990 ° C with vyderzhka in the zone of maximum temperature for 15 minutes. Soldering is carried out in metal cassettes for fixing the leads.
Пример2. Подготовительные операции те же, что и в примере 1. Спаивание осуществл ют при 970 С с вьщержкой в зоне максимальной температуры 20 мин.Example2. The preparatory operations are the same as in example 1. Soldering is carried out at 970 ° C with a booster in the zone of maximum temperature for 20 minutes.
Изготовленные согласно предлагае - мому способу проходные изол торы неThe bushing insulators manufactured according to the proposed method are not
00
5five
00
5five
имеют трещин.have cracks.
отлипаний и натекани detachment and leakage
-1-3 - -1-3 -
гели . Узлы герметичны м Па-с имеют высокую механическую прочность и вьщерживают испытание на термоцик- лирование 10 циклов.gels The assemblies sealed m Pa-s have high mechanical strength and impose a 10-cycle thermocycling test.
Claims (1)