SU1181337A1 - Electrolyte for deposition of niobium coatings - Google Patents

Electrolyte for deposition of niobium coatings Download PDF

Info

Publication number
SU1181337A1
SU1181337A1 SU823465708A SU3465708A SU1181337A1 SU 1181337 A1 SU1181337 A1 SU 1181337A1 SU 823465708 A SU823465708 A SU 823465708A SU 3465708 A SU3465708 A SU 3465708A SU 1181337 A1 SU1181337 A1 SU 1181337A1
Authority
SU
USSR - Soviet Union
Prior art keywords
dimethylformamide
electrolyte
niobium
methanol
dichloride
Prior art date
Application number
SU823465708A
Other languages
Russian (ru)
Inventor
Ю.И. Микшис
П.П. Кентра
Б.А. Книжников
Ю.А. Ольдекоп
Original Assignee
Ордена Трудового Красного Знамени Институт Химии И Химической Технологии Ан Литсср
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ордена Трудового Красного Знамени Институт Химии И Химической Технологии Ан Литсср filed Critical Ордена Трудового Красного Знамени Институт Химии И Химической Технологии Ан Литсср
Priority to SU823465708A priority Critical patent/SU1181337A1/en
Application granted granted Critical
Publication of SU1181337A1 publication Critical patent/SU1181337A1/en

Abstract

ЭЛЕКТРОЛИТ ДЛЯ ОСАЖДЕНИЯ НИОБИЕБЫХ ПОКРЫТИЙ, содержащий ионы .ниоби , соль натри  и растворитель, отличающийс  тем, что. с целью повьшени  выхода по току, он в качестве ионов ниоби , содержит дициклопентадиенилниобийдихлорид , а в качестве соли натри  и растворител  соответственно перхлорат натри  и диметилформамид imH смесь диметилформамида с метанолом при соотношении 4:1 - 20:1 по объему при следующем соотношении компонентов , г/л: Дициклопентадиенилниобийдихлорид 5-10 Перхлорат натри  10-50 Диметилформамид или смесь диметилформаS мида с метанолом До 1 л (ЛELECTROLYTE FOR DEPOSITION OF NIOBILE COATINGS, containing niobium ions, sodium salt and a solvent, characterized in that. in order to increase current efficiency, it contains dicyclopentadienylniobium dichloride as niobium ions, and sodium perchlorate and dimethylformamide imH mixture of dimethylformamide and methanol as a sodium salt and solvent, respectively, at a ratio of 4: 1 to 20: 1 by volume with the following ratio of components, g / l: Dicyclopentadienylniobium dichloride 5-10 Sodium perchlorate 10-50 Dimethylformamide or a mixture of dimethylformaSide with methanol To 1 L (L

Description

со ее Изобретение относитс  к гальваностегии , в частности к электроосаждению ниобиевых покрытий и может быть использавано в электронной технике и приборостроении. Цепью изобретени   вл етс  повышение выхода по току. Положительньм эффект достигаетс  за счет введени  в электролит в качестве источника ионов ниоби  дицик лопентадиенилниобийдихлорида, а в качестве соли натри  и растворител  соответственно перхлората натри  и диметилформамида или емеси диметилформамида с метанолом.. Состав дициклопентадиенилниобийдихлорида может быть представлен следующей структурной формулой 5T-(C2H5)2NbCl2 Электролит готов т следующим об 72 Расчетное количество дициклопентадиенилниобийдихлорида раствор ют в диметилформамиде или смеси диметилформамида с метанолом и добавл ют перхлорат натри . Процесс электроосаждени  проводитс  при температуре 20 - 40 С и катодной плотности тока 0,05 0 ,05 А/дм в течение 0,25-2 ч. Потенциал катода при этом имеет значение 0,9-1,5 В (относительно насы- щенного каломельного электрода). В качестве материала катода используют медь, платину, графит, а в качестве анода - графит. Соотношение площадей катода и анода составл ет 1:2-10. В процессе электролиза через электролит пропускают инертный газ - азот. Перед электроосаждением провод т электрохимическую проработку электролита при плотности тока 0,15 - 5 А/дм. Количество пропускаемого электричества составл ет 1-25 А-ч/л. Изобретение может быть проиллюстIts invention relates to electroplating, in particular to the electroplating of niobium coatings and can be used in electronic engineering and instrument-making. The circuit of the invention is an increase in current efficiency. The positive effect is achieved by introducing niobium dicyclopentadienylniobium dichloride into the electrolyte as a source of ions, and as a sodium salt and solvent, respectively, sodium perchlorate and dimethylformamide or a mixture of dimethylformamide with methanol. Prepared as follows: 72 Calculated amount of dicyclopentadienylniobium dichloride is dissolved in dimethylformamide or a mixture of dimethylformamide and methanol and sodium perchlorate is added. The process of electroplating is carried out at a temperature of 20–40 ° C and a cathode current density of 0.05–0.05 A / dm for 0.25–2 h. The potential of the cathode is 0.9–1.5 V (relative to the saturated calomel electrode). Copper, platinum, graphite are used as the cathode material, and graphite is used as the anode. The ratio of the cathode and anode areas is 1: 2-10. In the process of electrolysis an inert gas — nitrogen — is passed through the electrolyte. Before electroplating, an electrolytic electrolyte study is carried out at a current density of 0.15 - 5 A / dm. The amount of electricity transmitted is 1-25 Ah. The invention can be illustrated

Металлический ниобийMetal niobium

4040

ДициклопентадиеНИЛниобийдихлоридDicyclopentadieneNILniobium dichloride

Гидроксид натри Sodium hydroxide

70 1570 15

Хлорид натри Sodium chloride

Перхлорат натри Sodium perchlorate

ГлицеринGlycerol

До лTill l

МетанолMethanol

Диме тилформамидDima Tilformamide

Потенциал катода. В: при электроосажденииThe potential of the cathode. B: during electrodeposition

5050

150150

5050

30thirty

10ten

150 150

До л До лTo l to l

До лTill l

0,950.95

0,980.98

Катодна  плотность тока, .Cathode current density,.

при проработкеwhile working

при электроосажденииduring electrodeposition

Продолжительность электролиза , ч:Duration of electrolysis, h:

Продолжение таблицыTable continuation

5 0,45 0.4

5 0,25 0,2

5 0,15 0.1

Claims (1)

ЭЛЕКТРОЛИТ ДЛЯ ОСАЖДЕНИЯ НИОБИЕВЫХ ПОКРЫТИЙ, содержащий ионы ниобия, соль натрия и растворитель, отличающийся тем, что, с целью повышения выхода по току, он в качестве ионов ниобия, содержит дициклопентадиенилниобийдихло— рид, а в качестве соли натрия и растворителя соответственно перхлорат натрия и диметилформамид или смесь диметилформамида с метанолом при соотношении 4:1 - 20:1 по объему при следующем соотношении компонентов , г /л:ELECTROLYTE FOR DEPOSITION OF NIOBIUM COATINGS, containing niobium ions, sodium salt and solvent, characterized in that, in order to increase current efficiency, it contains dicyclopentadienylniobium dichloride as niobium ions, and sodium perchlorate and dimethylformamide as sodium salt and solvent, respectively or a mixture of dimethylformamide with methanol in a ratio of 4: 1 to 20: 1 by volume in the following ratio of components, g / l: . Дициклопентадиенил-. Dicyclopentadienyl- ниобийдихлорид niobium dichloride 5-10 5-10 Перхлорат натрия Диметилформамид или Sodium Perchlorate Dimethylformamide or 10-50 10-50 смесь диметилформа- a mixture of dimethylform <0 <0 мида с метанолом mida with methanol До 1 л Up to 1 liter (Л с (L s
Q0Q0 СО соSO with
SU823465708A 1982-07-07 1982-07-07 Electrolyte for deposition of niobium coatings SU1181337A1 (en)