Composition for forming silicon-containing resist underlayer film removable by wet process

Info

Publication number
SG11201703607RA
SG11201703607RA SG11201703607RA SG11201703607RA SG11201703607RA SG 11201703607R A SG11201703607R A SG 11201703607RA SG 11201703607R A SG11201703607R A SG 11201703607RA SG 11201703607R A SG11201703607R A SG 11201703607RA SG 11201703607R A SG11201703607R A SG 11201703607RA
Authority
SG
Singapore
Prior art keywords
composition
underlayer film
wet process
resist underlayer
forming silicon
Prior art date
Application number
SG11201703607RA
Other languages
English (en)
Inventor
Hiroyuki Wakayama
Makoto Nakajima
Wataru Shibayama
Masahisa Endo
Original Assignee
Nissan Chemical Ind Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nissan Chemical Ind Ltd filed Critical Nissan Chemical Ind Ltd
Publication of SG11201703607RA publication Critical patent/SG11201703607RA/en

Links

Classifications

    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/004—Photosensitive materials
    • G03F7/09—Photosensitive materials characterised by structural details, e.g. supports, auxiliary layers
    • G03F7/11—Photosensitive materials characterised by structural details, e.g. supports, auxiliary layers having cover layers or intermediate layers, e.g. subbing layers
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/004—Photosensitive materials
    • G03F7/075—Silicon-containing compounds
    • G03F7/0752—Silicon-containing compounds in non photosensitive layers or as additives, e.g. for dry lithography
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
    • C09D183/02—Polysilicates
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
    • C09D183/04—Polysiloxanes
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
    • C09D183/04—Polysiloxanes
    • C09D183/06—Polysiloxanes containing silicon bound to oxygen-containing groups
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D4/00—Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/004—Photosensitive materials
    • G03F7/075—Silicon-containing compounds
    • G03F7/0757—Macromolecular compounds containing Si-O, Si-C or Si-N bonds
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/004—Photosensitive materials
    • G03F7/09—Photosensitive materials characterised by structural details, e.g. supports, auxiliary layers
    • G03F7/091—Photosensitive materials characterised by structural details, e.g. supports, auxiliary layers characterised by antireflection means or light filtering or absorbing means, e.g. anti-halation, contrast enhancement
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/20—Exposure; Apparatus therefor
    • G03F7/2002—Exposure; Apparatus therefor with visible light or UV light, through an original having an opaque pattern on a transparent support, e.g. film printing, projection printing; by reflection of visible or UV light from an original such as a printed image
    • G03F7/2004—Exposure; Apparatus therefor with visible light or UV light, through an original having an opaque pattern on a transparent support, e.g. film printing, projection printing; by reflection of visible or UV light from an original such as a printed image characterised by the use of a particular light source, e.g. fluorescent lamps or deep UV light
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/26—Processing photosensitive materials; Apparatus therefor
    • G03F7/38—Treatment before imagewise removal, e.g. prebaking
    • G—PHYSICS
    • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
    • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
    • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
    • G03F7/26—Processing photosensitive materials; Apparatus therefor
    • G03F7/40—Treatment after imagewise removal, e.g. baking
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02107—Forming insulating materials on a substrate
    • H01L21/02109—Forming insulating materials on a substrate characterised by the type of layer, e.g. type of material, porous/non-porous, pre-cursors, mixtures or laminates
    • H01L21/02112—Forming insulating materials on a substrate characterised by the type of layer, e.g. type of material, porous/non-porous, pre-cursors, mixtures or laminates characterised by the material of the layer
    • H01L21/02123—Forming insulating materials on a substrate characterised by the type of layer, e.g. type of material, porous/non-porous, pre-cursors, mixtures or laminates characterised by the material of the layer the material containing silicon
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/027—Making masks on semiconductor bodies for further photolithographic processing not provided for in group H01L21/18 or H01L21/34
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer
    • H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic Table or AIIIBV compounds with or without impurities, e.g. doping materials
    • H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26
    • H01L21/31—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to form insulating layers thereon, e.g. for masking or by using photolithographic techniques; After treatment of these layers; Selection of materials for these layers
    • H01L21/3105—After-treatment
    • H01L21/311—Etching the insulating layers by chemical or physical means
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
    • C08G77/04—Polysiloxanes
    • C08G77/14—Polysiloxanes containing silicon bound to oxygen-containing groups

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • General Physics & Mathematics (AREA)
  • Organic Chemistry (AREA)
  • Wood Science & Technology (AREA)
  • Materials Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Architecture (AREA)
  • Structural Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Computer Hardware Design (AREA)
  • Power Engineering (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Manufacturing & Machinery (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • Spectroscopy & Molecular Physics (AREA)
  • Materials For Photolithography (AREA)
  • Silicon Polymers (AREA)
  • Photosensitive Polymer And Photoresist Processing (AREA)
  • Exposure And Positioning Against Photoresist Photosensitive Materials (AREA)
  • Drying Of Semiconductors (AREA)
  • Exposure Of Semiconductors, Excluding Electron Or Ion Beam Exposure (AREA)
SG11201703607RA 2014-11-19 2015-11-06 Composition for forming silicon-containing resist underlayer film removable by wet process SG11201703607RA (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014234591 2014-11-19
PCT/JP2015/081345 WO2016080217A1 (ja) 2014-11-19 2015-11-06 湿式除去が可能なシリコン含有レジスト下層膜形成組成物

Publications (1)

Publication Number Publication Date
SG11201703607RA true SG11201703607RA (en) 2017-06-29

Family

ID=56013763

Family Applications (1)

Application Number Title Priority Date Filing Date
SG11201703607RA SG11201703607RA (en) 2014-11-19 2015-11-06 Composition for forming silicon-containing resist underlayer film removable by wet process

Country Status (7)

Country Link
US (1) US11815815B2 (zh)
JP (1) JP6660023B2 (zh)
KR (1) KR102439087B1 (zh)
CN (1) CN107077072B (zh)
SG (1) SG11201703607RA (zh)
TW (1) TWI691560B (zh)
WO (1) WO2016080217A1 (zh)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102570307B1 (ko) * 2016-10-31 2023-08-25 주식회사 이엔에프테크놀로지 식각 조성물
JP6899220B2 (ja) * 2017-01-11 2021-07-07 株式会社ダイセル レジスト除去用組成物
CN110494807A (zh) * 2017-03-31 2019-11-22 日产化学株式会社 具有羰基结构的含有硅的抗蚀剂下层膜形成用组合物
JP6853716B2 (ja) * 2017-03-31 2021-03-31 信越化学工業株式会社 レジスト下層膜材料、パターン形成方法、及びレジスト下層膜形成方法
JP7157392B2 (ja) * 2017-07-06 2022-10-20 日産化学株式会社 アルカリ性現像液可溶性シリコン含有レジスト下層膜形成組成物
TWI653263B (zh) * 2017-08-04 2019-03-11 日商信越化學工業股份有限公司 Substrate with multilayer resist film and pattern forming method
JP7185189B2 (ja) * 2017-10-25 2022-12-07 日産化学株式会社 アンモニウム基を有する有機基を含むシリコン含有レジスト下層膜形成組成物を用いる半導体装置の製造方法
KR20200132864A (ko) * 2018-03-19 2020-11-25 닛산 가가쿠 가부시키가이샤 보호된 페놀기와 질산을 포함하는 실리콘함유 레지스트 하층막 형성 조성물
JPWO2020138189A1 (ja) * 2018-12-27 2021-11-18 日産化学株式会社 膜形成用組成物
KR102053921B1 (ko) * 2019-03-13 2019-12-09 영창케미칼 주식회사 반도체 제조 공정에 있어서 식각 패턴 신규 형성 방법
KR20220143055A (ko) * 2020-02-19 2022-10-24 도쿄엘렉트론가부시키가이샤 기판 처리 방법 및 기판 처리 시스템
JPWO2021201167A1 (zh) * 2020-03-31 2021-10-07
WO2022210901A1 (ja) * 2021-03-31 2022-10-06 日産化学株式会社 シリコン含有レジスト下層膜形成用組成物
WO2023157772A1 (ja) * 2022-02-16 2023-08-24 日産化学株式会社 保護膜形成用組成物

Family Cites Families (47)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11258813A (ja) 1998-03-13 1999-09-24 Jsr Corp 反射防止膜形成用組成物および反射防止膜
US6730454B2 (en) 2002-04-16 2004-05-04 International Business Machines Corporation Antireflective SiO-containing compositions for hardmask layer
JP4072643B2 (ja) * 2002-11-08 2008-04-09 Ｊｓｒ株式会社 レジスト下層膜用組成物
AU2003302526A1 (en) * 2002-12-02 2004-06-23 Tokyo Ohka Kogyo Co., Ltd. Composition for forming antireflection coating
JP4244315B2 (ja) * 2002-12-02 2009-03-25 東京応化工業株式会社 レジストパターン形成用材料
KR100857967B1 (ko) * 2003-06-03 2008-09-10 신에쓰 가가꾸 고교 가부시끼가이샤 반사 방지막 재료, 이것을 이용한 반사 방지막 및 패턴형성 방법
JP2005173552A (ja) 2003-11-20 2005-06-30 Tokyo Ohka Kogyo Co Ltd リソグラフィー用下層膜形成材料およびこれを用いた配線形成方法
JP4340167B2 (ja) * 2004-02-03 2009-10-07 信越化学工業株式会社 珪素含有レジスト下層膜材料及びパターン形成方法
JP4553835B2 (ja) 2005-12-14 2010-09-29 信越化学工業株式会社 反射防止膜材料、及びこれを用いたパターン形成方法、基板
JP4659678B2 (ja) * 2005-12-27 2011-03-30 信越化学工業株式会社 フォトレジスト下層膜形成材料及びパターン形成方法
CN100498543C (zh) * 2006-01-25 2009-06-10 中芯国际集成电路制造(上海)有限公司 将背面曝光用于嵌入式相移掩模聚焦离子束蚀刻的方法
JP4600678B2 (ja) * 2006-02-13 2010-12-15 信越化学工業株式会社 レジスト組成物並びにこれを用いたパターン形成方法
CN101517487B (zh) * 2006-09-25 2012-08-08 日立化成工业株式会社 放射线敏感性组合物、二氧化硅系覆膜的形成方法、二氧化硅系覆膜、具有二氧化硅系覆膜的装置和部件以及绝缘膜用感光剂
KR100896451B1 (ko) * 2006-12-30 2009-05-14 제일모직주식회사 카본 함량이 개선된 고 내에칭성 반사방지 하드마스크조성물, 이를 이용한 패턴화된 재료 형상의　제조방법
JP2008277748A (ja) * 2007-03-30 2008-11-13 Renesas Technology Corp レジストパターンの形成方法とその方法により製造した半導体デバイス
US20090042133A1 (en) * 2007-08-10 2009-02-12 Zhong Xiang Antireflective Coating Composition
JP4946787B2 (ja) 2007-10-22 2012-06-06 Ｊｓｒ株式会社 レジスト下層膜用組成物及びその製造方法
JP4793592B2 (ja) * 2007-11-22 2011-10-12 信越化学工業株式会社 金属酸化物含有膜形成用組成物、金属酸化物含有膜、金属酸化物含有膜形成基板及びこれを用いたパターン形成方法
KR101524712B1 (ko) * 2007-11-30 2015-06-01 닛산 가가쿠 고교 가부시키 가이샤 블록화 이소시아네이트기를 갖는 실리콘 함유 레지스트 하층막 형성 조성물
JP5015892B2 (ja) 2008-10-02 2012-08-29 信越化学工業株式会社 ケイ素含有膜形成用組成物、ケイ素含有膜形成基板及びパターン形成方法
JP5446648B2 (ja) * 2008-10-07 2014-03-19 信越化学工業株式会社 パターン形成方法
JP4790786B2 (ja) * 2008-12-11 2011-10-12 信越化学工業株式会社 塗布型ケイ素含有膜の剥離方法
CN102498440B (zh) 2009-09-16 2016-11-16 日产化学工业株式会社 含有具有磺酰胺基的硅的形成抗蚀剂下层膜的组合物
JP5062352B2 (ja) * 2010-09-09 2012-10-31 Ｊｓｒ株式会社 レジストパターン形成方法
SG192113A1 (en) 2011-01-24 2013-08-30 Nissan Chemical Ind Ltd Composition for forming resist underlayer film, containing silicon that bears diketone-structure-containing organic group
JP5785121B2 (ja) * 2011-04-28 2015-09-24 信越化学工業株式会社 パターン形成方法
JP5650086B2 (ja) * 2011-06-28 2015-01-07 信越化学工業株式会社 レジスト下層膜形成用組成物、及びパターン形成方法
JP5453361B2 (ja) * 2011-08-17 2014-03-26 信越化学工業株式会社 ケイ素含有レジスト下層膜形成用組成物、及びパターン形成方法
US9337052B2 (en) * 2011-10-06 2016-05-10 Nissan Chemical Industries, Ltd. Silicon-containing EUV resist underlayer film forming composition
JPWO2013080929A1 (ja) * 2011-12-01 2015-04-27 Jsr株式会社 多層レジストプロセスに用いられるレジスト下層膜形成用組成物、レジスト下層膜及びその形成方法、並びにパターン形成方法
CN104081282B (zh) * 2012-02-01 2019-07-30 日产化学工业株式会社 使用溶剂显影用形成含硅抗蚀剂下层膜的组合物的半导体装置的制造方法
JP5882776B2 (ja) * 2012-02-14 2016-03-09 信越化学工業株式会社 レジスト下層膜形成用組成物、及びパターン形成方法
JP6120013B2 (ja) * 2012-04-23 2017-04-26 日産化学工業株式会社 添加剤を含むケイ素含有ｅｕｖレジスト下層膜形成組成物
JP5642731B2 (ja) * 2012-04-27 2014-12-17 信越化学工業株式会社 パターン形成方法
JP5710546B2 (ja) * 2012-04-27 2015-04-30 信越化学工業株式会社 パターン形成方法
KR102307204B1 (ko) * 2012-07-30 2021-10-01 닛산 가가쿠 가부시키가이샤 설폰산오늄염을 함유하는 규소함유 euv 레지스트 하층막 형성 조성물
KR102139092B1 (ko) * 2012-09-24 2020-07-29 닛산 가가쿠 가부시키가이샤 헤테로원자를 갖는 환상유기기함유 실리콘함유 레지스트 하층막 형성조성물
JP5829994B2 (ja) * 2012-10-01 2015-12-09 信越化学工業株式会社 パターン形成方法
US8999625B2 (en) * 2013-02-14 2015-04-07 International Business Machines Corporation Silicon-containing antireflective coatings including non-polymeric silsesquioxanes
JP6215777B2 (ja) * 2013-06-27 2017-10-18 信越化学工業株式会社 塗布型ｂｐｓｇ膜形成用組成物、該組成物で膜を形成した基板、及び前記組成物を用いたパターン形成方法
JP6327484B2 (ja) * 2013-10-07 2018-05-23 日産化学工業株式会社 ポリ酸を含むメタル含有レジスト下層膜形成組成物
KR102314080B1 (ko) * 2014-06-17 2021-10-18 닛산 가가쿠 가부시키가이샤 페닐기 함유 크로모퍼를 갖는 실리콘 함유 레지스트 하층막 형성 조성물
JP6250514B2 (ja) * 2014-10-03 2017-12-20 信越化学工業株式会社 塗布型ｂｐｓｇ膜形成用組成物、基板、及びパターン形成方法
US10845703B2 (en) * 2014-11-19 2020-11-24 Nissan Chemical Industries, Ltd. Film-forming composition containing silicone having crosslinking reactivity
US9580623B2 (en) * 2015-03-20 2017-02-28 Shin-Etsu Chemical Co., Ltd. Patterning process using a boron phosphorus silicon glass film
KR102587656B1 (ko) * 2015-06-11 2023-10-11 닛산 가가쿠 가부시키가이샤 감방사선성 조성물
US9442377B1 (en) * 2015-06-15 2016-09-13 Rohm And Haas Electronic Materials Llc Wet-strippable silicon-containing antireflectant

Also Published As

Publication number Publication date
TWI691560B (zh) 2020-04-21
JP6660023B2 (ja) 2020-03-04
CN107077072B (zh) 2021-05-25
KR20170086467A (ko) 2017-07-26
US20170371242A1 (en) 2017-12-28
CN107077072A (zh) 2017-08-18
US11815815B2 (en) 2023-11-14
TW201634615A (zh) 2016-10-01
JPWO2016080217A1 (ja) 2017-08-31
KR102439087B1 (ko) 2022-09-01
WO2016080217A1 (ja) 2016-05-26

Similar Documents

Publication Publication Date Title
SG11201703607RA (en) Composition for forming silicon-containing resist underlayer film removable by wet process
IL253109A0 (en) Compound, resin, material for the production of underlayer film for lithography, underlayer film for lithography, method of creating a pattern and method of cleaning
SG11201701945RA (en) Process for making cyclohexanone
GB201419807D0 (en) Method for estimating the occupancy of a parking lot
SG11201700443WA (en) Process for making cyclohexanone
SG11201701362UA (en) Coating composition for pattern reversal on soc pattern
SG11201609095VA (en) Material for forming film for lithography, composition for forming film for lithography, film for lithography, pattern forming method and purification method
SG11201701429SA (en) Process for making cyclohexanone
GB2529333B (en) Apparatus for printing onto objects
IL249664B (en) A process for creating thin inorganic layers
SG11201700298XA (en) Silicon-containing resist underlayer film forming composition having halogenated sulfonylalkyl group
SG11201605465SA (en) Composite sheet for protective-film formation
IL250145A0 (en) A process for creating thin inorganic layers
TWM489308U (en) Exposure machine
SG11201706378XA (en) Method for producing polarizing film
SG11201610188PA (en) Resist underlayer film-forming composition
GB201405335D0 (en) Resist composition
IL246810A0 (en) A process for producing thin inorganic layers
SG11201700801RA (en) Composition for forming underlayer film for lithography, underlayer film for lithography and pattern forming method
EP3127144A4 (en) Photo-masks for lithography
SG11201704448RA (en) Method for the wet deposition of thin films
FR3029930B1 (fr) Flanc pour pneumatique
FI20145416A (fi) Tulostusjärjestelmä
PT2923690T (pt) Composição para estabilizar compostos fotossensíveis
PL3113919T3 (pl) Sposób powlekania fragmentu powierzchni