SG10201707903VA - Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same - Google Patents
Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the sameInfo
- Publication number
- SG10201707903VA SG10201707903VA SG10201707903VA SG10201707903VA SG10201707903VA SG 10201707903V A SG10201707903V A SG 10201707903VA SG 10201707903V A SG10201707903V A SG 10201707903VA SG 10201707903V A SG10201707903V A SG 10201707903VA SG 10201707903V A SG10201707903V A SG 10201707903VA
- Authority
- SG
- Singapore
- Prior art keywords
- hot
- producing
- steel sheet
- same
- coated steel
- Prior art date
Links
- 229910000831 Steel Inorganic materials 0.000 title 1
- 229910001297 Zn alloy Inorganic materials 0.000 title 1
- 239000011248 coating agent Substances 0.000 title 1
- 238000000576 coating method Methods 0.000 title 1
- 238000004519 manufacturing process Methods 0.000 title 1
- 239000010959 steel Substances 0.000 title 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/002—Heat treatment of ferrous alloys containing Cr
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
- C21D8/0426—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
- C21D8/0473—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0478—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing involving a particular surface treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
- C22C18/04—Alloys based on zinc with aluminium as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/004—Dispersions; Precipitations
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Coating With Molten Metal (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Metal Rolling (AREA)
- Oil, Petroleum & Natural Gas (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013066576 | 2013-03-27 | ||
JP2014060809A JP5826321B2 (ja) | 2013-03-27 | 2014-03-24 | めっき密着性に優れた溶融亜鉛系めっき鋼板の製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
SG10201707903VA true SG10201707903VA (en) | 2017-11-29 |
Family
ID=51624126
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SG10201707903VA SG10201707903VA (en) | 2013-03-27 | 2014-03-25 | Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same |
SG11201507737QA SG11201507737QA (en) | 2013-03-27 | 2014-03-25 | Hot-dip zinc alloy coated steel sheet excellent in coatingadhesion, and method for producing the same |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SG11201507737QA SG11201507737QA (en) | 2013-03-27 | 2014-03-25 | Hot-dip zinc alloy coated steel sheet excellent in coatingadhesion, and method for producing the same |
Country Status (13)
Country | Link |
---|---|
US (1) | US9523142B2 (fr) |
EP (1) | EP2980259A4 (fr) |
JP (1) | JP5826321B2 (fr) |
KR (1) | KR102014062B1 (fr) |
CN (1) | CN105051238B (fr) |
AU (1) | AU2014245876B2 (fr) |
BR (1) | BR112015024016A2 (fr) |
CA (1) | CA2904131C (fr) |
MX (1) | MX366702B (fr) |
MY (1) | MY172243A (fr) |
NZ (1) | NZ711709A (fr) |
SG (2) | SG10201707903VA (fr) |
WO (1) | WO2014157155A1 (fr) |
Families Citing this family (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
MX2017008452A (es) | 2014-12-24 | 2017-11-09 | Posco | Material de acero emplacado con aleacion de zinc que tiene caracteristicas excelentes de soldado y resistencia a la corrosion de partes procesadas y metodo de manufactura del mismo. |
JP6209175B2 (ja) * | 2015-03-03 | 2017-10-04 | 日新製鋼株式会社 | めっき表面外観およびバーリング性に優れた溶融Zn−Al−Mg系めっき鋼板の製造方法 |
KR101736619B1 (ko) * | 2015-12-15 | 2017-05-17 | 주식회사 포스코 | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 |
KR102075182B1 (ko) | 2015-12-24 | 2020-02-10 | 주식회사 포스코 | 도금성이 우수한 고강도 용융 아연계 도금 강재 및 그 제조방법 |
KR102170060B1 (ko) | 2016-01-27 | 2020-10-26 | 제이에프이 스틸 가부시키가이샤 | 고항복비형 고강도 아연 도금 강판 및 그의 제조 방법 |
US10492602B2 (en) * | 2017-01-26 | 2019-12-03 | Bose Corporation | Electronics enclosure mounting |
JP7059091B2 (ja) | 2018-04-24 | 2022-04-25 | モレックス エルエルシー | 電子部品 |
TWI676508B (zh) * | 2018-05-18 | 2019-11-11 | 日商日本製鐵股份有限公司 | Al系鍍敷鋼板及其製造方法 |
CN114686651A (zh) * | 2020-12-31 | 2022-07-01 | 通用汽车环球科技运作有限责任公司 | 具有降低的液态金属致脆(lme)敏感性的锌涂覆的钢 |
CN113564483A (zh) * | 2021-08-06 | 2021-10-29 | 云南中科安居环保新材料有限公司 | 一种高强度轻钢别墅龙骨精品抗震钢材制备工艺 |
CN113751530B (zh) * | 2021-09-28 | 2024-03-26 | 攀钢集团攀枝花钢钒有限公司 | 一种用于冲压用热浸镀带钢镀层附着力检验的方法 |
WO2023238938A1 (fr) * | 2022-06-10 | 2023-12-14 | 日本製鉄株式会社 | Tôle d'acier trempée à chaud |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3715220B2 (ja) * | 2001-06-22 | 2005-11-09 | 日新製鋼株式会社 | 耐食性に優れたZn−Al−Mg系溶融めっき鋼材 |
JP4544579B2 (ja) | 2004-09-29 | 2010-09-15 | 日新製鋼株式会社 | 高強度溶融Zn−Al−Mg合金めっき鋼板の製造方法 |
JP4837459B2 (ja) | 2006-06-30 | 2011-12-14 | 新日本製鐵株式会社 | 外観が良好な耐食性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法 |
JP4781836B2 (ja) * | 2006-02-08 | 2011-09-28 | 新日本製鐵株式会社 | 耐水素脆性に優れた超高強度鋼板とその製造方法及び超高強度溶融亜鉛めっき鋼板の製造方法並びに超高強度合金化溶融亜鉛めっき鋼板の製造方法 |
US7608155B2 (en) * | 2006-09-27 | 2009-10-27 | Nucor Corporation | High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same |
JP5264234B2 (ja) * | 2008-03-24 | 2013-08-14 | 日新製鋼株式会社 | 耐溶融金属脆化割れ性に優れたZn−Al−Mg系めっき鋼板およびその製造方法 |
JP5391607B2 (ja) * | 2008-08-05 | 2014-01-15 | Jfeスチール株式会社 | 外観に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5672747B2 (ja) * | 2009-03-31 | 2015-02-18 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5660796B2 (ja) * | 2010-03-31 | 2015-01-28 | 日新製鋼株式会社 | 溶融亜鉛系めっき高張力鋼板の製造法 |
JP5495921B2 (ja) * | 2010-04-23 | 2014-05-21 | 日新製鋼株式会社 | 溶融亜鉛系めっき高張力鋼板の製造法 |
KR20130087593A (ko) * | 2010-11-26 | 2013-08-06 | 제이에프이 스틸 가부시키가이샤 | 용융 Al-Zn계 도금 강판 |
-
2014
- 2014-03-24 JP JP2014060809A patent/JP5826321B2/ja active Active
- 2014-03-25 AU AU2014245876A patent/AU2014245876B2/en active Active
- 2014-03-25 CN CN201480018101.XA patent/CN105051238B/zh active Active
- 2014-03-25 MY MYPI2015703363A patent/MY172243A/en unknown
- 2014-03-25 WO PCT/JP2014/058208 patent/WO2014157155A1/fr active Application Filing
- 2014-03-25 EP EP14774669.7A patent/EP2980259A4/fr not_active Withdrawn
- 2014-03-25 SG SG10201707903VA patent/SG10201707903VA/en unknown
- 2014-03-25 US US14/773,398 patent/US9523142B2/en active Active
- 2014-03-25 KR KR1020157024871A patent/KR102014062B1/ko active IP Right Grant
- 2014-03-25 SG SG11201507737QA patent/SG11201507737QA/en unknown
- 2014-03-25 CA CA2904131A patent/CA2904131C/fr active Active
- 2014-03-25 NZ NZ711709A patent/NZ711709A/en not_active IP Right Cessation
- 2014-03-25 BR BR112015024016A patent/BR112015024016A2/pt not_active Application Discontinuation
- 2014-03-25 MX MX2015013368A patent/MX366702B/es active IP Right Grant
Also Published As
Publication number | Publication date |
---|---|
KR102014062B1 (ko) | 2019-08-27 |
BR112015024016A2 (pt) | 2017-07-18 |
JP2014208902A (ja) | 2014-11-06 |
US20160024632A1 (en) | 2016-01-28 |
AU2014245876A1 (en) | 2015-10-08 |
CA2904131C (fr) | 2019-10-22 |
CN105051238A (zh) | 2015-11-11 |
EP2980259A1 (fr) | 2016-02-03 |
KR20150133708A (ko) | 2015-11-30 |
AU2014245876B2 (en) | 2018-06-14 |
EP2980259A4 (fr) | 2016-11-30 |
NZ711709A (en) | 2020-07-31 |
US9523142B2 (en) | 2016-12-20 |
CN105051238B (zh) | 2017-10-10 |
MY172243A (en) | 2019-11-19 |
JP5826321B2 (ja) | 2015-12-02 |
SG11201507737QA (en) | 2015-10-29 |
WO2014157155A1 (fr) | 2014-10-02 |
CA2904131A1 (fr) | 2014-10-02 |
MX2015013368A (es) | 2016-01-08 |
MX366702B (es) | 2019-07-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
SG10201707903VA (en) | Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same | |
HK1199910A1 (zh) | 製造耐腐蝕、光澤、金屬塗覆基材的方法,該金屬塗覆基材,及其用途 | |
SG11201706948RA (en) | HOT-DIP Al-Zn-Mg-Si COATED STEEL SHEET AND METHOD OF PRODUCING THE SAME | |
EP3006526A4 (fr) | Tôle d'acier revêtue d'un complexe d'aluminium et de zinc par un procédé d'immersion à chaud et caractérisée par une remarquable résistance aux intempéries, à la corrosion et aux bases, son procédé de fabrication et agent de traitement de surface associé | |
EP3054025A4 (fr) | Tôle d'acier galvanisé à chaud à haute résistance et son procédé de fabrication | |
EP3085802A4 (fr) | Tôle d'acier galvanisée par immersion à chaud, à résistance élevée et son procédé de fabrication | |
ZA201309330B (en) | Cold-rolled steel plate coated with zinc or a zinc alloy, method for manufacturing same, and use of such a steel plate | |
EP2990501A4 (fr) | Tôle d'acier galvanisée par immersion à chaud alliée destinée à être utilisée lors d'un estampage à chaud et procédé permettant de fabriquer une pièce en acier | |
EP2957648A4 (fr) | TÔLE EN ACIER GALVANISÉE À CHAUD DANS UN BAIN Al-Zn ET PROCÉDÉ DE PRODUCTION CORRESPONDANT | |
ZA201409389B (en) | Outer coating for an underground piping member made from iron, coated piping member and method for depositing the coating | |
EP3045558A4 (fr) | Tôle d'acier galvanisée par immersion à chaud et tôle d'acier recuite après galvanisation ayant une apparence et une adhésivité excellentes de placage et son procédé de fabrication | |
ZA201503075B (en) | Alloyed hot-dip galvanized steel sheet and method of manufacturing the same | |
EP2762601A4 (fr) | Tôle d'acier comprenant une couche galvanisée à chaud au trempé et présentant une mouillabilité et une adhérence supérieures et son procédé de production | |
EP2876182A4 (fr) | Bande d'acier plaquée d'alliage de zinc fondu présentant une excellente résistance à la corrosion et une excellente surface externe et procédé de fabrication correspondant | |
EP3205741A4 (fr) | Procédé de métallisation par immersion à chaud en continu, bande d'acier zinguée par immersion à chaud et matériel de métallisation par immersion à chaud en continu | |
EP3106528A4 (fr) | Feuille d'acier galvanisée par immersion à chaud de haute résistance, et procédé de fabrication de feuille d'acier galvanisée par immersion à chaud, alliée, à haute résistance | |
EP3045559A4 (fr) | Feuille d'acier galvanisée par immersion à chaud et feuille d'acier recuite après galvanisation d'apparence et de capacité d'adhésion de revêtement excellentes, et leur procédé de fabrication | |
EP3530768A4 (fr) | Tôle d'acier plaquée, procédé de fabrication d'une tôle d'acier galvanisée à chaud, et procédé de fabrication de tôle d'acier allié galvanisée à chaud | |
PL3018230T3 (pl) | Blacha stalowa cienka walcowana na zimno, ocynkowana blacha stalowa cienka walcowana na zimno oraz sposób ich wytwarzania | |
EP2963152A4 (fr) | Tôle d'acier plaquée avec du zinc contenant de l'aluminium et procédé permettant de produire cette dernière | |
EP3034646A4 (fr) | Procédé de production pour tôles d'acier à haute résistance galvanisées par immersion à chaud et procédé de production pour tôles d'acier allié à haute résistance galvanisées par immersion à chaud | |
PL3553201T3 (pl) | Sposób wytwarzania formowanej blachy stalowej powleczonej metaliczną powłoką na bazie glinu i zawierającą tytan | |
EP2940180A4 (fr) | Tôle d'acier revêtue d'aluminium-magnésium et son procédé de fabrication | |
EP3103892A4 (fr) | Tôle d'acier allié galvanisé par immersion à chaud et son procédé de production | |
PT2954086T (pt) | Chapa com revestimento de znalmg com uma microestrutura particular e correspondente processo de produção |