RU2633210C2

RU2633210C2 - Applying decorative enamel to products from amber

Info

Publication number: RU2633210C2
Application number: RU2015144877A
Authority: RU
Inventors: Сергей Александрович Самарин; Александр Анатольевич Кузин; Владимир Евгеньевич Корешков
Original assignee: Общество с ограниченной ответственностью "Эль-Боско"
Priority date: 2015-10-20
Filing date: 2015-10-20
Publication date: 2017-10-11
Also published as: RU2015144877A

Abstract

FIELD: technological processes.

SUBSTANCE: method of applying decorative enamel to the products of amber is characterized by the fact that at the heart of amber product a recess is carved along the area of future figure, the depth of 0.5-1 mm, then the enamel of cold chemical curing is poured into the cut recess on the amber plate and placed in a muffle furnace heated to a temperature of 40-80°C, with a holding time of 4-24 hours, depending on the composition, layer thickness and enamel colour, or light-curing enamel is pour, and is stand under ultraviolet radiation with a wavelength of 195-480 nm, with a holding time of 2-10 minutes, depending on the composition, layer thickness and enamel colour.

EFFECT: obtaining decorative effect from connection of decorative product from amber with applied enamel, adjusting transparency and colour of received products.

1 cl

Description

Изобретение относится к области изготовления декоративных украшений из янтаря, а также к получению особых декоративных эффектов.The invention relates to the field of manufacturing decorative amber jewelry, as well as to obtaining special decorative effects.

Известен патент на изобретение RU №2314934, в котором описан способ, заключающийся в том, что на пластине из янтаря, полученной методом прессования, вырезается рисунок. Затем в емкость с бесцветной эмалью, холодного химического отверждения, разогретой до температуры 43°С, погружается янтарная пластина с нанесенным рисунком и вакуумируется в течение 1,5 часов. Причем состояние вакуума поддерживают в течение 10 минут. После вакуумирования пластина янтаря, покрытая бесцветной эмалью, сушится при температуре 30-45°С на воздухе, в течение 24 часов. При осуществлении способа может использоваться только бесцветная эмаль.Known patent for the invention RU No. 2314934, which describes the method, which consists in the fact that on a plate of amber obtained by pressing, cut out the picture. Then, an amber plate with a pattern is immersed in a container with colorless enamel, cold chemical curing, heated to a temperature of 43 ° C, and vacuumized for 1.5 hours. Moreover, the state of vacuum is maintained for 10 minutes. After evacuation, the amber plate coated with colorless enamel is dried at a temperature of 30-45 ° C in air for 24 hours. When implementing the method, only colorless enamel can be used.

Данная технология проста, однако требует наличия вакуумной камеры, кроме того, не обеспечивает требуемого декоративного эффекта, поскольку применяется бесцветная эмаль. Кроме того, из-за сил поверхностного натяжения на поверхности эмали, не обеспечивается 100-процентное залегание эмали только в вырезанные на поверхности янтаря выемки. Обязательно будут присутствовать частичные растекания эмали по поверхности изделия. Нанесенное покрытие в высушенном состоянии выглядит неаккуратно и требует впоследствии финишной обработки, как правило, шлифовки и полировки.This technology is simple, but it requires a vacuum chamber, in addition, it does not provide the required decorative effect, since colorless enamel is used. In addition, due to the surface tension forces on the enamel surface, 100% enamel coverage is not ensured only in recesses cut out on the surface of amber. Partial spreading of enamel on the surface of the product will certainly be present. The applied coating in the dried state does not look well and subsequently requires finishing, as a rule, grinding and polishing.

Задачей данного изобретения является получение декоративного эффекта от соединения декоративного изделия из янтаря с нанесенной эмалью, регулирование прозрачности и цвета получаемых изделий.The objective of the invention is to obtain a decorative effect from combining a decorative amber product with applied enamel, regulating the transparency and color of the resulting products.

Технический результат отличается технологичностью и снижением трудоемкости, не требует применения сложного оборудования.The technical result is technologically advanced and reduces the complexity, does not require the use of sophisticated equipment.

Технический результат достигается тем, что в основе изделия из янтаря делают выемки глубиной 0,5-1 мм, которые соответствуют будущему рисунку эмалью, и в них вручную заливают эмаль. Далее, в зависимости от технологии отверждения эмали, поступают по-разному.The technical result is achieved by the fact that at the base of the amber product, they make recesses with a depth of 0.5-1 mm, which correspond to the future pattern with enamel, and enamel is manually poured into them. Further, depending on the technology of curing enamel, they act differently.

Если применяется химически отверждаемая эмаль, изделие помещают в муфельную печь, разогретую до температуры 40-80°С, и выдерживают в печи от 4 до 24 часов, в зависимости от состава, толщины слоя и цвета эмали. Если применяется светоотверждаемая эмаль, изделие помещают в камеру с ультрафиолетовым излучением с длиной волны 195-480 нм, с временем выдержки 2-10 минут, в зависимости от состава, толщины слоя и цвета эмали. При необходимости осуществляется окончательная обработка затвердевшей эмали шлифовальной бумагой и абразивными (полировочными) пастами.If chemically set enamel is used, the product is placed in a muffle furnace heated to a temperature of 40-80 ° C and kept in the oven for 4 to 24 hours, depending on the composition, layer thickness and color of the enamel. If light-curing enamel is used, the product is placed in a chamber with ultraviolet radiation with a wavelength of 195-480 nm, with a holding time of 2-10 minutes, depending on the composition, layer thickness and color of the enamel. If necessary, final processing of hardened enamel with sanding paper and abrasive (polishing) pastes is carried out.

Данный способ применим в ювелирной промышленности.This method is applicable in the jewelry industry.

Claims

The method of applying decorative enamel on amber products, characterized in that the basis of the amber product is cut out a recess in the area of the future pattern, 0.5-1 mm deep, then cold chemical curing enamel is poured onto the amber plate in the cut-out recess and placed in a muffle furnace heated to a temperature of 40-80 ° C, with a holding time of 4-24 hours, depending on the composition, layer thickness and color of the enamel, or pour light-cured enamel, and incubated under ultraviolet radiation with a wavelength of 195-480 nm, with an rzhki 2-10 minutes depending on the composition, thickness and color enamel.